Abstract
Steering magnetism by electric fields upon interfacing ferromagnetic (FM) and ferroelectric (FE) materials to achieve an emergent multiferroic response bears a great potential for nano-scale devices with novel functionalities. FM/FE heterostructures allow, for instance, the electrical manipulation of magnetic anisotropy via interfacial magnetoelectric (ME) couplings. A charge-mediated ME effect is believed to be generally weak and active in only a few angstroms. Here we present an experimental evidence uncovering a new magnon-driven, strong ME effect acting on the nanometer range. For Co92Zr8 (20 nm) film deposited on ferroelectric PMN-PT we show via ferromagnetic resonance (FMR) that this type of linear ME allows for electrical control of simultaneously the magnetization precession and its damping, both of which are key elements for magnetic switching and spintronics. The experiments unravel further an electric-field-induced negative magnetic permeability effect.
Similar content being viewed by others
Introduction
Magnetic-based information processing as realized for instance in memory devices and sensors relies on switching the magnetization (M) between equilibrium states. Such a process evolves in general through a damped precession. The magnetic precession is directly governed by the effective magnetic field Heff whereas the precessional damping is dependent on α, the dimensionless Gilbert damping parameter1. Engineering both, Heff and α is thus of a key importance for a reliable and swift magnetic switching2,3. In a coupled FE/FM system Heff is augmented by an additional interfacial ME interaction3,4,5,6,7,8,9,10,11 and hence becomes dependent on the ferroelectric polarization that is inherently controllable by electrical means. This opens the door for the electric control of M, as shown in recent studies on voltage-controlled magnetic anisotropy via FMR excitation in appropriately synthesized FM/FE heterostructures12,13,14,15. The damping is a nonlinear spin relaxation of precession due to the combined effects of intrinsic impurity scattering16,17 and spin-orbit interactions18,19, as well as extrinsic nonlocal spin pumping20,21,22 and is vital for achieving high-speed magnetic functionality. It is however challenging to manipulate damping, particularly by electrical means, even though possible magnetic control of damping has been observed in some left-handed metamaterials23,24,25 close to FMR frequency26,27,28.
A direct gate-voltage control of magnetic permeability is still an open question despite its key role in ME devices and metamaterials with negative refraction index. A way to achieve this is offered by a recently predicted mechanism of ME coupling for FM/FE29; according to which in FM a spiral magnetic ordering builds up at FM/FE interface with a nanometer range determined by spin diffusion length. This non-collinear ordering is coupled to the FE polarization (a brief summary of mathematical details is included in the supplementary materials to this paper). Since spiral order entails a spin orbital coupling30 we expect thus a gate-voltage dependent influence on damping (via coupling to polarization). Indeed, we report here FMR experiments evidencing that both the effective magnetic field and Gilbert precessional damping are directly controllable in Co92Zr8(CoZr)/Pb(Mg1/3Nb2/3)0.7Ti0.3O3(PMN-PT) heterostructure by means of a gate voltage. Furthermore, we find that magnetic excitations pumped by the external electric field by virtue of the magnetoelectric may result in electric field-induced negative imaginary part of magnetic susceptibility (permeability) at room temperature.
Results
Several ME coupling mechanisms in composite FM/FE heterostructures were envisaged, in particular ME-effect driven by spin-polarized screening, strain, or/and exchange bias3,4,5,6,7,11,31. A detailed analysis show, however, that the latter two indirect ME interactions: the interfacial strain-mediated and exchange-mediated couplings, contribute with an additional magnetic-anisotropy type term to the FM free energy F, i.e., they alter only the effective magnetic field by Heff = −δF/δM (which governs directly the precessional motion) but they have no direct influence on the damping parameter α of the magnetization evolution M(t). This is readily inferred from the phenomenological Landau-Lifshitz-Gilbert (LLG) equation (here γ is the gyromagnetic ratio and Ms is the saturation magnetization). This also applies to screening of FE polarization via interfacial charge accumulation. What about spin-driven ME coupling? As shown recently, when a FM is brought in contact with a FE a non-collinear spin density s(r, t) develops in the FM interface on the scale of the spin diffusion length λm in response to the adjacent FE polarization29. Ensuring electric neutrality one finds: (i) A linear ME coupling and thus an effective gate-controlled magnetic field. (ii) An induced spin (orbital) torque resulting in an electrically tunable effective magnetic damping. Furthermore, considering that with e and being the electron charge and the surface electrostatic screening charge density respectively, the induced spin density s(r, t) is linearly determined by the applied electric field E32,33,34,35,36 and the dielectric permittivity ε (in the unit of the vacuum permittivity ε0) at the FM/FE interface which can be significantly enhanced up to several orders (compared with ε ~ 1 at the interface of the bulk FM metal). On the other hand, due to the large spin-diffusion length in FM metals37, ME effects may have substantial influence on FM films with thickness over tens of nanometers. Having these properties in mind we have chosen polycrystalline Co92Zr8 (20 nm) layer with an intrinsic damping α = 0.008 and Pb(Mg1/3Nb2/3)0.7Ti0.3O3 with ε ≈ 4–6 × 103 as our candidates for FM and FE subsystem, respectively. It should be noted that similar results are observed for CoZr film with a thickness equal to 10 nm.
A sketch of the sample and the measurement configuration is shown in Fig. 1a–c. The CoZr thin films were prepared on one-side-polish (011)-oriented PMN-PT single-crystal substrates at room temperature by radio frequency magnetron sputtering. A vibrating sample magnetometer (VSM) measurements demonstrated an electric field control of magnetic hysteresis loops with an in-plane uniaxial magnetic anisotropy (cf. Fig. s1 in the Supplementary). In Fig. 1d, the dynamic magnetoelectric response was investigated by using a more direct and sensitive FMR spectroscopy38 at room temperature under different gate voltages. In the bias range 0–14 kV/cm, resonance spectra with dispersion structure were observed. The form of the FMR line shape, however, differs quantitatively in low and high external electric fields which becomes increasingly obvious after integrating the signals over the applied static magnetic field (cf. Fig. 1e). A clear change in the sign of the integrated Lorentzian lineshape is observed by comparing the profiles in the two limit cases with applied electric field 0 kV/cm and 14 kV/cm. This is insofar important as the microwave power, P(H), absorbed by the CoZr film in our experimental geometry reads P (H) = ωℑχz |h|2 /2 with h being the amplitude of the applied rf driving field with frequency ω = 8.969 GHz and ℑχz is the imaginary part of dynamic magnetic susceptibility. Thus, the experiment unravels the emergence of positive-to-negative transition of ℑχz in natural FM metal by applying external electric field for coupled FM/FE structures. We note, that negative ℑχz does not mean that the system is dissipating negative energy, since in the presence of the external electric field (and the magnetoelectric coupling) the energy is not conserved. It is rather so, that excitations triggered by the electric field are transferred to the spin system via the magnetoelectric coupling and this shows up in the FMR, effectively as negative ℑχz. This novel observation we expect to have important implications for future applications of composite FM/FE systems to optical applications.
For an insight into the electrical tuning of magnetic dynamics, we study the resonance spectra based on the phenomenological LLG equation, which has been widely used for interpreting and predicting vast experimental results of magnetic structures (See Ref. 39 and the supplementary). We find
where Hr is the resonance field, Δ characterizes the half-maximum linewidth, connected to the relaxation processes by . In principle, the integrated absorption lineshape is almost perfectly Lorentzian as Δ Hr,40 which is fully fulfilled by our absorption experiments. The same measurement performed with a CoZr thin film of equivalent thickness on top of Si substrate also possesses a perfectly symmetric resonance lineshape in all applied bias ranges (the inset in Fig. 2b). Whereas, as for small damping and if the magnetization M being parallel to the externally applied magnetic field, a non-zero phase shift would be expected and the line shape of FMR spectrum does not exclusively correspond to imaginary magnetic susceptibility, as follows from LLG equation, but represents a mixture of imaginary and the real part of the susceptibility41. Given the asymmetric nature of the real part of the dynamic susceptibility as inferred from LLG, we conclude that the asymmetric profile at moderate electric fields in Fig. 1e is a mixture effect. Solid lines in Fig. 1e show fits with an asymmetric Lorentzian function. The derived values of the resonance field Hr and effective inhomogeneous line broadening, Δeff = Δcos ϕ with ϕ being the mixture phase between the real and imaginary part of the susceptibility, are shown in Fig. 2a; the electric-field-dependence of Hr is almost linear. We note that together with an effective dielectric permittivity ε ≈ 103 at the interface, the linear fit of E to Hr indicates an interfacial linear magnetoelectric interaction with a strong coupling strength that amounts to 0.32 s/F, in good agreement with our theoretical prediction29,42,43 and the experimental estimation in Co/BaTiO3 thin films13. Furthermore, the linear growth of Hr with E implies an increasing negative surface spin density, which will give rise to a decrease of the effective damping and more detectable, a sign transition in small α at the critical electric field. Taking the odd-parity of the imaginary part of the magnetic susceptibly and its relation to damping α39, we expect a phase transition close to the frequency of FMR, which is in line with the experimental observations. The nonmonotonic behavior of the effective Δeff may be due to a nonlinear interplay of the higher order effects with nonlocal damping22, originating from the dissipative flow of nonequilibrium intralayer spin currents within the interface.
Experimentally, several multiferroic heterostructures based on (011)PMN-PT, such as Fe3O4/PMN-PT44, Ni0.79Fe0.21/PMN-PT14 and Ni0.46Zn0.54Fe2O4/PMN-PT45 were realized, the magnetic properties are found to be co-mediated by the interfacial strain- and screening-driven ME interaction due to the piezoelectricity of PMN-PT. To confirm the absence of stress-strain effect on the damping in our measurements, a 5 nm Ta layer was inserted between the CoZr and PMN-PT substrate to have a CoZr/Ta/PMN-PT heterostructure. Due to the isolation by the metallic (non-magnetic) Ta film with small dielectric permittivity, no considerable screening charge is expected on CoZr layer. A strain-mediated ME coupling transferred through the Ta thin layer remains as the main factor that influences the magnetization dynamics. Its consequence is a shift of the resonance field only, which is consistent with the experimental results (Fig. 2b). No noticeable changes, let alone a reversal is observed in ℑχz up to 16 kV/cm. To further clarify the interfacial strain effect on CoZr/PMN-PT heterostructure itself, we investigated the angular dependence of the resonance field for CoZr/PMN-PT film when varying the applied static magnetic field in-plane. Typically, the influence of the stress-strain effect on the magnetic anisotropy is more pronounced than the surface anisotropy stemming from the screening effect at the FM/FE interface. Inspecting the values under E = 0 kV/cm and those for E = 8 kV/cm, the FMR effective magnetic field Hr should possesses a large amplitude modification, as reported in the previous experiment on PMN-PT-based heterostructures14,45. However, under the present measurement conditions, the change concerning the amplitude of Hr at each angle, are small (cf. Fig. s2 in the Supplementary). Its angular dependence is found to be well described by an in-plane uniaxial anisotropy and the phase-shift of Hr under different applied external electric fields can be understood as an angle mismatch of the easy axis of the uniaxial anisotropy with respect to the [100]-direction. Such a small contribution of the strain-mediated ME interaction to the magnetic dynamics hints on the polycrystalline nature of our CoZr film, the average on the randomly oriented grains may suppress possible magnetostrictive effects, similar to polycrystalline Co/BaTiO3 heterostructure in Ref.13.
Discussion
The direct electric control of magnetic dynamics reported here offers a qualitatively new way to manipulate multiferroic devices with fast low-power heterogeneous read/write capability through the interfacial ME interaction. The static linear coupling manifests itself as an effective magnetic field and the dynamic coupling possesses substantial influence on magnetic damping in the thin FM film. A further interesting point is that a fully electric-field control of magnetic permeability can be realized in natural FM metals in contact with FE by external electric field at room temperature. Indeed, our recent direct permeability measurements of polycrystalline CoZr/PMN-PT and Co/PMN-PT show the emergence of positive-to-negative transition in both real and imaginary parts of magnetic permeability. Given that the dielectric permittivity of metal is negative below plasma frequent, the electric tuning of magnetic permeability which opens new perspectives to envisage spin-wave amplification by stimulated emission of radiation device46.
Methods
The base pressure was 2.5 × 10−5 Pa and a 0.2 Pa pressure of Argon was used in the sputtering. Co target with regularly placed Zr chips, which was 70 mm in diameter and 3 mm in thickness, was used to deposit the CoZr layer. The composition of the deposited magnetic layer was adjusted by controlling the number of the Zr chips, as shown in Fig. 1a in the main text. The film was deposited at oblique angle 20° without any applied field, which induced in-plane uniaxial anisotropy. Pt layers were sputtered on both the top and bottom sides of the FM/FE structure as electrodes. Cu wires were connected to the electrodes and dc voltage was applied to the PMN-PT along (011) with an electrometer. The magnetic properties of the samples were measured by a vibrating sample magnetometer. An in-plane uniaxial magnetic anisotropy is evident by a rectangle easy-axis hysteresis loop with the remanence ration Mr/Ms ≈ 1. Further details of electric field induced changes of the static magnetic properties are given in the supplementary material to this paper. In-plane FMR measurements were performed in a JEOL, JES-FA 300 (X-band at ω = 8.969 GHz with the power 1 mW) spectrometer at room temperature. As shown in Fig. 1b of the main text, the FMR setup. The electromagnet produces the static in-plane magnetic field. A cylindrical cavity resonator is placed at the center of the electromagnet. The microwave unit connected with the cavity resonator by waveguide generates microwave (the rf magnetic field is normal to the FM/FE films) and detects the reflection. As for the influence of the current, no current was injected into the ferromagnetic layer in the experiment. The leakage current during the measurements is below nA, which is much smaller than any other relevant effect in the system and also ways below the required current density for a current induced torque acting on the magnetization.
Additional Information
How to cite this article: Jia, C. et al. Electric tuning of magnetization dynamics and electric field-induced negative magnetic permeability in nanoscale composite multiferroics. Sci. Rep. 5, 11111; doi: 10.1038/srep11111 (2015).
References
Stöhr, J. & Siegmann, H. C. Magnetism: From Fundamentals To Nanoscale Dynamics (Springer-Verlag, Berlin Heideberg, 2006).
Brataas, A., Kent, A. D. & Ohno, H. Current-induced torques in magnetic materials. Nature Materials 11, 372–381 (2012).
Vaz, C. A. F. Electric field control of magnetism in multiferroic heterostructures. J. Phys.: Condens. Matter 24, 333201 (2012).
Fiebig, M. Revival of the magnetoelectric effect. J. Phys. D: Appl. Phys. 38, R123–R152 (2005).
Eerenstein, W., Mathur, N. D. & Scott, J. F. Multiferroic and magnetoelectric materials. Nature 442, 759–765 (2006).
Ramesh, R. & Spaldin, N. A. Multiferroics: progress and prospects in thin films. Nature Materials 6, 21–29 (2007).
Vaz, C. A. F., Hoffman, J., Ahn, C. H. & Ramesh, R. Magnetoelectric coupling effects in multiferroic complex oxide composite structures. Adv. Mater. 22, 2900–2918 (2010).
Kleemann, W. Switching magnetism with electric fields. Physics 2, 105 (2009).
Velev, J. P., Jaswal, S. S. & Tsymbal, E. Y. Multi-ferroic and magnetoelectric materials and interfaces. Phil. Trans. R. Soc. A 369, 3069–3097 (2011).
Fusil, S., Garcia, V., Barthlmy, A. & Bibes, M. Magnetoelectric Devices for Spintronics. Annu. Rev. Mater. Res. 44, 91–116 (2014).
Nelson, C. T. et al. Domain dynamics during ferroelectric switching. Science 334, 968–971 (2011).
Nozaki, T. et al. Electric-field-induced ferromagnetic resonance excitation in an ultrathin ferromagneticmetal layer. Nature Physics 8, 491–496 (2012).
Jedrecy, N. et al. Strong magnetoelectric coupling in multiferroic Co/BaTiO3 thin films. Phys. Rev. B 88, 121409 (2013).
Nan, T. et al. Quantification of strain and charge co-mediated magnetoelectric coupling on ultra-thin Permalloy/PMN-PT interface. Sci. Rep. 4, 3688 (2014).
Liu, M. & Sun, N. X. Voltage control of magnetism in multiferroic heterostructures. Phil. Trans. R. Soc. A 372, 20120439 (2014).
Brataas, A., Tserkovnyak, Y. & Bauer, G. E. W. Scattering theory of Gilbert damping. Phys. Rev. Lett. 101, 037207 (2008).
Ebert, H., Mankovsky, S., Ködderitzsch, D. & Kelly, P. J. Ab-Initio calculation of the Gilbert damping parameter via the linear response formalism. Phys. Rev. Lett. 107, 066603 (2011).
Hals, K., Nguyen, A. & Brataas, A. Intrinsic coupling between current and domain wall motion in (Ga,Mn)As. Phys. Rev. Lett. 102, 256601 (2009).
Hickey, M. & Moodera, J. Origin of intrinsic Gilbert damping. Phys. Rev. Lett. 102, 137601 (2009).
Urban, R., Woltersdorf, G. & Heinrich, B. Gilbert damping in single and multilayer ultrathin films: role of interfaces in nonlocal spin dynamics. Phys. Rev. Lett. 87, 217204 (2001).
Tserkovnyak, Y., Brataas, A., Bauer, G. & Halperin, B. I. Nonlocal magnetization dynamics in ferromagnetic heterostructures. Rev. Mod. Phys. 77, 1375–1421 (2005).
Nembach, H., Shaw, J., Boone, C. & Silva, T. Mode- and size-dependent Landau-Lifshitz damping in magnetic nanostructures: evidence for nonlocal damping. Phys. Rev. Lett. 110, 117201 (2013).
Smith, D. R. Metamaterials and negative refractive index. Science 305, 788–792 (2004).
Shalaev, V. M. Optical negative-index metamaterials. Nature photonics 1, 41–48 (2007).
Fertman, E. L. & Beznosov, A. B. Natural media with negative index of refraction: perspectives of complex transition metal oxides (review article). Low Temp. Phys. 37, 572–582 (2011).
Pimenov, A., Loidl, A., Przyslupski, P. & Dabrowski, B. Negative refraction in ferromagnet-superconductor superlattices. Phys. Rev. Lett. 95, 247009 (2005).
Pimenov, A., Loidl, A., Gehrke, K., Moshnyaga, V. & Samwer, K. Negative refraction observed in a metallic ferromagnet in the gigahertz frequency range. Phys. Rev. Lett. 98, 197401 (2007).
Engelbrecht, S., Shuvaev, A. M., Luo, Y., Moshnyaga, V. & Pimenov, A. Negative refraction in natural ferromagnetic metals. Europhys. Lett. 95, 37005 (2011).
Jia, C. L. et al. Mechanism of interfacial magnetoelectric coupling in composite multiferroics. Phys. Rev. B 90, 054423 (2014).
Katsura, H., Nagaosa, N. & Balatsky, A. V. Spin Current and Magnetoelectric Effect in Noncollinear Magnets. Phys. Rev. Lett. 95, 057205 (2005).
Burton, J. D. & Tsymbal, E. Y. Magnetoelectric interfaces and spin transport, Phil. Trans. R. Soc. A 370, 4840 (2012).
Rondinelli, J. M., Stengel, M. & Spaldin, N. A. Carrier-mediated magnetoelectricity in complex oxide heterostructures. Nature Nanotech. 3, 46–50 (2007).
Duan, C.-G. et al. Surface magnetoelectric effect in ferromagnetic metal films. Phys. Rev. Lett. 101, 137201 (2008).
Maruyama, T. et al. Large voltage-induced magnetic anisotropy change in a few atomic layers of iron. Nature Nanotech. 4, 158–161 (2009).
Mardana, A., Ducharme, S. & Adenwalla, S. Ferroelectric control of magnetic anisotropy. Nano Lett. 11, 3862–3867 (2011).
Pantel, D., Goetze, S., Hesse, D. & Alexe, M. Reversible electrical switching of spin polarization in multiferroic tunnel junctions. Nature Materials 11, 289–293 (2012).
Bass, J. & Pratt, W. P., Jr. Spin-diffusion lengths in metals and alloys and spin-flipping at metal/metal interfaces: an experimentalists critical review. J. Phys.: Condens. Matter 19, 183201 (2007).
Lindner, J., Meckenstock, R. & Farle, M. [Applications of Ferromagnetic Resonance] Characterization of Materials. [ Elton N. Kaufmann1 (ed.)] (John Wiley & Sons, 2012).
Yalcin, O. (ed.) Ferromagnetic Resonance - Theory And Applications ; 10.5772/50583 (InTech, 2013).
Celinski, Z., Urquhart, K. B. & Heinrich, B. Using ferromagnetic resonance to measure the magnetic moments of ultrathin films. Journal of Magnetism and Magnetic Materials 166, 6–26 (1997).
Hoffmann, F. et al. Mapping the magnetic anisotropy in (Ga,Mn)As nanostructures. Phys. Rev. B 80, 054417 (2009).
Sukhov, A., Horley, P. P., Jia, C.-L. & Berakdar, J. Magnetoelectric coupling in a ferroelectric/ferromagnetic chain revealed by ferromagnetic resonance. J. Appl. Phys. 113, 013908 (2013).
Sukhov, A. et al. Angular dependence of ferromagnetic resonance as indicator of the nature of magnetoelectric coupling in ferromagnetic-ferroelectric heterostructures Phys. Rev. B 90, 224428 (2014).
Liu, M. et al. Non-volatile ferroelastic switching of the Verwey transition and resistivity of epitaxial Fe3O4/PMN-PT (011). Sci. Rep. 3, 1876 (2013).
Dong, C. et al. Piezoelectric control of magnetic anisotropy in the Ni0.46Zn0.54Fe2O4/ Pb(Mg1/3Nb2/3)O3-PbTiO3 composite. Appl. Phys. Lett. 104, 062403 (2014).
Berger, L. Emission of spin waves by a magnetic multilayer traversed by a current. Phys. Rev. B 54, 9353–9358 (1996).
Acknowledgements
This research was supported by the National Basic Research Program of China (No. 2012CB933101), the National Natural Science Foundation of China (No. 11104123, 11474138, 11034004 and 11374131), the Program for Changjiang Scholars and Innovative Research Team in University (No. IRT1251), the German Research Foundation (No. SFB 762) and the Fundamental Research Funds for the Central Universities (No. 2022013zrct01/2022013zr0017).
Author information
Authors and Affiliations
Contributions
All authors contributed to the planning, discussion and analysis of this research. C.-J. J., F.-L. W. and D.-S. X. performed the sample fabrication and measurements. C.-L. J. and J.B. developed the theoretical model for the analysis and wrote the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Jia, C., Wang, F., Jiang, C. et al. Electric tuning of magnetization dynamics and electric field-induced negative magnetic permeability in nanoscale composite multiferroics. Sci Rep 5, 11111 (2015). https://doi.org/10.1038/srep11111
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep11111
- Springer Nature Limited
This article is cited by
-
Magnon-tuning non-volatile magnetic dynamics in a CoZr/PMN-PT structure
Scientific Reports (2020)
-
Structure and magnetic properties of epitaxial LiFe5O8 film with different growth temperatures
Applied Physics A (2019)
-
Non-Volatile Ferroelectric Switching of Ferromagnetic Resonance in NiFe/PLZT Multiferroic Thin Film Heterostructures
Scientific Reports (2016)