Abstract
Controlled conductive filament formation in the resistive random access memory device is an essential requirement for analog resistive switching to develop artificial synapses. In this work, we have studied Au/Ti/HfAlOx/TiN-NP/HfAlOx/ITO RRAM device to demonstrate conductance quantization behavior to achieve the high-density memory application. Stepwise change in conductance under DC and pulse voltage confirms the quantized conductance states with integer and half-integer multiples of G0. Reactive TiN-NPs inside the switching layer helps to form and rupture the atomic scale conductive filaments due to enhancing the local electric field inside. Bipolar resistive switching characteristics at low SET/RESET voltage were obtained with memory window > 10 and stable endurance of 103 cycles. Short-term and long-term plasticities are successfully demonstrated by modulating the pre-spike number, magnitude, and frequency. The quantized conductance behavior with promising synaptic properties obtained in the experiments suggests HfAlOx/TiN-NP/HfAlOx switching layer is suitable for multilevel high-density storage RRAM devices.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Resistive random access memory (RRAM) has become attractive and it shows promise for future non-volatile memory devices due to its simple structure of switching layer sandwiched between two electrodes, with high-density memory structure, high speed, and low electrical power consumption [1,2,3]. The principle working mechanism of RRAM device is believed to be due to the formation and dissociation of the conductive filaments (CFs) formed inside the switching layers by applying external electric fields [4, 5]. However, the stochastic nature of CFs formation during device operation can hinder the large-scale commercial application of the RRAM device. So several process optimizations such as doped switching layers, metal electrode selection, bilayer switching layer structures, and metal nanocrystal incorporation are needed to control the CFs formation to improve the device-to-device and cycle-to-cycle variability [6,7,8,9,10,11,12,13]. Among different techniques, nanoparticles embedded oxide-based switching layers are examined extensively, influencing CFs formation and improving the resistive switching process. Recently, Liu et al. have described that Cu NPs inside SiO2 can control the forming process and, by stabilizing the resistive switching, improve the endurance characteristics [14]. Ag embedded Al2O3:Ag:ZnO switching layer also exhibited a high Ion/Ioff ratio with gradual SET and RESET characteristics [15]. Ag-NPs included Al2O3 switching layers also show DC cycling stability due to enhancing the local electric field due to the presence of oxygen vacancies and Ag ions [16]. Bousoulas et al. described that multilevel memory state, better variability, and long retention were achieved by Pt-nanocrystals (NCs) inclusion inside TiOx due to local field enhancement [10]. Also, embedding Pt-NCs inside switching layers, the local electric field leads to narrow and controlled CFs formation, further enhancing the switching performances described by Sakellaropoulos et al. [9]. In RRAM, gradual synaptic weight change manipulation by applying external stimuli is essential for high-density memory storage and artificial synaptic device for neuromorphic application. The presence of low oxygen vacancies that promotes gradual change in conductance states of nanoscale filamentary synaptic devices was observed [17, 18]. The atomic point contacts (APCs) were recently studied, which control the construction of the quantized conductance states. Change in quantized conductance states is the intrinsic property of the nanoscale CFs and is commonly found in oxide-based switching layers mediated by the formation and movement of oxygen vacancies and oxygen ions [4, 19, 20]. Stepwise increase in conductance due to precise atomic control of electron transport in conductive filaments leads to a higher memory density. G0 = 2e2/h (77 µS) is the quantum conductance unite, where e is the electronic charge, and the h is the Plank constant [21, 22]. The atomic layer deposition (ALD) technique is promising for achieving high-density metal nanoparticles with controlled thickness [23]. In this work, we have included ALD-based TiN-NP into HfAlOx matrix to control the quantized conductance state and have studied the synaptic properties for neuromorphic applications. Finally, we have studied gradual conductance change with integer and half-integer multiples of G0 in both SET and RESET processes in detail for the RRAM device consisting HfAlOx/TiN-NP/HfAlOx switching layer. Also, the short-term plasticity (STP) and long-term potentiation (LTP) were studied by controlling the pulse number and spike frequency.
Experiments
Initially, commercially available indium tin oxide (ITO) (resistivity ~ 60 Ω/sq)-coated glass was used for device fabrication. The surface of ITO was washed stepwise with acetone, isopropyl alcohol, and DI water. After cleaning immediately, ITO samples were moved for the atomic layer deposition chamber (Lucida D100 thermal ALD). Nearly 5 nm of HfAlOx (TMA 1 + TEMAH 2) was deposited before TiN deposition. HfAlOx alloy ALD deposition details have been given in earlier work [24]. After deposition of HfAlOx alloy layer, 20 cycles of TiN were deposited with a showerhead plasma-type ALD by titanium tetrachloride (TiCl4) and NH3 as precursors. Another layer of 5 nm HfAlOx alloy dielectric was grown to sandwich the TiN-NP inside HfAlOx layers. Using a photolithography, Au/Ti bilayer top electrodes (TEs) were deposited by an e-beam evaporator with a deposition rate of 0.3 Å/s. A liftoff process in acetone achieved the top electrode with an area of 100 × 100 µm. Cross section analysis, elemental profile, the surface morphology of different deposited layers were scanned by field emission transmission electron microscope (JEOL JEM-F200) and field emission scanning electron microscope (JEOL-7800F). Keithley 4200 SCS semiconductor parameter analyzer along with a 4225-PMU ultrafast current–voltage (I–V) pulse module was utilized for all DC and pulse leakage current vs voltage (I-V) characteristics. All resistive switching properties were measured with the external electrical DC/pulse bias given to the top Au/Ti electrode, and the bottom electrode was in the ground.
Results and Discussion
After the sample preparation with a focused ion beam (FIB), the cross section of the Au/Ti/HfAlOx/TiN-NP/HfAlOx/ITO RRAM device was examined by the transmission electron microscope (TEM) as shown in Fig. 1a. From the TEM image, all the layers from the device are clearly shown. The thickness of the overall switching layer was ~ 10 nm which was similar to the target thickness controlled by the ALD recipe of AlO, HfO, and TiN cycles. Also, the cross-sectional energy-dispersive spectroscopy (EDS) analysis (Fig. 1b) was done to detect different layers of the device. The presence of Au, Ti, Al, Hf, O, and Sn was confirmed by the EDS line scan as shown in Fig. 1b. From the atomic percentage of Ti profile, the small shoulder of Ti intensity inside the HfAlOx region was detected, which is believed to be emerged due to the presence of TiN-NP as highlighted by the black circles in Fig. 1b. Scanning transmission electron microscope (STEM) along with energy-dispersive spectroscopy (EDS) mapping is provided in Additional file 1: Fig. S1 to confirm all layers in the NP-based RRAM device. Although from the cross section TEM analysis, the presence of TiN-NP was not clear, which may be due to the similar color contrast of HfAlOx and TiN-NP or the surface oxidation of the TiN surface during 2nd layer of HfAlOx deposition. Although due to higher atomic concentration of Ti from Au/Ti top electrode is dominated, the Ti intensity due to the presence of TiN-NP inside the HfAlOx matrix was suppressed. In the previous work, the Ti presence was clearly demonstrated by the cross-sectional STEM image, core-level XPS spectra of TiN-NP, and elemental profile of Ti across the cross section of ITO/HfAlOx/TiN-NP/HfAlOx/ITO RRAM device [24]. In the supporting information, to observe the distribution of TiN-NPs surface morphology on the TiN-NP/HfAlOx/ITO structure, scanning electron microscope (SEM) image is presented in Additional file 1: Fig. S2. From Additional file 1: Fig. S2, a clear distribution of TiN-NP was achieved at a deposition temperature of 300 °C with 20 cycles of TiN ALD. High-density TiN-NPs distribution on HfAlOx can be promising for RRAM applications for controlling oxygen vacancy and the formation of controlled conductive filaments during device switching operation. Variation in diameter of the NPs was observed (ranges from ~ 2 to 25 nm), which can be controlled by proper thermal treatment.
Figure 2a and d shows the electroforming and first RESET characteristics of Au/Ti/HfAlOx/ITO RRAM device with and without TiN-NP inclusion. Devices show forming voltages at the range of ‒4.6 V ~ ‒5.5 V as shown in the comparison characteristics in Additional file 1: Fig. S3. However, a reduction in the effective electric field during the forming process was observed after introducing TiN-NP inside HfAlOx matrix as shown in Additional file 1: Fig. S3. However, the conduction mechanism before forming processes was changed, due to the presence of additional intrinsic defects after introducing TiN-NP as confirmed by the Additional file 1: Fig. S3. The uniformity of forming voltages was also more precise in the case of Au/Ti/HfAlOx/TiN-NP/HfAlOx/ITO RRAM devices due to the presence of ALD-based TiN-NP.
Also, during the first RESET, the improvement in uniform memory window as well as lower RESET voltages was observed, as shown in Fig. 2d. Similar improvement was monitored by Wu et al. in their study with nanocrystals-based RRAM devices [25]. Figure 2b and e is the typical bipolar resistive switching characteristics of both devices. In both devices, the SET and RESET properties were clearly demonstrated. After introducing TiN-NP, the memory window was clearly increased, as shown in Fig. 2e. In the supporting information (Additional file 1: Fig. S4), the comparison characteristics of bipolar switching characteristics, endurance properties of first 500 cycles, and the distribution of LRS and HRS have been given for both devices. In the Au/Ti/HfAlOx/ITO RRAM device, the conductive filaments (CFs) form in the canonical shape between top and bottom electrode during the electroforming process. The presence of tri-valent Al atoms inside tetra-valent HfO2 transition oxide creates intrinsic oxygen vacancies (VO). Also, it is already reported that the reactive Ti electrode can scavenge O-ions (formation of thin TiOx layer) from underlying HfAlOx insulator due to its weakly bonded O-atoms [26]. So in the SET process, VO is accumulated near the CFs and the oxygen ions (O‒) are depleted due to the external electric field, which further connects the top and bottom electrode and brings the device into a low-resistance state (LRS) [27]. Schematic illustration is described in the inset of Fig. 2b. During RESET operation, the O‒ migrated back to the tip of the CFs and recombined with VO, narrowing the CFs and increasing the device's resistance (HRS). As shown in Fig. 2e, the enhancement in the memory window can be the results from denser and bigger CFs due to the surface defects (originated from TiOxNy/HfAlOx interface) of embedded TiN-NPs inside HfAlOx [9]. The enhancement of Ion/Ioff ratio during the endurance test up to 1000 cycles of NP-embedded RRAM device clearly indicated that the induced oxygen vacancy generation was prominent due to the larger effective area of TiN-NP surface. Also, according to Gao et al., the presence of metal NPs inside switching insulators enhances the local electric field, which further helps the formation of CFs and rupture during the RESET process [16]. The inset of Fig. 2e shows the local field enhancement and formation and rupture of CFs during SET and RESET due to TiN-NPs present inside amorphous HfAlOx matrix. A similar phenomenon has also been reported earlier by Liu et al. [14]. According to Gao et al. and Liu et al., Ag and Cu NPs inside the switching layers enhance the electric field around the NPs and form the conical shaped conducting filament, improving the uniformity of the witching cycles and reducing the switching electric field. However, these NPs may dissolve into Ag or Cu cations during the switching process. These mobile metal ions can migrate and deposit on the electrodes. So, the SET and RESET process involves both oxygen vacancy and migrated metal ions, as reported previously by Gao et al. and Liu et al. In this experiment, the TiN-NP does not dissolve after applying an external electric field and maintaining the original shape. Also, the surface oxidation of TiN-NP helps form a TiOxNy/HfAlOx interface which further allows controlled stepwise gradual SET and RESET characteristics.
To evaluate the atomic point contacts (APCs) in Au/Ti/HfAlOx/TiN-NP/HfAlOx/ITO RRAM device with quantized conductance, the electroforming and first RESET of the device were restricted with minimum current compliance and RESET voltage as shown in Fig. 3a. CFs were found to be formed by slowly increasing the forming voltage with a step of ‒0.05 V, and at ~ ‒5.0 V, electroforming was observed at Icc of 10µA. Similarly, during the first RESET of the device, with a step voltage of + 0.05 V, full RESET was achieved at + 1.2 V. By tuning the conductive filament size, the quantized conductance states were controlled due to APCs creation and annihilation process [4, 28]. Figure 3b shows the RESET I-V characteristics with the distinguishable stepwise decrease in currents, indicating different quantized conductance levels. With similar behavior, repetitive ten cycles were recorded in Au/Ti/HfAlOx/TiN-NP/HfAlOx/ITO RRAM device. As the voltage sweep rate is critical to achieving conductance quantization behavior, during the measurement, a very slow DC sweep rate was applied (0.002 V/step) as the change in quantized states lasted for a very narrow voltage region [29]. Normalized conductances (G/G0) have been plotted in Fig. 3c, which shows initially the conductance jumps down to ~ 3.5G0 due to CFs dissolution atom-by-atom. Continuously increasing the RESET step voltage, the conductance of the devices becomes stable at integer and half-integer multiples of ~ 2.5 G0, ~ 2 G0, and ~ 1.5 G0, which clearly shows the quantized conductance behavior. Although the physical reason for the half-integer conductance is yet to be explored, according to Shu et al., the possible explanation is assumed to be due to the presence of diffused other atomic metal impurities near the CFs shift Fermi energy level of CF [30]. Similar half-integer conductance was also observed in ZnO, HfO2, Nb2O5, SiO2 oxide-based switching layers [4, 5, 19, 31].
The statistical distribution of the normalized quantized conductance is plotted in Fig. 3d. Conductance peaks were found to be concentrate near the integer, and half-integer multiples of G0 counted with quantized conductance states in every 0.1G0/step as discussed above. So this phenomenon reflects the fact that TiN-NP-based HfAlOx switching layers are suitable for conductance quantization during the switching process. In this case, due to the presence of TiN-NP, the nanoscale CFs formation during forming process give an ideal condition to realize the quantized conductance [32]. Schematic illustration is drawn in Fig. 3e, which explains the CF formation and dissolution of CF by O‒ recombination to VO. The VO and O‒ are separated during the forming process and form the localized CFs assisted by the TiN-NPs inside HfAlOx at negative applied voltage to the top electrode. After successively increasing RESET voltage step by step by positive electric field at the top electrode, the conductance decreases driven by oxygen ions that recombine O‒ to VO in an atomic scale. Precise control of quantized conductance state also has been demonstrated by both negative pulse from ‒0.54 V/1 ms to ‒0.8 V/1 ms during potentiation and positive pulse from + 0.58 V/1 ms to + 0.84 V/1 ms during depression at interval of 0.5 s as shown in Fig. 3f, and g. Increasing/decreasing conductance at the read voltage of ± 0.1 V as shown in Fig. 3 confirmed the change of conductance by increasing pulse amplitude. During application of negative pulse, initially, the normalized conductance ~ 1G0, and after application of negative pulse amplitude up to ‒0.8 V, the conductance increases to ~ 3.5G0. A similar decrease in conductance was observed with stable integer and half-integer of G0 after applying pulse amplitude up to ‒0.84 V. This behavior shows the stability of the CFs due to the presence TiN-NP inside HfAlOx matrix. Similar behavior of conductance control is also demonstrated by Younis et al. and Gao et al. [29, 33]. Details of measurement techniques and plotting for the quantized conductance are given in the supplementary material under Additional file 1: Fig. S6(a), and (b).
To emulate the biological synapse through the synaptic weight changes is known as synaptic plasticity which includes short-term plasticity (STP) and long-term potentiation (LTP) and can be measured by excitatory postsynaptic current (EPSC) [34,35,36]. Also, the conversion from STP to LTP process in biological synapses can be possible by rehearsing the applied stimulation [37]. Synaptic weight (SW) change has been recorded to evaluate these characteristics depending on the increasing spike number and frequency, as shown in Fig. 4a–d. The EPSC was found to be increased gradually depending on the spiking number, as shown in Fig. 4a. In supporting information, increasing SW has been presented under different applied pulse voltage amplitude (at ‒0.3 V/100 µs to ‒0.7 V/100 µs) with pulse number of 1 to 10 as shown in Additional file 1: Fig. S5. It was clearly demonstrated as expected depending on the pulse amplitude and numbers, EPSC increased gradually in accordance with the presynaptic spike. Similar EPSC increment behavior dependence of presynaptic spikes voltage was observed by Yu et al. [38]. Maximum EPSC recorded during the first and final pulse input was denoted by the An and A1. EPSC gain (An/A1) plotted in Fig. 4b clearly demonstrates the SW increment depending on the pulse number and spike amplitudes. Short-term memory (STM) to long-term memory (LTM) transition was observed after increasing the spike number from 1(STM) to 10(LTM) at the spike voltage of ‒0.4 V/100 µs, as the postsynaptic current at the base voltage of ‒0.1 V increased (resting current) indicated by the arrow in Fig. 4a. Similar transition behavior has been observed by Kim et al. and Chen et al. [36, 39]. It is interesting to note that at low spike voltage (‒0.3 V/100 µs), even after the application of 10 pulses, memory transition did not occur at the read voltage of ‒0.1 V (shown in Additional file 1: Fig. S5), which confirms the short-term plasticity due to weak filament formation [35]. Depending on the repetition of spikes, the STM to LTM transition increased the filament size accumulating the O-vacancies near the TiN-NPs surface inside the HfAlOx matrix. The schematic model transition from STP to LTP depends on the process of rehearsal repetition, as shown in Fig. 4a [36]. After the application of 1 to 5 pulse stimuli, the conductance temporarily increases, but due to the weak filament formation, the synaptic weight quickly returns to its initial state. Although after application of 10 and more stimuli at the same spike amplitude, highly increased conductance of synapses was observed due to induced strong filaments formed by the O-vacancies. As a result, the CFs found not to be ruptured quickly, and consequently, the pulse-induced O-vacancy inside the switching layer remained stored, leading to LTM.
Absorption of O-vacancy near the conductive filaments can also be controlled by altering the spike frequency. Synaptic filtering characteristics (spike rate-dependent plasticity, SRDP) were also studied with increasing applied pulse frequency from 2 to 100 Hz (decreasing the spike interval) [40]. As shown in Fig. 4c, the pulse amplitude was constant at ‒0.5 V/20 µs and the representative EPSC was presented by applying 10 consecutive presynaptic pulses with different frequencies. The EPSC gain (A10/A1), as shown in Fig. 4d, was increased from 0.2 to 1.7 by increasing the frequency from 2 to 100 Hz confirmed the filtering characteristics. At low frequency (with longer delay time), the EPSC changes due to the applied spike but due to the longer delay, most of the accumulated O-vacancies migrated back, leading to less EPSC gain[34, 41,42,43]. Although due to the higher frequency enhanced EPSC gain achieved, the diffused O-ions (formation of O-vacancy) were unable to reach back to its initial state with such a short time[34]. As shown in Fig. 4c, the arrow on the resting current after 100 Hz pulse frequency indicates that the STM turns into LTM with stronger intensity. A magnified EPSC at the pulse frequency of 100 Hz is presented in the inset of Fig. 4d. So, TiN-NP inserted HfAlOx switching layer properties can mimic synaptic dynamic high-pass filtering characteristics, which is very important for neuromorphic computing [44]. The measurement details and data processing method for EPSC variation under different spike number and frequency scheme are described in Additional file 1: Fig. S7 and Fig. S8.
Conclusion
In summary, we have demonstrated a well-controlled stepwise change of quantum conductance in the Au/Ti/HfAlOx/TiN-NP/HfAlOx/ITO RRAM device. Atomic layer deposition of TiN-NP enables controlling a very low thickness of the overall switching layer. The presence of TiN-NP inside the HfAlOx matrix enhances the memory window due to the TiOxNy/HfAlOx interface on the surface of TiN-NP, which helps for gradual change in conductance in atomic scale. The conductance quantization and multilevel memory behaviors controlled by TiN-NP inside HfAlOx show the suitability for implementing high-density memory storage. A conductance state transition from short-term plasticity to long-term potentiation behavior also suggests that HfAlOx/TiN-NP/HfAlOx switching layer can be mimicked similar to biological synapses.
Availability of data and material
All data generated or analyzed during this study are included in this article and its supplementary information file.
Abbreviations
- NP:
-
Nanoparticles
- RRAM:
-
Resistive random access memory
- ALD:
-
Atomic layer deposition
- TiN:
-
Titanium nitride
- CF:
-
Conductive filament
- DC:
-
Direct current
- NCs:
-
Nanocrystals
- APCs:
-
Atomic point contacts
- STP:
-
Short-term plasticity
- LTP:
-
Long-term potentiation
- ITO:
-
Indium tin oxide
- TEs:
-
Top electrodes
- HRS:
-
High-resistance states
- LRS:
-
Low-resistance states
- FIB:
-
Focused ion beam
- TEM:
-
Transmission electron microscope
- RS:
-
Resistive switching
- EDS:
-
Energy-dispersive spectroscopy
- SEM:
-
Scanning electron microscopic
- STEM:
-
Scanning transmission electron microscopy
- EPSC:
-
Excitatory postsynaptic current
- SW:
-
Synaptic weight
References
Strukov DB, Snider GS, Stewart DR, Williams RS (2008) The missing memristor found. Nature 453:80–84. https://doi.org/10.1038/nature06932
Waser R, Dittmann R, Staikov C, Szot K (2009) Redox-based resistive switching memories nanoionic mechanisms, prospects, and challenges. Adv Mater 21:2632–2663. https://doi.org/10.1002/adma.200900375
Sun W, Gao B, Chi M et al (2019) Understanding memristive switching via in situ characterization and device modeling. Nat Commun 10:3453. https://doi.org/10.1038/s41467-019-11411-6
Zhu X, Su W, Liu Y et al (2012) Observation of conductance quantization in oxide-based resistive switching memory. Adv Mater 24:3941–3946. https://doi.org/10.1002/adma.201201506
Xue W, Li Y, Liu G et al (2020) Controllable and stable quantized conductance states in a Pt/HfOx/ITO memristor. Adv Electron Mater 6:1–9. https://doi.org/10.1002/aelm.201901055
Ryu SW, Cho S, Park J et al (2014) Effects of ZrO2 doping on HfO2 resistive switching memory characteristics. Appl Phys Lett. https://doi.org/10.1063/1.4893568
Mahata C, Kim S (2021) Modified resistive switching performance by increasing Al concentration in HfO2 on transparent indium tin oxide electrode. Ceram Int 47:1199–1207. https://doi.org/10.1016/j.ceramint.2020.08.238
Lin KL, Hou TH, Shieh J et al (2011) Electrode dependence of filament formation in HfO2 resistive-switching memory. J Appl Phys. https://doi.org/10.1063/1.3567915
Sakellaropoulos D, Bousoulas P, Tsoukalas D (2019) Impact of Pt embedded nanocrystals on the resistive switching and synaptic properties of forming free TiO2-x/TiO2-y-based bilayer structures. J Appl Phys. https://doi.org/10.1063/1.5094242
Bousoulas P, Stathopoulos S, Tsialoukis D, Tsoukalas D (2016) Low-power and highly uniform 3-b multilevel switching in forming free TiO2-x-based RRAM with embedded Pt nanocrystals. IEEE Electron Dev Lett 37:874–877. https://doi.org/10.1109/LED.2016.2575065
Mahata C, Lee C, An Y et al (2020) Resistive switching and synaptic behaviors of an HfO2/Al2O3 stack on ITO for neuromorphic systems. J Alloys Compd 826:154434. https://doi.org/10.1016/j.jallcom.2020.154434
Yan X, Zhao J, Liu S et al (2018) Memristor with Ag-cluster-doped TiO2 films as artificial synapse for neuroinspired computing. Adv Funct Mater 28:1705320. https://doi.org/10.1002/adfm.201705320
Pei Y, Yan L, Wu Z et al (2021) Artificial visual perception nervous system based on low-dimensional material photoelectric memristors. ACS Nano 15:17319–17326. https://doi.org/10.1021/acsnano.1c04676
Liu C-Y, Huang J-J, Lai C-H, Lin C-H (2013) Influence of embedding Cu nano-particles into a Cu/SiO2/Pt structure on its resistive switching. Nanoscale Res Lett 8:156. https://doi.org/10.1186/1556-276X-8-156
Wang DT, Dai YW, Xu J et al (2016) Resistive switching and synaptic behaviors of TaN/Al2O3/ZnO/ITO flexible devices with embedded Ag nanoparticles. IEEE Electron Device Lett 37:878–881. https://doi.org/10.1109/LED.2016.2570279
Gao L, Li Y, Li Q et al (2017) Enhanced resistive switching characteristics in Al2O3 memory devices by embedded Ag nanoparticles. Nanotechnology. https://doi.org/10.1088/1361-6528/aa6cd0
Frascaroli J, Brivio S, Covi E, Spiga S (2018) Evidence of soft bound behaviour in analogue memristive devices for neuromorphic computing. Sci Rep 8:1–12. https://doi.org/10.1038/s41598-018-25376-x
Zhang W, Gao B, Tang J et al (2019) Analog-type resistive switching devices for neuromorphic computing. Phys Status Solidi - Rapid Res Lett 13:1–13. https://doi.org/10.1002/pssr.201900204
Deswal S, Malode RR, Kumar A, Kumar A (2019) Controlled inter-state switching between quantized conductance states in resistive devices for multilevel memory. RSC Adv 9:9494–9499. https://doi.org/10.1039/C9RA00726A
Li Y, Long S, Liu Y et al (2015) Conductance quantization in resistive random access memory. Nanoscale Res Lett. https://doi.org/10.1186/s11671-015-1118-6
Petzold S, Piros E, Eilhardt R et al (2020) Tailoring the switching dynamics in yttrium oxide-based RRAM devices by oxygen engineering: from digital to multi-level quantization toward analog switching. Adv Electron Mater 6:1–13. https://doi.org/10.1002/aelm.202000439
Zhao J, Zhou Z, Zhang Y et al (2019) An electronic synapse memristor device with conductance linearity using quantized conduction for neuroinspired computing. J Mater Chem C 7:1298–1306. https://doi.org/10.1039/C8TC04395G
Song G-T, Wang Y, Qi Y et al (2020) Fabrication of titanium nitride nanoparticles onto carbon nanotubes by atomic layer deposition for utilization as Pt electrocatalyst supports. Rare Met 39:784–791. https://doi.org/10.1007/s12598-019-01284-5
Mahata C, Kim S (2021) Electrical and optical artificial synapses properties of TiN-nanoparticles incorporated HfAlO-alloy based memristor. Chaos, Solitons Fractals 153:111518. https://doi.org/10.1016/j.chaos.2021.111518
Wu Q, Banerjee W, Cao J et al (2018) Improvement of durability and switching speed by incorporating nanocrystals in the HfOx based resistive random access memory devices. Appl Phys Lett. https://doi.org/10.1063/1.5030780
Sokolov AS, Son SK, Lim D et al (2017) Comparative study of Al2O3, HfO2, and HfAlOx for improved self-compliance bipolar resistive switching. J Am Ceram Soc 100:5638–5648. https://doi.org/10.1111/jace.15100
Huang YJ, Chao SC, Lien DH et al (2016) Dual-functional memory and threshold resistive switching based on the push-pull mechanism of oxygen ions. Sci Rep 6:1–10. https://doi.org/10.1038/srep23945
Petzold S, Piros E, Eilhardt R et al (2020) Tailoring the switching dynamics in yttrium oxide-based RRAM devices by oxygen engineering: from digital to multi-level quantization toward analog switching. Adv Electron Mater 6:2000439. https://doi.org/10.1002/aelm.202000439
Younis A, Chu D, Li S (2014) Voltage sweep modulated conductance quantization in oxide nanocomposites. J Mater Chem C 2:10291–10297. https://doi.org/10.1039/c4tc01984a
Shu C, Li CZ, He HX et al (2000) Fractional conductance quantization in metallic nanoconstrictions under electrochemical potential control. Phys Rev Lett 84:5196–5199. https://doi.org/10.1103/PhysRevLett.84.5196
Mehonic A, Vrajitoarea A, Cueff S et al (2013) Quantum conductance in silicon oxide resistive memory devices. Sci Rep 3:1–8. https://doi.org/10.1038/srep02708
Zhao X, Xu H, Wang Z et al (2015) Nonvolatile/volatile behaviors and quantized conductance observed in resistive switching memory based on amorphous carbon. Carbon N Y 91:38–44. https://doi.org/10.1016/j.carbon.2015.04.031
Gao S, Zeng F, Chen C et al (2013) Conductance quantization in a Ag filament-based polymer resistive memory. Nanotechnology. https://doi.org/10.1088/0957-4484/24/33/335201
Chen J, Li E, Yan Y et al (2019) Flexible metal oxide synaptic transistors using biomass-based hydrogel as gate dielectric. J Phys D Appl Phys. https://doi.org/10.1088/1361-6463/ab3ea9
Zhou L, Yang S, Ding G et al (2019) Tunable synaptic behavior realized in C 3 N composite based memristor. Nano Energy 58:293–303. https://doi.org/10.1016/j.nanoen.2019.01.045
Kim MK, Lee JS (2018) Short-term plasticity and long-term potentiation in artificial biosynapses with diffusive dynamics. ACS Nano 12:1680–1687. https://doi.org/10.1021/acsnano.7b08331
McGaugh JL (2000) Memory–a century of consolidation. Science (80-) 287:248–251. https://doi.org/10.1126/science.287.5451.248
Yu F, Zhu LQ, Gao WT et al (2018) Chitosan-based polysaccharide-gated flexible indium tin oxide synaptic transistor with learning abilities. ACS Appl Mater Interfaces 10:16881–16886. https://doi.org/10.1021/acsami.8b03274
Chen H, Liu C, Wu Z et al (2019) Time-tailoring van der waals heterostructures for human memory system programming. Adv Sci. https://doi.org/10.1002/advs.201901072
Shim H, Sim K, Ershad F et al (2019) Stretchable elastic synaptic transistors for neurologically integrated soft engineering systems. Sci Adv 5:1–12. https://doi.org/10.1126/sciadv.aax4961
Li X, Yu B, Wang B et al (2020) Multi-terminal ionic-gated low-power silicon nanowire synaptic transistors with dendritic functions for neuromorphic systems. Nanoscale 12:16348–16358. https://doi.org/10.1039/d0nr03141k
Pillai PB, De Souza MM (2017) Nanoionics-based three-terminal synaptic device using zinc oxide. ACS Appl Mater Interfaces 9:1609–1618. https://doi.org/10.1021/acsami.6b13746
Wu G, Feng P, Wan X et al (2016) Artificial synaptic devices based on natural chicken albumen coupled electric-double-layer transistors. Sci Rep 6:23578. https://doi.org/10.1038/srep23578
Wang Y, Yang Y, He Z et al (2020) Laterally coupled 2D MoS2 synaptic transistor with ion gating. IEEE Electron Device Lett 41:1424–1427. https://doi.org/10.1109/LED.2020.3008728
Acknowledgements
Not applicable.
Funding
This research was supported by National R&D Program through the National Research Foundation of Korea (NRF) funded by Ministry of Science and ICT(2020M3F3A2A01085755) and in part by Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education (2018R1A6A1A03023788).
Author information
Authors and Affiliations
Contributions
CM designed the experiment, performed the electrical measurements, analyzed the results and drafted the paper. MI participated in partial performed the electrical measurements and collecting data. MK and SK supervised the work and helped correction of the manuscript. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Additional file 1.
Supporting information.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mahata, C., Ismail, M., Kang, M. et al. Synaptic Plasticity and Quantized Conductance States in TiN-Nanoparticles-Based Memristor for Neuromorphic System. Nanoscale Res Lett 17, 58 (2022). https://doi.org/10.1186/s11671-022-03696-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-022-03696-2