Abstract
Magnetic insulators (MIs) attract tremendous interest for spintronic applications due to low Gilbert damping and the absence of Ohmic loss. Spin-orbit torques (SOTs) on MIs are more intriguing than magnetic metals since SOTs cannot be transferred to MIs through direct injection of electron spins. Understanding of SOTs on MIs remains elusive, especially how SOTs scale with the MI film thickness. Here, we observe the critical role of dimensionality on the SOT efficiency by studying the MI layer thickness-dependent SOT efficiency in tungsten/thulium iron garnet (W/TmIG) bilayers. We show that the TmIG thin film evolves from two-dimensional to three-dimensional magnetic phase transitions as the thickness increases. We report the significant enhancement of the measured SOT efficiency as the TmIG thickness increases, which is attributed to the increase of the magnetic moment density. We demonstrate the current-induced SOT switching in the W/TmIG bilayers with a TmIG thickness up to 15 nm.
Similar content being viewed by others
Introduction
The interplay between heavy metals (HMs) and magnetic insulators (MIs) in heavy metal/magnetic insulator (HM/MI) bilayer systems has attracted tremendous attention from both fundamental research and practical applications1,2,3,4. First, the HM/MI bilayer benefits from the low Gilbert damping in the MI. In contrast to magnetic metal, MIs only allow spin information to propagate through magnons, instead of itinerant electrons, due to their large electronic bandgaps. The absence of Ohmic loss from the magnetic layer makes HM/MI bilayers more energy efficient than HM/magnetic metal bilayers.
The second advantage of the HM/MI bilayer is that the spin-orbit coupling in the HM or at the HM/MI interface allows the efficient generation of spin-orbit torques (SOTs) on the MI layer through the spin Hall effect (SHE) or Rashba–Edelstein effect5,6,7,8,9. These SOTs enable efficient manipulation of magnetization dynamics in the MI layer. Although the MI layer is electrically insulating, SOT-driven magnetization dynamics of MIs can be detected through anomalous Hall resistance (AHR) and spin Hall magnetoresistance (SMR) in the HM layer10,11,12,13. By probing the AHR, current-induced magnetization switching (CIMS) was observed in both Pt/BaFe12O1914 and Pt/Tm3Fe5O12 (TmIG) bilayers15,16. However, whether SOTs in Pt/MI bilayers are from SHE remains ambiguous due to the potential existence of the Rashba–Edelstein effect16. It remains unclear whether the switching direction will be opposite when we utilize HMs with opposite spin Hall angles. Moreover, the observed damping-like SOT efficiency (ξDL) in the Pt/TmIG that is responsible for switching is still much lower than those in the Pt/ferromagnetic metals (FMs)15,17,18. To understand the origin of SOTs and to increase the value of ξDL in HM/MI bilayers, we utilize a HM with a large spin Hall angle opposite to that of Pt in a HM/MI bilayer, demonstrate magnetization switching, and analyze the contributions to the SOT.
In this article, we study the ξDL and CIMS in tungsten (W)/TmIG heterostructures with different TmIG layer thicknesses (tTmIG). The thickness dependence of the damping-like SOT allows us to understand the interplay between spin current and magnetism in TmIG. Here, W is chosen since it is reported to give the largest spin Hall angle among elemental HMs and its sign is opposite to that of Pt19. When the TmIG film thickness is reduced from 15 to 3.2 nm, the effective exchange coupling is strongly reduced due to long-wavelength thermal fluctuations, resulting in a dimensional crossover from three-dimension-like to two-dimension-like magnetic phase transitions. We quantify ξDL by using second-harmonic Hall measurements20,21. The ξDL increases with the tTmIG in W/TmIG bilayers; this is attributed to the enhanced magnetic moment density due to suppression of thermal fluctuations. We then demonstrate the CIMS in W/TmIG bilayers up to tTmIG = 15 nm; for tTmIG = 15 nm, the switching current density is as low as 8 × 1010 A/m2. The estimated current switching efficiency enhances as tTmIG increases, which is consistent with the increase of ξDL with tTmIG. Importantly, the switching direction of our W/TmIG devices is indeed opposite to that of the Pt/TmIG device15; this contrast confirms the important role of SHE in CIMS of MIs.
Results
Dimensional crossover of magnetism
To access SOT and realize CIMS, we prepare high-quality TmIG thin films with different tTmIG and characterize their magnetic properties. These TmIG(111) thin films were grown on substrate Nd3Ga5O12(111) by pulsed laser deposition13. All TmIG thin films show an atomically flat surface with mean roughness as low as 0.1 nm (Fig. 1a), providing a sharp interface for efficient spin momentum transfer. The Gilbert damping of TmIG thin films increases as the thickness decreases (see Supplementary Note 1). The large lattice mismatch between the TmIG and the Nd3Ga5O12 provides the tensile strain to generate perpendicular magnetic anisotropy in all TmIG thin films. The nature of perpendicular magnetic anisotropy is confirmed using magnetization hysteresis loops of TmIG thin films as a function of an out-of-plane magnetic field (Fig. 1b), from which we can determine saturation magnetization (MS). We observe a strong tTmIG dependence of the MS at room temperature (Fig. 1c); the MS reduces significantly from the bulk MS (110 emu/cm3)22 with decreasing film thickness. Note that the estimated dead layer thickness is less than 1 nm (see Fig. 1c inset and Supplementary Note 2), which also suggests a sharp interface between TmIG and substrate23. The reduction of the MS at room temperature is attributed to finite size effect, strong thermal fluctuation and strong surface modification effect in ultrathin magnetic films24,25,26. Following ref. 25, we extract the critical exponents β for magnetic phase transitions in these TmIG thin films using temperature dependence of magnetic moment (M–T). The M–T curves follow the M = M0(1 − T/TC)β (Fig. 1d), where zero-temperature magnetic moment (M0) and Curie temperature (TC) are fitting parameters. The tTmIG-dependent β is better illustrated using log–log plots as shown in Fig. 1e and the results are summarized in Fig. 1f. We see a clear increase of β from 0.16 ± 0.06 to 0.42 ± 0.02 when the tTmIG increases from 3.2 to 15 nm, where the uncertainty is coming from the fitting. This increase of β suggests a dimensional crossover from two-dimension-like to three-dimension-like magnetism since 2D Ising model and 3D Heisenberg model predict β to be 0.125 and 0.365, respectively26,27. The dimensional crossover happens at around 6 nm, which is one order of magnitude larger than the typical transition thickness around 1 nm for magnetic metals25,26,27. In the following sections, we point out that the reduction of MS due to dimensional crossover has a major influence on the magnitude of the SOT and switching efficiency, which has been neglected in the previous experiments.
SOT measurement
To perform resistance, SOT, and CIMS measurements, we fabricate W(5 nm)/TmIG(tTmIG) thin films into Hall bar devices (Fig. 2a). By using four-probe resistance measurements in different Hall bar devices, we determine the W resistivity to be 155 ± 15 µΩ·cm, where the uncertainty is estimated from the multiple (>20) device measurements. According to ref. 19, pure α-W has resistivity around 20 µΩ·cm, and 6 nm-thick W with mixed α- and β-phases has a resistivity as high as 170 µΩ·cm. So, most likely, our 5 nm-thick W thin films have mixed α- and β-phases. The AHR in the W/TmIG is accurately determined by the sharp anomalous Hall hysteresis at low fields (Fig. 2b). The transverse planar Hall resistance (PHR) accompanying the longitudinal SMR is measured by rotating the magnetization in the xy-plane (Fig. 2c). The observation of sizeable AHR and PHR (SMR) indicates that there is a significant spin current being transmitted across the W/TmIG interface or a sizable spin mixing conductance11 (see Supplementary Note 3).
We quantify ξDL by using the second-harmonic analysis of both AHR and PHR (RAHE and RPHE)20,21. The second-harmonic Hall resistance (\(R_{\mathrm{H}}^{2\omega }\)) in a single domain subjected to an in-plane magnetic field can be written as21,28
where HK and Hext are perpendicular magnetic anisotropy effective field and in-plane external field, respectively. In Eq. (1), \(R_{{\mathrm{FL}}}^{2\omega }\) and \(R_{{\mathrm{DL}}}^{2\omega }\) are the peak values of cos 2φsin φ and sin φ components in \(R_{\mathrm{H}}^{2\omega }\), which are field-like SOT and damping-like SOT contributions, respectively. HFL and HDL are the current-induced field-like and damping-like effective fields, respectively. For example, when the Hext = 2500 Oe, we observe significant contributions from both damping-like and field-like SOTs, as reflected by the cos 2φsin φ and sin φ angle dependencies (see Fig. 2d and Supplementary Note 4). According to Eq. (1), slopes of linear fits to the \(R_{{\mathrm{DL}}}^{2\omega }\) as a function of 1/(Hext − HK) (Fig. 2e) give the information about HDL, and the intercepts are the spin Seebeck resistances (or voltages), which is field-independent in the single domain case (see Eq. (1))21,29.
We calculate ξDL using \(\xi _{{\mathrm{DL}}} = \frac{{2eM_{\mathrm{S}}t_{{\mathrm{TmIG}}}H_{{\mathrm{DL}}}}}{{\hbar J_{{\mathrm{ac}}}}}\)6, where e is the electron charge, ħ is the reduced Planck constant, and Jac is the applied current density. We observe a characteristic increase of ξDL as tTmIG increases with a saturation length of 10 nm (see Fig. 2f). Similarly, previous experiments have revealed a saturation length around 1 nm in FM heterostructures18,30,31. This saturation length is very close to the measured penetration depth of transverse spin current for FMs using spin pumping technique32,33,34. Thus, the saturation length has been interpreted as an indicator of penetration depth33,34. However, for our MI TmIG thin films, the scenario becomes complex since the electron spin cannot directly tunnel into the MI and the magnetism of MI thin films is strongly dependent on the MI thickness (Fig. 1). Note that the SOT efficiency (ξDL~0.02) in our W/TmIG (≥9 nm) devices is smaller than that in β-W/CoFeB (ξDL~0.3)19. There are two possible reasons. First, our W thin films are in mixed phases, which have a smaller spin Hall angle. Second, the material interfaces in W/magnetic metal and W/MI bilayers could be very different17, which requires further investigations.
SOT switching
After quantifying the SOT efficiency, we perform the CIMS experiments for W/TmIGs with different tTmIG. The switching is achieved in all devices with tTmIG up to 15 nm and the switching phase diagrams are summarized in Fig. 3a. In the presence of an external field along the +y direction, a sufficiently large charge current along the +y direction will cause magnetization (AHR) switching from the +z direction to the −z direction (negative to positive). The required amount of charge current to flip the magnetization decreases as the external field increases. When we apply a sufficiently large charge current along the −y direction while keeping the external field along the +y direction, the magnetization (AHR) is switched from the −z direction to the +z direction (positive to negative) (upper panels in Fig. 3b, c). For the same current direction, the switching direction is opposite when we reverse the external field direction (lower panels in Fig. 3b, c). All of the above facts agree with the picture of SOT-driven magnetization switching. Note that the switching current density is as low as 6 × 1010 A/m2 for the W (5 nm)/TmIG (9.6 nm) (Fig. 3b), which is three times smaller than the Pt (5 nm)/TmIG (8 nm) case15. This suggests that W enables more energy efficient magnetization switching.
The switching direction driven by current-induced SOTs is consistent with the sign of the spin Hall angle of W, and it is opposite to that in the Pt/TmIG bilayer15. Therefore, our work strongly suggests the dominant role of the SHE in the generation of SOTs and CIMS in HM/MI bilayers. However, we do notice that there could be an interfacial Rashba–Edelstein effect at the W/TmIG interface contributing to the SOTs by comparative analyses of SOTs and SMR (AHR) (see Supplementary Note 5).
To quantitatively compare the switching efficiency of W/TmIG devices with different tTmIG, we define an effective switching efficiency as \(\eta = \frac{{2eM_{\mathrm{S}}t_{{\mathrm{TmIG}}}H_{\mathrm{P}}}}{{\hbar J_{{\mathrm{sw}}}(H_{\mathrm{y}} \to 0)}}\)35, where HP is the domain wall depinning field estimated from the coercive field (see Supplementary Note 6) and Jsw(Hy → 0) is the zero-field limit of current density in the switching phase diagram. This formula is chosen because the CIMS is achieved through domain nucleation and domain wall motion in the Hall bar devices due to the large scale of our Hall bar devices, of which the channel width is 20 µm36. We observe a dramatic increase of η with tTmIG (Fig. 3d), for which we consider two reasons. First, the ξDL increases with tTmIG, which means that the same amount of charge current in the W layer generates stronger damping-like SOT on the TmIG layer. Thus, the increase of ξDL contributes to a lower Jsw and thus a larger η. Second, the Joule heating effect becomes much more significant when a larger charge current is applied, which is the case for switching a thicker TmIG. Joule heating causes reduction of thermal stability through decreasing the MS and HP; these two values will be smaller than those measured at the low current limit. Therefore, the MS and HP used to calculate η are overestimated, leading to a larger η.
Discussion
Here, we discuss the mechanism for the MI thickness dependence of ξDL. We propose that ξDL depends on MS when MS of the thin films is well below the corresponding bulk value. The Landau–Lifshitz–Gilbert equation in the presence of damping-like SOT can be written as
where \(\hat m\) is the unit vector of magnetization, \(\hat \sigma\) is the unit vector of current-induced spin polarization, γ is the gyromagnetic ratio, α is the Gilbert damping, tM is the thickness of the magnetic layer, JC is the charge current density, and \(\vec H_{{\mathrm{eff}}}( = \vec H_{\mathrm{K}} + \vec H_{{\mathrm{ext}}})\) is the total effective magnetic field acting on the magnetization. The last term on the right-hand side of Eq. (2) arises due to the absorption of transverse spin current by the magnet, which is referred to as the current-induced damping-like (dissipative) SOT. Its strength is parameterized by dimensionless efficiency parameters ξDL. The origin of the SOT can be understood in a simple microscopic picture as follows. A charge current at the HM and ferromagnet interface induces an accumulation of spin density, \(\rho \hat \sigma\), due to the finite spin-orbit interaction (for example, by SHE or Rashba–Edelstein effect). Here, ρ is the magnitude of the spin density, which is proportional to the strength of the spin-orbit interaction. This spin density interacts with the ferromagnet via exchange interaction, of the form \(U_{{\mathrm{ex}}} \sim \rho M_{\mathrm{S}}\hat m \cdot \hat \sigma\), enabling the absorption of the spin current by the ferromagnet. In the perturbative treatment, the spin current absorbed by the ferromagnet can be obtained up to second order in the exchange interaction to yield the damping-like SOT with \(\xi _{{\mathrm{DL}}}\sim M_{\mathrm{S}}^2\)37. The positive correlation between ξDL and MS is referred as the MS-effect; it has also been theoretically studied in the frame of spin pumping effect (in Appendix B of ref. 38), which is the Onsager reciprocal process of the spin torque effect. The increase of spin mixing conductance with MS is consistent with the calculation from first principles39 when the surface modification effect presents in the ultrathin regime26.
Our experiments are the demonstrations of the MS-effect; we show that as the thickness increases, the SOT efficiency significantly increases with MS in the low MS-regime (see Fig. 4), which is in qualitative agreement with the MS-effect. Also, we show that as the temperature decreases, the SOT efficiency increases with MS, due to suppression of thermal fluctuations (see Supplementary Note 7). Intuitively, as the magnetic moment density (MS) increases, the interfacial exchange interaction is enhanced, which allows more spin current to pass through the interface. As the thickness increases, the SOT efficiency saturates earlier than MS, around half of the bulk magnetization (60 emu/cm3), which suggests that the SOT is determined by the local magnetization that is saturated at a smaller thickness than the global magnetization MS. Our experiments show the need for further investigation of the interaction between ultrathin magnetic films and HMs, which would include the spin physics of dimensional crossover.
In summary, we have systematically studied the dimensional crossover of magnetism and its effect on SOTs in ultrathin MI films with perpendicular magnetic anisotropy. The characteristic increase of SOT efficiency with the MI thickness can be understood from the enhancement of magnetic moment density and the suppression of thermal fluctuations. In addition, we have realized CIMS in W/TmIG devices with tTmIG up to 15 nm. The switching current density for W/TmIG devices is lower or comparable with these for HM/FM despite the fact that the saturated ξDL is estimated to be only around 0.02 at this stage, which is much less than the 0.3 that is estimated for W in W/CoFeB bilayers19. Further improvement of the ξDL could be done by spin mixing conductance matching40 and surface treatment41. Our results presented here show the great potential of ultrathin MI-based spintronics.
Methods
Materials growth and characterization
All TmIG(111) films were grown on Nd3Ga5O12(111) by pulsed laser deposition13 before transferring to a magnetron sputtering chamber in the ambient condition. At room temperature, we deposited a 5 nm-thick W layer on top of TmIG followed by subsequent deposition of MgO (2 nm)/TaOx (3 nm) layers to protect W from oxidization. Magnetization hysteresis loops as a function of an out-of-plane magnetic field were measured by a vibrating sample magnetometer and a superconducting quantum interference device. The nominal thin film area is 5 × 5 mm2.
Devices fabrication and characterization
The films were patterned into Hall bar devices (Fig. 2a) by using standard photolithography and dry etching for the resistance, SOT, and switching measurements. The channel width is 20 µm, and the distance between two neighboring Hall contacts is 26 µm. We measured the second-harmonic Hall resistance by applying Iac,r.m.s = 1 mA (Jac,r.m.s = 1010 A/m2) with a frequency ω/2π = 195.85 Hz. The magnetic field and angle controls were done in a physical properties measurement system. The CIMS experiments were performed in the ambient environment by applying a pulse current with 5 ms pulse width and reading Hall voltage subsequently.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
References
Kajiwara, Y. et al. Transmission of electrical signals by spin-wave interconversion in a magnetic insulator. Nature 464, 262 (2010).
Bauer, G. E., Saitoh, E. & van Wees, B. J. Spin caloritronics. Nat. Mater. 11, 391 (2012).
Uchida, K. et al. Observation of the spin Seebeck effect. Nature 455, 778 (2008).
Wu, M.-Z. & Hoffmann, A. Recent Advances in Magnetic Insulators—From Spintronics to Microwave Applications (Academic Press, 2013).
Miron, I. M. et al. Perpendicular switching of a single ferromagnetic layer induced by in-plane current injection. Nature 476, 189 (2011).
Liu, L. et al. Spin-torque switching with the giant spin Hall effect of tantalum. Science 336, 555 (2012).
Qiu, X. et al. Spin-orbit-torque engineering via oxygen manipulation. Nat. Nanotechnol. 10, 333 (2015).
Yu, G. et al. Switching of perpendicular magnetization by spin-orbit torques in the absence of external magnetic fields. Nat. Nanotechol. 9, 548 (2014).
Liu, L., Lee, O. J., Gudmundsen, T. J., Ralph, D. C. & Buhrman, R. A. Current-induced switching of perpendicularly magnetized magnetic layers using spin torque from the spin Hall effect. Phys. Rev. Lett. 109, 096602 (2012).
Nakayama, H. et al. Spin Hall magnetoresistance induced by a nonequilibrium proximity effect. Phys. Rev. Lett. 110, 206601 (2013).
Chen, Y.-T. et al. Theory of spin Hall magnetoresistance. Phys. Rev. B 87, 144411 (2013).
Hahn, C. et al. Comparative measurements of inverse spin Hall effects and magnetoresistance in YIG/Pt and YIG/Ta. Phys. Rev. B 87, 174417 (2013).
Tang, C. et al. Anomalous Hall hysteresis in Tm3Fe5O12/Pt with strain-induced perpendicular magnetic anisotropy. Phys. Rev. B 94, 140403(R) (2016).
Li, P. et al. Spin-orbit torque-assisted switching in magnetic insulator thin films with perpendicular magnetic anisotropy. Nat. Commun. 7, 12688 (2016).
Avci, C. O. et al. Current-induced switching in a magnetic insulator. Nat. Mater. 16, 309 (2017).
Li, J. et al. Deficiency of the bulk spin Hall effect model for spin-orbit torques in magnetic-insulator/heavy-metal heterostructures. Phys. Rev. B 95, 241305(R) (2017).
Zhang, W., Han, W., Jiang, X., Yang, S.-H. & Parkin, S. S. P. Role of transparency of platinum–ferromagnet interfaces in determining the intrinsic magnitude of the spin Hall effect. Nat. Phys. 11, 496 (2015).
Pai, C.-F., Ou, Y., Vilela-Leão, L. H., Ralph, D. C. & Buhrman, R. A. Dependence of the efficiency of spin Hall torque on the transparency of Pt/ferromagnetic layer interfaces. Phys. Rev. B 92, 064426 (2015).
Pai, C.-F. et al. Spin transfer torque devices utilizing the giant spin Hall effect of tungsten. Appl. Phys. Lett. 101, 122404 (2012).
Garello, K. et al. Symmetry and magnitude of spin-orbit torques in ferromagnetic heterostructures. Nat. Nanotechnol. 8, 587 (2013).
Avci, C. O. et al. Interplay of spin-orbit torque and thermoelectric effects in ferromagnet/normal-metal bilayers. Phys. Rev. B 90, 224427 (2014).
Paoletti, A. Physics of Magnetic Garnets (North-Holland Publishing Company, 1978).
Tang, C. et al. Above 400-K robust perpendicular ferromagnetic phase in a topological insulator. Sci. Adv. 3, e1700307 (2017).
Zhang, R. & Willis, R. F. Thickness-dependent Curie temperatures of ultrathin magnetic films: effect of the range of spin-spin interactions. Phys. Rev. Lett. 86, 2665 (2001).
Huang, F., Kief, M. T., Mankey, G. J. & Willis, R. F. Magnetism in the few-monolayers limit: a surface magneto-optic Kerr-effect study of the magnetic behavior of ultrathin films of Co, Ni, and Co–Ni alloys on Cu(100) and Cu(111). Phys. Rev. B 49, 3962 (1994).
Vaz, C. A. F., Bland, J. A. C. & Lauhoff, G. Magnetism in ultrathin film structures. Rep. Prog. Phys. 71, 056501 (2008).
Li, Y. & Baberschke, K. Dimensional crossover in ultrathin Ni(111) films on W(110). Phys. Rev. Lett. 68, 1208 (1992).
Shao, Q. et al. Strong Rashba–Edelstein effect-induced spin-orbit torques in monolayer transition metal dichalcogenide/ferromagnet bilayers. Nano Lett. 16, 7514 (2016).
Uchida, K. et al. Observation of longitudinal spin-Seebeck effect in magnetic insulators. Appl. Phys. Lett. 97, 172505 (2010).
Kim, J. et al. Layer thickness dependence of the current-induced effective field vector in Ta|CoFeB|MgO. Nat. Mater. 12, 240 (2013).
Pai, C.-F., Mann, M., Tan, A. J. & Beach, G. S. D. Determination of spin torque efficiencies in heterostructures with perpendicular magnetic anisotropy. Phys. Rev. B 93, 144409 (2016).
Ghosh, A., Auffret, S., Ebels, U. & Bailey, W. E. Penetration depth of transverse spin current in ultrathin ferromagnets. Phys. Rev. Lett. 109, 127202 (2012).
Qiu, X. et al. Enhanced spin-orbit torque via modulation of spin current absorption. Phys. Rev. Lett. 117, 217206 (2016).
Ou, Y., Pai, C.-F., Shi, S., Ralph, D. C. & Buhrman, R. A. Origin of fieldlike spin-orbit torques in heavy metal/ferromagnet/oxide thin film heterostructures. Phys. Rev. B 94, 140414(R) (2016).
Lee, O. J. et al. Central role of domain wall depinning for perpendicular magnetization switching driven by spin torque from the spin Hall effect. Phys. Rev. B 89, 024418 (2014).
Yu, G. et al. Magnetization switching through spin-Hall-effect-induced chiral domain wall propagation. Phys. Rev. B 89, 104421 (2014).
Bender, S. A. & Tserkovnyak, Y. Interfacial spin and heat transfer between metals and magnetic insulators. Phys. Rev. B 91, 140402(R) (2015).
Ohnuma, Y., Adachi, H., Saitoh, E. & Maekawa, S. Enhanced dc spin pumping into a fluctuating ferromagnet near T C. Phys. Rev. B 89, 174417 (2014).
Jia, X., Liu, K., Xia, K. & Bauer, G. E. W. Spin transfer torque on magnetic insulators. Europhys. Lett. 96, 17005 (2011).
Du, C., Wang, H., Yang, F. & Hammel, P. C. Enhancement of pure spin currents in spin pumping Y3Fe5O12/Cu/metal trilayers through spin conductance matching. Phys. Rev. Appl. 1, 044004 (2014).
Jungfleisch, M. B., Lauer, V., Neb, R., Chumak, A. V. & Hillebrands, B. Improvement of the yttrium iron garnet/platinum interface for spin pumping-based applications. Appl. Phys. Lett. 103, 022411 (2013).
Acknowledgements
We acknowledge helpful discussions with Sadamichi Maekawa, Chi-Feng Pai, Wei Zhang, Yi Li, Ke Xia, Yongxi Ou, and Can Onur Avci. This work is supported as part of the Spins and Heat in Nanoscale Electronic Systems (SHINES), an Energy Frontier Research Center funded by the US Department of Energy (DOE), Office of Science, Basic Energy Sciences (BES), under Award # DE-SC0012670. Q.S., G.Y., A.N., S.A.R., P.U., Q.L.H., L.P., Y.T., and K.W. are also very grateful to the support from the Function Accelerated nanoMaterial Engineering (FAME) Center and Center for Spintronic Materials, Interfaces and Novel Architectures (C-SPIN), two of six centers of Semiconductor Technology Advanced Research network (STARnet), a Semiconductor Research Corporation (SRC) program sponsored by Microelectronics Advanced Research Corporation (MARCO) and Defense Advanced Research Projects Agency (DARPA). G.Y. acknowledges the financial support from the National Natural Science Foundation of China (NSFC)–Science Foundation Ireland (SFI) Partnership Programme [Grant No. 51861135104] and the 1000 Youth Talents Program.
Author information
Authors and Affiliations
Contributions
Q.S. and G.Y. conceived the project. C.T., Y.L. and J.X.L. grew the thin films, performed the film characterizations and magnetic measurements. Q.S. and P.Z. performed the SOT measurements. Q.S., G.Y., C.H. and P.Y. performed the resistance measurements. Q.S, C.T. and G.Y. analyzed the transport data. Q.S., P.Z., G.Y. and C.H. performed the switching measurements. A.N. and C.Z. fabricated the Hall bar devices. P.U., S.K. and Y.T. proposed the MS-effect. All authors contributed to the discussion. Q.S., G.Y., C.T, J.S. and K.L.W. wrote the manuscript with the input from all other authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Shao, Q., Tang, C., Yu, G. et al. Role of dimensional crossover on spin-orbit torque efficiency in magnetic insulator thin films. Nat Commun 9, 3612 (2018). https://doi.org/10.1038/s41467-018-06059-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-06059-7
- Springer Nature Limited
This article is cited by
-
Magnetoresistive detection of perpendicular switching in a magnetic insulator
Communications Physics (2024)
-
Electrical detection of spin pumping in van der Waals ferromagnetic Cr2Ge2Te6 with low magnetic damping
Nature Communications (2023)
-
Strong variation of spin-orbit torques with relative spin relaxation rates in ferrimagnets
Nature Communications (2023)
-
Current-induced switching of proximity-induced ferromagnetic surface states in a topological insulator
Nature Communications (2021)
-
Interfacial Dzyaloshinskii-Moriya interaction arising from rare-earth orbital magnetism in insulating magnetic oxides
Nature Communications (2020)