Abstract
The interplay of nearly degenerate orders in quantum materials can lead to a myriad of emergent phases. A prominent case is that of the high-Tc cuprates for which the relationship between superconductivity and a short-ranged, incommensurate charge density wave in the CuO2 planes involving the \(d_{x^2 - y^2}\) orbitals (Cu-CDW) is a subject of great current interest. Strong modifications of the strength and coherence of this Cu-CDW have been achieved by applying large magnetic fields, uniaxial pressure, or via the interfacial coupling in cuprate/manganite multilayers. However, such modifications do not alter the dominant orbital character. Here we investigate cuprate/manganite multilayers with resonant inelastic X-ray scattering (RIXS) and show that a new kind of Cu-based density wave order can be induced that has not been previously observed in the cuprates. This order has an unusually small in-plane wave vector in the range of Q|| < 0.1 reciprocal lattice units (r.l.u.), a large correlation length of about 40 nm, and a predominant \(d_{z^2}\) orbital character, instead of the typical \(d_{x^2 - y^2}\) one. Its appearance is determined by the hole doping of the manganite which is a key parameter controlling the interfacial charge transfer and orbital reconstruction. We anticipate that the observation of a previously unknown type of density wave order at the YBCO interface will allow for fresh perspectives on the enigmatic relation between superconductivity and charge order (CO) in the cuprates.
Similar content being viewed by others
Introduction
The complex phase diagram of the cuprate high-Tc superconductors is a prime example of the varied properties of strongly correlated quantum materials that arise from competing orders and nearly degenerate ground states1. Besides the enduring puzzle of the superconducting pairing mechanism, the exact nature of the normal state in these materials remains elusive. In particular, in the underdoped regime where a so-called pseudogap depletes the low-energy electron states already well above Tc2,3,4, various spin and/or charge orders have been found to coexist with superconductivity. Intense studies have been carried out on the remnants of antiferromagnetic (AF) correlations in the strongly underdoped regime5,6 and on the so-called stripe order with coupled spin and charge modulations in La1.875Ba0.125CuO47,8. More recently, the focus has shifted to an incommensurate Cu-CDW order that was first observed in underdoped YBa2Cu3O7-δ (YBCO)9,10, and, meanwhile, also in several other compounds. In bulk samples at ambient conditions this static Cu-CDW, with a wave vector of Q|| ≈ 0.25–0.3 reciprocal lattice units (r.l.u.) and \(d_{x^2 - y^2}\) orbital character, is relatively weak and short-ranged. Its relationship with superconductivity remains controversial, with the proposed scenarios ranging from simple competition11, over intertwined orders such as the enigmatic pair-density wave state12,13, to a superconducting pairing mechanism that is mediated by CDW-fluctuations14,15,16. It is still debated whether the short-range CDW correlations are driven by Fermi-surface nesting17, or rather by a tendency towards charge segregation provoked by strong electronic correlations16. However, the recent observation of a re-entrant Cu-CDW with a small wave vector of Q|| = 0.15 r.l.u. in strongly overdoped Bi-2201 is difficult to reconcile with a pure nesting scenario16.
Various successful attempts have been undertaken to enhance and modify the Cu-CDW in order to further explore its origin and relationship with superconductivity. In underdoped YBCO, the strength and the correlation length of the Cu-CDW with Q|| ≈ 0.3 r.l.u. have been strongly enhanced by applying large magnetic fields that suppress superconductivity18,19 or uniaxial pressure along the a-axis, which enhances the orthorhombicity, but suppresses SC only partially20. In both cases, there appears to be a strong competition between SC and the long-range CDW. A strong enhancement of the Cu-CDW with Q|| ≈ 0.3 r.l.u. has also been achieved in YBCO/manganite multilayers for which the competition with superconductivity appears to be weak21. Moreover, for YBCO/ Nd1-x(Ca1-ySry)xMnO3 (YBCO/NCSMO) multilayers with x = 0.35, it has been demonstrated that the magnitude of the Cu-CDW can be strongly modified via the tolerance factor (or the Sr content) NCSMO, which controls its intrinsic charge and orbital (CO) order22.
The YBCO layers of the latter YBCO/NCSMO multilayers have anomalous superconducting properties. For multilayers for which the tolerance factor, t (or the Sr content, y) of the manganite is small enough to induce an insulating state with CE-type charge and orbital (Mn-CO) order, the YBCO layers exhibit a granular superconducting state which gives rise to an insulator-like upturn of the resistance below Tc, instead of the expected drop to zero resistance22,23,24. This unusual behavior occurs only in multilayers for which the thickness of the YBCO layer is below a critical value of dYBCO ≤ 7−8 nm and where the manganite layers display the Mn-CO23,25. Notably, a coherent SC response below Tc can be restored here by the application of a large magnetic field25, which is known to weaken and suppress the Mn-CO of the manganite. This unusual kind of magnetic-field-induced transition from an insulating to a superconducting state is absent in corresponding Nd1-x(Ca1-ySry)xMnO3/ YBa2Cu3O7/ Nd1-x(Ca1-ySry)xMnO3 (NYN) multilayers for which the manganite has a larger tolerance factor (Sr content, y) and thus an itinerant ferromagnetic instead of the Mn-CO ground state24. These trends suggest that the granular superconducting state of the YBCO layers is induced by a proximity effect due to the coupling with the Mn-CO of the adjacent manganite layers. While the interfacial coupling mechanism remains to be established, is seems likely that the concomitant induced (or strongly enhanced) Cu-CDW order in the YBCO layer plays an important role in the formation of the granular superconducting state.
This calls for further studies of the relationship between the manganite and cuprate charge/orbital orders in these multilayers. In the following, we present a combined resonant inelastic and elastic X-ray spectroscopy (RIXS and REXS) and X-ray absorption spectroscopy (XAS) study at the Cu L3-edge of a NYN trilayer with x = 0.5 and y = 0.25. In this sample, the hole doping of the manganite has been adjusted to obtain a long-ranged Mn-CO order, unlike the previously studied multilayers with x = 0.3–0.35 for which the Mn-CO is strongly disordered24,25. To our surprise we find that a new kind of Cu-based order is induced in the YBCO layer that has an unusually short wave vector in the range of Q|| ≈ 0.09–0.096 r.l.u., a large correlation length of about 40 nm, and a predominant \(d_{z^2}\) character, rather than the standard \(d_{x^2 - y^2}\) one. Moreover, we identify the hole doping of the manganite layers as a key parameter that determines not only its own charge/orbital and magnetic order, but also allows modification of the interfacial charge transfer and the occupation of the \(d_{z^2}\) orbitals in the interfacial CuO2 planes. Our observations provide insights into the interfacial coupling between the Mn- and Cu-based charge and magnetic orders, and they suggest a new route to induce coupled quantum states in these cuprate/manganite multilayers.
Results
Different Bragg peaks of elastic RIXS signal at x = 0.5 and 0.35
Figure 1a shows a sketch of a NYN trilayer and the scattering geometry of the RIXS setup. The scattering angle between the incident (kin) and scattered (kout) X-ray beams (Ψ = 130°), and the resulting magnitude of the scattering vector Q = kin − kout are kept fixed during the experiment. The in-plane component Q|| is varied here by rotating the sample, and is zero at specular reflection, when the angles α and β are equal (see Fig. 1a). The corresponding variation of the out-of-plane component Q⊥ is not considered in the following, since the Cu-based order is expected to be quasi-two-dimensional. Typical RIXS intensity spectra of the outgoing scattered photons as a function of their energy loss (ΔE) are displayed in Fig. 1b for different in-plane momentum transfer values. In the present case, the incident energy is resonant with the Cu L3-edge (i.e., resonant with a Cu 2p to 3d transition).
As a consequence, the elastic signal at ΔE = 0 is very sensitive to the scattering from the Cu-3d valence electrons and is used in the following to probe the Bragg peak of the charge/spin order of the Cu ions. The inelastic signal at ΔE < 0 is not further discussed here, but contains rich information on phonons, magnons, and crystal field excitations between the Cu-3d levels that will be presented elsewhere. As can be clearly observed in the raw data, a significant enhancement of the elastic peak is found within a particular range of Q|| values, signifying the occurrence of a Bragg peak, and hence an underlying order.
The Q|| dependence of the elastic signal of the NYN trilayer with x = 0.5 is analyzed in more detail in Fig. 1c, revealing a pronounced Bragg peak at an in-plane wave vector of Q|| ≈ −0.096 r.l.u. To obtain this curve, the RIXS spectra in Fig. 1b at different in-plane scattering vectors are obtained by rotating the sample with respect to the beam. The elastic part of the RIXS spectra is then summed to give the total elastically scattered intensity. Interestingly, the observed Bragg peak occurs at a much smaller wave vector than the one due to the ordinary Cu-CDW of YBCO, which is expected at Q|| ≈ ±0.3 r.l.u.10. The scan over a wider Q||-range in Fig. 1d reveals that no Bragg peak around Q|| ≈ 0.3 r.l.u. occurs for the x = 0.5 NYN trilayer. Also shown, for comparison, are the data of a NYN trilayer with x = 0.35 and y = 0.2 (green symbols) for which a pronounced Bragg peak is observed at Q|| ≈ −0.33 r.l.u.22. Correspondingly, from REXS data (see Supplementary Fig. 10, Supplementary Material), the x = 0.35 NYN trilayer shows no Bragg peak around Q|| ≈ −0.096 r.l.u. This observation of mutually exclusive Bragg peaks in the x = 0.5 and x = 0.35 NYN trilayers implies that the underlying orders are of different nature and are controlled by the hole doping of the manganite layers.
Comparably small ordering wave vectors as observed in the x = 0.5 NYN trilayer have only been reported for strongly overdoped Bi-2201 with Q|| ≈ 0.15 r.l.u.16, and for the spin component of the so-called stripe order of LBCO with Q|| ≈ 0.125 r.l.u.7,8. The Bragg peak in the present case is also rather narrow with a half-width at half-maximum of ΔQ|| ≈ 0.003 r.l.u. corresponding to a correlation length of \(\xi = a\left( {\pi {\Delta}Q_{||}} \right)^{ - 1}\) ≈ 39 nm (using the in-plane lattice parameter a = 3.87 Å of the La0.3Sr0.7Al0.65Ta0.35O3 (LSAT) substrate). This value is about an order of magnitude larger than for YBCO bulk or thin film samples, with the exception of the 3D-CDW that can be induced with high magnetic field18,19 and uniaxial pressure20.
Polarization dependence of Bragg peak at x = 0.5
Further evidence of the distinct nature of the Cu-based order underlying the Bragg peak at Q|| ≈ 0.096 r.l.u. comes from measurements obtained at different polarizations, and from comparing the enhancement of the peak obtained on either side of Γ-point of the Brillouin zone (Fig. 1d, inset). The elastic scattering intensity measured in a RIXS experiment depends on geometric factors and the orbital character of the states involved in the scattering process. Particularly relevant are the electric field component of the X-ray beams with respect to the scattering plane (π or σ polarization), and the incident angle of the beam with respect to the sample surface (grazing incidence or grazing exit beam, see Fig. 1a). The latter of these defines the surface projection of the momentum transferred during the RIXS process, and hence the position in the Brillouin zone. The effect of these factors will clearly vary depending on the orbital symmetry involved in the scattering process, e.g., in-plane \(d_{x^2 - y^2}\) or out-of-plane \(d_{z^2}\). Therefore, obtaining measurements under different geometries and comparing with scattering cross-section calculations for specific orbitals, allows the determination of the dominant orbital symmetry for a particular scattering process. Figure 2a, b shows the Q|| scans at 930.4 eV for π and σ polarization in grazing incidence (incident angle > 0) and grazing exit (incident angle < 0) geometries. The overlaid fits of the Bragg peak are obtained using a Lorentzian line-shape and an exponential background; dashed gray lines show the background contribution. We observe that the Bragg peak enhancement is considerably larger for π-polarization than for σ-polarization for both grazing incidence and exit geometries. This corresponds to a complete reversal compared with previous reports of \(d_{x^2 - y^2}\) order10,16, where σ-polarization shows the strongest signal. This suggests that the behavior underlying the newly observed Bragg peak corresponds to a different orbital symmetry than in previous observations. This finding is further highlighted in Fig. 2c, which compares the maximum Bragg peak intensities (symbols) obtained under the different scattering conditions presented in Fig. 2a, b with the corresponding calculated RIXS cross-sections as a function of δ. By comparing the expectations of the RIXS cross-sections for a \(d_{x^2 - y^2}\) orbital under the same scattering conditions as in the experiment, see Fig. 2c, it is immediately clear that the observed geometric dependence cannot be explained by a dominant \(d_{x^2 - y^2}\) orbital character that is typically observed in the cuprates.
Instead, the enhancement of the Bragg peak intensity with out-of-plane light polarization indicates the participation of \(d_{z^2}\) orbitals. Indeed, we find a reasonable agreement with the calculated RIXS cross-sections for scattering into \(d_{z^2}\) states with a spin-flip process. The calculated curves for spin-flip processes with spins oriented along [001] are shown in Fig. 2d, and are again compared with the measured Bragg peak intensities. In particular, the spin-flip scattering involving \(d_{z^2}\) orbitals correctly predicts the observed reversal of cross-sections compared with the \(d_{x^2 - y^2}\) case in Fig. 2c. This therefore implies a dominant role of the out-of-plane \(d_{z^2}\) orbitals in the Q|| = 0.096 r.l.u. order. In the supplementary materials (Supplementary Note 4 and Supplementary Fig. 3), we present comparisons between additional orbital symmetries and the observed geometric dependence. These reveal that \(d_{z^2}\) orbitals with spins pointing along either [001] or [110] can reproduce the reversed cross-section behavior with respect to \(d_{x^2 - y^2}\) orbitals. We also present there the case of \(d_{z^2}\) orbitals without a spin-flip process, i.e., involving only charge scattering. Although the agreement with the experimental data is better than for the case of \(d_{x^2 - y^2}\) orbitals, it is still worse than for the case of \(d_{z^2}\) orbitals with a spin-flip process. Furthermore, the calculations highlight that no configuration with in-plane \(d_{x^2 - y^2}\) orbitals comes close to reproducing the observed polarization- and angular-dependence of the Bragg peaks. Differentiating the possible spin scenarios, and whether there is mixed charge and spin character to the order, will require additional experimental input, such as a polarization analysis of the scattered X-rays that goes beyond the scope of the present work.
The present results therefore establish that the x = 0.5 NYN trilayer hosts a new kind of incommensurate Cu-based order that strongly involves the \(d_{z^2}\) orbitals and likely has a mixed spin/charge character. In the following, we denote it for simplicity as Cu-\(d_{z^2}\) order.
Resonant elastic X-ray scattering (REXS) study of the Bragg peak at x = 0.5
The Bragg peak of the x = 0.5 NYN trilayer due to the Cu density wave order at Q|| ≈ −0.096 r.l.u. and its unusual polarization dependence have also been observed with REXS experiments26,27. In a REXS experiment the energy of the diffracted X-rays is not analyzed, the Bragg peak of the elastic signal is therefore superimposed on a background that includes the inelastic signal and thus is larger than in RIXS. The scattering geometry of the REXS experiment was adjusted to probe the Bragg peak in the same configuration as in the RIXS experiments, i.e., at (H K L) = (−0.096, 0, 1.56). The value of H was scanned while keeping K and L constant by rotating the sample as well as the detector to vary the angle of incidence on the sample θ and the scattering angle 2θ. Note that L = 1.56 is close to the expected broad maximum of the Bragg-peak of the quasi-2D CDW order at L = 1.5, especially considering the finite size broadening of ΔQ⊥ = 0.053 r.l.u. that arises from the small thickness of the YBCO layer of only 6 unit cells.
Figure 3 displays a wide-range H-scan at 9 K for both π and σ polarizations, which confirms that the Bragg peak due to the Cu-\(d_{z^2}\) order occurs on both sides of the specular peak at (±0.094, 0, 1.56). Moreover, it shows for both polarizations how the background has been accounted for with a polynomial function. Figure 3b displays the background subtracted response for both polarizations, which highlights a large difference between π and σ polarization in the intensity of the Bragg peaks that confirms the trend seen in the RIXS data evidencing a predominant \(d_{z^2}\) orbital character of this Cu density wave order, as discussed in the previous section and shown in Fig. 2. Note that the width of the Bragg peak in the REXS data is larger than for the RIXS data in Fig. 1. We suspect that this difference is due to a lateral variation of the Bragg peak position and the larger beam spot for the REXS experiments (H × V: 100 μm × 50 μm) as compared to RIXS (H × V: 52 μm × 4 μm). Evidence for a variation of the Bragg-peak position in the range of Q|| = 0.09–0.1 r.l.u. is indeed seen in the RIXS data, e.g., in Fig. 2 where the values differ between −Q and +Q and in the SOM (see Supplementary Fig. 6). Note that the RIXS data in the range of ΔE < 0.5 eV do not show any inelastic component (see the intensity map in Fig. 1c) that might be peaked around Q|| ≈ 0.09–0.1 r.l.u. and thus might contribute to the peak seen in REXS.
Figure 3c−e displays representative curves of a temperature scan of the Bragg peak that was performed in π-polarization. The background has been described with a simpler, linear function that also provides a reasonable description of the background of the full scan around the specular peak (π-polarization, in Fig. 3a). Both the Bragg peak due to the charge order and the specular peak at H = 0 have been described with Gaussian functions. The temperature dependence of the obtained position and area of the Bragg peak is displayed in Fig. 3f, g. It reveals that the Bragg peak due to the static Cu-\(d_{z^2}\) order persists to rather high temperature and vanishes well above 170 K. The Cu-\(d_{z^2}\) order thus has a somewhat higher onset temperature than the Cu-CDW with \(d_{x^2 - y^2}\) character, which develops rather gradually below 150 K in bulk YBCO10,11 and in the range from 120 to 175 K in corresponding YBCO/manganite heterostructures with x = 0.3−0.3521,22.
XAS and resonance of RIXS Bragg peak
We have complemented the above results with X-ray absorption spectroscopy (XAS) measurements that reveal important differences between the NYN trilayers for x = 0.5 and x = 0.35 with respect to the strength of the interfacial charge transfer and orbital reconstruction. Figure 4a shows a sketch of the XAS experiment with X-rays in π or σ polarization and an incidence angle of 30°. Information on the interfacial Cu ions and the bulk-like Cu ions is obtained from the comparison of the XAS spectra measured in total electron yield (TEY) and fluorescence yield (FY), respectively. Due to the small escape depth of the photo-excited electrons of only a few nanometers, the TEY signal arises predominantly from the Cu ions at the topmost YBCO/manganite interface. The FY signal, however, is equally sensitive to all Cu ions and thus representative of the majority of the Cu ions away from the interface.
Figure 4b, e compares the FY spectra of the trilayers with x = 0.35 and x = 0.5. These resemble the spectra of bulk-like YBCO showing a sharp resonance at 931 eV and a strong linear dichroism towards σ polarization (μab) that confirms that the holes in the CuO2 planes away from the interface have predominantly \(d_{x^2 - y^2}\) character. The corresponding TEY signal at x = 0.35 in Fig. 4c reveals some remarkable differences with respect to the FY signal. In particular, a clear redshift of the resonance by about 0.5 eV is observed, as well as a strong enhancement of the c-axis component μc with π−polarization that gives rise to a weak inversion of the X-ray linear dichroism (XLD). Both features were previously observed in YBCO/manganite multilayers with a similar hole doping of the manganite of x = 0.3–0.3528. They have been explained in terms of a transfer of electrons from the manganite to the YBCO and an orbital reconstruction of the interfacial Cu ions that leads to a redistribution of holes from the \(d_{x^2 - y^2}\) to the \(d_{z^2}\) orbitals29,30. Moreover, it has been shown that this charge transfer and orbital reconstruction are robust features that occur at this doping level irrespective of whether the manganite layer is an itinerant ferromagnetic29,30 or an AF charge/orbital ordered insulator22.
The more remarkable is our finding that for the TEY resonance of the trilayer with x = 0.5 in Fig. 4d both the red shift and the enhancement of the c-axis signal, and thus the interfacial charge transfer and orbital reconstruction are strongly reduced compared to the x = 0.35 sample in Fig. 4c. The reduced transfer of electrons from the manganite to the YBCO layer (or the smaller red shift of the TEY resonance) is naturally explained in terms of the larger hole doping of the manganite at x = 0.5, which lowers the Fermi-level of the manganite and thereby reduces its mismatch with respect to that of YBCO. The reason for the concomitant weakening of the orbital reconstruction of the interfacial Cu ions (i.e., a reduced density of \(d_{z^2}\) holes) is less obvious. It may involve additional effects such as a change of the position of the apical oxygen ion, which slightly reduces the hybridization of the \(d_{z^2}\) levels of the interfacial Mn and Cu ions. A full understanding requires further theoretical and experimental studies of the detailed structure of the interface, which hopefully will be motivated by our work.
Finally, Fig. 4f shows the evolution of the amplitude of the elastic Bragg peak in the RIXS data at x = 0.5 as a function of the incident photon energy (see Supplementary Note 5 and Supplementary Fig. 6 for more details and raw spectra). It exhibits a clear resonance with a maximum slightly below the resonance of the TEY-XAS signal (see Fig. 4d) and significantly below one of the resonance for the Bragg peak at Q|| ≈ 0.3 at x = 0.3522 and in plain YBCO31. This trend is consistent with our interpretation that this Cu-\(d_{z^2}\) order originates predominantly from the interfacial CuO2 planes. Certainly, it excludes the possibility that the Cu-\(d_{z^2}\) originates from the CuO chains, for which the resonance would occur around 933.8 eV32,33. Moreover, a Bragg-peak that arises from a superstructure of oxygen vacancies in the CuO chains would persist well above room temperature, in contrast to the trend shown in Fig. 3g.
Discussion
The present work emphasizes the range of ordered phases that develop in the high-Tc cuprates, and, in particular, suggests that these can be induced to involve the out-of-plane orbitals, in contrast to previous observations. This raises important questions about the coupling mechanism at the cuprate/manganite interface that induces (or enhances) these different orders. It is likely that Jahn-Teller distortions due to the CE-type charge/orbital order of the manganite are induced that can be transported into the cuprate via the interfacial Ba-O layer. In turn, these distortions may trigger an orbital order of the interfacial CuO2 layer through a variation of the orbital reconstruction along the interface with a certain alternation to the \(d_{z^2}\) and \(d_{x^2 - y^2}\) levels. A lateral ordering of the \(d_{z^2}\) and \(d_{x^2 - y^2}\) orbitals could also explain the magnetic component of the Cu-\(d_{z^2}\) order that is suggested by our calculations. It would give rise to a modulation of the in-plane AF exchange couplings since the exchange between a pair of \(d_{x^2 - y^2}\) spins is strongly reduced when one orbital is replaced by a \(d_{z^2}\) orbital, and even becomes weakly ferromagnetic for spins on two adjacent \(d_{z^2}\) orbitals30. Additionally, the Cu-\(d_{z^2}\) order in the multilayer with x = 0.5 occurs despite a reduced density of \(d_{z^2}\) holes on the interfacial CuO2 plane as compared to the multilayer with x = 0.35, for which the usual \(d_{x^2 - y^2}\) CDW order prevails. This suggests that an optimal density of \(d_{z^2}\) holes, or a particular ratio with respect to the \(d_{x^2 - y^2}\) holes, is required to stabilize the Cu-\(d_{z^2}\) order and might be directly linked to its particularly long wavelength (small wave vector).
Another interesting aspect concerns the relationship of this Cu-based density wave order with superconductivity. The magneto-transport data of the NYN trilayer with x = 0.5 that are detailed in the (SOM) and reported in Khmaladze et al.24 provide evidence for a strong granularity of the superconducting order. They also suggest that the grain boundaries, which break the superconducting coherence and lead to Coulomb-blocking effects in the YBCO layer, are related to the domain boundaries of the Mn-CO in the manganite layers. Indeed, the Coulomb-blockade is stronger in NYN trilayers with x = 0.35, for which the Mn-CO order is weaker and more short-ranged (high density of domain boundaries), than in corresponding NYN trilayers with x = 0.5 (fewer domain boundaries)24. Interestingly, the induced Cu-based density wave order follows a similar trend as the Mn-CO in that the correlation length of the Q ≈ −0.096 r.l.u. order at x = 0.5 with ξ ≈ 40 nm exceeds the one of the Cu-CDW with Q ~ 0.3 r.l.u. at x = 0.35 with ξ < 10 nm. This fits into the picture that the Mn-CO acts as a template for a Cu-based density wave order that is intertwined with the SC order with common domain boundaries at which the SC coherence is broken.
While many open questions remain, our findings open new routes for exploring the physics of intertwined ordered phases and demand both further theoretical and experimental work on the electronic and structural properties of the cuprate/manganite interface. They also raise hopes that other exotic Cu-based orders can be induced by modifying the doping of the cuprate and manganite layers. In particular, the manganite provides a range of charge, orbital, and magnetic orders for which the interaction with the cuprate remains unexplored. Finally, with electric field gating it may even be possible to switch between different Cu-based orders at the YBCO/manganite interface to study their relationship with superconductivity or to develop new device and sensing applications.
Methods
Sample growth and characterization
Trilayers of Nd1-x(Ca1-ySry)xMnO3(20 nm)/ YBa2Cu3O7(7 nm)/ Nd1-x(Ca1-ySry)xMnO3(10 nm) with x = 0.5, y = 0.25 and x = 0.35, y = 0.2 and a 1 nm thick LaAlO3 capping layer were grown with pulsed laser deposition (PLD) on (001)-oriented La0.3Sr0.7Al0.65Ta0.35O3 (LSAT) substrates. Details of the growth conditions and the sample characterization are given in Supplementary Note 1. The electronic transport and magnetization measurements showing the superconducting and magnetic properties of the trilayers are reported in ref. 24. In particular, for the NYN trilayer with x = 0.5 and y = 0.25 the R–T curve in zero magnetic field exhibits the onset of superconducting transition below Tc ≈ 82 K followed by a steep increase of the resistance below about 60 K that is characteristic of a granular SC state. In 9 Tesla, a regular superconducting transition occurs with the same onset temperature that is completed below about 55 K. Note that the SC transition, which for fully oxygenated and thus slightly overdoped bulk YBCO is around 90 K, is typically reduced for very thin YBCO layers. In bare thin films this is due to finite size and strain effects as well as related defects. In addition, for the present multilayers, there is a reduction in the hole doping of the interfacial CuO2 layers that arises due to the transfer of electrons from the neighboring manganite layers and the missing CuO chain layer at both the top and bottom interfaces30,34,35,36.
Resonant inelastic X-ray scattering
The RIXS experiments at the Cu L3-edge were performed at the ADRESS beamline of the Swiss Light Source (SLS) at the Paul Scherrer Institute (PSI) in Switzerland37,38. The scattering angle between the incoming and outgoing X-ray beams was 130°. The angle δ, which gives the projection of transferred momentum along the surface direction, is defined as zero when the angles α and β are equal (specular reflection), i.e., δ = Ψ /2 – α. An energy resolution of 130 meV (full-width at half-maximum) was determined from the elastic scattering off a carbon-filled acrylic tape. The incident photon energy scale was shifted in order to match the X-ray absorption spectrum measured in TEY at ADRESS beamline to the corresponding spectrum obtained at the XTreme beamline (see below). The energy scale of the incident energies used for the RIXS data has been corrected accordingly.
All the RIXS data presented in the main text are corrected for self-absorption assuming same light polarization for the incoming and outgoing beams. The correction procedure and the case of cross-polarization is discussed in Supplementary Note 3 of the SOM. The RIXS spectra used in Figs. 1 and 2 have been then normalized to the integrated intensity of the dd excitations.
RIXS cross-section calculations
Cross-section calculations for the RIXS process were performed using a single-ion model following Moretti Sala et al.28. This calculation takes into account the atomic symmetries of the core-level p and valence d-orbitals and the geometry of the experimental setup, namely the π and σ polarization of incident light and the scattering angles of the experiment. Since measurements were performed at the Cu L-edge, the atomic cross-sections of the elastic RIXS signal were calculated assuming X-ray absorption and emission to and from valence d-levels. We show here calculations for valence states with symmetry \(d_{x^2 - y^2}\) or \(d_{z^2}\). Calculations for other d-orbitals have been performed, but are found not to correspond to the obtained data. (Supplementary Note 4). Processes without a spin-flip (elastic) and with spin-flip have both been calculated, assuming spin along the [110] direction for \(d_{x^2 - y^2}\) states and along both [001] and [110] for \(d_{z^2}\) states. In order to compare the calculated cross-section with the observed RIXS intensities (arbitrary units), a constant conversion factor is applied, which is given in each of the figure captions.
Resonant elastic X-ray scattering (REXS)
REXS experiments at the Cu L3-edge (931 eV) were performed at the UE46 PGM-1 beamline of the BESSY II synchrotron at Helmholtz-Zentrum Berlin fur Materialen und Energie (HZB) in Germany. The X-ray photodiode from the diffractometer can move in a continuous way to a large range of angles and the energy-integrating nature of the photodiode will show the elastic peak superimposed on a background that includes all the inelastic components. The scattering geometry of the REXS was adapted to probe the Bragg peak in similar configuration as RIXS experiments. The errors were calculated using ref. 39.
X-ray absorption spectroscopy
X-ray absorption spectroscopy (XAS) and X-ray linear dichroism (XLD) at the at the Cu L3-edge were measured in total electron yield (TEY) and fluorescence yield (FY) mode at the XTreme beamline of the SLS at the PSI in Switzerland.40 The angle of incidence of the X-ray beam was set to 30° such that the response in σ polarization, μσ, corresponds to the ab plane response of YBCO, μab = μσ, whereas the c-axis response, μc, is obtained from the signal in π-polarization, μπ = μc* according to the geometrical factor, μc = 1/(μπ cos2(θ) − μσ tan2(θ)). In Fig. 3b–e the data have been normalized to the maximum of the polarization-averaged absorption \(\mu _{{\mathrm{avg}}} = \max [(2\mu _{ab})/3]\) at the Cu L3-edge.
Data availability
The data will be made available upon reasonable request to the corresponding authors.
Change history
25 February 2021
A Correction to this paper has been published: https://doi.org/10.1038/s41535-021-00323-8
References
Keimer, B. et al. From quantum matter to high-temperature superconductivity in copper oxides. Nature 518, 179–186 (2015).
Alloul, H., Ohno, T. & Mendels, P. 89Y NMR evidence for a fermi-liquid behavior in YBa2Cu3O6+x. Phys. Rev. Lett. 63, 1700–1703 (1989).
Homes, C. C. et al. Optical conductivity of c axis oriented YBa2Cu3O6.70: evidence for a pseudogap. Phys. Rev. Lett. 71, 1645–1648 (1993).
Lorama, J. W., Mirza, K. A., Cooper, J. R. & Tallon, J. L. Specific heat evidence on the normal state pseudogap. J. Phys. Chem. Solids 59, 2091–2094 (1998).
Niedermayer, C. et al. Common phase diagram for antiferromagnetism in La2−xSrxCuO4 and Y1−xCaxBa2Cu3O6 as seen by muon spin rotation. Phys. Rev. Lett. 80, 3843–3846 (1998).
Julien, M. H. Magnetic order and superconductivity in La2-x-Sr xCuO4: a review. Phys. B 329–333, 693–696 (2003).
Tranquada, J. M. et al. Evidence for stripe correlations of spins and holes in copper oxide superconductors. Nature 375, 561–563 (1995).
Tranquada, J. M. et al. Coexistence of, and competition between, superconductivity and charge-stripe order in La1.6−xNd0.4SrxCuO4. Phys. Rev. Lett. 78, 338–341 (1997).
Wu, T. et al. Magnetic-field-induced charge-stripe order in the high-temperature superconductor YBa2Cu3Oy. Nature 477, 191–194 (2011).
Ghiringhelli, G. et al. Long-range incommensurate charge fluctuations in (Y,Nd)Ba 2Cu3O6+x. Science 337, 821–825 (2012).
Chang, J. et al. Direct observation of competition between superconductivity and charge density wave order in YBa2Cu3O6.67. Nat. Phys. 8, 871–879 (2012).
Fradkin, E., Kivelson, S. A. & Tranquada, J. M. Colloquium: theory of intertwined orders in high temperature superconductors. Rev. Mod. Phys. 87, 457–482 (2015).
Edkins, S. D. et al. Magnetic field-induced pair density wave state in the cuprate vortex halo. Science 364, 976–980 (2019).
Castellani, C., Castro, C. D. & Grilli, M. Singular quasiparticle scattering in the proximity of charge instabilities. Phys. Rev. Lett. 75, 4650–4653 (1995).
Caprara, S., Castro, C. D., Seibold, G. & Grilli, M. Dynamical charge density waves rule the phase diagram of cuprates. Phys. Rev. B 95, 224511 (2017).
Peng, Y. Y. et al. Re-entrant charge order in overdoped (Bi,Pb)2.12Sr1.88CuO6+δ outside the pseudogap regime. Nat. Mater. 17, 697–702 (2018).
Comin, R. et al. Charge order driven by Fermi-arc instability in Bi2Sr2−xLa xCuO6+δ. Science 343, 390–392 (2014).
Gerber, S. et al. Three-dimensional charge density wave order in YBa2Cu3O6.67 at high magnetic fields. Science 350, 949–952 (2015).
Chang, J. et al. Magnetic field controlled charge density wave coupling in underdoped YBa2Cu3O6+x. Nat. Commun. 7, 11494 (2016).
Kim, H. H. et al. Uniaxial pressure control of competing orders in a high-temperature superconductor. Science 362, 1040–1044 (2018).
Frano, A. et al. Long-range charge-density-wave proximity effect at cuprate/manganate interfaces. Nat. Mater. 15, 831–834 (2016).
Perret, E. et al. Coupled Cu and Mn charge and orbital orders in YBa2Cu3O7/Nd0.65(Ca1-ySry)0.35MnO3 multilayers. Commun. Phys. 1, 45 (2018).
Mallett, B. P. P. et al. Granular superconductivity and magnetic-field-driven recovery of macroscopic coherence in a cuprate/manganite multilayer. Phys. Rev. B 94, 180503(R) (2016).
Khmaladze, J. et al. Granular superconductivity and charge/orbital order in YBa2Cu3 O7/manganite trilayers. Phys. Rev. Mater. 3, 084801 (2019).
Tokura, Y. Critical features of colossal magnetoresistive manganites. Rep. Prog. Phys. 69, 797–851 (2006).
Fink, J., Schierle, E., Weschke, E. & Geck, J. Resonant elastic soft x-ray scattering. Rep. Prog. Phys. 76, 056502 (2013).
Weschke, E. & Schierle, E. The UE46 PGM-1 beamline at BESSY II. J. Large-scale Res. Facilities 4, A127 (2018).
Moretti Sala, M. et al. Energy and symmetry of dd excitations in undoped layered cuprates measured by Cu L3 resonant inelastic x-ray scattering. New J. Phys. 13, 043026 (2011).
Chakhalian, J. et al. Orbital reconstruction and covalent bonding at an oxide interface. Science 318, 1114–1117 (2007).
Sen, K. et al. X-ray absorption study of the ferromagnetic Cu moment at the YBa2Cu3 O7/La2/3Ca1/3MnO3 interface and variation of its exchange interaction with the Mn moment. Phys. Rev. B 93, 205131 (2016).
Bluschke, M. et al. Stabilization of three-dimensional charge order in YBa2Cu3O6+x via epitaxial growth. Nat. Commun. 9, 2978 (2018).
Achkar, A. J. et al. Distinct charge orders in the planes and chains of ortho-III-ordered YBa2Cu3O6+δ superconductors identified by resonant elastic x-ray scattering. Phys. Rev. Lett. 109, 167001 (2012).
Magnuson, M. et al. Self-doping processes between planes and chains in the metal-to-superconductor transition of YBa2Cu3O6.9. Sci. Rep. 4, 7017 (2014).
Malik, V. K. et al. Pulsed laser deposition growth of heteroepitaxial YBa2Cu3O7/ La0.67Ca0.33MnO3 superlattices on NdGaO3 and Sr0.7La0.3Al0.65Ta0.35O3 substrates. Phys. Rev. B 85, 054514 (2012).
Varela, M. et al. Nanoscale analysis of YBa2Cu3O7−x/La0.67Ca0.33MnO3 interfaces. Solid-State Electron. 47, 2245–2248 (2003).
Salafranca, J. et al. Competition between covalent bonding and charge transfer at complex-oxide interfaces. Phys. Rev. Lett. 112, 196802 (2014).
Ghiringhelli, G. et al. SAXES, a high resolution spectrometer for resonant X-ray emission in the 400–1600 eV energy range. Rev. Sci. Instrum. 77, 113108 (2006).
Strocov, V. N. et al. High-resolution soft X-ray beamline ADRESS at the Swiss light source for resonant inelastic X-ray scattering and angle-resolved photoelectron spectroscopies. J. Synchrotron Radiat. 17, 631–643 (2010).
Bevington, P. R. Data Reduction and Error Analysis for the Physical Sciences, Ch. 4 and 5 (McGraw-Hill, New York, 1969).
Piamonteze, C. et al. X-Treme beamline at SLS: X-ray magnetic circular and linear dichroism at high field and low temperature. J. Synchrotron Radiat. 19, 661–674 (2012).
Acknowledgements
We acknowledge fruitful discussion with Dr. Steven Johnston and experimental support provided by Dr. Enrico Schierle during the REXS beamtime. Work at the University of Fribourg was supported by the Swiss National Science Foundation (SNSF) through Grants No. 200020-172611 and CRSII2-154410/1. C.M. acknowledges the support by the SNSF grants No. PZ00P2_154867 and PP00P2_170597. The RIXS and XAS experiments were performed, respectively, at the ADRESS beamline and the Xtreme beamline of the Swiss Light Source at the Paul Scherrer Institute. The work at the ADRESS beamline is supported by the Swiss National Science Foundation through project no. 200021_178867, the NCCR MARVEL and the Sinergia network Mott Physics Beyond the Heisenberg Model (MPBH). The REXS experiments (Supplementary information) were performed at UE46_PGM-1 beamline at the BESSY II synchrotron in the Helmholtz-Zentrum, Berlin (HZB). This project received funding from the European Union’s Horizon 2020 research and innovation program under grant agreement No. 730872. We thank J.-L. Andrey and O. Raetzo from the Physics Department workshop at UniFr for technical assistance. T.C.A. acknowledges funding from the European Union’s Horizon 2020 research and innovation programme under the Marie Skłodowska-Curie grant agreement No. 701647 (PSI-FELLOW-II-3i program).
Author information
Authors and Affiliations
Contributions
RIXS measurements were carried out by R.G., C.W.N., M.R., S.S., E.P., Y.T., W.Z., T.C.A., T.S., C.M., and C.B. and analyzed by R.G. and C.W.N. Samples were grown and characterized by J.K. and S.S. Experimental support during the RIXS experiment, including alignment of the spectrometer and maintenance of the beamline were performed by E.P., Y.T., W.Z., D.M, T.C.A., and T.S.; XAS measurements were obtained by R.G. and C.P. and analyzed by R.G. The RIXS calculations were performed by C.W.N. and C.M. The REXS measurements were carried out by R.G., S.S., C.B., and E.W. and analyzed by R.G. and S.S. The manuscript was written by C.W.N., C.M., R.G., and C.B. with contributions from all authors. C.M. and C.B. were responsible for the overall project planning and direction. R.G. and C.W.N. have contributed equally.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gaina, R., Nicholson, C.W., Rumo, M. et al. Long-ranged Cu-based order with \(d_{z^2}\) orbital character at a YBa2Cu3O7/ manganite interface. npj Quantum Mater. 6, 12 (2021). https://doi.org/10.1038/s41535-021-00311-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41535-021-00311-y
- Springer Nature Limited
This article is cited by
-
Orbital elasticity control of phase diagram for La0.67Sr0.33MnO3 films
Science China Materials (2024)
-
Orbital-selective charge-density wave in TaTe4
npj Quantum Materials (2023)