Abstract
Perpendicular magnetic tunnel junctions based on MgO/CoFeB structures are of particular interest for magnetic random-access memories because of their excellent thermal stability, scaling potential, and power dissipation. However, the major challenge of current-induced switching in the nanopillars with both a large tunnel magnetoresistance ratio and a low junction resistance is still to be met. Here, we report spin transfer torque switching in nano-scale perpendicular magnetic tunnel junctions with a magnetoresistance ratio up to 249% and a resistance area product as low as 7.0 Ω µm2, which consists of atom-thick W layers and double MgO/CoFeB interfaces. The efficient resonant tunnelling transmission induced by the atom-thick W layers could contribute to the larger magnetoresistance ratio than conventional structures with Ta layers, in addition to the robustness of W layers against high-temperature diffusion during annealing. The critical switching current density could be lower than 3.0 MA cm−2 for devices with a 45-nm radius.
Similar content being viewed by others
Introduction
Perpendicular anisotropy-based magnetic tunnel junctions (p-MTJs) have great potential for reducing power dissipation and scaling to feature sizes below 20 nm1,2,3,4,5,6,7, and thus have been extensively studied to develop spin-transfer torque magnetic random access memories (STT-MRAMs) and very-large-scale integrated circuits (VLSIs)8,9,10,11,12,13. In particular, p-MTJs with a MgO/CoFeB/heavy metal (e.g., Ta, Hf) structure have attracted interest for their enhanced perpendicular anisotropy that originates from both MgO/CoFeB and CoFeB/heavy metal interfaces14,15,16,17,18, bringing a reasonable magnetoresistance ratio (TMR) and STT switching critical current density (JC). Furthermore, p-MTJs with a double MgO/CoFeB interface free layer, i.e., MgO/CoFeB/Ta/CoFeB/MgO, have been shown to possess a considerable thermal stability factor (Δ), and JC comparable to that of p-MTJs with a single interface19,20,21,22.
However, a critical issue in terms of double MgO/CoFeB interfaces is the incorporation of an additional MgO layer, which makes it even more difficult to reduce the resistance area product (RA) below 10 Ω µm2, while maintaining a TMR above 150% (see Supplementary Note 1 and Supplementary Fig. 1)23,24,25,26. On the other hand, for those typical configurations using Ta layers, the TMR, interfacial perpendicular magnetic anisotropy (PMA), and other magnetic properties degrade rapidly at the 400 °C back end of line (BEOL) temperature27,28,29,30,31. Thus, there is a need to understand how to enable nano-fabrication compatibility, as well as to reach a compromise between low write energy and large sense margins.
To address those concerns, W was recently reported to replace Ta as spacer and bridging layers in top-pinned p-MTJ films32,33,34,35,36,37. A TMR of 141% after 400 °C annealing and a Δ of 61 have been obtained from blank films34. These improvements were partially attributed to the suppression of atom diffusion and crystalline structure of the W layer, whereas the essential role of W layers in TMR enhancement has not been clearly revealed. Besides, STT switching behaviour and junction resistance were also not shown in these studies.
In our study, a bottom-pinned p-MTJ stack with atom-thick W layers and double MgO/CoFeB interfaces was patterned into nanopillars to demonstrate STT switching with relatively low JC. In addition to the strong thermal endurance shown in Cs-corrected transmission electron microscopy (TEM) observation, a further increased TMR of 249% and an RA as low as 7 Ω µm2 are simultaneously achieved. Furthermore, by using the first-principles calculation, atom-thick W layers are found to induce resonant tunnelling transmission more efficiently than Ta layer, providing a comprehensive explanation of the origin for this large TMR.
Results
PMA of p-MTJ films
The p-MTJ stacks we studied here were composed of, from the substrate side, [Co (0.5)/Pt (0.2)]6/Co (0.6)/Ru (0.8)/Co (0.6)/[Pt (0.2)/Co (0.5)]3/W (0.25)/CoFeB (1.0)/MgO (0.8)/CoFeB (1.3)/W (0.2)/CoFeB (0.5)/MgO (0.75)/Ta (3.0) (Fig. 1a, numbers in parenthesis denote layer thickness in nm), and were deposited on thermally oxidized Si substrate with a 75 nm Ta/CuN/Ta seed layer by a Singulus magnetron sputtering machine. Ultrathin MgO layers were employed to minimize RA. Those p-MTJ films were then subject to vacuum annealing from 350 to 430 °C for an hour. And the p-MTJ film annealed at 390 °C (see Supplementary Note 2 and Supplementary Fig. 2) was patterned into circular nanopillars with 45–150 nm radius (r) using electron beam (e-beam) lithography and Ar ion milling, as shown in Fig. 1b.
We investigated the magnetic characteristics of blank samples using a physical properties measurement system-vibrating sample magnetometer (PPMS-VSM). Figure 1c illustrates the representative M–H hysteresis loops under out-of-plane and in-plane magnetic fields, where the p-MTJ film was annealed at 410 °C. The upper and bottom CoFeB free layers present strong ferromagnetic coupling through a 0.2-nm W spacer layer and switch simultaneously according to the minor loop (inset of Fig. 1c), which is significant to enable STT switching19. We also performed a first-principles calculation to study the dependence of the magnetic coupling between the two CoFeB free layers on the thickness of W spacer layer. The p-MTJ stacks reveal the strongest ferromagnetic coupling while using a single-atom W spacer layer, while a transition to weak antiferromagnetic coupling at three-atom W layers33. Therefore, the thickness of the 0.2 nm W spacer layer is critical for the STT switching. Moreover, the enhancement of thermal endurance at 410 °C should be related to the lower atom diffusion when using W, instead of Ta, as the spacer and bridging layers31. Annealing at higher temperature could improve the crystalline quality of the MgO barrier and the bcc (body-centred cubic) texture of the CoFeB layers1,38, thus a larger TMR can be expected.
Thermal stability factor estimation
To minimize data loss for large memory capacities (e.g., 1 Gb), as well as to meet the industry standard retention time of 10 years, Δ > 60 is required. This factor can be expressed as: \({\it \Delta} = \frac{E}{{{k}_{\mathrm{B}}T}} = \frac{{M_{\mathrm{s}}H_{\mathrm{K}}V}}{{2{k}_{\mathrm{B}}T}}\), where E is the energy barrier between two magnetization states, Ms the saturation magnetization, HK the anisotropy field, V the volume of the free layer, kB the Boltzmann constant, and T the absolute temperature. To further understand the situation of Δ in this case, we quantified HK as a function of CoFeB thickness using the ferromagnetic resonance (FMR) method.
The p-MTJ films with a MgO/CoFeB (t = 1.2 ~ 1.6)/W (0.2)/CoFeB (0.5)/MgO free layer were prepared, where t represents the thickness of the bottom CoFeB free layer. For the p-MTJ film with t = 1.3 nm (corresponding to the one patterned into nanopillars), HK is around 3102 Oe, indicating a significant Δ ~ 60 for p-MTJs on 3x-nm technology node (Fig. 1d). Besides, for t = 1.2 nm, HK is as large as 4313 Oe, and a HC of 70 Oe has been achieved (see Supplementary Note 3 and Supplementary Fig. 3), which is sufficient to overcome the disturbance caused by the read operation. A near-zero shift field suggests an effective reduction of stray field from the Co/Pt SAF reference layer. The p-MTJs have the potential to be further scaled and optimized, specifically for low-power VLSIs and other applications.
Spin transfer torque in p-MTJs
Magnetic field and current sweeps were performed at room temperature (295 K) to characterize the STT behaviour in nanopillars. Figure 2a presents the resistance transition of an p-MTJ (r = 90 nm) versus magnetic field applied along the out-of-plane direction. The two CoFeB free layers switch as a single layer, and the resistance states are bi-stable: positive field leads to parallel (P) to anti-parallel (AP) perpendicular magnetization switching, while negative field causes the reverse operation. A TMR as large as 249% is achieved. Meanwhile, an RA as low as 7 Ω µm2 is obtained, which is 40% lower than the typical value of double barrier p-MTJs19. Because the RA maintains almost constant with regard to different junction areas, current shunting caused by sidewall redeposition can be excluded. Figure 2b shows STT switching and its detection by resistance change along with DC current sweep. The JC measured here is +6.0/−5.4 MA cm−2, which is comparable to that of p-MTJs using Ta spacer and bridging layers; in particular, p-MTJs with r = 45 nm show an average absolute JC around 2.8 MA cm−2 (see Supplementary Note 4 and Supplementary Fig. 4).
We also characterized STT switching using pulse current with various durations τP at room temperature (295 K). The JC measured from the p-MTJ (TMR = 237% in Fig. 3a) with r = 75 nm is +6.9/−6.5 MA cm−2 at τP = 100 μs (Fig. 3b). Additionally, we characterized JC as a function of τP/τ0, where τ0 = 1 ns is the characteristic attempt time. As plotted in Fig. 3c, the intrinsic critical current density JC0 is fitted as 7.8 MA cm−2. Because the exchange coupling between two magnetic layers has a dependence on the temperature39, this measurement was also conducted at 35 K (see Supplementary Note 5 and Supplementary Fig. 5), which can also eliminate the impact of thermally activated transition.
First-principles calculation of TMR
We theoretically explain this high TMR by the first-principles calculation, which combines the Keldysh nonequilibrium Green’s function with the density functional theory (NEGF-DFT)40. This technique has been used in our preliminary TMR calculation41. Here, atomic structures were built according to our experimental p-MTJ configuration, i.e., Ta (001)/CoFe (001)/X/CoFe (001)/MgO (001)/CoFe (001)/Ta (001), where the X represents W or Ta spacer layers for comparison (see Supplementary Note 6 and Supplementary Fig. 6).
The computed TMRs for the MTJ stacks with single-atom W or Ta spacer layer are 245% and 90%, respectively, which are consistent with our experiments and the previous results based on Ta layers19,20,21. Spin-resolved conductance was obtained by using Landauer–Büttiker formula: \(G_\sigma = \frac{{e^2}}{h}\mathop {\sum }\nolimits_{{\boldsymbol{{k}}}_\parallel } T_\sigma \left( {\boldsymbol{{{k}}}}_\parallel ,{{E}_{\rm F}} \right)\), where the \(\mathop {\sum }\nolimits_{{\boldsymbol{ {k}}}_\parallel } T_\sigma \left( {{\boldsymbol{{k}}}}_\parallel ,{E_{\rm F}} \right)\) is the transmission coefficient at the Fermi level EF with spin σ and transverse Bloch wave vector \({\boldsymbol{{k}}}_\parallel = \left( {k_x,k_y} \right)\); e is the electron charge and h is the Planck constant. Here, we plotted the transmission spectrums with log scale in the Brillouin zone as shown in Fig. 4 for analysis, and the colour bar shows the transmission probability from low (blue) to high (red). It can be seen that for the majority spin in the P state (Fig. 4a, e), a broad peak centred at k|| = (0, 0) appears due to the slow decay of Δ1 state. For the minority spin in P state (Fig. 4b, f), sharp peaks called hot spots appear at edges (shown in the red circle). This is caused by the resonant tunnelling transmission, which occurs when the localized interface states on the two CoFe/MgO interfaces align in energy42. Whereas in the AP state (Fig. 4c, d, g, h), the transmission coefficients of the hot spots are relatively lower.
As the resonant tunnelling transmission is sensitive to the bias voltage (Vb), we further calculated the dependence on Vb of TMR. For the p-MTJ with W spacer layer, the TMR dramatically drops with increasing Vb: when Vb = 10 mV, the TMR is 173%; and when Vb = 50 mV, the TMR has decreased to 107%. On the contrary, for the p-MTJ with Ta spacer layer, the TMR remains 88% at Vb = 50 mV. This intense TMR decay is consistent with our experimental results (e.g., Fig. 2b), while the p-MTJ using Ta insertion presents less dependency22. Accordingly, we conclude that the resonant tunnelling transmission with higher transmission coefficient could contribute to the large TMR for the p-MTJ stack with W spacer layer.
To establish a more distinct physical picture, we present how the scattering state, which is the absolute square of the tunnelling electron wavefunction, changes at CoFe/MgO interfaces (see Supplementary Note 7 and Supplementary Fig. 7). And the transmission probability is proportional to the density of scattering states. In the case of atom-thick W spacer layer, a higher density of scattering states is obtained at the region around the k|| = (0, 1) point, leading to a larger conductance in the P state.
Crystallization and atom distribution study
Spherical aberration corrected TEM (Cs-corrected TEM) and atomic-resolution electron energy-loss spectroscopy (EELS) were applied to study the structural properties of the p-MTJ stacks. Figure 5a shows a Cs-corrected TEM image of the p-MTJ stack annealed at 390 °C, which verifies the excellent crystalline quality of the MgO barrier, though the atom-thick W spacer and bridging layers are too thin to be captured. Figure 5b maps the EELS intensities of W, B, and Mg after 410 °C annealing, and no distinct change of W distribution is shown compared with the nominal locations of W spacer and bridging layers, especially at increasing temperatures (see Supplementary Note 8 and Supplementary Fig. 8). Because W is a heavy metal element, we established an energy-dispersive X-ray spectroscopy EDS test as a further confirmation. As mapped in Fig. 5c, no signal of W was detected within the MgO barrier or at the CoFeB/MgO interfaces, supporting the point that W is robust against high-temperature diffusion. Besides, the peaks of B and W are quite close in the EELS profiles, indicating a large amount of B existing in the W spacer and bridging layers. Thus, the W layers not only provide a typical bcc template for the texture of adjacent CoFeB layers, but also absorb B atoms during annealing to create robust interfacial PMA. Both the crystalline structure and atom distribution contribute to the interfacial PMA, TMR, and thermal endurance.
Discussion
Overall, the TMR enhancement we have achieved mainly originates from two factors: from the viewpoint of mechanism, the efficient resonant tunnelling induced by the atom-thick W layer could contribute to a larger TMR than the conventional p-MTJs with Ta layers; on the other hand, the W layer is robust against high-temperature diffusion, resulting in better crystallinity of MgO barrier and higher TMR.
In addition, the single-atom W layers we used also benefit the p-MTJ nano-pillars from the following aspects. First, we have experimentally and theoretically revealed that the largest TMR can be achieved by using single-atom W layers under this situation. The p-MTJ films with 0.2 nm W spacer layer possess TMRs about 20% higher than that of samples using 0.3 nm (see Supplementary Fig. 2a). This corresponds to the tendency obtained from the first-principles calculation: the calculated TMR decreases from 245% to 171% while increasing the thickness of W from a single-atom layer to three atoms (see Supplementary Note 9 and Supplementary Table 1).
Second, the JC we obtained is comparable to that for p-MTJs configured with Ta layers, and does not scale with the enhanced Δ, which can be ascribed to the lower damping constant (α). The α of conventional p-MTJs using Ta layers is sub-optimal for its strong spin–orbit coupling and atom diffusion during high-temperature annealing. Our earlier experiments have proved that α is material dependent, thus could be reduced by replacing Ta with W as the spacer layer43. Further, the thinner the W spacer layer is, the lower the α becomes, because W diffusion is weakened with decreasing thickness44.
Third, the 0.2 nm W spacer layer enables the two CoFeB free layers to switch as a single layer in STT measurement by inducing a strong ferromagnetic coupling; and the 0.25 nm W bridging layer can ensure the stable ferromagnetic coupling between CoFeB reference layer and SAF layers. It has been widely investigated that the exchange coupling between two ferromagnetic layers separated by a nonmagnetic interlayer exhibits oscillatory behaviour due to the RKKY (Ruderman–Kittel–Kasuya–Yosida) iteration39,45,46,47. Moreover, as we calculated, as the nonmagnetic interlayer becomes thicker, the ferromagnetic coupling weakens monotonically and converts to antiferromagnetic coupling at three-atom W layers. Therefore, the atom-thick W spacer layer is critical for the switching reliability of our device regarding STT performance. However, our p-MTJ stack is a complex system involving stray field and other factors, thus more specific experiment should be carried out to prove this tendency.
To conclude, we demonstrated for the first time current-induced magnetization switching in p-MTJs with atom-thick W spacer and bridging layers, which present a large TMR of 249% and an RA as low as 7 Ω µm2. In particular, the experimental investigations and theoretical analyses provide an insight into the role of atom-thick W layers in determining TMR. We believe that this work provides a critical path to the research and development of new generation STT-MRAM (see Supplementary Note 1 and Supplementary Fig. 1).
Methods
Film growth
The p-MTJ stacks in our work were mainly grown with linear dynamic deposition technology by a Singulus TIMARIS 200 mm magnetron sputtering machine at a base pressure of 3.75 × 10−9 Torr. The substrates were thermally oxidized Si with a 75-nm Ta/CuN/Ta seed layer polished by chemical mechanical planarization. MgO deposition was performed by RF sputtering. The base pressure for vacuum annealing oven is around 3.75 × 10−10 Torr.
Device fabrication
To observe the STT effect, nanopillars were defined by e-beam lithography in the centre of 4-µm-wide bottom electrodes followed by Ar ion milling. Then they were fully covered with SiO2 for insulation. After the lift-off procedure, via holes were made over the bottom electrodes. Both the bottom electrodes and p-MTJs were then connected to 90 nm Ti/Au electrodes to allow electrical contact for measurement using e-beam evaporation.
Magnetic and electrical measurement
The blank stacks were studied with PPMS-VSM and FMR systems. The Cs-corrected TEM was performed by JEM ARM 200F. The PPMS-VSM used is the Quantum Design VersaLab. The setup for current-induced p-MTJ switching using the four-probe method consists of a Lake Shore CRX-VF cryogenic probe station, a Keithley 6221 current source, and a 2182 nanovolt metre.
Data availability
All data generated or analyzed during this study are included in this published article (and its Supplementary Information).
References
Ikeda, S. et al. A perpendicular-anisotropy CoFeB/MgO magnetic tunnel junction. Nat. Mater. 9, 721–724 (2010).
Worledge, D. C. et al. Spin torque switching of perpendicular Ta/CoFeB/MgO-based magnetic tunnel junctions. Appl. Phys. Lett. 98, 022501 (2011).
Hu, J. M., Li, Z., Chen, L. Q. & Nan, C. W. High-density magnetoresistive random access memory operating at ultralow voltage at room temperature. Nat. Commun. 2, 553 (2011).
Kim, W. et al. Extended scalability of perpendicular STT-MRAM towards sub-20nm MTJ node. In 2011 International Electron Devices Meeting 24.1.1-24.1.4 (IEEE, 2011).
Gajek, M. et al. Spin torque switching of 20 nm magnetic tunnel junctions with perpendicular anisotropy. Appl. Phys. Lett. 100, 132408 (2012).
Wong, H. S. P. & Salahuddin, S. Memory leads the way to better computing. Nat. Nanotechnol. 10, 191–194 (2015).
Chun, K. C. et al. A scaling roadmap and performance evaluation of in-plane and perpendicular MTJ based STT-MRAMs for high-density cache memory. IEEE J. Solid-State Circuits 48, 598–610 (2013).
Kent, A. D. & Worledge, D. C. A new spin on magnetic memories. Nat. Nanotechnol. 10, 187–191 (2015).
Park, C. et al. Systematic optimization of 1 Gbit perpendicular magnetic tunnel junction arrays for 28 nm embedded STT-MRAM and beyond. In 2015 IEEE International Electron Devices Meeting (IEDM) 26.2.1–26.2.4 (IEEE, 2015).
Hu, G. et al. STT-MRAM with double magnetic tunnel junctions. In 2015 IEEE International Electron Devices Meeting (IEDM) 26.3.1–26.3.4 (IEEE, 2015).
Slaughter, J. M. et al. Technology for reliable spin-torque MRAM products. In 2016 IEEE International Electron Devices Meeting (IEDM) 21.5.1–25.5.4 (IEEE, 2016).
Chung, S. W. et al. 4Gbit density STT-MRAM using perpendicular MTJ realized with compact cell structure. In 2016 IEEE International Electron Devices Meeting (IEDM) 27.1.1–27.1.4 (IEEE, 2016).
Song, Y. J. et al. Highly functional and reliable 8Mb STT-MRAM embedded in 28nm logic. In 2016 IEEE International Electron Devices Meeting (IEDM)27.2.1–27.2.4 (IEEE, 2016).
Shimabukuro, R., Nakamura, K., Akiyama, T. & Ito, T. Electric field effects on magnetocrystalline anisotropy in ferromagnetic Fe monolayers. Phys. E 42, 1014–1017 (2010).
Yang, H. X. et al. First-principles investigation of the very large perpendicular magnetic anisotropy at Fe/MgO and Co/MgO interfaces. Phys. Rev. B 84, 054401 (2011).
Peng, S. Z. et al. Origin of interfacial perpendicular magnetic anisotropy in MgO/CoFe/metallic capping layer structures. Sci. Rep. 2 (2015).
Soumyanarayanan, A., Reyren, N., Fert, A. & Panagopoulos, C. Emergent phenomena induced by spin-orbit coupling at surfaces and interfaces. Nature 539, 509–517 (2016).
Peng, S. Z. et al. Giant interfacial perpendicular magnetic anisotropy in MgO/CoFe/capping layer structures. Appl. Phys. Lett. 110, 072403 (2017).
Sato, H. et al. Perpendicular-anisotropy CoFeB-MgO magnetic tunnel junctions with a MgO/CoFeB/Ta/CoFeB/MgO recording structure. Appl. Phys. Lett. 10, 022414 (2012).
Yakushiji, K. et al. Ultralow-voltage spin-transfer switching in perpendicularly magnetized magnetic tunnel junctions with synthetic antiferromagnetic reference layer. Appl. Phys. Express 6, 113006 (2013).
Kan, J. J., Gottwald, M., Park, C., Zhu, X. & Kang, S. H. Thermally robust perpendicular STT-MRAM free layer films through capping layer engineering. IEEE Trans. Magn. 51, 1–5 (2015).
Devolder, T., Le Goff, A. & Nikitin, V. Size dependence of nanosecond-scale spin-torque switching in perpendicularly magnetized tunnel junctions. Phys. Rev. B 93, 224432 (2016).
Meng, H., Wang, J., Diao, Z. & Wang, J. P. Low resistance spin-dependent magnetic tunnel junction with high breakdown voltage for current-induced-magnetization-switching devices. J. Appl. Phys. 97, 10C926 (2005).
Amiri, P. K. et al. Low write-energy magnetic tunnel junctions for high-speed spin-transfer-torque MRAM. IEEE Electron. Device Lett. 32, 57–59 (2011).
Zhao, W. S. et al. Design considerations and strategies for high-reliable STT-MRAM. Microelectron. Reliab. 51, 1454–1458 (2011).
Wang, K. L., Alzate, J. G. & Amiri, P. K. Low-power non-volatile spintronic memory: STT-RAM and beyond. J. Phys. D 46, 074003 (2013).
Miyakawa, N., Worledge, D. C. & Kita, K. Impact of Ta diffusion on the perpendicular magnetic anisotropy of Ta/CoFeB/MgO. IEEE Magn. Lett. 4, 1000104 (2013).
Thomas, L. et al. Perpendicular spin transfer torque magnetic random access memories with high spin torque efficiency and thermal stability for embedded applications. J. Appl. Phys. 115, 172615 (2014).
Liu, T., Zhang, Y., Cai, J. W. & Pan, H. Y. Thermally robust Mo/CoFeB/MgO trilayers with strong perpendicular magnetic anisotropy. Sci. Rep. 4, 5895 (2014).
Sinha, J. et al. Influence of boron diffusion on the perpendicular magnetic anisotropy in Ta/CoFeB/MgO ultrathin films. J. Appl. Phys. 117, 043913 (2015).
An, G. G. et al. Highly stable perpendicular magnetic anisotropies of CoFeB/MgO frames employing W buffer and capping layers. Acta Mater. 87, 259–265 (2015).
Kim, J. H. et al. Ultrathin W space layer-enabled thermal stability enhancement in a perpendicular MgO/CoFeB/W/CoFeB/MgO recording frame. Sci. Rep. 5, 16903 (2015).
Lee, D. Y., Hong, S. H., Lee, S. E., & Park, J. G. Dependency of tunnelling-magnetoresistance ratio on nanoscale spacer thickness and material for double MgO based perpendicular-magnetic-tunnelling-junction. Sci. Rep. 6, 38125 (2016).
Lee, S. E., Takemura, Y. & Park, J. G. Effect of double MgO tunnelling barrier on thermal stability and TMR ratio for perpendicular MTJ spin-valve with tungsten layers. Appl. Phys. Lett. 109, 182405 (2016).
Lee, S. E., Shim, T. H. & Park, J. G. Perpendicular magnetic tunnel junction (p-MTJ) spin-valves designed with a top Co2Fe6B2 free layer and a nanoscale-thick tungsten bridging and capping layer. NPG Asia Mater. 9, e324 (2016).
Tezuka, N. et al. Perpendicular magnetic tunnel junctions with low resistance-area product: high output voltage and bias dependence of magnetoresistance. IEEE Magn. Lett. 7, 3104204 (2016).
Liu, Y. et al. High thermal stability in W/MgO/CoFeB/W/CoFeB/W stacks via ultrathin W insertion with perpendicular magnetic anisotropy. J. Magn. Magn. Mater. 410, 123–127 (2016).
Ikeda, S. et al. Tunnel magnetoresistance of 604% at 300 K by suppression of Ta diffusion in CoFeB/MgO/CoFeB pseudo-spin-valves annealed at high temperature. Appl. Phys. Lett. 93, 082508 (2008).
Celinski, Z. & Heinrich, B. Exchange coupling in Fe/Cu, Pd, Ag, Au/Fe trilayers. J. Magn. Magn. Mater. 99, L25–L30 (1991).
Taylor, J., Guo, H. & Wang, J. Ab initio modelling of quantum transport properties of molecular electronic devices. Phys. Rev. B 63, 245407 (2001).
Zhou, J. Q. et al. Large influence of capping layers on tunnel magnetoresistance in magnetic tunnel junctions. Appl. Phys. Lett. 109, 242403 (2016).
Tao, L. L. et al. Tunnelling magnetoresistance in Fe3Si/MgO/Fe3Si (001) magnetic tunnel junctions. Appl. Phys. Lett. 104, 172406 (2014).
Zhang, B. Y. et al. Influence of heavy metal materials on magnetic properties of Pt/Co/heavy metal tri-layered structures. Appl. Phys. Lett. 110, 012405 (2017).
Sabino, M. P. R., Ter Lim, S. & Tran, M. Influence of Ta insertions on the magnetic properties of MgO/CoFeB/MgO films probed by ferromagnetic resonance. Appl. Phys. Express 7, 093002 (2014).
Parkin, S. S. P. & Mauri, D. Spin engineering: Direct determination of the Ruderman-Kittel-Kasuya-Yosida far-field range function in ruthenium. Phys. Rev. B 44, 7131 (1991).
Kawakami, R. K. et al. Determination of the magnetic coupling in the Co/Cu/Co (100) system with momentum-resolved quantum well states. Phys. Rev. Lett. 82, 4098 (1999).
Kawakami, R. K. et al. Quantum-well states in copper thin films. Nature 398, 132–134 (1999).
Acknowledgements
The authors gratefully acknowledge the National Natural Science Foundation of China (Grant No. 61571023, 61627813, 61501013), International Collaboration Project B16001 and 2015DFE12880, and Beijing Municipal of Science and Technology (Grant No. D15110300320000) for their financial support of this work. The authors also would like to thank Lin Gu and Qinghua Zhang from Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, for the technical support of Cs-corrected TEM.
Author information
Authors and Affiliations
Contributions
W.Z. conceived and supervised the project. M.W. fabricated the devices, initiated the measurements. M.W., and W.Z. wrote the manuscript. W.C. performed the measurements. K.C., and J.W. optimized the e-beam lithography flow. J.Z., and S.P. carried out the first-principles calculation. H.Y., W.K., Y.Z., and A.F. helped analyse the data. J.W., J.L., and B.O. developed, grew and optimized the films. All authors discussed the results and implications.
Corresponding author
Ethics declarations
Competing financial interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, M., Cai, W., Cao, K. et al. Current-induced magnetization switching in atom-thick tungsten engineered perpendicular magnetic tunnel junctions with large tunnel magnetoresistance. Nat Commun 9, 671 (2018). https://doi.org/10.1038/s41467-018-03140-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-03140-z
- Springer Nature Limited
This article is cited by
-
Effective electrical manipulation of a topological antiferromagnet by orbital torques
Nature Communications (2024)
-
Single-nanometer CoFeB/MgO magnetic tunnel junctions with high-retention and high-speed capabilities
npj Spintronics (2024)
-
Skyrmion-mediated nonvolatile ternary memory
Scientific Reports (2024)
-
Spintronics intelligent devices
Science China Physics, Mechanics & Astronomy (2023)
-
Temperature stability of Co/Pt and Co/Pd synthetic antiferromagnets using an Ir spacer
Journal of Materials Science: Materials in Electronics (2023)