Abstract
Wear-related energy and material loss cost over 2500 Billion Euro per year. Traditional wisdom suggests that high-strength materials reveal low wear rates, yet, their plastic deformation mechanisms also influence their wear performance. High strength and homogeneous deformation behavior, which allow accommodating plastic strain without cracking or localized brittle fracture, are crucial for developing wear-resistant metals. Here, we present an approach to achieve superior wear resistance via in-situ formation of a strong and deformable oxide nanocomposite surface during wear, by reaction of the metal surface with its oxidative environment, a principle that we refer to as ‘reactive wear protection’. We design a TiNbZr-Ag alloy that forms an amorphous-crystalline oxidic nanocomposite surface layer upon dry sliding. The strong (2.4 GPa yield strength) and deformable (homogeneous deformation to 20% strain) nanocomposite surface reduces the wear rate of the TiNbZr-Ag alloy by an order of magnitude. The reactive wear protection strategy offers a pathway for designing ultra-wear resistant alloys, where otherwise brittle oxides are turned to be strong and deformable for improving wear resistance.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Wear-related energy loss and component damage, including friction and remanufacturing of components that failed by wear contacts, accounts for 23% of the global energy consumption with an estimated cost of over 2500 Billion Euro per year1. Since metals are the most used engineering materials, wear-resistant metals have long been the pursuit in materials design, yet are challenging to achieve2. According to classical wear theory, a material with higher strength exhibits higher wear resistance due to a reduced contact area at a fixed stress3. High-strength martensitic steels4 and cobalt-based alloys5 have been extensively used in environments with severe wear. Nanograined metals with higher strength than their coarse-grained counterparts have been developed for achieving improved wear resistance6. However, there exist conflicting reports about the wear performance of nanograined metals7. It has been found that grain growth or grain boundary sliding/grain rotation mechanisms (following the inverse Hall-Petch relation8) can reduce wear resistance9. The wear resistance of nanograined metals can be enhanced if their structural evolution upon wear promotes homogeneous plastic deformation, which prevents strain softening and brittle fracture10. Therefore, the design of wear-resistant metals requires a high strength in conjunction with appreciable homogeneous deformation ability upon wear. Gradient nanograined metals offer enhancement in wear resistance compared to their nanograined counterparts, due to the suppression of inhomogeneous plastic deformation at the contact surfaces, restricting sliding-induced cracking and localized brittle fracture11. Amorphous alloys, or metallic glasses (MGs), lack crystalline structures and usually possess improved yield strengths (σy~E/50, E is elastic modulus) compared to their crystalline counterparts12. Nevertheless, the plastic deformation of MGs is highly localized in shear bands, which results in cracks and brittle wear particles, thus evoking a micro-cutting mechanism which dramatically accelerates wear13. The plastic deformability of MGs can be enhanced when introducing chemical or topological heterogeneity to generate multiple shear bands, e.g., by introducing glass-glass interfaces (nanoglasses)14, a secondary amorphous phase (dual-phase MGs)15, or a crystalline phase (amorphous-crystalline composites)16,17. However, the shear banding response of the amorphous phase still limits wear resistance18. Surface oxides, with a nanocomposite structure comprising crystalline oxide nanoparticles embedded in an amorphous matrix, can be formed on steels19 and cobalt-based alloys20 during wear. It has been reported that nanocomposites containing brittle crystalline phases usually reveal inhomogeneous plastic deformation due to shear banding21. If the brittle crystalline phase (such as crystalline oxide nanoparticles) in the nanocomposite is replaced by a ductile solid solution crystalline phase, homogeneous plastic deformation can be achieved22.
Here, we propose an alloy design concept based on an enthalpy-guided approach to promote formation of solid solution nanocrystals, rather than crystalline oxide nanoparticles, in the amorphous matrix during wear. This structure enables a high strength and homogeneous plastic deformation of the friction-induced oxidic nanocomposite surface layer. We realize this concept in a multi-component (TiNbZr)75Ag25 (at.%) alloy, by blending a TiNbZr medium-entropy alloy with Ag to create the desired self-lubricating nanostructure upon wear exposure. A ball-on-disk sliding test at a maximum contact stress of 1.0 GPa reveals that the (TiNbZr)75Ag25 alloy exhibits a friction coefficient of around 0.09 in air. The tribological contact introduces environmental O into the alloy, facilitating new atomic coordination with large negative enthalpy of mixing, which enhances the alloy’s glass-forming ability23. Besides, Ag has a positive enthalpy of mixing with Nb (+16 kJ/mol)24, which serves as a thermodynamic driving force for the nucleation of Ag nanocrystals from the amorphous matrix. Consequently, a ~400 nm thick amorphous-crystalline nanocomposite layer, with ~10 nm-sized Ag nanocrystals embedded in an amorphous oxide matrix, forms on the crystalline alloy surface upon wear in air. This surface nanocomposite exhibits a yield strength of 2.4 GPa and homogeneous deformation to 20% strain, as revealed by nano-pillar compression tests at ambient temperature. The formation of a strong and deformable oxide nanocomposite surface promotes an ultralow wear rate of the (TiNbZr)75Ag25 alloy, which is two orders of magnitude lower than that of a TiNbZr alloy exposed to identical test conditions, and is an order of magnitude lower than that of a (TiNbZr)75Ag25 alloy tested in Ar atmosphere. This represents a strategy for achieving exceptional wear resistance by utilizing the structural and chemical evolution of metal surfaces through alloying them not during synthesis but in-situ during wear-exposure with environmental O. We refer to this principle as ‘reactive wear protection’.
Results
Structure and composition characterizations
We deposited (TiNbZr)75Ag25 (at.%) films on equiatomic TiNbZr alloy sheets using a combinatorial magnetron co-sputtering approach25. By varying the distance between the substrates and the sputtering targets, TiNbZr-Ag alloys with different Ag content were prepared in a single deposition (Fig. 1a). For comparison, we also investigated (TiNbZr)90Ag10 (at.%) and equiatomic TiNbZr alloy films. X-ray diffraction (XRD) spectra (Supplementary Fig. 1) suggest that the TiNbZr, (TiNbZr)90Ag10, and (TiNbZr)75Ag25 alloys assume a single-phase body centered cubic (bcc) structure. Transmission electron microscopy (TEM) shows that the (TiNbZr)75Ag25 alloy and the reference TiNbZr alloy are both composed of ~100-nm-diameter nanograins elongated along the growth direction (Fig. 1b, c). No secondary phase is observed in these alloys, as confirmed by selected area electron diffraction (SAED) analysis (inset in Fig. 1b, c). We further characterized the elemental distribution using atom probe tomography (APT) (Fig. 1d). The (TiNbZr)75Ag25 alloy has an average composition of Ti25Nb27Zr23Ag25 (at.%), and the grain boundaries are enriched with Ag. The grain boundary segregation is driven by a reduction in free energy following the Gibbs adsorption isotherm26. We observe composition striations within the grains (Supplementary Fig. 2). Ag has a Pauling electronegativity of 1.93, a value that is distinctly different from that of the other three elements (1.54 for Ti, 1.33 for Zr, and 1.60 for Nb)27. This difference might explain the underlying bonding effects behind the nanoscale chemical inhomogeneity observed in the material28.
Mechanical properties and wear behavior
Alloying with Ag leads to the increase of the yield strength (σy) from 1.1 ± 0.1 GPa for the TiNbZr alloy to 1.3 ± 0.2 GPa for the (TiNbZr)90Ag10 alloy and 1.7 ± 0.2 GPa for the (TiNbZr)75Ag25 alloy, as probed in uniaxial micropillar compression experiments (Supplementary Fig. 3). The increased strength can be attributed to the enhanced solid solution strengthening and the formation of composition striations via Ag addition, both increasing the friction stress that acts against dislocation motion. All three alloys reveal homogeneous deformation to compressive strain of 30%.
The wear behavior of the TiNbZr, (TiNbZr)90Ag10, and (TiNbZr)75Ag25 alloys was studied by sliding them against stainless-steel balls (4-mm-diameter) in ambient air (Fig. 2). The sliding velocity was 1 mm/s, the slide stroke was 5 mm, and the contact force was 5 N, corresponding to a maximum Hertzian contact stress of 1.0 GPa. One sliding cycle corresponds to two strokes, and the sliding duration was 1800 s for 180 cycles. The TiNbZr alloy reveals a steady state friction coefficient of ~0.25, representing a typical constant friction observed in unlubricated sliding of metals29. The (TiNbZr)90Ag10 alloy exhibits a lower steady state friction coefficient of ~0.16, which is mainly attributed to the lubricating effect of Ag30. Notably, the (TiNbZr)75Ag25 alloy shows a low friction coefficient (~0.09) throughout the wear process (Fig. 2a). The stainless-steel ball maintains its spherical shape despite the high contact stress (Supplementary Fig. 4). We compared the morphology of the wear surfaces of the TiNbZr and (TiNbZr)75Ag25 alloys using a 3D optical microscope (Fig. 2b, c1, d1). The (TiNbZr)75Ag25 alloy shows a narrow and smooth wear track, which is profoundly different from the wide and deep wear track of the TiNbZr alloy. Hence, the (TiNbZr)75Ag25 alloy has a dramatically smaller wear volume (1.5 × 105 μm3) as compared to the TiNbZr (3.0 × 107 μm3) and (TiNbZr)90Ag10 (1.1 × 107 μm3) alloys, corresponding to a two orders of magnitude reduction in specific wear rate (1.7 × 10−5 mm3 N−1 m−1) compared to the TiNbZr (3.3 × 10−3 mm3 N−1 m−1) and (TiNbZr)90Ag10 (1.2 × 10−3 mm3 N−1 m−1) alloys.
Friction-induced amorphous-crystalline oxidic nanocomposite surface layer
To understand the wear mechanism, we investigated the structures of the wear surfaces at atomic scale using TEM and aberration-corrected scanning TEM (STEM). In the worn TiNbZr alloy, the original columnar grains have been refined into ~10-nm-diameter globular grains within ~1 μm depth from the surface (Fig. 2c2–c4). Grain refinement is a common phenomenon for crystalline metals exposed to wear. This effect is attributed to the high density of dislocations forming sub-grain boundaries to reduce their distortion energy29. The wear surface of the (TiNbZr)90Ag10 alloy shows a multilayer structure comprising regions of a ~20-nm-thick nanocrystalline phase separated by ~5-nm-thick amorphous interfaces (Supplementary Fig. 5). In the worn (TiNbZr)75Ag25 alloy, the nanograins are slightly curved at a depth of 1.6–3.4 μm below the surface, and globular grains with ~30 nm diameter are observed at 1.6 μm depth from the surface (Fig. 2d2). Different from the two reference alloys, a ~400-nm-thick amorphous surface layer, in which nanocrystals with diameters from 5 nm to 20 nm are embedded, is found in the worn (TiNbZr)75Ag25 alloy (Fig. 2d3). The nanocrystals have face centered cubic (fcc) structure (Fig. 2d4). Energy-dispersive X-ray spectroscopy (EDS) results indicate that the amorphous matrix and the nanocrystals are enriched with O and Ag, respectively (Supplementary Fig. 6). Therefore, the ~400-nm-thick surface layer of the worn (TiNbZr)75Ag25 alloy is identified as an amorphous-crystalline nanocomposite containing ~10 nm-sized Ag nanocrystals embedded in a TiNbZr-O amorphous oxide. Furthermore, many Ag nanocrystals contain nanotwins (Supplementary Fig. 7), which results from the low stacking fault energy (~16 mJ m−2) of Ag31.
In order to unveil the formation mechanism of the amorphous-crystalline nanocomposite on the wear surface, we further performed correlative TEM-APT experiments on the nanocomposite surface to analyze the structural and chemical information also at near-atomic scale. Through correlative TEM investigation of an APT sample (Fig. 3a), prepared from the top surface of the wear track, we identified the nanocrystals and amorphous phase as Ag and Ti17Nb13Zr13Fe2O55 (at.%), respectively (Fig. 3b, c). Another APT analysis from the wear scar reveals three compositionally distinct regions (Fig. 3d, e), i.e., an amorphous region, Ag nanocrystals, and a nanocrystalline region. The nanocrystalline region has a composition (Ti24Nb26Zr20Ag29O1 (at.%)) close to that of the original material. The three compositionally distinct regions, revealed by APT probing, agree well with the same features observed by STEM-EDS characterization (Supplementary Fig. 6). During the wear process, plastic deformation is associated with the generation and movement of dislocations, confined inside the nanograins by the grain boundaries of the (TiNbZr)75Ag25 alloy (Fig. 3f1). The accumulation of a high density of dislocations leads to the formation of sub-grain boundaries29. Consequently, the originally 100-nm-wide columnar grains are refined into ~30-nm-diameter globular grains, shown in the nanocrystalline region in Fig. 2d2. The evolving high grain boundary density provides abundant pathways for the ingress of O32. Moreover, Ag is a highly active catalyst, promoting fast dissociation of atmospheric O2 and enabling adsorption of O33. The grain boundaries of the as-fabricated (TiNbZr)75Ag25 alloy are enriched with Ag, further accelerating this process. Therefore, massive amounts of O are blended into the alloy’s sub-surface region (Fig. 3f2). The empirical rules of glass-forming ability (GFA) state that an alloy containing three or more elements with large negative enthalpy of mixing and significant atomic size difference are prone to form a glass24. The incorporation of the small O atoms into the (TiNbZr)75Ag25 alloy modifies the atomic coordination with directed bond contributions and a large negative enthalpy of mixing23, thus enabling the in-situ formation of an amorphous oxide during wear. Although Ag has a relative large negative enthalpy of mixing with Zr and Ti (−20 kJ/mol and −2 kJ/mol, respectively), it has a positive enthalpy of mixing with Nb (+16 kJ/mol)24, which serves as a thermodynamic driving force to nucleate the Ag nanocrystals in the amorphous Ti17Nb13Zr13Fe2O55 matrix (Fig. 3f3).
Discussion
Amorphous materials generally deform via the activation and motion of collective atomic rearrangements, i.e., shear transformation zones (STZs)34. With the onset of plastic deformation, the STZs evolve into mature shear bands which propagate rapidly and lead to catastrophic failure. If the size of the amorphous regions is smaller than 100 nm, shear banding events can be suppressed, leading to high strength and homogeneous plastic flow35. It has been demonstrated that crystal-glass nanocomposite alloys, with solid solution nanocrystals embedded in the amorphous matrix, reveal homogeneous plastic deformation, due to the confined plastic flow behavior of the amorphous phase22,36. Similarly, the amorphous-crystalline nanocomposite generated in the current study during wear benefits from this dual-phase structure, due to the resulting homogeneous plastic flow. Hence, cracking and brittle failure are suppressed in the nanocomposite nanolayer. Shear bands are not observed in the worn (TiNbZr)75Ag25 alloy in SEM (Supplementary Fig. 8) and TEM/STEM (Fig. 2) observations, confirming homogeneous plastic flow of the material. In fact, the homogeneous plastic flow behavior of amorphous materials usually indicates that the flow stress approaches the theoretical strength regime35. Compared with conventional nanograined metals37, the amorphous phase with its theoretical strength effectively prevents softening that could have been potentially caused by the Ag nanocrystals and their coarsening. Therefore, the grain size of the Ag nanocrystals, spatially confined in the amorphous-crystalline nanocomposite nanolayer, remains unchanged along the through-thickness direction, and the material close to the surface sustains high strains38. Furthermore, the Ag nanocrystals reveal a higher probability for nanotwinning on the top surface of the wear track (Fig. 3a) and in the wear debris (Supplementary Fig. 7), which are regions that experience high local strains. The nanotwin boundaries not only provide effective barriers against dislocation motion but also serve as an additional independent shear carrier39, contributing to a high flow stress and deformability of the Ag nanocrystals. As a result, the amorphous-crystalline surface nanocomposite formed during the reactive wear process exhibits a compressive strength σy of 2.4 GPa that is 41% above that of the as-fabricated (TiNbZr)75Ag25 alloy, and reveals homogeneous deformation to a strain of 20% without catastrophic failure (Fig. 4a, b). The nano-scratch tests suggest that the nanocomposite reveals a wear volume that is 42% lower than that of the as-fabricated (TiNbZr)75Ag25 alloy (Fig. 4c, d).
We further compared the wear behavior of the (TiNbZr)75Ag25 alloy in Ar atmosphere and ambient air, respectively (Fig. 4e, f). The alloy tested in Ar and in ambient air has in both cases a comparable friction coefficient of ~0.08. However, in Ar atmosphere with little O, the reactive wear process is suppressed, which leads to an 11 times higher wear volume compared to the one measured in air. The oxidic nanocomposite in-situ formed in air has a σy that is 41% higher than that of the (TiNbZr)75Ag25 alloy, leading to a reduced contact area during wear. Moreover, the nanocomposite reveals homogeneous plastic deformation, preventing cracking or localized brittle fracture upon wear exposure. Therefore, once the oxidic nanocomposite is formed on the crystalline alloy’s surface during wear, its high strength and plastic deformability lead to a substantial improvement in wear resistance. The notable difference in wear volumes of the (TiNbZr)75Ag25 alloy upon wear in Ar and air proves the effective protection effect through the development of a friction-induced oxide nanocomposite surface. It works through exploiting the chemical interaction between the worn multi-component alloy and its oxidative environment, leading to excellent wear resistance, an effect referred to as reactive wear protection.
In order to reveal the controllability of the formation of the amorphous-crystalline nanocomposite, we evaluated the wear behavior of the (TiNbZr)75Ag25 alloy in ambient air for various sliding durations (180 cycles, 720 cycles, and 1800 cycles), sliding velocities (1 mm/s, 2 mm/s, and 4 mm/s), and contact forces (5 N, 10 N, and 15 N) (Supplementary Fig. 9). The increase of the sliding duration from 180 cycles to 1800 cycles (while the other wear conditions remained unchanged) leads to a reduction of the specific wear rate by 58%, from 1.7 × 10−5 mm3 N−1 m−1 to 7.0 × 10−6 mm3 N−1 m−1. TEM investigation reveals that the thickness of the amorphous-crystalline nanocomposite surface layer increases from 400 nm (Fig. 2d2) to 1.55 μm (Supplementary Fig. 10a1-a3) after increasing the sliding duration from 180 cycles to 1800 cycles. This observation suggests a dynamic formation process of the oxidic nanocomposite during wear, i.e., the high-strength nanocomposite is gradually thickened with ongoing sliding exposure. On the other hand, the increase of the sliding velocity or contact force (while the other wear conditions remained unchanged) leads to an increased wear rate of the (TiNbZr)75Ag25 alloy. A higher velocity shortens the time for the alloy’s surface to react with the environmental O during sliding, hindering the formation of an oxidic nanocomposite. Therefore, a thinner oxide nanocomposite layer with a thickness of only 115 nm is formed on the alloy’s surface after sliding with a velocity of 4 mm/s for 180 cycles (Supplementary Fig. 10b1-b3), resulting in a higher specific wear rate of 5.5 × 10−5 mm3 N−1 m−1. Similarly, a higher contact force of 15 N leads to deeper contact during wear, which induces a thinner nanocomposite layer with a thickness of 240 nm (Supplementary Fig. 10c1–c3) and a higher specific wear rate of 4.2 × 10−5 mm3 N−1 m−1. Although the thickness of the nanocomposite surface layer changes with the sliding condition, the amorphous-crystalline structure of the surface layer is identical for all testing conditions in the present work. This finding indicates that the formation mechanism of the amorphous-crystalline oxidic nanocomposite does not change with the sliding condition, confirming the intrinsic reactive wear protection ability of the (TiNbZr)75Ag25 alloy.
In summary, we propose a strategy to design wear-resistant alloys through in-situ formation of strong and deformable oxide nanocomposite surfaces during wear, a process which we refer to as ‘reactive wear protection’. A representative bcc structured (TiNbZr)75Ag25 (at.%) alloy was developed, which yields a two orders of magnitude lower wear rate than the reference TiNbZr alloy. Upon wear in ambient air, the (TiNbZr)75Ag25 alloy forms an in-situ 400-nm-thick amorphous-crystalline nanocomposite surface layer, through reaction with the environmental O, comprising an amorphous Ti17Nb13Zr13Fe2O55 matrix containing ~10-nm-sized Ag nanocrystals. The high wear resistance of the (TiNbZr)75Ag25 alloy is achieved by the synergistic effect of the low friction coefficient (~0.09) of the alloy and the in-situ formation of an amorphous-crystalline oxidic nanocomposite surface, which exhibits a high strength and homogeneous plastic flow behavior. The study provides a guideline to the future design of wear-resistant alloys, which is based on the formation of amorphous-crystalline nanocomposite surface following the reactive wear protection approach, i.e., by alloying the surface with environmental atoms during wear.
Methods
Materials fabrication
We prepared (TiNbZr)-Ag alloy films by magnetron co-sputtering of an equiatomic TiNbZr alloy target and an elemental Ag (99.99% purity) target. The alloy films were deposited on 1-mm-thick equiatomic TiNbZr cast alloy substrates. The substrates were polished to possess mirror-like surfaces prior to deposition. The varying distances between the substrates and the targets generated a series of (TiNbZr)-Ag alloys with different Ag content in a single deposition. The growth rate of the alloy films was controlled to be ~2.4 Å/s by manipulating the target power. The alloy films have a thickness of 4 μm. As a reference material, the TiNbZr alloy film was fabricated by sputtering with an equiatomic TiNbZr alloy target at a deposition rate of 2 Å/s. The base vacuum for sputtering was below 10−7 Torr, and the Ar pressure during sputtering was 0.3 Pa.
Structure characterization
The structures of the TiNbZr, (TiNbZr)90Ag10, and (TiNbZr)75Ag25 alloy films were investigated using grazing incidence XRD (GIXRD) and transmission electron microscopy (TEM). GIXRD measurements were conducted using a Rikaku SmartLab diffractometer equipped with a Co Kα source. The incidence angle was 2°. TEM observations were carried out in a JEOL JEM-2200FS operated at 200 kV. Annular bright field (ABF)-scanning TEM (STEM) imaging was performed in a probe aberration-corrected STEM (FEI Titan Thermis) operated at 300 kV. The probe semi-convergence angle was 17 mrad, and the inner and outer semi-collection angles of the annular detector were from 13 to 21 mrad. TEM foils were prepared from the samples in a focused ion beam (FIB) workstation using Ga ions (FEI Helios Nanolab 600i). The final cleaning voltage/current was 5 kV/48 pA followed with 2 kV/23 pA.
Atom probe tomography
The near-atomic scale elemental information of the as-deposited and worn (TiNbZr)75Ag25 alloy was obtained using a LEAPTM 5000X HR (Cameca) under high vacuum of 2 × 10−11 Torr. Atom probe tomography (APT) measurements of the as-deposited alloy were conducted in voltage mode with a pulse fraction of 15%, a pulse rate of 125 kHz, a target evaporation rate of 3 ions for 1000 pulses, and a specimen temperature of 60 K. The wear surface of the alloy was characterized in laser mode with a laser pulse energy of 40 pJ, a pulse rate of 125 kHz, and a specimen temperature of 60 K. The reconstruction of the 3D atom maps was carried out using the CAMECA integrated visualization and analysis software IVAS 3.8.6. Needle-shaped specimens for APT characterization were prepared using a site-specific FIB lift-out procedure40, and the final cleaning voltage/current was 2 kV/23 pA. For correlative TEM-APT investigation, the needle-shaped specimens were fabricated on a halved Mo TEM grid41 and subsequently analyzed in TEM (JEOL JEM-2200 FS) operated at 200 kV, followed by APT characterization.
Mechanical properties
Nanoindentation tests were performed using a Hysitron TI700 nanoindenter with a Berkovich diamond tip. At least nine indentations were made on each alloy, and the indentation depth was kept within 10% of the film thickness. The elastic modulus is 85 GPa for the TiNbZr alloy, 85 GPa for the (TiNbZr)90Ag10 alloy, and 90 GPa for the (TiNbZr)75Ag25 alloy. The 1-μm-diameter micro-pillars and 200-nm-diameter nano-pillars for compression were fabricated from the samples using the FIB workstation. The final milling parameters were 30 kV and 10 pA. The taper angle of each pillar was carefully kept below 1.5°. The aspect ratio (height/diameter) was around 2. The pillar diameter was determined at 20% pillar height to avoid overestimation of strength due to taper angle. The compression experiments were performed in a nanoindenter (Keysight G200) with a diamond punch in load-control mode at a nominal strain rate of 5 × 10−3 s−1. Each compression experiment was conducted for at least five times to ensure repeatability.
Wear performance analysis
The wear behavior of the TiNbZr, (TiNbZr)90Ag10, and (TiNbZr)75Ag25 alloy films deposited on TiNbZr substrates was evaluated by ball-on-disk reciprocating-sliding experiments using a Bruker UM II wear tester. The sliding tests were conducted under dry contact conditions in ambient air or in Ar atmosphere. 4-mm-diameter 316 L stainless steel balls were used to slide against the samples. The slide stroke was 5 mm. The elastic modulus of 316 L stainless steel is 193 GPa. The frictional force (F) was recorded by the wear tester automatically, and the friction coefficient was calculated as F/P, P is the contact force. The 3D profiles of the wear tracks were measured using a Wyko NT8000 optical profiler (Veeco Instruments Inc.).
The nanoscale wear behavior of the (TiNbZr)75Ag25 alloy film and the amorphous-crystalline nanocomposite was evaluated in the nanoindenter (Keysight G200) using a 10-μm-radius spherical diamond tip. The scratch force was 5 mN and the scratch distance was 80 μm. The surface morphology of the alloy was characterized in scanning mode using the same diamond tip with 0.1-mN-force before and after scratching. The data of 5 μm to the left and to the right was omitted to avoid border effect.
Data availability
All relevant data supporting the findings of this study are contained in the paper and its Supplementary Information files. All other relevant data are available from the corresponding authors (C.L., G.W. and D.R.) upon request.
References
Holmberg, K. & Erdemir, A. Influence of tribology on global energy consumption, costs and emissions. Friction 5, 263–284 (2017).
Yao, B., Han, Z., Li, Y. S., Tao, N. R. & Lu, K. Dry sliding tribological properties of nanostructured copper subjected to dynamic plastic deformation. Wear 271, 1609–1616 (2011).
Lim, S. C. Recent developments in wear-mechanism maps. Tribol. Int. 31, 87–97 (1998).
Valtonen, K., Ojala, N., Haiko, O. & Kuokkala, V. T. Comparison of various high-stress wear conditions and wear performance of martensitic steels. Wear 426–427, 3–13 (2019).
Opris, C. D., Liu, R., Yao, M. X. & Wu, X. J. Development of Stellite alloy composites with sintering/HIPing technique for wear-resistant applications. Mater. Des. 28, 581–591 (2007).
Farhat, Z. N., Ding, Y., Northwood, D. O. & Alpas, A. T. Effect of grain size on friction and wear of nanocrystalline aluminum. Mater. Sci. Eng. A 206, 302–313 (1996).
Gao, N., Wang, C. T., Wood, R. J. K. & Langdon, T. G. Tribological properties of ultrafine-grained materials processed by severe plastic deformation. J. Mater. Sci. 47, 4779–4797 (2012).
Meyers, M. A., Mishra, A. & Benson, D. J. Mechanical properties of nanocrystalline materials. Prog. Mater. Sci. 51, 427–556 (2006).
Talachi, A. K., Eizadjou, M., Manesh, H. D. & Janghorban, K. Wear characteristics of severely deformed aluminum sheets by accumulative roll bonding (ARB) process. Mater. Charact. 62, 12–21 (2011).
Rupert, T. J. & Schuh, C. A. Sliding wear of nanocrystalline Ni-W: structural evolution and the apparent breakdown of Archard scaling. Acta. Mater. 58, 4137–4148 (2010).
Chen, X., Han, Z., Li, X. & Lu, K. Lowering coefficient of friction in Cu alloys with stable gradient nanostructures. Sci. Adv. 2, e1601942 (2016).
Demetriou, M. D. et al. A damage-tolerant glass. Nat. Mater. 10, 123–128 (2011).
Greer, A. L., Rutherford, K. L. & Hutchings, I. M. Wear resistance of amorphous alloys and related materials. Int. Mater. Rev. 47, 87–112 (2002).
Gleiter, H. Nanoglasses: a new kind of noncrystalline material and the way to an age of new technologies? Small 12, 2225–2233 (2016).
Li, F. C. et al. Micromechanical mechanism of yielding in dual nano-phase metallic glass. Scr. Mater. 154, 186–191 (2018).
Wu, Y., Xiao, Y., Chen, G., Liu, C. T. & Lu, Z. Bulk metallic glass composites with transformation-mediated work-hardening and ductility. Adv. Mater. 22, 2770–2773 (2010).
Hofmann, D. C. et al. Designing metallic glass matrix composites with high toughness and tensile ductility. Nature 451, 1085–1089 (2008).
Liu, Y., Yitian, Z., Xuekun, L. & Liu, Z. Wear behavior of a Zr-based bulk metallic glass and its composites. J. Alloy. Compd. 503, 138–144 (2010).
Yin, C.-h., Liang, Y.-l., Liang, Y., Li, W. & Yang, M. Formation of a self-lubricating layer by oxidation and solid-state amorphization of nano-lamellar microstructures during dry sliding wear tests. Acta. Mater. 166, 208–220 (2019).
Viat, A. et al. Brittle to ductile transition of tribomaterial in relation to wear response at high temperatures. Wear 392–393, 60–68 (2017).
Wu, G., Chan, K.-C., Zhu, L., Sun, L. & Lu, J. Dual-phase nanostructuring as a route to high-strength magnesium alloys. Nature 545, 80–83 (2017).
Wu, G. et al. Crystal–glass high-entropy nanocomposites with near theoretical compressive strength and large deformability. Adv. Mater. 32, 2002619 (2020).
Li, H. X., Gao, J. E., Jiao, Z. B., Wu, Y. & Lu, Z. P. Glass-forming ability enhanced by proper additions of oxygen in a Fe-based bulk metallic glass. Appl. Phys. Lett. 95, 161905 (2009).
Takeuchi, A. & Inoue, A. Classification of bulk metallic glasses by atomic size difference, heat of mixing and period of constituent elements and its application to characterization of the main alloying element. Mater. Trans. 46, 2817–2829 (2005).
Li, M. X. et al. High-temperature bulk metallic glasses developed by combinatorial methods. Nature 569, 99–103 (2019).
Raabe, D. et al. Grain boundary segregation engineering in metallic alloys: a pathway to the design of interfaces. Curr. Opin. Solid State Mater. Sci. 18, 253–261 (2014).
Guo, S. & Liu, C. T. Phase stability in high entropy alloys: formation of solid-solution phase or amorphous phase. Prog. Nat. Sci. Mater. Int 21, 433–446 (2011).
Ding, Q. et al. Tuning element distribution, structure and properties by composition in high-entropy alloys. Nature 574, 223–227 (2019).
Padilla, H. A. II, Boyce, B. L., Battaile, C. C. & Prasad, S. V. Frictional performance and near-surface evolution of nanocrystalline Ni-Fe as governed by contact stress and sliding velocity. Wear 297, 860–871 (2013).
Shi, X. et al. Tribological behavior of TiAl matrix self-lubricating composites containing silver from 25 to 800 °C. Wear 303, 486–494 (2013).
Liu, X. et al. High-order hierarchical nanotwins with superior strength and ductility. Acta. Mater. 149, 397–406 (2018).
Liu, L., Li, Y. & Wang, F. Electrochemical corrosion behavior of nanocrystalline materials—a review. J. Mater. Sci. Technol. 26, 1–14 (2010).
Li, W. X., Stampfl, C. & Scheffler, M. Why is a noble metal catalytically active? The role of the O-Ag interaction in the function of silver as an oxidation catalyst. Phys. Rev. Lett. 90, 256102 (2003).
Wang, W. H. The elastic properties, elastic models and elastic perspectives of metallic glasses. Prog. Mater. Sci. 57, 487–656 (2012).
Jang, D. & Greer, J. R. Transition from a strong-yet-brittle to a stronger-and-ductile state by size reduction of metallic glasses. Nat. Mater. 9, 215–219 (2010).
Wu, G. et al. Hierarchical nanostructured aluminum alloy with ultrahigh strength and large plasticity. Nat. Commun. 10, 5099 (2019).
Schiøtz, J., Di Tolla, F. D. & Jacobsen, K. W. Softening of nanocrystalline metals at very small grain sizes. Nature 391, 561–563 (1998).
Hamilton, G. M. Explicit equations for the stresses beneath a sliding spherical contact. Proc. Inst. Mech. Eng. Part C. J. Mech. Eng. Sci. 197, 53–59 (1983).
Lu, K., Lu, L. & Suresh, S. Strengthening materials by engineering coherent internal boundaries at the nanoscale. Science 324, 349–352 (2009).
Miller, M. K., Russell, K. F. & Thompson, G. B. Strategies for fabricating atom probe specimens with a dual beam FIB. Ultramicroscopy 102, 287–298 (2005).
Herbig, M. et al. Atomic-scale quantification of grain boundary segregation in nanocrystalline material. Phys. Rev. Lett. 112, 126103 (2014).
Acknowledgements
This project has received funding from the European Union’s Horizon 2020 Research and Innovation Programme (Grant Agreement 958457-FORGE). We greatly acknowledge the Deutsche Forschungsgemeinschaft (German Research Foundation, SPP 2006). Z.L. acknowledges the financial support by the National Science Foundation of China (Grant No. 51971248). M.H. acknowledges the Deutsche Forschungsgemeinschaft—contract No.: HE 7225/1-1—for funding. We thank Benjamin Breitbach (MPIE) for assisting with XRD characterization. We thank Dr. Fucong Lyu and Dr. Chong Wang in the City University of Hong Kong for their help with wear testing and analysis.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
D.R., C.L., and G.W. designed the project and the material; C.L. and G.W. designed the magnetron sputtering experiment; B.G., C.L., G.W. and H.Z. conducted APT investigation and data analysis; C.L. and Z.L. conducted FIB and TEM experiments; Y.B. and C.L.L. carried out the macro-wear experiments; W.X. and C.L. performed compression and nano-wear experiments; X.W., W.L. and G.D. conducted STEM characterization and data analysis; M.H. and A.F. analyzed the wear mechanism; C.L., G.W. and D.R. wrote the paper; all authors contributed to the discussion of the results.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks W. Mark Rainforth and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, C., Li, Z., Lu, W. et al. Reactive wear protection through strong and deformable oxide nanocomposite surfaces. Nat Commun 12, 5518 (2021). https://doi.org/10.1038/s41467-021-25778-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-25778-y
- Springer Nature Limited
This article is cited by
-
Subsurface deformation mechanism and the interplay relationship between strength-ductility and fretting wear resistance during fretting of a high-strength titanium alloy
Friction (2024)
-
Unlocking wear resistance in an ultrastrong dual-phase high-entropy alloy by interface-constrained deformation of brittle Laves phases
Friction (2024)
-
Plasma-Sprayed Nanodiamond-Reinforced NiCrBSi Composite Coating for Improved Wear and Corrosion Resistance
Journal of Thermal Spray Technology (2024)
-
Research status of tribological properties optimization of high-entropy alloys: a review
Journal of Materials Science (2023)
-
Defect Control of Electro-spark Deposition WC–Co Coatings via Adjusting Pulse Energy and Deposited Layer Number
Journal of Materials Engineering and Performance (2023)