Abstract
In this work, CoMoO4@NiMoO4·xH2O core-shell heterostructure electrode is directly grown on carbon fabric (CF) via a feasible hydrothermal procedure with CoMoO4 nanowires (NWs) as the core and NiMoO4 nanosheets (NSs) as the shell. This core-shell heterostructure could provide fast ion and electron transfer, a large number of active sites, and good strain accommodation. As a result, the CoMoO4@NiMoO4·xH2O electrode yields high-capacitance performance with a high specific capacitance of 1582 F g−1, good cycling stability with the capacitance retention of 97.1% after 3000 cycles and good rate capability. The electrode also shows excellent mechanical flexibility. Also, a flexible Fe2O3 nanorods/CF electrode with enhanced electrochemical performance was prepared. A solid-state asymmetric supercapacitor device is successfully fabricated by using flexible CoMoO4@NiMoO4·xH2O as the positive electrode and Fe2O3 as the negative electrode. The asymmetric supercapacitor with a maximum voltage of 1.6 V demonstrates high specific energy (41.8 Wh kg−1 at 700 W kg−1), high power density (12000 W kg−1 at 26.7 Wh kg−1), and excellent cycle ability with the capacitance retention of 89.3% after 5000 cycles (at the current density of 3A g−1).
Similar content being viewed by others
Introduction
In recent years, smart electronic devices have attracted tremendous research interest due to their unique features and potential applications in the next generation wearable electronic devices1,2,3. However, meeting the increasing demand of future emerging markets are lightweight, solid state, and flexible energy devices4,5,6,7. Among them, supercapacitors (SCs) are considered as promising candidates that can offer long cycle life, high power density, fast charge/discharge rates and safety8,9,10,11,12,13,14,15. Unfortunately, the energy densities of supercapacitors are still unsatisfactory, which seriously limit their practical applications. According to the energy density equation: E = 1/2 CV2 16,17, the energy density (E) can be enhanced by improving the specific capacitance (C) and/or the operating potential window (V). Therefore, an effective alternative approach to increase the energy density is to fabricate the asymmetric supercapacitors (ASC). It can make full use of the different potential windows of the two electrodes to provide a maximum operation voltage in the cell system, accordingly resulting in a greatly enhanced specific capacitance and significantly improved energy density.
Recently, a variety of materials have been explored for possible applications as the cathode in asymmetric supercapacitors, such as transition metal oxides, metal hydroxides and conducting polymer18,19,20,21,22,23. In particular, metal molybdates are particularly attractive as an important family of inorganic materials24.
Previous studies show that CoMoO4 has excellent rate capability and cyclic properties. However, its specific capacitance is lower than that of most reported oxides25. Interestingly, NiMoO4 possesses a high specific capacitance, ascribed to the high electrochemical activity of the nickel ion, but its rate capability is inferior. This encouraged some researchers to fabricate a CoMoO4 and NiMoO4 based composite with a unique nanostructure, which will combine the advantages of both CoMoO4 and NiMoO4. For example, Liu et al. synthesized CoMoO4-NiMoO4·xH2O bundles on Ni foam by a chemical co-precipitation method. The mixed bundles showed a capacitance of 1039F g−1 at a current density of 1A g−1 and excellent rate capability, superior to single-phase NiMoO4·xH2O26. Yin et al. reported active carbon and hierarchical nanosheet-based CoMoO4-NiMoO4 nanotubes as negative and positive electrodes of the supercapacitor, respectively. This electrode delivered high specific energy of 33 W h kg−1 and high power density of 6000 W kg−1 27. Zhang and his coworkers showed NiMoO4@CoMoO4 hierarchical nanospheres and explored the symmetric capacitor with the potential window of 1.5 V28.
The above reports indicate that the composite materials with special structures show better performance than those of the individual component. Therefore, this motivated us to design and fabricate an elegant CoMoO4 and NiMoO4 core-shell heterostructured electrode with a novel nanostructure, which might combine the merits of both high specific capacitance originating from NiMoO4 and excellent rate capability provided by CoMoO4, together with the well-designed architecture to improve the performance.
At present, carbonaceous materials are still the most mainly used anode materials, such as activated carbon, grapheme, and nitrogen-doped carbons29,30,31,32. However, carbonaceous materials show quite small specific capacitances (100–250F g−1) compared with pseudocapacitive anode33,34,35,36. Among the reported pseudocapacitive anode materials, Fe2O3 exhibits many advantages such as low cost, environmental friendliness and safety37,38,39,40. Moreover, Fe2O3-based electrode shows higher specific capacitance and wider voltage window compared with the carbonaceous materials. However, the intrinsic poor conductivity and aggregated morphology of Fe2O3-based electrodes restrict their electrochemical performance. An effective method is to synthesize the binder-free electrodes, which directly grown on the conductive substrates. Hence, the poor conductivity of the Fe2O3 electrode is no longer a problem. And the nanostructures facilitate the electrolyte to penetrate the inner part of electrodes and benefits for improving the utilization of their pseudocapacitance41.
In this work, we report the flexible CoMoO4@NiMoO4·xH2O core-shell heterostructures cathode and Fe2O3 nanorods (NWs) anode directly grown on the carbon fabric for high-performance asymmetric solid-state supercapacitors. As a cathode material, the flexible 3D networked CoMoO4@NiMoO4·xH2O core-shell heterostructures electrode exhibits excellent electrochemical performance in contrast to that of individual flexible CoMoO4 and NiMoO4·xH2O. It shows a high capacitance of 1582F g−1, high rate performance, as well as an outstanding long-term cycling ability with the capacitance retention of 97.1% after 3000 cycles at 1A g−1. Even at the current density of 5A g−1, the capacitance still can be retained up to 93.2% after 10000 cycles. As an anode material, the flexible Fe2O3 nanorods electrode exhibits the specific capacitance of 516.7F g−1 at the current density of 1A g−1, which is much higher than carbonaceous materials. Even at a high current density of 15A g−1, it still retains a specific capacitance of 312.5F g−1. In addition, since the negative potential window for the Fe2O3 nanorods is 0~−1.2 V, the Fe2O3 nanorods anode and the CoMoO4@NiMoO4·xH2O cathode can fully utilize their large theoretical pseudocapacitance in the corresponding complementary potential windows. Therefore, the perfect matching between CoMoO4@NiMoO4·xH2O and Fe2O3 nanorods is quite obvious. The solid-state asymmetric CoMoO4@NiMoO4·xH2O//Fe2O3 supercapacitor device with a maximum voltage of 1.6 V shows high specific energy (41.8 Wh kg−1 at 700 W kg−1), power density (12000 W kg−1 at 26.7 Wh kg−1) and excellent cycling stability.
Results and Discussion
The schematic illustration for the preparation of the CoMoO4@NiMoO4·xH2O core-shell heterostructure grown on carbon fabric is presented in Fig. 1. CoMoO4@NiMoO4·xH2O composites were prepared by a simple template-free hydrothermal process coupled with a calcination treatment. The formation schematic illustration of CoMoO4@NiMoO4·xH2O composites grown on carbon fiber (CF) was presented in Fig. 1. The preparation process mainly involves two steps. In the first step, a light purple CoMoO4 precursor is generated on the carbon cloth surface by hydrothermal reaction. After heat treatment, the dark purple CoMoO4 NWs were supported on the carbon cloth. In the second step, CoMoO4 NWs were immersed into the light green precursor solution of NiMoO4 for further hydrothermal process and heat treatment. Finally, flexible CoMoO4@NiMoO4·xH2O composites were formed on the CF. Optical images of the as prepared electrodes are shown in Fig. S1. The morphologies and microstructures of the as prepared products were investigated and the results are shown in Fig. 2. The SEM image in Fig. 2a shows the carbon fabric composed of crossed carbon fibers with the average diameter of about 15 μm. The morphology of the CoMoO4 NWs is shown in Fig. 2b, which indicates the products with high density are uniformly distributed on the fibers of the CF. The CoMoO4 NWs have an average diameter of 100 nm and length of around 1.5 μm. Figure 2c reveals the SEM image of NiMoO4·xH2O NSs which possesses a nanostructure composed of nanosheets with an average thickness of 10 nm. These nanosheets are interconnected with each other and contain a highly porous network structure. Figure 2d indicates the final product, the networked CoMoO4@NiMoO4·xH2O nanostructures are successfully produced on the carbon fibers on a large scale. Figure 2e,f clearly demonstrates that NiMoO4·xH2O NSs are homogeneously covered on the whole surfaces of CoMoO4 NWs, forming an interconnected and a highly porous 3D morphology, which may offer not only 3D networks for fast electron transportation, but also spaces critical for ion diffusion. The experiments with different reaction times changed from 1 h to 10 h were further researched to explore the composite structure as shown in Fig. 2g–i. When the reaction time is 1 h, the morphology seems like nanowires without NiMoO4 NSs deposition on CoMoO4 NWs. When the reaction time up to 5 h, it can be found that the whole CoMoO4 layer was covered by NiMoO4 nanosheets and the whole CoMoO4 nanowires arrays’ morphology is remained. Further changing the reaction time to 10 h, the whole CoMoO4 layer was covered by much more NiMoO4 nanosheets has been deposited with an obvious change in morphology. The morphology is core-shell structure with much more NiMoO4 nanosheets deposited on CoMoO4 nanowires arrays. TEM images with different magnifications have been conducted (Fig. S2). It further confirmed that the CoMoO4 layer was covered by much more NiMoO4 nanosheets has been deposited. Brunauer-Emmett-Teller (BET) analysis results show that the specific surface area of CoMoO4@NiMoO4·xH2O is 100.79 m2 g−1, which is much higher in contrast to that of CoMoO4 NWs (37.93 m2 g−1) and NiMoO4·xH2O NSs (79.37 m2 g−1) (Fig. S3). This core-shell configuration can provide a higher surface area, which is mainly attributed to the interconnected NiMoO4·xH2O NSs and the aligned CoMoO4 NWs scaffold that creating a 3D structure and highly porous surface morphology. Such configuration is of great importance to promote electrolytes accessibility and increase the utilization of the active materials. The whole zone of Fig. 2f is selected to research the SEM mapping (Fig. S4). It can be clearly seen that only elements of O, Co, Ni and Mo could be found in CoMoO4@NiMoO4·xH2O.
The phase structures of the as-prepared products were analyzed by X-ray diffraction. As shown in Fig. S5, NiMoO4·xH2O and CoMoO4 are in good agreement with the standard patterns for NiMoO4·xH2O (PDF, card no. 13-0128) and monoclinic CoMoO4 (PDF, card no. 21-0868), respectively. In addition, several weak diffraction peaks attributed to the impurity phase of NiMoO4 (PDF, card no. 12-0348) and CoMoO6 ·0.9H2O (PDF, card no. 14-1186) are found. The results are consistent with the previous research42. The XRD pattern of CoMoO4@NiMoO4·xH2O contains the diffraction peaks of both NiMoO4·xH2O and CoMoO4, indicating the presence of both phases.
The microstructure of the as-prepared products was further characterized by TEM and SAED. Figure 3a depicts the low-magnification TEM image of CoMoO4 NWs with the diameter of about 100 nm. The measured lattice spacing of 0.67 nm in HRTEM image (Fig. 3b) is corresponding to the (001) planes of monoclinic CoMoO4. Figure 3c shows the corresponding selected area electron diffraction (SAED) pattern. The SAED pattern of the CoMoO4 shows a set of well-defined spots, indicative of its single-crystallinity property. The diffraction rings can be readily indexed to the (001), and (020) planes of the CoMoO4 phase, which is consistent with the above XRD result. TEM images in Fig. 3d confirm the core-shell structure with the CoMoO4 NWs as the core parts and NiMoO4·xH2O NSs as the shell layers. HRTEM image (Fig. 3e) reveals the interplanar spacing of 0.43 nm, 0.40 nm, and 0.32 nm, corresponding to those of 4.30 Å, 4.06 Å, and 3.26 Å given in the PDF 13-0128 in the standard files of NiMoO4·xH2O43,44. The SAED pattern (Fig. 3f) indicates the polycrystalline nature of CoMoO4@NiMoO4·xH2O, and the diffraction rings can be readily indexed to the (020), (220) and (040) planes of the NiMoO4 phase, which is consistent with the above XRD result. TEM images and elemental mapping of the CoMoO4 and CoMoO4@NiMoO4·xH2O (Fig. S6) further indicate that the elements of Co, Mo, O and Ni are distributed uniformly on the core and the shell.
The electrochemical storage application of as-prepared products was evaluated by testing them as electrodes for supercapacitors in a three-electrode configuration. We firstly compared the cyclic voltammetric (CV) curves of CF, CoMoO4 NWs, NiMoO4·xH2O NSs, and CoMoO4@NiMoO4·xH2O electrodes at the scan rate of 5 mV s−1 (Fig. 4a). The results indicate that the contribution of the CF substrate is tiny compared with the other three electrodes. The current density and enclosed CV curve area of the CoMoO4@NiMoO4·xH2O are much larger than CoMoO4 NWs and NiMoO4·xH2O NSs, due to the networked porous hybrid structural effect from the CoMoO4 NWs and ultrathin NiMoO4·xH2O NSs. Figure 4b further describes the CV characteristics of the CoMoO4@NiMoO4·xH2O electrode at different scan rates. Each CV curves consist of a pair of redox peaks, indicating pseudocapacitive behavior of CoMoO4@NiMoO4·xH2O. The Faradic reactions correspond to the redox peaks for CoMoO4 NWs45,46,47 and NiMoO4·xH2O NSs48,49 are as follows:
The electrochemical capacitance of CoMoO4@NiMoO4·xH2O is attributed to the quasi reversible electron transfer process that mainly involves the Co2+/Co3+ and the Ni2+/Ni3+ redox couple, and probably mediated by the OH− ions in the alkaline electrolyte. The main function of Mo element is to improve the conductivity of metal molybdates and achieve the enhanced electrochemical capacitance26,46,47. The peak current increases linearly with the increase of the scan rate, which suggests that the kinetics of the interfacial Faradic redox reactions and the rates of electronic and ionic transport are rapid enough in the present scan rates. The shape of the CV curves is not significantly influenced by the increase of the scan rates, which indicates the improved mass transportation and electron conduction in the host materials. Figure 4c shows the galvanostatic charge-discharge (GCD) curves of the CoMoO4@NiMoO4·xH2O electrode within a potential range of 0 to 0.5 V at various current densities. The corresponding comparative CV and GCD curves of CoMoO4 NWs, and NiMoO4·xH2O NSs are shown in Fig. S7. The specific capacitances of the three electrodes derived from the discharging curves at different current densities are compared and shown in Fig. 4d. The specific capacitances of CoMoO4@NiMoO4·xH2O calculated according to the Equation (6) are 1582, 1470, 1380, 1248, 1160, and 1050F g−1 at the current densities of 1, 3, 5, 8, 10, and 15A g−1, much higher than those of the pristine CoMoO4 NWs and NiMoO4·xH2O NSs. This core-shell CoMoO4@NiMoO4·xH2O heterostructure shows a rate capability of 64% with a high specific capacitance of 1582F g−1 at a current density of 1A g−1 and 1050F g−1 at a current density of 15A g−1. The CoMoO4 NWs exhibits a good rate capability of 68.2% but a low specific capacitance of 396F g−1 at a current density of 1A g−1 and 270F g−1 at a current density of 15A g−1. The NiMoO4·xH2O NSs shows a high specific capacitance of 1108F g−1 at the current density of 1A g−1, but only 37.9% of this value remained at a high current density of 15A g−1, indicating relatively weaker rate capability compared with CoMoO4 NWs. Nevertheless, the CoMoO4@NiMoO4·xH2O combines the advantages of the good rate capability of CoMoO4 and the high specific capacitance of NiMoO4·xH2O. The cyclic stability of supercapacitors is another critical issue in practical use. Cyclic tests for the three electrodes were carried out for over 3000 cycles at 1A g−1. Figure 4e presents that the CoMoO4@NiMoO4·xH2O electrode exhibits an excellent long-term stability with only 2.9% capacitance loss after 3000 cycles, which is much better than 6.1% capacitance loss for the CoMoO4 NWs and 30% capacitance loss for the NiMoO4·xH2O NSs electrode after the same cycles. The charge/discharge curves of the CoMoO4@NiMoO4·xH2O electrode obtained at the last cycle are remained much the same as the ones obtained in the first cycle (Fig. S8). Furthermore, tests were also carried out for up to 10000 cycles at a current density of 5A g−1. As shown in Fig. S9, the CoMoO4@NiMoO4·xH2O electrode exhibits excellent long-term stability with 93.2% capacitance retention. In addition, the charge-discharge curves shape the insets in Fig. S9 are still keeping quite stable after 10000 cycles, indicating the CoMoO4@NiMoO4·xH2O electrode has good cycle performance. Figure S10 shows SEM images of the CoMoO4@NiMoO4·xH2O electrode before and after 10000 cycles. It shows that a few of the CoMoO4@NiMoO4·xH2O aggregate compared with that of the as-prepared CoMoO4@NiMoO4·xH2O after 10000 cycles.
To further insight into the influence of electrochemical impedance to the electrode for supercapacitors, electrochemical impedance spectroscopy (EIS) of the CoMoO4 NWs, the NiMoO4·xH2O NSs and the CoMoO4@NiMoO4·xH2O electrodes were measured in the frequency range from 0.01 Hz to 100 kHz at an open circuit potential with a superimposed 5 mV sinusoidal voltage (Fig. 4f). The three electrodes indicate similar two forms with a semicircle at the high frequency region and a straight line at the low frequency. At the high frequency, the intersection of the curve at the real part shows the resistance of the electrochemical system (Rs) and the semicircle diameter shows the charge-transfer resistance (Rct). Rs includes the ionic resistance of electrolyte, inherent resistance of the electroactive material, and contact resistance at the interface between electrode and electrolyte50. The semicircle of the Nyquist plot corresponds to the Faradic reactions and its diameter represents the interfacial Rct in the high frequency. The inset in Fig. 4f shows an equivalent circuit used to match with the EIS curves to measure Rs and Rct. Zw and CPE are the Warburg impendence reflected by the straight line in the low frequency51,52. As expected, CoMoO4@NiMoO4·xH2O shows the lower internal resistances (Rs) 0.62 Ω compared with CoMoO4 (2.76 Ω) and NiMoO4·xH2O (6.15 Ω), indicative of improved electrical conductivity. The CoMoO4@NiMoO4·xH2O electrode also demonstrates lower charge-transfer resistance 1.86 Ω than CoMoO4 (5.24 Ω) and NiMoO4·xH2O (8.85 Ω) as shown in Fig. 4f. Moreover, the CoMoO4@NiMoO4·xH2O electrode also demonstrates the smallest diffusive resistance. The above results show that the combination of fast ion diffusion as well as low electro-transfer resistance is also responsible for the enhanced electrochemical performance of the CoMoO4 and NiMoO4·xH2O core-shell electrode. This is mainly caused by the networked porous core-shell structure with larger specific surface area, resulting in enhanced utilization of the electrode materials and facilitated supply of OH− to the electrode53. It is believed that the hybrid structure with low diffusion and electron-transfer resistances are beneficial to the excellent supercapacitor performance.
Figure 5a further reveals the current density dependence of the cycling performance of the CoMoO4@NiMoO4·xH2O electrode. A stable specific capacitance of about 1050F g−1 can be found in the first 100 cycles at the current density of 15A g−1. Changing the current density successively, the hybrid electrode still exhibits stable capacitance in different forms. When changing the current density back to 15A g−1, the electrode can fully recover the specific capacitance of 1050F g−1. These results further indicate the CoMoO4@NiMoO4·xH2O electrode has excellent stabilities and rate performance.
To explore the flexibility of the electrode, we compared the GCD curves and cyclic performance of the electrode under flat and bending for electrochemical test at a current density of 3A g−1. As indicated in Fig. 5b and c, the GCD profiles confirm the negligible attenuation of charge-discharge interval of the bent electrode compared to its flat state. Figure 5c shows the corresponding specific capacitance variation tendency under a bent state compared to its natural state after 3000 cycles. The specific capacitance retention for the flat one is 99.3% and the other two bent forms are still keeping 98.9% and 98.5% capacitance, respectively. The corresponding GCD curves of the first ten cycles for the three forms show no obvious changes (the insets). The results further confirm the electrode is mechanically robust.
The high specific capacitance of the CoMoO4@NiMoO4 core-shell heterostructures electrode are impressive values when compared to those of many previously reported CoMoO4 or NiMoO4 oxides based electrodes, as shown in Table S1. The above results reveal high specific capacity, excellent cycling stability, outstanding rate capability, and mechanically flexibility of the CoMoO4@NiMoO4·xH2O core-shell electrode. It mainly attribute to the 3D networked heterostructure and a direct growth on the flexible conductive carbon fabric substrate. As schematically demonstrated in Fig. 1, first, carbon fabric as conductive substrate has good electrical conductivity, high porosity and excellent mechanical flexibility. This leads to the fact that electrons can transport more efficiently during charge-discharge processes and therefore large improvement in specific capacitance. Second, the unique core-shell hierarchical structure has an increased portion of exposed surface, which provides more active sites for ions and electrons access to the surface of the electrode. The porosity of the surface further shortens the diffusion paths for ions so that accelerate the redox reaction to take place and enhance the rate capability. Thirdly, this 3D networked core-shell nanostructures on carbon fabric is a stale architecture with excellent mechanical robust and flexibility, which can improve the cycling stability evidently during long-term cycling. Finally, the CoMoO4 and NiMoO4·xH2O are good pseudocapacitor materials due to their multiple oxidation states for reversible Faradaic reactions. The heterostructure allows synergistic contributions from the CoMoO4 with excellent cycling ability and good rate capability, and NiMoO4·xH2O with high specific capacitance.
In order to research the practical application of the as-prepared electrodes, flexible solid-state asymmetric supercapacitor device was assembled by using CoMoO4@NiMoO4·xH2O core-shell heterostructures as the cathode and the Fe2O3 NRs as anode, respectively. Before assembling the asymmetric supercapacitor device, we firstly researched the microstructure and electrochemical properties of Fe2O3 NRs. Figure S11a shows SEM image of the as synthesized Fe2O3 NRs with an average diameter of 100 nm and length of approximate 200 nm directly attached to the CF substrate. The phase structures of the as-prepared Fe2O3 NRs were analyzed by X-ray diffraction. Figure S11b indicates the as-prepared Fe2O3 is in good agreement with the standard pattern for rhombohedral Fe2O3 (PDF, card no. 33-0664). To investigate the electrochemical performance of the Fe2O3 nanorods, we tested the CV curves at different scan rates in a three-electrode measurement (Fig. S12a). Figure S12b exhibits the GCD curves at different current densities with the potential window 0~−1.2 V and the specific capacitances are calculated from the GCD curves. At the current density of 1A g−1, the Fe2O3 nanorods exhibit the specific capacitance of 516.7F g−1. Even at a high current density of 15A g−1, it can still retain a specific capacitance of 312.5F g−1. The unique 1D nanostructure is quite beneficial for the rapid electrolyte flow to more accessible electrochemical active sites, enhancing the capacitive performance as a result. The electrochemical performance of the Fe2O3 NRs in the wide negative potential window and high specific capacitance are favorable for using as an anode material.
Based upon the above experimental results and discussions, the perfect matching between the flexible CoMoO4@NiMoO4·xH2O and Fe2O3 NRs electrodes is quite obvious. The Fe2O3 NRs anode and the CoMoO4@NiMoO4·xH2O cathode can fully utilize their large theoretical pseudocapacitance in the corresponding complementary potential windows. As shown in Fig. S13, they exhibit large pseudocapacitance in the exactly complementary potential windows. The charge balances for the positive and negative electrodes have been calculated in the supporting information.
Supercapacitors based on CoMoO4@NiMoO4·xH2O//Fe2O3 exhibit superb device characteristics for flexible energy storage applications. Firstly, a CV measurement is performed in a two-electrode system. Figure 6a shows the CV curves of CoMoO4@NiMoO4·xH2O//Fe2O3 ACS device collected at different potential voltages at a scan rate of 5 mV s−1. The stable potential window of the ASC can be extended to as large as 1.6 V without obvious polarization curves. Figure 6b shows the CV curves of the optimized CoMoO4@NiMoO4·xH2O//Fe2O3 ASC device collected at various scan rates with the potential window 0~1.6 V. All the curves show obvious pseudocapacitance features with redox peaks within 0~1.6 V, which can be attributed to the cathode and anode materials with the faradaic reactions. To further evaluate the electrochemical performance of the asymmetric cell, GCD tests of the solid-state asymmetric supercapacitor at various current densities are performed. As shown in Fig. 6c, all the charge-discharge curves show nearly symmetric behavior, confirming the excellent capacitive behavior of the device over the entire voltage range. The total specific capacitance (Ct), which is calculated based on the total mass of active materials in the two electrodes, reaches 153.6F g−1 at the current density of 1A g−1 and still can retain 75F g−1 at a high current density of 15A g−1 (Fig. S14). Figure S14 also shows a little decrease of the specific capacitance under large current density, implying a high rate performance. The cycling life tests over 5000 cycles for CoMoO4@NiMoO4·xH2O//Fe2O3 were carried out at 3A g−1. As depicted in Fig. 6d, the CoMoO4@NiMoO4·xH2O//Fe2O3 ASC device exhibits a long-term electrochemical stability, and the capacitance retention after 5000 cycles is 84%. The charge-discharge curve keeps quite symmetric after 5000 cycles, indicating that there are no significant structural changes of the CoMoO4@NiMoO4·xH2O//Fe2O3 ASC device during the charge-discharge processes (Fig. 6d). In order to further confirm the reliability of the cycle life of the device, the cycle number of the positive electrode CoMoO4@NiMoO4·xH2O and negative electrode Fe2O3 also have been added (as shown in Fig. S15) to 5000 cycles at a current density of 3A g−1. The results indicate that the positive electrode and negative electrode have better cycle performance. The flexibility of the CoMoO4@NiMoO4·xH2O//Fe2O3 ACS device was performed under bending for 0°, 90° and 180° with the electrochemical test at the current density of 3A g−1. The compared GCD curves are indicated in Fig. 6e. The GCD profiles have almost no obvious changes, confirming that the CoMoO4@NiMoO4·xH2O//Fe2O3 ACS device has a remarkable mechanical flexibility. The excellent mechanical robustness and intimate interfacial contact for the multiple components demonstrate their promising utility as a flexible energy storage device.
To further demonstrate the energy and power performance of the flexible solid-state supercapacitor, Ragone plot was described based on the charge-discharge data. As shown in Fig. 6f, the energy density and power density of CoMoO4@NiMoO4·xH2O//Fe2O3 were calculated according to the Equations (7) and (8) the maximum specific energy as high as 41.8 Wh kg−1 is obtained at a current density of 1A g−1 with power density of 900 W kg−1 under the operating voltage of 1.6 V. The flexible ASC device possesses a maximum power density of 12000 W kg−1 at the current density of 15A g−1 with specific energy of 26.7 Wh kg−1. With an operating potential of 1.6 V, we achieve a much higher specific energy of for our asymmetric supercapacitors compared with the previous reported work54,55,56,57,58,59.
Conclusions
In summary, we have designed and synthesized the flexible CoMoO4@NiMoO4·xH2O core-shell heterostructure cathode and Fe2O3 nanorods anode directly on carbon fabric. This 3D networked CoMoO4@NiMoO4·xH2O core-shell heterostructure facilitates fast ion diffusion and electron transfer at the electrode/electrolyte interface. The CoMoO4@NiMoO4·xH2O core-shell heterostructure allow the synergistic contribution of both materials leading to a better electrochemical performance. As a positive material, it exhibits excellent supercapacitor performance with a high capacitance, desirable rate performance and excellent cycling stability. Furthermore, as a negative material, Fe2O3 NWs show high specific capacitance and wide potential window compared with carbon materials. Flexible solid-state CoMoO4@NiMoO4·xH2O//Fe2O3 asymmetric supercapacitor is assembled by using CoMoO4@NiMoO4·xH2O as positive and Fe2O3 as negative electrodes, respectively. The flexible solid-state asymmetric supercapacitor with a maximum voltage of 1.6 V shows high specific energy, high power density and excellent cycling stability. Such a flexible solid-state asymmetric supercapacitor with superior performance is expected to be a promising candidate for application in energy storage devices.
Experimental details
Synthesis of the CoMoO4 nanowire (NW) arrays on carbon fabric (CF)
Prior to the synthesis, commercial CF pieces (1 cm × 1 cm × 0.1 cm in size) were firstly ultrasonic-treated in acetone, ethanol mixture and ultrapure water, respectively. Then they were dipped in 6 M nitric acid solution and rinsed successively by ultrapure water, followed by drying in an oven at 60 °C for 5 h.
For the preparation of the CoMoO4 nanowires, 1.46 g of Co(NO3)2·6H2O and 1.21 g of Na2MoO4·7H2O were dissolved in 50 ml of ultrapure water under constant magnetic stirring to form a uniform light purple solution. The washed carbon fabric substrates and the light purple solution were together transferred into a 100 ml Teflon-lined stainless steel autoclave and reacted at 180 °C for 12 h. When the autoclave was cooled down to room temperature naturally, the resulting products were collected and rinsed with ultrapure water for several times. Then the products were dried in an oven at 60 °C for 12 h. Finally, to obtain CoMoO4 NWs, the dried samples were further annealed at 300 °C for 1 h in air.
Preparation of the NiMoO4·xH2O nanosheets (NSs) on carbon fabric
In a typical procedure, 0.25 g Ni(CH3COO)2·4H2O, 0.2 g ammonium molybdate tetrahydrate, and 0.24 g CO(NH2)2 were dissolved in 40 ml of ultrapure water and stirred constantly for 0.5 h. The solution and the cleaned CF were transferred into a 100 ml Teflon-lined stainless steel autoclave which was heated to 160 °C for 10 h. After the autoclave was cooled down to ambient, the samples were washed with ultrapure water and dried at 60 °C for 12 h. Finally, the samples were annealed at 400 °C in air for 3 h to obtain NiMoO4·xH2O NSs deposited directly on CF.
Preparation of the CoMoO4@NiMoO4·xH2O heterostructures
The as obtained CoMoO4 NWs on CF were immersed into the precursor solution of NiMoO4. Then they were together transferred to a 100 ml Teflon-lined stainless steel autoclave. The autoclave was sealed and maintained at 160 °C for 10 h and then cooled down to ambient. The as prepared CoMoO4@NiMoO4·xH2O core-shell heterostructures were rinsed and dried at 60 °C for 12 h. Finally, the samples were annealed at 400 °C in air for 3 h to obtain CoMoO4@NiMoO4 deposited on CF.
Preparation of the Fe2O3 nanorods (NRs) on carbon fabric
The Fe2O3 NRs were prepared as follows: 1.08 g FeCl3·6H2O and 0.56 g Na2SO4 were dissolved in 80 ml of ultrapure water and constantly stirred for 0.5 h. The mixed solution and the cleaned CF were transferred together into a 100 ml Teflon-lined stainless steel autoclave which was heated to 120 °C for 8 h. After the autoclave was cooled to ambient naturally, the samples washed with distilled water and dried at 60 °C for 12 h. Finally, the samples were annealed at 400 °C in air for 3 h to obtain Fe2O3 NRs. Na2SO4 was used as the structure-directing agent to facilitate the uniform growth of 1D structures60.
Materials Characterizations
The microstructure and morphology were characterized by Scanning electron microscopy (SEM, Hitachi S-4800, at an acceleration voltage of 20 kV) and Transmission electron microscopy (TEM, JEOL JEM-2010). The phase structures of the as-prepared products were characterized by X-ray diffraction (XRD, Rigaku D/max-rB, Cu Kα radiation, λ = 0.1542 nm, 40 kV, 100 mA). Brunauer-Emmett-Teller (BET) analysis was carried out to evaluate the surface area and pore size distribution of the as prepared products. Surface Area Analyzer (NOVA2000E) was used to measure N2-sorption isotherm.
Electrochemical measurements
The electrochemical measurements were firstly conducted in a three-electrode form. CoMoO4@NiMoO4·xH2O/CF electrodes were used as the working electrode. A platinum foil (1 cm × 4 cm) acted as the counter electrode and a saturated calomel electrode (SCE) acted as the reference electrode. 2.0 M KOH aqueous solution served as the electrolyte. The electrochemical measurements were carried out on a CHI 660 C electrochemistry workstation (Shanghai, China). Cyclic voltammetry (CV) tests were conducted in a potential range of −0.2~0.6 V (versus SCE) at different sweep rates of 5~100 mV s−1. The constant current charge/discharge tests were carried out at various current densities within a potential range of 0~0.5 V (versus SCE), and the cycling behavior was characterized up to 3000 cycles (at a current density of 3A g−1) and 10000 cycles (at a current density of 5A g−1), respectively. Electrochemical impedance spectroscopy (EIS) was performed to determine the capacitive performance at open circuit voltage with a frequency range of 0.01~105 Hz. The CV curves and charge-discharge curves of Fe2O3 NRs were also tested. These electrochemical measurements were performed in a three-electrode system.
Assembly of the solid-state asymmetric supercapacitor (ASC)
Solid-state ASC was fabricated using CoMoO4@NiMoO4·xH2O electrode as the positive electrode and Fe2O3 NRs electrode as the negative electrode. The CoMoO4@NiMoO4·xH2O electrode was resized to 1.0 cm × 1.0 cm in size with an average mass loading of 1.8 mg cm−2. The Fe2O3 NRs electrode was resized the same size with the mass loading of 2.3 mg cm−2. Then, the polyvinyl alcohol (PVA)/KOH gel electrolyte was prepared by mixing as-prepared 6 g PVA with 5.6 g KOH in 50 ml of deionized water and heated at 80 °C under stirring for 3 h until it became homogeneously clear. The electrodes and the separator were soaked in the gel for 5 min, then taken out from the gel, and assembled together. The device was placed in the air for 24 h and became solid. Afterward, the ASC device was assembled by sandwiching PVA/KOH gel electrolyte film between the Fe2O3/CF and CoMoO4@NiMoO4·xH2O/CF electrodes under mechanical stress. The specific capacitance, energy density, and power density of the ASC were all calculated based on the total mass of both negative and positive electrodes excluding the weights of current collectors. The thickness of the as-prepared solid-state ASC was measured to be about 1.15~1.34 mm. All electrochemical tests of the ASC device were performed in a two electrode configuration at ambient temperature.
The following equations were used to calculate the specific capacitance Cs (F g−1), specific energy E (Wh kg−1) and power density P (W kg−1):
where I (A) represents the discharge current, Δt(s) is the discharge time, ΔV (V) is the potential drop during discharge process, m (g) is the mass of the active materials, S is the enclosed area of the discharge curve and coordinate axis, and U (V) is the potential window.
Additional Information
How to cite this article: Wang, J. et al. Assembly of flexible CoMoO4@NiMoO4·xH2O and Fe2O3 electrodes for solid-state asymmetric supercapacitors. Sci. Rep. 7, 41088; doi: 10.1038/srep41088 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Peng, X. et al. Two dimensional nanomaterials for flexible supercapacitors. Chemical Society Reviews 43, 3303–3323 (2014).
Shao, Y. et al. Graphene-based materials for flexible supercapacitors. Chemical Society Reviews 44, 3639–3665 (2015).
Wang, Z. R. et al. Transferable and flexible nanorod-assembled TiO2 cloths for dye-sensitized solar cells, photodetectors, and photocatalysts. ACS Nano 5, 8412–8419 (2011).
Chang, Z. et al. Hybrid system for rechargeable magnesium battery with high energy density. Sci. Rep. 5, 11931 (2015).
Yang, L. et al. Hierarchical network architectures of carbon fiber paper supported cobalt oxide nanonet for high-capacity pseudocapacitors. Nano Lett. 12, 321–325 (2012).
Wang, X. et al. Fiber-based flexible all-solid-state asymmetric supercapacitors for integrated photodetecting system. Angewandte Chemie International Edition 53, 1849–1853 (2014).
Lu, X. et al. Stabilized TiN nanowire arrays for high-performance and flexible supercapacitors. Nano Lett. 12, 5376−5381 (2012).
Chen, X. Y. et al. Nitrogen-doped porous carbon for supercapacitor with long-term electrochemical stability. J. Power Sources 230, 50–58 (2013).
Senthilkumar, S. T., Wang, Y. & Huang, H. Advances and prospects of fiber supercapacitors. Journal of Materials Chemistry A 3, 20863–20879 (2015).
Wang, Q. et al. Flexible coaxial-type fiber supercapacitor based on NiCo2O4 nanosheets electrodes. Nano Energy 8, 44–51 (2014).
Wang, Z. et al. Surface modified nanocellulose fibers yield conducting polymer-based flexible supercapacitors with enhanced capacitances. ACS nano 9, 7563–7571 (2015).
Wang, X. J., Hou, Y. Y., Zhu, Y. S., Wu, Y. P. & Holze, R. An aqueous rechargeable lithium battery using coated Li metal as negative electrode. Sci. Rep. 3, 1401 (2013).
Choi, B. G. et al. High performance of a solid-state flexible asymmetric supercapacitor based on graphene films. Nanoscale 4, 4983–4988 (2012).
Qian, Z., Peng, T., Wang, J. & Qu, L. Construction of Hybrid Supercapacitor–Batteries with dual‐scale shelled architecture. ChemSusChem 7, 1881–1887 (2014).
Davoglio, R. A., Biaggio, S. R., Bocchi, N. & Rocha-Filho, R. C. Flexible and high surface area composites of carbon fiber, polypyrrole, and poly (DMcT) for supercapacitor electrodes. Electrochimica. Acta 93, 93–100 (2013).
Demarconnay, L., Raymundo-Pinero, Beguin, E. & F. Adjustment of electrodes potential window in an asymmetric carbon/MnO2 supercapacitor. J. Power Sources 196, 580 (2011).
Yan, J. et al. Amorphous Ni (OH) 2@ three-dimensional Ni core–shell nanostructures for high capacitance pseudocapacitors and asymmetric supercapacitors. J. Adv. Funct. Mater. 22, 2632–2641 (2012).
Xia, X. H. et al. A new type of porous graphite foams and their integrated composites with oxide/polymer core/shell nanowires for supercapacitors: structural design, fabrication, and full supercapacitor demonstrations. Nano Lett. 14, 1651–1658 (2014).
Xu, J. et al. Flexible asymmetric supercapacitors based upon Co9S8 nanorod//Co3O4@RuO2 nanosheet arrays on carbon cloth. ACS Nano 7, 5453–5462 (2013).
Huang, M. L., Gu, C. D., Ge, X., Wang, X. L. & Tu, J. P. NiO nanoflakes grown on porous graphene frameworks as advanced electrochemical pseudocapacitor materials. J. Power Sources 259, 98–105 (2014).
Yu, H. et al. Hierarchically porous three-dimensional electrodes of CoMoO4 and ZnCo2O4 and their high anode performance for lithium ion batteries. Nanoscale 6, 10556–10561 (2014).
Zhang, K. et al. Integrated SnO2 nanorod array with polypyrrole coverage for high-rate and long-life lithium batteries. Phys. Chem. Chem. Phys. 17, 7619- 7623 (2015).
Bao, J. et al. All-solid-state flexible thin-film supercapacitors with high electrochemical performance based on a two-dimensional V2O5·H2O/graphene composite. J. Mater. Chem. A 2, 10876–10881 (2014).
Candler, J. et al. New insight into high-temperature driven morphology reliant CoMoO4 flexible supercapacitors. New Journal of Chemistry 39, 6108–6116 (2015).
Liu, M. C. et al. Hydrothermal process for the fabrication of CoMoO4· 0.9 H2O nanorods with excellent electrochemical behavior. New J. Chem. 36, 1713 (2012).
Liu, M. C. et al. Design and synthesis of CoMoO4–NiMoO4·×H2O bundles with improved electrochemical properties for supercapacitors. J. Mater. Chem. A 1, 1380–1387 (2013).
Yin, Z. X. et al. A Bi2Te3@CoNiMo composite as a high performance bifunctional catalyst for hydrogen and oxygen evolution reactions. J. Mater. Chem. A 3, 22750–22758 (2015).
Zhang, Z. et al. Facile hydrothermal synthesis of NiMoO4@CoMoO4 hierarchical nanospheres for supercapacitor applications. Phys. Chem. Chem. Phys. 17, 20795–20804 (2015).
Zhang, B. H. et al. Nanowire Na0.35MnO2 from a hydrothermal method as a cathode material for aqueous asymmetric supercapacitors. J. Power Sources 253, 98–103 (2014).
Zhu, S. J. et al. Flower-like MnO2 decorated activated multihole carbon as high-performance asymmetric supercapacitor electrodes. Mater. Lett. 135, 11–14 (2014).
Tang, Q., Chen, M. M., Wang, L. & Wang, G. A novel asymmetric supercapacitors based on binder-free carbon fiber paper@nickel cobaltite nanowires and graphene foam electrodes. J. Power Sources 273, 654–662 (2015).
Long, C. L. et al. Nitrogen‐Doped Carbon Networks for High Energy Density Supercapacitors Derived from Polyaniline Coated Bacterial Cellulose. Adv. Funct. Mater. 24, 3953–3961 (2014).
Wang, H. et al. One-step preparation of single-crystalline Fe2O3 particles/graphene composite hydrogels as high performance anode materials for supercapacitors. Nano Energy 7, 86–96 (2014).
Tang, Q. Q., Wang, W. Q. & Wang, G. C. The perfect matching between the low-cost Fe2O3 nanowire anode and the NiO nanoflake cathode significantly enhances the energy density of asymmetric supercapacitors. J. Mater. Chem. A 3, 6662–6670 (2015).
Long, C. L., Jiang, L. L., Wei, T., Yan, J. & Fan, Z. J. High-performance asymmetric supercapacitors with lithium intercalation reaction using metal oxide-based composites as electrode materials. J. Mater. Chem. A 2, 16678–16686 (2014).
Wang, R. T., Yan, X. B., Lang, J. W., Zheng, Z. M. & Zhang, P. A hybrid supercapacitor based on flower-like Co(OH)2 and urchin-like VN electrode materials. J. Mater. Chem. A 2, 12724–12732 (2014).
Ma, Z. L., Huang, X. B., Dou, S., Wu, J. H. & Wang, S. Y. One-pot synthesis of Fe2O3 nanoparticles on nitrogen-doped graphene as advanced supercapacitor electrode materials. J. Phys. Chem. C 118, 17231–17239 (2014).
Qu, Q., Yang, S. & Feng, X. 2D Sandwich‐like Sheets of Iron Oxide Grown on Graphene as High Energy Anode Material for Supercapacitors. Adv. Mater. 23, 5574–5580 (2011).
Yang, P. et al. Low-cost high-performance solid-state asymmetric supercapacitors based on MnO2 nanowires and Fe2O3 nanotubes. Nano Lett. 14, 731–736 (2014).
Chen, L. F., Yu, Z. Y., Ma, X., Li, Z. Y. & Yu, S. H. In situ hydrothermal growth of ferric oxides on carbon cloth for low-cost and scalable high-energy-density supercapacitors. Nano Energy 9, 345–354 (2014).
Zhang, G. Q., Wu, H. B., Hoster, H. E., Chan-Park, M. B. & Lou, X. W. Single-crystalline NiCo2O4 nanoneedle arrays grown on conductive substrates as binder-free electrodes for high-performance supercapacitors. Energy Environ. Sci. 5, 9453–9456 (2012).
Liu, M. C. et al. Facile fabrication of CoMoO4 nanorods as electrode material for electrochemical capacitors. Materials Letters 94, 197–200 (2013).
Xiao, W., Chen, J. S., Li, C. M., Xu, R. & Lou, X. W. Synthesis, Characterization, and Lithium Storage Capability of AMoO4 (A=Ni, Co) Nanorods. Chem. Mater. 22, 746–754 (2010).
Cai, D. P. et al. Enhanced performance of supercapacitors with ultrathin mesoporous NiMoO4 nanosheets. Electrochimica Acta 125, 294–301 (2014).
Kong, L. B. et al. Porous cobalt hydroxide film electrodeposited on nickel foam with excellent electrochemical capacitive behavior. J. Solid State Electrochem. 15, 571–577 (2011).
Mai, L. Q. et al. Hierarchical MnMoO4/CoMoO4 heterostructured nanowires with enhanced supercapacitor performance. Nat. Commun. 2, 381–385 (2011).
Yu, X. Z., Lu, B. G. & Xu, Z. Super Long-Life Supercapacitors Based on the Construction of Nanohoneycomb-Like Strongly Coupled CoMoO4-3D Graphene Hybrid Electrodes. Adv. Mater. 26, 1044–1051 (2014).
Xiao, K. et al. Direct self-assembly of Fe2O3/reduced grapheme oxide nanocomposite for high-performance lithium-ion batteries. J. Mater. Chem. A. 3, 6128–6135 (2015).
Ghosh, D., Giri, S. & Das, C. K. Synthesis, characterization and electrochemical performance of graphene decorated with 1D NiMoO4· nH2O nanorods. Nanoscale 5, 10428–10437 (2013).
Zhang, B. et al. Urchin-like Li4Ti5O12-carbon nanofiber composites for high rate performance anodes in Li-ion batteries. J. Mater. Chem. 22, 12133–12140 (2012).
He, Y. M. et al. Freestanding three-dimensional graphene/MnO2 composite networks as ultralight and flexible supercapacitor electrodes. ACS Nano 7, 174–182 (2013).
Wang, K. P. & Teng, H. S. Structural feature and double-layer capacitive performance of porous carbon powder derived from polyacrylonitrile-based carbon fiber. J. Electrochem. Soc. 154, A993 (2007).
Xu, M. W., Kong, L. B., Zhou, W. J. & Li, H. L. Hydrothermal synthesis and pseudocapacitance properties of α-MnO2 hollow spheres and hollow urchins. J. Phys. Chem. C 111, 19141 (2007).
He, Y. et al. Constructed uninterrupted charge-transfer pathways in three-dimensional micro/nanointerconnected carbon-based electrodes for high energy-density ultralight flexible supercapacitors. ACS Appl. Mater. Interfaces 6, 210–218 (2014).
Yu, P. et al. Polyaniline nanowire arrays aligned on nitrogen-doped carbon fabric for high-performance flexible supercapacitors. Langmuir 29, 12051–12058 (2013).
Tang, P., Han, L. & Zhang, L. Facile synthesis of graphite/PEDOT/MnO2 composites on commercial supercapacitor separator membranes as flexible and high-performance supercapacitor electrodes. ACS Appl. Mater. Interfaces 6, 10506–10515 (2014).
Yuan, C. et al. Template-engaged synthesis of uniform mesoporous hollow NiCo2O4 sub-microspheres towards high-performance electrochemical capacitors. RSC Advances 3, 18573–18578 (2013).
Liu, X. et al. Hierarchical NiCo2O4@NiCo2O4 core/shell nanoflake arrays as high-performance supercapacitor materials. ACS applied materials & interfaces 5, 8790–8795 (2013).
Tang, Z., Tang, C. H. & Gong, H. A High Energy Density Asymmetric Supercapacitor from Nano-architectured Ni(OH)2/Carbon Nanotube Electrodes. Adv. Funct. Mater. 22, 1272–1278 (2012).
Song, Y. Q., Qin, S. S., Zhang, Y. W., Gao, W. Q. & J. P. Liu, Large-scale porous hematite nanorod arrays: direct growth on titanium foil and reversible lithium storage. J. Phys. Chem. C 114, 21158–21164 (2010).
Acknowledgements
We thank National Natural Science Foundation of China (Nos 51572058, 91216123, 51174063, 51502057), the Natural Science Foundation of Heilongjiang Province (E201436), the International Science & Technology Cooperation Program of China (2013DFR10630, 2015DFE52770) and Specialized Research Fund for the Doctoral Program of Higher Education (SRFDP 20132302110031), Natural Science Foundation of Heilongjiang Province of China (Grant No. E2016062), the China Postdoctoral Science Foundation (General Financial Grant No. 2014M561345), the Heilongjiang Postdoctoral Science Foundation (LBH-Z14105).
Author information
Authors and Affiliations
Contributions
Jiupeng Zhao and Yao Li designed this experiment and supervised the manuscript. Jing Wang and Leipeng Zhang carried out the electrochemical experiments, wrote the the manuscript and other analysis. Xiang Zhang, Yanlong Tian and Xusong Liu analyzed and discussed the results and wrote the manuscript. Xiaoxu Liu revised the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wang, J., Zhang, L., Liu, X. et al. Assembly of flexible CoMoO4@NiMoO4·xH2O and Fe2O3 electrodes for solid-state asymmetric supercapacitors. Sci Rep 7, 41088 (2017). https://doi.org/10.1038/srep41088
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep41088
- Springer Nature Limited