Abstract
We grew silicon nanowires (SiNWs) by a vapor-liquid-solid (VLS) mechanism using metal catalysts of gold (Au), titanium (Ti), manganese (Mn), and iron (Fe) under a high flow rate of hydrogen (H2). This combination of catalyst types and high gas flow rate revealed the potential for growing various SiNWs, including kinked SiNWs (with Au), ultra-thin SiNWs having diameters about 5 nm (with Ti), rough-surfaced SiNWs (with Mn), and ribbon-shaped SiNWs tens of microns in width (with Fe). The high flow rate of gas affects the VLS mechanism differently for each combination; for example, it induces an unstable solid-liquid interfaces (with Au), active etching of the catalyst (with Ti), sidewall deposition by a vapor-solid (VS) mechanism, and an asymmetric precipitation of Si in the catalyst (with Fe). Our combinatorial approach may provide a new path for the structural modulation of SiNWs via the VLS mechanism.
PACS: 80; 81; 82
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Background
Silicon nanowires (SiNWs) have considerable potential for several applications including electronics [1-4], sensors [5-7], energy conversion [8-11], and photonic devices [12,13] owing to their novel physical and chemical properties. Meanwhile, the structural modulation of NWs is critical to exploit their potential and realize devices with high performance [14-16]. For example, kinked [17-20] and branched [21,22] SiNWs have advantages in some applications due to their higher surface-to-volume ratio. SiNWs are generally grown by the vapor-liquid-solid (VLS) mechanism with the assistance of metal catalysts [23-25]. This mechanism is simple and versatile for SiNW preparation; however, structural modulation using this method is difficult because the liquid catalysts have a globular shape resulting from surface tension, which confines the shape of the NWs to a rod form, limiting further shape or size variation. Some structural modification of SiNWs during their growth has been studied by changing the pressure or temperature [26]; however, these alterations have shown only limited success, for example, the growth of kinked nanowires [27-29]. And catalyst diffusion during the growth determines the shape of nanowire [30].
Here, we report on the growth of various SiNWs using metal catalysts of gold (Au), titanium (Ti), manganese (Mn), and iron (Fe) under a high flow rate of hydrogen (H2). Through the combination of different types of catalyst and a high flow rate of gas, we could grow structurally modulated SiNWs that are kinked, ultra thin, with a rough surface, or have a thin ribbon shape. The results indicate that the high flow rate of H2 significantly affects the growth mode behavior, making room for the structural modulation of SiNWs via the VLS mechanism.
Methods
The SiNWs were grown on Si (100) substrates. The substrates were degreased with solvent, etched in a HF solution, and rinsed with deionized H2O. The substrates were then immersed in a diluted hydrofluoric acid solution (HF:H2O = 1:9). Two approaches were initially investigated for positioning the catalyst on the substrates to choose the ideal approach for the growth of NWs: (1) deposition of metal films and (2) supplying the metal component in the vapor phase by evaporation of metal precursors. In the case of the Au and Ti catalysts, metal layers approximately 5 nm (Au) and 2 nm (Ti) thick were deposited on the substrates. In the case of the Mn and Fe catalysts, each was supplied to the substrates through the gas phase using MnCl2 (99.99%, Sigma-Aldrich, St. Louis, MO, USA) or FeI2 (99.99%, Sigma-Aldrich, St. Louis, MO, USA) powders as a precursor for the metal catalyst. The SiNWs were grown in a hot wall quartz tube reactor under a H2 flow rate of 300 to 3,000 sccm∙min−1 using Si tetrachloride (SiCl4) (99.9999%, Sigma-Aldrich, St. Louis, MO, USA) as the Si source at 1,050°C for 30 min. The morphologies of the SiNWs were characterized by scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM).
Results and discussion
A general method to obtain SiNWs is based on VLS method with gold catalyst [31-33]. The gold is a metal that works well as catalyst compared to other metals. Figure 1a shows an SEM image of typical SiNWs grown on a Si substrate using an Au catalyst. Under a low gas flow rate, e.g., 300 sccm∙min−1, straight SiNWs with smooth surfaces were grown, as reported in numerous previous studies. Transmission electron microscopy (TEM) investigation revealed that the SiNW growth direction was [113]. A HRTEM image (Figure 1b) shows that the SiNWs are single crystalline. The globule at the tip of the NWs indicates the working of VLS mechanism for the growth of NWs. In this system, low gas flow rate and interface between Au-Si alloy and Si were stable during the growth. And SiNWs confined the shape of the NWs to a flat rod form due to a globular shape of the liquid Au catalyst.
Figure 1c,d shows the SiNWs grown under a high flow rate of H2 gas (3,000 sccm∙min−1). These show that primarily kinked SiNWs were grown on the substrate. Figure 1e,f,g shows that the SiNW growth direction is [101], and the kinks are away from the [101] to other <101 > directions. In previous studies, kinked SiNWs were grown by modulating the pressure, displaying a kinking between two [112] oriented segments at defined positions along the length of the NWs [34-36]. The d spacing measured from the Fourier transform of TEM is 3.103 Å for the (112) plane and 3.155 Å for the (110) plane, respectively, that are within 2% of the values of pure Si. The composition analysis using energy-dispersive X-ray analysis (EDAX) in TEM also showed only Si without any impurities.
As a result of the liquid-solid interface instability in the VLS mechanism, the amount of the Si component supplied to the liquid catalysts during the course of growth can be changed by differences in pressure. Similarly, the high flow rate of the H2 supplies less of the Si component to the liquid catalysts since such a high flow rate dilutes the precursor concentration in the gas phase. This induces instability of the liquid alloy-solid interface due to a dilute Si concentration in the catalysts, leading to an irregular stacking of Si at the interfaces, kinking the growth direction.
Figure 2 shows the SiNWs grown using Ti as the catalyst. As shown, the diameter of SiNWs ranged from 5 to 30 nm. It should be noted that the diameter is less than those formed with Au catalysts. It should also be noted that the diameter correlates to the H2 gas flow rate, becoming smaller with an increased flow rate. As shown in Figure 2b,c,d, the SiNWs have diameters of about 30 ± 10 nm with a 1,000 sccm∙min−1 hydrogen flow rate, 20 ± 5 nm with 2,000 sccm∙min−1, and 5 ± 1 nm with 3,000 sccm∙min−1. The d spacing measured from the Fourier transform of TEM and the composition analysis using EDAX in TEM showed only Si without any impurities or silicides.
It was revealed that Ti catalyst is essential for the growth of SiNWs since any NWs were not grown on the substrate without Ti catalysts. However, liquid globules were not found at the tip of the SiNWs grown with Ti. This indicates that Ti worked as a catalyst at the early stage of the VLS mechanism before being etched during the H2 flow with SiCl4 growth by the HCl by product gas, disappearing in the NWs. We already reported that Pt-Si liquid globules were etched out under a chloride atmosphere [37]. It is similar tendency to using the Ti catalyst. The etching of Ti in chlorinated environments has been reported in the literature [38,39]. It can also be assumed that the etching rate is proportional to the gas flow rate. Therefore, the etching is significant with the high gas flow rate, leading to a smaller size of the Ti catalyst, which resulted in smaller SiNWs. It should be noted that very thin SiNWs with sub-10 nm diameters could be easily obtained by the combination of a high gas flow rate and Ti catalyst.
SiNWs were also grown on a Si (100) substrate using a combination of Mn and high gas flow rate. As reported previously [40,41], Figure 3a shows a SEM image of the SiNWs grown on the substrate with the assistance of Mn catalyst under 3,000 sccm∙min−1 of H2. The SiNWs grew in the <111 > direction, tenths of μm in length and tenths of nm in diameter, relatively larger than the other NWs in this study. The SiNWs show globular droplets at their tips that indicate the operation of the VLS mechanism. The composition of globules was 64% of Si and 36% of Mn, and any Mn component was not found in the nanowires [40]. It should be noted that the SiNWs grown with Mn showed a rough surface compared to the other catalysts, as shown in Figure 3b,c. It should also be noted that the SiNWs were tapered with larger diameters toward the bottom. This indicates a sidewall deposition by the vapor-solid (VS) mechanism, which involves the direct deposition of Si atoms from the vapor, resulting in a roughened surface. This side growth may be caused by the high flow rate of gas that enhances the atom adsorption rate on crystalline surfaces by increasing effective collisions and impinging atoms from the vapor to the nanowire surface, inducing VS growth in the radial direction [42,43]. Nanoscale-controlled curvature radius could be controlled by a well-defined amorphous SiO2 layer/Si [44]. The side wall roughening has been observed in the previous study by using Au-Si-Mn catalysts [45]; however, the roughening mechanism is different. That is, the shape of catalyst leads the faceting of nanowires in the previous study; however, collisions and impinging of atoms leads the faceting in this study.
It should be noted that the VS growth precedes only in the Mn catalyst case, and this may be due to a slow growth rate of the NWs with the Mn catalyst. Our study indicates that the growth rate of the SiNWs with Mn catalysts is slow compared to other catalysts, such as Au or Pt [46], which could provide enough time for a sidewall growth [40,41]. The larger diameter of the NWs may also contribute to the side growth, since the Gibbs-Thompson effect plays a critical role for thinner nanowires that prevent the sidewall deposition over the course of the growth [47]. Figure 3d shows the detailed crystal structures of the rough SiNWs from the top to the bottom regions. The features observed in the fast Fourier transform (FFT) image of the rough SiNW indicate that the lowest surface energy facets, the {111} planes with a surface energy of 1.23 J/m2, were exposed. This suggests that the roughening of the NW surface contributes to minimizing the surface energy and, in turn, decreasing the stability of the SiNWs.
Finally, ribbon-shaped SiNWs could be grown by using a Fe catalyst under a high gas flow rate. Figure 4a shows SiNWs grown under different flow rates. Under a low flow rate of H2, such as 1,000 sccm∙min−1, typical SiNWs were grown on the substrate (Figure 4a). Under a moderate H2 flow rate (2,000 sccm∙min−1), ribbon-shaped SiNWs with a width of about 3 μm were grown (Figure 4b). Under a high gas flow rate of 3,000 sccm∙min−1, these SiNWs have widths of 10 to 20 μm and lengths of hundreds of micrometers (Figure 4c). This clearly indicates that the width of the SiNWs increased with increasing flow rate. The SEM and TEM images (Figure 4d,e) also show that the VLS mechanism is operating for the growth of these ribbon-shaped SiNWs. A HRTEM analysis demonstrates that the SiNWs are single crystals with the <100 > growth direction. The inset of Figure 4e shows the elemental mapping of the iron and silicon X-ray intensity compositing along the nanowire. As shown in Figure 4f, the width of SiNW is thicker, with a typical width of 40 nm at the bottom (right) to 20 μm at the tip (left). The thicknesses of these ribbon-shaped SiNWs are approximately 16 to 20 nm (Figure 4g).
The growth of ribbon-shaped SiNWs by the VLS mechanism is interesting since the liquid catalyst globule generally results in rod-shaped SiNWs for the majority of instances. It should be noted that the shape of the catalyst could itself be ribbon-like, as shown in Figure 4c, thus leading to the growth of ribbon-shaped SiNWs.
In this study, the Fe component is supplied to the substrate through the vapor phase continuously with the SiCl4; thus, they dissolve and alloy together, forming liquid droplets during the course of the growth. In the conditions, the dissolving rate of Fe and Si would be different, which would produce a compositional gradient in the Fe-Si droplet. The compositional gradient may not be significant under a low gas flow rate; however, it will likely be significant under a high flow rate because the dissolution rate of the metal components directly depends on the vapor impinging on the liquid catalyst. This gradient will result in the precipitation of Si asymmetrically at the solid-liquid interface, i.e., the precipitation of Si mainly occurred at the Si-rich sides, resulting in the widening of the SiNWs to form ribbons.
Conclusions
In this study, we demonstrated that various SiNWs could be grown by simply combining a high flow rate of gas with different types of catalyst. Considering the limitations of the VLS mechanism for a structural modulation of SiNWs, our combinatorial approach provides a new path for this modulation. It also provides a route to study the unusual VLS growth of SiNWs under high gas flow rates, i.e., highly dynamic conditions, that should be helpful toward advancing devices in several applications.
Abbreviations
- EDS:
-
energy-dispersive spectroscopy
- SEM:
-
scanning electron microscopy
- SiNWs:
-
silicon nanowires
- TEM:
-
transmission emission microscopy
- VLS:
-
vapor-liquid-solid
References
Cui Y, Lieber CM. Functional nanoscale electronic devices assembled using silicon nanowire building blocks. Science. 2001;291(5505):851–3.
Vallett AL, Minassian S, Kaszuba P, Datta S, Redwing JM, Mayer TS. Fabrication and characterization of axially doped silicon nanowire funnel field-effect transistors. Nano Lett. 2010;10:4813.
Weisse JM, Lee CH, Kim DR, Zheng X. Fabrication of flexible and vertical silicon nanowire electronics. Nano Lett. 2012;12(6):3339–43.
Park TE, Min BC, Kim IS, Yan JE, Jo MH, Chang JY, et al. Exchange-induced electron transport in heavily phosphorus-doped Si nanowires. Nano Lett. 2011;11(11):4730–5.
Paska Y, Haick H. Interactive effect of hysteresis and surface chemistry on gated silicon nanowire gas sensors. Appl Mater Interfaces. 2012;4(5):2604–17.
Wang H, Han X, Ou X, Lee CS, Zhang X, Lee ST. Silicon nanowire based single-molecule SERS sensor. Nanoscale. 2013;5:8172–6.
Ragman SFA, Yusof NA, Hashim U, Nor NM. Design and fabrication of silicon nanowire based sensor. Int J Electrochem Sci. 2013;8:10946–60.
Peng KQ, Wang X, Li L, Hu Y, Lee ST. Silicon nanowires for advanced energy conversion and storage. Nanotoday. 2013;8(1):75–97.
Peng KQ, Wang X, Wu XL, Lee ST. Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion. Nano Lett. 2009;9(11):3704–9.
Zhu J, Yu Z, Burkhar GF, Hsu CM, Connor ST, Xu Y, et al. Optical absorption enhancement in amorphous silicon nanowire and nanocone arrays. Nano Lett. 2009;9(1):279–82.
Tsakalakos L, Balch J, Fronheiser J, Korevaar BA, Sulima O, Rand J. Silicon nanowire solar cells. Appl Phys Lett. 2007;91:233117.
Bronstrup G, Jahr N, Leiterer C, Csaki A, Fritzsche W, Christiansen S. Optical properties of individual silicon nanowires for photonic devices. ACS Nano. 2010;4(12):7113–22.
Yan R, Gargas D, Yang P. Nanowire photonics. Nat Photonics. 2009;3:569–76.
Brus L. Luminescence of silicon materials: chains, sheets, nanocrystals, nanowires, microcrystals, and porous silicon. J Phys Chem. 1994;98:3575–81.
Hochbaum AI, Chen R, Delgado RD, Liang W, Garnett EC, Najarian M, et al. Enhanced thermoelectric performance of rough silicon nanowires. Nature. 2008;451:163–7.
Cui Y, Zhong Z, Wang D, Wang WU, Lieber CM. High performance silicon nanowire field effect transistors. Nano Lett. 2003;3:149–52.
Tian B, Xie P, Kempa TJ, Bell DC, Lieber CM. Single-crystalline kinked semiconductor nanowire superstructures. Nat Nanotechnol. 2009;4:824–9.
Xu L, Jiang Z, Qing Q, Mai L, Zhang Q, Lieber CM. Design and synthesis of diverse functional kinked nanowire structures for nanoelectronic bioprobes. Nano Lett. 2013;13:746–51.
Wu ZH, Mei X, Blumin M, Ruda HE, Liu JQ, Kavanagh KL. Growth, branching, and kinking of molecular-beam epitaxial 110 GaAs nanowires. Appl Phys Lett. 2003;83:3368.
Hyun YJ, Lugstein A, Steinmair M, Bertagnolli E, Pongratz P. Orientation specific synthesis of kinked silicon nanowires grown by the vapour–liquid–solid mechanism. Nanotechnology. 2009;20:125606.
Doerk GS, Ferralis N, Carraro C, Maboudian R. Growth of branching Si nanowires seeded by Au-Si surface migration. J Mater Chem. 2008;18:5376–81.
Wang D, Qian F, Yang C, Zhong Z, Lieber CM. Rational growth of branched and hyperbranched nanowire structures. Nano Lett. 2004;4:871–4.
Wagner RS, Ellis WC. Vapor‐liquid‐solid mechanism of single crystal growth. Appl Phys Lett. 1964;4:89–90.
Givargizov EI. Fundamental aspects of VLS growth. J Cryst Growth. 1975;31:20–30.
Choi HJ. Vapor–liquid–solid growth of semiconductor nanowires. In: Yi GC, editor. Semiconductor nanostructures for optoelectronic devices, processing, characterization, and applications. Berlin Heidelberg: Springer; 2012. p. 1–36.
Westwater J, Gosain DP, Tomiya S, Usui S, Ruda H. Growth of silicon nanowires via gold/silane vapor–liquid-solid reaction. JVSTB. 1997;15:554.
Madras P, Dailey E, Drucker J. Kinetically induced kinking of vapor-liquid-solid grown epitaxial Si nanowires. Nano Lett. 2009;9:3826–30.
Yoon H, Kim SI, Lee SH, In JH, Kim JW, Ryoo HS, et al. Three-dimensionally kinked high-conducting CoGe nanowire growth induced by rotational twinning. J Mater Chem C. 2013;1:6259–64.
Musin IR, Filler MA. Chemical control of semiconductor nanowire kinking and superstructure. Nano Lett. 2012;12(7):3363–8.
Hannon JB, Kodambaka Ross FM, Tromp RM. The influence of the surface migration of gold on the growth of silicon nanowires. Nature. 2006;440:69–71.
Hofmann S, Ducati C, Neill RJ, Piscanec S, Ferrari AC, Geng J, et al. Gold catalyzed growth of silicon nanowires by plasma enhanced chemical vapor deposition. J Appl Phys. 2003;94:6005.
Xu T, Nys P, Addad A, Lebedev OI, Urbieta A, Salhi B, et al. Faceted sidewalls of silicon nanowires: Au-induced structural reconstructions and electronic properties. Phys Rev B. 2012;81:115403.
Hochbaum AI, Fan R, He R, Yang P. Controlled growth of Si nanowire arrays for device integration. Nano Lett. 2005;5(3):457–60.
Wu Y, Cui Y, Huynh L, Barrelet CJ, Bell DC, Lieber CM. Controlled growth and structures of molecular-scale silicon nanowires. Nano Lett. 2004;4(3):433–6.
Geaney H, Dickinson C, Weng W, Kiely CJ, Barrett CA, Gunning RD, et al. Role of defects and growth directions in the formation of periodically twinned and kinked unseeded germanium nanowires. Cryst Growth Des. 2011;11:3266–72.
Krylyuk S, Davydov AV, Levin L. Tapering control of Si nanowires grown from SiCl4 at reduced pressure. ACS Nano. 2011;5(1):656–64.
Park TE, Lee KY, Kim IS, Chang JY, Voorhees P, Choi HJ. Combinatorial growth of Si nanoribbons. Nanoscale Res Lett. 2011;6:476.
Fracassi F, d’Agostino R. Chemistry of titanium dry etching in fluorinated and chlorinated gases. Pure Appl Chem. 1992;4:703–7.
d’Agostino R, Fracassi F, Pacifico C. Dry etching of Ti in chlorine containing feeds. J App Phys. 1992;72:4351.
Park YH, Kim J, Kim H, Kim I, Lee KY, Seo D, et al. Thermal conductivity of VLS-grown rough Si nanowires with various surface roughnesses and diameters. Appl Phys A Mater Sci Process. 2011;104:7–14.
Kim H, Park YH, Kim I, Kim J, Choi HJ, Kim W. Effect of surface roughness on thermal conductivity of VLS-grown rough SiGe nanowires. Appl Phys A Mater Sci Process. 2011;104:23.
Nebol'sin VA, Shchetinin AA. Role of surface energy in the vapor–liquid-solid growth of silicon. Inorg Mater. 2003;39:899–903.
Geelhaar L, Cheze C, Weber WM, Averbeck R, Riechert H, Kehagias T, et al. Axial and radial growth of Ni-induced GaN nanowires. Appl Phys Lett. 2007;91:093113.
Nakamura Y, Isogawa M, Ueda T, Yamasaka S, Matsui H, Kikkawa J, et al. Anomalous reductions of thermal conductivity in coherent nanocrystal architecture for silicon thermoelectric material. J Nanoen. 2014;11:029.
Meng E, Li W, Nakane K, Shirahashi Y, Hayakawa Y, Tatsuoka H. Shape modification of Si nanowires by using faceted silicide catalysts nucleated in Au-Si catalyst solution during the growth. AIP Adv. 2013;3:092107.
Jeong H, Park T, Seong H, Kim M, Kim U, Choi HJ. Growth kinetics of silicon nanowires by platinum assisted vapour–liquid–solid mechanism. Chem Phys Lett. 2009;467:331–4.
Eaglesham D, White A, Feldman L, Moriya N, Jcobson D. Equilibrium shape of Si. Phys Rev Lett. 1993;70:1643–6.
Acknowledgements
This research was supported by Nanomaterials Technology Development program (Green Nano Technology Development program) through the National Research Foundation of Korea (NRF) funded by the Ministry of Education Science and Technology (NRF-2014M3A7B4051580) and grant (NRF-2012R1A2A1A03010558) from the National Research Foundation (NRF) of Korea funded by the Ministry of Science, the Yonsei University-SNU collaborative Research Fund of 2014.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
DS carried out the main part of the structural analysis and drafted the manuscript. JL, SWK, IK, JN, and MH participated in the discussion of SEM, TEM sampling, and EDS. HJC participated in the design of the study, draft preparation, and coordination. All authors read and approved the final manuscript.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Seo, D., Lee, J., Kim, S.W. et al. Structural modulation of silicon nanowires by combining a high gas flow rate with metal catalysts. Nanoscale Res Lett 10, 190 (2015). https://doi.org/10.1186/s11671-015-0893-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-015-0893-4