Abstract
The nodal-line semiconductor Mn3Si2Te6 is generating enormous excitment due to the recent discovery of a field-driven insulator-to-metal transition and associated colossal magnetoresistance as well as evidence for a new type of quantum state involving chiral orbital currents. Strikingly, these qualities persist even in the absence of traditional Jahn-Teller distortions and double-exchange mechanisms, raising questions about exactly how and why magnetoresistance occurs along with conjecture as to the likely signatures of loop currents. Here, we measured the infrared response of Mn3Si2Te6 across the magnetic ordering and field-induced insulator-to-metal transitions in order to explore colossal magnetoresistance in the absence of Jahn-Teller and double-exchange interactions. Rather than a traditional metal with screened phonons, the field-driven insulator-to-metal transition leads to a weakly metallic state with localized carriers. Our spectral data are fit by a percolation model, providing evidence for electronic inhomogeneity and phase separation. Modeling also reveals a frequency-dependent threshold field for carriers contributing to colossal magnetoresistance which we discuss in terms of polaron formation, chiral orbital currents, and short-range spin fluctuations. These findings enhance the understanding of insulator-to-metal transitions in new settings and open the door to the design of unconventional colossal magnetoresistant materials.
Similar content being viewed by others
Introduction
Phase transitions involving electronic heterogeneity are well-established in quantum materials, as evidenced by the way electron correlations lead to Mott systems with insulator-to-metal transitions1,2,3 and low carrier densities generate colossal magnetoresistance (CMR)4,5. These principles were explored in nearly Dirac materials like EuMnSb26, Mott insulating Ti-doped Ca3Ru2O77, and perovskite manganites such as La1−xSrxMnO38,9, and although there is a significant body of work revealing insulator-to-metal transitions triggered by temperature, pressure, and light10,11,12,13,14,15,16, magnetically-driven transitions are particularly attractive due to their ability to support CMR. The latter typically relies upon Jahn-Teller distortions and double-exchange mechanisms, although the recent discovery of Mn3Si2Te6 demonstrates that these interactions are not required, while also introducing a novel quantum state involving chiral orbital currents17 that merits further investigation.
Mn3Si2Te6 hosts trigonal \(P\bar{3}1c\) symmetry with two different Mn(II) sites as well as alternately stacked honeycomb and triangular layers18,19. This nodal line semiconductor displays an insulator-to-metal transition and CMR under a magnetic field for H∥c20,21. Significant magnetic anisotropy arises from strong spin-orbit coupling due to Te orbits coupled with Mn spins; this proximity effect is consistent with strong hybridization between Mn and Te orbitals and is easily perturbed by small dc currents17,20,21,22. Whether Mn3Si2Te6 hosts a spin-rotation-favored insulator-to-metal transition or chiral orbital current state-induced CMR17,21, the majority of measurements thus far involve transport techniques, making it difficult to ascertain the microscopic aspects of the electronic response—especially in the presence of a chiral orbital current that might create electronic localization in combination with spin-phonon coupling, topological nodal-line degeneracy, magnetization anisotropy, and magnetic fluctuations21,23,24,25,26,27,28. Questions have therefore arisen about how itinerary and electron correlations compete with localization and whether carriers are created homogeneously as part of the insulator-to-metal transition and CMR effect. Magneto-infrared spectroscopy is a powerful tool for addressing these issues.
In order to unravel the origin of CMR in a material that does not host Jahn-Teller or double-exchange interactions and to search for spectroscopic signatures of chiral loop currents, we measured the infrared response of Mn3Si2Te6 across the magnetic ordering and insulator-to-metal transitions. Rather than a conventional metal with a Drude response and screened phonons, the field-driven insulator-to-metal transition leads to a weakly metallic state with localized carriers. We discuss this localization in terms of the large polaron model, expectations for chiral orbital currents, and the ability of short-range spin fluctuations to give rise to Slater peaks17,29,30,31,32. The dynamics of these pinned carriers are captured by the percolation model, which emphasizes the ubiquity of electronic heterogeneity in CMR systems. In this case, a frequency-dependent threshold magnetic field accounts for the gradual formation of the weakly metallic high field phase. These findings complement the understanding of bad metal behavior in correlated oxides, reinforce the role of new quantum states in field-driven insulator-to-metal transitions and their CMR effects, and pave the way for the development of unconventional CMR materials.
Results and discussion
Classic semiconducting properties at 300 K and across the ferrimagnetic transition
Figure 1 displays the room temperature reflectance of Mn3Si2Te6 along with the optical conductivity calculated via Kramers-Kronig analysis. σ1(ω) is low and flat, characteristic of a semiconductor, punctuated by a series of sharp phonons and localized electronic excitations at higher frequencies33. Lattice dynamics calculations allow us to assign the phonons, reveal symmetries, and analyze the displacement patterns [Fig. 1b and Supplementary Table 1, Supplementary Information]. Extrapolation of σ1(ω) to zero frequency is in reasonable agreement with the dc conductivity20. The electronic properties are typical of a semiconductor with indirect and direct gaps of 0.43 and 1.73 eV, respectively [Supplementary Note 11]. The gap sizes are similar to those in CrSiTe3 due to the common [Si2Te6]6− cluster anion34,35. We assign the strong electronic features near 20,000 cm−1 shown in the inset to a combination of charge transfer and d-to-d excitations.
To investigate how strongly these phonons interact with the Mn spin system, we measured the infrared response across the ferrimagnetic ordering transition. Figure 2 summarizes the optical conductivity of Mn3Si2Te6 as a function of temperature. Here we show six representative vibrational modes fit by Voigt functions, indicated by the red-shaded area. All of the phonons harden on approach to the magnetic ordering transition [Fig. 2b–g]—a trend that we quantify with a traditional anharmonic model36,37. Below TC = 74 K18, the frequency vs. temperature data deviates from the model curve that typifies the high-temperature phase. This perturbation is characterized by a frequency shift: Δω = λ〈Si ⋅ Sj〉, where λ is the spin-phonon coupling constant, and 〈Si ⋅ Sj〉 is the spin-spin correlation function between the (i,j) nearest neighbors. The latter approaches S2 in the low-temperature limit. The spin-phonon coupling constants that we extract for the infrared-active modes are modest—less than ± 0.25 cm−1 [Supplementary Table 1, Supplementary Information]—similar in size to the λ’s for the Raman-active phonons23. These values are significantly smaller than those in heavy and mixed-metal oxides38 ruling out a substantial role for spin-phonon coupling of q = 0 phonons in the insulator-to-metal transition and CMR effect.
Bad metal behavior in the high-field phase
Having placed the properties of the semiconducting phase on a firm foundation, we turn our attention to the metallic phase of Mn3Si2Te6, using a magnetic field to drive the insulator-to-metal transition. Figure 3a shows the reflectance ratio as a function of magnetic field. This quantity (discussed in Supplementary Note 5) highlights the sharp phonons as well as broad changes in the electronic background. We used these data along with the absolute reflectance at base temperature and zero field to back-calculate the reflectance as a function of magnetic field [Fig. 3b]. The reflectance rises systematically between 3 and 9 T, consistent with transport results that place the insulator-to-metal transition in this range17,21. That said, the rise is nowhere near what is expected for a true metal like copper. Instead of developing a signature Drude response, we see over-damped behavior even at full field (17.5 T), characteristic of a bad metal39,40. We simulate this effect in Supplementary Note 6. At the same time, the phonons remain prominent and are not well-screened. This reveals that Mn3Si2Te6 does not behave as a conventional metal following the field-induced insulator-to-metal transition.
Figure 3c displays the optical conductivity of Mn3Si2Te6 across the insulator-to-metal transition. The most striking feature is the build-up of localized excitations with increasing magnetic field rather than the development of a free carrier (Drude) response. Electronic character is demonstrated by the broad energy range as well as the Fano lineshape of the phonons that ride on top of this band in the high field phase41. That said, the phonon positions are nearly rigid over the entire field range, excluding the lattice as the origin of these effects. Close-up views of these trends and the near-zero spin-phonon coupling constants that result from the absence of a frequency shift across the field-induced insulator-to-metal transition are given in Supplementary Fig. 6 of the Supplementary Note 7.
We can analyze the electronic properties in greater depth by focusing on charge localization. A sum rule analysis of the low energy localized excitation in σ1(ω) yields the oscillator strength trend shown in Fig. 4a. The spectral weight, which is proportional to the effective number of carriers, increases rapidly near 5 T and levels off above 10 T. This growth in the number of carriers aligns nicely with the field-driven insulator-to-metal transition and the associated CMR effect. To better connect charge localization, the number of carriers, and CMR, we examined several fixed-frequency cuts of σ1(ω) along with the dc conductivity from ref. 21. We note in passing that although the field enhances both ac and dc conductivities across the insulator-to-metal transition, the overall magnitude of σdc in the high field phase is not very large, consistent with our picture of Mn3Si2Te6 as a bad metal. Turning back to the analysis of electronic localization in the optical conductivity [Fig. 4b], we see that the ac conductivities at 200 and 400 cm−1 vary across the insulator-to-metal transition in a manner similar to (but broader than) the dc conductivity. This makes sense because σ1(ω → 0) is σdc. By contrast, carriers pinned at 700 cm−1 are not nearly as responsive to the transition. These findings suggest that carriers with frequencies below ≈400 cm−1 may be the primary contributors to CMR.
Unraveling electronic heterogeneity and localization
Electronic heterogeneity plays a foundational role in establishing the properties of CMR manganites. One way to quantify inhomogeneity and phase separation is with the percolation model42. This model, originally developed to describe progressively increasing concentrations of metallic nanoparticles in a dielectric background like glass, has been successfully applied to correlated electron materials like VO2 across the phase transition43, WS2 nanotubes under pressure44, and rare-earth nickelates like NdNiO345. In these modern settings, the percolation model refers to “droplets” of metallicity embedded in a dielectric matrix (which represents a competing phase), as illustrated in the Supplementary Note 10. To focus on the electronic properties (and avoid the phonons), we employ a single-frequency variant of this approach.
We express the percolation model in fixed frequency form as \({\sigma }_{1}({\omega }_{0})={S}_{2}+({S}_{1}-{S}_{2})/(1+{e}^{(H-{H}_{0})/\Delta H})\)44. Here, ω0 is the fixed frequency in question, and σ1(ω0) is a fixed-frequency cut of σ1(ω). S1 and S2 are the fit values of σ1(ω0) at 0 and 17.5 T. H0 defines the percolation threshold at the fixed frequency ω0. The percolation threshold is the critical magnetic field at which the concentration of the metallic phase rises sufficiently to provide long-range connectivity. This is the parameter that gives physical significance to the model. H is magnetic field, and ΔH represents the slope of the curve (or the range over which percolation persists—from zero to full percolation). As shown in Fig. 4b, trends in σ1(ω0) vs. H are perfectly captured with fits to the model, demonstrating that the shape of the insulator-to-metal transition is a consequence of electronic heterogeneity. This means that the insulator-to-metal transition begins with a small amount of metallic phase embedded in a dielectric matrix, and with increasing magnetic field, the concentration of the metallic phase grows while that of the semiconducting phase diminishes. The fact that magnetization is not fully saturated at 17.5 T20,21,26 is consistent with our picture of an under-developed metallic phase above the insulator-to-metal transition.
Figure 4c shows the percolation threshold of Mn3Si2Te6 as a function of frequency extracted from the percolation model fits in Fig. 4b. The trend demonstrates that carriers react based on their degree of localization. Low-frequency carriers respond quickly to magnetic fields and reach their percolation threshold by 4 T, whereas the higher-frequency carriers react more slowly and require larger fields to become mobile. In fact, examination reveals that carriers with frequencies below 400 cm−1 exhibit a percolation threshold field between 3 and 4 T where dc resistance is already suppressed by >97.5%20. On the other hand, carriers above 400 cm−1 host percolation thresholds increase with frequency—a tendency that creates an uneven magnetic field response in σ1(ω) [Fig. 3c]. This distribution of percolation thresholds explains why the insulator-to-metal transition is so broad and why the conductivity is not fully developed even in fields that ought to place the material well above the transition. Mn3Si2Te6 is a clean system without mixed valencies or doping, so carriers that are less responsive to applied field are what keep the system in an electronically localized state even above the insulator-to-metal transition.
Modeling the localized excitation: large polaron, chiral loop currents, or short-range spin fluctuations
The field-driven development of the localized electronic excitation suggests that there may be important vibronic interactions or distortions of the magnetic order that pin the charge to the lattice or spin texture in the form of lattice or magnetic polarons46,47,48. A polaronic-like structure has already been observed at lower energies (~40 cm−1) under high fluences33, making it logical that additional polaronic excitations can be created in this material. Certainly, our measurements reveal strong field-induced charge localization in the optical conductivity, and electron-phonon coupling is evidenced by the Fano line shape of the in-plane Si stretching modes near 365 cm−1 [Fig. 3c]. We tested this hypothesis by fitting a large polaron model29,30,31 to the optical conductivity of Mn3Si2Te6 at 17.5 T. As shown in Fig. 4d, a single large polaron model fits the spectrum reasonably well. We extract a radius of ~6 Å, an effective mass of 1.1me, an absorption threshold of 90 cm−1, and a polaron density of np = 1.8 × 1019 cm−3. Within this picture, the presence of the polaron is attributable to the low carrier density originating from Mn-Te hybridization near the Fermi level22,49 combined with the overall charge transfer character of the material. The limited mobility of this structure is what constrains the development of a more traditional metallic response, although it is still sufficient to produce a CMR effect. We emphasize that the large polaron model is likely a major simplification and that the shape of the bound state is very sensitive to our choices of polaron size, mass, and density. The impact of these parameters is discussed in Supplementary Note 7. In any case, after revealing the behavior of Mn3Si2Te6 in a magnetic field and unveiling a competing state via a percolative process, the next challenge is to study this state further and to render it stable at zero magnetic field by chemical substitution.
The fact that phonons are rigid under a magnetic field suggests that we should consider mechanisms beyond charge or spin polaron models. An alternative framework for understanding the presence of localized carriers in the high field phase of Mn3Si2Te6 involves the presence of chiral orbital currents flowing along the edges of the MnTe6 octahedra17. The loop currents themselves are presumably in the ab-plane, and the moment is generated along c. Carriers pinned near 300 cm−1 are consistent with this picture, and based on the resonance frequency, we expect an average loop size on the order of microns. A similar phase is present in smectic metals where current flowing along specific chains displays localization induced by strong interactions50. Time-dependent bistable switching17 and the slow development of magnetization (while changes in the dc resistivity are sharp)20 are consistent with this picture.
A different approach to understanding magneto-infrared effects in Mn3Si2Te6 involves Slater peaks due to short-range spin excitations. Slater argued51 that the insulating gap can occur solely due to antiferromagnetic order rather than strong on-site Coulomb repulsion. Such a system is called a Slater insulator. Later theoretical work32 showed that short-range spin fluctuations are sufficient to produce narrow Slater peaks at the edge of the gap near the metal-insulator transition of the Hubbard model, which almost continuously closes the gap at the metal-insulator transition32,51. Such excitations come from short-range order and yield a localized excitation in the optical conductivity. One characteristic of the Slater mechanism is the relative entropy between competing states. Typically, the metallic phase has larger entropy than the insulating phase, although in our case, analysis reveals that the entropies are similar52,53. More work is obviously needed to clarify the matter, especially real space spectroscopies to unravel electronic inhomogeneities and neutron scattering to determine whether the localized excitation has a magnetic origin.
Methods
Reflectance measurements
High-quality single crystals of Mn3Si2Te6 were grown by flux techniques21 and polished to expose the ab-plane. Near-normal reflectance was measured between 22 and 55,000 cm−1 using a series of spectrometers, and a Kramers-Kronig analysis provided the optical constants54. Here, we focus on the real part of optical conductivity (σ1(ω)). Temperature was controlled with an open-flow cryostat. The magnetic field was applied using a 17.5 T superconducting magnet (H∥c) at the National High Magnetic Field Laboratory in Tallahassee, FL.
Lattice dynamic calculations
First-principles calculations were performed using density functional theory as implemented in Vienna ab initio simulation package55,56,57 with the projector-augmented wave method57,58 and the Perdew-Burke-Ernzerhof 59 exchange-correlation function. The DFT-D2 method60 provided the van der Waals correction on a Γ centered 10 × 10 × 6k-point grid with a plane-wave cutoff energy of 500 eV. The internal coordinates of the experimental structure19 were relaxed with ferrimagnetic52 constraints and the vibrational modes were obtained using the finite difference method. Details are available in Supplementary Information.
Data availability
All raw data generated in this study are provided in the Source Data file. Source data are provided with this paper.
Code availability
All custom codes used in this study are available from the authors upon request.
References
McWhan, D. B. et al. Electronic specific heat of metallic Ti-doped V2O3. Phys. Rev. Lett. 27, 941–943 (1971).
Imada, M., Fujimori, A. & Tokura, Y. Metal-insulator transitions. Rev. Mod. Phys. 70, 1039–1263 (1998).
Gray, A. X. et al. Correlation-driven insulator-metal transition in near-ideal vanadium dioxide films. Phys. Rev. Lett. 116, 116403 (2016).
Ramirez, A. Colossal magnetoresistance. J. Condens. Matter Phys. 9, 8171 (1997).
Majumdar, P. & Littlewood, P. Magnetoresistance in Mn pyrochlore: electrical transport in a low carrier density ferromagnet. Phys. Rev. Lett. 81, 1314–1317 (1998).
Sun, Z. et al. Field-induced metal-to-insulator transition and colossal anisotropic magnetoresistance in a nearly Dirac material EuMnSb2. npj Quantum Mater. 6, 94 (2021).
Zhu, M. et al. Colossal magnetoresistance in a Mott insulator via magnetic field-driven insulator-metal transition. Phys. Rev. Lett. 116, 216401 (2016).
Urushibara, A. et al. Insulator-metal transition and giant magnetoresistance in La1−xSrxMnO3. Phys. Rev. B 51, 14103–14109 (1995).
Cooper, S. L. Optical spectroscopic studies of metal-insulator transitions in perovskite-related oxides, 161–219 (Springer Berlin Heidelberg, Berlin, Heidelberg, 2001).
Kuneš, J. et al. Metal-insulator transition in NiS2−xSex. Phys. Rev. B 81, 035122 (2010).
Kuwahara, H., Tomioka, Y., Asamitsu, A., Moritomo, Y. & Tokura, Y. A first-order phase transition induced by a magnetic field. Science 270, 961–963 (1995).
Kübler, C. et al. Coherent structural dynamics and electronic correlations during an ultrafast insulator-to-metal phase transition in VO2. Phys. Rev. Lett. 99, 116401 (2007).
Inoue, I. H., Goto, O., Makino, H., Hussey, N. E. & Ishikawa, M. Bandwidth control in a perovskite-type 3d1-correlated metal Ca1−xSrxVO3. I. Evolution of the electronic properties and effective mass. Phys. Rev. B 58, 4372–4383 (1998).
Nakamura, F. et al. From Mott insulator to ferromagnetic metal: a pressure study of Ca2RuO4. Phys. Rev. B 65, 220402 (2002).
Lee, J. S., Krockenberger, Y., Takahashi, K. S., Kawasaki, M. & Tokura, Y. Insulator-metal transition driven by change of doping and spin-orbit interaction in Sr2IrO4. Phys. Rev. B 85, 035101 (2012).
Feng, Y. et al. A continuous metal-insulator transition driven by spin correlations. Nat. Commun. 12, 2779 (2021).
Zhang, Y. et al. Control of chiral orbital currents in a colossal magnetoresistance material. Nature 611, 467–472 (2022).
Liu, Y. & Petrovic, C. Critical behavior and magnetocaloric effect in Mn3Si2Te6. Phys. Rev. B 98, 064423 (2018).
Vincent, H., Leroux, D., Bijaoui, D., Rimet, R. & Schlenker, C. Crystal structure of Mn3Si2Te6. J. Solid State Chem. 63, 349–352 (1986).
Ni, Y. et al. Colossal magnetoresistance via avoiding fully polarized magnetization in the ferrimagnetic insulator Mn3Si2Te6. Phys. Rev. B 103, L161105 (2021).
Seo, J. et al. Colossal angular magnetoresistance in ferrimagnetic nodal-line semiconductors. Nature 599, 576–581 (2021).
Zhang, Y., Lin, L.-F., Moreo, A. & Dagotto, E. Electronic structure, magnetic properties, spin orientation, and doping effect in Mn3Si2Te6. Phys. Rev. B 107, 054430 (2023).
Kwon, C. I. et al. Raman signatures of spin-phonon coupling in a self-intercalated van der Waals magnet Mn3Si2Te6. Curr. Appl. Phys. 53, 51–55 (2023).
Mijin, S. D. et al. Spin-phonon interaction and short-range order in Mn3Si2Te6. Phys. Rev. B 107, 054309 (2023).
Olmos, R. et al. Critical phenomena of the layered ferrimagnet Mn3Si2Te6 following proton irradiation. J. Appl. Phys. 130, 013902 (2021).
Ye, F. et al. Magnetic structure and spin fluctuations in the colossal magnetoresistance ferrimagnet Mn3Si2Te6. Phys. Rev. B 106, L180402 (2022).
Martinez, L. M. et al. Coherent spin-phonon coupling in the layered ferrimagnet Mn3Si2Te6. arXiv https://arxiv.org/abs/2308.14931 (2023).
Zhang, Y. et al. Current-sensitive Hall effect in a chiral-orbital-current state. Nat. Commun. 15, 3579 (2024).
Emin, D. Optical properties of large and small polarons and bipolarons. Phys. Rev. B 48, 13691 (1993).
Dixit, A., Chen, P., Lawes, G. & Musfeldt, J. L. Electronic structure and polaronic excitation in FeVO4. Appl. Phys. Lett. 99, 141908 (2011).
Hartinger, C., Mayr, F., Deisenhofer, J., Loidl, A. & Kopp, T. Large and small polaron excitations in La2/3(Sr/Ca)1/3MnO3 films. Phys. Rev. B 69, 100403 (2004).
Park, H., Haule, K. & Kotliar, G. Cluster dynamical mean field theory of the Mott transition. Phys. Rev. Lett. 101, 186403 (2008).
Wu, Q. et al. Pump-induced terahertz conductivity response and peculiar bound state in Mn3Si2Te6. Adv. Opt. Mater. 12, 2301863 (2023).
Siberchicot, B., Jobic, S., Carteaux, V., Gressier, P. & Ouvrard, G. Band structure calculations of ferromagnetic chromium tellurides CrSiTe3 and CrGeTe3. J. Phys. Chem. 100, 5863–5867 (1996).
Casto, L. et al. Strong spin-lattice coupling in CrSiTe3. APL Mater. 3, 041515 (2015).
Balkanski, M., Wallis, R. & Haro, E. Anharmonic effects in light scattering due to optical phonons in silicon. Phys. Rev. B 28, 1928 (1983).
Gu, Y. et al. Phonon mixing in the charge density wave state of ScV6Sn6. npj Quantum Mater. 8, 58 (2023).
Park, K. et al. Spin–phonon interactions and magnetoelectric coupling in Co4B2O9 (B= Nb, Ta). Appl. Phys. Lett. 122, 182902 (2023).
Gervais, F. Optical conductivity of oxides. Mater. Sci. Eng. R: Rep. 39, 29–92 (2002).
Petit, N., Soret, J.-C. & Gervais, F. Analysis of concentration dependence of optical conductivity of BaPb1−xBixO3 revisited. Solid State Commun. 110, 621–626 (1999).
Fano, U. Effects of configuration interaction on intensities and phase shifts. Phys. Rev. 124, 1866–1878 (1961).
Carr, G., Perkowitz, S. & Tanner, D. Far-infrared properties of inhomogeneous materials. Infrared Millim. Waves 13, 171–263 (1985).
Qazilbash, M. M. et al. Mott transition in VO2 revealed by infrared spectroscopy and nano-imaging. Science 318, 1750–1753 (2007).
O’Neal, K. R. et al. High pressure vibrational properties of WS2 nanotubes. Nano Lett. 16, 993–999 (2016).
Preziosi, D. et al. Direct mapping of phase separation across the metal–insulator transition of NdNiO3. Nano Lett. 18, 2226–2232 (2018).
Furdyna, J. K. Diluted magnetic semiconductors. J. Appl. Phys. 64, R29–R64 (1988).
Kuivalainen, P., Sinkkonen, J. & Stubb, T. Magnetic polarons in magnetic semiconductors. Int. J. Quantum Chem. 20, 507–519 (1981).
Kozyrev, N. et al. Optical manifestation of magnetic polarons bound to excitons and resident holes in a (Cd, Mn) Te quantum well. Phys. Rev. B 104, 045307 (2021).
Bigi, C. et al. Covalency, correlations, and interlayer interactions governing the magnetic and electronic structure of Mn3Si2Te6. Phys. Rev. B 108, 054419 (2023).
Donos, A. & Hartnoll, S. A. Interaction-driven localization in holography. Nat. Phys. 9, 649–655 (2013).
Slater, J. C. Magnetic effects and the Hartree-Fock equation. Phys. Rev. 82, 538–541 (1951).
May, A. F. et al. Magnetic order and interactions in ferrimagnetic Mn3Si2Te6. Phys. Rev. B 95, 174440 (2017).
Liu, Y. et al. Polaronic transport and thermoelectricity in Mn3Si2Te6 single crystals. Phys. Rev. B 103, 245122 (2021).
Wooten, F. Optical properties of solids (Academic Press, 1972).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
Grimme, S. Semiempirical GGA-type density functional constructed with a long-range dispersion correction. J. Comput. Chem. 27, 1787–1799 (2006).
Acknowledgements
Research at Tennessee is supported by Physical Behavior of Materials, Basic Energy Sciences, U.S. Department of Energy (DE-SC00023144). The work at Postech was supported by the National Research Foundation of Korea (NRF), funded by the Ministry of Science and ICT (No. 2022M3H4A1A04074153). The work at the University of Minnesota was funded by the Department of Energy through the University of Minnesota Center for Quantum Materials, under DE-SC0016371. Y.Z., L.L., and E.D. were supported by the U.S. Department of Energy, Office of Science, Basic Energy Sciences, Materials Sciences and Engineering Division. SWC is supported by the Center for Quantum Materials Synthesis (cQMS), funded by the Gordon and Betty Moore Foundation’s EPiQS initiative through GBMF10104 and by Rutgers University. KH thanks the National Science Foundation (DMR-2233892) for support. Work at Brookhaven National Laboratory (BNL) used the Infrared Lab at the National Synchrotron Light Source II, a U.S. Department of Energy (DOE) Office of Science User Facility operated for the DOE Office of Science by BNL under Contract No. DE-SC0012704. The National High Magnetic Field Laboratory in Tallahassee is supported by NSF Cooperative Agreement DMR-2128556 and the State of Florida.
Author information
Authors and Affiliations
Contributions
Y.G. and J.L.M. designed the study. C.D., C.W., and S.W.C. grew and characterized the crystals. Y.G. and C.H. studied sample aging and developed techniques to eliminate the surface TeO2 layer. Y.G. carried out reflectance measurements as a function of temperature. Y.G., K.S., M.O., and J.L.M. performed the magneto-infrared measurements. A.S., Y.Z., and L.F.L. performed lattice dynamics calculations and discussed the results with T.B. and E.D. Y.G. analysed the spectral data with guidance from J.L.M. S.W.C., E.D., and J.L.M. guided the discussion of percolation theory, Y.G. carried out the fits, and K.H. evaluated the Slater mechanism. Y.G., A.S., and J.L.M. wrote the manuscript. All authors commented on the text.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License, which permits any non-commercial use, sharing, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if you modified the licensed material. You do not have permission under this licence to share adapted material derived from this article or parts of it. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by-nc-nd/4.0/.
About this article
Cite this article
Gu, Y., Smith, K.A., Saha, A. et al. Unconventional insulator-to-metal phase transition in Mn3Si2Te6. Nat Commun 15, 8104 (2024). https://doi.org/10.1038/s41467-024-52350-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-52350-1
- Springer Nature Limited