Abstract
Achieving effective manipulation of perpendicular exchange bias effect remains an intricate endeavor, yet it stands a significance for the evolution of ultra-high capacity and energy-efficient magnetic memory and logic devices. A persistent impediment to its practical applications is the reliance on external magnetic fields during the current-induced switching of exchange bias in perpendicularly magnetized structures. This study elucidates the achievement of a full electrical manipulation of the perpendicular exchange bias in the multilayers with an ultrathin antiferromagnetic layer. Owing to the anisotropic epitaxial strain in the 2-nm-thick IrMn3 layer, the considerable exchange bias effect is clearly achieved at room temperature. Concomitantly, a specific global uncompensated magnetization manifests in the IrMn3 layer, facilitating the switching of the irreversible portion of the uncompensated magnetization. Consequently, the perpendicular exchange bias can be manipulated by only applying pulsed current, notably independent of the presence of any external magnetic fields.
Similar content being viewed by others
Introduction
In the rapidly evolving field of spintronics1,2,3,4,5,6,7, antiferromagnetic (AFM) materials have gained paramount importance in the development of advanced-generation memory and computing technologies8,9,10,11,12, garnering extensive attention benefiting from the advantages of zero net magnetization, robustness against external perturbations, and spin dynamics at the terahertz timescale. Recent research on AFM materials has been predominantly focused on the manipulation of Néel order in bulk antiferromagnets13,14,15,16 and the spin configuration at the antiferromagnet/ferromagnet interface, referring to the exchange bias (EB) effect17,18,19,20,21,22. The EB effect can induce a unidirectional exchange anisotropy, which manifests as a shift in hysteresis loops along the direction of external magnetic fields23,24 defined quantitatively as the exchange bias field (HEB) together with an expanded loop. Beyond the applications in traditional spintronic devices, the manipulation of the EB effect, intricately associated with the bulk magnetic state of AFM25, is expected to be a promising approach for detecting or writing information stored with the AFM order in advanced memory and logic devices26,27. Currently, two strategies can be utilized to manipulate the EB. The first one is to reorient the pinning direction via the conventional field-cooling process24, albeit necessitating elevated temperatures and an external field, thus hindering its application in spintronic devices. The second one is electric current-driven switching17,18,19,20,28,29,30,31,32,33,34,35. Nevertheless, in prior studies on exchange-biased multilayers with perpendicular magnetic anisotropy (PMA), the necessity of an external magnetic field for manipulating the EB is remained17,18,19,29,30,31,32,33,34, posing a technological challenge in applications, and the underlying mechanism of the current switching behavior warrants in-depth exploration.
γ-IrMn3, a widely adopted AFM material, has attracted significant research interest in both fundamental physics and pragmatic applications11,12,36,37,38. It is conventionally employed to pin the reference layer in information-storage devices with EB owing to its high Néel temperature (TN)39, large anisotropy40, and resistance to corrosion41. For practical applications, an optimal balance between a high TN and minimized thickness of IrMn3 layer becomes imperative. However, in multilayer configurations, the finite size effect results in a marked reduction in the TN of AFM layer compared to its bulk value, leading to the disappearance of the EB effect beneath a thickness threshold of the AFM layer42,43. Existing theories have elucidated a correlation between TN and the thickness of the IrMn3 layer (tIrMn)44, implying that when the thickness of IrMn3 is reduced to 2 nm, the TN will be suppressed to about 230 K, which is substantially below room temperature (RT). Typically, a considerable HEB in multilayers can be achieved when tIrMn exceeds 4 nm45,46,47,48. Therefore, one of the paramount challenges lies in manipulating the AFM exchange coupling to strike an intricate balance between the thickness and the TN of the AFM layer. Considering the sensitive dependence of exchange interaction between spins on interatomic distance40, the introduction of epitaxial strain emerges as a promising avenue due to its potential modulatory impact on the exchange bias effect at the antiferromagnet/ferromagnet interface39,49,50,51.
In this work, a considerable perpendicular exchange bias field is achieved at RT in single-crystalline multilayers with a 2-nm-thick IrMn3 layer accompanied by a distinct uncompensated magnetic structure, which is ascribed to the anisotropic epitaxial strain in the ultrathin AFM layer. Notably, the full electrical manipulation of the perpendicular exchange bias, obviating the need for external magnetic fields, is successfully realized. This research is instrumental in enhancing our understanding about the interplay of the exchange bias effect and epitaxial strain in multilayered structures and can greatly augment the roadmap for the design and deployment of versatile spintronic devices.
Results and discussion
Perpendicular exchange bias effect with ultrathin IrMn3 layer
The epitaxial Pt (3 nm)/Co (1 nm)/γ-IrMn3 (2 nm) multilayer was deposited onto an Al2O3 (0001) substrate as shown in Fig. 1a. The MgO (2 nm)/Cr (2 nm) was deposited as capping layers to avoid degradation. The single-crystalline structure and element distributions were characterized by cross-sectional scanning transmission electron microscopy (STEM) and energy dispersive X-ray spectroscopy (EDS). As shown in Fig. 1b, the high-angle annular dark field (HAADF) image demonstrates the high quality of the epitaxial Pt/Co/IrMn3 multilayer with a single-crystalline structure. The discernible image contrast and EDS mappings (Fig. 1c–f) of Pt, Co, and IrMn3 layers demonstrate their precise thickness, uniform elemental distributions, and smooth interfaces. The atomic ratio between Ir and Mn atoms in the IrMn3 layer was evaluated to be 22.2:77.8, in good agreement with the nominal ratio of 25:75. Subsequently, the film was fabricated into Hall bar devices with a width of 15 μm utilizing conventional lithography and ion milling to perform electrical transport measurements. The anomalous Hall effect (AHE) was measured by sweeping the magnetic field parallel to the out-of-plane direction while the current was injected along the current channel as illustrated in the inset of Fig. 1g. The good PMA of the epitaxial Pt/Co/IrMn3 structure can be confirmed by the square shape of the R-H loop as shown in Fig. 1g, and the perpendicular exchange bias field (HPEB) can be derived to be about 436 Oe simultaneously, in accordance with the value from the magnetization hysteresis loop obtained by vibrating sample magnetometer. It is noteworthy that such a high value of HPEB corresponds to a mere 2-nm-thick IrMn3 layer (The verification of robustness and reproducibility of HPEB can be found in P1 of the Supporting Information), contrasting with the prevalent notion of necessitating IrMn3 layers thicker than 4 nm to achieve a considerable HPEB. Additionally, the tIrMn dependence of the HPEB for the epitaxial Pt/Co/IrMn3 multilayer was investigated (refer to P2 of the Supporting Information), which indicated a critical thickness of about 1.5 nm for the IrMn layer to achieve a perpendicular exchange bias effect at RT.
In ensuing experiments, current-induced magnetization switching (CIMS) was conducted by applying a DC pulsed current along the longitudinal channel (as detailed in the Methods Section) under an in-plane magnetic field (Hext) of ±3000 Oe (depicted in Fig. 1h). As expected in the spin-orbit-torque (SOT) framework, the switching loops exhibited opposite switching polarities. In the absence of the in-plane magnetic field, a minimal CIMS ratio manifests, which is reasonable for γ-IrMn3 with the 3Q magnetic structure39,52,53. Notably, perpendicular exchange bias switching (PEBS) of epitaxial Pt/Co/IrMn3 can be realized by applying pulsed electrical current as depicted in Fig. 1i, j. For the initial state with negative HPEB, the magnetization of Co (mCo) is “up” which is antiparallel to the interfacial uncompensated magnetization of Mn (mMn). Then, the mCo can be switched to the “down” state by applying a magnetic field of −5000 Oe, while the mMn remains unchanged corresponding to the negative HPEB. When a pulsed current with a density of 2.7 × 107 A cm−2 is injected in the absence of the magnetic field, mMn reorients to antiparallel to mCo in the absence of the external fields, resulting in that the direction of HPEB was reversed to be positive, as shown in the insets of Fig. 1j. Moreover if the mCo is aligned to “up” state by applying a magnetic field of +5000 Oe and followed by a pulsed current, the HPEB can be switched back to the initial negative state. The insets in Fig. 1i reveal the four different states of the magnetic moment configurations at the interface during the PEBS process. The experimental results indicate that the sign of the perpendicular exchange bias can be switched by injecting the pulsed current based on a defined magnetization state of Co. In contrast to previous studies on perpendicular exchange bias, such current-driven manipulation can be realized without an external magnetic field. The magnetic field herein solely serves to change the magnetization direction of the Co layer.
Structural characterization and epitaxial strain
Comprehensive characterizations were performed to give an understanding of the crystalline structure of epaxial Pt/Co/IrMn3 multilayers. Figure 2a shows the in situ reflection high-energy electron diffraction (RHEED) patterns with sharp and continuous diffraction streaks corresponding to the Pt, Co, and IrMn3 layers, respectively, indicative of the formation of a high-quality epitaxial structure. The distances between the reflection streak and the first-order diffraction streak (d) of Pt (dPt) and IrMn3 (dIrMn) layers can be quantitatively analyzed through the line scan intensity curves of the RHEED patterns as shown in Fig. 2b, which are derived as a ratio of dIrMn/dPt = 1.01. It should be noticed that the lattice parameter of the Pt layer is close to the bulk value, attributed to the negligible lattice mismatch (0.95%) existing between the Pt (111) and the Al2O3 (0001) lattices and the epitaxial-strain release through a high-temperature annealing process. Based on the bulk lattice constant of Pt (3.923 Å), the lattice constant of the ultrathin IrMn3 is extracted as ~3.88 Å, representing a 2.7% expansion relative to its bulk value (3.778 Å). The distortion in the ultrathin IrMn3 layer elucidated by the RHEED pattern signifies in-plane tensile strain due to a large lattice mismatch between Co and IrMn3 (6.57%).
Figure 2c presents the X-ray diffraction (XRD) patterns of the Pt (3)/Co (1)/IrMn3 (2) (in nm). An enlarged view of the selected region in the inset highlights the (111) diffraction peak of 2-nm-thick IrMn3 (marked by the orange dashed line), which is located at 2θ = 40.68°. The peak’s position, to the left of the bulk value derived from the standard spectra of IrMn3 (41.36°, marked by the black dashed line), implies augmented interatomic distances along [111] direction. This corroborates the presence of out-of-plane tensile strain in the ultrathin IrMn3 layer, quantitatively extracted to be 1.35% according to Bragg’s law.
Moreover, the epitaxial strain is directly ascertainable based on the high-resolution HAADF image, revealing a well-defined atomically layered structure as shown in Fig. 2d. The average in-plane (along [\(11\bar{2}\)] direction) and out-of-plane (along [111] direction) atomic interlayer distances are derived to be 2.42 Å and 2.23 Å, respectively. In comparison with bulk IrMn3 (atomic interlayer distances of 2.31 Å and 2.18 Å along [\(11\bar{2}\)] and [111] directions, respectively), there exists a tensile strain of about 2.3% along [111] direction and 4.8% along [\(11\bar{2}\)] direction. The in-plane tensile strain is larger than that along the out-of-plane direction, consistent with the RHEED patterns and the XRD results. Figure 2e shows the schematic atomic arrangements characterizing the crystalline structure of both bulk and ultrathin IrMn3. Within the ultrathin IrMn3 layer, an anisotropic lattice distortion is evident, where the magnitude and direction of this distortion clearly are annotated with arrows.
The specific global uncompensated magnetization within the IrMn3 layer
It is widely acknowledged that the exchange bias effect in multilayers is intricately linked to the thickness of the AFM layer42,43. Based on the study by L. Frangou et al., which accounts for magnetic phase transitions and finite size-scaling54, a linear relationship between TN and the thickness of the AFM layer (tIrMn) has been discerned44. Specifically, for tIrMn < n0 (the finite divergence of the spin-spin correlation length near the TN, n0 ≈ 2.7 nm for IrMn344), \({T}_{{{{{{\rm{N}}}}}}}\left({t}_{{{{{{\rm{IrMn}}}}}}}\right)={T}_{{{{{{\rm{N}}}}}}}\left({{{{{\rm{bulk}}}}}}\right)\frac{{t}_{{{{{{\rm{IrMn}}}}}}}-d}{2{n}_{0}}\), wherein TN (bulk) represents the Néel temperature of the IrMn3 bulk (700 K55), and d is the interatomic distance, equating to 0.22 nm for IrMn3 along [111] direction. With the reduction of tIrMn to 2 nm, the TN of IrMn3 will be suppressed below RT (about 230 K). Typically, tIrMn needs to be larger than 4 nm to obtain a considerable HEB in multilayers.
On the other hand, the significantly diminished volume anisotropy energy (EA) of the 2 nm IrMn3 layer proves insufficient to resist the exchange energy at the antiferromagnet/ferromagnet interface (Eint)45. As the mCo rotates with the magnetic field, the mMn will be switched simultaneously, only resulting in an increase in coercivity. When the IrMn layer is thicker, there will be enough energy to produce exchange bias accompanied by an increased coercivity. This discussion, however, overlooks the influence of crystalline structure on EB49,50. Factoring in the nonnegligible tensile strain in the ultrathin IrMn3 layer, the contribution from the aforementioned anisotropic epitaxial strain becomes imperative to decipher the abnormal HPEB of 2-nm-thick IrMn3 in this work. More experimental evidence was gleaned from two control samples with distinct strain to further verify its effect on EB56,57 (refer to P3 of the Supporting Information). The results reveal that augmented epitaxial strain directly corresponds to a more significant exchange bias field, underscoring the pivotal role of lattice strain in modulating the exchange bias effect.
Furthermore, the atomistic simulation by the VAMPIRE software package was performed to further clarify the physical mechanism for the influence of the epitaxial strain in the single-crystalline IrMn358,59. A system with Co (1 nm)/IrMn3 (2 nm) was constructed in fcc-(111) orientation to duplicate the experimental structure as depicted in Fig. 3a. The effective exchange interactions between Mn atoms were limited to nearest (−3.7 × 10−21 J/link) and next-nearest (3.0 × 10−21 J/link) neighbors38,60,61. Other detailed parameters can be found in the P4 of the Supporting Information. For the configuration without epitaxial strain, no obvious HPEB manifests (refer to Fig. S9 of the Supporting Information). Factoring in the anisotropic tensile strain in ultrathin IrMn3, an additional magnetocrystalline anisotropy (MCA) associated with an extra anisotropy energy (EMCA = 1.0 × 10−22 J/atom) was introduced in the atomistic simulations. Upon applying a zero-field cooling process from 600 K, with mCo locked in either the “up” or “down” states, the resulting simulated hysteresis loop at 300 K manifests a distinctive HPEB of −413 Oe (red curve) or 377 Oe (blue curve). This suggests that the Eint can be overcome by introducing EMCA, resulting in the exchange bias field of the Pt/Co/IrMn3 with epitaxial strain. Additionally, the simulated PEBS process by the zero-field cooling process is in accordance with the experimental results of the field-free switching behavior by pulsed current, revealing a nonnegligible effect of the thermal accumulation within the device (refer to P6 of the Supporting Information).
More specifically, the interfacial net magnetization of the IrMn3 layer with EMCA = 1.0 × 10−22 J/atom was analyzed with the hysteresis loops to elucidate the origin of the exchange bias effect. According to previous research, the uncompensated magnet moment of IrMn3 consists of a reversible moment (nre) and an irreversible moment (nir)38, which correspond to the reversible and irreversible spins of the Mn atoms, respectively. The nir is strongly coupled to bulk AFM structure, which cannot rotate with the magnetic field, facilitating a pinning effect on the ferromagnetic (FM) layer. While the nre can be switched with mCo, augmenting the coercivity of the system. The directions of nre and nir corresponding to the opposite exchange bias effect can be determined by their components along different axes as depicted in Fig. 3b. At the positive (negative) saturation state, the interfacial net magnetization of the IrMn3 layer, which is defined as nPos (nNeg), can be expressed as nPos = nir + nre (nNeg = nir – nre). The magnitude of nir can be meticulously quantified by the vertical offset of the hysteresis loop, which is equal to (nPos + nNeg)/2, wherein the value of (nPos – nNeg)/2 is derived as the magnitude of nre. The nre and nir are presented with the statistical distribution of the magnetic moments along each axis as shown in the middle portion of Fig. 3b, which are extracted from the dispersive hysteresis loops attributed to the thermal disturbance of spins in the atomistic simulation62. Notably, the nre predominantly aligns with the z-axis for both states with negative (left portion) and positive (right portion) HPEB. More precisely, the nre flips with the mCo retaining AFM coupling, while the nir remains fixed as illustrated in the insets. The values of the nir for the two loops are extracted to be −130 μB (for the negative HPEB) and 107 μB (for the positive HPEB), respectively, which reverse in accordance with the mCo during the zero-field cooling process, thereby engendering opposite HPEB.
To elucidate the detailed AFM structure of the ultrathin IrMn3 layer, the spatially resolved magnetization along the depth of the Pt (3 nm)/Co (1 nm)/IrMn3 (2 nm) film was explored by polarized neutron reflectometry (PNR) measurements. The details of the nuclear profile and the magnetization configuration can be determined by the non-spin-flip reflectivities R++ (spin-up neutrons) and R-- (spin-down neutrons) and the corresponding spin-asymmetry ratios (R++ – R--) / (R++ + R--) (SA) with respect to wave vector transfer (Q) as shown in Fig. 3c. The corresponding profiles of the nuclear (nSLD) and magnetic scattering-length density (mSLD) are shown in Fig. 3d. Upon analysis, the thickness of the IrMn3 layer is detected to be 21.6 Å, corroborated by the nSLD profiles, consistent with the nominal thickness. Notably, there exists an abnormality for the ultrathin IrMn3 layer in terms of the mSLD profile. In conventional scenarios, uncompensated magnetization in the IrMn3 layer without epitaxial strain can be detected predominantly nearby the ferromagnet/IrMn3 interface, which is typified by AFM coupling with the FM layer17. Contrarily, the 2-nm-thick IrMn3 possesses pronounced uncompensated magnetization in the full range of the AFM layer exhibiting AFM coupling with Co. Previous neutron-scattering experiments indicate that the chemically disordered IrMn3 with tetrahedral (3Q) spin structure possesses compensated magnetization with 109.5° between spins of the four magnetic sublattices39. Specifically, the anisotropic tensile strain along in-plane and out-of-plane directions may lead to a decrement of the exchange coupling among Mn atoms, leading to a diminished in-plane exchange energy compared to its out-of-plane counterpart. This results in the inability of the ultrathin IrMn3 to retain its typical 3Q compensated magnetic structure (as depicted in the left of Fig. 3e). The attenuated AFM coupling among magnetic sublattices L1, L2, and L3 leads to an angular deviation of the constituent spins away from the in-plane direction, engendering a net magnetization in IrMn3 as illustrated in the right of Fig. 3e. In the configuration involving a 2-nm-thick single-crystalline IrMn3 layer, the residual epitaxial strain remains in such ultra-thin thickness. Consequently, a reversible net magnetization, attributable to this unreleased epitaxial strain, is detectable spanning the entire AFM layer, and this is validated by the PNR results.
As aforementioned, the nir is robustly pinned by the bulk AFM structure, precluding its synchronous switching with the mCo, thereby culminating in the manifestation of the exchange bias effect. However, when considering the ultrathin IrMn3 layer with globally uncompensated magnetic moments, the nre surrounding nir within the AFM IrMn3 layer can be switched with mCo. Consequently, nir transforms to a metastable state with higher energy, manifesting as a reduced energy barrier for switching. During the PEBS process, the increase in temperature resulting from the pulsed current leads to a reduction of EA, which weakens the coupling between nir and bulk spins within the IrMn3 layer. Specifically, when EA falls below Eint, the nre maintains stability owing to the coupling with Co, while the nir becomes decoupled from the bulk spins due to the diminished EA. It thus can be speculated that the nir prefers alignment with mCo (thus nre) in terms of energy, rather than with the bulk spins of IrMn3. As a result, throughout the PEBS process, the orientation of nir is exclusively influenced by mCo. This potentially allows the nir to be reoriented and recoupled with the IrMn3 bulk spins to revert to the lowest energy state, thereby facilitating the field-free switching of the perpendicular exchange bias.
Full electrical manipulation of PEBS
Building upon the underlying mechanism of PEBS driven by current, an innovative strategy to achieve full electrical manipulation entails the conception of a sample with the feasibility of field-free SOT switching of Co magnetization. Therefore, another structure was constructed consisting of Pt (3)/Cr wedge (0 ~ 0.3)/Co (1)/IrMn3 (2) (thickness in nm) as illustrated in Fig. 4a. An array of Hall bar devices was fabricated with the current channel perpendicular to the Cr wedge direction. The PMA and the HPEB can be simultaneously investigated by the AHE measurements. Figure 4b presents the AHE loops of six devices along the wedge direction. The results indicate that the PMA is sensitive to the thickness of the Cr insertion, and the exchange bias effect is maintained for all the devices. Figure 4c depicts the current switching curve of device D corresponding to a 0.2-nm Cr insertion. The device exhibits the viability of field-free magnetization switching driven by SOT owing to the lateral symmetry breaking, which originates from an in-plane component of the exchange bias field. The detailed discussion can be found in P7 of the Supporting Information63,64. Based on this, the full electrical manipulation of the PEBS process can be realized as exhibited in Fig. 4d. By applying a negative pulsed current with a density of −3 × 107 A cm−2 without external magnetic fields, the HPEB of the device switches from negative (−424 Oe) to positive (488 Oe) state. Similarly, a positive pulsed current with a density of 3 × 107 A cm−2 can also lead to the full electrical manipulation of the PEBS process from the positive (488 Oe) back to the negative (−403 Oe) state. Additionally, the intermediary state of the PEBS process exhibiting double-biased switching behavior can be manipulated by tuning the density of the pulsed current, which is discussed in P8 of the Supporting Information. This method of full electrical manipulation of PEBS holds significant implications for optimizing spintronic device configurations, and promotes the further application of the correlative devices.
In summary, we have reported a considerable exchange bias effect in a single-crystalline multilayered structure with a 2-nm-thick IrMn3 layer. The anisotropic epitaxial strain within the ultrathin AFM layer engenders additional magneto-crystalline anisotropy energy, which results in the exchange bias effect, together with a specific global uncompensated magnetization of IrMn3 corroborated by PNR. Noteworthy, by introducing a wedged insertion at the Pt/Co interface, the full electrical manipulation of perpendicular exchange bias is successfully realized. This study will shed light on the physical intention of the correlation between epitaxial strain and exchange bias effect in multilayered structures. It also seeks to pave a feasible pathway for establishing a practical route for the harnessing of the PEBS process, thereby bearing significant implications for the development and optimization of future spintronic memory and logic devices.
Methods
Film deposition and device fabrication
The epitaxial films were deposited onto polished Al2O3 (0001) single-crystal substrates, MgO (111) single-crystal substrates, and thermally oxidized Si substrates using a molecular beam epitaxy (MBE) system with a base pressure superior to 7.0 × 10−11 mbar. The Al2O3 substrates were cleaned by acetone and isopropanol in an ultrasound bath and annealed at 750 °C for 2 h in the MBE chamber prior to the deposition. A 3-nm Pt layer was directly deposited on the surface of the Al2O3 and MgO substrates at 100 °C and was annealed for half an hour at 600 °C to release the lattice stress and to smooth the surface. Afterward, a 1-nm Co layer and 2-nm IrMn3 layer were epitaxially deposited at 100 °C under an out-of-plane magnetic field (about 350 Oe). No post-annealing process was performed to avoid diffusion of Co and IrMn3 and simultaneously maintain the lattice strain in the IrMn3 layer. The polycrystalline film discussed in P3 of the Supporting Information was deposited onto Si substrates with a 500 nm thermal oxide layer using the same MBE system. All the layers were deposited at RT and the Pt layer was annealed at 350 °C. Finally, 2-nm MgO and 2-nm Cr capping layers were subsequently deposited at RT as the capping layers to avoid the degradation of the IrMn3 layer. For the sample prepared for the PNR measurements, MgO (2 nm)/Cr (5 nm) capping layers were deposited to amplify the signal-to-noise ratio in the PNR measurement and to improve the precision of data fitting with an increased thickness. The deposition rates for Pt, Co, Ir, and Mn were controlled to be 0.040, 0.020, 0.020, and 0.054 Å/s, respectively, which were well calibrated by in situ quartz crystal microbalance before deposition. The wedged Cr insertion was deposited with a rate of 0.020 Å/s under a removing shutter. After deposition, the films were patterned into Hall bar devices using standard UV lithography and etching processes. The width of the Hall bar is 15 µm.
Structural characterization
The formation of epitaxial (textured) structure and the high-quality surface was identified by RHEED and XRD with Cu-Kα radiation (λ = 1.542 Å). STEM and EDS characterizations were performed using a spherical-aberration-corrected FEI Themis Z microscope.
Electrical transport measurement
The exchange bias effective field at RT was determined by the electric transport measurements, carried out at several home-built magnetoelectric transport measurement systems, including electromagnets, Keithley 2604B current source, and Keithley 2182A voltage meter. The electric transport measurements at different temperatures were carried out using a physical property measurement system (PPMS DynaCool-14T). For the CIMS measurements, a pulsed DC electrical current was applied with a duration of 150 μs by Keithley 6221 current source. After an interval of 3 s for each data point, the Hall voltage was recorded under a small DC excitation current (500 μA). During the measurements of electrical manipulation for the exchange bias, a pulsed DC electrical current with a duration of 80 μs was applied by Keithley 6221 current source.
Polarized neutron reflectometry measurements
The PNR measurements were performed using the Multipurpose Reflectometer at the China Spallation Neutron Source. The experiments were performed under a 1.6 T in-plane magnetic field at RT. The neutron reflectivity curves were recorded as a function of the momentum transfer Q. Neutron beam was impinged onto the sample with an incident angle and was collected by a 3He detector. The collected data were fitted using the GenX software package.
Atomistic simulation
Spin dynamics simulations were performed solving the stochastic Landau–Lifshitz–Gilbert equation with a Heun numerical scheme. A system with Co (1 nm)/IrMn3 (2 nm) containing 147,392 atoms in total was constructed in (111)-oriented with fcc crystalline structure to reproduce the structure in experiments.
Data availability
The datasets generated during and/or analyzed during the current study are available from J.Q. (j.qi@ahu.edu.cn), and are provided in the Source Data file.
Code availability
There is no mathematical algorithm or custom code that is deemed central to the conclusion of this manuscript. However, the custom codes that were simply used for data analysis are available from J.Q. (j.qi@ahu.edu.cn) upon reasonable request.
References
Baltz, V. et al. Antiferromagnetic spintronics. Rev. Mod. Phys. 90, 015005 (2018).
Wadley, P. et al. Electrical switching of an antiferromagnet. Science 351, 587–590 (2016).
Jungwirth, T., Marti, X., Wadley, P. & Wunderlich, J. Antiferromagnetic spintronics. Nat. Nanotechnol. 11, 231–241 (2016).
Nakatsuji, S., Kiyohara, N. & Higo, T. Large anomalous Hall effect in a non-collinear antiferromagnet at room temperature. Nature 527, 212–215 (2015).
Chen, H., Niu, Q. & MacDonald, A. H. Anomalous Hall effect arising from noncollinear antiferromagnetism. Phys. Rev. Lett. 112, 017205 (2014).
Marti, X. et al. Room-temperature antiferromagnetic memory resistor. Nat. Mater. 13, 367–374 (2014).
Park, B. G. et al. A spin-valve-like magnetoresistance of an antiferromagnet-based tunnel junction. Nat. Mater. 10, 347–351 (2011).
Chen, X. et al. Octupole-driven magnetoresistance in an antiferromagnetic tunnel junction. Nature 613, 490–495 (2023).
Childress, J. R. et al. IrMn spin-valves for high density recording. IEEE Trans. Magn. 37, 1745–1748 (2001).
Devasahayam, A. J. & Kryder, M. H. Biasing materials for spin-valve read heads. IEEE Trans. Magn. 35, 649–654 (1999).
Fang, B. et al. Electrical manipulation of exchange bias in an antiferromagnet/ferromagnet‐based device via spin-orbit torque. Adv. Funct. Mater. 32, 2112406 (2022).
Oh, Y. W. et al. Field-free switching of perpendicular magnetization through spin-orbit torque in antiferromagnet/ferromagnet/oxide structures. Nat. Nanotechnol. 11, 878–884 (2016).
Chen, X. et al. Control of spin current and antiferromagnetic moments via topological surface state. Nat. Electron. 5, 574–578 (2022).
Chen, X. et al. Electric field control of Néel spin-orbit torque in an antiferromagnet. Nat. Mater. 18, 931–935 (2019).
Chen, X. et al. Observation of the antiferromagnetic spin Hall effect. Nat. Mater. 20, 800–804 (2021).
Huang, L. et al. Antiferromagnetic inverse spin Hall effect. Adv. Mater. 34, 2205988 (2022).
Peng, S. et al. Exchange bias switching in an antiferromagnet/ferromagnet bilayer driven by spin-orbit torque. Nat. Electron. 3, 757–764 (2020).
Lin, P. H. et al. Manipulating exchange bias by spin-orbit torque. Nat. Mater. 18, 335–341 (2019).
Wang, Y. et al. Time-resolved detection of spin-orbit torque switching of magnetization and exchange bias. Nat. Electron. 5, 840–848 (2022).
Kang, J. et al. Current-induced manipulation of exchange bias in IrMn/NiFe bilayer structures. Nat. Commun. 12, 6420 (2021).
Wei, L. et al. Full electric control of exchange bias at room temperature by resistive switching. Adv. Mater. 30, 1801885 (2018).
Qiu, X. P. et al. Rotation of the pinning direction in the exchange bias training effect in polycrystalline NiFe/FeMn bilayers. Phys. Rev. Lett. 101, 147207 (2008).
Nogués, J. & Schuller, I. K. Exchange bias. J. Magn. Magn. Mater. 192, 203–232 (1999).
Meiklejohn, W. H. & Bean, C. P. New magnetic anisotropy. Phys. Rev. 102, 1413–1414 (1956).
Schuller, I. K., Morales, R., Batlle, X., Nowak, U. & Güntherodt, G. Role of the antiferromagnetic bulk spins in exchange bias. J. Magn. Magn. Mater. 416, 2–9 (2016).
Du, A. et al. Electrical manipulation and detection of antiferromagnetism in magnetic tunnel junctions. Nat. Electron. 6, 425–433 (2023).
Wang, Y. Y. et al. Room-temperature perpendicular exchange coupling and tunneling anisotropic magnetoresistance in an antiferromagnet-based tunnel junction. Phys. Rev. Lett. 109, 137201 (2012).
Kim, H. J., Je, S. G., Jung, D. H., Lee, K. S. & Hong, J. I. Field-free control of exchange bias by spin Hall currents. Appl. Phys. Lett. 115, 022401 (2019).
Zhou, Z. P., Liu, X. H. & Wang, K. Y. Controlling vertical magnetization shift by spin-orbit torque in ferromagnetic/antiferromagnetic/ferromagnetic heterostructure. Appl. Phys. Lett. 116, 062403 (2020).
Stebliy, M. E. et al. Current-induced manipulation of the exchange bias in a Pt/Co/NiO structure. ACS Appl. Mater. Interfaces 13, 42258–42265 (2021).
Zhang, E. Z. et al. Manipulating antiferromagnetic interfacial states by spin-orbit torques. Phys. Rev. B 104, 134408 (2021).
Liu, X. H., Edmonds, K. W., Zhou, Z. P. & Wang, K. Y. Tuning interfacial spins in antiferromagnetic-ferromagnetic-heavy-metal heterostructures via spin-orbit torque. Phys. Rev. Appl. 13, 014059 (2020).
Dong, Y. N. et al. Room temperature manipulation of exchange bias in magnetic heterojunctions. J. Magn. Magn. Mater. 559, 169546 (2022).
Liu, R. et al. Manipulating exchange bias in Ir25Mn75/CoTb bilayer through spin-orbit torque. Appl. Phys. Lett. 122, 062401 (2023).
Arpaci, S. et al. Observation of current-induced switching in non-collinear antiferromagnetic IrMn3 by differential voltage measurements. Nat. Commun. 12, 3828 (2021).
Jenkins, S., Chantrell, R. W. & Evans, R. F. L. Exchange bias in multigranular noncollinear IrMn3/CoFe thin films. Phys. Rev. B 103, 014424 (2021).
Maldonado-Lopez, D., Takeuchi, N. & Guerrero-Sanchez, J. Understanding the noncollinear antiferromagnetic IrMn3 surfaces and their exchange-biased heterostructures from first-principles. ACS Appl. Electron. Mater. 3, 1086–1096 (2021).
Jenkins, S. et al. Atomistic origin of exchange anisotropy in noncollinear γ-IrMn3/CoFe bilayers. Phys. Rev. B 102, 140404 (2020).
Kohn, A. et al. The antiferromagnetic structures of IrMn3 and their influence on exchange-bias. Sci. Rep. 3, 2412 (2013).
Szunyogh, L., Lazarovits, B., Udvardi, L., Jackson, J. & Nowak, U. Giant magnetic anisotropy of the bulk antiferromagnets IrMn and IrMn3. Phys. Rev. B 79, 020403 (2009).
Migliorini, A. et al. Spontaneous exchange bias formation driven by a structural phase transition in the antiferromagnetic material. Nat. Mater. 17, 28–35 (2018).
Ambrose, T. & Chien, C. L. Finite-size effects and uncompensated magnetization in thin antiferromagnetic CoO layers. Phys. Rev. Lett. 76, 1743–1746 (1996).
Petti, D. et al. Storing magnetic information in IrMn/MgO/Ta tunnel junctions via field-cooling. Appl. Phys. Lett. 102, 192404 (2013).
Frangou, L. et al. Enhanced spin pumping efficiency in antiferromagnetic IrMn thin films around the magnetic phase transition. Phys. Rev. Lett. 116, 077203 (2016).
Khan, R. A. et al. Magnetic domain texture and the Dzyaloshinskii-Moriya interaction in Pt/Co/IrMn and Pt/Co/FeMn thin films with perpendicular exchange bias. Phys. Rev. B 98, 064413 (2018).
Ma, X. et al. Dzyaloshinskii-Moriya interaction across an antiferromagnet-ferromagnet interface. Phys. Rev. Lett. 119, 027202 (2017).
Huang, Y. et al. A spin‐orbit torque ratchet at ferromagnet/antiferromagnet interface via exchange spring. Adv. Funct. Mater. 32, 2111653 (2022).
Ali, M., Marrows, C. H. & Hickey, B. J. Onset of exchange bias in ultrathin antiferromagnetic layers. Phys. Rev. B 67, 172405 (2003).
Kim, J. V. & Stamps, R. L. Defect-modified exchange bias. Appl. Phys. Lett. 79, 2785–2787 (2001).
Ling, Y. et al. Strain control of phase transition and exchange bias in flexible Heusler alloy thin films. ACS Appl. Mater. Interfaces 13, 24285–24294 (2021).
Schumacher, D. et al. Inducing exchange bias in La0.67Sr0.33MnO3-δ/SrTiO3 thin films by strain and oxygen deficiency. Phys. Rev. B 88, 144427 (2013).
Wu, D. et al. Spin-orbit torques in perpendicularly magnetized Ir22Mn78/Co20Fe60B20/MgO multilayer. Appl. Phys. Lett. 109, 222401 (2016).
Zhang, W. et al. Giant facet-dependent spin-orbit torque and spin Hall conductivity in the triangular antiferromagnet IrMn3. Sci. Adv. 2, e1600759 (2016).
Zhang, R. & Willis, R. F. Thickness-dependent curie temperatures of ultrathin magnetic films: effect of the range of spin-spin interactions. Phys. Rev. Lett. 86, 2665–2668 (2001).
Yamaoka, T., Mekata, M. & Takaki, H. Neutron diffraction study of antiferromagnetism in face-centered cubic Mn-Ir alloys. J. Phys. Soc. Jpn. 31, 301–301 (1971).
Jang, D. & Atzmon, M. Grain-boundary relaxation and its effect on plasticity in nanocrystalline Fe. J. Appl. Phys. 99, 083504 (2006).
Heo, T. W. & Chen, L. Q. Phase-field modeling of displacive phase transformations in elastically anisotropic and inhomogeneous polycrystals. Acta Mater. 76, 68–81 (2014).
Evans, R. F. L. et al. Atomistic spin model simulations of magnetic nanomaterials. J. Phys. Condens. Matter 26, 103202 (2014).
Evans, R. F. L., Atxitia, U. & Chantrell, R. W. Quantitative simulation of temperature-dependent magnetization dynamics and equilibrium properties of elemental ferromagnets. Phys. Rev. B 91, 144425 (2015).
Yanes, R., Jackson, J., Udvardi, L., Szunyogh, L. & Nowak, U. Exchange bias driven by Dzyaloshinskii-Moriya interactions. Phys. Rev. Lett. 111, 217202 (2013).
Sakuma, A., Fukamichi, K., Sasao, K. & Umetsu, R. Y. First-principles study of the magnetic structures of ordered and disordered Mn-Ir alloys. Phys. Rev. B 67, 024420 (2003).
Meo, A. et al. Thermally nucleated magnetic reversal in CoFeB/MgO nanodots. Sci. Rep. 7, 16729 (2017).
Yu, G. et al. Switching of perpendicular magnetization by spin–orbit torques in the absence of external magnetic fields. Nat. Nanotechnol. 9, 548–554 (2014).
Fukami, S., Zhang, C., DuttaGupta, S., Kurenkov, A. & Ohno, H. Magnetization switching by spin-orbit torque in an antiferromagnet-ferromagnet bilayer system. Nat. Mater. 15, 535–541 (2016).
Acknowledgements
This work was supported by the National Key Research and Development Program of China (Grant 2022YFA1402602), the Natural Science Foundation of China (Grants 52130103, 12104486, 51971026, 12374099, 12174426, 52201200, 52201288), and the Beijing Natural Science Foundation Key Program (Grant Z190007).
Author information
Authors and Affiliations
Contributions
J.Q. and Y.C.Z. contributed equally to this work as the first authors. S.G.W. initialized, conceived, and supervised the project. J.Q. prepared the samples, fabricated devices, and performed measurements with contributions from Y.C.Z., Y.Z., G.Y., H.C.L., and B.K.S. Y.Z. and H.H. performed the atomistic simulations. T.Z. and J.L.L. performed and analyzed the neutron reflectometry. J.Q. and Y.C.Z. wrote the paper with the help of J.Y.Z., G.Q.Y., H.X.W., S.M.Z., B.G.S., and S.G.W. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Paul Steadman, Haiou Wang, and the other anonymous reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Qi, J., Zhao, Y., Zhang, Y. et al. Full electrical manipulation of perpendicular exchange bias in ultrathin antiferromagnetic film with epitaxial strain. Nat Commun 15, 4734 (2024). https://doi.org/10.1038/s41467-024-49214-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-49214-z
- Springer Nature Limited