Abstract
The aim of this study was to investigate the fracture behaviour of fissural dental enamel under simulated occlusal load in relation to various interacting factors including fissure morphology, cuspal angle and the underlying material properties of enamel. Extended finite element method (XFEM) was adopted here to analyse the fracture load and crack length in tooth models with different cusp angles (ranging from 50° to 70° in 2.5° intervals), fissural morphologies (namely U shape, V shape, IK shape, I shape and Inverted-Y shape) and enamel material properties (constant versus graded). The analysis results showed that fissures with larger curved morphology, such as U shape and IK shape, exhibit higher resistance to fracture under simulated occlusal load irrespective of cusp angle and enamel properties. Increased cusp angle (i.e. lower cusp steepness), also significantly enhanced the fracture resistance of fissural enamel, particularly for the IK and Inverted-Y shape fissures. Overall, the outcomes of this study explain how the interplay of compositional and structural features of enamel in the fissural area contribute to the resistance of the human tooth against masticatory forces. These findings may provide significant indicators for clinicians and technicians in designing/fabricating extra-coronal dental restorations and correcting the cuspal inclinations and contacts during clinical occlusal adjustment.
Similar content being viewed by others
Introduction
Dental enamel, as the most highly mineralised tissue in the human body, mainly consists of hydroxyapatite nanocrystals and traces of water and organic molecules. The crystalline structure as well as the high hardness and stiffness of enamel impart it with the capacity to tolerate a range of lifelong mechanical, thermal and chemical stimuli while still maintaining its cutting and masticatory functions. However, due to its highly mineralised composition, enamel is a relatively brittle biomaterial with an elastic modulus in the level of 100 GPa and a toughness value comparable to that of glass1. The brittle nature and high susceptibility to mechanical failure presents a more critical problem in deep fissures located in the occlusal surface of molar and premolar teeth. In these fissural regions, the thickness of enamel is significantly lower than enamel cusp tips and proximal surfaces. Moreover, the sharp angles and narrow curvatures within the fissure system potentially generate vulnerable sites of stress concentration and crack initiation in enamel.
The cusps of posterior teeth bear substantial bending and flexural loads during functional and specifically eccentric parafunctional occlusal movements. These applied loads can theoretically generate a horizontal force component which tends to open up the fissural space and create tensile stress concentration and subsequent cracks at the base of the fissure. Although it is common to see that cracking of the cusps initiates from the fissural area in carious teeth, the prevalence of fracture in the fissural area of sound natural teeth is surprisingly low2. The resistance of fissural enamel with presumably weak structural design and brittle nature, against millions of chewing cycle loads with up to 1200 N in magnitude is a thought-provoking phenomenon.
While occlusal enamel fissures seem to be susceptible sites for bacterial plaque retention, caries formation and crack initiation, their introduction into the dentition of heterodonts was a significant step in evolution which led to the transformation of canine-like teeth morphology of zyphodonts to the multicuspid dentition of heterodonts, with a broad diversity of tooth types and shapes3. This transformation enhanced the efficacy of the masticatory system of omnivores and optimised the utilisation of food caloric energy for an increased level of intricate physical and intellectual activities4. Natural remineralisation process through salivary minerals and organic biomolecules is a reparative mechanism for maintaining the integrity of enamel and restoring mildly demineralised crystals5.
The genesis of occlusal fissures happens during the bell stage of the tooth formation process, through folding invagination of the inner enamel epithelium and the subsequent fusion and mineralisation of adjacent developmental dental lobes6. While these fissures can display a range of depths and widths, from shallow grooves and fossae to deep and narrow pits and fissures, their morphology follows five main patterns7, namely I-shape, U-shape, inverted Y-shape (IY), IK-shape and V-shape.
Previous studies have revealed that enamel thickness and cusp size are the critical morphological factors involved in the fracture behaviour of enamel8. Other studies have focused on the microstructural features of enamel including its hierarchical organisation, the presence of micron-sized defects and the role of organic remnants, in the mechanical resistance and fracture behaviour of enamel8,9. However, little has been known to date about the effect of fissure geometry as well as the composition and material properties of enamel especially around the fissural area, on the resistance of the tooth against fracture. Understanding the structural and compositional features responsible for the superior mechanical performance of natural teeth, can provide substantial guidelines for optimizing design and fabrication of long lasting restorative ceramic crowns. Therefore, the current study aims to investigate the fracture behaviour of fissural dental enamel under simulated occlusal load in relation to various factors, including fissure morphology, cuspal angle and the underlying material properties of enamel.
Results
The influence of anatomical features and compositional factors, such as fissure types, cusp angulation and material properties on the stress distribution, fracture load and crack length in the occlusal fissure of the tooth, are presented in the following sections.
Fissure geometry
The contours of the maximum principal stress associated with crack initiation and propagation for the tooth models with the five types of fissure morphology at a cusp angle of 50° are shown in Fig. 1. The crack patterns at different stages of crack development, including crack initiation, crack growth to dentine-enamel junction (DEJ), and crack extension upon completion of indenter displacement loading were recorded for these five fissure geometries. For all the fissure shapes, the crack generally started from the floor of the fissure where high tensile stresses occurred. Mostly, it was observed that the cracks initiated on one side of the fissure, and then propagated in the same direction. The cracks stopped growing once they reached the DEJ, which is marked as the red line in each sub-figure of Fig. 1. With continuation of the loading, the crack passed through the DEJ and continued to grow in dentine. Consequently, the crack stopped in the dentine region when the displacement of the loading ball (0.2 mm) and the resultant loading was completed.
In the XFEM analysis, the reaction force on the spherical loading head was recorded as the fracture load10. As such, the loads corresponding to onset of the fissure crack are graphed in Fig. 2. On the basis of the fracture loads at crack initiation, the U shape fissures showed the highest value, followed by the IK shape. The remaining three geometries (V shape, I shape and Inverted Y shape) presented lower but similar loads. Regarding the crack length, as shown by the grey bars in Fig. 2, the longest extension was 1.25 mm which corresponds to the IY shape, followed by the V shape (1.12 mm), I shape (1.04 mm), IK shape (0.94 mm) and U shape (0.84 mm).
Cusp angle
The fracture loads at the onset of crack initiation were recorded from the XFEM analysis for different cusp angles (ranging from 50° to 70° at intervals of 2.5°) of each fissure geometry, as graphed in Fig. 3(a). It was observed that the fracture load rises with the increase in cusp angle (i.e. lower cusp steepness) for all fissure shapes. For the entire range of cusp angles, the U shape morphology resulted in the highest fracture load at crack initiation, followed by the IK shape. For the remaining three fissure types (V shape, I shape and IY shape), the fracture loads at crack initiation were similar when cusp angle was at the low value of 50° (Fig. 3(a)). Upon increasing the cusp angle up to 70°, the load values at crack initiation were somewhat scattered for these three geometries with a decreasing rank of I to IY and V shape fissures.
By comparing the fracture initiation loads between the cusp angles of 50° and 70°, a relatively large difference was observed for the IK shape, I shape and IY shape (Fig. 3(a)). For all the fissure geometries, the crack initiation load was relatively stable for the cusp angles between 50° and 57.5°; and then increased for the cusp angles from 57.5° to 70°. Regarding the IK shape, the loads at crack initiation were fluctuating and increasing. For the I shape and IY shape, the loads fluctuated when the cusp angle was between 50° and 60°, and increased when the cusp angle was between 60° and 70°.
Crack lengths and maximum load upon completion of the loading displacement were also recorded from the XFEM analysis for the different fissure geometries and various cusp angles (Fig. 3(b)). Comparative results of the crack length among all five fissure shapes are shown in Fig. 2 for the cusp angle of 50°. Figure 3(b) graphs the crack length values upon completion of loading for different cusp angles (from 50° to 70°). Accordingly, the crack lengths decreased with the increase in cusp angle for all the fissure geometries. The V shape had the least change in the crack length for different cusp angles between 50° and 70°. The slope of decreasing trend of the U shape was greater than that of the V shape, which was fairly stable within the entire cusp angle range. The IY shape, I shape, and IK shape had a similar trend, i.e. crack lengths declined sharply when cusp angle changed from 50° to 57.5°, followed by a smaller rate of crack length reduction in the cusp angle range of 60° to 70°. The reduction of the crack length was more significant in the IK and IY shape fissures, where the crack length almost halved when increasing the cusp angle from 50° to 70°. At the low cusp angle of 50°, the crack length of V shape fissures was significantly larger than those of the other fissure types which exhibited a decreasing rank of I shape, IY shape, U shape and IK shape.
Material properties of enamel
The fracture behaviour of enamel in relation to the gradient of mineral density and corresponding material properties of enamel in different parts of the tooth such as the fissure area were investigated for different fissure geometries. Accordingly, the fracture loads at different stages of crack formation were recorded for the models with constant material properties throughout the enamel in comparison with the models having an allocated CT-based gradient of material properties in enamel.
Figure 4 shows the comparative results of the fracture loads at crack initiation, crack growth to DEJ and upon completion of loading displacement for these models with the constant and graded material properties at a cusp angle of 50°. In general, the models with a gradient of mineral density and graded material properties showed a trend of increased fracture loads in all three stages of crack formation in comparison with the similar models with constant mineral density. The effect of graded versus constant mineral density was more significant in the second stage of crack development (crack propagation to DEJ) compared with the crack initiation and maximum crack extension at the displacement completion stages. In the crack initiation and loading completion stages, none of the fissure geometries were overly sensitive to the changes in the mineral density, where both the constant and gradient density models had relatively similar fracture loads. However, in the stage of crack growth to DEJ, the application of gradient density on the models significantly increased the load values for the U shape, V shape and I shape, to almost twice that of the models with constant density (Fig. 4). The graded mineral density also resulted in an increase of the loads for crack growth to the DEJ in the IK shape and IY shape models, however the effect was relatively small compared to the other three geometries.
Further to investigate the combined effect of fissure geometry, cuspal angle and material properties of enamel on the fracture behaviour of occlusal fissures, the crack length at the completion of the loading displacement was recorded. Figure 5 shows the comparative results of the crack length for the different fissure types at cusp angles of 50°, 60° and 70° for the models with constant and graded mineral density, respectively. It was noted that in general, the crack length in the models with graded mineral density was shorter than that in the constant density models regardless of cusp angle and fissure geometry.
At a low cusp angle of 50°, application of a CT-based gradient of mineral density had significant effect on the fracture resistance and led to a sizeable decrease in the crack length for all the fissure geometries. For both the gradient and constant mineral density patterns at 50° angle, the U shape geometry had the smallest crack length, followed by the IK shape, I shape and V shape. The IY shape demonstrated the most substantial crack length of all the fissure geometries, indicating lowest fracture resistance.
While the IY shape was the most affected geometry by the gradient mineral density at the low cusp angle of 50°, mineral density gradient did not have a significant influence on the crack length for the I shape and IK shape fissures at a cusp angle of 70°. In these fissure types, the effect of graded mineral density became smaller with increasing cusp angle from 50° to 70°. The influence of gradient density on the crack extension was evident in all cusp angles for the U shape and V shape fissures.
At the high cusp angle of 70°, gradient mineral density led to smaller crack lengths for the U shape, V shape and IY shape. As for the IK shape and I shape, change in mineral density had limited effect on the crack length.
Discussion
Cracking and fracture of the tooth imposes a significant concern in the dental clinic, with a questionable prognosis for tooth fracture in the majority of patients11. This issue is more frequently diagnosed in teeth with deteriorated structural integrity due to caries or large intra-coronal restorations12. However, the rate of fracture is very low in sound teeth despite the presence of deep fissures on the occlusal surface as well as thin brittle enamel in these areas of the tooth. This study investigated the interaction of various anatomical features and compositional factors which contribute to the resistance of the fissural enamel against fracture.
As shown in Fig. 1, in all the study groups, the cracks initiated at the fissure area where the maximum tensile stress was concentrated; and then propagated toward the right lower direction in the enamel, presumably due to the non-symmetrical structure of the modelled tooth. The non-symmetrical anatomy of the models were created to reflect the structural asymmetry of the natural premolar tooth in which the functional cusp is generally smaller and has a rounder shape in comparison with the sharper and larger non-functional cusp. The directional propagation of the crack toward the smaller cusp can be attributed to smaller bulk of the enamel and dentine together with the lower thickness of enamel, which leads to higher stress concentration.
Regarding the effect of occlusal fissure geometry on fracture resistance of the tooth, the results of the XFEM analysis showed that the fissures with larger curved morphology such as U and IK shape, exhibited higher resistance to fracture under simulated occlusal load irrespective of cusp angle and enamel material properties. At the crack initiation stage, these two fissure types required higher fracture loads to generate the crack. This may be explained by their curved morphology that distributed the stress over a wider area and prevented stress concentration around localised points in the fissure. On the other hand, the I, IY and V shape fissures displayed similarly lower fracture loads and longer crack lengths at the maximum load displacement due to their sharp and pointed shape at the tip of the fissure which prevented wider distribution of the stress and generated greater stress concentration.
The cusp angle is an important anatomical feature of the crown morphology which can be modified and adjusted in natural tooth and restorative crowns. Previous studies have evaluated the relation of cusp angle with the fracture resistance of ceramic crowns and the values between 50° and 70° have been suggested13 to be an optimum range of cusp angle. However, to the knowledge of the authors, the effect of cusp angles in combination with the fissure morphology and gradient properties of natural teeth have not been investigated so far.
As shown in Fig. 3(a), increasing the cusp angle results in an increase of the fracture resistance of the tooth. This finding is consistent with the mechanical test conducted on all ceramic porcelain veneered crowns with zirconia core by Sornsuwan et al.14. The applied occlusal force can be resolved into two components in the lateral and longitudinal (axial) directions. While higher cusp angulation is more related to the compressive stress and longitudinal (vertical) forces, steeper cusp inclination generates larger lateral (horizontal) forces in the fissure area which is the dominant factor in crack initiation and propagation. In the current study, the crack initiation load was almost unchanged for the cusp angles between 50° and 58°, but became sensitive to the cusp angle above 58° (Fig. 3(a)). The authors assume that at the cusp angle values below 58°, the tensile stress caused by the lateral (horizontal) force component is large enough to initiate and propagate the crack for all the fissure geometries. However, the crack length at the maximum displacement was still proportionate to the cusp angle value even in this low range of cusp angle values (Fig. 3(b)).
Material properties play an important role in crack growth of structures. While some studies have considered enamel as a homogenous material15, others have suggested enamel to be a functionally graded material (FGM) with a gradient of material properties16,17. In the present study, non-destructive microCT imaging was used to obtain mineral density maps in various sections of the tooth and subsequently generated Young’s modulus and fracture toughness maps of the specimen. Young’s modulus is a critical material property which influences the stress and strain energy, thereby determining crack initiation and propagation.
The XFEM procedure consisted of two stages; the first was crack initiation which simulated the crack nucleation and small crack growth; and the second stage modelled the propagation of the crack. Regarding crack initiation, materials with a lower modulus would allow more elastic deformation, i.e. more compliant (typically less brittle)18. Lower Young’s modulus leads to a lower tensile stress in the material; and therefore it would be more difficult for the crack to initiate. For the crack propagation, the determinant factor is the strain energy release rate (G)19, which is inversely proportional to Young’s modulus and directly proportional to the fracture toughness squared (Eq. 2). According to the mineral density maps of the tooth, enamel in the fissural region has a relatively lower Young’s modulus and higher fracture toughness than the outer enamel area. As a result, the crack would be more difficult to initiate and it would propagate more slowly under loading displacement in the fissural area.
As shown in Fig. 4, graded material properties had a more significant impact on the fracture load during the crack growth stage compared to the crack initiation and maximum crack extension stages. This observation is consistent with the known graded properties of enamel. The lower E modulus and higher K1c and strain energy release rate results in a crack requiring more load to grow across the enamel layer before reaching the DEJ. Regarding the load at crack completion, nevertheless, there was no significant difference in the fracture loads. This is due to the fact that the crack had already passed the DEJ and entered the dentine for both the constant property and graded enamel property groups and therefore the crack opening displacement is controlled by the strain energy release rate of the dentine. The reduction of fracture load due to the graded material properties was more manifest for a lower cusp angle, particularly in the fissures with V and I shape, where the increase of the cusp angle is not able to impart significant resistance against fracture.
As shown in Fig. 5, if the cusp angle is in the lower range of the suggested values, graded material properties could be one of the ways to increase the resistance of the tooth to crack growth. However, with the increase in cusp angle, the effect of material properties on crack length became smaller due to the lower tensile stress.
According to these findings, application of materials with higher fracture toughness around the occlusal grooves can be an effective strategy to lower the risk of fracture for the intra-coronal restoration or crowns under heavy masticatory loads when the cusp angle cannot be increased. While in theory, restorative crown designs with curved occlusal fissure morphology such as the U and IK shapes provide higher fracture resistance and better stress distribution, however in practice it is very difficult, if not impossible for the dentists and technicians, to develop such fine features on the occlusal surface of the ceramic crowns. Though, avoiding the creation of sharp fissures and narrow morphological features on the occlusal surface of the restoration is of utmost importance to the enhancement of durability and resistance of the tooth and restoration.
Based upon the findings of this study, the authors suggest three mechanisms have been incorporated into the natural design of the tooth, imparting it with the maximum resistance against masticatory loads while still maintaining the benefits of a multicuspid dentition with narrow and deep occlusal fissures.
The first mechanism is the rounding and radial extension of the fissure tip which allows more even distribution of the stresses over a larger area. The second mechanism involves the increase of the cusp angle (reduction of the cusp steepness) which has developed/evolved more noticeably in highly load bearing molar teeth compared to premolars. Interestingly, the gradual wear and attrition of the occlusal surfaces in subjects with high masticatory load level, which leads to the increase of the cusp angles, can be considered as a protective mechanism that can reduce the risk of cracking and tooth fracture in these subjects.
Finally, the gradient of mineral density and material properties within enamel, i.e. higher toughness of inner and fissural enamel, provides a way to offset the destructive consequences of stress concentration caused by the sharp morphology around fissure tips. The collective effect of these anatomical and compositional features along with the intricate microstructural properties such as hierarchy, remnant proteins, orientation and bundling of hydroxyapatite crystals makes enamel an extraordinary material with many unique properties.
Materials and Methods
Mineral density characterization and quantification
Extracted human premolar teeth were collected from oral surgery and orthodontic departments at Sydney Dental Hospital, The University of Sydney. The specimen collection and experimental methods were performed in accordance with the approval guidelines from Sydney local health district ethics review committee, protocol No X12–0065 & HREC/12/RPAH/106. Regarding specimen collection, each patient was provided an information sheet and informed consent was obtained from all subjects.
Mineral density distributions of teeth were characterised using a high-resolution desktop microscopic computed tomography system (Skyscan 1172, Skyscan N.V, Aartselaar, Belgium) at an accelerating source voltage of 100 keV, a source current of 100 μA, and an exposure time of 885 ms. Three hydroxyapatite discs with low, medium and high mineral densities were used for grey level calibration to determine the mineral density values of different parts of the tooth. Details of the employed phantoms are provided elsewhere20.
Low energy X-rays were eliminated using an inbuilt filter equal to 1.0 mm thickness of aluminium and 0.05 mm of copper to restrict the spectral bandwidth of the polychromatic radiation. The equivalent monochromatic energy spectrum of filtered X-rays had an effective mean energy of 60 keV. The long axes of the teeth were placed parallel with the centre of rotation of the mounting device. During the scanning process, the samples were rotated over 360° at angular increments of 0.14°, generating 2570 two-dimensional shadow projections with an image matrix of 2000 pixels × 1048 pixels. These images were saved as 16-bit Tagged Image File Format (TIFF) and consequently exported to a 3D cone beam reconstruction program (NRecon software, version 1.4.4; SkyScan) for the tomographic reconstruction of the tooth and production of tomographic images. The tomographic reconstruction produced a dataset of slice views in 16-bit TIFF format, which were perpendicular to the specimen rotation axis and had a voxel size resolution of 8–10 µm. Vertical bucco-lingual slice views were produced by re-slicing the reconstructed volume of the whole image stack in FIJI (W.S. Rasband, U.S. National Institutes of Health, Bethesda, Md, USA, http://imagej.nih.gov/ij/, 1997–2011).
The produced tomographic images were consequently imported into MATLAB (MatLab R2012b 8.0.0.783, Mathworks, Natick, MA, USA) for the de-noising process which increases the signal to noise ratio of the micro-CT images. De-noising was performed using a method based upon total variation regularisation21,22, with the following parameters: (regularisation parameter) = 0/04. (initial penalty parameter) = 3.
The calibration of mineral density was implemented by measuring and averaging grey level values of selected images of each hydroxyapatite phantom, followed by plotting the obtained grey level values against the mineral density value of that phantom. Based upon the plotted values, a calibration equation was used to transform the grey level values of the images into true mineral density values20.
Mineral mapping and colour-coding of the tooth was performed using the Colormap editor command in MATLAB by choosing Jet colour map with fixed RGB (Red, Green, Blue) index values for all of the colourized images. The colour codes were based upon the greyscale values and corresponding mineral densities of the specimen, thereby yielding a calibrated mineral map.
Finite element models
A bucco-lingual cross-sectional image was selected from the micro-CT dataset of an upper premolar tooth to construct the two-dimensional (2D) finite element (FE) models23. The anatomies of bone, enamel and dentine, were specified in the image processing software ScanIP (Simpleware Pty. Ltd, UK). Once surface refinement of masks for each component of the model was completed, the FE model was exported as an IGES file for further modification in SolidWorks (SolidWorks Corp., USA). The periodontal ligament (PDL) was then created by offsetting the outline of the root section of the tooth13,24. Five different geometries for the occlusal fissure including U shape, V shape, IK shape, I shape and Inverted Y (IY) shape were modelled as shown in Fig. 2(c). For each fissure geometry, nine FE models with varying cusp angles from 50° to 70° at intervals of 2.5° were constructed in SolidWorks. Nominated models of a tooth with the U shaped occlusal fissure and cusp angles of 50° and 70° are shown in Fig. 6(a and b), respectively.
The FE models were meshed by using four-node bilinear quadrilateral elements. The mesh convergence test was conducted to determine the appropriate mesh size for tooth models by balancing the accuracy of results and computational cost24,25. According to the results of the convergence test, the global mesh size was 0.09 mm for the tooth model and 0.2 mm for the loading sphere. Due to the complex geometry of fissure areas, the meshing refinement was further performed using a local mesh size of 0.03 mm. Consequently, the number of elements was 42,282 (Degree of freedom - DOF: 84,736) for the tooth model, and 440 (DOF: 934) for the loading sphere.
The models were loaded using a 5 mm diameter steel ball controlled by a downward displacement of 0.2 mm. As this finite element analysis was carried out to simulate the indentation process, the sphere model played the role of indenter ball. Therefore, the sphere model was set to be the a rigid body and the contact between sphere (indenter ball) and tooth surface was assigned a friction coefficient of 0.3 in tangential direction11. All the FE models were kinematically constrained on the outer and bottom surfaces of the bone region26,27.
Material properties of the components of the FE model
The loading sphere was treated as steel, which was modelled to be linear elastic, isotropic and homogeneous28. Regarding the tooth model, all the materials were considered to be isotropic and homogeneous11. However, for the enamel, three regions of inner, middle and outer enamel were considered separately in order to reflect the non-isotropic nature as well as the gradient of the mineral density6 and material properties which exist in natural enamel. These areas were determined based upon the mineral maps generated from microCT images of the tooth. Figure 7 shows the nominated colorized mineral map of a buccolingual section of a premolar tooth. The mineral map (contour) displays the gradient of mineral density decreasing from enamel surface towards the dentine-enamel junction.
Table 1 shows the values for the mineral density and corresponding Young’s modulus, fracture toughness and strain energy release rate in different areas of enamel.
Previous studies have quantified the relationship between mineral density and Young’s modulus in enamel3,6,29. Accordingly, the mineral density of enamel lies mainly within the linear portion of the mineral density versus elastic modulus curve18; and therefore, elastic modulus values can be calculated from the values of calibrated mineral density. The previous studies have also shown that the fracture toughness of enamel is correlated with the distribution of mineral density30. However, in contrast to the trend of Young’s modulus, the higher density values translate to lower fracture toughness values30,31.
The critical strain energy release rate G (J/m2) is a material parameter related to the fracture toughness KIC (MPa·m½), indicating the energy required to propagate unit area of a crack. For a 2D plane-strain model, strain energy release rate (G) can be calculated as follows:
where E is the Young’s modulus, ν is Poisson’s ratio and KIC is the fracture toughness of the material.
Extended finite element method (XFEM)
Fracture analysis signifies an important field in engineering and has gained growing popularity in dental materials and biomechanics research recently. Ichim et al.32 modelled crack initiation and propagation for a range of case scenarios, such as contact-induced damage in layered materials systems and the failure of enamel, dentine, restored tooth and all-ceramic dental bridges. Barani et al.33,34 investigated longitudinal cracking in enamel by XFEM, in which the simulated cracks were in agreement with the experimental observations of the crack growth in human teeth. Li et al.35 compared the CDEM and XFEM for studying the fracture behaviours of all-ceramic dental prostheses, showing the cons and pros of each method.
In this present study, the XFEM fracture analysis was performed to evaluate the formation of cracks in the occlusal fissure area using Abaqus 6.14 (ABAQUS, Inc, Providence, RI). The cracking criterion used here was the maximum principal stress criterion as36,
where \({\sigma }_{max}^{0}\) represents the allowable maximum principal stress of the materials (enamel and dentine), \({\sigma }_{1}^{e}\) is the maximum principal stress in element (e) and \({f}^{e}\) indicates the stress ratio, determining if cracking would initiate in the element. A crack was assumed to occur when the maximum principal stress exceeds the prescribed tensile strength of the material. The subsequent crack growth was based upon the strain energy release rate37. The cracking region was considered in both enamel and dentine in the XFEM models. Detailed background information about the mechanics of XFEM fracture analysis can be obtained from the literature38,39,40.
References
He, L. H., Fujisawa, N. & Swain, M. V. Elastic modulus and stress–strain response of human enamel by nano-indentation. Biomaterials 27, 4388–4398, https://doi.org/10.1016/j.biomaterials.2006.03.045 (2006).
Bader, J. D., Martin, J. A. & Shugars, D. A. Incidence rates for complete cusp fracture. Community dentistry and oral epidemiology 29, 346–353, https://doi.org/10.1111/j.1600-0528.2001.290504.x (2001).
Sahni, A. Evolutionary aspects of reptilian and mammalian enamel structure. Scanning microscopy 1, 1903–1912 (1987).
Gidmark, N. J., Tarrant, J. C. & Brainerd, E. L. Convergence in morphology and masticatory function between the pharyngeal jaws of grass carp, Ctenopharyngodon idella, and oral jaws of amniote herbivores. The Journal of experimental biology 217, 1925–1932, https://doi.org/10.1242/jeb.096248 (2014).
Featherstone, J. D. Dental caries: a dynamic disease process. Australian dental journal 53, 286–291, https://doi.org/10.1111/j.1834-7819.2008.00064.x (2008).
Shahmoradi, M. & Swain, M. V. Quantitative characterization and micro-CT mineral mapping of natural fissural enamel lesions. Journal of Dentistry 46, 23–29, https://doi.org/10.1016/j.jdent.2016.01.012 (2016).
Nagano, T. Relation between the form of pit and fissure and the primary lesion of caries. Shika gakuho 60, 80–90 (1960).
Chai, H., Lee, J. J.-W., Constantino, P. J., Lucas, P. W. & Lawn, B. R. Remarkable resilience of teeth. Proceedings of the National Academy of Sciences, pnas. 0902466106, https://doi.org/10.1073/pnas.0902466106 (2009).
He, L. H. & Swain, M. V. Understanding the mechanical behaviour of human enamel from its structural and compositional characteristics. Journal of the Mechanical Behavior of Biomedical Materials 1, 18–29, https://doi.org/10.1016/j.jmbbm.2007.05.001 (2008).
Molnár, G. & Gravouil, A. 2D and 3D Abaqus implementation of a robust staggered phase-field solution for modeling brittle fracture. Finite Elements in Analysis & Design 130, 27–38, https://doi.org/10.1016/j.finel.2017.03.002 (2017).
Zhang, Z. et al. Mechanical benefits of conservative restoration for dental fissure caries. Journal of the Mechanical Behavior of Biomedical Materials 53, 11–20, https://doi.org/10.1016/j.jmbbm.2015.08.010 (2016).
Jagadish, S. & Yogesh, B. Fracture resistance of teeth with Class 2 silver amalgam, posterior composite, and glass cermet restorations. Operative dentistry 15, 42–47 (1990).
Nanci, A. & Bosshardt, D. D. Structure of periodontal tissues in health and disease. Periodontology 2000 40, 11–28, https://doi.org/10.1111/j.1600-0757.2005.00141.x (2006).
Sornsuwan, T. & Swain, M. V. Influence of occlusal geometry on ceramic crown fracture; role of cusp angle and fissure radius. Journal of the Mechanical Behavior of Biomedical Materials 4, 1057–1066, https://doi.org/10.1016/j.jmbbm.2011.03.014 (2011).
Giannakopoulos, A., Kordolemis, A. & Zisis, T. Development of Strong Surfaces Using Functionally Graded Composites Inspired by Natural Teeth—A Theoretical Approach. Journal of engineering materials and technology 132, 011009 (2010).
He, L.-H., Yin, Z.-H., van Vuuren, L. J., Carter, E. A. & Liang, X.-W. A natural functionally graded biocomposite coating–human enamel. Acta biomaterialia 9, 6330–6337, https://doi.org/10.1016/j.actbio.2012.12.029 (2013).
Rahbar, N. & Soboyejo, W. Design of functionally graded dental multilayers. Fatigue & Fracture of Engineering Materials & Structures 34, 887–897, https://doi.org/10.1111/j.1460-2695.2011.01581.x (2011).
Chen, Y. & Fok, A. Stress distributions in human teeth modeled with a natural graded material distribution. Dental materials: official publication of the Academy of Dental Materials 30, e337–348, https://doi.org/10.1016/j.dental.2014.08.372 (2014).
Soderholm, K.-J. Review of the fracture toughness approach. Dental Materials 26, e63–e77, https://doi.org/10.1016/j.dental.2009.11.151 (2009).
Schwass, D. R., Swain, M. V., Purton, D. G. & Leichter, J. W. A system of calibrating microtomography for use in caries research. Caries Research 43, 314–321, https://doi.org/10.1159/000226230 (2009).
Shahmoradi, M., Lashgari, M., Rabbani, H., Qin, J. & Swain, M. A comparative study of new and current methods for dental micro-CT image denoising. Dentomaxillofacial Radiology 45, 20150302, https://doi.org/10.1259/dmfr.20150302 (2016).
Rudin, L. I., Osher, S. & Fatemi, E. Nonlinear total variation based noise removal algorithms. Physica D: Nonlinear Phenomena 60, 259–268, https://doi.org/10.1016/0167-2789(92)90242-F (1992).
Li, E. et al. Smoothed finite element method for analysis of multi-layered systems – Applications in biomaterials. Computers & Structures 168, 16–29, https://doi.org/10.1016/j.compstruc.2016.02.003 (2016).
Li, W., Swain, M. V., Li, Q., Ironside, J. & Steven, G. P. Fibre reinforced composite dental bridge. Part II: Numerical investigation. Biomaterials 25, 4995–5001, https://doi.org/10.1016/j.biomaterials.2004.01.011 (2004).
Zhang, Z., Zhou, S., Li, Q., Li, W. & Swain, M. V. Sensitivity analysis of bi-layered ceramic dental restorations. Dental materials: official publication of the Academy of Dental Materials 28, e6–14, https://doi.org/10.1016/j.dental.2011.11.012 (2012).
Yoda, N. et al. Role of implant configurations supporting three-unit fixed partial denture on mandibular bone response: biological-data-based finite element study. Journal of oral rehabilitation 43, 692–701, https://doi.org/10.1111/joor.12411 (2016).
Yoda, N. et al. Effect of configurations of implants supporting a four-unit fixed partial denture on loading distribution. The International journal of prosthodontics 30, 68–70, https://doi.org/10.11607/ijp.5033 (2017).
Zhang, Z. et al. Effects of design parameters on fracture resistance of glass simulated dental crowns. Dental materials: official publication of the Academy of Dental Materials 32, 373–384, https://doi.org/10.1016/j.dental.2015.11.018 (2016).
An, B., Wang, R., Arola, D. & Zhang, D. The role of property gradients on the mechanical behavior of human enamel. Journal of the Mechanical Behavior of Biomedical Materials 9, 63–72, https://doi.org/10.1016/j.jmbbm.2012.01.009 (2012).
Bajaj, D. & Arola, D. D. On the R-curve behavior of human tooth enamel. Biomaterials 30, 4037–4046, https://doi.org/10.1016/j.biomaterials.2009.04.017 (2009).
Bajaj, D. & Arola, D. Role of prism decussation on fatigue crack growth and fracture of human enamel. Acta biomaterialia 5, 3045–3056, https://doi.org/10.1016/j.actbio.2009.04.013 (2009).
Ichim, I., Li, Q., Li, W., Swain, M. V. & Kieser, J. Modelling of fracture behaviour in biomaterials. Biomaterials 28, 1317–1326, https://doi.org/10.1016/j.biomaterials.2006.10.035 (2007).
Barani, A., Chai, H., Lawn, B. R. & Bush, M. B. Mechanics analysis of molar tooth splitting. Acta biomaterialia 15, 237–243, https://doi.org/10.1016/j.actbio.2015.01.004 (2015).
Barani, A. et al. Mechanics of longitudinal cracks in tooth enamel. Acta biomaterialia 7, 2285–2292, https://doi.org/10.1016/j.actbio.2011.01.038 (2011).
Li, W. et al. Computational Fracture Modelling in Bioceramic Structures. Advanced Materials Research 268-270, 853–856, https://doi.org/10.4028/www.scientific.net/AMR.268-270.853 (2011).
Maiti, S. K. & Smith, R. A. Comparison of the criteria for mixed mode brittle fracture based on the preinstability stress-strain field. International Journal of Fracture 24, 5–22, https://doi.org/10.1007/bf00020264 (1984).
Giner, E., Sukumar, N., Tarancón, J. E. & Fuenmayor, F. J. An Abaqus implementation of the extended finite element method. Engineering Fracture Mechanics 76, 347–368, https://doi.org/10.1016/j.engfracmech.2008.10.015 (2009).
Mohammadi, S. Extended Finite Element Method: for Fracture Analysis of Structures. 13–90 (John Wiley & Sons, 2007).
Zhang, Z. et al. Thermally induced fracture for core-veneered dental ceramic structures. Acta biomaterialia 9, 8394–8402, https://doi.org/10.1016/j.actbio.2013.05.009 (2013).
Zhang, Z. et al. Fracture behavior of inlay and onlay fixed partial dentures - An in-vitro experimental and XFEM modeling study. J Mech Behav Biomed Mater 59, 279–290, https://doi.org/10.1016/j.jmbbm.2016.01.035 (2016).
Chun, K. J., Choi, H. H. & Lee, J. Y. Comparison of mechanical property and role between enamel and dentin in the human teeth. Journal of Dental Biomechanics 5, 1–7, https://doi.org/10.1177/1758736014520809 (2014).
Giannini, M., Soares, C. J. & de Carvalho, R. M. Ultimate tensile strength of tooth structures. Dental Materials 20, 322–329, https://doi.org/10.1016/S0109-5641(03)00110-6 (2004).
Acknowledgements
This work was supported by Australian Research Council (ARC) through the Discovery (DP160104602) Scheme.
Author information
Authors and Affiliations
Contributions
B.W. & M.S. wrote the manuscript, analysed data and performed both experimental and numerical analysis. Z.Z. was involved in writing manuscript and performed XFEM numerical analysis. Y.S., B.S., M.S., Q.L. were involved in writing manuscript and directing the study. All authors discussed results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wan, B., Shahmoradi, M., Zhang, Z. et al. Modelling of stress distribution and fracture in dental occlusal fissures. Sci Rep 9, 4682 (2019). https://doi.org/10.1038/s41598-019-41304-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-41304-z
- Springer Nature Limited