Abstract
NbP is a recently realized Weyl semimetal (WSM), hosting Weyl points through which conduction and valence bands cross linearly in the bulk and exotic Fermi arcs appear. The most intriguing transport phenomenon of a WSM is the chiral anomaly-induced negative magnetoresistance (NMR) in parallel electric and magnetic fields. In intrinsic NbP the Weyl points lie far from the Fermi energy, making chiral magneto-transport elusive. Here, we use Ga-doping to relocate the Fermi energy in NbP sufficiently close to the W2 Weyl points, for which the different Fermi surfaces are verified by resultant quantum oscillations. Consequently, we observe a NMR for parallel electric and magnetic fields, which is considered as a signature of the chiral anomaly in condensed-matter physics. The NMR survives up to room temperature, making NbP a versatile material platform for the development of Weyltronic applications.
Similar content being viewed by others
Introduction
Weyl semimetals1,2,3 are a recently realized, new topological matter4,5,6,7 in which conduction and valence bands touch linearly near the Fermi energy (EF). Weyl states are closely related to the well-known Dirac states8,9,10,11, where both time reversal and inversion symmetries are preserved. In contrast, Weyl states emerge when one of these symmetries is broken. The band touching points in a Weyl semimetal – so-called Weyl nodes – always come in spatially separated pairs of opposite chirality (χ = ±1), as sketched in Fig. 1a, which distinguish them from Dirac semimetals having two degenerate Weyl nodes of opposite chirality that form one Dirac node. Therefore, exotic features of Weyl semimetals include Fermi arcs, which connect two Weyl nodes of opposite chirality. This occurs even in the absence of an external magnetic field, which would be required for the realization of Fermi arcs in Dirac semimetals.
For relativistic Weyl and Dirac fermions, chirality is, in principle, a strictly conserved quantum number, which gives the direction of the fermion spin relative to the direction of its linear momentum. Nevertheless, when these relativistic fermions are subjected to electromagnetic fields with parallel electric and magnetic field components (E||B), the gauge invariance also has to be taken into account, and a breakdown of chiral symmetry occurs. The physical origin of this phenomenon lies in the splitting of the band structure into Landau levels in the presence of a magnetic field. In this scenario, only the zeroth Landau level of the Weyl band exhibits uni-directional fermion velocity, forward or backward along the magnetic field direction depending on its chirality. Without an additional electric field, the forward and backward moving zeroth Landau levels are equally filled; however, applying E||B leads to chiral charge pumping between the two branches, with a flow rate that is proportional to The electrons are forced to move – for example – in the forward direction, and consequently, the forward moving zeroth Landau level is filled more than the backward moving one. Such breaking of the chiral symmetry is referred to as the Adler-Bell-Jackiw or chiral anomaly12,13. In electrical transport measurements this anomaly leads to an additional topological current in parallel to the aligned electric and magnetic fields, decreasing the resistance of a Weyl semimetal with increasing magnetic field. Such a negative magnetoresistance (NMR) is considered to be a strong signature of broken chiral symmetry in condensed matter systems14,15. In the limit of weak B, Son and Spivak showed, in fact, that the resistance - in a condensed matter system with broken chiral symmetry and E||B - is inverse proportional to the squared magnetic field (R ~ 1/B2)16. NMR related to broken chirality has already been reported for Dirac semimetals such as Cd3As2 and Na3Bi and the Weyl metals TaAs, NbAs, Zn-doped NbP and the predicted type-II Weyl semimetal WTe217,18,19,20,21,22,23. In contrast, NMR in TaP has been related to the effect of current jetting24.
For TaAs-family compounds, which are recently discovered inversion-breaking Weyl semimetals4,5,6,25,26,27,28, two groups of Weyl points were found and classified into four pairs in the kz = 0 plane (called W1) and eight pairs off the kz = 0 plane (called W2) in the first Brillouin zone29. NbP is the lightest member of the TaAs family. It has a non-centrosymmetric crystal structure in a tetragonal lattice (space group I41md), as sketched in Fig. 1b. Intrinsic NbP has been intensively studied by magneto-transport29 and quantum oscillation measurements30,31. Ultrahigh mobility (5 · 106 cm2 V−1 s−1 at 9 T and 1.85 K)29 and huge magnetoresistance (8.5 · 105 % at 9 T and 1.85 K) attributed to electron-hole resonance32 have been observed29. Quantum oscillation measurements combined with ab initio calculations revealed that the W1 and W2 Weyl nodes are located −57 meV and +5 meV away from the intrinsic Fermi level (EF0) of the pristine NbP sample without intentional doping30. In contrast, Wang et al. reported that they were able to activate the W1 Weyl cones in Zn-doped NbP for chiral anomaly. For their samples, the W1 Weyl points are 15 meV above the Fermi level22.
For the magneto-transport measurements, elongated, Ga-doped NbP micro-ribbons of 50 μm × 2.46 μm × 526 nm were prepared by Ga focused ion beam (FIB) etching into the bulk sample. The XRD pattern of the (001) surface of the NbP bulk sample, as given in Fig. 1c, shows the good quality of the sample with the full-width half-maximum being no larger than 0.15 degrees. The NbP micro-ribbon was extracted from the bulk sample using a micromanipulator and electrically contacted using laser lithography, followed by a Ti/Pt metallization process. A micrograph of the electrically contacted sample can be seen in Fig. 1d. The high aspect ratio of the micro-ribbon with contact lines across the full width of the sample is chosen to supress current jetting and to ensure a homogenous E-field distribution, respectively33. The Ga concentration on the surface of the micro-ribbon (analysed by scanning electron microscopy energy dispersive x-ray spectroscopy (SEM-EDX)) revealed an average composition of 53% Nb, 45% P and 2% Ga with a slight Ga and Nb increase and a P decrease at the edge of the sample (Fig. 1e). Ga etching leads to a few nanometer-thick surface defect layer as commonly introduced by this fabrication technique and an exponentially decaying Ga-concentration deeper in the bulk of the micro-ribbon34. However, we note that, as stated by Moll et al.34, such an amorphous surface layer has no influence on the topological properties of the ribbon. Magneto-transport measurements from cryogenic temperatures up to room temperature and with applied magnetic fields up to ±9 T were performed with the current (100 nA) along the [100] axis and the magnetic field varying from the [100] axis (0°) to the [001] axis (90°).
At room temperature, the zero-field resistivity of the Ga-doped NbP micro-ribbon is enhanced by a factor of 15 compared to the intrinsic NbP bulk sample. A non-metallic resistivity ρ versus temperature T profile is observed (Fig. 1f). Lowering EF in Na3Bi and Cd2As3 to observe the NMR has previously resulted in a similar ρ(T), which was ascribed to thermal activation of holes across the gapless energy band due to the close vicinity of the Fermi level to the neutrality point17,19.
A quadratic low-field MR (MR = (ρ(B) − ρ(0))/ρ(B) · 100%, with ρ(0) for zero magnetic field and ρ(B) for an applied magnetic field B) and an unsaturated linear high-field magnetoresistance MR are observed in transverse magnetic fields (Fig. 2a). The MR at high fields is attributed to Abrikosov’s linear quantum MR35, resulting from thermal excitation into the lowest Landau level, which is consistent with the non-metallic ρ(T). Linearity induced by strong disorder36 is rather unlikely due to the high crystalline quality of our samples. Ultrahigh MR, as observed in intrinsic NbP, is not obtained in our samples (MR(300 K) = 4.46% to MR(5 K) = 6.42%), which probably originates from the absence of electron-hole resonance32 due to a Ga doping-induced Fermi level shift.
Our interpretation is supported by the analysis of strong Shubnikov-de Haas (SdH) oscillations (Fig. 2a), observed below 50 K. After subtracting a smooth background (Fig. 2b), Fast Fourier Transformation (FFT) (Fig. 2c) reveals six fundamental SdH oscillation frequencies - F1 = 3.47 T, F2 = 17.37 T, F3 = 24.56 T, F4 = 34.63 T, F5 = 43.08 T and F6 = 71.36 T - which are correlated with the corresponding electron and hole pockets by performing band structure calculations. NbP exhibits two electron and two hole pockets (E1, E2, H1 and H2) at the Fermi surface30. For applied magnetic fields along the [001] axis, hole pockets show one extremal orbit, while electron pockets exhibit 3 extremal orbits (labelled as neck, centre and arm in Fig. 2d). From the best fits of the experimentally observed SdH oscillation frequencies to the F versus E plot obtained from band structure calculations, F1 was identified with the E2 electron pocket, F2 with the H2 hole pocket, F3, F5 and F6 with the E1 electron pocket, and F4 with the H1 hole pocket. Accordingly, the Fermi energy in our Ga-doped NbP micro-ribbons is shifted to EF (doped) = +10 meV above the intrinsic Fermi level EF0 (compare in Fig. 2d). While the W2 points of intrinsic NbP are 5 meV above EF0, which prevents these connected W2 points from exhibiting NMR30, in the doped NbP, the Weyl points 5 meV below EF are truly separated, which makes them active for chiral anomaly. Given the theoretical position of the Fermi level, oscillation frequencies at 14.02 T and 20.04 T should also be experimentally observable. However, the broad peak at 17.37 T does not allow for sufficient resolution. From the position of the Fermi level, carrier concentrations of nh = 1.95 · 1019 cm−3 and ne = 4.19 · 1019 cm−3 were calculated such that electron-hole resonance and therefore ultrahigh MR are suppressed. Furthermore, for the most prominent SdH frequency (F2 = 17.37), we obtain a high mobility of 7.1 · 105 cm2/Vs at 5 K and a relatively low effective mass mc = 0.064 m0 from the magnetic field- and temperature-damping of the oscillations37.
Tilting the magnetic field parallel to the applied current, we observe a distinct NMR, which we explain via the chiral anomaly, (Fig. 3a,b). Based on the above analysis, the W2 points should be active for the chiral anomaly along the [100] axis. The NMR is very robust against temperature enhancement, as it is observed between 5 and 300 K. Although of the same order of magnitude, in contrast to the positive MR in transverse magnetic fields, the longitudinal NMR at 300 K is enhanced by a factor of 2.9 compared to the NMR at 25 K. We attribute this observation to the ionization of Ga, which increases at elevated temperatures, pushing the Fermi level even closer to the W2 points. Angle-dependent MR measurements (Fig. 3c) show that the observed NMR is sensitive to the angle (ϕ) between B and I, and can be well traced by a cos2(ϕ)-term at low fields, underscoring our assignment to chiral asymmetry. Moreover, at low magnetic fields the inverse of the NMR, the longitudinal positive magnetoconductance MC (Fig. 3d), is well described by B2- function, in accordance with the prediction of Son and Spivak16. At higher fields, however, the longitudinal MC becomes linear. This observation is in agreement with the theoretical description of a transition from a multi-Landau level chiral anomaly to the limit, where only one Landau level is occupied35. We note that the temperature broadening of the Fermi distribution will activate charge carriers that do not contribute to the NMR. Even at low temperatures likely several band as indicated in Fig. 2(d) will contribute to the transport in parallel to the Weyl cones at zero magnetic field. However, up to the highest temperature of 300 K measured here, we observe that the chiral anomaly seems to dominate the B-dependence of R, which could be interesting for Weyltronic applications28.
In conclusion, we have provided experimental evidence of chiral anomaly in Ga-doped NbP, which originates from the W2 cones. Our analysis is based on magneto-transport studies of Ga-doped NbP micro-ribbons combined with band structure simulations. The observation of a non-metallic temperature dependence of the resistivity and Abrikosov’s linear quantum MR, as well as the evaluation of the observed SdH oscillations, revealed that electron doping shifts the Fermi level in NbP as close as 5 meV above the W2 points, making them active for chiral anomaly. In fact, with parallel magnetic and electric fields, we observe a negative magnetoresistance, whose temperature, magnetic field and angle dependences are consistent with broken chiral symmetry. We believe that this work can pave the way to systematically accessing the unique properties of massless Weyl fermions near the Weyl nodes by material engineering, providing a versatile platform for the development of Weyltronic components.
Methods
Crystal growth
Polycrystalline NbP powder was synthesized by a direct reaction of niobium (Chempur 99.9%) and red phosphorus (Heraeus 99.999%) which were kept in an evacuated fused silica tube (t = 48 h, T = 800 °C). Subsequently, high-quality single crystals of NbP were grown from this microcrystalline powder via a chemical vapour transport reaction in a temperature gradient starting from 850 °C (source) to 950 °C (sink) using iodine (Alfa Aesar 99.998%)38 with a concentration of 13.5 mgcm−3 as a transport agent.
Crystal structure analysis
The XRD measurements were performed in a Panlaytical X’Pert four-circle diffractometer using Cu-Kα radiation. The sample was oriented with the help of the Euler cradle in the device. Afterwards, a θ−2θ was taken using a high-resolution optics with a Goebel mirror in the primary beam path and narrow soller slits on the detector side.
Definition of the micro-ribbon
From the NbP bulk sample, a 50 μm × 2.46 μm × 526 nm large micro-ribbon was cut with a dual-beam focused ion beam system (FIB) of the type FEI Helios 600i using 30 keV Ga+ ions (I = 65 nA − 80 pA). In order to avoid electrostatic repulsion, the as-cut NbP micro-ribbon was picked up ex-situ with a glass needle and transferred to a glass substrate.
Compositional analysis of the micro-ribbon
The compositional analysis was carried out in-situ in the FIB by energy dispersive X-ray analysis (EDX) using 15 keV electrons.
Definition of the electrical contacts
The NbP micro-ribbon placed on a 150 μm thick glass substrate was covered with a double layer of photo resist, composed of a layer lift-off resist covered with a layer of positive resist (Micro Chem LOR 3B and maP-1205). The electrical contact structure was defined as shown in Fig. 1d using a laser lithography system (Heidelberg Instruments μpg 101). Afterwards, the exposed parts of the photoresist were developed (developer ma-D331, t = 45 s, T = 20 °C) until an undercut structure was observed at the edges of the developed parts, which ensures a clean removal of the metal layer in the lift-off process. Before the metallization, the NbP contact areas were cleaned by Ar etching (t = 5 min, p = 7.4 × 10−3 Torr, flowAr = 15 sccm and P = 20 W) and subsequently 10 nm of Ti and 500 nm of Pt were sputtered without breaking the vacuum. In the lift-off process (Remover 1165, T = 80 °C, t = 1 h) residual metal parts were removed.
Transport measurements
Transport measurements were performed in a cryostatic system (PPMS DynaCool from Quantum Design) equipped with a 9 T electromagnet. The resistance measurements (Iac = 100 nA, f = 189 Hz) were performed on a rotary sample holder at temperatures between 5 K and 300 K and at a nitrogen pressure of 4 × 10−3mbar.
Band structure calculations
The ab initio band structure calculations were performed within the framework of density functional theory (DFT), which are implemented in the Vienna ab initio simulation package39. The core electrons were represented by the projector-augmented-wave potential. Generalized gradient approximation (GGA) is employed for the exchange correlation functional. Maximally localized Wannier functions (MLWFs) were used to interpolate the bulk Fermi surface40.
Additional Information
How to cite this article: Niemann, A. C. et al. Chiral magnetoresistance in the Weyl semimetal NbP. Sci. Rep. 7, 43394; doi: 10.1038/srep43394 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Volovik, G. E. The Universe in a Helium Droplet. (Clarendon Press, 2003).
Wan, X. et al. Topological semimetal and Fermi-arc surface states in the electronic structure of pyrochlore iridates. Phys. Rev. B 83, 205101 (2011).
Balents, L. Weyl electrons kiss. Physics (College. Park. Md). 4, 36 (2011).
Lv, B. Q. et al. Experimental discovery of Weyl semimetal TaAs. Phys. Rev. X 5, 31013 (2015).
Xu, S.-Y. et al. Discovery of a Weyl Fermion semimetal and topological Fermi arcs. Science 349, 6248 (2015).
Yang, L. X. et al. Weyl semimetal phase in the non-centrosymmetric compound TaAs. Nat. Phys. 11, 728–732 (2015).
Belopolski, I. et al. Discovery of a new type of topological Weyl fermion semimetal state in MoxW1−xTe2 . Nat. Commun. 7, 13643 (2016).
Young, S. M. et al. Dirac semimetal in three dimensions. Phys. Rev. Lett. 108, 140405 (2012).
Borisenko, S. et al. Experimental realization of a three-dimensional Dirac semimetal. Phys. Rev. Lett. 113, 027603 (2014).
Schoop, L. M. et al. Dirac Cone Protected by Non-Symmorphic Symmetry and 3D Dirac Line Node in ZrSiS. Nat. Commun. 7, 11696 (2015).
Wang, X. et al. Evidence of Both Surface and Bulk Dirac Bands and Anisotropic Nonsaturating Magnetoresistance in ZrSiS. Adv. Electron. Mater. 2, 1600228 (2016).
Adler, S. L. Axial-vector vertex in spinor electrodynamics. Phys. Rev. 177, 5 (1969).
Bell, J. S. & Jackiw, R. A PCAC puzzle: π0 → γγ in the σ-model. Nuovo Cim. A60, 4 (1969).
Nielsen, H. B. & Ninomiya, M. The Adler-Bell-Jackiw anomaly and Weyl fermions in a crystal. Phys. Lett. B 130, 6 (1983).
Burkov, A. Chiral anomaly without relativity. Science 350, 6259 (2015).
Son, D. T. & Spivak, B. Z. Chiral anomaly and classical negative magnetoresistance of Weyl metals. Phys. Rev. B 88, 104412 (2013).
Li, H. et al. Negative Magnetoresistance in Dirac Semimetal Cd3As2 . Nat. Commun. 7, 10301 (2015).
Li, C. et al. Giant negative magnetoresistance induced by the chiral anomaly in individual Cd3As2 nanowires. Nat. Commun. 6, 10137 (2015).
Xiong, J. et al. Evidence for the chiral anomaly in the Dirac semimetal Na3Bi. Science 350, 6259 (2015).
Huang, X. et al. Observation of the chiral-anomaly-induced negative magnetoresistance: In 3D Weyl semimetal TaAs. Phys. Rev. X 5, 031023 (2015).
Yang, X. et al. Chiral anomaly induced negative magnetoresistance in topological Weyl semimetal NbAs. arXiv: 1506.03190 (2015).
Wang, Z. et al. Helicity-protected ultrahigh mobility Weyl fermions in NbP. Phys Rev. B 93, 121112(R) (2016).
Wang, Y. et al. Gate-Tunable Negative Longitudinal Magnetoresistance in the Predicted Type-II Weyl Semimetal WTe2 . Nat. Commun. 7, 13142 (2016).
Arnold, F. et al. Negative magnetoresistance without well-defined chirality in the Weyl semimetal TaP. Nat. Commun. 7, 11615 (2016).
Arnold, F. et al. Chiral Weyl Pockets and Fermi Surface Topology of the Weyl Semimetal TaAs. Phys. Rev. Lett. 117, 146401 (2016).
Liu, Z. K. et al. Evolution of the Fermi surface of Weyl semimetals in the transition metal pnictide family. Nat. Mater. 15, 4457 (2016).
Xu, N. et al. Observation of Weyl nodes and Fermi arcs in tantalum phosphide. Nat. Comm. 7, 11006 (2015).
Xu, S.-Y. et al. Discovery of a Weyl fermion state with Fermi arcs in niobium arsenide. Nat. Phys. 11, 3437 (2015).
Shekhar, C. et al. Extremely large magnetoresistance and ultrahigh mobility in the topological Weyl semimetal candidate NbP. Nat. Phys. 11, 3372 (2015).
Klotz, J. et al. Quantum oscillations and the Fermi surface topology of the Weyl semimetal NbP. Phys. Rev. B 93, 121105 (2016).
Sergelius, P. et al. Berry phase and band structure analysis of the Weyl semimetal NbP. Sci. Rep. 6, 33859 (2016).
Ali, M. N. et al. Large, non-saturating magnetoresistance in WTe2 . Nature 514, 13763 (2014).
Hirschberger, M. et al. The chiral anomaly and thermopower of Weyl fermions in the half-Heusler GdPtBi. Nat. Mat. 4684 (2016).
Moll, P. J. W. et al. Transport evidence for Fermi-arc-mediated chirality transfer in the Dirac semimetal Cd3As2 . Nature 535, 266–270 (2016).
Abrikosov, A. A. Quantum magnetoresistance. Phys. Rev. B 58, 5 (1998).
Parish, M. M. & Littlewood, P. B. Non-saturating magnetoresistance in heavily disordered semiconductors. Nature 426, 162–165 (2003).
Shoenberg, D. Magnetic oscillations in metals. (Cambridge University Press, 1984).
Martin, J. & Gruehn, R. Zum chemischen Transport vom Monophosphiden MP (M=Zr, Hf, Nb, Ta, Mo, W) und Diphosphiden MP2 (M=Ti, Zr, Hf). Z. Krist. 182, 180–182 (1988).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Mostofi, A. A. et al. wannier90: A tool for obtaining maximally-localised Wannier functions. Comput. Phys. Commun. 178, 685–699 (2008).
Acknowledgements
The authors gratefully acknowledge the work of Tina Sturm and Almut Pöhl defining the NbP micro-ribbon and conducting the compositional analysis and Andy Thomas for helpful discussion. This work was financially supported by the Deutsche Forschungsgemeinschaft DFG via Project DFG-SFB 1143 and DFG-RSF-Project No. (NI 616/22-1) ‘Influence of the topological states on the thermoelectric properties of Weyl-Semimetals’ and by the ERC Advanced Grant No. (291472) ‘Idea Heusler’.
Author information
Authors and Affiliations
Contributions
J.G. conceived the original idea for the project. A.C.N. performed the electrical measurements with the help of J.G., S.B. and P.S., R.H. characterized the crystal structure. B.R. supervised the micro-ribbon definition and the compositional analysis. S.-C.W. and B.Y. calculated the band structure. V.S. and M.S. synthesized the single crystal samples. All authors analysed the results. J.G. and A.C.N. wrote the manuscript with substantial contributions from all authors. C.F. and K.N. supervised the project.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Niemann, A., Gooth, J., Wu, SC. et al. Chiral magnetoresistance in the Weyl semimetal NbP. Sci Rep 7, 43394 (2017). https://doi.org/10.1038/srep43394
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep43394
- Springer Nature Limited
This article is cited by
-
Intrinsic negative magnetoresistance from the chiral anomaly of multifold fermions
Nature Communications (2024)
-
Magnetoresistive-coupled transistor using the Weyl semimetal NbP
Nature Communications (2024)
-
Possible permanent Dirac- to Weyl-semimetal phase transition by ion implantation
NPG Asia Materials (2022)
-
Experimental signatures of the chiral anomaly in Dirac–Weyl semimetals
Nature Reviews Physics (2021)
-
Weak localization and small anomalous Hall conductivity in ferromagnetic Weyl semimetal Co2TiGe
Scientific Reports (2019)