Abstract
The realization of ultra-low power Si-based resistive switching memory technology will be a milestone in the development of next generation non-volatile memory. Here we show that a high performance and ultra-low power resistive random access memory (RRAM) based on an Al/a-SiNx:H/p+-Si structure can be achieved by tuning the Si dangling bond conduction paths. We reveal the intrinsic relationship between the Si dangling bonds and the N/Si ratio x for the a-SiNx:H films, which ensures that the programming current can be reduced to less than 1 μA by increasing the value of x. Theoretically calculated current-voltage (I–V ) curves combined with the temperature dependence of the I–V characteristics confirm that, for the low-resistance state (LRS), the Si dangling bond conduction paths obey the trap-assisted tunneling model. In the high-resistance state (HRS), conduction is dominated by either hopping or Poole–Frenkel (P–F) processes. Our introduction of hydrogen in the a-SiNx:H layer provides a new way to control the Si dangling bond conduction paths and thus opens up a research field for ultra-low power Si-based RRAM.
Similar content being viewed by others
Introduction
As device sizes continue to be scaled down, conventional flash memory is expected to reach its physical size limits in the near future. As a potential replacement for flash memory, resistive random access memory (RRAM) has attracted considerable attention because of advantages that include a simple fabrication process, fast operating speeds, long retention times and good scalability1,2,3,4. However, the normal programming currents of RRAMs (>10 μA) are still much higher than those required for flash memory (<10 nA)5,6 and thus reduction of the device current and power consumption is an important issue for RRAM applications. The lowest reported reset current for RRAM to date is approximately 1 μA when using the high-k material Al2O37 and this result was ascribed to the low defect density of the Al2O3 film. In contrast to resistive switching memories based on high-k materials, resistive switching (RS) in low power Si-based devices is a more attractive and promising prospect because of the full compatibility of these devices with traditional complementary metal-oxide-semiconductor (CMOS) technology. Among the available Si-based RRAM materials, amorphous-SiNx (a-SiNx) films exhibit more stable RS behavior at lower operating voltages than conventional SiOx films8,9,10,11,12,13,14. It should be noted that the programming currents of a-SiNx-based devices are higher (~100 μA) because high numbers of random traps make the pristine a-SiNx films leakier. Finding an effective way to control the conduction paths in these films has been a challenging issue. To reduce the power of a-SiNx-based devices, we introduced hydrogen into the a-SiNx film, which then shows greatly improved insulating properties with low leakage current because of the hydrogen passivation effect15. We found that the field-enhanced thermal breakage of weak Si-H bonds and the H+ ions migration result in the generation and re-passivation of Si dangling bonds in the a-SiNx:H films. Here we show a tunable dangling bond path effect on the programming current of a-SiNx:H based on variation of the N/Si ratio. By tuning the N/Si ratio x from 0.62 to 1.17, the number of dangling bonds can be reduced to produce programming currents of less than 1 μA. In addition, the electroforming and set operations of a-SiNx:H layers are easier than that required for Al2O3 and SiOx layers because of the weak Si-H bond energy and the comparatively low dielectric breakdown strength of a-SiNx:H16. We demonstrate that an appropriate N/Si ratio can be used to control the concentrations of Si-H bonds and Si dangling bonds, which is the crucial factor in production of ultra-low power devices. Lower N/Si ratios result in increased numbers of Si dangling bonds and high programming currents, while high N/Si ratios will make the film too insulated and make the forming process difficult to be completed. The a-SiNx:H-based RRAM with optimum N/Si ratio is expected to be a suitable candidate for ultra-low power Si-based RRAMs.
Results
Programming current reduction by N/Si ratio tuning
A schematic of the Al/a-SiNx:H/p+-Si device structure is shown in Fig. 1. An approximately 8-nm-thick a-SiNx:H film was deposited on a p+-Si substrate. The substrate resistivity was in the 0.004–0.0075 Ω∙cm range, which ensured good conductivity as the bottom electrode. For the electrical measurements, we deposited aluminum (Al) as top and back electrode layers. A cross-sectional high-resolution transmission electron microscopy (HRTEM) image of the Al/a-SiN1.17:H/p+-Si structure is shown on the right of Fig. 1. During all the electrical measurements, the bias signal was applied to the top electrode with the back electrode grounded. Figure 2a shows the initial I-V curves and forming processes of four devices with different N/Si ratios. The ratio x is determined to be 1.17, 0.93, 0.77 and 0.62 for these devices through X-ray photoelectron spectroscopy (XPS) measurements. We notice that for all devices, the forming current value decreases by several orders with increasing x from 0.62 to 1.17. As indicated by Tao et al17, the bandgap energy of the a-SiNx:H film decreases with increasing Si concentration. The narrower bandgap causes more electrons or holes to be thermally excited to localized states near the conduction or valence bands because the carrier density is proportional to , where Eg denotes the bandgap energy. Therefore, more charge carriers take part in conduction, which leads to increased initial currents. After the forming process, the devices with x = 0.62, 0.93 and 1.17 present bipolar RS behavior, as shown in Fig. 2b. The set and reset currents also decrease obviously with increasing x. For devices with x = 0.62–0.93, the programming current can be reduced from 1 mA to 10 μA. This value is close to that previously reported for SiNx-based RRAM9,10. The current also decreases further with increasing x, reaching a very low value of less than 1 μA when x = 1.17. This shows that we can control the current and power of a-SiNx:H-based RRAM devices by tuning the N/Si ratio.
Bipolar switching performance of ultra-low power a-SiN1.17:H device
The details of the memory performance of the SiN1.17:H device with the lowest measured current are shown in Fig. 3a. Polarity-dependent bipolar switching occurs for a compliance current of 1 μA when the bias voltage increases to 3.2 V. After the forming process, the current reaches a higher value and the device switches from the initial resistance state (IRS) to the low resistance state (LRS). A reset process can be achieved when a negative bias is applied to the device. When the negative voltage reaches −1.2 V, the current decreases rapidly and the device switches to the high resistance state (HRS). Subsequently, under application of a positive voltage ranging from 0 to 2.5 V, the device can switch back to the LRS, which corresponds to the set state. We successfully repeated this switching process for 800 cycles through DC voltage sweeps. The endurance of the HRS and the LRS is shown in Fig. 3b. The device shows good reliability at a read voltage of 0.5 V. Figure 3c shows the retention characteristics of this device at room temperature and at 80 °C. After a retention time of 105 s, the HRS and LRS currents are still equal to that of the initial state. The I-V characteristics of 30 cycles are presented in Fig. 3d. It is shown that the device maintains a similar on/off ratio and shows good reliability. The observed fluctuations may be caused by random migration of defects during RS cycling and the fluctuation becomes more prominent when the programming current is ultra-low18. The small asymmetry between the positive and negative I-V characteristics is related to the variation of the work functions of the top and bottom electrodes, which induces different tunneling barriers in LRS conduction. The work function of the top Al electrode is 4.2 eV, which is smaller than that of the bottom p+-Si electrode, at approximately 5.0 eV. Therefore, the positive current may be smaller than the negative current.
It should be noted that the reset current here is 740 nA, which is less than 1 μA. Under such low current conditions, we observe a reset sweep stop at −0.8 V although it actually stops at 0 V. The reason lies in the production of a positive transient current. We found that a positive transient current exist in our device as the applied negative voltage decreases, which is due to the discharging of trap states in a-SiNx:H film19. The intensity of transient current is less than 1 pA. When the dc current of our devices is high, this effect of transient current is not obvious. But with the magnitude of negative voltage decreasing to less than 0.8 V, the dc current becomes very lower than that of the transient current. And the effect of positive transient current is then evident. The value of opposite current can-not be plotted in the logarithmic coordinates. Thus the data of current in the scale from −0.8 to 0 V can-not be shown in this form. Furthermore the read current of HRS and LRS at 0.5 V are about pA and nA order, respectively. These parameters here are obviously lower than that of other RRAM. Meanwhile the low set voltage (~2.5 V) and reset voltage (~−1.6 V) confirm that an ultra-low power resistive switching is now realized in the Al/a-SiN1.17:H/p+-Si structure. I-V characteristic of forming process with negative voltage is shown in the inset of Fig. 3d, which is almost identical to the positive curves except a little bit higher voltage. The observed RS behavior in two directions proves that ultra-low power RS originate solely from a-SiNx:H film itself.
To assess the uniformity of the a-SiNx:H devices, the statistical distributions of the operating voltages and currents are shown in Fig. 3e. The devices show good uniformity with small deviations. We also measured the size dependence characteristics of the devices. It is found the HRS and LRS current decrease with electrode size reduced from 300 μm to 30 μm, as shown in the inset of Fig. 3f. Figure 3f also shows the bipolar RS behavior when the size decreased to 30 μm and the programming current can be reduced to less than 100 nA with the operating voltage increased to 3.2 V. We see that the reset sweep seems to stop at −1 V, which indicates the effect of transient current. The increased operation voltage may be related to the wet etching process for Al electrode with the smaller diameter of 30 um. Interfacial contact between the Al electrode and SiN1.17:H film is easily affected during the wet etching process because the a-SiNx:H film thickness is only 8 nm. Overall, the operation power can be reduced by down-scaling of device size.
Temperature dependence of current in the a-SiN1.17:H device
We also measured the temperature dependence of the HRS and LRS currents in the analysis of the conduction process of the SiN1.17:H device, as shown in Fig. 4a. The current of the HRS clearly decreases with decreasing temperatures from 350 K to 160 K. This indicates that the conduction of HRS is sensitive to temperature change, i.e., it is a thermal-activated conduction process. The temperature dependence of the current density under an electric field of 1.9 MV/cm is shown in Fig. 4b. Based on the slope of the ln J vs 1/T, the activation energy of HRS at high temperature is calculated to be 0.4 eV. The temperature dependence of HRS current here is unlike that in usual RRAM devices, where slightly temperature dependence is observed4,20. In usual RRAM devices with much higher current, the HRS is usually formed due to rupture of conductive filament and the conduction is dominated by tunneling process. Tunneling conduction is independent on temperature, so slightly temperature dependence can be observed in usual RRAM devices. In contrast to the HRS current of ultra-low power device, the LRS current remains the same with decreasing temperature from 350 K to 160 K, as shown in Fig. 4a, which means that LRS is insensitive to temperature changes. This reveals that LRS in the ultra-low power device is dominated by tunneling process instead. It is verified that the characteristics of LRS are not related to the metal filaments, where the LRS resistance generally increases with increasing temperature.
Atomic configurations of a-SiNx:H films with different N/Si ratios
To investigate the relationship between the mechanism and the configurations of a-SiNx:H films with various N/Si ratios, we analyzed the corresponding Fourier transform infrared (FTIR) spectroscopy and electron spin resonance (ESR) spectra as shown in Fig. 5. The absorption bands at 841 cm−1, 1176 cm−1, 2173 cm−1 and 3356 cm−1 correspond to the Si-N stretching, N-H rocking, Si-H stretching and N-H stretching modes, respectively21. The Si-H and N-H bonds are derived from the hydrogenation of silicon nitride. It is clearly shown that the intensity of the Si-H bonds in films with x = 0.62–0.93 is much higher than that in sample with x = 1.17. This can be ascribed to the increased Si concentrations in films with lower x values. The excess Si atoms combine with H atoms to form more Si-H bonds in the films. In all the a-SiNx:H films with various N/Si ratios, we observed a resonance peak with a g value of 2.0042 as shown in Fig. 5b, which is related to the paramagnetic center of the Si dangling bonds 22. It is also found the resonance peak intensity increases with decreasing x value. And the a-SiN1.17:H film has the lowest resonance peak. The weak Si dangling bonds signal in SiN1.17:H shows that few original Si dangling bonds remain in the film. However, for films with lower N/Si ratios, the intensity of the resonance peak is stronger, indicating that more Si dangling bonds exist in these films. The calculated density of Si dangling bonds changes from 1 × 1017 to 5 × 1017 cm−3 as x varies from 1.17 to 0.62. This implies that the Si dangling bonds can be controlled by tuning N/Si ratio.
Dehydrogenation effect on initial current
In order to demonstrate the role of H in our devices, we measured the initial currents of two devices after dehydrogenation treatment, with results as shown in Fig. 6a. The two devices were annealed at 500 °C and 600 °C for 10 min in vacuum. Dehydrogenation generally occurs at 400 °C, so the annealing temperatures and time used here ensures the release of hydrogen. The reduction of H content was confirmed by the FTIR spectrum shown in Fig. 6b. The disappearance of the absorption peak of Si–H stretching vibration mode at 2173 cm−1 indicates that a proportion of the hydrogen atoms have effused from the SiN1.17:H films. When compared with that of the pristine device, the intensity of initial current for the devices annealed at 500 °C increases sharply and becomes close to that of LRS current. Furthermore, for the device annealed at 600 °C, the intensity of IRS current is nearly as high as that of the LRS current. The increase in the initial current is ascribed to increments in the number of dangling bonds or trap states induced by dehydrogenation23. The similar trends for initial current change in the device after dehydrogenation and the device under an applied electric field reveals that H atoms in SiN1.17:H films play a key role in the RS process. It is clearly observed that the number of Si-H bonds decreases with increasing N/Si ratio, as verified by the FTIR spectra shown in Fig. 5a, while the number of N-H bonds increases with increasing N/Si ratio. Because the N-H bonds are stronger and more stable than Si-H bonds, the Si dangling bonds are mainly generated from broken Si-H bonds. When more Si atoms exist, then more dangling bonds will be produced. Therefore, a tunable dangling bond path can be obtained by variation of N/Si ratio with the assistance of H atoms.
Discussion
As revealed by the FTIR and ESR that there are many Si-H bonds and a few Si dangling bonds in the pristine a-SiNx:H films. Si-H bonds can be broken during the forming or set process due to the field-enhanced thermal breakage24,25, because the Si-H bond energy (3.0 eV) is much lower than that of Si-N (3.7 eV)24. The H+ ions from broken Si-H bonds migrate toward the cathode under the positive electric field, producing many new Si dangling bonds in the film. A schematic illustration of this process is shown in Fig. 7a. The Si dangling bonds are neutral traps near the middle of the bandgap and can form a conductive path when the number of dangling bonds achieves a certain level. The carriers can flow through the Si dangling bond conduction path by tunneling process. In our previous work26, the similar process is demonstrated in SiOx film. The Si-O bonds could be broken to form Si dangling bonds at high electric field through standard Boltzmann process. In the a-SiNx:H film, the operation voltage is much lower than that of SiOx film because the Si-H bond energy is weaker than that of Si-O bonds. As the negative voltage was applied, the H+ ions can migrate back and re-passivate the Si dangling bonds with the aid of thermal effect, leading to the decrease of Si dangling bonds. Si dangling bond pathway thus ruptures and the device returns to the HRS.
Based on the above analysis, we will explain how the programming current can be controlled by tuning Si dangling bond conduction paths. As illustrated in Fig. 5 the pristine devices with higher N/Si ratios initially contain fewer Si-H bonds, which results in far fewer Si dangling bonds being generated during the forming process. The conduction path containing fewer Si dangling bonds will produce lower currents for LRS. Figure 7b,c shows the schematic diagram of Si dangling bond conduction path in the devices with different N/Si ratio, respectively. As for the sample with x = 0.62–0.93 shown in Fig. 7b, the Si dangling bonds are partially re-passivated and the conduction path ruptures in HRS. When N/Si ratio increases to 1.17, the conduction path can not pass through the whole film because of the low Si dangling bonds density. It is observed that the LRS current in a-SiN1.17:H device is close to the HRS current in SiN0.93:H device as shown in Fig. 2b. Furthermore the conduction path nearly dissolves in HRS as presented in Fig. 7c, because the HRS current in a-SiN0.93:H device is close to IRS current. Consequently, the Si dangling bond conduction path can be tuned by controlling N/Si ratio of the a-SiNx:H films.
According to the analysis of atomic configuration of a-SiNx:H film with different N/Si ratio, we perform theoretical calculations to investigate the conduction mechanism of the proposed ultra-low power device. As reported in the literatures about conduction mechanism of silicon nitrides27,28,29, the main carriers in a-SiNx:H films are holes and the current conduction mechanism is dominated by hopping between localized states under low electric fields and Poole–Frenkel (P–F) process under higher electric fields. The current density versus electric field relationship in the P–F process is expressed as28
where E is electric field, J is the current density, q is the electronic charge, is the barrier height of trap, ε0 is the permittivity of free space, εd is the dynamic dielectric constant, k is the Boltzmann constant and T is the temperature. We agree that the IRS of all our devices obey this conduction model. For the HRS of SiN1.17:H device, we plot the set curve with ln (J/E) against as shown in Fig. 8a. When the electric field E < 1.25 MV/cm, ln (J/E) is constant and independent of the electric field, which indicates ohmic conduction in this region. This corresponds to the hopping process under low electric fields. Then, when E > 1.25 MV/cm, the straight line of the plots implies the dominant role of P–F process. According to equation (1), the value of dynamic dielectric constant can be estimated from the slope of ln (J/E) – plot. Here the value of εd is 4.2, which is between the dielectric constant in the optical range, 4 and the static dielectric constant 7. As pointed out by S.M. Sze28, the value of εd is of paramount importance, which confirms that the HRS is dominated by P–F process. This conduction model is consistent with the current temperature dependence shown in Fig. 4, because P–F effect is a thermal activated conduction process. By entering the activation energy 0.4 eV into equation (1), the potential well q of the trap in P–F effect is determined to be 0.9 eV. The energy band diagram of the conduction process in HRS is presented in Fig. 9a,b.
On the other hand, the LRS plots are also found to be close to a straight line, but the calculated εd is about 22.6, which is far beyond the scope above. Considering that LRS is insensitive to temperature change, we conjecture that the conduction of LRS should be dominated by tunneling mechanism rather than P–F process. We firstly exclude the probability of Fowler–Nordheim (F–N) tunneling model for LRS conduction in a-SiN1.17:H device. The F–N tunneling is due to current tunneling through the triangular barrier with a high electric field (>6 MV/cm). However, the LRS current here were measured under electric field less than 3 MV/cm. So the electric field is too low to generate F–N tunneling current. Alternatively, if the insulation film is very thin (<4 nm), the electrons can flow through the film by direct tunneling under low electric field. However the SiN1.17:H film is 8 nm thick and thus the possibility of direct tunneling can also be eliminated. Recently the trap-assisted tunneling (TAT) model has been used to explain the stress-induced leakage current in nitrided oxide films30,31,32,33, which includes two-step tunneling process via traps in the film. The carriers first tunnel into the trap state from one electrode and then tunnel into the other electrode. The tunneling current can be generated under low electric field even in much thicker film. In the a-SiN1.17:H device, the new Si dangling bonds that were created during forming or set process provides the intermediate states for TAT conduction and generate a considerable tunneling current. Therefore the TAT conduction is the most reasonable conduction mechanism for LRS in a-SiN1.17:H films. The conductive path is composed of Si dangling bonds. The energy band diagram of this conduction process is shown in Fig. 9c.
In order to further verify whether or not the Si dangling bond conduction paths obey the TAT conduction model, we give a calculation to fit this model and clarify the trap energy level in our device. We use a generalized thermionic TAT model to describe the tunneling process in LRS33. Under low electric fields in this model, the tunneling occurs through a trapezoidal barrier. While under high fields tunneling through the triangular barrier becomes more significant. In our devices the measured voltage of LRS is less than 2 V, so we only have to take the trapezoidal barrier tunneling into account. As shown in Fig. 9c, the holes tunnel from Al top electrode to the trap state of Si dangling bonds in the film and then tunnel to the valence band of p+-Si. The equation for this current is given as33
where Nt is the trap concentration, ϕt is the trap energy level, d is the film thickness and fFD is the Fermi-Dirac function, which is described by
ϕB is the barrier height between electrode and film. P1 and P2 are the tunneling probabilities for the two-step process, where
and Ct is the trap energy dependent rate constant that is given by
We calculated the I-V curve using equation (2) for comparison with experimental LRS data as shown in Fig. 8b. The parameter values used in calculation are shown inside this figure. It is notable that the ϕt value is 1.65 V. This value is close to the energy level of Si dangling bonds in the silicon nitride film29,34, which theoretically confirms that the generated trap states originate from Si dangling bonds. Therefore LRS in the ultra-low power device is dominated by the TAT conduction with Si dangling bonds as the intermediate trap states. Here the value of trap concentration Nt is 3.8 × 1021 cm−3 because sufficient trap centers are needed to produce a considerable TAT current. As reported in ref. 33, a higher trap density of 6 × 1022 cm−3 was used to calculate the TAT current. Although the trap density is high in low power device, the current is lower than that of SiN0.62~0.93:H devices because the conduction path is not continuous and it is dominated by two-step tunneling process. As for the SiN0.62~0.93:H devices, the trap density should be much higher and the current is dominated by continuous conduction.
In conclusion, we demonstrate that ultra-low power Si-based bipolar resistive switching memory devices can be realized in Al/a-SiNx:H/p+-Si structure by tuning Si dangling bond conduction paths. The relationship between Si dangling bonds and the N/Si ratio x for a-SiNx:H films reveals that programming current can be reduced to less than 1 μA with operating voltage of less than 2.5 V by increasing the value of x. We found that the field-enhanced thermal breakage of weak Si-H bonds and migration of the H+ ions result in the generation and re-passivation of Si dangling bonds in a-SiNx:H films. Consequently tunable dangling bond paths can be obtained by varying the N/Si ratio. Our theoretical calculation of I-V curves for the LRS indicates that the energy level of LRS trap states is in close agreement with the value of Si dangling bond, which confirms that Si dangling bond conduction paths dominate the TAT model. While, for HRS the conduction is dominated by either hopping or P–F process. Our introduction of hydrogen to the resistive switching a-SiNx film provides a new way to control the Si dangling bond conduction path and this opens up a potential research field for ultra-low power Si-based RRAM.
Methods
The a-SiNx:H films in this paper were deposited on p+-Si substrates in a plasma-enhanced chemical vapour deposition (PECVD) system operating at 250 °C, with SiH4 and NH3 as the reaction gases. To form the top electrode, 300-nm-thick aluminum with a diameter of 300 μm were deposited on the top of the films using thermal evaporation method. The smaller top electrode with diameter of 30 and 100 um was fabricated by lithographic method combined with wet etching. The rear of the substrate was also coated with a thin Al layer to reduce the contact resistance. The entire fabrication process is very simple and does not require any high-temperature treatment. To reduce the programming current, samples with four different Si/N ratios were prepared by varying the flow rate ratio of SiH4 and NH3. The N/Si atomic concentration ratios of the samples are determined through XPS measurement using the PHI 5000 VersaProbe. The microstructure of the sample was revealed by HRTEM using a Tecnai G2 F20 electron microscope operating at 200 kV. The ESR spectrum was measured in the Bruker EMX-10/12 system and FTIR spectrum was measured in the NEXUS870 system. The dehydrogenation process was carried out by annealing treatment at 500 °C and 600 °C for 10 min in vacuum, respectively. The electrical characteristics of the samples were measured using the Agilent B1500A semiconductor analyzer in atmosphere and the temperature dependence of the I-V characteristics was examined in the Lake Shore CRX-4K system under a vacuum of 5 × 10−5 Torr.
Additional Information
How to cite this article: Jiang, X. et al. a-SiNx:H-based ultra-low power resistive random access memory with tunable Si dangling bond conduction paths. Sci. Rep. 5, 15762; doi: 10.1038/srep15762 (2015).
References
Waser, R., Dittmann, R., Staikov, G. & Szot, K. Redox-based resistive switching memories–nanoionic mechanisms, prospects and challenges. Adv. Mater. 21, 2632–2663 (2009).
Waser, R. & Aono, M. Nanoionics-based resistive switching memories. Nat. Mater. 6, 833–840 (2007).
Pan, F., Gao, S., Chen, C., Song, C. & Zeng, F. Recent progress in resistive random access memories: materials, switching mechanisms and performance. Mater. Sci. Eng. R. 83, 1–59 (2014).
Ielmini, D., Bruchhaus, R. & Waser, R. Thermochemical resistive switching: materials, mechanisms and scaling projections. Phase Trans. 84, 570–602 (2011).
Pan, F. Experimental and simulation study of resistive switches for memory applications. UC Berkeley: Electrical Engineering & Computer Sciences. (2012). Available at: http://escholarship.org/uc/item/38d5q41d. (Accessed: 4th September, 2012).
Yang, X. & Chen, I.-W. Dynamic-load-enabled ultra-low power multiple-state RRAM devices. Sci. Rep. 2, 744 (2012).
Wu, Y., Lee, B. & Wong, H.-S. P. Al2O3-based RRAM using atomic layer deposition (ALD) with 1-μA reset current. IEEE Electron Device Lett. 31, 1449–1451 (2010).
Mehonic, A. et al. Electrically tailored resistance switching in silicon oxide. Nanotechnology. 23, 455201 (2012).
Kim, H. D., An, H. M. & Kim, T. G. Resistive-switching behavior in Ti/Si3N4/Ti memory structures for ReRAM applications. Microelectron. Eng. 98, 351–354 (2012).
Hong, S. M., Kim, H. D., An, H. M. & Kim, T. G. Effect of work function difference between top and bottom electrodes on the resistive switching properties of SiN films. IEEE Electron Device Lett. 34, 1181–1183 (2013).
Kim, H. D., An, H. M., Hong, S. M. & Kim, T. G. Unipolar resistive switching phenomena in fully transparent SiN-based memory cells. Semicond. Sci. Technol. 27, 125020 (2012).
Kim, H. D., Yun, M. J. & Kim, T. G. Forming-free resistive switching characteristics and improved reliability in sub-stoichiometric NbNx films. Phys. Status. Solidi. RRL. 9, 264–268 (2015).
Makihara, K., Fukushima, M., Ohta, A., Ikeda, M. & Miyazaki, S. Characterization of resistance-switching properties of SiOx films using Pt nanodots electrodes. ECS Trans. 50, 459–464 (2013).
Ohta, A. et al. Characterization of resistive switching behaviors of RF sputtered Si oxide resistive random access memories with Ti-based electrodes. Jpn. J. Appl. Phys. 52, 11NJ06 (2013).
Kim, H. D., An, H. M. & Kim, T. G. Improved reliability of Au/Si3N4/Ti resistive switching memory cells due to a hydrogen postannealing treatment. J. Appl. Phys. 109, 016105 (2011).
McPherson, J., Kim, J.-Y., Shanware, A. & Mogul, H. Thermochemical description of dielectric breakdown in high dielectric constant materials. Appl. Phys. Lett. 82, 2121–2123 (2003).
Tao, M. et al. Electrical conduction in silicon nitrides deposited by plasma enhanced chemical vapour deposition. Philos. Mag. B. 73, 723–736 (1996).
Ambrogio, S. et al. Statistical fluctuations in HfOx resistive-switching memory: Part I—set/reset variability. IEEE Trans. Electron Devices 61, 2912–2919 (2014).
Zous, N. K., Wang, T., Yeh, C. C., Tsai, C. W. & Huang, C. Transient effects of positive oxide charge on stress-induced leakage current in tunnel oxides. Appl. Phys. Lett. 75, 734–736 (1999).
Yu, S., Guan, X. & Wong, H.-S. P. Conduction mechanism of TiN/HfOx/Pt resistive switching memory: A trap-assisted tunneling model. Appl. Phys. Lett. 99, 063507 (2011).
Hao, H. L., Wu, L. K., Shen, W. Z. & Dekkers, H. F. W. Origin of visible luminescence in hydrogenated amorphous silicon nitride. Appl. Phys. Lett. 91, 201922 (2007).
Warren, W. L., Kanicki, J., Rong, F. C. & Poindexter, E. H. Paramagnetic point defects in amorphous silicon dioxide and amorphous silicon nitride thin films. J. Electrochem. Soc. 139, 880–889 (1992).
Maeda, M. & Arita, Y. Electrical properties and their thermal stability for silicon nitride films prepared by plasma-enhanced deposition. J. Appl. Phys. 53, 6852–6856 (1982).
McPherson, J. W. & Mogul, H. C. Underlying physics of the thermochemical E model in describing low-field time-dependent dielectric breakdown in SiO2 thin films. J. Appl. Phys. 84, 1513–1523 (1998).
McPherson, J. W., Khamankar, R. B. & Shanware, A. Complementary model for intrinsic time-dependent dielectric breakdown in SiO2 dielectrics. J. Appl. Phys. 88, 5351–5359 (2000).
Wang, Y. f. et al. Resistive switching mechanism in silicon highly rich SiOx (x<0.75) films based on silicon dangling bonds percolation model. Appl. Phys. Lett. 102, 042103 (2013).
Mead, C. A. Electron transport mechanisms in thin insulating films. Phys. Rev. 128, 2088–2093 (1962).
Sze, S. M. Current transport and maximum dielectric strength of silicon nitride films. J. Appl. Phys. 38, 2951–2956 (1967).
Robertson, J. & Powell, M. J. Gap states in silicon nitride. Appl. Phys. Lett. 44, 415–417 (1984).
Houng, M. P., Wang, Y. H. & Chang, W. J. Current transport mechanism in trapped oxides: A generalized trap-assisted tunneling model. J. Appl. Phys. 86, 1488–1491 (1999).
Suzuki, E., Schroder, D. K. & Hayashi, Y. Carrier conduction in ultrathin nitrided oxide films. J. Appl. Phys. 60, 3616–3621 (1986).
Cheng, X. R., Cheng, Y. C. & Liu, B. Y. Nitridation-enhanced conductivity behavior and current transport mechanism in thin thermally nitrided SiO2 . J. Appl. Phys. 63, 797–802 (1988).
Sathaiya, D. M. & Karmalkar S. Thermionic trap-assisted tunneling model and its application to leakage current in nitrided oxides and AlGaN/GaN high electron mobility transistors. J. Appl. Phys. 99, 093701 (2006).
Mo, C., Zhang, L., Xie, C., & Wang, T. Luminescence of nanometer-sized amorphous silicon nitride solids. J. Appl. Phys. 73, 5185 (1993).
Acknowledgements
This work was supported by the State Key Development Program for Basic Research of China (Grant Nos. 2010CB934402 and 2013CB632101), the National Nature Science Foundation of China (Grant Nos. 61071008, 61376004 and 11374153), the Fundamental Research Funds for the Central Universities (Grant Nos. 1095021030, 1116021004 and 1114021005), the Research Fund for the Doctoral Program of Higher Education of China (Grant No. 20130091110024) and a Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions.
Author information
Authors and Affiliations
Contributions
X.F.J. designed and performed the experiments. X.F.J. and Z.Y.M. analyzed the results and wrote the manuscript. J.X., K.J.C., L.X. and F.D. discussed the work in depth and made suggestions for this work. W.L. and X.F.H. provided assistance with the experiments. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Jiang, X., Ma, Z., Xu, J. et al. a-SiNx:H-based ultra-low power resistive random access memory with tunable Si dangling bond conduction paths. Sci Rep 5, 15762 (2015). https://doi.org/10.1038/srep15762
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep15762
- Springer Nature Limited
This article is cited by
-
High Performance All Nonmetal SiNx Resistive Random Access Memory with Strong Process Dependence
Scientific Reports (2020)
-
The use of MACE technique on amorphous silicon-rich silicon nitride thin films for the formation of spherical silica nanoparticles
Journal of Materials Science (2019)
-
Power- and Low-Resistance-State-Dependent, Bipolar Reset-Switching Transitions in SiN-Based Resistive Random-Access Memory
Nanoscale Research Letters (2016)