Abstract
High-entropy ceramics attract more and more attention in recent years. However, mechanical properties especially strength and fracture toughness for high-entropy ceramics and their composites have not been comprehensively reported. In this work, high-entropy (Ti0.2Zr0.2Hf0.2Nb0.2Ta 0.2)B2 (HEB) monolithic and its composite containing 20 vol% SiC (HEB–20SiC) are prepared by hot pressing. The addition of SiC not only accelerates the densification process but also refines the microstructure of HEB, resulting in improved mechanical properties. The obtained dense HEB and HEB–20SiC ceramics hot pressed at 1800 ℃ exhibit four-point flexural strength of 339±17 MPa and 447±45 MPa, and fracture toughness of 3.81±0.40 MPa·m1/2 and 4.85±0.33 MPa·m1/2 measured by single-edge notched beam (SENB) technique. Crack deflection and branching by SiC particles is considered to be the main toughening mechanisms for the HEB–20SiC composite. The hardness Hv0.2 of the sintered HEB and HEB–20SiC ceramics is 23.7±0.7 GPa and 24.8±1.2 GPa, respectively. With the increase of indentation load, the hardness of the sintered ceramics decreases rapidly until the load reaches about 49 N, due to the indentation size effect. Based on the current experimental investigation it can be seen that the room temperature bending strength and fracture toughness of the high-entropy diboride ceramics are within ranges commonly observed in structure ceramics.
Article PDF
Avoid common mistakes on your manuscript.
References
Yeh JW, Chen SK, Lin SJ, et al. Nanostructured high-entropy alloys with multiple principal elements: Novel alloy design concepts and outcomes. Adv Eng Mater 2004, 6: 299–303.
George EP, Raabe D, Ritchie RO. High-entropy alloys. Nat Rev Mater 2019, 4: 515–534.
Gild J, Zhang YY, Harrington T, et al. High-entropy metal diborides: A new class of high-entropy materials and a new type of ultrahigh temperature ceramics. Sci Rep 2016, 6: 37946–37956.
Zhang Y, Jiang ZB, Sun SK, et al. Microstructure and mechanical properties of high-entropy borides derived from boro/carbothermal reduction. J Eur Ceram Soc 2019, 39: 3920–3924.
Shen XQ, Liu JX, Li F, et al. Preparation and characterization of diboride-based high entropy (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)B2–SiC particulate composites. Ceram Int 2019, 45: 24508–24514.
Gu JF, Zou J, Sun SK, et al. Dense and pure high-entropy metal diboride ceramics sintered from self-synthesized powders via boro/carbothermal reduction approach. Sci China Mater 2019, 62: 1898–1909.
Failla S, Galizia P, Fu S, et al. Formation of high entropy metal diborides using arc-melting and combinatorial approach to study quinary and quaternary solid solutions. J Eur Ceram Soc 2020, 40: 588–593.
Chen H, Xiang HM, Dai FZ, et al. Porous high entropy (Zr0.2Hf0.2Ti0.2Nb0.2Ta0.2)B2: A novel strategy towards making ultrahigh temperature ceramics thermal insulating. J Mater Sci Tech 2019, 35: 2404–2408.
Sarker P, Harrington T, Toher C, et al. High-entropy high-hardness metal carbides discovered by entropy descriptors. Nat Commun 2018, 9: 4980.
Castle E, Csanádi T, Grasso S, et al. Processing and properties of high-entropy ultra-high temperature carbides. Sci Rep 2018, 8: 8609.
Wei XF, Liu JX, Li F, et al. High entropy carbide ceramics from different starting materials. J Eur Ceram Soc 2019, 39: 2989–2994.
Lu K, Liu JX, Wei XF, et al. Microstructures and mechanical properties of high-entropy (Ti0.2Zr0.2Hf0.2-Nb0.2Ta0.2)C ceramics with the addition of SiC secondary phase. J Eur Ceram Soc 2020, 40: 1839–1847.
Rost CM, Sachet E, Borman T, et al. Entropy-stabilized oxides. Nat Commun 2015, 6: 8485.
Jiang SC, Hu T, Gild J, et al. A new class of high-entropy perovskite oxides. Scripta Mater 2018, 142: 116–120.
Li F, Zhou L, Liu JX, et al. High-entropy pyrochlores with low thermal conductivity for thermal barrier coating materials. J Adv Ceram 2019, 8: 576–582.
Dong Y, Ren K, Lu YH, et al. High-entropy environmental barrier coating for the ceramic matrix composites. J Eur Ceram Soc 2019, 39: 2574–2579.
Qin Y, Liu JX, Li F, et al. A high entropy silicide by reactive spark plasma sintering. J Adv Ceram 2019, 8: 148–152.
Gild J, Braun J, Kaufmann K, et al. A high-entropy silicide: (Mo0.2Nb0.2Ta 0.2Ti0.2W0.2)Si2. J Materiomics 2019, 5: 337–343.
Chen XQ, Wu YQ. High-entropy transparent fluoride laser ceramics. J Am Ceram Soc 2020, 103: 750–756.
Li F, Bao WC, Sun SK, et al. Synthesis of single-phase metal oxycarbonitride ceramics. Scripta Mater 2020, 176: 17–22.
Ma HB, Man ZY, Liu JX, et al. Microstructures, solid solution formation and high-temperature mechanical properties of ZrB2 ceramics doped with 5vol.% WC. Mater Design 2015, 81: 133–140.
Zou J, Zhang GJ, Zhang H, et al. Improving high temperature properties of hot pressed ZrB2–20vol% SiC ceramic using high purity powders. Ceram Int 2013, 39: 871–876.
Zhang GJ, Jin ZZ, Yue XM. TiN–TiB2 composites prepared by reactive hot pressing and effects of Ni addition. J Am Ceram Soc 1995, 78: 2831–2833.
Smith CS. Introduction to grains, phases, and interfaces—An interpretation of microstructure. Trans AIME 1948, 175: 15–51.
Taya M, Hayashi S, Kobayashi AS, et al. Toughening of a particulate-reinforced ceramic-matrix composite by thermal residual stress. J Am Ceram Soc 1990, 73: 1382–1391.
Keihn FG, Keplin EJ. High-temperature thermal expansion of certain group IV and group V diborides. J Am Ceram Soc 1967, 50: 81–84.
Li H, Bradt RC. The microhardness indentation load/size effect in rutile and cassiterite single crystals. J Mater Sci 1993, 28: 917–926.
Gong JH, Wu JJ, Guan ZD. Examination of the indentation size effect in low-load Vickers hardness testing of ceramics. J Eur Ceram Soc 1999, 19: 2625–2631.
Jiang D Y. Recent progresses in the phenomenological description for the indentation size effect in microhardness testing of brittle ceramics. J Adv Ceram 2012, 1: 38–49.
Duan YB, Jiang DY, Hu J. Determination of the load-independent hardness by analyzing the nanoindentation loading curves: A case study on fused silica. J Adv Ceram 2019, 8: 583–586.
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Nos. 51532009, 51872045); Science and Technology Commission of Shanghai Municipality (No. 18ZR1401400); the Fundamental Research Funds for the Central Universities (Nos. 2232018D3-32, 2232019A3-13); and State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University (No. 19ZK0113).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence http://creativecommons.org/licenses/by/4.0/, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit http://creativecomm-ons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, JX., Shen, XQ., Wu, Y. et al. Mechanical properties of hot-pressed high-entropy diboride-based ceramics. J Adv Ceram 9, 503–510 (2020). https://doi.org/10.1007/s40145-020-0383-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40145-020-0383-8