Abstract
Silicate glasses have evolved from basic structural materials to enabling materials for advanced applications. In this article, we unravel the origin of the mixed alkali effect for alkali silicate 22.7R2O–77.3SiO2 glasses (R = Na and/or K) by identifying the variation in the alkali ion location around the non-bridging oxygen atoms. To do so, we constructed a state-of-the art structural model, which reproduces both diffraction and NMR data with a particular focus on the behavior of the alkali ions. A novel topological analysis using persistent homology found that sodium-potassium silicate glass shows a significant reduction in large cavities as a result of the mixed alkali effect. Furthermore, a highly correlated pair arrangement between sodium and potassium ions around non-bridging oxygen atoms was identified. The potassium ions can be trapped in K–O polyhedra due to the increased bridging oxygen coordination; therefore, the correlated pair arrangement is likely the intrinsic origin of the mixed alkali effect.
Similar content being viewed by others
Introduction
Silicate glasses are one of the oldest materials in history and are commonly used in the modern glass industry. They have varying physicochemical properties, such as melting point, glass transition temperature, viscoelasticity, thermal expansion and chemical durability with the addition of the other network forming cations, such as boron and aluminum ions, and the network modifiers, namely, alkali metal or alkali earth metal ions. They are typically manufactured as window glasses for buildings and automobiles and display glasses for TV panels and mobile phones.
It is well known that a short-range structural unit in silica (SiO2) and silicate glasses is a SiO4 tetrahedron. Unlike the structure of crystalline materials such as quartz or cristobalite, silica glass does not have long-range periodicity, and the structure can be described as a network of corner-sharing and randomly connected SiO4 tetrahedra via bridging oxygen on the basis of Zachariasen’s random network theory1. On the other hand, the formation of an intermediate-range order in disordered materials, including silica glass, is indicated by the first sharp diffraction peak (FSDP) in neutron diffraction (ND) and X-ray diffraction (XRD) patterns2,3,4. The FSDP of silica glass has been extensively investigated by ND/XRD and molecular dynamics (MD) simulations5,6,7, and it has been found that the three-dimensional network possesses a periodicity ( = 2π/QFSDP) of ~4 Å and correlation length ( = 2π/ΔQFSDP) of ~10 Å, which is associated with the formation of large cavities.
It is possible to infer that the introduction of alkali ions into SiO2 glass causes partial cleavage of the tetrahedron network, and thus, the numbers of non-bridging oxygen (NBO) and silicon with Qn (n < 4) (where n is the number of bridging oxygen atoms in a SiO4 tetrahedron)8 increase by breaking the silicon–oxygen bonds. Consequently, the cavity volume decreases since the alkali ions occupy the cavity site. Contrary to a simple structural change, interpretation of the FSDP in binary alkali silicate glasses is rather complicated. This is because the FSDP mainly consists of at least six partial correlations in binary alkali silicate glasses, and hence, the aid of computer simulation is helpful. Previous MD simulation studies9,10 have suggested that the ring structure formed by SiO4 tetrahedra is affected by alkali ions, resulting in broadening of the ring size distribution. Although theoretical simulations claim that the FSDP position and width are modified by alkali ions10, they fail to reproduce the FSDP shape experimentally observed by neutron diffraction11,12. In particular, in the case of potassium silicate glass, the FSDP in the neutron diffraction data is not a simple peak11, and it is not easily reproduced by MD simulations.
The structure of multicomponent alkali silicate glasses under solid and melted conditions has also been extensively studied using various experimental techniques, such as NMR8,13,14 and Raman spectroscopy15,16, quasielastic neutron scattering17,18, and positron annihilation spectroscopy19. However, it is still difficult to fully understand the intermediate-range order in alkali silicate glasses solely using these experimental methods. To reveal the effect of alkali ions on the silicate network in the intermediate range, it is necessary to visualize a reliable atomistic model while maintaining consistency between the theoretical atomistic model and the experimental diffraction data.
In this work, we therefore try to unravel the atomistic structure of three kinds of 22.7R2O-77.3SiO2 glasses (R = Na and/or K) using reverse Monte Carlo (RMC) modeling in conjunction with ND and high-energy XRD (HEXRD). To reveal the mixed alkali effect, single Na (Na100 glass), single K (K100 glass) and an equal mixture of Na and K ions (Na50K50 glass) were investigated. Since both Na and K ions are abundant in the Earth’s crust and essential for modifying the physical and chemical properties of glass, it is worth investigating the intrinsic origin of the mixed alkali effect, which might arise from the difference in ionic radii. Indeed, it is well known that alkali mixing causes several unusual phenomena; that is, when an alkali ion is gradually replaced by another one, some physical properties vary in an extremely nonlinear trend. For instance, a composition containing equally mixed alkali ions has a pronounced maximum electrical resistivity and a substantially lower viscosity as a concave function of the alkali content, although the variation in the molar volume is almost linear with the alkali content20. These facts suggest that ionic migration is inhibited by the alkali mixing associated with the formation of NBO atoms in a modified network model of alkali silicate glasses proposed by Greaves21. A large number of studies investigating this phenomenon have been reported22,23,24, and schematic models involving NBO atoms for binary alkali oxide glasses have been proposed21,25,26. The details of the previous studies are reviewed by Habasaki et al.27 Nevertheless, the origin of the mixed alkali effect remains unclear because the previous simulation studies did not visualize the alkali ion coordination around the NBO atoms in the structural model to be consistent with the multiple experimental dataset, e.g., diffraction and NMR. Therefore, it is worthwhile to revisit the glass structure with a special focus on the alkali ion coordination around the NBO atoms towards reconciling the mixed alkali effect.
In this article, we measured X-ray and neutron-weighted structural factors of the aforementioned three alkali silicate glasses, whose dielectric constants show a clear mixed alkali effect (Fig. S1), using state-of-the art techniques. The diffraction data were utilized to reconstruct atomistic views of the glasses using a combination of RMC and MD simulations (RMC-MD) in conjunction with the NMR data8. For the RMC-MD simulation, proper constraints for the coordination numbers of silicon, bond angle distribution of O–Si–O, partial pair-distribution functions within the first coordination shell, and Qn distributions were adopted to avoid physically unreasonable configurations. The optimized atomistic models were investigated by a sophisticated topological analysis based on persistent homology to highlight the modification of the glass structure by alkali mixing, in addition to the ordinal ring size and cavity size distribution analyses. We especially focused on the behavior of the alkali ions around the NBO atoms, as well as that of the cavities in the glasses to tackle the intrinsic origin of the mixed alkali effect.
Materials and methods
Materials
Alkali silicate glasses were prepared from mixtures of reagent grade SiO2, Na2CO3, and K2CO3 powders. The mixtures were melted at 1923 K in air. Each melt was quenched and annealed at the glass transition temperature and then cooled slowly by 1 K/min. The nominal and analyzed compositions of the glasses are listed in Table S1. The alkali ion contents were determined by a Z-2310 atomic absorption spectrophotometer (Hitachi High-tech Science Corp.) in aqueous solutions of the decomposed glasses, and the densities were measured with the Archimedes method.
Diffraction measurements
The ND experiments were conducted on a high intensity total diffractometer, NOVA28, installed at BL21 of the Materials and Life Science Experimental Facility at the J-PARC spallation neutron source. Crushed glass samples were transferred into vanadium-nickel null alloy cells 6 mm in diameter. The wavelength range of the incident neutron beam was 0.12 Å < λ < 8.3 Å.
The observed scattering intensities for the samples were corrected for instrumental background, absorption of the samples and cell, and multiple and incoherent scattering and then normalized by the incident beam profile.
The HEXRD experiments were performed on a two-axis diffractometer, which is dedicated for disordered materials, at the BL04B2 beamline of the SPring-8 synchrotron radiation facility29. Crushed glass samples were transferred into SiO2 glass capillaries. The wavelength of the incident X-ray was 0.2011 Å. The raw data were corrected for polarization, absorption and background, and the contribution of Compton scattering was subtracted using standard data analysis software29.
The fully corrected data were normalized to give a Faber-Ziman30 total structure factor S(Q). Total correlation functions, T(r), were obtained by a Fourier transform with a Lorch function31.
Modeling
The RMC modeling of the Na100, Na50K50, and K100 glasses was performed using the RMC++ code32. The atomic number densities assumed were 0.0728 Å-3, 0.0687 Å-3, and 0.0642 Å-3 for the Na100, Na50K50, and K100 glasses, respectively. The starting configurations, which contain 3300 particles for the three glasses, were created using hard-sphere Monte Carlo (HSMC) simulations with constraints to avoid physically unrealistic structures. The r-spacing for the calculations of partial pair-distribution functions was set to 0.05 Å. Two kinds of constraints were applied: the closest atom–atom approach and the Si–O connectivity. The first one can avoid unreasonable spikes in the partial pair-distribution functions. The second forces silicon atoms to coordinate to four oxygen atoms within a cutoff distance of 1.90 Å. In addition, the fixed neighbor constraints33 were applied for the Si–O correlation at 1.45–1.90 Å to reproduce the Q0:Q1:Q2:Q3:Q4 ratio obtained by the NMR study8. According to the NMR measurements, the Q0:Q1:Q2:Q3:Q4 ratio is 0:0:1.5:55.8:42.7, 0:0:1.2:56.5:42.4, and 0:0:0.8:57.2:42.0 for the Na100, Na50K50 and K100 glasses, respectively. The ratios obtained by the RMC-MD modeling were 0:0:2.2:54.4:43.4, 0:0:2.5:54.7:42.8, and 0:0:3.2:53.2:43.6 for the Na100, Na50K50 and K100 glasses, respectively. After the HSMC simulations, the RMC simulations were conducted to reproduce the X-ray S(Q) and neutron S(Q) data. Following the RMC simulations, the atomic configurations were optimized by the MD simulations.
The MD simulations were performed using the LAMMPS package34 with the Morse-type interatomic potential developed by Pedone et al.35. For the alkali silicate glasses, the structures obtained by the RMC simulations were optimized by minimizing the energy using the conjugate gradient method. During the optimization, the volume was kept constant. In the case of silica glass, a random configuration composed of 3000 atoms was prepared with respect to the experimental density, and then, an equilibrium configuration was constructed using the melt quenching method. That is, following the melting simulation at 3500 K for 500 ps, the model was cooled down to 300 K with a quenching rate of 1 K/ps. Eventually, the system was equilibrated at 300 K for 300 ps. The equation of motion was integrated with a 1 fs time step with the canonical ensemble (NVT). A Nosé–Hoover thermostat36 was employed to control temperature.
After the MD simulations, all configurations were refined by additional RMC simulations while constraining the coordination number of silicon, the bond angle distribution for O–Si–O, and the partial pair-distribution functions within the first coordination shell to avoid formation of an unfavorable disordered structure.
Topological analyses
The primitive (Si–O)n ring size distributions for the alkali silicate glass were calculated using the R.I.N.G.S. code37. The surface cavity analysis was performed employing the pyMolDyn code38 with a cut off distance rc = 2.5 Å. The persistent homology analyses were performed using the HomCloud package39. Given a set of points in space, persistent homology captures the topological multiscale structures, and those identified are compactly expressed in a persistence diagram. The construction of the persistence diagram follows the process schematically described in Fig. 1a. We first replace each point with a sphere and increase the radius from zero to a sufficiently large value, which corresponds to the changing resolution of our input x, y, and z coordinates of atoms. Then, we record the pair of radii (b, d) at which a ring in a specific location appears (birth) and disappears (death). The persistence diagram is a histogram of the birth-death plane counting of rings at the coordinate (b, d). The diagram enables one not only to count the number of rings but also to characterize those shapes at multiscales. Typical examples of birth-death pairs for typical regular structures are depicted in Fig. 1b–d. For regular hexagonal points whose distance between points is a, the ring appears at radius a/2 and disappears at radius a, as shown in Fig. 1b. For a regular triangular configuration, the ring appears at a/2 and disappears at \(\sqrt {\frac{1}{3}} a \approx 0.577a\), as shown in Fig. 1c, and the one-dimensional persistence diagram for regular hexagonal/triangular points is shown in Fig. 1d. Further details are described in ref. 40. In this article, persistence diagrams are used to investigate rings and polyhedral formations in atomic configurations. We also note that the detected rings are recorded during the computation of the diagrams, and hence, we can explicitly identify their geometric shapes.
Results and discussion
The mixed alkali effect
Figure S1 shows the dielectric constants, εr, for the alkali silicate glasses measured at different frequencies. It is well known that mixed alkali glasses show a pronounced reduction in dc conductivity in comparison with single alkali glasses20,41. Indeed, the εr shown in Fig. S1 exhibits a nonlinear trend as a function of the K2O amount and has a minimum value in the Na50K50 glass at all frequencies. It is also observed that the mixed alkali effect diminishes with increasing frequency. This behavior is in agreement with the previous study on the 33.3(Na2O+Li2O)-66.7SiO2 system41. Thus, the mixed alkali effect is clearly observed in the electrical properties of the alkali silicate glasses.
Structure factors and real-space functions
Figure 2 compares the neutron and X-ray structure factors, SN,X(Q), between the alkali silicate glasses and SiO2 glass. A sharp FSDP is observed at Q ~ 1.5 Å−1 in the SN,X(Q) for SiO2 glass, whereas the FSDP becomes broader when alkali ions are added. The FSDP also appears in the SN(Q) for the alkali silicate glasses, but the shape of the peak is very complicated. Indeed, an extra peak is observed at Q ~ 0.8 Å−1 in the case of the K100 glass. On the other hand, the FSDP is not visible in the SX(Q) for both the Na50K50 and K100 glasses due to the large weighting factors of potassium for X-rays. The second principle peak (PP) is found only in the SN(Q) because the PP reflects the oxygen-oxygen correlation, which is easily detected by neutrons. It is worth noting that an average of the diffraction profiles of the Na100 and K100 glasses (black broken curve) is almost identical to the experimental data for the Na50K50 glass (green curve) for both SN(Q) and SX(Q), implying that the mixed alkali effect cannot be detected easily in the diffraction data. Readers can find the enlarged figures in Fig. S2, which show only subtle differences.
The neutron and X-ray total correlation functions, TN,X(r), for the alkali silicate glass are shown in Fig. 3. The Si–O correlation peak is located at 1.62 Å with a Si–O coordination number of 4.0 ± 0.1 in all glasses, and the Na–O correlation exhibits a small peak at approximately 2.3 Å in the cases of the Na100 and Na50K50 glasses. The O–O correlation peak and the Si–Si correlation peak are found at 2.63 Å and 3.08 Å, respectively, in SiO2 glass, but the peak overlaps with the K-O correlation peak for the Na50K50 and K100 glasses. It is expected from the Si–Si correlation peak that a more complicated structure should be formed in the alkali silicate glasses. However, it is not easy to extract more detailed information beyond the short range according to real space analysis, demonstrating the limitation of pairwise real-space correlations, although element-specific experimental real-space functions can extract long-range information42.
Analysis of partial structure
To obtain clear insight into the intermediate-range structure beyond the short range, we performed dedicated data-driven structure modeling with a combination of RMC and classical MD simulations. First, the atomic configurations, which reproduce the Qn distributions measured by NMR spectroscopy8, for the alkali silicate glasses were constructed by the RMC modeling technique. After that, the obtained structures were optimized using the classical MD simulation and minimizing the energy and then eventually subsequent RMC to refine the configurations. The final results of the RMC-MD modeling are plotted in Fig. 2 as solid colored curves. Good agreement between the RMC-MD model and the experimental data is obtained.
Figure 4a-c compare the ND/HEXRD SN,X(Q) and the partial structure factors, Sij(Q) (i and j are atoms), for the alkali silicate glasses, allowing us to find the contribution of any pairs of Sij(Q) to the overall FSDP and PP. The most striking features are the very prominent negative contributions of the alkali-alkali (Na–Na, Na–K, and K–K) partials to the FSDP. A similar negative contribution was reported in the result of the MD simulation for potassium disilicate glass10, but a negative trend is more apparent in our data. This is definitely a signature of the inhomogeneous distribution of the alkali ions14,17 and is strongly related to the variations in the partial pair-distribution functions, gij(r), for the alkali-oxygen correlations (see Fig. S3). We would like to emphasize here that the final RMC refinement of the experimental data enables us to visualize the intriguing variation in each correlation peak due to the finer structures in comparison with those obtained by the MD simulations (see Fig. S4). Comparisons of Sij(Q) for the network-forming components between SiO2 glass and the alkali silicate glasses are summarized in Fig. 4d. We can see prominent positive contributions to the FSDP from the Si-Si, Si-O, and O-O partial structure factors, Sij(Q), in the case of SiO2 glass. Intriguingly, the partial structure factors of Si-Si, Si-O, and O-O for the Na100 glass have less of a contribution to the FSDP, but the contribution is still positive, suggesting that the sodium ion does not modify the Si-O network significantly due to its small size. We can hardly observe the positive contributions of the partial structure factors to the FSDP in both the Na50K50 and K100 glasses. Indeed, this is reasonable if we take account of the difference in the alkali ion size between sodium and potassium ions (approximately 0.4 Å from the T(r) data in Fig. 3 and the gij(r) data in Fig. S3). Accordingly, it is possible to conclude that the extended-range order proposed by Price et al.43 can be formed only in the Na50K50 and K100 glasses.
Analysis of the three-dimensional atomistic structure
As discussed above, it is difficult to identify any detailed structural information on the basis of the pairwise correlation relating to the mixed alkali effect because the S(Q) and T(r) of Na50K50 glass are roughly identical to the average of those of Na100 and K100 glasses. Therefore, it is necessary to analyze the RMC-MD-generated atomistic configuration to extract structural information. Figure 5a (upper) depicts the primitive (Si-O)n ring statistics. It is well known that SiO2 glass shows a broad ring size distribution44, although a six-atom ring, which is the only possible ring structure in the crystalline phase with comparable density (cristobalite), is dominant. This broad distribution is the result of topological disorder according to Cooper and Gupta45, and hence, this is a very important characteristic in glass. In the case of alkali silicate glasses, we can see a broader distribution due to the introduction of alkali ions breaking down the Si-O network, which is consistent with previous studies10,11. It is worth mentioning that the fractions of the larger rings (n ≧ 13) increase with the addition of K2O (see Table 1), suggesting that K100 glass is the most topologically disordered. The cavity surfaces are visualized in Fig. 5b (middle). Obviously, SiO2 glass, which yields the largest cavity volume ratio of 32.2%, exhibits a string-like cavity. The cavity volume ratio in the alkali silicate glasses increases monotonically with the increase in the K2O amount and cannot provide any evidence for the mixed alkali effect in the intermediate-range structure as well as the NMR data8. To shed light on the mixed alkali effect, we evaluated the cavity volume distribution in Fig. 5c (bottom), and the maximum cavity sizes in Table 1. The volume of the largest cavity of SiO2 glass is 14,206 Å3, and the maximum cavity volumes for the Na100, Na50K50, and K100 glasses are 166, 323, and 1,310 Å3, respectively, representing the nonlinear variation of the structure with increasing K2O content. Indeed, Fig. 5c (bottom) demonstrates that the maximum cavity size of the Na50K50 glass is obviously smaller than the average value of the Na100 and K100 glasses. Assuming that the size difference between sodium and potassium ions is 0.4 Å, the smaller size cavities should prevent the migration of potassium ions in the Na50K50 glass, which explains why the dielectric constant of the Na50K50 glass is the lowest, as shown in Fig. S1.
Persistent homology analysis
To obtain more detailed information to reconcile the mixed alkali effect, we applied a novel topological approach, the persistent homology analysis40, to extract the topology. Fig. S5a-c show the alkali-centric persistence diagrams for the alkali silicate glasses. We can observe two prominent profiles along the diagonal for all the glasses. It is known that the profile with a very short lifetime represents three-body correlations, as shown in Fig. S5d-f, and distinguishable differences among the three glasses are not observed in the short lifetime distributions, indicating that the short-range structures should be analogous. On the other hand, the alkali-centric persistence diagrams of Na50K50 glass for Na-centric, Na/K-centric, and K-centric data shown in Fig. 6 exhibit a striking difference. Both the Na-centric (Fig. 6a) and K-centric data (Fig. 6c) do not have any characteristic profiles, while only the Na/K-centric persistence diagram (Fig. 6b) has two profiles at dk ~5 and ~10 Å2. These profiles demonstrate that Na and K are highly correlated with edge-sharing oxygen in Na50K50 glass, similar to Na-O-K. Indeed, the connectivity analysis46 confirmed that 81% of Na, K, and O atoms form a network in Na50K50. We compare the profiles shown in Fig. 6d–f with the partial pair-distribution functions, gij(r), for the series of alkali silicate glasses in Fig. 6g. As seen in Fig. 6g (left), we can hardly observe differences among gNaNa(r), gNaK(r), and gKK(r) because they contain only 1-dimensional information. On the other hand, the three-body correlation as a function of distance in Fig. 6g (right) shows the formation of specific correlations between Na and K ions, as mentioned above. Thus, the persistence diagram enables us to extract the characteristic topology in the glasses. To obtain more detailed structural information associated with the breakdown of the silicate network, alkali-oxygen polyhedra with the formation of edge-sharing NBO atoms in alkali silicate glasses are visualized in Fig. 7a-c. We believe that the visualization should provide us with crucial information to uncover the origin of the mixed alkali effect, as demonstrated in Fig. S1. Contrary to the similar schematic drawings in the previous studies21,25,26, we depicted the atomistic configurations from the structural models, which are consistent with both the NMR and the diffraction data, for the first time, provide us with more accurate information to reconcile the mixed alkali effect. A comparison between the Na100 and K100 glasses suggests that the shape of the Na-O polyhedra is planar, whereas that of the K-O polyhedra is polyhedral. To understand the nature of the alkali-oxygen polyhedra, we calculated the coordination numbers of the bridging oxygen (BO) and NBO around the alkali ions, as summarized in Table 1. The alkali-NBO coordination number is ~2 in both the Na100 and K100 glasses, and the alkali-BO coordination number is 2.1 in the Na100 glass. On the other hand, the K100 glass exhibits a larger coordination number, 2.4, and this trend is enhanced in the Na50K50 glass, in which the K-BO coordination number is almost 3. The K-O polyhedra that are highly coordinated to the BO and Na-O polyhedra are highlighted in black in Fig. 7b, where the potassium atom is trapped by a higher number of BO atoms (see Fig. 7d). It is likely that these specific configurations involving NBO atoms are a bottleneck in ionic conduction because the trapped potassium ions disturb ionic migration. It has been reported that each kind of alkali ion has an independent conduction pathway according to MD simulations on lithium potassium metasilicate glass47. Accordingly, Habasaki et al. found that the transfer of alkali ions through different ion sites has a low probability and proposed an interpretation for restricted ion jumping among the sites occupied by other types of ions due to a mismatch in the occupation energies of unlike alkali ions48. Our intriguing finding; that is, the local environment of potassium ions in the highly coordinated K–O polyhedra is significantly different from that of sodium ions in the four-coordinated Na–O polyhedra, successfully proves their hypothesis. In addition, the specific correlations between the different ions, which are found in the Na50K50 glass by the persistent homology (Fig. 6g (right)) and connectivity analyses, profoundly inhibited the ionic migration in the Na50K50 glass further. Hence, the local structure associated with alkali connectivity is the intrinsic origin of the mixed alkali effect. In summary, we have succeeded in visualizing the modified network model proposed by Greaves with the bottleneck structure, which stands for the mixed alkali effect21.
In this study, for the first time, we reconstructed the most reliable and accurate structure models for the alkali silicate glasses by using the combined RMC-MD method and reproducing the NMR spectra and the neutron and X-ray structure factors simultaneously. On the basis of the most reliable structural model, we have succeeded in reconciling the mixed alkali effect based on the behaviors of the alkali ions around the NBO atoms, as well as the modification of the Si–O network by addition of alkali oxides. The advanced topological analysis allows us to extract novel information on the structure to understand the origin of the mixed alkali effect. This dedicated approach therefore offers a way to find crucial knowledge to uncover other properties in glasses.
Data availability
The datasets generated during and/or analyzed during the current study are available from the corresponding author upon reasonable request.
References
Zachariasen, W. H. The atomic arrangement in glass. J. Am. Chem. Soc. 54, 3841–3851 (1932).
Elliott, S. R. The origin of the first sharp diffraction peak in the structure factor of covalent glasses and liquids. J. Phys. Condens. Matter 4, 7661–7678 (1992).
Salmon, P. S. Real space manifestation of the first sharp diffraction peak in the structure factor of liquid and glassy materials. Proc. R. Soc. Lond. A 445, 351–365 (1994).
Gaskell, P. H. & Wallis, D. J. Medium-range order in silica, the canonical network glass. Phys. Rev. Lett. 75, 66–69 (1996).
Wright, A. C. Neutron scattering from vitreous silica. V. The structure of vitreous silica: What have we learned from 60 years of diffraction studies? J. Non-Cryst. Solids 179, 84–115 (1994).
Brüning, R. & Cottrell, D. X-ray and neutron scattering observations of structural relaxation of vitreous silica. J. Non-Cryst. Solids 325, 6–15 (2003).
Susman, S. et al. Intermediate-range order in permanently densified vitreous SiO2: a neutron-diffraction and molecular-dynamics study. Phys. Rev. B 43, 1194–1197 (1991).
Maekawa, H., Maekawa, T., Kawamura, K. & Yokokawa, T. The structural groups of alkali silicate glasses determined from 29Si MAS-NMR. J. Non-Cryst. Solids 127, 53–64 (1991).
Du, J. & Corrales, L. R. First sharp diffraction peak in silicate glasses: Structure and scattering length dependence. Phys. Rev. B 72, 092201 (2005).
Du, J. & Corrales, L. R. Compositional dependence of the first sharp diffraction peaks in alkali silicate glasses: a molecular dynamics study. J. Non-Cryst. Solids 352, 3255–3269 (2006).
Wicks, J. D., McGreevy, R. L. & Börjesson, L. A network problem: modelling alkali-silicate glasses with RMC. Phase Transit. 61, 195–213 (1997).
Hannon, A. C., Vessal, B. & Parker, J. M. The structure of alkali silicate glasses. J. Non-Cryst. Solids 150, 97–102 (1992).
Florian, P., Vermillion, K. E., Grandinetti, P. J., Farnan, I. & Stebbins, J. F. Cation distribution in mixed alkali disilicate glasses. J. Am. Chem. Soc. 118, 3493–3497 (1996).
Tokuda, Y., Oka, T., Takahashi, M. & Yoko, T. Inhomogeneous distribution of Na+ in alkali silicate glasses. J. Ceram. Soc. Jpn. 119, 909–915 (2011).
McMillan, P. Structural studies of silicate glasses and melts-applications and limitations of Raman spectroscopy. Am. Mineral. 69, 622–644 (1984).
Mysen, B. Physics and chemistry of silicate glasses and melts. Eur. J. Mineral. 15, 781–802 (2003).
Meyer, A., Horbach, J., Kob, W., Kargl, F. & Schober, H. Channel formation and intermediate range order in sodium silicate melts and glasses. Phys. Rev. Lett. 93, 027801 (2004).
Kargl, F., Meyer, A., Koza, M. M. & Schober, H. Formation of channels for fast-ion diffusion in alkali silicate melts: a quasielastic neutron scattering study. Phys. Rev. B 74, 014304 (2006).
Inoue, K., Kataoka, H., Nagai, Y., Hasegawa, M. & Kobayashi, Y. Short and medium range order in two-component silica glasses by positron annihilation spectroscopy. J. Appl. Phys. 115, 204903 (2014).
Isard, J. O. The mixed alkali effects in glass. J. Non-Cryst. Solids 1, 235–261 (1969).
Greaves, G. N. EXAFS and the structure of glass. J. Non-Cryst. Solids 71, 203–217 (1985).
Dyre, J. C., Maass, P., Roling, B. & Sidebottom, D. L. Fundamental questions relating to ion conduction in disordered solids. Rep. Prog. Phys. 72, 046501 (2009).
Huang, C. & Cormack, A. N. Structure and energetics in mixed-alkali-metal silicate glasses from molecular dynamics. J. Mater. Chem. 2, 281–287 (1992).
Swenson, J. & Adams, S. Mixed alkali effect in glasses. Phys. Rev. B 47, 155507 (2003).
Greaves, G. N. & Ngai, K. L. Reconciling ionic-transport properties with atomic structure in oxide glasses. Phys. Rev. B 52, 6358–6380 (1995).
Park, B. & Cormack, A. N. Molecular dynamics simulations of structural changes in mixed alkali (Li±K) silicate glasses. J. Non-Cryst. Solids 255, 112–121 (1999).
Habasaki, J., Leon, C. & Ngai, K. L. Dynamics of glassy, crystalline and liquid ionic conductors Springer International Publishing, Switzerland, 2017.
Otomo, T. et al. Fundamental research of hydrogen storage mechanism with high-intensity total diffractometer. KENS Rep. 17, 28–36 (2011).
Kohara, S. et al. Structural studies of disordered materials using high-energy x-ray diffraction from ambient to extreme conditions. J. Phys. Condens. Matter 19, 506101 (2007).
Faber, T. E. & Ziman, J. M. A theory of the electrical properties of liquid metals III. The resistivity of binary alloys. Philos. Mag. 11, 153–173 (1965).
Lorch, E. Neutron diffraction by germania, silica and radiation-damaged silica glasses. J. Phys. C: Solid State Phys. 2, 229–237 (1969).
Gereben, O., Jóvári, P., Temleitner, L. & Pusztai, L. A new version of the RMC++, reverse Monte Carlo programme, aimed at investigating the structure of covalent glasses. J. Optoelectron. Adv. Mater. 9, 3021–3027 (2007).
Evrard, G. & Pusztai, L. Reverse Monte Calro modelling of the structure of disordered materials with RMC++: a new implementation of the algorithm in C. J. Phys. Condens. Matter 17, S1–S13 (2005).
Plimpton, S. Fast parallel algorithms for short-range molecular dynamics. J. Comput. Phys. 117, 1–19 (1995).
Pedone, A., Malavasi, G., Menziani, M. C., Cormack, A. N. & Segre, U. A new self-consistent empirical interatomic potential model for oxides, silicates, and silica-based glasses. J. Phys. Chem. B 110, 11780–11795 (2006).
Nosé, S. A unified formulation of the constant temperature molecular dynamics methods. J. Chem. Phys. 81, 511–519 (1984).
Roux, S. Le & Jund, P. Ring statistics analysis of topological networks: New approach and application to amorphous GeS2 and SiO2 systems. Comput. Mater. Sci. 49, 70–83 (2010).
Heimbach et al. pyMolDyn: Identification, structure, and properties of cavities/vacancies in condensed matter and molecules. J. Comput. Chem. 38, 389–394 (2017).
https://www.wpi-aimr.tohoku.ac.jp/hiraoka_labo/homcloud/index.en.html.
Hiraoka, Y. et al. Hierarchical structures of amorphous solids characterized by persistent homology. Proc. Natl Acad. Sci. USA 113, 7035–7040 (2016).
Tomozawa, M. & McGahay, V. Mechanism of the mixed alkali effect based upon the thermodynamic state of glass. J. Non-Cryst. Solids 128, 48–56 (1991).
Salmon, P. S., Martin, R. A., Mason, P. E. & Cuello, G. J. Topological versus chemical ordering in network glasses at intermediate and extended length scales. Nature 435, 75–78 (2005).
Price, D. L. et al. Short-, intermediate-, and extended-range order in rubidium germanate glasses. Phys. Rev. B 55, 11249–11254 (1997).
Kohara, S. et al. Relationship between topological order and glass forming ability in densely packed enstatite and forsterite composition glasses. Proc. Natl Acad. Sci. USA 108, 14780–14785 (2011).
Gupta, P. K. & Cooper, A. R. Topologically disordered networks of rigid polytopes. J. Non-Cryst. Solids 123, 14–21 (1990).
Kohara, S. et al. Lead silicate glasses: Binary network-former glasses with large amounts of free volume. Phys. Rev. B 82, 134209 (2010).
Habasaki, J., Okada, I. & Hiwatari, Y. MD study of the mixed alkali effect in a lithium-potassium metasilicate glass. J. Non-Cryst. Solids 183, 12–21 (1995).
Habasaki, J., Okada, I. & Hiwatari, Y. MD study of the mixed alkali effect in terms of the potential surface in the lithium-potassium metasilicate glass. J. Non-Cryst. Solids 208, 181–190 (1996).
Acknowledgements
This work was partially supported by JST-PRESTO ‘Advanced Materials Informatics through Comprehensive Integration among Theoretical, Experimental, Computational and Data-Centric Sciences’, Japan Grant Number JPMJPR15N4 (to S.K.); the ‘Materials Research by Information Integration’ Initiative (MI2I) project of the Support Program for Starting Up Innovation Hub from JST (To Y.O., S.K., and Y.H.); JST CREST 15656429 (to Y.H.); and JSPS KAKENHI Grant Number JP19K05648 (to Y.O.). The synchrotron radiation experiments were performed at BL04B2 of SPring-8 with the approval of the Japan Synchrotron Radiation Research Institute (JASRI; Proposal Nos. 2016A1499 and 2017B0134). The neutron experiment at the Materials and Life Science Experimental Facility of the J-PARC was performed under a user program (Proposal No. 2017A0146). We acknowledge Dr. Toshiya Otomo and Dr. Kazutaka Ikeda for their help in the neutron diffraction measurement using the spectrometer NOVA at J-PARC. Dr. Hirokazu Masai is gratefully appreciated for helpful discussions.
Author information
Authors and Affiliations
Contributions
S.K. and Y.T. designed this research. Samples were prepared by H.H. and S.I. Dielectric constants were measured by H.H. Neutron diffraction measurements were performed by Y.T. and Y.O. High-energy X-ray diffraction measurements were conducted by Y.T., S.K., and Y.O. Molecular dynamics simulations were performed by T.T. and S.U. The obtained data were analyzed by S.K., Y.T., Y.O., S.F., I.O., and Y.H.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Onodera, Y., Takimoto, Y., Hijiya, H. et al. Origin of the mixed alkali effect in silicate glass. NPG Asia Mater 11, 75 (2019). https://doi.org/10.1038/s41427-019-0180-4
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41427-019-0180-4
- Springer Japan KK
This article is cited by
-
Formation of a zirconium oxide crystal nucleus in the initial nucleation stage in aluminosilicate glass investigated by X-ray multiscale analysis
NPG Asia Materials (2024)
-
Combinatorial characterization of metastable luminous silver cations
Scientific Reports (2024)
-
Glass–ceramic sealant with different alkali contents made from natural and waste materials for SOFC
Journal of Thermal Analysis and Calorimetry (2023)
-
Mixed-Alkali Effect on Thermal Property and Elastic Behavior in Borosilicate Glasses
Journal of Wuhan University of Technology-Mater. Sci. Ed. (2023)
-
Structure of alumina glass
Scientific Reports (2022)