Abstract
Filler particle functionalization with thiourethane oligomers has been shown to increase fracture toughness and decrease polymerization stress in dental composites, though the mechanism is poorly understood. The aim of this study was to systematically characterize the effect of the type of filler surface functionalization on the physicochemical properties of experimental resin composites containing fillers of different size and volume fraction. Barium glass fillers (1, 3 and 10 µm) were functionalized with 2 wt% thiourethane-silane (TU-Sil) synthesized de novo and characterized by thermogravimetric analysis. Fillers treated with 3-(Trimethoxysilyl)propyl methacrylate (MA-Sil) and with no surface treatment (No-Sil) served as controls. Fillers (50, 60 and 70 wt%) were incorporated into BisGMA-UDMA-TEGDMA (5:3:2) containing camphorquinone/ethyl-4-dimethylaminobenzoate (0.2/0.8 wt%) and 0.2 wt% di-tert-butyl hydroxytoluene. The functionalized particles were characterized by thermogravimetric analysis and a representative group was tagged with methacrylated rhodamine B and analyzed by confocal laser scanning microscopy. Polymerization kinetics were assessed by near-IR spectroscopy. Polymerization stress was tested in a cantilever system, and fracture toughness was assessed with single edge-notched beams. Fracture surfaces were characterized by SEM. Data were analyzed with ANOVA/Tukey's test (α = 0.05). The grafting of thiourethane oligomer onto the surface of the filler particles led to reductions in polymerization stress ranging between 41 and 54%, without affecting the viscosity of the composite. Fracture toughness increased on average by 35% for composites with the experimental fillers compared with the traditional methacrylate-silanized groups. SEM and confocal analyses demonstrate that the coverage of the filler surface was not homogeneous and varied with the size of the filler. The average silane layer for the 1 µm particle functionalized with the thiourethane was 206 nm, much thicker than reported for traditional silanes. In summary, this study systematically characterized the silane layer and established structure–property relationships for methacrylate and thiourethane silane-containing materials. The results demonstrate that significant stress reductions and fracture toughness increases are obtained by judiciously tailoring the organic–inorganic interface in dental composites.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Satisfactory mechanical properties and ability to mimic the dental substrate make resin composites the most popular choice for direct dental restorations. However, fifty percent of all resin-based restorations fail in less than 10 years, which inevitably causes unnecessary removal of additional sound tooth structure and pain and discomfort to the patient, in addition to costing millions of dollars annually1. The poor quality of the bond and seal at the restoration margin due to the stress generated during the polymerization reaction is implicated as one of the factors leading to the replacement of dental composite restorations2,3. In addition, fracture is also indicated as one of the primary reasons for the limited clinical lifespan of composite restorations1. Thus, efforts have been focused on modifying the composition of dental composite restoratives to address these shortcomings.
One of the latest developments in composite formulation has been the introduction of toughening, stress-reducing thiourethane oligomer additives. These are high molecular weight species, obtained via a facile click reaction chemistry that produces loosely crosslinked pre-networks bearing pendant thiol functionalities. When added to methacrylate monomer mixtures, the pendant thiols undergo chain-transfer reactions with the vinyl free radicals, which delays gelation/vitrification and leads to an overall improvement in conversion and a decrease in polymerization stress4,5,6. In general, these additives have been successful in reducing polymerization stress without jeopardizing elastic modulus and degree of conversion of the final polymer. However, a common effect of the addition of pre-polymerized oligomers to the composite’s resin matrix is an increase in the resin viscosity, which can potentially limit the amount of inorganic filler that can be incorporated, as well as compromise overall handling characteristics. One strategy to overcome this limitation is to graft thiourethane oligomers to the surface of filler particles. One recent publication using this approach demonstrated up to 35% reduction in polymerization stress for the resultant composite, accompanied by significantly improved mechanical properties7. This is especially promising because it may allow for more homogenous distribution of the thiourethane oligomer into the material, while minimizing the impact on the final viscosity of the composite7.
Despite the demonstrated benefits of the use of thiourethane oligomers as additives to the resin matrix5,6 or to the filler surface8, the mechanism for stress reduction and toughening effects is not completely understood. For instance, in separate studies, the net concentrations of thiourethanes added to the matrix, i.e., approximately 20%5,6, or to the filler surface, i.e. roughly 6%8, were markedly different, yet the levels of stress reduction and toughening were similar. Chain-transfer reactions alone cannot explain the similarities, since the concentration of pendant SH in the filler-based studies was relatively low. One hypothesis is that the formation of low Tg polymer brush structures on the surface of the filler are able to deform to compensate for the change in free volume inherent in the polymerization reaction9,10. This strategy targets the interface between filler and matrix, one area where stress concentration is more marked11.
To better understand the observed effects and provide a mechanism of action for the thiourethane additive requires a more systematic evaluation that takes into consideration the size and loading of fillers. Therefore, the aim of the present study was to assess the effect of particle size and loading, as well as the type of filler surface treatment, on polymerization stress development and fracture toughness of experimental resin composites. Polymerization kinetics and film thickness were also evaluated to ensure that producing a formulation with excellent shrinkage stress and toughness properties did not compromise the clinically relevant characteristics of curing efficiency and handling. The tested hypothesis was that the reduction in polymerization stress and increase in fracture toughness expected with the thiourethane-treated particles will be potentiated as the overall content of thiourethane increases.
Materials and methods
Thiourethane synthesis and functionalization of filler particles
All chemicals were sourced from Sigma-Aldrich (Milwaukee, WI, USA) and used without further purification, unless otherwise noted. The thiourethane (TU) oligomer was obtained by a click reaction in solution of pentaerythritol tetra-3-mercaptopropionate (PETMP), 1,3-bis(1-isocyanato-1-methylethyl)benzene (BDI), and 3-(triethoxysilyl)propyl isocyanate (2.5:1:1 mol, respectively), as previously described in detail6. The purified oligomers were characterized by mid-IR (by the disappearance of the isocyanate peak at 2270 cm-1) and NMR spectroscopy (appearance of resonance signals at 3.70 ppm).
Filler particles were functionalized with the TU silane described above or 3-(Trimethoxysilyl)propyl methacrylate, which were mixed at 2 wt% in an ethanol:millipore water solution (80:20 vol%) acidified by glacial acetic acid (pH ~ 4.5). This concentration was determined in a previous study in order to ensure full coverage of the particles12. Barium-alumino silicate particles (average size of 1.0 ± 0.2, 3.0 ± 1.0 and 10.0 ± 2.0 µm, Specialty Glass, Oldsmar, FL) were dispersed into the solution, agitated for 24 h and then filtered, washed in hexanes, and dried for 4 days at 37 °C. The selected sizes represent a range of the larger size of particles used in hybrid composites. Particles were characterized with thermogravimetric analysis (Discovery TGA55, TA Instruments—Waters LLC, New Castle, DE). Approximately 15 mg of filler was placed in a platinum pan and subjected to a heat ramp (50 to 850 °C, 10 °C/min). Percent mass loss was recorded as a function of temperature and all samples were tested in triplicate. Results were reported as the average total mass loss (%).
Experimental groups
Experimental resin composites containing 50, 60 or 70 wt% (26.8, 35.5, and 46.1 vol%, respectively) of the three different sizes of thiourethane-functionalized, methacrylate-silanized or untreated filler particles were produced by mixing the fillers into an organic resin matrix composed of 50 wt% BisGMA (Bisphenol A diglycidyl dimethacrylate), 30 wt% UDMA (urethane dimethacrylate), and 20 wt% TEGDMA (triethylene glycol dimethacrylate). The photoinitiator system was composed by 0.2 wt% camphorquinone, 0.8 wt% EDMAB (ethyl 4-dimethylaminobenzoate), and 0.2 wt% inhibitor BHT (2,6-di-tert-butyl-4-methylphenol). The twenty seven experimental groups are summarized in Fig. 1. All photocuring procedures were carried out using the DEMI Plus, with a 8 mm light guide (Kerr Dental, Orange, CA, USA) and 550 mW/cm2 radiant exitance as checked daily using a laser power meter (PM5200 Power Max, PM3 sensor, Molectron, Portland, OR, USA).
Polymerization stress
The stress of polymerization was assessed using a single cantilever system—Bioman, consisting of a specimen sandwiched between a fixed fused silica slide and a steel piston connected to a load cell13. The piston surface (5 mm in diameter) was treated with a metal primer (Z-Prime Plus, Bisco Inc., Schaumburg, IL, USA) and the fused silica slide surface was treated with silane (Ceramic Primer, 3 M ESPE, St. Paul, MN, USA). The 0.8-mm gap between the upper piston and the lower silica slide was filled with the composite paste, and the force generated by the shrinkage of the materials was followed in real-time during the photopolymerization (40 s, through the glass, at 550 mW/cm2). Data were recorded for 10 min and the final value was used for the calculation of contraction stress (n = 5).
Fracture toughness
The single-edge notch beam method was used to analyze the fracture toughness, according to ASTM Standard E399-9014. Resin composite bars of 5 mm × 2 mm × 25 mm were prepared in split steel molds having a razor blade insert, providing a 2.5 mm long notch at the center and through the thickness of the cured beam. The samples, sandwiched between two glass slides, were irradiated for 60 s on each side (4 overlapping exposures of 20 s each to cover the entire bar length) with the light guide in contact with the glass. After 24 h in dry storage, the fracture toughness test was carried out in three-point bending (20 mm span) in a universal testing machine (MTS Criterion, Eden Prairie, MN, US) at a cross-head speed of 0.5 mm/min (n = 8).
Fracture toughness was calculated according to the following Eq. (1):
where: P is load at fracture (N), L is the length, B is the thickness, W is the width, and a is the notch length (all dimensions in mm).
Kinetics of polymerization
Cylindrical samples (6 mm in diameter and 0.8 mm in thickness) were photoactivated through a glass slide (40 s, 1.5 cm of distance between the Demi light guide and glass slide surface, delivering 150 mW/cm2 to the surface of the specimen). The polymerization was followed in real time (180 s) using the methacrylate vinyl overtone peak at 6165 cm−1 by near-infrared spectroscopy (near-IR—Nicolet 6700, Thermo Electron Corporation, Waltham, MA, US) at 2 scans per spectrum with 4 cm−1 resolution (n = 3). The area of the peak was used to calculate degree of conversion (DC) as a function of time, and rate of polymerization15. The DC at the maximum rate of polymerization (DC at RPMAX) was used as a proxy for the onset of vitrification.
Handling/film thickness
Specimen preparation for testing the film thickness followed ISO 4049 guidelines, as described previously in the literature16. In summary, 0.1 g of the uncured composites was laminated between two Mylar sheets and statically loaded with 2 kg for 60 s. At the end of this time, the load was removed and the samples photocured for 60 s on each side. The thickness of the resin composite films was measured with a digital caliper at five different locations for each sample and the mean of the measurements was calculated as the final thickness (n = 5).
Space between the particles
The spacing between the filler particles for each experimental group was estimated with Eq. (2), making the broad assumptions of a spherical particulate of uniform size and homogenous distribution of the particles in the resin:
where: Dp is the average filler size (in µm) and Vp is the filler volume fraction .
Microscopy analyses
After testing, fracture toughness bars were cleaned in water in an ultrasonic bath for 10 min and mounted on aluminum stubs. Fracture surfaces were coated with approximately a 6 nm layer of gold/palladium (Leica EM ACE600 High Vacuum Sputter Coating). Imaging was carried out under high vacuum, accelerating voltage of 20 kV and working distance around 10 mm (JEOL, JSM-5600 LV, SEM, Japan).
The 1 µm-sized thiourethane functionalized filler particles were tagged with Methacryloxyethyl thiocarbamoyl rhodamine B (PolyFluor 570, Polysciences, Warrington, PA, USA) for confocal imaging. In summary, 2 g of filler were stirred with 0.1 wt% of the methacrylated rhodamine for 24 h in 5 ml of methylene chloride and catalytic amounts of triethylamine. The fillers were washed with acetone, ethanol and water and dried at 37 °C for 4 days. The tagged fillers were incorporated at 10 wt% in the resin matrix containing 0.01 wt% of fluorescein (Sigma-Aldrich, Milwaukee WI, USA). One drop of the material was dispensed in a FluoroDish (Fisher Scientific, Waltham, MA, USA), forming a sample 650 µm thick. The samples were imaged using an inverted confocal laser scanning microscope (ZEISS LSM 880, CarlZeiss US, White Plains, NY, USA) with a 63 × 1.4NA objective and the Fast Airyscan module17. Fast Airyscan increases acquisition speed and improves resolution. Increased speed is achieved by modulating the laser beam from round to oblong, which can scan four pixels at once. Improved resolution is achieved by capturing 16 images of a single field of view across a specialized detector. Each image contains positional information that enables the reconstruction of a single super-resolution image17. Samples were excited at 561 nm and 488 nm. Z-stacks were collected with a 0.2 µm step size over 11.25 µm. The micrographs were processed using the ZEN 3.1 Blue and Black editions software. Thiourethane coating thickness was measured in 2D images at the central Z-stack slice of the sample using the software Zeiss ZEN 3.1 (blue edition) (Carl Zeiss Microscopy GmbH). Three lines (horizontal, vertical, and diagonal) were drawn along the image of representative filler particles and the average of the six points is reported.
Statistical analysis
Data were statistically analyzed with three-way ANOVA and Tukey’s test for multiple comparisons (α = 0.05) after verifying normality and homoscedasticity (Anderson–Darling and Levene tests, respectively). First, a three-way ANOVA was conducted to determine possible interaction between the different factors (filler amount, size and surface treatment). Then, to facilitate data interpretation, each of the filler particle sizes was analyzed separately using two-way ANOVA and Tukey’s test (α = 0.05).
Results
The TGA results show that filler surface coverage ranged between 11.7 and 5.8% for thiourethane-functionalized particles and between 2.9 and 0.4% for methacrylate-silanized fillers (Fig. 2). Unsilanized particles showed a mass ranging between 0.1–0.8% during the experiment, likely attributed to water adsorption by these more hydrophilic particles18. In general, TU fillers had 4–5 times greater mass loss than MA particles, and the weight loss increased with the decrease in filler size. Inter-particle spacing distance was calculated assuming spherical particles and lack of agglomeration, and is presented along with the results for clarity. As expected, spacing increased with the increase in filler size at each filler volume (Fig. 2B).
Surface functionalization and particle size played a significant role in all experimental tests (p > 0.05). Filler particle percentage did not affect DC at RPMAX and final DC (p = 0.121 and 0.615, respectively). The three-factor interaction was significant, except for DC at RPMAX and final DC (p = 0.325 and 0.074, respectively). Data for each of the filler particle sizes was analyzed separately by two-way ANOVA and Tukey’s test (Table 1). Three-way ANOVA for all tested factors and interactions are also shown in Table 1.
TU-Sil groups showed significantly lower polymerization stress in comparison with No-Sil and MA-Sil groups: 41% for 3 and 10 µm filler size, and 54% for 1 µm-sized particles. Stress was not affected by the filler percentage within the same type of surface treatment, with only a few exceptions (No-Sil 1 µm; MA-Sil 1 µm; MA-Sil 10 µm, where the stress was higher with the 70% filler in comparison with the 50%). No-Sil and MA-Sil exhibited comparable results regardless of the particle size and filler volume (p > 0.05). The polymerization stress was significantly affected by all tested factors, but the interaction between surface treatment versus particle size, and particle size versus filler percentage were not significant (p > 0.05) (Table 1 and Fig. 3).
For fracture toughness, all three tested factors and interactions were statistically significant (p < 0.05) (Table 1). TU-Sil groups presented the highest values for 1 µm-sized filled composites, ranging between 1.63 and 1.56 MPa.m0.5 (Fig. 3). For 3 and 10 µm particles, there was no statistical difference between TU-Sil and MA-SIL groups (p > 0.05). No-Sil groups showed the lowest results regardless of the tested particle size. For all surface treatments and particles sizes, the filler percentage did not affect the fracture toughness results (p > 0.05).
TU-Sil showed the highest values of final DC (ranging between 71.5 and 68.3%) and MA-Sil particles the lowest ones (ranging between 63.7 and 53.8%) for filler particles of 1 and 3 µm. For 10 µm particles, MA-Sil showed the highest final DC values (ranging bewteen 70.8 and 72.2%) and TU-Sil the lowest ones (ranging between 59.2 and 61.6%). In terms of kinetics of polymerization, in general, No-Sil groups had higher RPMAX and DC at RPMAX, regardless of the filler particle size (Fig. 4 and Table 2). TU-Sil groups showed similar or lower results, and were comparable to MA-Sil groups.
Regarding film thickness, all studied factors and interactions were statistically significant (p < 0.05, Table 1 and Fig. 2C). 70%-filled groups produced the highest film thickness regardless of the surface treatment and particle size. Film thickness was highest at 1 µm and 3 µm for the composites with 70% fillers with no treatment. No difference was observed between 50 and 60%-filled groups.
The analysis of fractured surfaces from fracture toughness bars showed marked differences in terms of filler-organic matrix interface among the three surface treatments (Fig. 5). NO-Sil groups showed bare particles clearly separated from the organic matrix, most easily visualized for the largest particle size. MA-Sil typically showed particles entirely encapsulated within resin matrix, and TU-Sil particles presented a mixed aspect (bare and covered particles), with the exposure of filler surface most obvious for the two larger filler sizes.
The confocal fluorescent images for the TU-containing groups are presented in Fig. 6. The methacrylate silane groups were not imaged with this technique because the coating’s minimal thickness fell below the resolution of the confocal microscope. In Fig. 6, individual particles are shown in three different perspectives: 2D, 3D top view and x–y, x–z, and y–z orthogonal projections of a confocal section. The projection images show large regions with no coverage, especially for the 10 µm-sized filler particles. The average coating thickness of the filler particles were measured in the 2D images using the histogram feature on Zen Blue (Zeiss) as an average of 6 different regions. The thickness for the 1, 3 and 10 µm particles was 649 ± 107 nm, 1226 ± 334 nm, and 1885 ± 981 nm, respectively.
Discussion
The incorporation of pre-polymerized additives, including thiourethane oligomers, to the formulation of resin composites has shown desirable outcomes, such as the reduction in volumetric shrinkage19 and shrinkage stress4,19, and increase in fracture toughness4,5,6. However, this strategy usually leads to a non-negligible increase in viscosity, which prevents the incorporation of higher percentages of inorganic fillers6, and negatively affects handling characteristics. This ultimately limits the amount of pre-polymers that can be added before other properties start to deteriorate (6—30% TU in cements). For this reason, the functionalization of the inorganic filler surface with oligomeric species has been proposed, and, at least for thiourethanes, has shown similar reduction in polymerization stress and improvement in mechanical properties without compromising the viscosity of the composite paste7,8. In this study, TU functionalized filler particle characteristics were studied in a systematic fashion to gain insight into the mechanisms leading to the reinforcing and stress-reducing outcomes observed with thiourethane oligomers.
The same standard functionalization method was used for the thiourethane and the conventional methacrylate silane (MA-Sil). The grafting to the filler surface was accomplished in a slightly acidic aqueous alcohol solution (pH ≅ 4.5) to hydrolyze the alkoxy groups, forming reactive silanols (≡Si–OH), which further react with themselves by a condensation process to form oligomeric siloxanes (–Si–O–Si–bonds). At the same time, the growing silane networks link to the inorganic substrate through hydrogen bonds with the hydroxyl groups present on the particle surface20,21,22. The filler surface functionalization efficiency was assessed by thermogravimetric analysis (Fig. 2A). For the particles functionalized with the MA-Sil, all organics were burned off at 500 °C and no additional mass was lost at higher temperatures. For TU-Sil fillers, the maximum mass loss was observed closer to 600 °C, which was also expected based on the much greater molecular weight of the oligomer compared to the small-molecule methacrylate silane. The untreated particles (NO-Sil), used as received from the manufacturer, also showed mass loss at a similar temperature, which could be due to impurities from the manufacturing process. For all surface treatments, the mass loss increased with a decrease in the average particle size23, which was expected since at the same mass, 1 µm-sized particles have ten times more free surface area available to be functionalized than 10 µm-sized particles (Table 3). It is noteworthy that the mass loss as a function of surface area was different for each surface treatment. For the NO-Sil and MA-Sil groups, 1 µm-sized particles showed ten times more weight loss than 10 µm-sized particles: 1.61 and 0.22% for 1 µm and 10 µm-sized particles, respectively (NO-Sil) and 2.91 and 0.39% for 1 µm and 10 µm-sized particles, respectively (MA-Sil). For the TU-Sil groups, the mass loss did not linearly scale with the particle size (weight loss = 11.73% and 5.82% for 1 µm and 10 µm-sized particles, respectively). This difference can be at least partially explained by differences in molecular weight (~ 250 g/mol for the MA-Sil and 5 kDa—or roughly 5,000 g/mol—for TU-Sil)6, as well as differential thickness of the coating. The monotonic increase in weight loss with decreasing filler size is consistent with the formation of a monolayer for the methacrylate silanes. In contrast, it is possible that the thiourethane oligomer is crosslinked onto the surface, which will be further discussed later. It is also possible that the silanization process with the thiourethane oligomer is not as efficient, and that results in non-uniform functionalization, as shown in the imaging results.
SEM micrographs (Fig. 5B) were used to characterize the particle–matrix interface. While the MA-Sil particles are entirely coated with organic matrix, thiourethane particles seem to be more heterogeneously coated, with some naked regions, and others showing better interaction with the matrix (Fig. 5C). This pattern is also identified in the confocal images which show uneven distribution of the thiourethane oligomer along the filler particle surface (Fig. 7), alternating areas with a layer of 649–1885 nm in thickness depending on the filler size and other naked regions (Table 3 and Fig. 6). The coating on the larger filler particles was much more disperse, with extensive areas of the filler remaining uncovered. The bulky thiourethane oligomer is likely tethered onto the filler surface at multiple locations, creating steric constraints for additional chain grafting, ultimately limiting the overall graft density24. It is important to point out that the starting concentration of TU oligomer during the filler functionalization was the same for all filler sizes, and the mass of filler used here was the same regardless of the size. This results in much greater overall surface area and smaller inter-particle distancing in the smaller filler particles. This likely explains why the thickness of the silane layer was similar for the 1 and 3 µm particles, at around 649 and 1226 nm, respectively, but much thicker for the 10 µm particles (1885 nm). In summary, for the larger particles, the greater inter-particle spacing and smaller overall surface area, likely combined to increase the coating thickness. The surface area vs. particle size relationship also explains the mass loss data from the TGA, which shows greater mass loss with the smaller particles, again due to the greater filler surface area per volume of material afforded by smaller particles. In addition to the mechanisms that will be discussed in more detail later, it is possible that the uncoated areas act as defect sites, which are known to lead to lower stress development25.
During polymerization, the monofunctional methacrylate silane co-polymerizes with the vinyl-containing matrix, and establishes a short and rigid bond with the filler surface20, which contributes to stress generation. In contrast, the high molecular weight thiourethane silane establishes multiple covalent interactions with the polymerizing organic matrix via the pendant thiols. The bonds formed are flexible thiocarbamate bonds which can serve as sites for relaxation of the overall polymerization stress26. In the specific case of the thiuorethane oligomers studied here, some stress relaxation during polymerization is also afforded by the delayed gelation vitrification5,6,7, but more recent studies have also pointed to the possibility of stress relaxation via dynamic bond adaptation behavior in the glassy state27,28,29,30. The dynamic relaxation behavior of thiourethanes is currently being investigated and will be reported separately. Preliminary studies using time–temperature superposition experiments have already demonstrated faster relaxation times for fillers treated with TU-Sil31. Different from the strategy where the stress-relieving molecules is randomly distributed in the matrix4,5,6, in composites with TU functionalized fillers, the stress relieving molecules are localized at the filler-matrix interface, a region of stress concentration32. This may account for the significant reduction in stress transfer between the two constituent phases of the resin composites25, even at a much lower overall TU concentration than that present when TU is added directly to the resin matrix. Additionally, the thiourethane likely forms thick and highly dense polymer structures on the surface of the particle, which may also contribute to dissipate part of the generated stress33,34 and to increase plastic deformation during stress development that help accommodate changes in free volume34,35. The multifunctional nature of thiourethanes also leads to differences in crosslinking in the siloxane layer and enhanced interface adhesion25. This may compensate for the uneven coverage of the filler particle by the thiourethane silane mentioned earlier, and helps explain why mechanical properties are not compromised, in spite of the presence of naked regions on the filler particle surface. Finally, the stress development and the mechanical properties of the resin composites are also dependent on the degree of agglomeration of the filler particles36. Systems with greater filler dispersion show improved storage modulus, tensile strength, toughness and lower polymerization stress due to the enhanced matrix-filler interaction and interfacial adhesion25. When polymer chains are grafted onto the particle surface there is steric repulsion, which minimizes their tendency to agglomerate due to the van der Walls attraction and, ultimately, promotes a more uniform dispersion of the particles.
The stress development can also be correlated with the kinetics of polymerization. The fact that with NO-Sil and MA-Sil composites had similar stress behavior was unexpected since, in theory, in the absence of bonding between the particles and the organic matrix, the filler particles should effectively behave as voids, leading to stress relief37. However, in general NO-Sil composites showed markedly faster polymerization reaction, which may have led to earlier development of diffusional limitations and a rise in stiffness, minimizing the opportunity for stress relaxation. The higher RPMAX and DC at RPMAX found in NO-Sil formulations may have resulted from the increased system mobility imposed by the absence of functional silanes at the interface38. As expected, the addition of TU-Sil led to significant reduction in polymerization stress, ranging between 41 and 54% in comparison with the MA-Sil groups. The reduction in stress is explained by chain-transfer reactions of the thiols with the vinyl groups, which delays the point in conversion at which the stiffness of the networks begins to significantly increase, and past which any increase in conversion results in disproportionately higher stress. In general, the addition of TU-Sil particles into the resin composite formulations decreased the RPMAX, as well as the conversion registered at RPMAX, in agreement with previous studies4, indicating at least some effect in delayed network formation (Fig. 4). The somewhat slower polymerization reaction did not compromise the final DC; on the contrary, TU-Sil formulations showed the highest values for 1 and 3 µm-sized filler particles. For the 10 µm-sized particles, conversion was similar to the methacrylate controls. This may be due to the lower concentrations of thiourethane in this composition (Table 4), which may have been insufficient to affect the polymerization reaction kinetics. Chain-transfer reactions are also responsible for more homogeneous network formation, which decreases the development of internal stress, especially immediately after the diffusion limitation occurs5,39,40. It is also possible that the simple presence of the low Tg thiourethane on the surface of the filler particle may play a similar role in stress relief, acting as a ductile zone for plastic deformation between the filler and the organic matrix, which ultimately yields stress absorption at the interface and toughening. Interestingly, it seems that the localization of thiourethanes directly at the surface of the filler particle significantly decreases the overall concentration of thiourethane needed to produce significant reduction in polymerization stress, compared to what is needed when TU is added directly into the matrix4,5,6. Therefore, several mechanisms may be operating at the filler-matrix interface, as mentioned throughout the discussion, and summarized in Fig. 7. It is important to reiterate, however, that the stress reduction is not gained at the expense of reduced conversion.
A potential concern over the uneven coverage of the filler particles with the TU might be the susceptibility of the particles to being dislodged under load, consequently, compromising the mechanical properties. In this study, the fracture toughness results showed the opposite effect for the 1 µm TU-Sil, with significant enhancement for all the three groups containing TU-treated particles (1.60 ± 0.03 MPa•m1/2) in comparison to MA-Sil groups (1.19 ± 0.08 MPa•m1/2) (Fig. 3). This 34% increase in fracture toughness is attributed to the flexible thiocarbamate covalent bonds4, and may also be due to lower levels of internal stress accumulation41,42. For 3 and 10 µm-sized fillers, there were no statistical differences between TU-Sil and MA-Sil, which indicates that the percentage of the thiourethane incorporated into the mixtures (Table 5) was not sufficient to significantly improve the fracture toughness. In fact, the confocal images demonstrate that the TU-Sil layer was much more uneven than for the 1 µm filler, which correlates with the data for mass loss shown in Table 3, as already mentioned. The SEM micrographs of the fracture surfaces containing TU-Sil particles showed chunks of organic matrix covering some regions of the particle’s surface, which may indicate that the fracture sometimes propagated through the organic matrix, but also along the resin-filler interface in these systems. In contrast, in the MA-Sil systems the fractured surfaces were typically covered by a thin and uniform layer of resin, which indicates that the fracture propagated through resin matrix near the fillers. This adds evidence to the fact that, though not being entirely coated by the silane, the interaction of the inorganic fillers to the organic resin in thiourethane-containing systems still allows for lower stress concentration at the filler-matrix interface. In addition, the uncoated areas on the TU-Sil filler particles might provide an energy releasing path around the particles, contributing to the enhanced toughness37. Groups containing NO-Sil particles showed, as expected, the lowest fracture toughness, due to the absence of interfacial bonding between the filler particles and the organic matrix. The mass percentage of filler particles incorporated into the formulation did not impact the mechanical resistance, which is in agreement with results reported previously in the literature for composites with different levels of 1 µm-sized barium-alumina borosilicate particles43. This previous study has shown that the flexural strength decreases and the flexural modulus increases slightly as the filler particle load increases from 40 to 60 wt% and, above 60 wt%, there is a gradual increase in both flexural strength and modulus. The results were correlated with particle size distribution, particle–matrix adhesion strength, and arrangement of the filler particles into the organic matrix43. In highly loaded systems (above 60 wt%), there was a tendency for a percolated network particle structure to be formed, which are aggregates of filler associated with mechanical reinforcement43. However, it is important to highlight that there is a threshold for increase in filler particle content and increase in mechanical performance, above which the addition of higher amounts of filler leads to decreased particle–matrix adhesion strength, possibly due to the formation of agglomerates. This threshold varies according to the filler particle system. It is possible to assume that, at least for the larger filler sizes (3 and 10 µm), the load range used in this study was insufficient to result in significant differences in fracture toughness. For the 1 µm filler particles, the fracture toughness results agree with our previous work demonstrating significant increase in values when comparing methacrylate vs thiourethane silanes7.
One thing to note is that, even though the filler loading followed standardized mass ratios (50, 60, and 70 wt%), for the TU-Sil groups, a much higher percentage of the filler weight corresponded to the mass of the silane, compared to the methacrylate groups. As a consequence, the actual inorganic filler loading varied significantly among the groups (Table 5). In general, TU-Sil composites contain 10 wt% less filler than MA-Sil formulations with 1 µm-sized particles, 6.5 wt% less with 3 µm-sized particles, and 5.4 wt% less with 10 µm-sized particles. This translated into thinner film thickness for groups containing TU-Sil particles (Fig. 2C). In addition, the film thickness is also affected by the distance between particles. For smaller filler sizes, the particles become more compacted (closer to each other), which also leads to an increase in filler content (Fig. 2B). As expected, the smaller particles led to greater viscosity as more of the resin matrix is influenced by contact with the fillers, and the smaller inter-particle spacing leads to more filler-filler interactions, both of which result in thickening of the paste.
An additional potential advantage of the thiourethane coating is its hydrophobicity. As it is well known, the presence of ester bonds makes the methacrylate silane prone to hydrolytic degradation. The siloxane layer degradation, caused by the vulnerability of the oxane bonds to hydrolysis due to its significant ionic character, increases the concentration of hydroxyl ions44, which leads to an autocatalytic reaction. As result of this reaction, there is a weakening of the filler-matrix bonding, leaching of chemical compounds, generation of micro-cracks at the interface, particle debonding, and, ultimately compromised mechanical properties45. Even though it was not the main goal of the present study to investigate the hydrolytic stability of the interfaces, the use of the thiourethanes (a multifunctional, hydrophobic, crosslinked, high molecular weight oligomer) as a particle coating can be envisioned to improve the durability and the hydrolytic stability of the interfacial siloxane bond. This may ultimately improve the durability of the filler-matrix bonding.
Conclusion
In general, the functionalization of the inorganic filler particles surface with the prepolymerized thiourethane significantly reduced polymerization stress generation without compromising the viscosity and film thickness of the materials. In addition, a significant enhancement in fracture toughness was observed in thiourethane formulations filled with 1 µm-sized particles. The stress reducing/relieving and toughening effects of the polymeric network, however, have been confirmed with the use of the thiourethanes in this filler-functionalization strategy, even though several concomitant mechanisms are likely at play.
References
Gordan, V. V. et al. Repair or replacement of restorations: A prospective cohort study by dentists in The National Dental Practice-Based Research Network. J. Am. Dent. Assoc. 146, 895–903 (2015).
Kopperud, S. E., Tveit, A. B., Gaarden, T., Sandvik, L. & Espelid, I. Longevity of posterior dental restorations and reasons for failure. Eur. J. Oral Sci. 120, 539–548 (2012).
Ferracane, J. L. & Hilton, T. J. Polymerization stress—Is it clinically meaningful?. Dent. Mater. 32, 1–10 (2016).
Bacchi, A. & Pfeifer, C. S. Rheological and mechanical properties and interfacial stress development of composite cements modified with thio-urethane oligomers. Dent. Mater. 32, 978–986 (2016).
Bacchi, A., Consani, R. L., Martim, G. C. & Pfeifer, C. S. Thio-urethane oligomers improve the properties of light-cured resin cements. Dent. Mater. 31, 565–574 (2015).
Bacchi, A., Dobson, A., Ferracane, J. L., Consani, R. & Pfeifer, C. S. Thio-urethanes improve properties of dual-cured composite cements. J. Dent. Res. 93, 1320–1325 (2014).
Fugolin, A. P., Sundfeld, D., Ferracane, J. L. & Pfeifer, C. S. Toughening of dental composites with thiourethane-modified filler interfaces. Sci. Rep. 9, 2286 (2019).
Faria-e-Silva, A. L. & Pfeifer, C. S. Impact of thio-urethane additive and filler type on light-transmission and depth of polymerization of dental composites. Dent. Mater. 33, 1274–1285 (2017).
Fronza, B. M. et al. Nanogel-based filler-matrix interphase for polymerization stress reduction. J. Dent. Res. 98, 779–785 (2019).
Xiong, D., Deng, Y., Wang, N. & Yang, Y. Influence of surface PMPC brushes on tribological and biocompatibility properties of UHMWPE. Appl. Surf. Sci. 298, 56–61 (2014).
Metin, D., Tihminlioǧlu, F., Balköse, D. & Ülkü, S. The effect of interfacial interactions on the mechanical properties of polypropylene/natural zeolite composites. Compos. A Appl. Sci. Manuf. 35, 23–32 (2004).
Goulart, M. et al. Thiourethane filler functionalization for dental resin composites: Concentration-dependent effects on toughening, stress reduction and depth of cure. Mater. Sci. Eng. C. 1, 118 (2021).
Watts, D. C. & Satterthwaite, J. D. Axial shrinkage-stress depends upon both C-factor and composite mass. Dent. Mater. 24, 1–8 (2008).
Standard Test Method for Plane-Strain Fracture Toughness of Metallic Materials. West Conshohocken, PA: ASTM International; 1997.
Stansbury, J. W. & Dickens, S. H. Determination of double bond conversion in dental resins by near infrared spectroscopy. Dent. Mater. 17, 71–79 (2001).
Da Costa, J., McPharlin, R., Hilton, T. & Ferracane, J. Effect of heat on the flow of commercial composites. Am. J. Dent. 22, 92–96 (2009).
Huff, J. The Fast mode for ZEISS LSM 880 with Airyscan: High-speed confocal imaging with super-resolution and improved signal-to-noise ratio. Nat. Methods 13, 1–2 (2016).
Krzemińska, S., Greszta, A., Różański, A., Safandowska, M. & Okrasa, M. Effects of heat exposure on the properties and structure of aerogels for protective clothing applications. Microporous Mesoporous Mater. 285, 43–55 (2019).
Moraes, R. R. et al. Control of polymerization shrinkage and stress in nanogel-modified monomer and composite materials. Dent. Mater. 27, 509–519 (2011).
Matinlinna, J. P., Lassila, L. V. J. & Vallittu, P. K. The effect of five silane coupling agents on the bond strength of a luting cement to a silica-coated titanium. Dent. Mater. 23, 1173–1180 (2007).
Kango, S. et al. Surface modification of inorganic nanoparticles for development of organic-inorganic nanocomposites—A review. Prog. Polym. Sci. 38, 1232–1261 (2013).
Hermanson, G. T. Silane Coupling Agents (Academic Press, 2013).
Karabela, M. M. & Sideridou, I. D. Synthesis and study of properties of dental resin composites with different nanosilica particles size. Dent. Mater. 27, 825–835 (2011).
Mittal, V. Polymer Brushes: Substrates, Technologies, and Properties (CRC Press, 2012).
Amdjadi, P., Ghasemi, A., Najafi, F. & Nojehdehian, H. Pivotal role of filler/matrix interface in dental composites: Review. Biomed. Res. (India). 28, 1054–1065 (2017).
Hoyle, C. E. & Bowman, C. N. Thiol-ene click chemistry. Angewandte Chem. Int. Ed. 49, 1540–1573 (2010).
Gamardella, F., De la Flor, S., Ramis, X. & Serra, A. Recyclable poly (thiourethane) vitrimers with high Tg. Influence of the isocyanate structure. Reactive Funct. Polym. 151, 104574 (2020).
Gamardella, F., Guerrero, F., De la Flor, S., Ramis, X. & Serra, A. A new class of vitrimers based on aliphatic poly (thiourethane) networks with shape memory and permanent shape reconfiguration. Eur. Polymer J. 122, 109361 (2020).
Li, L., Chen, X. & Torkelson, J. M. Reprocessable polymer networks via thiourethane dynamic chemistry: Recovery of cross-link density after recycling and proof-of-principle solvolysis leading to monomer recovery. Macromolecules 52, 8207–8216 (2019).
Liu, Q. et al. Design and development of self-repairable and recyclable crosslinked poly (thiourethane-urethane) via enhanced aliphatic disulfide chemistry. J. Polym. Sci. 58, 1092–1104 (2020).
Lewis, S., Fugolin, A., Ferracane, J. & Pfeifer, C. Stress relaxation behavior in glassy methacrylate networks containing thiourethane-based oligomers. Dent. Mater. 35, e29–e30 (2019).
Feng, L., Suh, B. I. & Shortall, A. C. Formation of gaps at the filler–resin interface induced by polymerization contraction stress: Gaps at the interface. Dent. Mater. 26, 719–729 (2010).
Brittain, W. J. & Minko, S. A structural definition of polymer brushes. J. Polym. Sci., Part A: Polym. Chem. 45, 3505–3512 (2007).
Ochsmann, J. W. et al. Stress-structure correlation in ps-pmma mixed polymer brushes. Macromolecules 45, 3129–3136 (2012).
Ferracane, J. L., Ferracane, L. L. & Braga, R. R. Effect of admixed high-density polyethylene (HDPE) spheres on contraction stress and properties of experimental composites. J. Biomed. Mater. Res. B Appl. Biomater. 66B, 318–323 (2003).
Ranade, R. A., Ding, J., Wunder, S. L. & Baran, G. R. UHMWPE as interface toughening agent in glass particle filled composites. Compos. A Appl. Sci. Manuf. 37, 2017–2028 (2006).
Ferracane, J. L., Berge, H. X. & Condon, J. R. In vitro aging of dental composites in water—Effect of degree of conversion, filler volume, and filler/matrix coupling. J. Biomed. Mater. Res. 42, 465–472 (1998).
Halvorson, R. H., Erickson, R. L. & Davidson, C. L. The effect of filler and silane content on conversion of resin-based composite. Dent. Mater. 19, 327–333 (2003).
Lu, H., Carioscia, J. A., Stansbury, J. W. & Bowman, C. N. Investigations of step-growth thiol-ene polymerizations for novel dental restoratives. Dent. Mater. 21, 1129–1136 (2005).
Senyurt, A. F., Hoyle, C. E., Wei, H., Piland, S. G. & Gould, T. E. Thermal and mechanical properties of cross-linked photopolymers based on multifunctional thiol-urethane ene monomers. Macromolecules 40, 3174–3182 (2007).
Greisel, M. et al. Influence of residual thermal stress in carbon fiber-reinforced thermoplastic composites on interfacial fracture toughness evaluated by cyclic single-fiber push-out tests. Compos. A Appl. Sci. Manuf. 66, 117–127 (2014).
Park, H. Y., Kloxin, C. J., Fordney, M. F. & Bowman, C. N. Stress relaxation of trithiocarbonate-dimethacrylate-based dental composites. Dent. Mater. 28, 888–893 (2012).
Rodríguez, H. A., Kriven, W. M. & Casanova, H. Development of mechanical properties in dental resin composite: Effect of filler size and filler aggregation state. Mater. Sci. Eng., C 101, 274–282 (2019).
Antonucci, J. M., Dickens, S. H., Fowler, B. O., Xu, H. H. K. & McDonough, W. G. Chemistry of silanes: Interfaces in dental polymers and composites. J. Res. Natl. Inst. Stand Technol. 110, 541–558 (2005).
Karabela, M. M. & Sideridou, I. D. Effect of the structure of silane coupling agent on sorption characteristics of solvents by dental resin-nanocomposites. Dent. Mater. 24, 1631–1639 (2008).
Acknowledgements
This study was funded by NIH-NIDCR (R01-DE026113 and U01-DE023756 to CSP and JLF, K02-DE025280 to CSP), CAPES-Brazil (Coordenação de Apoio a Pessoal de Ensino Superior, finance code 001 to ARC) and FAPESP-Brazil (Fundação de Amparo à Pesquisa do Estado de São Paulo, grants #2016/03576-9 to LCS).
Author information
Authors and Affiliations
Contributions
A.F.: investigation, data curation, forma analysis, writing original draft; A.R.C.: investigation, writing original draft; L.C.-S., L.C.C. and S.H.L.: investigation; J.L.F.: conceptualization, writing—review and editing; C.S.P.: conceptualization, writing—review and editing, supervision, administration and funding acquisition.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Fugolin, A.P.P., Costa, A.R., Correr-Sobrinho, L. et al. Toughening and polymerization stress control in composites using thiourethane-treated fillers. Sci Rep 11, 7638 (2021). https://doi.org/10.1038/s41598-021-87151-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-87151-9
- Springer Nature Limited
We’re sorry, something doesn't seem to be working properly.
Please try refreshing the page. If that doesn't work, please contact support so we can address the problem.