Abstract
Current-induced spin-orbit torques (SOTs) are of interest for fast and energy-efficient manipulation of magnetic order in spintronic devices. To be deterministic, however, switching of perpendicularly magnetized materials by SOT requires a mechanism for in-plane symmetry breaking. Existing methods to do so involve the application of an in-plane bias magnetic field, or incorporation of in-plane structural asymmetry in the device, both of which can be difficult to implement in practical applications. Here, we report bias-field-free SOT switching in a single perpendicular CoTb layer with an engineered vertical composition gradient. The vertical structural inversion asymmetry induces strong intrinsic SOTs and a gradient-driven Dzyaloshinskii–Moriya interaction (g-DMI), which breaks the in-plane symmetry during the switching process. Micromagnetic simulations are in agreement with experimental results, and elucidate the role of g-DMI in the deterministic switching processes. This bias-field-free switching scheme for perpendicular ferrimagnets with g-DMI provides a strategy for efficient and compact SOT device design.
Similar content being viewed by others
Introduction
Spin-orbit torque (SOT) is a leading contender as a fast and low-power method to manipulate magnetic order in spintronic devices, particularly for artificial intelligence and high-performance computing applications where high-speed on-chip memory is required1,2,3,4. SOT switching of ferrimagnetic (FIM) materials, in particular, is of great current interest5,6,7,8,9. FIMs exhibit the exchange-dominated high-frequency (sub-terahertz) dynamics of antiferromagnets, which can result in high switching speed5,6,7, while avoiding the difficulties of controlling domain size commonly encountered in antiferromagnets4. They can also utilize the relatively straightforward electrical readout methods available in ferromagnetic material systems (due to their non-zero magnetization)7,8,9. Hence, FIMs are promising as near-term candidates for practical high-performance SOT devices.
Typically, for memory applications where information is encoded in the direction of the magnetization in magnets with perpendicular magnetic anisotropy (PMA), SOT switching is realized in a non-magnet/ferromagnet (NM/FM) or NM/FIM heterostructure with the assistance of an external in-plane magnetic field Hex along the current direction1,2,10,11,12. SOTs originating from the spin Hall effect (SHE) in the NM (e.g., heavy metals2,10 or topological insulators11,12) or from the Rashba effect1,13 at the NM/FM interface can drive the adjacent magnetization to switch, while Hex breaks the in-plane inversion symmetry and leads to a deterministic switching direction for a particular direction of the in-plane current.
The requirement of external Hex in switching, however, hinders the integration of SOT devices on semiconductor chips. Thus, mechanisms to break the in-plane (structural or magnetic) symmetry, instead of Hex, are being investigated to realize practical SOT memory devices13,14,15,16,17,18,19,20,21,22,23,24,25,26,27,28. To date, these have included in-plane exchange bias fields14,15,16, interlayer exchange coupling17,18, in-plane structural, composition, or interfacial oxidation asymmetry19,20,21,22,23,24,25, and combining multiple competing sources of spin torque in one device26,27,28. However, with the exception of methods combining more than one source of torque, these schemes all rely on breaking the static in-plane symmetry in the device. In many cases, this makes it difficult to build large arrays with uniform device properties on the same wafer.
Here we experimentally show, instead, that a structure featuring in-plane symmetry, along with inversion asymmetry only along the growth direction, can also exhibit deterministic switching due to the dynamic in-plane breaking of symmetry during the switching process, induced by the Dzyaloshinskii–Moriya interaction (DMI).
The DMI effect can induce spin textures (e.g., domain walls and skyrmions) with broken chiral symmetry29,30,31,32. Therefore, DMI has recently been theoretically proposed as a symmetry-breaking mechanism that, in combination with damping-like and field-like SOTs, may enable deterministic switching in the absence of an external field33,34,35. However, field-free deterministic switching due to the combined action of DMI and SOT has not been reported to date.
Our approach to engineer the required DMI is inspired by a recent work reporting a large bulk DMI in a rare-earth (RE)-transition-metal (TM) ferrimagnet (FIM), where a vertical composition gradient was brought about by the natural inhomogeneous elemental composition distribution in alloys with large thickness36. Here, in order to maximize the DMI, we instead engineer a vertical composition gradient in the FIM layer by depositing ultrathin individual layers with a varying RE/TM composition ratio, leading to a broken inversion symmetry along the growth direction. This results in a gradient-driven DMI (g-DMI) which has the same symmetry as interfacial DMI in previously studied NM/FIM and NM/FM systems, which, however, is present throughout the bulk of the FIM due to the continuous composition gradient.
In addition, as RE elements possess large spin-orbit coupling (SOC) due mainly to their 5d band37,38, they can generate spin-currents as large as those generated in nonmagnetic 5d metals such as Pt at the opposite end of the 5d metal series39. The 3d electrons of cobalt possess a much smaller SOC and the f electrons of Tb do not participate in the conduction. The combination of large spin-orbit-coupling and broken inversion symmetry generates Rashba interactions40, which give rise to current-induced Rashba spin polarizations and resulting spin currents41 which, in turn, can produce a SOT on the FIM magnetization, as discussed in the next section.
Using the combination of SOT and g-DMI effects, we demonstrate efficient field-free SOT magnetization switching in a single ferrimagnetic CoTb layer with a vertical composition gradient. Experiments and simulations indicate that this scheme can eliminate the need for NM and Hex simultaneously in the previously mentioned SOT switching systems. The field-free switching data are in agreement with micromagnetic simulations. Our work provides a pathway towards field-free SOT switching of perpendicular ferrimagnets which can potentially be scaled to large wafer size with good uniformity.
Results
Large SOT originating from the Tb composition gradient
As a ferrimagnetic alloy, in which RE elements and TM elements are coupled anti-ferromagnetically, CoTb can exhibit robust PMA in a wide composition range8,9. To investigate the exact composition range of PMA, a series of Al (2 nm)/Co1-aTba (6 nm)/Al (3 nm) films (see Fig. 1a) were deposited on thermally oxidized silicon substrates, with a being the concentration of Tb in the alloy. Here, Al was chosen due to its negligible SOT. CoTb was constructed by a co-sputtering process of Co and Tb at different powers to control the stoichiometry of the final CoTb layer. As shown in Fig. 1b, Co0.87Tb0.13 and Co0.56Tb0.44 were the most Co-rich and the most Tb-rich samples which provided good PMA properties in this heterostructure. In addition, by the fitting of the net saturation magnetization Ms dependence on composition, Co0.71Tb0.29 was determined as the magnetization compensation point at room temperature.
Guided by this information, samples with a vertical composition gradient were deposited next. As illustrated in Fig. 1c, the ferrimagnet consists of six layers of CoTb, each having a thickness of 1 nm. Here, we fixed the bottom layer composition as Co0.87Tb0.13, while the other five deposited layers followed a certain Tb composition step δ, resulting in a nominal gradient of δ per nanometer. Hence, their composition can be expressed as Co0.87-nδTb0.13+nδ, where n = 1, 2, 3, 4, 5. Figure 1d shows that increasing the composition gradient leads to a decrease of the overall Ms of the sample, which corresponds to the Co-rich part tendency in Fig. 1b, i.e., increasing the average Tb composition makes the sample approach the magnetic compensation point8,9. When δ arrives at 0.07, the sample is nearly compensated (Ms < 50 emu/cc), while the sample starts to show an in-plane magnetization component when exceeding δ = 0.07. We thus only discuss gradients δ in the range from 0 to 0.07. To verify the existence of and quantify the composition gradient in our samples, high-resolution cross-sectional scanning transmission electron microscopy (STEM) and energy-dispersive X-ray spectroscopy (EDS) were performed on the sample with δ = 0.07. Figure 1e shows the structure of the ordered layers in the sample. No obvious crystal structure is observed, revealing the amorphous nature of the CoTb layer as expected. EDS curves versus the thickness direction in Fig. 1f exhibit a prominent inhomogeneous spatial distribution of Co and Tb elements. With the measured position penetrating to the substrate, Co (Tb) intensity shows an increasing (decreasing) tendency, which corresponds well with the designed structure in Fig. 1c.
To perform electrical measurements, the films were fabricated into Hall bar devices with a width of 10 μm by conventional lithography and ion milling. The inset in Fig. 2a displays the device as well as the measurement contact configurations. Based on the anomalous Hall effect resistance (RAHE) measurements, all samples show clear PMA consistent with the film-level magnetometry results. The case of δ = 0.06 is shown as an example in Fig. 2a. Note that with δ varying from 0.00 to 0.07, the RAHE loop does not change its polarity, revealing that all samples remain Co-rich overall.
Standard harmonic measurements were then carried out in a large field range to determine the SOT efficiency as well as the effective spin Hall angle of each sample42,43. When an alternating current j = j0sin(ωt) is applied along the x axis, the SOT-induced alternating effective field will generate magnetization oscillations around the equilibrium position, which contributes to the rise of a second-harmonic Hall resistance R2ω. In the regime where the in-plane magnetic field \(\left|{H}_{x}\right|\) exceeds the magnetic anisotropy field Hk, R2ω can be described by the equation42,43
where HDL and Roffset are the damping-like SOT effective field and resistance offset, respectively. Figure 2b, c plot the first harmonic resistance Rω and R2ω of the sample with δ = 0.06. By fitting Fig. 2c with Eq. (1), the SOT efficiency ξ = HDL/jCoTb, where jCoTb is the corresponding current density in the CoTb layer, is determined to be 3.2 ± 0.3 Oe/(1010 A/m2). The calculation of jCoTb can be found in Supplementary Note S1.
We then calculated the damping-like effective spin Hall angle by θDL = 2eMstCoTbHDL/ℏjCoTb, where tCoTb is the CoTb layer thickness. The θDL values of samples with different gradients δ are summarized in Fig. 2d. Interestingly, θDL shows a clear increasing tendency as a function of δ. At δ = 0.07, the maximum value of θDL is determined to be 0.061 ± 0.006, which is comparable to the reported effective spin Hall angle in Pt10.
The appearance of this sizeable SOT is a consequence of the combined large spin-orbit-coupling and broken inversion symmetry in our structure, which give rise to current-induced Rashba spin polarizations and resulting spin currents40,41. The breaking of the inversion symmetry in a magnetic layer can result from nonsymmetric interfaces, as in the classical model of Manchon and Zhang44, or from composition gradients as in our samples, which can be called “g-Rashba” by analogy with “g-DMI” coined above for DMI. In a magnetic or ferrimagnetic material, the Rashba spin polarization and the resulting spin currents present a combination of terms of spin anomalous hall effect (SAHE) symmetry (spin-polarized along the axis of the magnetization, M) and SHE symmetry (spin-polarized along the y axis for current along x and emission along z), see Note S1 in39 for Rashba-induced spin currents and the more general theory by Stiles and coworkers45,46.
The SAHE term, polarized along with the magnetization M, cannot generate a torque on M. The SHE-like spin current in a magnetic layer can generate a Damping-Like (DL) spin transfer torque on M if there is a possible transfer of the spins carried by this current, either from the magnetic layer to outside41,47 or between different parts of the magnetic layer. Spin transfer from the magnetization of the CoTb layer to outside cannot work in our samples because the CoTb layer is inserted between two thin layers of the light element and weak absorber Al. In contrast, the asymmetric distribution of CoTb layers of different compositions, with higher 5d concentrations and larger Rashba spin polarization at the top, can give rise to unbalanced spin transfers between different parts of the sample. In our samples, there should be some imbalance between the transfer to the bottom magnetization of the larger downward spin currents jCoTbθDL,top emitted from top and the transfer to the top of the smaller upward spin currents jCoTbθDL,bottom emitted with opposite spin polarization from the bottom. The final torque is difficult to predict precisely because it will depend on how the gradient of Tb concentration is reflected in the variation of both the Rashba interaction and other parameters, such as the spin dephasing length, controlling the proportion of spin transfer. In rough approximation, the DL torque should correspond to the transfer of a spin current of the order of jCoTb(θDL,top − θDL,bottom) (the bracket corresponds to an effective spin Hall angle θDL which, as expected, is zero if the layer is homogeneous).
Field-free switching of perpendicular CoTb by SOT and gradient-driven DMI
We next performed SOT-induced magnetization switching experiments on the CoTb samples with a vertical composition gradient. Following the measurement strategy shown in Fig. 3a, successive write current pulses with a duration of 0.1 ms (orange bars, current from positive to negative and then back to positive) were injected in the x axis of the Hall bar, while a small sensing current of 0.1 mA (blue triangles) was applied after each pulse to detect the magnetization state via RAHE. Figure 3b shows RAHE as a function of the injected write current density jCoTb in the sample with δ = 0.07, under a bias field Hex along the x axis varying from 100 Oe to −100 Oe. The successful magnetization switching verifies the existence of intrinsic SOTs in the CoTb with composition gradient. Meanwhile, the current-driven RAHE shows a similar amplitude to the field-driven RAHE, revealing that a nearly complete switching of the CoTb is achieved by the current. We define the critical switching current jc as the value of jCoTb where half of the maximum resistance change is achieved. From Fig. 3b, the jc of this 6 nm thick sample was determined to be around 9 × 1010 A/m2. An analysis of the Hex dependence of jc can be found in Supplementary Note S2.
Supplementary Note S8 compares the SOT switching efficiency of these CoTb gradient samples—defined as jc/(t ∙ Keff), where t is the magnetic film thickness and Keff is its effective perpendicular anisotropy energy density— with: (i) previous reports of SOT switching of ferrimagnetic CoTb films (in the presence of a bias magnetic field)9,48,49,50, and (ii) field-free deterministic SOT switching of perpendicular ferromagnetic layers15,19,21,27. In all cases, the CoTb samples with vertical composition gradient show the best SOT switching efficiency.
As expected in the SOT framework, the switching loops show opposite switching polarities under ±100 Oe. More interestingly, a full SOT switching loop in the absence of Hex is observed as well. This field-free switching loop has the same polarity as the cases with a positive Hex. In addition, almost no switching signal is detected in this sample when Hex = −20 Oe. These results indicate the existence of an effective internal field that participates in the SOT switching process. We attribute this effective field to the g-DMI in the CoTb layer36.
To quantify the g-DMI-induced effective field HDMI in our sample, a method based on the magnetic droplet nucleation model was used36,51. As depicted in the inset of Fig. 3c, the hysteresis loop was measured by sweeping the magnetic field at an angle θ with respect to the z-axis. Figure 3c illustrates the magnetization switching curves in the negative field range with different angles. If we denote the magnetic field where the magnetization is switched from the “up” state to the “down” state by Hsw, then, the coercive field Hc and the accompanying in-plane field Hn can be expressed by Hswcosθ and Hswsinθ, respectively.
Figure 3d shows the measured Hc as a function of Hn. As described in earlier works, the curve shows a clear plateau, and Hc starts to decrease after Hn passes a threshold value. This threshold Hn corresponds to HDMI36,51. In this manner, HDMI was determined to be around 23 Oe in the 6 nm CoTb layer with δ = 0.07. We note that this value is very close to the absolute value of applied in-plane Hex (−20 Oe, see Fig. 3b) where magnetization switching vanishes, which is consistent with the hypothesis that the g-DMI-induced effective field is responsible for the observed field-free switching33,34,35.
To investigate the role of the composition gradient on the switching behavior in more detail, SOT switching experiments were also performed in the following samples: (A) 6 nm thick CoTb with δ = 0.06 per 1 nm; (B) 9 nm thick CoTb with δ = 0.07 per 1.5 nm; (C) 4.2 nm thick CoTb with δ = 0.07 per 0.7 nm. Note that samples A and B have a smaller slope of the composition gradient compared to the previously discussed samples (where we had a 6 nm thick CoTb film with δ = 0.07 per 1 nm), due to the smaller value of δ and the larger overall CoTb thickness, respectively. On the other hand, the slope of the composition gradient is increased in sample C, due to the reduced overall CoTb thickness for the same value of δ.
The results are shown in Supplementary Notes S3, S4, and S5. All the samples exhibited clear deterministic switching loops in the absence of Hex, and the value of Hex where switching vanished corresponded well to the measured value of HDMI. This is in agreement with the fact that the g-DMI is responsible for the in-plane symmetry-breaking and zero-field switching observed in these samples. As expected, the jc values of samples A and B (>10 × 1010 A/m2) were larger than that in the 6 nm thick CoTb layer with δ = 0.07. On the contrary, a smaller jc (~7.5 × 1010 A/m2), as well as a higher HDMI (~40 Oe), were achieved in sample C, as expected based on its steeper composition gradient.
In addition, we also studied the role of device orientation, device location on the wafer, and applied current history in the field-free SOT switching. These experiments are described in Supplementary Notes S9 and S10. They show that device orientation does not influence the field-free switching polarity, confirming that the switching is independent of conventional lateral asymmetry. Moreover, we found that the applied writing current history provides a training effect that determines the polarity of its subsequent current-induced switching loops. This behavior was consistent for multiple devices measured across different locations on a 100 mm wafer.
Switching behavior of a CoTb film with an inverse composition gradient
To further verify the origin of SOTs and g-DMI, we studied the SOT switching behavior in a 6 nm thick CoTb layer with an inverse composition gradient (δ = −0.07), i.e., Tb concentration decreasing from bottom to the top of the layers. The details of this sample are described in Fig. 4a, while Fig. 4b shows the obtained SOT switching curves of this sample under different Hex. The switching loops always show opposite polarity compared to those of the sample with δ = 0.07 (comparison of Figs. 4b and 3b). This indicates that the vertical broken symmetry directions in these two samples are opposite, confirming again that the SOTs in the CoTb layer truly originates from the vertical composition gradient.
SOT switching in the absence of Hex was also observed in this sample, and the zero-field loop exhibits a polarity similar to switching loops under negative Hex. In addition, the deterministic switching vanishes at a positive Hex of ~15 Oe. Both of these characteristics, which are determined by g-DMI in our field-free switching explanation, are opposite to the ones observed in the sample with δ = 0.07. Thus, we conclude that the inverse composition gradient also induces an HDMI with opposite sign compared to the previous case. The combination of the reversed sign of SOT compared to our reference device, along with the opposite sign of HDMI explains the field-free switching data of Fig. 4b and is consistent with the observations in Fig. 3b.
Modeling and simulations
To shed light on the underlying mechanism of this field-free switching phenomenon, we performed micromagnetic simulations. Our micromagnetic framework is based on a two-sublattice model strongly coupled through an exchange interaction41,52,53,54,55,56. Along with the exchange interaction, we also take into account the anisotropy, the DMI, and the torque exerted by SOT. Supplementary Note S6 provides details of the micromagnetic model. The g-DMI originates from the composition gradient along the z axis36 and therefore the symmetry breaking is, from a modeling point of view, similar to the case of interfacial DMI observed in other multilayer systems57,58,59.
To mimic the experimental setup (see Fig. 2a) we consider a cross geometry initially saturated along the +z direction. From this initial state, we apply an electric current for 20 ns (from ton,1 to toff,1), let the system relax for 12 ns more, and repeat the process with the opposite polarization of the current (from ton,2 to toff,2). Figure 5b shows the time evolution of the average z component of the magnetization for the first sublattice (black line) together with the timing of the two current pulses.
As observed in previous numerical studies33,34,35,53, the deterministic switching starts with the nucleation of a domain at the edge of the sample because of the magnetization tilting toward an in-plane direction imposed by the DMI boundary conditions (see Fig. 5a). In other words, the nucleation of a new domain at the edge is driven by the SOT applied to this in-plane component at the edge (Fig. 5c–e). The switching occurs via a strongly nonuniform magnetization pattern, given by the higher DW velocity in the edges as compared to the central region due to the combined effects of the DMI boundary conditions, the DMI, and exchange fields (Fig. 5f–h). After the current is switched off, the magnetization relaxes to the reversed uniform ground state (Fig. 5i–j). The same process is observed for the current pulses of opposite polarity (see Fig. S7 in Supplementary Note S7). To consider a more realistic memory device geometry, we also implemented similar simulations for a pillar with a diameter of 400 nm (see Fig. S8 in Supplementary Note S7). The main conclusions about the switching process are not affected when considering this pillar geometry.
Discussion
We have demonstrated a field-free DMI-SOT switching scheme in a thick perpendicular CoTb layer with a vertical composition gradient. The broken structural inversion symmetry along the growth direction induces both strong SOTs and g-DMI. Notably, this gradient-driven switching mechanism is promising to realize field-free switching under a relatively low current density and has the potential to be scalable to a large wafer size. The SOT switching efficiency is significantly better than in previous field-free SOT switching experiments in ferromagnets, as well as previous (field-assisted) SOT switching experiments in conventional CoTb layers without composition gradient. Given that the SOT in our structure originates within the bulk of the CoTb gradient film, it could in principle be further enhanced by interfacing with an appropriate heavy metal layer to provide additional interfacial SOT. Notably, since the g-DMI in our structure also originates from the composition gradient within the bulk, it does not impose any constraints on the choice of the heavy metal layer for interfacial SOT, thus providing freedom in device design. Finally, we note that large tunneling magnetoresistance (TMR) ratios have already been demonstrated in magnetic tunnel junctions based on FIMs60,61,62. Therefore, it is possible to integrate the CoTb gradient films presented here into SOT memory devices with TMR readout. Our findings go beyond the conventional paradigm of SOT-induced perpendicular magnetization switching with the assistance of external field and SOT sources and being applicable to ferrimagnets, pave the way towards the development of ultrafast SOT memory arrays.
Methods
Sample growth and characterization
A series of Al (2)/CoTb (6)/Al (3) (thickness in nm) stacks were deposited on thermally oxidized silicon substrates by DC and RF sputtering under a base pressure lower than 10−8 Torr. The composition of CoTb was controlled by setting the deposition power of Co and Tb targets. Vibrating sample magnetometry was used to quantify the magnetic properties of each sample. STEM and EDS characterizations were performed by a JEM-ARM200F microscope.
Device fabrication and electrical measurement
The films were fabricated into Hall bar devices of 10 μm width by optical lithography and ion milling techniques. For AHE and DMI measurements, DC current was applied along the x axis, while for SOT switching measurements, current pulses (0.1 ms width) were applied. A Hall probe was inserted in the probe station to detect the actual magnetic field values during measurement, thus guaranteeing the absence of any \({H}_{{ex}}\) contributions due to remanent fields. For harmonics measurements, two SR830 lock-in amplifiers were used to detect the first and second harmonic Hall voltage induced by an AC current with a frequency of 133.33 Hz.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
References
Miron, I. M. et al. Perpendicular switching of a single ferromagnetic layer induced by in-plane current injection. Nature 476, 189–193 (2011).
Liu, L. et al. Spin–torque switching with the giant spin Hall effect of tantalum. Science 336, 555–558 (2012).
Emori, S., Bauer, U., Ahn, S. M., Martinez, E. & Beach, G. S. Current-driven dynamics of chiral ferromagnetic domain walls. Nat. Mater. 12, 611–616 (2013).
Shi, J. et al. Electrical manipulation of the magnetic order in antiferromagnetic PtMn pillars. Nat. Electron. 3, 92–98 (2020).
Cai, K. et al. Ultrafast and energy-efficient spin–orbit torque switching in compensated ferrimagnets. Nat. Electron. 3, 37–42 (2020).
Siddiqui, S. A. et al. Current-induced domain wall motion in a compensated ferrimagnet. Phys. Rev. Lett. 121, 057701 (2018).
Kim, K. et al. Fast domain wall motion in the vicinity of the angular momentum compensation temperature of ferrimagnets. Nat. Mater. 16, 1187–1192 (2017).
Zheng, Z. et al. Enhanced spin-orbit torque and multilevel current-induced switching in W/Co-Tb/Pt heterostructure. Phys. Rev. Appl. 12, 044032 (2019).
Finley, J. & Liu, L. Spin-orbit-torque efficiency in compensated ferrimagnetic cobalt-terbium alloys. Phys. Rev. Appl 6, 054001 (2016).
Liu, L., Lee, O. J., Gudmundsen, T. J., Ralph, D. C. & Buhrman, R. A. Current-induced switching of perpendicularly magnetized magnetic layers using spin torque from the spin Hall effect. Phys. Rev. Lett. 109, 096602 (2012).
Han, J. et al. Room-temperature spin-orbit torque switching induced by a topological insulator. Phys. Rev. Lett. 119, 077702 (2017).
Zheng, Z. et al. Perpendicular magnetization switching by large spin orbit torques from sputtered Bi2Te3. Chin. Phys. B 29, 078505 (2020).
Cui, B. et al. Field-Free Spin-orbit torque switching of perpendicular magnetization by the Rashba interface. ACS Appl. Mater. Inter. 11, 39369–39375 (2019).
Oh, Y. W. et al. Field-free switching of perpendicular magnetization through spin-orbit torque in antiferromagnet/ferromagnet/oxide structures. Nat. Nanotechnol. 11, 878–884 (2016).
van den Brink, A. et al. Field-free magnetization reversal by spin-Hall effect and exchange bias. Nat. Commun. 7, 1–6 (2016).
Fukami, S., Zhang, C., DuttaGupta, S., Kurenkov, A. & Ohno, H. Magnetization switching by spin–orbit torque in an antiferromagnet–ferromagnet bilayer system. Nat. Mater. 15, 535–541 (2016).
Lau, Y. C. et al. Spin–orbit torque switching without an external field using interlayer exchange coupling. Nat. Nanotechnol. 11, 758–762 (2016).
Liu, Y., Zhou, B. & Zhu, J. G. J. Field-free magnetization switching by utilizing the spin Hall effect and interlayer exchange coupling of iridium. Sci. Rep. 9, 1–7 (2019).
Yu, G. et al. Switching of perpendicular magnetization by spin–orbit torques in the absence of external magnetic fields. Nat. Nanotechnol. 9, 548 (2014).
Razavi, A. et al. Deterministic spin-orbit torque switching by a light-metal insertion. Nano Lett. 20, 3703–3709 (2020).
Chen, T. Y., Chan, H. I., Liao, W. B. & Pai, C. F. Current induced spin-orbit torque and field-free switching in Mo-based magnetic heterostructures. Phys. Rev. Appl. 10, 044038 (2018).
Cao, Y. et al. Deterministic magnetization switching using lateral spin-orbit torque. Adv. Mater. 32, 1907929 (2020).
Luo, Z. et al. Chirally coupled nanomagnets. Science 363, 1435–1439 (2019).
You, L. et al. Switching of perpendicularly polarized nanomagnets with spin orbit torque without an external magnetic field by engineering a tilted anisotropy. Proc. Natl Acad. Sci. USA 112, 10310 (2015).
Wu, H. et al. Chiral symmetry breaking for deterministic switching of perpendicular magnetization by spin-orbit torque. Nano Lett. 21, 515–521(2020).
Ma, Q. et al. Switching a perpendicular ferromagnetic layer by competing spin currents. Phys. Rev. Lett. 120, 117703 (2018).
Cai, K. et al. Electric field control of deterministic current-induced magnetization switching in a hybrid ferromagnetic/ferroelectric structure. Nat. Mater. 16, 712–716 (2017).
Wang, M. et al. Field-free switching of a perpendicular magnetic tunnel junction through the interplay of spin–orbit and spin-transfer torques. Nat. Electron. 1, 582–588 (2018).
Dzialoshinskii, I. E. Thermodynamic theory of ‘weak’ ferromagnetism in antiferromagnetic substances. Sov. Phys. JETP 5, 1259–1272 (1957).
Moriya, T. Anisotropic super exchange interaction and weak ferromagnetism. Phys. Rev. 120, 91–98 (1960).
Je, S. G. et al. Asymmetric magnetic domain-wall motion by the Dzyaloshinskii–Moriya interaction. Phys. Rev. B 88, 214401 (2013).
Rößler, U. K., Bogdanov, A. N. & Pfleiderer, C. Spontaneous skyrmion ground states in magnetic metals. Nature 442, 797–801 (2006).
Chen, B., Lourembam, J., Goolaup, S. & Lim, S. T. Field-free spin-orbit torque switching of a perpendicular ferromagnet with Dzyaloshinskii–Moriya interaction. Appl. Phys. Lett. 114, 022401 (2019).
Wu, K., Su, D., Saha, R. & Wang, J. P. Deterministic field-free switching of a perpendicularly magnetized ferromagnetic layer via the joint effects of the Dzyaloshinskii–Moriya interaction and damping-and field-like spin–orbit torques: an appraisal. J. Phys. D. Appl. Phys. 53, 205002 (2020).
Dai, M. & Hu, J. M. Field-free spin–orbit torque perpendicular magnetization switching in ultrathin nanostructures. NPJ Comput. Mater. 6, 1–10 (2020).
Kim, D. H. et al. Bulk Dzyaloshinskii–Moriya interaction in amorphous ferrimagnetic alloys. Nat. Mater. 18, 685 (2019).
Burzo, E., Chioncel, L., Tetean, R. & Isnard, O. On the R 5d band polarization in rare-earth–transition metal compounds. J. Phys. Condens. Matter 23, 026001 (2010).
Campbell, I. A. Indirect exchange for rare earths in metals. J. Phys. F. Met. Phys. 2, L47 (1972).
Céspedes-Berrocal, D. et al. Current-induced spin torques on single GdFeCo magnetic layers. Adv. Mater. 33, 2007047 (2021).
Rashba, E. I. Properties of semiconductors with an extremum loop. I. Cyclotron and combinational resonance in a magnetic field perpendicular to the plane of the loop. Sov. Phys. Solid State 2, 1109 (1960).
Manchon, A. et al. Current-induced spin-orbit torques in ferromagnetic and antiferromagnetic systems. Rev. Mod. Phys. 91, 035004 (2019).
Fan, Y. et al. Magnetization switching through giant spin-orbit torque in a magnetically doped topological insulator heterostructure. Nat. Mater. 13, 699 (2014).
Schulz, T. et al. Effective field analysis using the full angular spin orbit torque magnetometry dependence. Phys. Rev. B 95, 224409 (2017).
Manchon, A. & Zhang, S. Theory of nonequilibrium intrinsic spin torque in a single nanomagnet. Phys. Rev. B 78, 212405 (2008).
Amin, V. P., Li, J., Stiles, M. D. & Haney, P. M. Intrinsic spin currents in ferromagnets. Phys. Rev. B 99, 220405 (2019).
Amin, V. P., Haney, P. M. & Stiles, M. D. Interfacial spin–orbit torques. J. Appl. Phys. 128, 151101 (2020).
Amin, V. P. & Stiles, M. D. Spin transport at interfaces with spin-orbit coupling: Phenomenology. Phys. Rev. B 94, 104420 (2016).
Zhang, R. Q. et al. Current-induced magnetization switching in a CoTb amorphous single layer. Phys. Rev. B 101, 214418 (2020).
Je, S. G. et al. Spin-orbit torque-induced switching in ferrimagnetic alloys: experiments and modeling. Appl. Phys. Lett. 112, 062401 (2018).
Wang, H. et al. Spin-orbit-torque switching mediated by an antiferromagnetic insulator. Phys. Rev. Appl. 11, 044070 (2019).
Kim, S. et al. Magnetic droplet nucleation with a homochiral Néel domain wall. Phys. Rev. B 95, 220402 (2017).
Hals, K. M., Tserkovnyak, Y. & Brataas, A. Phenomenology of current-induced dynamics in antiferromagnets. Phys. Rev. Lett. 106, 107206 (2011).
Sánchez-Tejerina, L. et al. Dynamics of domain-wall motion driven by spin-orbit torque in antiferromagnets. Phys. Rev. B 101, 014433 (2020).
Martínez, E., Raposo, V. & Alejos, Ó. Current-driven domain wall dynamics in ferrimagnets: Micromagnetic approach and collective coordinate’s model. J. Magn. Magn. Mater. 491, 165545 (2019).
Sánchez-Tejerina, L. et al. Unified framework for micromagnetic modeling of ferro-, ferri-, and antiferromagnetic materials at mesoscopic scale: domain wall dynamics as a case study. IEEE Magn. Lett. 11, 1–5 (2020).
Cutugno, F. et al. Micromagnetic understanding of switching and self-oscillations in ferrimagnetic materials. Appl. Phys. Lett. 118, 052403 (2021).
Heide, M., Bihlmayer, G. & Blügel, S. Dzyaloshinskii–Moriya interaction accounting for the orientation of magnetic domains in ultrathin films: Fe/W (110). Phys. Rev. B 78, 140403 (2008).
Martinez, E., Emori, S. & Beach, G. S. Current-driven domain wall motion along high perpendicular anisotropy multilayers: the role of the Rashba field, the spin Hall effect, and the Dzyaloshinskii–Moriya interaction. Appl. Phys. Lett. 103, 072406 (2013).
Tomasello, R. et al. Domain periodicity in an easy-plane antiferromagnet with Dzyaloshinskii-Moriya interaction. Phys. Rev. B 102, 224432 (2020).
Reza, A. K. & Roy, K. Fast switching in CoTb based ferrimagnetic tunnel junction. J. Appl. Phys. 126, 023901 (2019).
Bai, X. J. et al. Influence of the thickness of the FeCoGd layer on the magnetoresistance in FeCoGd-based spin valves and magnetic tunnel junctions. J. Phys. D: Appl. Phys. 41, 215008 (2008).
Jeong, J. et al. Termination layer compensated tunneling magnetoresistance in ferrimagnetic Heusler compounds with high perpendicular magnetic anisotropy. Nat. Commun. 7, 1–8 (2016).
Acknowledgements
This work was supported by a grant from the U.S. National Science Foundation, Division of Electrical, Communications and Cyber Systems (NSF ECCS-1853879), the National Natural Science Foundation of China (Grant no. 61971024 and 51901008), the International Mobility Project (Grant no. B16001) and National Key Technology Program of China (Grant no. 2017ZX01032101). This work was also supported by the National Science Foundation Materials Research Science and Engineering Center at Northwestern University (NSF DMR-1720319) and made use of its Shared Facilities at the Northwestern University Materials Research Center. This work also made use of the NUFAB facility of Northwestern University’s NUANCE Center, which has received support from the SHyNE Resource (NSF ECCS-1542205), the IIN, and Northwestern’s MRSEC program (NSF DMR-1720139). Z.Y.Z also acknowledges the support from the China Scholarship Council (No. 201906020022). G.F., L.S.T, and M.C. would like to acknowledge the contribution of the COST Action CA17123 “Ultrafast optomagneto-electronics for nondissipative information technology”.
Author information
Authors and Affiliations
Contributions
P.K.A., W.S.Z., and Y.Z. planned and supervised the project. Z.Y.Z. and Y.Z. designed the experiments and fabricated the devices with help from V.L.-D. and J.S. Z.Y.Z., V.L.-D., X.F., L.C., Z.W., Z.Z., and Y.X performed the measurements of the samples and analyzed the data. B.H., K.Z., and Y.G.Z. performed the STEM imaging. L.S.-T., M.C., and G.F. implemented the micromagnetic code and performed the simulations. A.F. contributed to the theoretical explanation and data interpretation. Z.Y.Z., P.K.A., G.F., and Y.Z. co-wrote the manuscript. All the authors read and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks BingJin Chen and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zheng, Z., Zhang, Y., Lopez-Dominguez, V. et al. Field-free spin-orbit torque-induced switching of perpendicular magnetization in a ferrimagnetic layer with a vertical composition gradient. Nat Commun 12, 4555 (2021). https://doi.org/10.1038/s41467-021-24854-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-24854-7
- Springer Nature Limited
This article is cited by
-
Highly efficient field-free switching of perpendicular yttrium iron garnet with collinear spin current
Nature Communications (2024)
-
Spin current and spin-orbit torque induced by ferromagnets
npj Spintronics (2024)
-
Effective electrical manipulation of a topological antiferromagnet by orbital torques
Nature Communications (2024)
-
Reconfigurable spintronic logic gate utilizing precessional magnetization switching
Scientific Reports (2024)
-
Generation of out-of-plane polarized spin current by non-uniform oxygen octahedral tilt/rotation
Nature Communications (2024)