Abstract
The ultimate frontier in nanomaterials engineering is to realize their composition control with atomic scale precision to enable fabrication of nanoparticles with desirable size, shape and surface properties. Such control becomes even more useful when growing hybrid nanocrystals designed to integrate multiple functionalities. Here we report achieving such degree of control in a family of rare-earth-doped nanomaterials. We experimentally verify the co-existence and different roles of oleate anions (OA−) and molecules (OAH) in the crystal formation. We identify that the control over the ratio of OA− to OAH can be used to directionally inhibit, promote or etch the crystallographic facets of the nanoparticles. This control enables selective grafting of shells with complex morphologies grown over nanocrystal cores, thus allowing the fabrication of a diverse library of monodisperse sub-50 nm nanoparticles. With such programmable additive and subtractive engineering a variety of three-dimensional shapes can be implemented using a bottom–up scalable approach.
Similar content being viewed by others
Introduction
Nanocrystal engineering, design and fabrication of nanocrystals with desirable size, shape1,2,3,4,5,6, surface properties7 and composition8,9 is attracting growing interest due to its essential role in fundamental research and commercial relevance. Rare-earth-doped upconversion nanocrystals have recently emerged as the new generation of functional nanomaterials, because they exhibit exceptional optical, magnetic and chemical properties underpinning their diverse applications. In particular, alkaline rare-earth fluoride (AREF4) nanocrystals10,11,12, including hexagonal-phase β-NaYF4, β-NaGdF4, β-NaNdF4 or β-NaLuF4 are used in full-colour displays12,13, photovoltaics14, security inks15, forensic science16, autofluorescence-free biomolecular sensing17,18,19, multimodal in vivo bio-imaging (fluorescence, magnetic resonance imaging, X-ray, SPECT and so on.)20 and theranostics17,21,22,23. A trial-and-error approach is frequently used to produce nanoparticles with spherical, rod-like or other shapes24,25,26 by varying dopant concentrations and/or constituent materials27, reaction time and temperature28,29,30,31. This random sampling of vast, multidimensional parameter space, needs to be done rationally, with proper understanding of the underpinning growth mechanisms.
Here we find that oleate anions (OA−), the dissociated form of oleic acid molecules (OAH), have variable, dynamic roles in mediating the growth of AREF4 nanocrystals. This allows us to introduce a molecular approach to tailoring the shape and composition of AREF4 nanocrystals. This new method is based on a selective epitaxial core–shell growth process in the presence of oleic acid, commonly used as a surfactant during the synthesis of β-AREF4 nanocrystals32. Drawing inspiration from the recently discovered co-existence of oleic acid molecules (OAH) and their dissociated form, oleic acid ions (OA−) in the binary systems of PbS33 and PbSe nanocrystals34, we hypothesize that the change in the ratio of OA− to OAH could influence the interaction of these ligands with the particle surface and hence the resulting morphology. Our computational modelling (Fig. 1, Supplementary Figs 1–6, Supplementary Notes 1 and 2 and Supplementary Table 1) and experimental results (Figs 2, 3, 4, Supplementary Figs 7–35, Supplementary Tables 2 and 3 and Supplementary Notes 3–18) demonstrate that the preferential affinity of OAH and OA− to different crystalline facets dictates the formation of nanocrystals of different shape. Importantly, we demonstrate that the precise control over the shell thickness and the particle shape can be achieved by deliberately switching the passivation, additive and subtractive roles of these surfactants.
Results
Computational modelling
To quantify the surface coordination chemistry between β-NaYF4 surface and OAH and OA− ligands, we performed first-principles calculations based on density functional theory using CASTEP (CAmbridge Serial Total Energy Package)35. As shown in Fig. 1b and Supplementary Fig. 1, we treated the (001) and (100) planes of the β-NaYF4 nanocrystals terminated with specific atomic arrangement as the most stable facets according to the calculated surface energies. Considering that the oxygen moiety in the ligands has a strong binding affinity to Y3+ ions at the particle surface36, we modelled the interactions between the OAH and OA− molecules and the Y3+ ions under a number of conditions, such as different adsorption configurations (Supplementary Figs 2 and 3 and Supplementary Note 1), ligand chain length and ligand coverage (Supplementary Figs 4 and 5 and Supplementary Note 2). The key conclusion from these simulations is that OA− preferentially binds to RE3+ ions exposed on the (100) facet of the hexagonal fluoride nanocrystal, with a much higher binding energy (−35.4 eV) than on the (001) facet (−21.8 eV). It should be noted that the OAH molecule binds with a higher probability to the (001) facet than the (100) facet and has relatively small binding energies of −9.4 eV and −4.6 eV, respectively, on each of these facets (Supplementary Table 1). Our charge analysis (Supplementary Fig. 6) further indicates that such selective binding is attributed to the difference in the atomic arrangements of these two facets (Fig. 1b), giving rise to different charge transfer paths between the ligands and the surface ions.
Controlled epitaxial growth direction
The binding preferences of OAH and OA− molecules to different facets were first used to induce longitudinal epitaxial growth. We demonstrated (Fig. 1c) that sub-micrometre-sized NaYF4 crystals of different aspect ratios could be prepared by tuning the concentration ratio of OA− to OAH in the hydrothermal synthesis system. As shown in Supplementary Fig. 7, higher concentrations of OA− encourage epitaxial growth along a longitudinal direction. A similar effect was observed in the synthesis of sub-50 nm NaYF4 nanoparticles prepared by a co-precipitation method. Figure 2a,b show that high concentration of NaOH leads to longitudinally grown nanoparticles because of a large concentration of passivating OA− ions on the (100) facets (Supplementary Figs 8–10). The zeta potential of +20 mV for NaYF4 nanocrystals after the removal of ligands (Supplementary Fig. 11) shows that the RE3+ cations are more abundant on the crystal surfaces than the F− ions. We further systemically studied other possible factors that could influence the epitaxial shell growth (experimental details in Supplementary Methods), including the reaction temperature (Supplementary Fig. 12 and Supplementary Note 3), the oleic acid concentration (Supplementary Fig. 13 and Supplementary Note 4), the F− ion concentration (Supplementary Fig. 14 and Supplementary Note 5) and the Na+ concentration (Supplementary Fig. 15 and Supplementary Note 6). From these results, we confirm that the ratio of OA−/OAH is a key factor that determines the epitaxial shell growth direction. However other parameters also have an effect on the growth speed or can change the OA−/OAH ratio that indirectly affects the direction of growth. To rule out the effect of OH− on longitudinal growth, we added sodium oleate as the sodium source instead of hydroxide and identical results were obtained (Supplementary Fig. 16 and Supplementary Note 7). Supplementary Figures 17 and 18 further confirm that high ratio of OA−/OAH directs longitudinal deposition of heterogeneous shells (NaGdF4) on the end surfaces of NaYF4 core. Interestingly, subtractive growth (dissolution) is observed from their side (100) surfaces. This results in concurrent decrease of the core width from 26 to 18 nm, thus producing dumbbell-shaped nanocrystals (Supplementary Note 8).
Moreover, we found that the addition of KOH further accelerates longitudinal growth rate (Supplementary Fig. 19 and Supplementary Note 9) due to a higher dissociation constant of KOH than NaOH, which increases the dissociation of OAH producing more OA−. With the aid of KOH, heterogeneous ‘bamboo-shaped’ nanorods (NRs) with sharp edges were formed in a stepwise manner with a length of up to 173 nm (Fig. 2b, Supplementary Fig. 21 and Supplementary Note 10). The interesting one-dimension architecture of ‘bamboo-shaped’ NRs suggests that integrated multiple functionalities can be built. Thus our new platform enables rational design and facile synthesis of multiple sections of rare-earth-doped heterogeneous materials and investigation of their interactions and functions within a single integrated rod. We were also able to induce transversal epitaxial growth by increasing the amount of OAH and reducing the amount of NaOH. At a reaction temperature of 290 °C, the transversal growth was observed and NaGdF4 rings of 7-nm-thick around the NaYF4 cores formed without a measurable change in the longitudinal direction (Fig. 2c, Supplementary Figs 23 and 24 and Supplementary Note 11). Notably, the dissolution of the (100) facets of the cores took place as well, and the width of the core was, again, reduced from 49 to 30 nm at both ends. The observed dissolution always occurred on the (100) facets in both cases of longitudinal and transversal growth. This is consistent with the strong chelating character of OA− on the (100) facet, and with the fact that NaYF4 is dissolved faster than NaGdF4 because NaYF4 is comparably less energetically stable12. To shed more light on this issue, we provided more evidence in the Supplementary Fig. 25 and Supplementary Note 12 to show that the dissolution of core is caused by the thermal stability difference between core and shell materials in presence of OA− which leads to higher binding strength on the side surfaces. By comparing growth of NaTbF4 as shell or NaYbF4 as shell on a NaYF4 core (Supplementary Fig. 25), we demonstrate that the dissolution of the core requires the shell materials to have higher thermal stability than the core material. Larger difference of thermal stability between core and shell result in a higher dissolution rate.
Controlled migration growth
By combining the approaches of longitudinal and transversal growth and selective dissolution with consideration of lattice mismatch (Supplementary Tables 2 and 3), we synthesized a variety of three-dimensional (3D) hybrid nanostructures (Supplementary Figs 26–34). Figure 3 shows a typical example of real-time evolution of morphology and composition of the NaYF4/NaGdF4/NaNdF4 NCs, including the dissolution process of the NaYF4/NaGdF4 nanocrystals and subsequent longitudinal growth of NaNdF4. The dissolution of NaYF4/NaGdF4 is initiated by the OA− adsorbed on the surface of the nanocrystals. The concomitant depletion of dissolved F− ions used for longitudinal growth of NaNdF4 in the presence of high concentration of OA− facilitates the dissolution of NaYF4/NaGdF4 nanocrystals and this, in turn, promotes longitudinal growth of NaNdF4. Following the dissolution of the Y3+ and Gd3+ ions from the surface of NaYF4–NaGdF4 nanocrystals, these ions then participate in the epitaxial growth of NaNdF4 nanocrystals, as evidenced by the elemental mapping (Fig. 3h). Moreover, our real-time sampling transmission electron microscope data further confirmed the underpinning mechanism (Fig. 3a–g, Supplementary Figs 26–28). The size of nanocrystal core decreased significantly in the first 5 min, indicating that the dissolution rate of the nanocrystals is faster than their growth rate. After 15 min, new material started to form at the top and at the bottom ends of the core with simultaneous decrease of the nanocrystal core width. This observation rules out ‘surface mobility’ (‘atom diffusion’) as the possible driving force behind the formation of the final shell, otherwise it is expected that the dissolution of NaYF4 and growth of NaNdF4 would occur at the same time. The only mechanism which explains the shape of this nanocrystal is that the absence of F− source in the reaction solution at its beginning prevents growth of NaNdY4 until the concentration of released F− source exceeds a certain threshold.
Our control experiments (Supplementary Fig. 29 and Supplementary Note 15) further support the mechanism of OA−-induced dissolution in which a firm bonding of the surfactant OA− to the surface RE3+ cations is the main factor responsible for the removal of the surface crystalline layers (experimental details in Supplementary Methods). As shown in Supplementary Fig. 29, we applied transversal growth approach to first grow a layer of NaGdF4 on the side surfaces of NaYF4 core. We see that smaller mismatch of NaGdF4 versus NaNdF4 compared with the NaYF4 versus NaNdF4 fails to direct the transversal migration growth of the NaNdF4 on the side surfaces of NaGdF4. Instead, dissolution occurs in the first 10 min of the reaction (Supplementary Fig. 29a,b) and both dissolution from the side surfaces and epitaxial growth of NaNdF4 on the end surfaces of NaGdF4/NaYF4 cores result in a thinner and longer nanocrystal.
Guided by the principle that the ratio of OA−/OAH controls the direction of epitaxial shell growth, we further demonstrated (as shown in Supplementary Fig. 30 and Supplementary Note 16) that a low ratio of OA−/OAH at a lower temperature directs the migration growth along transverse direction. This enables the formation of heterogeneous NaYF4/NaGdF4/NaNdF4 nanocrystals in the shape of a flower, although in this case the dissolution process on the side surfaces of nanocrystals is much less efficient because there are too few OA− ligands bound to RE3+ cations on the (100) facet. Two additional experiments (Supplementary Note 17) demonstrate that well established parameters, such as reagent concentration, can be further applied to fine-tune our programmable protocols for other types of heterogeneous nanocrystals. During the formation of hourglass-shaped nanocrystals, the decrease in the amount of Nd3+ source is found to hinder the migration growth process and yield sharper tips (Supplementary Fig. 31), whereas a supply of additional F− ions in the reaction increases the diameter of dumbbell ends with round tips (Supplementary Fig. 32). Such level of fine tuning to grow progressively sharper tips may suggest future rational methods, for example to optimize tip-sensitive physical and biochemical properties of NRs.
Figure 4 shows an array of heterogeneous NaREF4 nanostructures synthesized by carrying out specific sequences of longitudinal, transversal growth, selective dissolution and directional migration growth of epitaxial shells in the presence of various OA−/OAH ratios. To the best of our knowledge, these sub-50 nm nanoparticles are the smallest 3D objects prepared by a bottom–up additive and subtractive process. To illustrate the application of this novel method we designed and synthesized multifunctional NaYF4/NaLuF4/NaGdF4 heterogeneous nanocrystals with two NaGdF4 rings on a NaLuF4/NaYF4 NRs (Supplementary Figs 33 and 34 and Supplementary Note 18). The hexagonal-phase NaYF4 nanocrystal is an efficient luminescence upconversion material37. The addition of NaLuF4 enables X-ray computed tomography38, whereas using NaGdF4 enables magnetic resonance imaging39. To the best of our knowledge, this work presents the first controlled fabrication of sub-50 nm 3D shaped heterogeneous nanocrystals logically programmed by the combinational approaches of OA−-assisted longitudinal growth, transversal growth and selective crystalline facet dissolution with consideration of crystallographic mismatch rates.
Discussion
The nanoscale engineering capability presented in this work enables quantitative studies which are virtually impossible by conventional approaches. We anticipate that optical properties of these nanostructures can be designed to precisely promote or inhibit inter-particle energy transfer. Similarly, magnetic properties may be optimized to enhance magnetic resonance imaging by correlating the morphology with the surface distribution of magnetic signals. In addition, such hybrid nanomaterials may be used as a platform for transporting biologically important molecules across cell membranes. Furthermore, access to a new library of precisely controlled shapes of nanoparticles provide a novel approach for the targeted delivery in nanomedicine where optimized morphologies of these nanoscale molecular carriers will yield greater efficiencies. This process could be further facilitated by harnessing the anisotropic properties of different types of nanoparticles that permit diverse surface functionalizations and multi-modal bio-conjugations. The concept presented in this work may further advance our current capabilities of nanoscale programmable and reproducible engineering of new classes of heterogeneous materials in scalable quantities. Our findings may lead to a new class of multifunctional nanomaterials and provide the groundwork for developing previously unforeseen applications of nanoparticles with complex programmable shapes and surface properties.
Methods
Hydrothermal synthesis of NaYF4 crystal
The β-NaYF4 disks were synthesized via a slightly modified hydrothermal reaction. In a typical experiment, NaOH (3.75 mmol) was first dissolved into 1.5 mL of double distilled water, followed by the addition of OA (7.5 mmol) and ethanol (2.5 mL) while undergoing vigorous stirring. Thereafter, an aqueous solution of NaF (0.5 M; 2 mL) was added to form a turbid mixture. Subsequently, a 1.2 mL aqueous solution of YCl3 (Yb3+/Tm3+=10/0.5 mol%; 0.2 M) was added and the solution was stirred for 20 min. The resulting mixture was then transferred into a 14 mL Teflon-lined autoclave and heated to 220 °C and the temperature maintained for 12 h. After cooling down to room temperature, the reaction product was isolated by centrifugation and washed with ethanol. In this work, different amounts of NaOH were added to adjust the ratio of OA−/OAH by its reaction with OAH to form OA−.
NaYF4 nanocrystal cores
In a typical procedure, 4 ml of methanol solution of YCl3 (2.0 mmol) was magnetically mixed with OA (38 mmol) and ODE (93 mmol) in a 100-ml three-neck round-bottom flask. The mixture was then degassed under the Ar flow and then heated to 150 °C for 30 min to form a clear solution, before cooling to room temperature. 15 ml of methanol solution containing NH4F (8 mmol) and NaOH (5 mmol) was added to the solution of YCl3 in OA and ODE and stirred for 60 min. The mixture solution was slowly heated to 110 °C and kept at 110 °C for 30 min to completely remove methanol and any residual water. The mixture solution was then quickly heated to the reaction temperature of 300 °C and aged for 1 h. After the solution was left to cool down to room temperature, ethanol was added to precipitate the nanocrystals. The product was washed with cyclohexane, ethanol and methanol for at least 4 times, before the final NaYF4 nanocrystals were re-dispersed in 10 ml cyclohexane in preparation for their further use.
Longitudinal growth of NaYF4 NRs
YCl3 (0.2 mmol) in 1 ml methanol solution was magnetically mixed with OA (9.5 mmol) and ODE (25 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (5 ml) containing NH4F (0.8 mmol) and NaOH (0.5 mmol) was added and stirred for 60 min. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to completely remove methanol and residual water. The solution was then injected with 0.2 mmol NaYF4 of nanocrystals in cyclohexane and the mixture kept at 110 °C for another 10 min to evaporate the cyclohexane. Then, the reaction mixture was quickly heated to 310 °C and aged for 1 h.
NaGdF4/NaYF4 nano-dumbbells
GdCl3 (0.2 mmol) in 1 ml methanol solution was magnetically mixed with OA (9.5 mmol) and ODE (25 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under an Ar flow and heated to 150 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (4 ml) containing NH4F (0.8 mmol) and NaOH (0.5 mmol) was added to the OA and ODE solution and stirred for 60 min. The solution is slowly heated to 110 °C and kept at 110 °C for 30 min to remove methanol and the remaining water completely. Then, 0.2 mmol of NaYF4 core nanocrystals in cyclohexane was injected into the reaction solution. After holding the reaction temperature at 110 °C for further 10 min to evaporate all cyclohexane, the reaction mixture was quickly heated to 310 °C and aged for 1 h.
NaGdF4/NaYF4 NRs by adding KOH
GdCl3 (0.2 mmol) in 1 ml of methanol solution was magnetically mixed with OA (9.5 mmol) and ODE (25 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 min to form a clear solution, before cooling to room temperature. Methanol solution (5 ml) containing NH4F (0.8 mmol), KOH (0.4 mmol) and NaOH (0.5 mmol) was added into the OA and ODE solution and stirred for 60 min. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to remove the methanol and water completely. The reaction mix was then injected with 0.2 mmol of NaYF4 core nanocrystals in cyclohexane, into the reaction solution. After holding the reaction mix at 110 °C for further 10 min to evaporate all cyclohexane, the mixture was heated rapidly to 310 °C before aging for 1 h at this temperature.
NaYF4/NaGdF4/NaYF4 NCs in a bamboo-like shape
0.2 mmol of YCl3 in 1 ml of methanol solution was magnetically mixed with OA (9.5 mmol) and ODE (25 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (5 ml) containing NH4F (0.8 mmol), KOH (0.4 mmol) and NaOH (0.5 mmol) was added into the OA and ODE solution and stirred for 60 minutes. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to remove the methanol and water completely. The reaction solution was then injected with 0.2 mmol of NaYF4/NaGdF4 NRs in cyclohexane solution. After the reaction at 110 °C for a further 10 min to evaporate all the cyclohexane, the reaction mixture was quickly heated to 310 °C and held at this temperature for 1 h.
NaYF4/NaGdF4/NaYF4/NaGdF4 NCs in a bamboo-like shape
The same procedure for synthesizing NaYF4/NaGdF4/NaYF4 NCs in bamboo-like shape was repeated, and then followed by the injection of 0.2 mmol of the five-section NaYF4/NaGdF4/NaYF4 nano-bamboos which acted as the core, all in cyclohexane solution, into the reaction solution. After holding at 110 °C for a further 10 min to evaporate all cyclohexane, the reaction mixture was quickly heated to 310 °C and held again for 1 h.
NaYF4/NaGdF4/NaNdF4 NCs in an hourglass shape
NdCl3 (0.4 mmol) in 2 ml of methanol solution was magnetically mixed with OA (9.5 mmol) and ODE (25 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (5 ml) containing KOH (0.8 mmol) and NaOH (0.8 mmol) was added and stirred for 60 min. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to completely remove the methanol and some of the water. It was then injected with 0.1 mmol 50 nm × 60 nm NaYF4/NaGdF4 nano-prisms particles, in a solution of cyclohexane. After having been kept at 110 °C for another 10 min to evaporate all cyclohexane, the reaction mixture was quickly heated to 310 °C. Samples (500 ul) of the reaction solution were collected each time with a syringe at 5, 15, 30, 40, 50 and 60 min after the start of the reaction.
Transversal growth of NaGdF4 shell onto NaYF4 core
GdCl3 (0.1 mmol) in 1 ml methanol solution was magnetically mixed with OA (19.0 mmol) and ODE (18.7 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (3 ml) containing NH4F (0.4 mmol) and NaOH (0.15 mmol) was added into the OA and ODE solution and stirred for 60 min. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to remove completely the methanol and water. Then 0.1 mmol of the NaYF4 cores in cyclohexane solvent were injected into the reaction mix. After being kept at 110 °C for further 10 min to evaporate all cyclohexane, the reaction mixture was quickly heated up to 290 °C and held at that temperature for 3 h.
Synthesis of NaYF4/NaGdF4/NaNdF4 NCs in flower shape
NdCl3 (0.1 mmol) in 1 ml of methanol solution was magnetically mixed with OA (19 mmol) and ODE (18.7 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (5 ml) containing NaOH (0.6 mmol) was added and stirred for 60 min. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to completely remove the methanol and some of the water. Then, the reaction mix was injected with 0.1 mmol of 50 nm NaYF4/NaGdF4 nano-prisms prisms (NaGdF4 growing on the lateral faces of NaYF4 nanocrystal), suspended in a cyclohexane solution. After holding at 110 °C for another 10 min to evaporate all cyclohexane, the reaction mixture was quickly heated to 300 °C. samples (500 ul) of the reaction solution were collected each time with a syringe after 10, 25 and 45 min of the reaction time.
Synthesis of NaYF4/NaGdF4/NaNdF4 sharp-end dumbbell
NdCl3 (0.1 mmol) in 1 ml of methanol solution was magnetically mixed with OA (9.5 mmol) and ODE (25 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 160 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (5 ml) containing KOH (0.2 mmol) and NaOH (0.2 mmol) was added and stirred for 60 min. Note: in this reaction no NH4F was added to the solution. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to remove the methanol and the water completely. It was then injected with 0.1 mmol of NaYF4/NaGdF4 NR particle in suspended in cyclohexane solvent into the reaction solution. After holding at 110 °C for a further 10 min to evaporate all cyclohexane, the reaction mixture was quickly heated to 310 °C and held at this temperature for a further 30 min.
Synthesis of NaYF4/NaGdF4/NaNdF4 round-end dumbbell
NdCl3 (0.1 mmol) in 1 ml of methanol solution was magnetically mixed with OA (9.5 mmol) and ODE (25 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 160 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (5 ml) containing NH4F (0.3 mmol), KOH (0.2 mmol) and NaOH (0.2 mmol) was added and the mixture was stirred for 60 min. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to remove the methanol and the water completely. Then, it was injected with 0.1 mmol of NaYF4/NaGdF4 NRs suspended in cyclohexane into the reaction solution. After being held at 110 °C for further 10 min to evaporate all cyclohexane, the reaction mixture was quickly heated to 310 °C and held for 30 min at this temperature.
Synthesis of pure α-NaGdF4 NCs
Methanol solution (2 ml) of GdCl3 (1.0 mmol) was magnetically mixed with OA (19 mmol) and ODE (47 mmol) in a 100-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 minutes to form a clear solution, and then cooled to room temperature. Methanol solution (10 ml) containing NH4F (4 mmol) and NaOH (2.5 mmol) was added and stirred for 60 min. Then, the solution was slowly heated to 110 °C and kept at 110 °C for 30 min to remove the methanol and water completely. After that, the reaction mixture was quickly heated to 240 °C and aged for 45 min.
Synthesis of NaLuF4/NaYF4 NRs
LuCl3 (0.1 mmol) in 1 ml method solution was magnetically mixed with OA (19 mmol) and ODE (25 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (2 ml) containing NaOH (0.15 mmol) and 0.4 mmol NH4F was added and stirred for 60 min. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to completely remove the methanol and some of the water. It was then injected with 0.4 mmol of NaYF4 seed particles in a cyclohexane solution. After holding the reaction mix at 110 °C for a further 10 min to evaporate cyclohexane, the reaction mixture was quickly heated to 290 °C and held at that temperature for a further 1 h.
Synthesis of NaLuF4/NaYF4 NRs with NaGdF4 double-ring
GdCl3 (0.1 mmol) in 1 ml methanol solution was magnetically mixed with OA (19.0 mmol) and ODE (18.7 mmol) in a 50-ml three-neck round-bottom flask. The mixture was degassed under Ar flow and heated to 150 °C for 30 min to form a clear solution, and then cooled to room temperature. Methanol solution (2 ml) containing NaOH (at 0.15 mmol) was added and stirred for 60 min. The solution was slowly heated to 110 °C and kept at 110 °C for 30 min to completely remove the methanol and some of the water. It was then injected with 0.1 mmol of the NaYF4/NaLuF4 seed particles, in a cyclohexane solution, into the reaction solution. After having been held the reaction mix at 110 °C for another 10 min to evaporate cyclohexane, the reaction mixture was quickly heated to 300 °C. It was then, injected with 0.02 mmol of α-NaGdF4 nanocrystals into the reaction system. This was done every 10 min for 5 times at 300 °C. The reaction mix was held at this temperature for another 10 min after the last injection.
Additional information
How to cite this article: Liu, D. et al. Three-dimensional controlled growth of monodisperse sub-50 nm heterogeneous nanocrystals. Nat. Commun. 7:10254 doi: 10.1038/ncomms10254 (2016).
References
Jia, G. H. et al. Couples of colloidal semiconductor nanorods formed by self-limited assembly. Nat. Mater. 13, 302–308 (2014).
Jones, M. R., Seeman, N. C. & Mirkin, C. A. Programmable materials and the nature of the DNA bond. Science 347, 1260901 (2015).
Ye, X. et al. Seeded growth of metal-doped plasmonic oxide heterodimer nanocrystals and their chemical transformation. J. Am. Chem. Soc. 136, 5106–5115 (2014).
Yu, H. et al. Dumbbell-like bifunctional Au-Fe3O4 nanoparticles. Nano Lett. 5, 379–382 (2005).
Jun, Y. W., Choi, J. S. & Cheon, J. Shape control of semiconductor and metal oxide nanocrystals through nonhydrolytic colloidal routes. Angew. Chem. Int. Ed. 45, 3414–3439 (2006).
Hill, J. P. et al. Self-assembled hexa-peri-hexabenzocoronene graphitic nanotube. Science 304, 1481–1483 (2004).
Yin, Y. & Alivisatos, A. P. Colloidal nanocrystal synthesis and the organic-inorganic interface. Nature 437, 664–670 (2005).
Zeng, H. & Sun, S. H. Syntheses, properties and potential applications of multicomponent magnetic nanoparticles. Adv. Funct. Mater. 18, 391–400 (2008).
Qian, H. F., Zhu, Y. & Jin, R. C. Atomically precise gold nanocrystal molecules with surface plasmon resonance. Proc. Natl Acad. Sci. USA 109, 696–700 (2012).
Zheng, W. et al. Lanthanide-doped upconversion nano-bioprobes: electronic structures, optical properties, and biodetection. Chem. Soc. Rev. 44, 1379–1415 (2015).
Wang, X., Zhuang, J., Peng, Q. & Li, Y. D. A general strategy for nanocrystal synthesis. Nature 437, 121–124 (2005).
Wang, F. et al. Simultaneous phase and size control of upconversion nanocrystals through lanthanide doping. Nature 463, 1061–1065 (2010).
Deng, R. et al. Temporal full-colour tuning through non-steady-state upconversion. Nat. Nanotechnol. 10, 237–242 (2015).
Ramasamy, P. & Kim, J. Combined plasmonic and upconversion rear reflectors for efficient dye-sensitized solar cells. Chem. Commun. 50, 879–881 (2014).
Lu, Y. Q. et al. Tunable lifetime multiplexing using luminescent nanocrystals. Nat. Photon. 8, 33–37 (2014).
Wang, J. et al. Near-infrared-light-mediated imaging of latent fingerprints based on molecular recognition. Angew. Chem. 126, 1642–1646 (2014).
Huang, P. et al. Lanthanide-doped LiLuF4 upconversion nanoprobes for the detection of disease biomarkers. Angew. Chem. Int. Ed. 53, 1252–1257 (2014).
Zhao, J. et al. Single-nanocrystal sensitivity achieved by enhanced upconversion luminescence. Nat. Nanotechnol. 8, 729–734 (2013).
Gargas, D. J. et al. Engineering bright sub-10-nm upconverting nanocrystals for single-molecule imaging. Nat. Nanotechnol. 9, 300–305 (2014).
Liu, Q. et al. F-18-labeled magnetic-upconversion nanophosphors via rare-earth cation-assisted ligand assembly. ACS Nano 5, 3146–3157 (2011).
Idris, N. M. et al. In vivo photodynamic therapy using upconversion nanoparticles as remote-controlled nanotransducers. Nat. Med. 18, 1580–1585 (2012).
Wang, C., Cheng, L. & Liu, Z. Upconversion nanoparticles for photodynamic therapy and other cancer therapeutics. Theranostics 3, 317–330 (2013).
Kang, X. J. et al. Lanthanide-doped hollow nanomaterials as theranostic agents. Wiley Interdiscip. Rev. Nanomed. Nanobiotechnol. 6, 80–101 (2014).
Mai, H. X., Zhang, Y. W., Sun, L. D. & Yan, C. H. Highly efficient multicolor up-conversion emissions and their mechanisms of monodisperse NaYF4: Yb,Er core and core/shell-structured nanocrystals. J. Phys. Chem. C 111, 13721–13729 (2007).
Shen, J. et al. Tunable near infrared to ultraviolet upconversion luminescence enhancement in (alpha-NaYF4:Yb,Tm)/CaF2 core/shell nanoparticles for in situ real-time recorded biocompatible photoactivation. Small 9, 3213–3217 (2013).
Wen, H. et al. Upconverting near-infrared light through energy management in core-shell-shell nanoparticles. Angew. Chem. Int. Ed. 52, 13419–13423 (2013).
Johnson, N. J. & van Veggel, F. C. Lanthanide-based hetero-epitaxial core-shell nanostructures: the compressive vs. tensile strain asymmetry. ACS Nano 8, 10517–10527 (2014).
Zhang, C. & Lee, J. Y. Prevalence of anisotropic shell growth in rare earth core-shell upconversion nanocrystals. ACS Nano 7, 4393–4402 (2013).
Johnson, N. J. J. & van Veggel, F. C. J. M. Sodium lanthanide fluoride core-shell nanocrystals: a general perspective on epitaxial shell growth. Nano Res. 6, 547–561 (2013).
Xia, Y., Xiong, Y., Lim, B. & Skrabalak, S. E. Shape-controlled synthesis of metal nanocrystals: simple chemistry meets complex physics? Angew. Chem. Int. Ed. 48, 60–103 (2009).
Zhuang, Z., Peng, Q. & Li, Y. Controlled synthesis of semiconductor nanostructures in the liquid phase. Chem. Soc. Rev. 40, 5492–5513 (2011).
Wang, F., Deng, R. R. & Liu, X. G. Preparation of core-shell NaGdF4 nanoparticles doped with luminescent lanthanide ions to be used as upconversion-based probes. Nat. Protoc. 9, 1634–1644 (2014).
Zherebetskyy, D. et al. Hydroxylation of the surface of PbS nanocrystals passivated with oleic acid. Science 344, 1380–1384 (2014).
Bealing, C. R., Baumgardner, W. J., Choi, J. J., Hanrath, T. & Hennig, R. G. Predicting nanocrystal shape through consideration of surface-ligand interactions. ACS Nano 6, 2118–2127 (2012).
Clark, S. J. et al. First principles methods using CASTEP. Z. Kristallogr. 220, 567–570 (2005).
Sui, Y. Q., Tao, K., Tian, Q. & Sun, K. Interaction between Y3+ and oleate ions for the cubic-to-hexagonal phase transformation of NaYF4 nanocrystais. J. Phys. Chem. C 116, 1732–1739 (2012).
Yi, G. et al. Synthesis, characterization, and biological application of size-controlled nanocrystalline NaYF4: Yb, Er infrared-to-visible up-conversion phosphors. Nano Lett. 4, 2191–2196 (2004).
Xia, A. et al. Gd3+ complex-modified NaLuF4-based upconversion nanophosphors for trimodality imaging of NIR-to-NIR upconversion luminescence, X-Ray computed tomography and magnetic resonance. Biomaterials 33, 5394–5405 (2012).
Hou, Y. et al. NaGdF4 nanoparticle-based molecular probes for magnetic resonance imaging of intraperitoneal tumor xenografts in vivo. ACS Nano 7, 330–338 (2012).
Acknowledgements
We thank D. Birch in Microscope Unit at Macquarie University and D.R.G. Mitchell in Electron Microscopy Centre at the University of Wollongong for their help and valuable discussion on transmission electron microscope characterizations. This project is primarily supported by the Australian Research Council (ARC) Future Fellowship Scheme (FT 130100517; D.J.), ARC Centre of Excellence Scheme through Centre for Nanoscale BioPhotonics, Macquarie University Research Fellowship Scheme (X.X.), ARC LIEF grant (LE120100104, Y.D.), ARC Discovery Project (DP140102581, Y.D.), China Scholarship Council CSC scholarships (no.201206170136, D.L., C.M.) and the Agency for Science, Technology and Research (A*STAR; grant no. 1231AFG028, X.L.).
Author information
Authors and Affiliations
Contributions
D.J. and X.L. conceived the project and supervised the research; X.X., D.L., D.J. and X.L. designed the experiments; D.L., C.M., Y.Z. and S.W. conducted synthesis; X.Q. and X.X. conducted crystallography analysis and computational modelling; D.L., Y.D., S.D., W.R. and X.X. conducted characterizations and analysis; D.L., X.X., X.Q. and Y.Z. prepared figures and supplementary information sections; D.J., D.L., X.X., E.M.G., X.Qin. and X. Liu wrote the manuscript. All authors contributed to data analysis, discussions and manuscript preparation.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-35, Supplementary Tables 1-3, Supplementary Notes 1-18, Supplementary Methods and Supplementary References (PDF 5603 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Liu, D., Xu, X., Du, Y. et al. Three-dimensional controlled growth of monodisperse sub-50 nm heterogeneous nanocrystals. Nat Commun 7, 10254 (2016). https://doi.org/10.1038/ncomms10254
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms10254
- Springer Nature Limited
This article is cited by
-
Co-catalytic metal–support interactions in single-atom electrocatalysts
Nature Reviews Materials (2024)
-
Lanthanide-based microlasers: Synthesis, structures, and biomedical applications
Nano Research (2024)
-
Assessing the reproducibility and up-scaling of the synthesis of Er,Yb-doped NaYF4-based upconverting nanoparticles and control of size, morphology, and optical properties
Scientific Reports (2023)
-
Next generation lanthanide doped nanoscintillators and photon converters
eLight (2022)
-
NaBiF4-based hollow upconversion nanoparticles for temperature sensing
Light: Science & Applications (2022)