Abstract
The interest in mechanical properties of two-dimensional materials has emerged in light of new device concepts taking advantage of flexing, adhesion and friction. Here we demonstrate an effective method to measure adhesion of graphene atop highly ordered pyrolytic graphite, utilizing atomic-scale ‘blisters’ created in the top layer by neon atom intercalates. Detailed analysis of scanning tunnelling microscopy images is used to reconstruct atomic positions and the strain map within the deformed graphene layer, and demonstrate the tip-induced subsurface translation of neon atoms. We invoke an analytical model, originally devised for graphene macroscopic deformations, to determine the graphite adhesion energy of 0.221±0.011 J m−2. This value is in excellent agreement with reported macroscopic values and our atomistic simulations. This implies mechanical properties of graphene scale down to a few-nanometre length. The simplicity of our method provides a unique opportunity to investigate the local variability of nanomechanical properties in layered materials.
Similar content being viewed by others
Introduction
Adhesion is a key parameter in fabrication of next generation nanoscale mechanical resonators based on two-dimensional (2D) materials1,2, and a rapidly growing family of 2D heterostructures3,4,5,6,7,8. Various methods to measure the adhesion energy have been tested and reported previously9,10,11,12. However, nanoscale measurements of these properties are generally very challenging due to the weak interlayer bonding in layered materials13. Even for graphite, a direct measurement of interlayer adhesion energy is still limited13,14, despite many theoretical predictions15,16,17. Only recently, an adhesion energy of 0.227 J m−2 was determined from direct measurements of mesoscopic graphene contacts, using the shearing of the individual graphitic mesa structures13. Several studies reported the utilization of graphene micron-sized blisters or bubbles created by intercalated nanoparticles at the hetero-interface between graphene and the SiO2 substrate18, or by inflation of pre-made microcavities on the SiO2 substrate to form graphene bubbles9. Nevertheless, all such blisters are of relatively large scale, and may not be readily compatible with van der Waals heterostructures.
Here we demonstrate that the ‘blister’ method can be scaled down to 1–2 nm by using atomic-scale intercalation. We intercalate neon atoms into graphite, which in turn deform enclosing graphene sheets to create atomic-scale blisters on the surface. Detailed experimental analysis of these atomic blisters leads to a direct estimate of adhesion energy of ∼0.221 J m−2 between the first-layer graphene and graphite bulk, which is closely comparable with the recent direct measurement of adhesion energy between mesoscopic graphite contacts13. At the same time we measure the strain within the blister area by direct topographic analysis, and we prove the feasibility to displace buried intercalates. Our experimental results for adhesion energy, the local topographic characteristics of the blisters as well as the low diffusion barrier of intercalates are strongly supported by density functional theory (DFT) calculations.
Results
STM characterization for atomic blisters
Representative scanning tunnelling microscopy (STM) images of graphene blisters on highly ordered pyrolytic graphite (HOPG) are shown in Fig. 1a,b. The blister in Fig. 1b has a nearly Gaussian shape with the height h of ∼0.14 nm and full-width at half-maximum of ∼0.93 nm, respectively (Fig. 1d). For reference, the atomic radius of a neon atom is ∼38 pm, while that of carbon is ∼67 pm (ref. 19). The van der Waals radius is similar for both atoms (neon ∼154 pm and carbon ∼170 pm)20. Taking into consideration the approximate lateral size of the blister of ∼1.9 nm (at the base in Fig. 1d), we estimate that only a couple of neon atoms are intercalated in the blister, while the strain in the top graphene sheet is delocalized over ∼60 atoms around the neon intercalates. Besides the atomic blisters, other defects are observed such as holes created by ion bombardment, as shown in the STM image of Fig. 1a (enclosed by squares). These point defects are due to missing carbon atoms. For the purpose of this article, we only focus on the blisters of the chemically undisrupted top graphene sheet. Since we are working with a grounded sample, and both graphite and graphene are electronically conducting materials, Ne impurity is charge neutral. Neutralization of the low energy Ne+ is well-known for metal surfaces with work functions in the range from 3–5.5 eV (refs 21, 22). Our DFT calculations further confirm that there is a minimal (<0.05 e) charge transfer between the intercalated Ne atoms and surrounding carbon atoms of the graphite, further asserting that we can treat Ne intercalates as essentially neutral atoms.
Lattice strain caused by the intercalate
To map out atomic positions and their local neighbourhoods, we employed image processing as illustrated in Fig. 1e,f. Figure 1e indicates the x–y–z coordinate map of atom centres extracted from Fig. 1b. Each dot represents the carbon atoms observed by STM (every other carbon atom on HOPG), and the blister region can be clearly identified by the height difference (in Fig. 1e). Furthermore, we estimated the tensile strain in the blister by mapping out the expansion of the C..C distance, as seen in Fig. 1f. The colour of each point here represents the percentage of expansion of C..C distance (between every other carbon atoms on HOPG) in the blister region compared with the one in the undistorted graphene region. The C..C distances are expanded from ∼1% up to a remarkable ∼25% compared with the undistorted graphene, with an average increase of ∼6%. Several methods can be used to estimate the strain. For example, by using the model for the mechanics of graphene bubbles developed by Yue et al.10 (equations (18) and (19) in ref. 10), we obtain the maximum strain for both radial and circumferential strains of ∼3% at the central deflection of the blister as illustrated in Fig. 1b. Alternatively, based on the definition of Georgiou et al.23 in which the strain is determined as the percentage increase between the length of the arc and the width of the bubble, and in combination with the line-profile indicated in Fig. 1d and the strain map from Fig. 1f, we estimate a strain of ∼1–3% for the blister in Fig. 1b. Overall, this analysis confirms that in the blister structure, the top layer of graphene is stretched to accommodate subsurface intercalated atoms.
Analytical models
Several models have been used before by Yue et al.10 to analyse the adhesion energy between graphite layers: the membrane model, the nonlinear plate model and the linear plate model. The membrane model is applicable for large graphene bubbles (h>10 nm). The nonlinear plate model is generally more accurate and suitable for all sized bubbles. Within this model, the adhesion energy (Γ) of the graphene blister having a characteristic radius a and a height h, (Fig. 1d) is obtained from the equation10:
Here E2D is the 2D Young’s modulus of graphene; D is the bending stiffness, which for macroscopic graphene is D=0.238 nN nm (or equivalently 1.5 eV)10,24; while μ represents a function of the Poisson ratio ν:
The linear plate model is an approximation of the nonlinear plate model for small sized bubbles generally having h<0.3 nm and h<<a. In such cases the first term in equation (1) can be ignored and the adhesion energy is expressed as
which is simply a function of the blister’s height h and radius a. Although this linear plate model was derived for a small blister, it’s validity for atomic scale is not clear a priori. In this study, we test this model extension by using the simplified version of the linear plate model given in equation (3) to determine the adhesion energy of graphene to graphite. For this purpose, to quantitatively identify the height h and the radius a of the atomic blister, we fit the STM line-profile with a Gaussian function:
as indicated by the red curve in Fig. 1d.
Measurements of adhesion energy
We measured a number of line profiles over the blister by repeated rotation of the one-dimensional cross-section (such as the lines A–C in Fig. 1d inset), fitted them by a Gaussian function (4) to find the radius a and the height h, and obtained the adhesion energy via equation (3). Figure 2 (data sets in red) shows the calculated adhesion energies with respect to different measurements. The mean of the adhesion energy obtained is 0.221±0.011 J m−2 (Fig. 2). Our result is very close to the recently reported graphite adhesion energy of 0.227 J m−2 (ref. 13). Regarding the errors, the adhesion energy is proportional to h2/a4, while a Gaussian shape did not always represent the blister profile. Therefore, even picometre-scale variation of a and h cause a relatively wide scatter of the adhesion energy. Nevertheless, our method provides a simple route to measure the adhesion energy and our results are closely matching other reported values13,14,25,26. Our study also demonstrates that the linear plate model developed by Yue et al.10 can provide estimation for the adhesion energy even for atomic scaled blisters. At these scales, the models can be compared directly to results from first principles or molecular dynamics simulations15,16,17,27,28,29.
Pressure inside the blister
Another physical property of interest is the pressure on the top-layer graphene exerted by the buried Ne atoms. This quantity was calculated using the corresponding expressions from the nonlinear plate model10,
where p is the pressure in Pascal (Pa) unit, E2D is the 2D Young’s modulus of graphene, D is the bending stiffness, a and h are radius and height of the blister; while μ represents the function of the Poisson ratio ν given in equation (2). For E2D=0.323 TPa nm and ν=0.179, we estimate a pressure of 5.4 GPa within the nonlinear plate model (an estimate for the membrane model is 6.3 GPa). For reference, the pressure of the macroscopic blisters determined in the work of Yue et al.10 was a thousand-fold smaller ranging between 1 and 2 MPa. A high value of the pressure in our experiments reflects the incompressibility of the individual Ne atoms.
Density functional theory verification
Our approach is further validated by atomistic modelling using DFT calculations. Figure 3a presents the results of simulations and illustrates top and side views of a system of four neon atoms intercalated into a graphene bilayer. A corresponding simulated STM image (Fig. 3b) bears close resemblance to experiment. We have simulated 1–4 intercalated Ne atoms and then used a 2D-Gaussian function to fit the distribution of atomic coordinates. The variation in the height of the blister with the number of neon atoms incorporated in the graphene bilayer is plotted in Fig. 3c. The results are within the range of STM measured values (see Fig. 1d). Figure 3d shows the dependence of the adhesion energy on the number of neon atoms. The squares are from DFT calculations, while circles represent the results from the linear plate model applied to the calculated structures. These values are well within the range of the ones derived from experiments and can be extrapolated to zero intercalates leading to a value for adhesion energy of ∼0.235 J m−2. Notably the adhesion energy does decrease with the increase in the number of intercalated Ne atoms. These results suggest that the local adhesion of graphene layers can be substantially influenced by an increase in the number of intercalated neon atoms, particularly if they are localized in the same region. It is also expected that further increase in concentration of intercalated neon atoms can induce local exfoliation of the top graphene layer.
Manipulation of blisters
Our experiments further indicate the feasibility of tip-induced manipulation of subsurface Ne atoms. Figure 4a,b demonstrate the effect of several STM scans at decreased tip–surface distance (tip–surface distance was reduced by decreasing the bias down to 10 mV, while increasing the tunnelling current up to 3 nA). The blister highlighted by a circle in Fig. 4a has been moved out of the current image frame as seen in Fig. 4b. We calculated the minimum energy diffusion pathway of a single Ne atom in the gap of the graphene bilayer between neighbour energy minima using the nudged elastic band method. As seen from Fig. 4c, a relative modest barrier of only 0.14 eV is encountered by the diffusing Ne atom in the gap that strongly supports the feasibility of manipulating subsurface intercalates.
Smaller height blister versus deeper layer intercalation
One may question the applicability of STM to measure topographic height. In fact, it is well-known that the atomic corrugation of graphite in STM images depends on the tip conditions30,31,32,33,34,35,36,37. In earlier studies32,33,34, even giant atomic corrugations of graphite (1–7 Å, or even larger up to 24 Å) have been reported in STM images, which were often related to tip-induced elastic deformations or to other experimental limitations such as contaminations at ambient conditions32,33,34. Tersoff et al.37 demonstrated theoretically that the atomic corrugation of graphite in STM images is close to 0.3 Å or less, which is similar to the corrugation (∼0.35 Å) obtained in our case as illustrated in Fig. 1b. In combination with our theoretical calculations of the blister height in Fig. 3c, we believe that ∼0.3 Å represents an accurate value of the graphite atomic corrugation and therefore the profile measurement in Fig. 1b represents accurately the blister’s height.
In a few cases (see Fig. 1c and the corresponding line profile in Supplementary Fig. 2) the measured graphite atomic corrugation was smaller, ∼0.1 Å. In such a case the blister, likewise, has a smaller height of ∼0.03 nm. A proper scale (with a factor of 3.5) was applied to the z-height in this case to make the atomic corrugation in Fig. 1c close to the one in Fig. 1b. Upon applying the linear plate model to the rescaled blister profile, a mean adhesion energy of ∼0.19 J m−2 was obtained out of 32 total measurements of the rescaled blister (data sets in blue in Fig. 2).
On the other hand, the smaller height of the blister may be due to Ne atoms intercalated into the deeper layers. Although we believe that this is not the case for the blister in Fig. 1c (see Supplementary Note 1), deeper layer intercalation is possible judging by the stability of the final state. We carried out DFT calculations of deep intercalates and determined a substantial reduction of the blister height when intercalating beyond the first layer (see Supplementary Note 2 and Supplementary Figs 3, 4 and 6). Experimentally we do detect occasional small protrusions after Ne+ sputtering, which may correspond to such deep intercalates (see Supplementary Fig. 1 and Supplementary Note 2). However, direct estimates of the adhesion energy as described above should be applied only to the case when the Ne atoms are located immediately underneath the surface (see Supplementary Fig. 5).
Nc-AFM characterization for atomic blisters
An alternative, more direct method for the measurement of the blister topography can be obtained using non-contact atomic force microscopy (nc-AFM). Nc-AFM detects short-range forces, and the nc-AFM image provides direction information about the corresponding tip–surface interaction38. The atomically resolved nc-AFM image (Fig. 5b) shows protruding blisters that compare favourably to those observed in STM over the same blister. Line profiles comparison (Fig. 5c) does indicate small height variations between STM (Fig. 5a) and nc-AFM (Fig. 5b) measurements. (STM measured height of ∼0.16 nm versus nc-AFM measured height of ∼0.10 nm). However, the overall shape of the blister is consistent in both measurements, convincingly indicating that the topographic lattice deformations are induced by the Ne atom intercalate.
In conclusion, we demonstrate a direct method to measure the adhesion energy of graphene on graphite, by intercalating inert gas atoms between graphene sheets. Measurements are based on the shape and heights of the graphene blisters at the atomic scale and analysed using analytical methods (linear plate models) and DFT calculations. Our results are in good agreement with recently reported direct measurements of adhesion energy for graphite. Local topographic analysis also provides detailed atomic information related to the graphene blisters, such as local strain and the mobility of subsurface noble gas atoms. We envision that this methodology can be applied to other layered materials to estimate the adhesion energy and the related elastic mechanical properties at atomic level. Moreover, intercalation of noble gas atoms may provide a feasible pathway to create electronically interesting ‘Gaussian’ impurities39,40.
Methods
Experiments
An HOPG sample (Grade SPI-1) was purchased from SPI Supplies. The experiments were conducted by using the SPECS Joule-Thomson (JT) cryogenic STM/AFM in an ultrahigh vacuum chamber with a base pressure ≤1 × 10−10 mbar. The nc-AFM measurements were carried out in the same system with a SPECS Kolibri sensor. HOPG was freshly cleaved by the scotch tape method and quickly transferred into ultrahigh vacuum. The HOPG was subsequently annealed up to 500 °C for ∼20 min. The blisters and associated defects on HOPG were created by briefly sputtering the sample with Ne+ ions (0.11 kV, 5.5 × 10−8 mbar, for ∼20 s). These sputtering conditions are necessary for the reproducibility of atomic sized blisters. Lighter neon was chosen over argon to minimize creation of point defects by sputtering. STM images were taken after cooling the sample to both liquid nitrogen (77 K) and liquid helium (4.3 K) temperatures. The STM profile measurements over different blisters taken at 77 and 4.3 K yield consistent results, suggesting in this temperature range adhesion energy shows little change, as may be expected (see Supplementary Note 3). Atomic-scale analysis was performed using a methodology described earlier41,42. Atomic (x, y) positions were determined with subpixel precision using a combination of image processing and fitting routines. After the atomic positions were established, a survey of the six nearest neighbours was conducted to obtain the data in Fig. 1f.
Theory
The adsorption properties of Ne atoms in the gap between two parallel graphene layers were investigated based on DFT calculations using Vienna ab initio simulation package (VASP)43,44 in conjunction with periodic slab models. The computations used the Perdew-Burke-Ernzerhof (PBE)45 exchange correlation functional and the projector-augmented wave method of Blöchl46,47. The standard PBE functional was corrected to include long-range dispersion interactions using the Tkatchenko and Scheffler (TS) method48. A cutoff energy of 500 eV was used for the plane-wave basis set. The slab model used in calculations consists of a 12 × 12 graphene bilayer separated in the vertical direction by a vacuum width of 16 Å. After the initial optimization of the bare graphene bilayer the bottom layer was kept fixed in subsequent Ne adsorption calculations while the top layer was fully relaxed. Additional information about the energetics of single Ne atom diffusion in the gap of graphene has been calculated using the climbing image-nudged elastic band method49,50. For selective adsorption configurations the corresponding STM images were calculated using the Tersoff–Hamman approach with an energetic interval around the Fermi level similar to the one used experimentally51. The sampling of Brillouin zone was performed using a single Γ-point in the case structural optimizations while a Monkhorst-Pack scheme52 with a grid mesh of 0.005 Å−1 k-point separation was used for STM image calculations.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
Additional information
How to cite this article: Wang, J. et al. Atomic intercalation to measure adhesion of graphene on graphite. Nat. Commun. 7, 13263 doi: 10.1038/ncomms13263 (2016).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Bunch, J. S. et al. Electromechanical resonators from graphene sheets. Science 315, 490–493 (2007).
Bunch, J. S. et al. Impermeable Atomic membranes from graphene sheets. Nano Lett. 8, 2458–2462 (2008).
Lee, C., Wei, X., Kysar, J. W. & Hone, J. Measurement of the elastic properties and intrinsic strength of monolayer graphene. Science 321, 385–388 (2008).
Lee, C. et al. Frictional characteristics of atomically thin sheets. Science 328, 76–80 (2010).
Bunch, J. S. & Dunn, M. L. Adhesion mechanics of graphene membranes. Solid State Commun. 152, 1359–1364 (2012).
Boddeti, N. G. et al. Mechanics of adhered, pressurized graphene blisters. J. Appl. Mech. 80, 040909 (2013).
Boddeti, N. G. et al. Graphene blisters with switchable shapes controlled by pressure and adhesion. Nano Lett. 13, 6216–6221 (2013).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Koenig, S. P., Boddeti, N. G., Dunn, M. L. & Bunch, J. S. Ultrastrong adhesion of graphene membranes. Nat. Nano 6, 543–546 (2011).
Yue, K., Gao, W., Huang, R. & Liechti, K. M. Analytical methods for the mechanics of graphene bubbles. J. Appl. Phys. 112, 083512 (2012).
Yoon, T. et al. Direct measurement of adhesion energy of monolayer graphene as-grown on copper and its application to renewable transfer process. Nano Lett. 12, 1448–1452 (2012).
Jiang, T. & Zhu, Y. Measuring graphene adhesion using atomic force microscopy with a microsphere tip. Nanoscale 7, 10760–10766 (2015).
Koren, E., Lörtscher, E., Rawlings, C., Knoll, A. W. & Duerig, U. Adhesion and friction in mesoscopic graphite contacts. Science 348, 679–683 (2015).
Benedict, L. X. et al. Microscopic determination of the interlayer binding energy in graphite. Chem. Phys. Lett. 286, 490–496 (1998).
Kolmogorov, A. N. & Crespi, V. H. Registry-dependent interlayer potential for graphitic systems. Phys. Rev. B 71, 235415 (2005).
Spanu, L., Sorella, S. & Galli, G. Nature and strength of interlayer binding in graphite. Phys. Rev. Lett. 103, 196401 (2009).
Lebègue, S. et al. Cohesive properties and asymptotics of the dispersion interaction in graphite by the random phase approximation. Phys. Rev. Lett. 105, 196401 (2010).
Zong, Z., Chen, C.-L., Dokmeci, M. R. & Wan, K. Direct measurement of graphene adhesion on silicon surface by intercalation of nanoparticles. J. Appl. Phys. 107, 026104 (2010).
Clementi, E., Raimondi, D. L. & Reinhardt, W. P. Atomic screening constants from SCF functions. II. Atoms with 37 to 86 electrons. J. Chem. Phys. 47, 1300–1307 (1967).
Mantina, M., Chamberlin, A. C., Valero, R., Cramer, C. J. & Truhlar, D. G. Consistent van der Waals radii for the whole main group. J. Phys. Chem. A 113, 5806–5812 (2009).
Kutana, A., Gordon, M. J. & Giapis, K. P. Neutralization of hyperthermal Ne+ on metal surfaces. Nucl. Instrum. Methods Phys. Res. Sect. B Beam Interact. Mater. Atoms 248, 16–20 (2006).
Tolstogouzov, A., Daolio, S., Pagura, C. & Greenwood, C. L. Neutralization of low-energy Ne+ ions scattered from metal surfaces: study by mass-resolved ion-scattering spectrometry. Surf. Sci. 466, 127–136 (2000).
Georgiou, T. et al. Graphene bubbles with controllable curvature. Appl. Phys. Lett. 99, 093103 (2011).
Kudin, K. N., Scuseria, G. E. & Yakobson, B. I. C2F, BN, and C nanoshell elasticity from ab initio computations. Phys. Rev. B 64, 235406 (2001).
Liu, Z. et al. Interlayer binding energy of graphite: a mesoscopic determination from deformation. Phys. Rev. B 85, 205418 (2012).
Zacharia, R., Ulbricht, H. & Hertel, T. Interlayer cohesive energy of graphite from thermal desorption of polyaromatic hydrocarbons. Phys. Rev. B 69, 155406 (2004).
Rydberg, H. et al. Van der Waals density functional for layered structures. Phys. Rev. Lett. 91, 126402 (2003).
Sun, X.-Y., Wu, R., Xia, R. & Xu, Y.-J. Blister formation in graphene coating on the nanoparticle decorated copper surface. RSC Adv. 4, 46646–46652 (2014).
Herbig, C. et al. Xe irradiation of graphene on Ir(111): from trapping to blistering. Phys. Rev. B 92, 085429 (2015).
Binnig, G. et al. Energy-dependent state-density corrugation of a graphite surface as seen by scanning tunneling microscopy. EPL Europhys. Lett. 1, 31 (1986).
Tománek, D. & Louie, S. G. First-principles calculation of highly asymmetric structure in scanning-tunneling-microscopy images of graphite. Phys. Rev. B 37, 8327–8336 (1988).
Mamin, H. J., Ganz, E., Abraham, D. W., Thomson, R. E. & Clarke, J. Contamination-mediated deformation of graphite by the scanning tunneling microscope. Phys. Rev. B 34, 9015–9018 (1986).
Soler, J. M., Baro, A. M., García, N. & Rohrer, H. Interatomic forces in scanning tunneling microscopy: giant corrugations of the graphite surface. Phys. Rev. Lett. 57, 444–447 (1986).
Pethica, J. B. Comment on ‘interatomic forces in scanning tunneling microscopy: giant corrugations of the graphite surface’. Phys. Rev. Lett. 57, 3235–3235 (1986).
Batra, I. P. et al. A study of graphite surface with STM and electronic structure calculations. Surf. Sci. 181, 126–138 (1987).
Tersoff, J. Role of tip electronic structure in scanning tunneling microscope images. Phys. Rev. B 41, 1235–1238 (1990).
Tersoff, J. & Lang, N. D. Tip-dependent corrugation of graphite in scanning tunneling microscopy. Phys. Rev. Lett. 65, 1132–1135 (1990).
Torbrügge, S., Schaff, O. & Rychen, J. Application of the KolibriSensor® to combined atomic-resolution scanning tunneling microscopy and noncontact atomic-force microscopy imaging. J. Vac. Sci. Technol. B 28, C4E12–C4E20 (2010).
Carrillo-Bastos, R., Faria, D., Latgé, A., Mireles, F. & Sandler, N. Gaussian deformations in graphene ribbons: flowers and confinement. Phys. Rev. B 90, 041411 (2014).
Schneider, M., Faria, D., Viola Kusminskiy, S. & Sandler, N. Local sublattice symmetry breaking for graphene with a centrosymmetric deformation. Phys. Rev. B 91, 161407 (2015).
Belianinov, A. et al. Identification of phases, symmetries, and defects through local crystallography. Nat. Commun. 6, 7801 (2015).
Belianinov, A. et al. Big data and deep data in scanning and electron microscopies: deriving functionality from multidimensional data sets. Adv. Struct. Chem. Imaging 1, 1–25 (2015).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Tkatchenko, A. & Scheffler, M. Accurate molecular van der Waals interactions from ground-state electron density and free-atom reference data. Phys. Rev. Lett. 102, 073005 (2009).
Jónsson, H., Mills, G. & Jacobsen, K. W. in Classical and Quantum Dynamics in Condensed Phase Simulations (eds Berne, B.J., Ciccotti, G., Coker, D.F.) Ch. 16 (World Scientific (1998).
Henkelman, G., Uberuaga, B. P. & Jónsson, H. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).
Tersoff, J. & Hamann, D. R. Theory and application for the scanning tunneling microscope. Phys. Rev. Lett. 50, 1998–2001 (1983).
Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Acknowledgements
Experiments were conducted at the Center for Nanophase Materials Sciences (CNMS), which is a DOE Office of Science User Facility. Image analysis was carried out in collaboration with the Institute for Functional Imaging of Materials at the Oak Ridge National Laboratory. Computations were conducted at National Energy Technology Laboratory on Joule supercomputer system.
Author information
Authors and Affiliations
Contributions
J.W., A.P.B. and P.M. designed the research. J.W., S.J. and P.M. conducted the experiments. A.B. and S.V.K. provided guidance in the data analysis. J.W. and P.M. performed the data analysis. D.C.S. conducted the DFT calculations. J.W. and P.M. wrote the paper with inputs and corrections from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-6, Supplementary Notes 1-3 and Supplementary References. (PDF 1123 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wang, J., Sorescu, D., Jeon, S. et al. Atomic intercalation to measure adhesion of graphene on graphite. Nat Commun 7, 13263 (2016). https://doi.org/10.1038/ncomms13263
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms13263
- Springer Nature Limited
This article is cited by
-
Mechanics of 2D material bubbles
Nano Research (2023)