Abstract
Porous ZnFe2O4 hollow microspheres with a diameter of about 100–210 nm were successfully prepared by simple template-free hydrothermal route in ethylene glycol (EG) solution. The formation mechanism and properties have been also demonstrated. The structural, morphological, and magnetic properties of ZnFe2O4 hollow microspheres were investigated by means of X-ray powder diffraction (XRD), field emission scanning electron microscopy, Fourier transform infrared spectroscopy, and physical properties measurements system. The surface area was determined using the BET method. XRD and IR analyses confirm the cubic spinel phase of ZnFe2O4 hollow microspheres. Every magnetic microsphere is made up of many ultrafine ZnFe2O4 nanoparticles with porous structure. The as-prepared porous magnetic hollow spheres have higher surface area and excellent magnetic properties at room temperature.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Background
The ecofriendly functional nanostructures, such as transition metal oxides with spinel structure MFe2O4 (M = Mn, Fe, Co, Ni, Zn, etc.) have attracted considerable attention in the recent decade because of the fundamental scientific interest in relation to size/shape effects and their potential technological applications in many important fields [1]. Among the family of ferrite materials, zinc ferrite (ZnFe2O4) has a normal spinel structure with the tetrahedral A sites preferentially occupied by Zn2+ and octahedral B sites occupied by Fe3+, which results in anti-ferromagnetic properties at TN = 10 K [2].
In recent years, hollow micro-nano-materials have attracted broad attention due to their superior properties, such as low density, large specific area, distinct magnetic property, well-defined pore topology, and more appropriate pore size (>50 nm) compared with nanocrystalline materials, and have been proven to be promising in widespread applications in microelectronics, drug delivery, catalysis, energy storage, and gas sensing [3–6]. It has been found that nano-scaled materials exhibit promising properties that are quite different from their corresponding bulk materials [7]. Worldwide research efforts are underway to find new applications for ferrites in addition to improving their existing functional properties. In the past, various methodologies have been adopted for the preparation of hollow spheres [8–12]. However, the main process for the preparation of hollow spheres generally requires removable templates such as monodispersed silica, polystyrene latex spheres, metal nanoparticles, gas bubbles, and polymer spheres followed by sequential adsorption of magnetic nanoparticles on the templates [13–18]. The typical procedure is that the template is coated by either direct surface reaction utilizing special functional groups on the core or controlled precipitation of inorganic precursors on the surface of template to induce coating, followed by the removal of template core through calcination or solvent dissolution [19–21]. Definitely, the template or surfactant direct synthesis suffers from the disadvantages of low yield and high cost; template-free methods have drawn increasing attention.
As the magnetic properties of these spinel ferrite nanocrystallines are affected by their morphology, shape-controlled synthesis of spinel ferrites has attracted much attention. The past two decades have seen a wealth of methods to synthesize different ZnFe2O4 nanostructures with uniform size and shape, including nanoflowers [22], nanotubes [23], nanorods [24], and nanocubes [17].
However, there are still no reports for the preparation of porous zinc ferrite hollow microspheres. It appears that it remains a challenge to explore an economic, template-free, and effective strategy to synthesize magnetic ZnFe2O4 with sphere morphology. The purpose of our study is to synthesize monodispersed purified hollow ferrite spheres in low temperature from EG solution with simple template-free hydroothermal method. Zinc chloride and ferric chloride were used as cation sources in the reaction system. EG and polyethylene glycol (PEG) were used as solvent and surfactant, respectively, and sodium acetate as a weak base. The phase structure, morphology, elemental, and magnetic behavior of the hollow microspheres were investigated in detail.
Methods
Magnetic ZnFe2O4 hollow spheres were synthesized by simple template-free hydrothermal method. All of the reactants were analytical grade and were used without any further purification. The starting materials for the present study included FeCl3·6H2O, ZnCl2·4H2O, sodium acetate (CH3COONa 3H2O,), ethylene glycol (EG), and PEG. A typical synthesis was performed as follows: 1.35 g FeCl3·6H2O and 0.55 g ZnCl2·4H2O were dissolved into 40 mL EG. About 3.6 g NaAc and 2 g PEG were added into the solution and stirred under 50 °C for 30 min to form a homogeneous brown solution. The hydrothermal synthesis was carried out in a 100mL Teflon-lined stainless steel autoclave cell without any agitation for 16 h at 180 °C. After being cooled to room temperature, the black products were collected by a magnet, washed several times with distilled water to remove the impurities, and finally dried at 80 °C for 8 h. The yield of ZnFe2O4 microspheres is relatively high (85.9 %) for hydrothermal method.
The crystal structure was determined using X-ray diffraction (XRD, Bruker D2 Advanced Diffractometer with Cu Kα radiation). Morphological studies were conducted using field emission scanning electron microscope (FE-SEM, Hitachi S-4800). The element distribution and the content (wt%) of ZnFe2O4 within the hollow spheres were detected by energy dispersive X-ray spectroscopy (EDX). The specific surface area of the obtained material was measured according to the Brunauer–Emmett–Teller (BET) method using Micromeritics ASAP-2020 V4.0 apparatus with liquid nitrogen at 77 K. BET surface area of ZnFe2O4 was determined to be 44.163 m2 g−1. The FTIR spectrum was recorded on a KBr pellet (Bruker Tensor 27). Magnetic studies at room temperature have been carried out using physical properties measurement system (PPMS).
Results and discussion
XRD patterns of all samples show very broad peaks, indicating poor crystallinity and ultrafine nature of the particles. The crystalline structure of the as-synthesized ZnFe2O4 hollow sphere was characterized by powder XRD. As shown in Fig. 1, the diffraction peaks match well with the standard patterns of the cubic structure of spinel-phase Zn ferrite (JCPDS file no. 82–1042), where the diffraction peaks at 2θ values of 30.0°, 35.3°, 42.9°, 53.2°, 56.7°, 62.3°, and 76.6° can be attributed to the reflection of (220), (311), (400), (422), (333), (440), and (533) planes of the spinel ZnFe2O4, respectively. No additional peak of the impurity phase was observed in the XRD patterns, showing that the prepared ferrites are pure.
The general morphology of the as-prepared ZnFe2O4 hollow sphere products observed by field emission SEM (FE-SEM) and typical images at different magnifications are shown in Fig. 2a–c, it was observed that the major morphological feature is a regular spherical shape with an average particle diameter of about 100–210 nm. The high-magnification FE-SEM image (Fig. 2c) reveals that each micro-hollow sphere is very similar to hollow spheres and it is actually composed of aggregates of more primary particles.
EDX results from hollow spheres showed that it was mainly composed of Zn, Fe, and O (Fig. 2d). Quantification of the EDX spectrum showed that the ratio of Zn, Fe, and O was about 1:2:4, suggesting that the porous hollow spheres had a chemical formula of ZnFe2O4.
On the basis of the above experimental results and observations, a formation mechanism of the ZnFe2O4 hollow spheres is designed, schematically illustrated in Fig. 3. The reaction begins with the mixture of FeCl3·6H2O, ZnCl2·4H2O, Sodium acetate (CH3COONa 3H2O), EG, and PEG. In our system, the Zn2+ and Fe3+ ions were nucleated under hydrothermal conditions with the water generated from metal precursors to form nanosized crystalline ZnFe2O4. PEG serves as a structure-directing template, as it can easily self-assemble to form spherical grains. The Ostwald ripening process also plays an important role in the formation of nanocrystals. According to the Ostwald ripening mechanism, crystalline particles will grow into crystalline nuclei, which aggregate isotropically to form spherical grains in ethanol solution and further to microspherical crystallites. During growth, the smaller, less crystalline particles will be dissolved gradually, while the larger, more crystalline particles will grow bigger. Eventually, the core can grow gradually to form a solid sphere. As the crystal grows, the porous ZnFe2O4 microsphere was formed at last. Finally, the massy porous ZnFe2O4 microspheres are formed, as evidenced by XRD (Fig. 1), SEM (Fig. 2), TGA (Fig. 4), and FTIR (Fig. 6).
As shown in Fig. 4, the TG curve shows that porous ZnFe2O4 hollow spheres have three weight loss steps from room temperature to 800 °C under air atmosphere. The first weight loss of about 3.7 % in the range 25–220 °C was due to the loss of residual water in ZnFe2O4 hollow spheres. The combustion of carbon was complete at a relatively low temperature (<400 °C). From the weight change between 150 and 400 °C, the organic matter content (carbon and oxygen containing surface groups) was determined to be 40 wt%.
The nitrogen sorption isotherm of resultant ZnFe2O4 hollow spheres and their corresponding pore-size distribution curve are exhibited in Fig. 5. The nitrogen adsorption desorption isotherm belongs to type IV category according to international union of pure and applied chemistry classification, suggesting the presence of mesopores. The specific surface area was thus estimated, by BET equation [25], to be 44 m2 g−1. In addition, the sorption exhibits type IV isotherm, and the pore analysis has revealed that the pore sizes in the porous microspheres mainly fall into 3–9 nm, as seen in the inset of Fig. 5. Hysteresis loops can be observed in the curve, attest to the existence of a mesoporous structure. The high surface area and pore volume further confirm that the hollow microspheres have porous structure which will broaden the application of the product.
Theoretically, all MFe2O4 either normal or inverse spinel oxides of transition metals have four infrared active modes. These vibrations occur at frequencies of ν1 (650–550 cm−1), ν2 (525–390 cm−1), ν3 (380–335 cm−1), and ν4 (300–200 cm−1) [26].
The ν1 and ν2 bands are generated due to intrinsic vibrations of tetrahedral and octahedral coordination compounds. Absorption of ν1 happens due to the bond stretching of tetrahedral metal ions and oxygen, while ν2 vibration is observed due to the vibration of oxygen in the direction perpendicular to the axis joining the tetrahedral ions and oxygen. The ν3 mode is obtained from the Fe3+–O complexes at octahedral sites [27]. The frequency of ν4 vibration depends on the mass of tetrahedral metal ion complexes, which gives information about the vibration of ions occupying at tetrahedral site.
In order to make sure of its chemical compositions, the Fourier transform infrared spectrometry (FTIR) spectrum of the ZnFe2O4 hollow sphere product was verified. As shown in Fig. 6, the two bands at 582 and 435 cm−1 represented the characteristic peaks of tetrahedral and octahedral Fe–O stretching for ZnFe2O4. The appearance of bands at 1,081 and 2,925 cm−1 is assigned to the stretching of ether groups and the characteristic absorptions of alkyl (R-CH2) stretching modes. In addition, the bands at 3,432 and 1,650 cm−1 are attributed to the surface hydroxyl and the adsorbed water molecules, respectively [28]. Hydroxyl group contribution was observed at 3,432 cm−1. The appearance of these peaks in the spectrum confirmed the presence of PEG and adsorbed EG on the surface of particles. The above FTIR analysis matches well with the XRD result, which confirms that the as-obtained products are pure-phase spinel Zn ferrite.
Such porous oriented ZnFe2O4 hollow spheres exhibited good magnetic property [29]. Magnetic measurements of the samples were carried out at room temperature using a PPMS with a peak field of 20 kOe. The hysteresis loops for porous zinc ferrite hollow microspheres are shown in Fig. 7. As clearly shown, the variation of magnetization as a function of the applied field presents a narrow cycle, and the observed hysteresis loops are a characteristic behavior of soft magnetic materials. The saturation magnetization (Ms) of the zinc ferrite hollow spheres is about 32 emu g−1, which is close to the value of bulk ZnFe2O4 (36 emu g−1) [30]. The low saturation magnetization of the ferrite NPs is generally believed to be due to the decreased particle size and the presence of an anti-ferromagnetic layer on the surface. In the close-up view (not shown in Figure), the curve presents a very small hysteresis loop with a remnant magnetization (Mr) of 1.3 emu g−1 and a coercivity (Hc) of 16 Oe, denoting the ferromagnetic behavior of the sample. Table 1 shows the previously reported saturation magnetization values for zinc ferrite nanocrystallines synthesized by various methods [31–37], from which we could conclude that our present Ms value at ambient temperature is obviously higher than that of most of the reported uniform ZnFe2O4 nanocrystallines through the facial hydrothermal synthesis.
Conclusions
ZnFe2O4 hollow microspheres with diameters of about 210 nm were successfully synthesized under low temperature through template-free hydrothermal method. These ZnFe2O4 porous hollow spheres have excellent magnetic properties and higher surface area. The proposed method is easy, nontoxic, and reproducible. EG plays a key role in the synthesis of hollow spheres. Further work to investigate and fabrication of Co, Mn, and NiFe2O4 hollow microspheres is in progress. This method may provide a simple and scalable synthesis approach for preparing advanced materials based on various multicomponent hollow structures for multipurpose application.
References
Park, J., Joo, J., Kwon, S., Jang, Y., Hyeon, T.: Synthesis of monodisperse spherical nanocrystals. Angew. Chem. Int. Ed. 46, 4630 (2007)
Yao, C., Zeng, Q., Goya, G.F., Torres, T., Liu, J., Wu, H., Ge, M., Zeng, Y., Wang, Y., Jiang, J.Z.: ZnFe2O4 nanocrystals: synthesis and magnetic properties. J. Phys. Chem. C 111, 12274 (2007)
Lou, X.W., Archer, L.A., Yang, Z.C.: Hollow micro/nanostructures: synthesis and applications. Adv. Mater. 20, 3987 (2008)
Kathleen, J.P., Jules, S.J., Edith, M.: Double-walled polymer micro-spheres for controlled drug release. Nature 367, 258 (1994)
Penchal Reddy, M., Kim, I.G., Madhuri, W., Ramamanohar Reddy, N., Siva Kumar, K.V., Ramakrishna Reddy, R.: Microwave assisted sol-gel synthesis, characterization and magnetic properties of NiFe2O4 nanoparticles. J. Sol–Gel Sci. Technol. 70, 400 (2014)
Zhou, X.B., Han, Y.H., Zhou, J., Shen, L., Penchal Reddy, M., Lee, J., Bae, S.I., Lee, D.Y., Huang, Q.: Ferrite multiphase/carbon nanotube composites sintered by microwave sintering and spark plasma sintering. J. Ceram. Soc. Jpn. 122, 881 (2014)
Lai, X., Halpert, J.E., Wang, D.: Recent advances in micro-nano-structured hollow spheres for energy applications: from simple to complex systems. Energy Environ. Sci. 5, 5604 (2012)
Bruce, P.G., Scrosati, B., Tarascon, J.M.: Nanomaterials for rechargeable lithium batteries. Angew. Chem. Int. Ed. 47, 2930 (2008)
Lou, X.W., Yuan, C.L., Archer, L.A.: Double-walled SnO2 nano-cocoons with movable magnetic cores. Adv. Mater. 19, 3328 (2007)
Bourret, G.R., Lennox, R.B.: 1D Cu(OH)2 nanomaterial synthesis templated in water micro droplets. J. Am. Chem. Soc. 132, 6657 (2010)
Dhas, N.A., Suslick, K.S.: Sonochemical preparation of hollow nano-spheres and hollow nanocrystals. J. Am. Chem. Soc. 127, 2368 (2005)
Kim, D., Park, J., An, K.: Synthesis of hollow iron nano frames. J. Am. Chem. Soc. 129, 5812 (2007)
Peng, S., Sun, S.: Synthesis and characterization of monodisperse hollow Fe3O4 nanoparticles. Angew. Chem. Int. Ed. 46, 4155 (2007)
Ni, S.B., Lin, S.B., Pan, Q.T., Yang, F., Huang, K., Wang, X.Y., He, D.Y.: Synthesis of core-shell α-Fe2O3 hollow micro-spheres by a simple two-step process. J. Alloys. Compd. 478, 876 (2009)
Tada, M., Kanemaru, T., Hara, T., Nakagawa, T., Handa, H.: Synthesis of hollow ferrite nanospheres for biomedical applications. J. Magn. Magn. Mater. 321, 1414 (2009)
Li, Y.M., Li, W.Y., Chou, S.L., Chen, J.: Synthesis, characterization and electrochemical properties of aluminum-substituted alpha-Ni(OH)2 hollow spheres. J. Alloys Compd. 456, 339 (2008)
Wang, C., Xiangfeng, C., Mingmei, W.: Highly sensitive gas sensors based on hollow SnO2 spheres prepared by carbon sphere template method. Sens. Actuat. B 120, 508 (2007)
Schmidt, H.T., Ostafin, A.E.: Liposome directed growth of calcium phosphate nanoshells. Adv. Mater. 14, 532 (2002)
Gao, S., Zhang, H., Wang, X., Deng, R., Sun, D., Zheng, G.: ZnO-based hollow microspheres: biopolymer-assisted assemblies from ZnO nanorods. J. Phys. Chem. B. 110, 15847 (2006)
Yan, C., Xue, D.: Room temperature fabrication of hollow ZnS and ZnO architectures by a sacrificial template route. J. Phys. Chem. B. 110, 7102 (2006)
Kou, H., Wang, J., Pan, Y., Guo, J.: Fabrication of hollow ZnO microsphere with Zinc powder precursor Mater. Chem. Phys. 99, 325 (2006)
Lv, H., Ma, L., Zeng, P., Ke, D., Peng, T.: Synthesis of floriated ZnFe2O4 with porous nanorod structures and its photocatalytic hydrogen production under visible light. J. Mater. Chem. 20, 3665 (2010)
Zhang, G., Li, C., Cheng, F.: ZnFe2O4 tubes: synthesis and application to gas sensors with high sensitivity and low-energy consumption. J. Chem. Sens. Actuat. B. 120, 403 (2007)
Zu, P.C., Wen, Q.F., Zhang, B., Yang, H.G.: High-yield synthesis and magnetic properties of ZnFe2O4 single crystal nanocubes in aqueous solution. J. Alloys. Compd. 550, 348 (2013)
Brunauer, S., Emmett, P.H., Teller, E.: Adsorption of gases in multimolecular layers. J. Am. Chem. Soc. 60, 309 (1938)
Julien, C., Massot, M., Vicente, C.P.: Structural and vibrational studies of LiNi1−yCo y VO4 (0 ≤ y ≤ 1) cathodes materials for Li-ion batteries. Mater. Sci. Eng. B 75, 6 (2000)
Waldron, R.D.: Phys. Rev. 99, 1727 (1955)
Song, X.F., Gao, L.: Synthesis, characterization, and optical properties of well- defined N-doped, hollow silica/titania hybrid microspheres. Langmuir 23, 11850 (2007)
Han, C., Zhao, D., Deng, C., Hu, K.: A facile hydrothermal synthesis of porous magnetite microspheres. Mater. Lett. 70, 70 (2012)
Kurikka, V.P.M., Shafi, Y.K., Gedanken, A., Prozorov, R., Balogh, J., Lendvai, J., Felner, I.: Sonochemical preparation of nanosized amorphous NiFe2O4 particles. J. Phys. Chem. B 101, 6409 (1999)
Yu, S.H., Fujino, T., Yoshimura, M.: Hydrothermal synthesis of ZnFe2O4 ultrafine particles with high magnetization. J. Magn. Magn. Mater. 256, 420 (2003)
Bluncson, C.R., Thompson, G.K., Evans, B.J.: Fe Mössbauer investigations of manganese-containing spinels. Hyperfine Interact. 90, 353 (1994)
Hochepied, J.F., Bonville, P., Pileni, M.P.: Nonstoichiometric zinc ferrite nanocrystals: syntheses and unusual magnetic properties. J. Phys. Chem. B 104, 905 (2000)
Lin, D., Nunes, A.C., Majkrzak, C.F., Berkowitz, A.E.: Polarized neutron study of the magnetization density distribution within a ZnFe2O4 colloidal particle II. J. Magn. Magn. Mater. 145, 343 (1995)
Pradeep, A., Priyadharsini, P., Chandrasekaran, G.: Structural, magnetic and electrical properties of nanocrystalline zinc ferrite. J. Alloys Compd. 509, 3917 (2011)
Sivakumar, M., Takami, T., Ikuta, T., Towata, A., Yasui, K., Tuziuti, T., Kozuka, T., Bhattacharya, D., Iida, Y.: Fabrication of zinc ferrite nanocrystals by sonochemical emulsification and evaporation: observation of magnetization and its relaxation at low temperature. J. Phys. Chem. B 110, 15234 (2006)
Gutierrez, V.B., Puche, S.R., Fernandez, M.J.T.: Superparamagnetism and inter particle interactions in ZnFe2O4 nanocrystals. J. Mater. Chem. 22, 2992 (2012)
Acknowledgments
Dr. M. Penchal Reddy would like to acknowledge the financial support by CAS fellowship for Postdoctoral and Visiting scholars from Developing Countries (Grant No. 2014FFGB0003). One of the authors Xiaobing Zhou thanks Ningbo Natural Science Foundation (Grant No. 2013A610131) for the financial support. We are grateful to the Journal Editor and the anonymous reviewers for their constructive and useful comments which improve the scientific content of the original paper.
Author’s contributions
MLPR is a postdoctoral scientist who performed the experiment and prepared the manuscript. XBZ is a doctoral student who studied on nanostructures. SD and QH supervised in conducting this work. All authors read and approved the final manuscript.
Conflict of interest
The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
This article is published under license to BioMed Central Ltd. Open Access This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution, and reproduction in any medium, provided the original author(s) and the source are credited.
About this article
Cite this article
Matli, P.R., Zhou, X., Shiyu, D. et al. Fabrication, characterization, and magnetic behavior of porous ZnFe2O4 hollow microspheres. Int Nano Lett 5, 53–59 (2015). https://doi.org/10.1007/s40089-014-0135-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40089-014-0135-2