Abstract
Densely integrated active photonics is key for next generation on-chip networks for addressing both footprint and energy budget concerns. However, the weak light-matter interaction in traditional active Silicon optoelectronics mandates rather sizable device lengths. The ideal active material choice should avail high index modulation while being easily integrated into Silicon photonics platforms. Indium tin oxide (ITO) offers such functionalities and has shown promising modulation capacity recently. Interestingly, the nanometer-thin unity-strong index modulation of ITO synergistically combines the high group-index in hybrid plasmonic with nanoscale optical modes. Following this design paradigm, here, we demonstrate a spectrally broadband, GHz-fast Mach–Zehnder interferometric modulator, exhibiting a high efficiency signified by a miniscule VπL of 95 V μm, deploying a one-micrometer compact electrostatically tunable plasmonic phase-shifter, based on heterogeneously integrated ITO thin films into silicon photonics. Furthermore we show, that this device paradigm enables spectrally broadband operation across the entire telecommunication near infrared C-band. Such sub-wavelength short efficient and fast modulators monolithically integrated into Silicon platform open up new possibilities for high-density photonic circuitry, which is critical for high interconnect density of photonic neural networks or applications in GHz-fast optical phased-arrays, for example.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Indium tin oxide (ITO), belonging to the class of transparent conductive oxides, is a material extensively adopted in high-tech industry such as in touchscreen displays of smartphones or contacts for solar cells. Recently, ITO has been explored for electro-optic (EO) modulation using its free-carrier dispersive effect enabling unity-strong index modulation1,2,3,4. The advantages of using ITO as opposed to traditional materials (e.g. Si) in photonic integrated circuit (PIC) modulation is manifold: (a) the carrier concentration in ITO can be 3–4 orders of magnitude higher compared to that of Si allowing more carriers to tune the dispersion behavior, this coupled with the capacitive gating schemes for altering ITO carrier concentrations as opposed to p–n junction based Si schemes, in turn, results in ITO modulators being able to obtain higher charge modulation per unit (lateral) area than Si for a given voltage; (b) the effect of the tuning carrier concentration on the optical parameters, i.e. index alteration, per unit applied bias, is in fact more dramatic compared to Si due to the lower permittivity of ITO compared to Si (\(\partial n = \partial \varepsilon^{1/2} \sim \partial \varepsilon /2\varepsilon^{1/2}\)); (c) the presence of an epsilon near zero (ENZ) region in the tolerable carrier concentration range within electro-static gating constraints can enhance attainable modulation effects; (d) the potential complementary-metal–oxide–semiconductor (CMOS) compatibility, i.e. the foundry adaptability of ITO allow for a seamless integration with the mature Si process. Thus, when taken together, ITO stands out from the crowd of next-generation active modulation materials. The potential foundry compatibility is the ‘actual’ reason for recent interest in usage of ITO in modulation. A feature we show here, the GHz-fast modulation capability using ITO, is forthcoming in recent literature. Phase-shifter technologies are used ubiquitously in data communication, optical phased arrays, analog and RF photonics, sensing etc. Here we demonstrate a Mach–Zehnder interferometer (MZI) based modulator paving the way for a comprehensive platform of heterogeneous integration of ITO-based electro-optic devices into silicon PICs. We have previously shown the interplay between optical waveguide modes (e.g. photonic bulk vs. plasmonic) and an active material figure-of-merit (∆n/∆α), where n is the real part of the complex refractive index and α is the optical loss, arising directly from Kramers–Kronig (K–K) relations5. This ITO material can be selectively adapted by process conditions6, for operation in either an n-dominant or α-dominant region defined by the level of the carrier concentration5. We have recently demonstrated an MZI based modulator using photonic-modal ITO-oxide-Si characterized by a VπL = 0.52 V∙mm3, and a plasmonic version deploying a lateral gate exhibiting a VπL = 0.063 V∙mm7 each deploying a different ITO process either for a photonic3 or plasmonic mode7. The latter enables strong light-matter-interactions i.e. extrinsic slow-light effects, coupled with the intrinsic slow-light effect of the ITO material, i.e. epsilon-near-zero (ENZ) effect allowing high mode confinement which is synergistic with the MOS capacitor approach of free-carrier modulation in ITO8. The net effect is that this slow-light scheme enables just 1–5 μm short π-phase-shifters5. Such micrometer-compact opto-electronics enable small capacitances, in the orders of ~ fF, facilitating a reduction in power consumption and small RC delays thus facilitating fast signal reconfiguration. Note, while operating at ENZ region incurs increased losses, which is non-ideal for phase shifter applications; as such, the desired operation region is here adequately close-to, but not at the high-loss ENZ (ENZ located in α-dominant region)5.
One can certainly assert that there are applications where established EO materials such as lithium niobate (LiNbO3, LN), especially bonded to Si, has particular modulation advantages. However, applications requiring dense chip component integration such as neuromorphic hardware, electronic-photonic hybrid accelerators or dense sensor arrays, etc. demand very dense integration of over ~ 104 optical components, where device footprint of even 100 μm2 starts to impact performance. For such applications, ITO provides synergistic benefits when monolithically and heterogeneously integrated with low-cost Si PICs. It is also worthwhile to mention here that, the demonstrated capabilities of ITO as a strong nonlinear material can designate desirability as one can combine many different functionalities on the same chip with the same active material9,10. In fact, unlike careful crystal orientation control in LN11, ITO thin films feature intrinsically homogeneous optical characteristics leading to high orders of process control. The lurking and fundamental challenges with LN modulators rest in their large footprint and weak electrostatics, which are both geometry related; electrostatically inefficient confinement of the RF field with both electrodes on opposite sides of waveguide necessarily widens the gap; whereas for the ITO case one of the electrodes is the active layer itself tightening the gap for efficient manipulations. This results in an about 100 × weaker electrostatics compared to an ITO ‘MOS’ like setup. ITO, in conjunction with a plasmonic optical metal–oxide–semiconductor (MOS) mode, on the other hand, can harness the full opportunities of electrostatic gating that the semiconductor industry has perfected over the last 1/2 century. In LN-optoelectronics, however, a metal contact cannot be placed in close proximity to the waveguide, which is required for efficient electrostatics, because the so-incurred loss-per-unit-length would be detrimental. Also, the selective etching process in microstructuring LN films is quite delicate and arduous; whereas heterogeneous integration of ITO thin films on Si is rather straightforward. Microstructured LN architectures are not compatible with the mature Si process flow, whilst the semiconductor industry already process ITO in their foundries for a plethora of applications including display technology and transparent contacts. When compared, LN seems the odd-one-out, and ITO bears much potential for market adoption specifically in short signaling applications (inter and intra-chip) and most significantly for emerging photonic accelerators and neuromorphic photonics (i.e. dense neural network connections)12.
Here, we introduce and demonstrate an ITO-plasmon-based phase-shifter heterogeneously integrated into a silicon photonic MZI delivering GHz-fast modulation while being spectrally broadband, thus opening up opportunities for multi-spectral operation. Refraining to exploit feedback from a resonator has several advantages: (a) no spectral alignment to the pump laser is required; (b) thus, no heaters are needed for thermal tuning, which would raise the power consumption per-device into the ~ nJ/bit levels13; (c) heat spreads ~ 100 μm’s across the PIC, thus packaging density can be significantly improved; (d) the photon-lifetime of high-quality (Q) cavities can limit RF modulation speeds due to the long photon lifetime, which is not the case here. Our ITO hybrid plasmonic MZI modulator can exploit efficient electrostatics to its fullest potential leading to CMOS-compatible (~ 1–2 V) small drive voltages when optimized in contrast to LN-based schemes. Note, despite the high losses per unit length the total loss of our approach is actually comparable to silicon photonics devices, because the device is just mere 1–3 μm short while enabling a VπL being 2–3 orders of magnitude smaller.
Figure of merit (FOM) for MZIs
Phase modulators invariably require some method of interferometric scheme such as cavity feedback or MZI-based arrangements to compare the actively modulated optical phase change with a reference beam in order to induce a change in optical transmitted amplitude via interference. As such, these schemes intrinsically suffer from an extended footprint conundrum, as opposed to electro absorption schemes that can be implemented rather straightforwardly in a linear waveguide arrangement. In MZIs, the product of the half-wave voltage and the active modulator length, VπL, is a key figure of merit (FOM), since both elemental parameters exhibit a tradeoff between obtaining π-phase shifts at the optical output with increased device length or applied voltage. As such, continuous efforts to minimize VπL in MZI schemes have succeeded in realizing miniscule FOMs (10′s of V μm) over the years (Table 1).
Lithium niobate-based MZIs are commercially available featuring rather high FOMs (VπL = 104–105 V μm) due to their field-based modulation mechanism characterized by the weak Pockels effect necessitating extremely long device lengths in the range of 1–10 cm. Improvements in performance are obtained with the QCSE in III-V30,31,33 or enhanced Pockels effect in emerging materials such as polymers27,34,36. Augmented light-confinement for improving optical and RF mode overlap (Γ) with the active material in plasmonic structures have also been sought34,35,36 (Table 1). This work focuses on an experimentally demonstrated plasmonic ITO based MZI device and the achieved FOM in our results suggests that our performance is on-par with recent exemplary works despite being the first of its kind.
The devices exhibiting a high-performance FOM (i.e. reduced VπL) amount to plasmonics, integration of organic/polymer materials, III-V quantum well structures, etc. (Table 1). While many of these schemes essentially offer acceptable performance, they are mostly difficult to integrate in the mature Si process. Our choice of ITO as the active modulation material can avail ease of fabrication and potential CMOS integration37.
Device design
A symmetrical (EO passive) 1 × 1 MZI structure with the same length for both Mach–Zehnder arms and 50:50 Y-junctions on both (input and output) sides on a Silicon on insulator (SOI) platform is chosen as the underlying structure for the modulator. This essential design choice ensures an equal optical output; we note that sidewall roughness, surface defects, alignment issues, and other such imperfections during fabrication can hinder from achieving perfectly symmetrical MZI structures. Beyond this passive MZI in SOI, subsequent processing for the active device region includes depositing a 10 nm thin film of ITO on the device section using ion beam deposition (IBD) and a top plasmonic metal (Ti/Au) stack on top of a portion of one arm separated by an oxide layer to facilitate gating (Fig. 1). We use a relatively high-k dielectric, Al2O3, for the gate oxide of 20 nm using atomic layer deposition (ALD) since the modulation efficiency i.e. (extinction-ratio, ER/bias-voltage) improves with enhanced electrostatics. Note, IBD allows for high-quality ITO films as it yields dense crystalline pinhole-free films with high uniformity, and the room temperature process deployed here does not anneal the ITO as a byproduct of the process (i.e. Sn carriers do not become activated, which would prevent the modulation potential, which is incidentally a different use of ITO compared to its application in touch screen displays or as low resistance contacts in the solar industry, for example). With respect to nanophotonic device fabrication, as required here, IBD enables precise controllability of material properties such as microstructure, non-stoichiometry, morphology, crystallinity for instance38,39.
The K-K relations dictate that highly-index tunable materials are accompanied by inherently increased absorption as a byproduct of modulation, and ITO is no different in this regard. This K-K modulated absorption in free-carrier dispersion based materials (e.g. Si, ITO) poses a tradeoff for utilizing such highly tunable active modulation materials40,41,42. As such, MZI arm optical outputs can become unbalanced during modulation which negatively impacts achievable ER43. The ER deterioration leads to degraded optical signal fidelity (i.e. phase errors at the output and alter frequency chirps) originating from the complex part of the optical phase44. However, improvements in the arm loss imbalance, and hence, ER, can be mitigated, however not extinguished, by tuning the arm field losses statically3; matching the amplitude of the optical signal (i.e. loss) in both arms of the MZI is an inherent challenge in utilizing a highly index tunable and lossy (by fundamental K-K) material such as ITO, achieving satisfactory modulation depth. The interference from both arms at the output Y-junction should converge ideally, this phenomenon is referred to hereafter as balancing. We choose to employ metallic strips on the un-modulated arm to justify the so incurred modulated loss counterpart from active tuning of the modulated arm enforcing via similar plasmonic broadband loss. We calculate the desired length of the passive metal contact, Lb on the un-modulated arm of the MZI (Fig. 1) taking into consideration both ON and OFF states of modulator operation imposing an averaged amount of loss on the un-modulated arm to balance the MZI and facilitating a high ER3.
Material and modal properties
The underlying modulation mechanism for ITO is free-carrier dispersion from an applied bias. The Drude model characterizes the ITO material response well in the near infra-red region (λ > 1 μm). The relative permittivity of free electron plasma in the Drude approximation can be written as \(\varepsilon_{r} = \varepsilon_{\infty } - \left[ {N_{c} q^{2} /\varepsilon_{0} m^{*} \left( {\omega^{2} + i\gamma \omega } \right)} \right]\); where \(\varepsilon_{\infty }\) is the dielectric constant of the undoped semiconductor also referred to as the high-frequency or “background” permittivity, q is the electronic charge, \(m^{*}\) is the conduction effective mass, ω is the angular frequency, and \(\gamma = 1/\tau\) is the collision frequency or scattering rate of the free carriers quantified by the detuning from any interband resonances thereof. Our deposited ITO thin films exhibit similar optical indices (real and imaginary parts) as obtained from Drude model fits in previous works40,41,42. Spectroscopic ellipsometry of deposited thin films show a decreasing real part, n and an increasing imaginary part, κ of the material index near our operating wavelength, λ = 1550 nm (Fig. 2a–e), which is expected from the K-K characteristics5,41.
Parameters obtained from variable angle spectroscopic ellipsometry (Ψ and ∆) and subsequent fitting derived analysis revealed relevant electrical and optical properties of our ITO thin film as deposited (Fig. 2a). Ellipsometric measurements address the change in the polarization (p- and s-polarizations) of the reflected light from our deposited ITO thin film through a ratio of the complex Fresnel coefficients (\(\rho = \tilde{r}_{p} /\tilde{r}_{s} = {\text{tan}}\left( {\Psi } \right){\text{exp}}\left( {i{\Delta }} \right)\)) where Ψ relates to an amplitude ratio and ∆ relates to the phase variation from the incident phase45. A general oscillator-based approach in fitting assures relevant physically realizable (K-K consistent) parameters extraction (see methods). A Drude fit in our wavelengths of interest (i.e. NIR region) indicates the as-deposited carrier concentration, Nc of 3.13 × 1020 cm-3. Corresponding parameters such as scattering time, τ of 4.72 ± 0.01 fs; resistivity, ρ of 8.41 × 10–4 Ω cm and mobility, μ of 23.72 ± 0.06 cm2/V-s are also extracted from the ellipsometric data and reinforced with further metrology such as 4-probe, transmission line, Hall-effect measurements, etc. An average carrier concentration change ∆Nc = 2.12 × 1020 cm-3 estimated from the gated measurements (see results and discussion section) places the operation of these devices between carrier levels of (2.07–4.19) × 1020 cm-3, which is still in the n-dominant operation region, however intentionally away from the high-loss ENZ (6–7 × 1020 cm-3) state, yet sufficiently near to capture a slow-light effect5. Modulated carrier concentration profile is implemented using the modified Thomas–Fermi approximation (MTFA) method characterized by the MTFA-associated screening length, λMTFA ∼ 3 nm46. MTFA allows for the quantum–mechanical influence of an infinite potential barrier at the surface and has shown compliance for semiconductors with surface band bending at the nanoscale46.
In an electrical capacitive stack with ITO being one of the electrodes, application of a drive voltage can place the capacitor into states of accumulation or depletion (inversion in ITO has not yet been demonstrated), thus changing the carrier concentration and hence the optical complex index. The optical property of the active material, here ITO, therefore changes significantly, resulting in strong optical modulation effects. In praxis, a 1/e decay length of about 5 nm has been measured before47, and modulation effects have been experimentally verified over 1/e2 (∼10 nm) thick films from the interface of the oxide and ITO1. In order to extract relevant parameters including the effective indices (real and imaginary parts, neff and κeff) and confinement factors, Γ, we perform FEM eigenmode analysis for our structure (Fig. 3a, inset). The first order transverse magnetic (TM)-like mode is selected following the TM-optimized grating couplers in the fabricated device and the mode profiles indicate an increase in the light confinement with modulation by almost 2.03 × which is aligned with results from our previous work as we operate sufficiently away from the ENZ point in the n-dominant region (Fig. 3a)5,40,41.
Passive MZI designs are swept using waveguide lengths for both the arms of the interferometer structure and the output waveguide separately to find the passive optical losses in the taped out structure and determine the length dependent and independent losses. In order to ascertain insertion losses arising from the fabricated active device, we choose to carry out a cutback measurement of the passive MZI structures varying lengths of the waveguides. Employing a cutback method, we can differentiate the length dependent and independent losses in the passive structure (Fig. 3b). The length independent losses (i.e. arising from the grating couplers, waveguide bends, Y-junctions, etc.) can aid the insertion loss calculations for the active device. We choose to vary the arm waveguide lengths of the MZI maintaining a symmetrical design and also independently varied the output waveguide length in the structure. Both the sweeps provide nearly the identical results in the static losses. We find the length independent static losses are about 22 dB for our MZI design accounting for all waveguide bends, grating couplers and Y-junctions. The Y-junctions used fair an average insertion loss of 0.28 ± 0.02 dB each48. Previously we found similar TM grating coupler losses to be 8 dB/coupler on the same SOI platform49. Neglecting the fabrication variation that might arise from separate multi project runs, we can roughly estimate the waveguide bending losses as 0.6 dB/bend from our structure with all bending radii of 60 μm maintained constant throughout the design (i.e. to and from the Y-junctions for both MZI arms and after the output Y-junction).
Active phase shifter devices are also swept in length from sub-λ (1.4 μm) to λ-scale (3.5 μm) range for determining propagation and coupling losses for the active capacitive stack formed by the ITO-oxide-metal layers from the waveguide and passivation cladding layer interface (Fig. 3c). Cutback measurements reveal 1.6 dB/μm propagation loss in the active capacitive stack and an additional 1.3 dB/coupler loss from in/out coupling of the mode from the Si waveguide, while the passive contact for loss balancing (Fig. 1a, Lb) exhibits a 1.2 dB/μm propagation loss and 1.1 dB/coupler loss correspondingly. The corresponding overall insertion losses (IL) for the differently scaled modulators range from 6.7 to 10.1 dB. Note that the high loss per unit length in plasmonics is alleviated by an enhanced light–matter interaction enabling λ-short device lengths; thus the total IL is comparable to Si photonic MZIs.
Results and discussion
Our sweep of the active phase-shifter device length (Lps) ranges from sub-λ (1.4 μm) to λ-scale devices (3.5 μm) (Fig. 1b). Broadband spectral response is measured in C-band region (~ 30 nm, Fig. 4a); which is expected since the plasmonic resonance of the mode has a FWHM of 100’s of nm. The spectral response of the device is determined by ITO dispersion and proximity to ENZ. For ultra–broadband applications (e.g. 100 + nm) ITO modulators for different spectral regions (e.g. ∆λ = 50 nm) can be processed using different conditions as demonstrated earlier6. Functional capacitor traits in the measured bias range is observed from I-V measurements (Fig. 4b). The I–V measurements do not portray any breakdown of the gate oxide or saturation behavior of the MOS capacitor in the applied voltage range. Note, the gate oxide breakdown occurs at nearly 12 V which was confirmed in several devices on the same chip.
DC electro-optic transmission power tests and squared cosine fit (as dictated by MZI operating principle, see methods) result in an ER of ~ 3 dB to > 8 dB, respectively (Fig. 4c). The measured VπL is just 95 ± 2 V∙μm and found to be rather constant across all device scaling. The quality of the fit symbolized by the coefficient of determination (R2) is above 0.99 in all three cases. While these prototype devices require a relatively high voltage (Vπ, as-is ~ 26 V, \(\varepsilon_{{r,Al_{2} O_{3} }}\) = 11, tox = 20 nm), the Vπ, future-option < 2 V can be reached using 5 nm high-k dielectrics (e.g. Hf3N450) in a push–pull configuration and trivial capacitor reductions during lithography. The results indicate a modal index change ∆neff of ~ 0.16 due to carrier modulation across the applied voltage range (Fig. 4d) and FEM eigenmode analysis (inset, Fig. 3a) reveals an index change in the active ITO material of about 0.6 (Fig. 4e) reflecting a ~ 2.03 × increase in the modal confinement factor (Γ) corresponding to active biasing, slightly lower than previous modulators in ITO3, and intentionally enabling lower insertion loss (IL). The effective index change with modulation can be expressed by a linear approximation with applied voltage as \(\partial n_{eff} /\partial V_{d}\) ∼ 7.98 × 10−3 V−1 ~ 1%V-1. The material index change shows meager nonlinearity for negative biasing as we operate in the ITO material’s n-dominant region sufficiently close to ENZ beneficially extracting proximal ENZ effects while staying away from the high-loss ENZ point to minimize IL concerns37. Note, the change in both the indices (material and effective) resemble a decrease in the corresponding indices as modulation assimilates to blue-shifts in device resonance, however, is barely resolvable in our single pass MZ configuration (Fig. 4a) but is well-known from any cavity based operations. Modal dispersion, \(\partial n_{eff} /\partial \lambda\) calculated from eigenmode analysis indicates 1.12 × 10–3 nm-1 resonance shift in our MOS structure. The calculated group index in the modal structure is 4.1 indicating slow-light effects attribute to about 0.76 nm shift in the corresponding spectrum across applied bias of 20 V (Fig. 4a). However, our non-resonant MZI measurements do naturally not resolve this resonance shift given the plasmonic mode interferes in ascertaining the central resonant wavelength; this reported value is taken from the transmission spectra which can relinquish to various noise in the system (Fig. 4a).
To test the temporal response of these sub-λ-compact ITO MZI modulators, we generate a low power modulating signal (0 dBm) with a network analyzer for obtaining the frequency response (S21). A bias-tee is used to mix the DC voltage bias of 6 V with the RF signal (Fig. 5a). A broadband EDFA (~ 35 dB) amplifies the RF output from the modulator and an optical tunable filter is used to enhance the signal fidelity which also reduces the undesired noise level by 20 dB. A high-speed photodetector (τresponse = 10′s ps) collects the modulated signal into a single mode fiber. The small signal response shows a -3 dB roll-off speed of 1.1 GHz (Fig. 5b). This matches RC-delay estimations for a capacitance of 213 fF (area = 42 μm2) and a total resistance of 680 Ω, which is aligned with our earlier results using similar process conditions3. Plasmonics enables reduced series resistance in device configurations as one of the contacts realized by metal is ‘free’ leading to small RC-delays51, as shown here. Dynamic switching energy of ~ 2.1 pJ/bit proportionately characterizes the spectral broadband tradeoff in the sub-λ device. Comparative performance metrics across all device length scaling are shown where the goal is to minimize the value in all axes (Fig. 5c). The sub-λ device outperforms both longer counterparts in all metrics mainly benefitting from the reduced resistance and capacitance. Future improvements such as optimized contact placement, pad-overlay optimization, annealing, plasma treatment, deployment of high-k gate dielectrics including tox scaling, and utilizing push–pull schemes can enable 10′s of GHz operation requiring only a few fJ/bit. It is worthy to point out that, in non-resonator schemes aJ/bit energy levels are presumably not feasible due to the tradeoff in spectral bandwidth (i.e. no cavity feedback)37. However, the switching energy of directional-coupler based 2 × 2 switches, for instance, does improve with the effective mode’s index change52, which, as we have seen herein, can be rather high using ITO hybrid photonics.
Conclusion
In conclusion, here, we have experimentally demonstrated a spectrally broadband, extremely compact (sub-wavelength short), GHz-fast ITO-based Mach Zehnder Interferometer-based modulator in silicon photonics exhibiting a low VπL of 95 V∙μm enabled by (a) efficient material modulation in ITO optimized for real-part index operation, (b) a plasmonic hybrid mode enhancing the light-matter interaction, (c) relatively low electrical resistance, and (d) operating away from an optical resonance. This demonstration bears relevance, since ITO is a foundry-compatible material with a reduced barrier for co-integration. Unlike the crystal orientation sensitive LiNbO3, ITO optoelectronics is synergistic to enhancing electrostatics known from transistor technology. Such micrometer-compact next generation and foundry-near phase-shifters and electro-optic modulators monolithically integrated with photonic integrated circuits, here silicon as an example, enable high PIC-component density valuable for applications such as data communication, signal processing, GHz-fast optical phased arrays for beam-steering applications, and neuromorphic photonics and optical information processing.
Materials and methods
MZI transfer matrix
Different configurations in MZI structures can be studied using the transfer matrix model. Each sub-component of the MZI is represented by a vector or a matrix and the final outputs are obtained by multiplying the individual matrices. The matrix formulation of the electric field outputs of the Y-junction is:
where, EIn, EY,Out1, and EY,Out2 are the electric field phasors of the input, output of arm 1, and output of arm 2, respectively. The δ1 and δ2 are the output power ratio of arm 1 and arm 2 of the Y-junction relative to the input. For a lossless Y-junction with identical splitting, δ1 = δ2 = ½. The outputs of the 50:50 directional coupler, ignoring loss, in matrix form is:
where, δ is the power splitting ratio between the two arms. The imaginary unit i represents the π/2 phase shift between the direct and cross coupled inputs. The propagation in the arms of the interferometer is modeled by modifying the amplitude and the phase of the phasors.
where, ϕ1 and ϕ2 is the total phase shift in arm 1 and arm 2, α1 and α2 is the optical propagation loss in the respective arms, and L1 and L2 are the total lengths of each arm. The terms EIn,arm1 and EIn,arm2 are the input fields at the two arms of the interferometer, respectively, and EOut,arm1 and EOut,arm2 are the fields after the two phase shifting regions, respectively.
Phase shift differences between the two paths of the interferometer, in silicon MZIs, can be introduced by an imbalance in length, thermal tuning, and modulation by the plasma dispersion effect. The imbalance can be unintentional, for instance due to variations in fabrication or intentional to create a measurable free spectral range and facilitate phase shift measurements. The total phase shift and loss can be divided into these three individual components, thus, the total phase shift for arm 1 and arm 2 can be expressed as:
where, Lnm,1 and Lnm,2 are the non-modulated lengths of each arm, Lactive,1 and Lactive,2 are the electrically modulated lengths of each arm, and Lthermal,1 and Lthermal,2 are the thermally modulated lengths of each arm. The effective index of refraction is a function of voltage for electrical modulation and a function of temperature for thermal modulation. With this partition, the total length of an arm L is the sum of the lengths Lnm, Lactive, and Lthermal of that arm. Finally, the total transmission can be obtained by multiplying the matrices together. For a 1 × 1 MZI, the output electric field is obtained as:
where, [Y] represents the vector of the Y-junctions at the output and input, and [MZ] is the 2 × 2 matrix for the phase shift in the arms of the interferometer. The output intensity Iout is then obtained by the square of the absolute value of the output electric field. The optical intensity in decibels is:
A simplified expression for the electric field at the output of the 1 × 1 MZI can be obtained by considering only one type of phase changing mechanism and assuming equal physical path lengths. The electric field output for this special case involves both an amplitude modulation and a phase modulation component. For intensity modulation, the amplitude modulation is desired but the phase modulation is unwanted. On the other hand, for phase shift keying modulation formats, the amplitude modulation that occurs is undesired.
The argument of the cosine term corresponds to the amplitude modulation as a byproduct of the phase variation whereas the exponential term corresponds to the actual change in the phase of the propagating wave. Similarly, a simplified expression for the intensity at the output of the 1 × 1 MZI can be obtained by employing the exponential-hyperbolic and Euler's relation. The transmission of the MZI is:
where, ∆α is the difference in loss between the two arms. The argument in the cosine term is the relative phase shift leading to the cosine term evaluating to 1 for constructive interference, and -1 for destructive interference.
ITO ion beam deposition
Ion beam depositions followed our earlier disclosed processes with some tweaks3,7. The 10 nm film of ITO was deposited on top of one of the passive waveguides (one arm of the MZ) on SOI substrate at room temperature via ion beam deposition (IBD) using the 4Wave IBD/BTD cluster sputter deposition system following a passivation oxide ALD layer of 5 nm. An RF ion gun focused Ar ions onto substrate targets of ITO. The ITO target stoichiometry is 90 wt % In2O3/10 wt % SnO2. A small flow of O2 (2 sccm) was used. The process used an Ar flow rate of 20 sccm, beam voltage of 600 V, beam current of 220 mA and acceleration voltage of 150 V. The sample was set at an angle of 115° and rotated at 10 rpm to ensure smooth profile. The deposition rate used was 0.77 Å/s. The temperature for the process was 20 °C to refrain annealing effects. The base vacuum used was 2 × 10–8 Torr and the deposition uniformity was confirmed as 1.5% (1σ) over a 190 mm diameter.
Fabrication processes
Fabrication processes of the active device followed our earlier disclosed methods with some necessary alterations3,7. The pattern transfers were done in e-beam lithography (EBL) using the Raith VOYAGER tool with PMMA based photoresists and MIBK1:3IPA developer for 60 s. 47 nm of Au for contacts was deposited using an e-beam evaporation system (CHA Criterion) as it has reasonably low ohmic loss at near IR wavelengths. An additional 3 nm adhesion layer of Ti was used in the contacts. The Al2O3 oxide was deposited using the atomic layer deposition (ALD) technique as it provides reliable performance characteristics. The Fiji G2 ALD tool was used at low temperature settings (100 °C) for 100 cycles to deposit about 20 nm of Al2O3 to ensure higher film quality and to avoid any annealing effects to the ITO. Filmetrics F20-UV system was used to characterize Al2O3 deposition rate. As the ALD tool does not allow patterned processing due to chamber contamination concerns, an etch step was required on top of the Si contact to remove the oxide over it for electrical probing. We used a rather slow wet etch process for Al2O3 using an MF319 solution in the contact pad area (See supplementary information S1). MF319 contains tetramethylammonium hydroxide (TMAH) which reacts with the Al and can etch the oxide thereof.
Spectroscopic ellipsometry
The J. A. Woollam M-2000 DI spectroscopic ellipsometer was used to characterize the optical constants of the deposited ITO thin films as it can provide fast and accurate thin film characterization over a wide spectroscopic range. Variable angle spectroscopic elliposometric (VASE) data was collected from three different angles of 65°, 70° and 75°. First, the transparent region was fitted using Cauchy model to find the closest thickness value for ITO thin film with the deposited value and was kept fixed. Then, the data was fitted using B-spline model and subsequently the fitting region was expanded from transparent region to the entire wavelength region. Afterwards the data was re-parameterized using different oscillators in GenOsc, i.e. Drude, Lorentz and Tauc-Lorentz oscillators to find relevant optical constants (See supplementary information S1). The Tauc-Lorentz model has been reported to provide excellent fitting to various TCO materials53,54. A mean square error (MSE) value of 2.001 and uniqueness of the fitted thickness parameter coupled with matching the thickness from deposition reinforces the fit.
References
Sorger, V. J., Lanzillotti- Kimura, N. D., Ma, R. & Zhang, X. Ultra-compact silicon nanophotonic modulator with broadband response. Nanophotonics 1(1), 17–22 (2012).
Melikyan, A. et al. Surface plasmon polariton absorption modulator. Opt. Express 19(9), 8855–8869 (2011).
Amin, R. et al. 052 V mm ITO-based Mach-Zehnder modulator in silicon photonics. APL Photonics 3(12), 126104 (2018).
Li, E., Gao, Q., Liverman, S. & Wang, A. X. One-volt silicon photonic crystal nanocavity modulator with indium oxide gate. Opt. Lett. 43(18), 4429–4432 (2018).
Amin, R. et al. Active material, optical mode and cavity impact on nanoscale electro-optic modulation performance. Nanophotonics 7(2), 455–472 (2017).
Gui, Y. et al. Towards integrated metatronics: a holistic approach on precise optical and electrical properties of indium tin oxide. Sci. Rep. 9(1), 11279 (2019).
Amin, R. et al. A lateral MOS-capacitor enabled ITO Mach-Zehnder modulator for beam steering. J. Lightwave Technol. 38(2), 282–290 (2020).
Kinsey, N. & Khurgin, J. B. Nonlinear epsilon-near-zero materials explained: opinion. Opt. Mater. Exp. 9(7), 2793–2796 (2019).
Alam, M. Z., Leon, I. D. & Boyd, R. W. Large optical nonlinearity of indium tin oxide in its epsilon-near-zero region. Science 352(6287), 795–797 (2016).
Alam, M. Z., Schulz, S. A., Upham, J., Leon, I. D. & Boyd, R. W. Large optical nonlinearity of nanoantennas coupled to an epsilon-near-zero material. Nat. Photonics 12(2), 79–83 (2018).
Wang, C. et al. Integrated lithium niobate electro-optic modulators operating at CMOS-compatible voltages. Nature 562(7725), 101–104 (2018).
Amin, R. et al. ITO-based electro-absorption modulator for photonic neural activation function. APL Mater. 7(8), 081112 (2019).
Dong, P., Chen, Y., Duan, G. & Neilson, D. T. Silicon photonic devices and integrated circuits. Nanophotonics 3(4–5), 215–228 (2014).
Gardes, F. Y., Thomson, D. J., Emerson, N. G. & Reed, G. T. 40 Gb/s silicon photonics modulator for TE and TM polarisations. Opt. Express 19(12), 11804–11814 (2011).
Courjal, N., Porte, H., Hauden, J., Mollier, P. & Grossard, N. Modeling and optimization of low chirp LiNbO3 Mach-Zehnder modulators with an inverted ferroelectric domain section. J. Lightwave Tech. 22(5), 1338–1343 (2004).
Lucchi, F. et al. Very low voltage single drive domain inverted LiNbO3 integrated electro-optic modulator. Opt. Express 15(17), 10739–10743 (2007).
Wooten, E. L. et al. A review of lithium niobate modulators for fiber-optic communications systems. IEEE J. Select. Topics Quant. Elec. 6(1), 69–82 (2000).
Liao, L. et al. 40 Gbit/s silicon optical modulator for high speed applications. Electron. Lett. 43(22), 1196–1197 (2007).
Janner, D., Tulli, D., Garcia-Granda, M., Belmonte, M. & Pruneri, V. Micro-structured integrated electro-optic LiNbO3 modulators. Laser Photon. Rev. 3(3), 301–313 (2009).
Ziebell, M. et al. 40 Gbit/s low-loss silicon optical modulator based on a pipin diode. Opt. Express 20(10), 10591–10596 (2012).
Thomson, D. et al. 50Gbit/s silicon optical modulator. IEEE Photon. Technol. Lett. 24(4), 234–236 (2012).
Thomson, D. J. et al. High contrast 40Gbit/s optical modulation in silicon. Opt. Express 19(12), 11507–11516 (2011).
Chen, L., Doerr, C. R., Dong, P. & Chen, Y.-K. Monolithic silicon chip with 10 modulator channels at 25 Gbps and 100-GHz spacing. Opt. Express 19(26), B946–B951 (2011).
Xiao, X. et al. High-speed, low-loss silicon Mach-Zehnder modulators with doping optimization. Opt. Express 21(4), 4116–4125 (2013).
Dong, P., Chen, L. & Chen, Y.-K. High-speed low-voltage single-drive push-pull silicon Mach-Zehnder modulators. Opt. Express 20(6), 6163–6169 (2012).
Wang, C., Zhang, M., Stern, B., Lipson, M. & Loncar, M. Nanophotonic lithium niobate electro-optic modulators. Opt. Express 26(2), 1547–1555 (2018).
Akiyama, S., Baba, T., Imai, M., Akagawa, T., Noguchi, M., Saito, E., Noguchi, Y., Hirayama, N., Horikawa, T., & Usuki, T. 50-Gbit/s silicon modulator using 250-m-long phase shifter based on forward-biased pin diodes. In Proceedings of 9th IEEE International Conference on Group IV Photonics (IEEE, 2012), pp. 192–194.
Brimont, A. et al. High-contrast 40 Gb/s operation of a 500 μm long silicon carrier-depletion slow wave modulator. Opt. Lett. 37(17), 3504–3506 (2012).
Fujikata, J., Ushida, J., Nakamura, T., Ming-Bin, Y., ShiYang, Z., Liang, D., Guo-Qiang, P. L., & Kwong, D. 25 GHz operation of silicon optical modulator with projection MOS structure. In Optical Fiber Communication Conference, OSA Technical Digest (CD) (Optical Society of America, 2010), paper OMI3.
Dogru, S. & Dagli, N. 0.77-V drive voltage electro-optic modulator with bandwidth exceeding 67 GHz. Opt. Lett. 39(20), 6074–6077 (2014).
Shin, J., Chang, Y.-C. & Dagli, N. 0.3 V drive voltage GaAs/AlGaAs substrate removed Mach-Zehnder intensity modulators. Appl. Phys. Lett. 92(20), 201103 (2008).
Chen, H.-W., Kuo, Y. & Bowers, J. E. Hybrid silicon modulators. Chin. Opt. Lett. 7(4), 280–285 (2009).
Dogru, S. & Dagli, N. 0.2 V drive voltage substrate removed electro-optic Mach-Zehnder modulators with MQW cores at 1.55 μm. J. Lightwave Technol. 32(3), 435–439 (2014).
Kieninger, C. et al. Silicon-organic hybrid (SOH) Mach-Zehnder modulators for 100 GBd PAM4 signaling with sub-1 dB phase-shifter loss. Opt. Express 28(17), 24693–24707 (2020).
Green, W. M. J., Rooks, M. J., Sekaric, L. & Vlasov, Y. A. Ultra-compact, low RF power, 10 Gb/s silicon Mach-Zehnder modulator. Opt. Express 15(25), 17106–17113 (2007).
Heni, W. et al. Silicon-organic and plasmonic-organic hybrid photonics. ACS Photon. 4(7), 1576–1590 (2017).
Amin, R. et al. Sub-wavelength GHz-fast broadband ITO Mach-Zehnder modulator on silicon photonics. Optica 7(4), 333–335 (2020).
Koh, S.-K., Han, Y., Lee, J. H., Yeo, U.-J. & Cho, J.-S. Material properties and growth control of undoped and Sn-doped In2O3 thin films prepared by using ion beam technologies. Thin Solid Films 496(1), 81–88 (2006).
Lee, S. H. et al. Properties of ITO (indium tin oxide) film deposited by ion-beam-assisted sputter. Mol. Cryst. Liq. Cryst. 564(1), 185–190 (2012).
Amin, R. et al. Low-loss tunable 1D ITO-slot photonic crystal nanobeam cavity. J. Opt. 20(5), 054003 (2018).
Amin, R. et al. A deterministic guide for material and mode dependence of on-chip electro-optic modulator performance. Solid-State Elect. 136, 92–101 (2017).
Amin, R., Khurgin, J. B. & Sorger, V. J. Waveguide-based electro-absorption modulator performance: Comparative analysis. Opt. Express 26(12), 15445–15470 (2018).
Shin, J. H. & Dagli, N. Ultralow drive voltage substrate removed GaAs/AlGaAs electro-optic modulators at 1550 nm. IEEE J. Sel. Top. Quan. Elect. 19(6), 150–157 (2013).
Kim, H. & Gnauck, A. H. Chirp characteristics of dual-drive Mach-Zehnder modulator with a finite DC extinction ratio. IEEE Photonics Technol. Lett. 14(3), 298–300 (2002).
Fujiwara, H. Spectroscopic Ellipsometry: Principles and Applications (Wiley, Germany, 2007).
Liu, X. et al. Tuning of plasmons in transparent conductive oxides by carrier accumulation. ACS Photonics 5(4), 1493–1498 (2018).
Dionne, J. A., Diest, K., Sweatlock, L. A. & Atwater, H. A. PlasMOStor: A metal–oxide–Si field effect plasmonic modulator. Nano Lett. 9(2), 897–902 (2009).
Zhang, Y. et al. A compact and low loss Y-junction for submicron silicon waveguide. Opt. Express 21(1), 1310–1316 (2013).
Maiti, R. et al. A semi-empirical integrated microring cavity approach for 2D material optical index identification at 1.55 μm. Nanophotonics 8(3), 435–441 (2019).
Becker, J. S., Kim, E. & Gordon, R. G. Atomic layer deposition of insulating hafnium and zirconium nitrides. Chem. Mater. 16(18), 3497–3501 (2004).
Sorger, V. J. et al. Scaling vectors of attoJoule per bit modulators. J. Opt. 20(1), 014012 (2017).
Dalir, H. et al. Atto-Joule, high-speed, low-loss plasmonic modulator based on adiabatic coupled waveguides. Nanophotonics 7(5), 859–864 (2018).
Rovira, P. I. & Collins, R. W. Analysis of specular and textured SnO2: F films by high speed four-parameter Stokes vector spectroscopy. J. Appl. Phys. 85(4), 2015–2025 (1999).
Fujiwara, H., Kondo, M. & Matsuda, A. Interface-layer formation in microcrystalline Si: H growth on ZnO substrates studied by real-time spectroscopic ellipsometry and infrared spectroscopy. J. Appl. Phys. 93(5), 2400–2409 (2003).
Acknowledgements
V.S. acknowledges support from Air Force Office of Scientific Research (FA9550-17-1-0071, FA9550-17-1-0377). H.D. and R.C are supported by AFOSR SBIR (FA9550-19-C-0003).
Author information
Authors and Affiliations
Contributions
R.A. and V.S. initiated the project and conceived the experiments. R.A designed and fabricated the devices. R.A. and R.M. performed the measurements and data analysis. Y.G., C.S., and M.M. performed supporting experiments. R.A. and J.B.K. provided modelling and the theoretical analysis. E.H. and H.D. performed the RF measurements. R.A. and V.S. co-wrote the manuscript; J.K.B. and R.T.C. provided suggestions throughout the project. All authors commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Amin, R., Maiti, R., Gui, Y. et al. Heterogeneously integrated ITO plasmonic Mach–Zehnder interferometric modulator on SOI. Sci Rep 11, 1287 (2021). https://doi.org/10.1038/s41598-020-80381-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-80381-3
- Springer Nature Limited
This article is cited by
-
Electrically tunable space–time metasurfaces at optical frequencies
Nature Nanotechnology (2024)
-
Nanophotonic modulator based on Silicon-ITO heterojunction and slot waveguide with 2D-graphene sheet
Journal of Optics (2023)
-
ITO film stack engineering for low-loss silicon optical modulators
Scientific Reports (2022)
-
High-performance Mach–Zehnder modulator using tailored plasma dispersion effects in an ITO/graphene-based waveguide
Scientific Reports (2022)