Abstract
The International Telecommunication Union announced a new color gamut standard of broadcast service television (BT 2020) for ultra-high-definition TV in 2012. To satisfy the wide-color gamut standard of BT 2020, monochromatic red (R), green (G), and blue (B) emissions require a small full width at half-maximum, which is an important property for improving color purity. Although organic light-emitting diode (OLED) displays are currently one of the main types of display technologies, their broad emission via strong vibronic coupling between ground and excited states is a major hurdle to overcome in the development of next-generation wide-color gamut displays. Thus, the development of OLED emitters with narrowband R–G–B emissions is of great significance. In this review, the recent progress in the development of OLED materials with narrowband emission is summarized by grouping them into fluorescent, phosphorescent, and thermally activated delayed fluorescent emitters to reveal the correlation between molecular structures, optical properties, and device characteristics. We discuss rational molecular design strategies to achieve narrow photoluminescence and electroluminescence and the underlying mechanisms for controlling the emission bandwidth. Finally, the challenges in the realization of wide-color gamut OLED displays and the future prospects of such devices are discussed.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Since the first organic light-emitting diode (OLED) was successfully demonstrated by Tang and Slyke in 19871, OLEDs have been extensively studied in both academia and industry, becoming a mainstream display technology in full-color televisions and smartphones. They have various advantages, such as a light weight, fast response time, wide viewing angle, facile chemical tunability of emitting molecules, low energy consumption, compatibility with flexible plastic substrates, and form factors for various types of displays2. Based on the light-emitting mechanisms, different types of OLEDs have been developed: fluorescence (1st generation)-based, phosphorescence (2nd generation)-based, and thermally activated delayed fluorescence (TADF, 3rd generation)-based OLEDs3. Recently, extensive research on the 4th generation of OLEDs is in progress to improve the device efficiency, lifetime, and color purity in particular. Despite the many advantages of OLEDs, their emission spectra often show broad bandwidths, which are extremely detrimental to achieving high color purity for future high-end display electronics such as high-definition TV and ultra-high-definition TV (UHDTV).
The “CIE (International Commission on Illumination) 1931 color space” was first defined based on tristimulus values; then, the modified CIE 1976 was announced, and both CIE 1931 and 1976 became the most widely accepted standards to define emission colors in the field of displays4. The CIE coordinate visualizes the entire range of colors that can be obtained by mixing the three primary colors (red (R), green (G), and blue (B)) by varying the wavelength and emission intensity. In 2012, the International Telecommunication Union (ITU) announced a new color gamut standard for UHDTVs called the Broadcast Service Television 2020 (BT 2020) (Fig. 1)5. Compared to the previously reported BT 709, the color gamut became wider with CIE coordinates for the R, G, and B colors of (0.708, 0.292), (0.170, 0.797), and (0.131, 0.046), respectively. This change was made because of the growing demand for monochromatic R, G, and B colors to improve color purity (Fig. 1a) 6.
Vibronic coupling in fluorescent and phosphorescent organic emitters between the singlet ground state (S0) and the singlet (S1), or triplet (T1) excited states together with charge transfer (CT) interactions often induces broad peaks in both photoluminescence (PL) and electroluminescence (EL) spectra, showing a full width at half-maximum (FWHM) of over 70 nm7,8,9,10,11. Organic emitters show significantly broader emission spectra than inorganic quantum dots (QDs) and perovskite-based emitters, limiting the potential for OLEDs with the high color purity proposed by BT 202012. Thus, the development of OLED emitters with narrowband R, G, and B emissions with extremely small FWHM is of paramount importance. As seen in Fig. 1b, the color gamut becomes wider with decreasing FWHM values in the emission spectra, satisfying the color gamut standard of BT 202013,14.
In this review, we summarize recent developments and important studies of organic light-emitting materials and devices with narrowband emission. We categorize these materials and devices based on their emission mechanism by grouping them into fluorescent, phosphorescent, and TADF emitters (Fig. 1c). Since there is currently no clear definition of “narrow emission”, we mainly focused on recent reports of OLED materials with a FWHM smaller than 50 nm in their emission spectra (Fig. 1d). Rational molecular design strategies to achieve narrow PL and EL emission and the related electronic structure and light-emitting characteristics, including the resulting device properties, are discussed to understand the underlying mechanisms for controlling the emission bandwidth. Finally, we provide our perspective on the remaining challenges in this research area that must be overcome to develop the next generation of wide-color gamut OLED displays.
Fluorescent organic light-emitting materials
π-Conjugated organic fluorophores suffer from limited color purity due to their broad emission spectra originating from the intrinsic vibronic coupling and structural relaxation of the S1 state (Fig. 2a). To achieve narrow EL spectra with a small FWHM, color filters and optical microcavities have been considered in the fabrication of fluorescent OLEDs15,16,17. However, the development of efficient organic fluorescent emitters with narrow emission bandwidths for high color purity remains an important goal. As shown in Fig. 2b, the relative intensity (I0-1/I0-0) of the 0–0 (between the ν = 0 vibrational levels of S0 and S1) and 0–1 (from ν = 0 of S1 to ν = 1 of S0) vibronic transitions is determined by the Huang–Rhys factor (S)18. When π-conjugated organic molecules have a locally excited (LE) state with a similar equilibrium geometry to the ground state (structural distortion, ΔQ \(\approx\) 0), a large orbital overlap results in a dominant 0–0 vibronic transition, converging the S value to zero and producing a sharp single emission peak19. In contrast, an increase in ΔQ by the formation of the CT state can induce a strong contribution from 0 to n (n = 1, 2, 3…) vibronic transitions, resulting in a broader emission peak9,18,20. Thus, the design of rigid structures with a lack of CT character in the excited state is crucial to decrease the S value and develop organic fluorescent materials with narrowband emission.
In this chapter, we focus on the molecular design of narrowband emitting fluorophores and structure-optical property correlations by categorizing the molecules into (i) twisted structures with bulky substituents with suppressed intermolecular aggregation, (ii) rigid/fused aromatic molecules without CT character, (iii) 5,12-dihydroquinolino[2,3-b]acridine-7,14-dione (quinacridone) and (iv) 4,4-difluoro-4-bora-3a,4a-diaza-s-indacene (BODIPY) derivatives (Fig. 3). Much of the previous work concerning fluorescent singlet emitters with narrow emission studied blue-emitting materials and their EL devices. Some quinacridone and BODIPY-based fluorophores have demonstrated green and red emission spectra with remarkably small FWHM values. The narrow emission with a predominant 0–0 vibronic transition can be ascribed to the enhanced LE character and negligible CT interaction in the rigid and symmetrical molecular structures. The light-emitting properties of representative singlet emitters with narrowband emission and their device characteristics are summarized in Table 1.
Twisted structures with bulky substituents
Various twisted molecular structures have been designed and synthesized to suppress free rotation, vibrational splitting, and intermolecular aggregation without excimer emission in the solid state with the aim of inducing narrowband emission21. In 2001, Kwon et al. reported a twisted spirobiflourene-based anthracene derivative, 9,10-bis[(2″,7″-di-tert-butyl)-9′,9″-spirobifluorenyl]anthracene (TBSA, 1–1)22. TBSA showed narrow PL spectra with FWHM values of 58 nm at a PL maximum wavelength (λPL) of 442 nm in thin films. Devices with an ITO/CuPc/α-NPD/TBSA/Alq3/LiF/Al configuration (full names of the abbreviations in the device architecture can be found in each table) showed a peak in the EL spectrum at 442 nm with an FWHM of 48 nm. By combining a rigid anthracene core with twisted xylene substituents, Kim et al. reported 9,10-bis(2,5-dimethyl-4-(naphthalen-2-yl)phenyl)anthracene (BDNA, 1–2) and 9,10-bis(2,5-dimethylbiphenyl-4-yl)anthracene (BDPA, 1–3)23. Because of the twisted conformation of the xylene substituents relative to the anthracene core, vibronic coupling and self-quenching effects are suppressed, and the highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) are localized mainly at the core. The PL spectra of BDNA and BDPA have small FWHM values of 19 and 18 nm at λPL = 431 and 426 nm in the thin film, respectively. Similarly, Anthony et al. synthesized an ethynylated tetracene derivative, 5,12-dimethoxy-6,11-bis(5-triisopropylsilylthienylethynyl)tetracene (1–4), which showed narrow PL emission with a small Stokes shift (20 nm) due to its rigid molecular structure24. The ITO/TPD/1–4/LiF/Al EL device displayed a sharp emission at 656 nm with an FWHM of 34 nm and did not exhibit substantial aggregate formation.
To prevent intermolecular packing, Park et al. designed a series of blue-emissive indenopyrazine (IPY) derivatives with terphenyl side groups, 6,6,12,12-tetraethyl-2,8-bis-[1,1′;3′,1″]-terphenyl-4′-yl-6,12-dihydro-diindeno[1,2-b;1′,2′-e]pyrazine (m-TP-EPY, 1-5), 6,6,12,12-tetraethyl-1,7-bis-[1,1′;3′,1″]terphenyl-4′-yl-6,12-dihydro-diindeno[1,2-b;1′,2′-e]pyrazine (o-TP-EPY, 1–6), and 6,6,12,12-tetraethyl-3,9-bis-[1,1′;3′,1″]terphenyl-4′-yl-6,12-dihydro-diindeno[1,2-b;1′,2′-e]pyrazine (p-TP-EPY, 1–7)25,26,27. The twisted molecular structure restricts the π-conjugation between the IPY core and terminal terphenyl groups, resulting in narrow blue PL spectra with small FWHM values between 40 and 50 nm in both chloroform and thin films. Based on a new phenanthro[9,10-d]imidazole (PI) building block, Ma and Lu et al. synthesized blue-emissive 1,2-diphenyl-phenanthro[9,10-d]imidazole (PPI, 1–8)28. In tetrahydrofuran (THF), a narrow PL band at λPL = 369 nm was measured with an FWHM of 34 nm and PL quantum yield (PLQY) of 70%. Subsequently, Lu further developed three PPI derivatives, (2-(4-(9H-carbazol-9-yl)phenyl)-1-phenyl-1H-phenanthro[9,10-d]imidazole) (M1, 1–9), 1-phenyl-2-(4-(3-(1-phenyl-1H-phenanthro[9,10-d]imidazol-2-yl)-9H-carbazol-9-yl)phenyl)-1H-phenanthro[9,10-d]imidazole (M2, 1–10), and 1-phenyl-2-(4-(triphenylsilyl)phenyl)-3a,11b-dihydro-1H-phenanthro[9,10-d]imidazole (SiPIM, 1–11)29,30. Similar PL spectra with a small FWHM of approximately 40 nm were measured in various solvents with different polarities, indicating the absence of intramolecular charge transfer (ICT) characteristics in these compounds. In particular, M1- and M2-based OLEDs with a device architecture of ITO/NPB/M1 or M2/TPBI/LiF/Al exhibited narrow EL spectra (FWHM ~40 nm) with CIE coordinates of (0.165, 0.050) and (0.166, 0.056), respectively.
The light-emitting properties of a new donor-acceptor type triphenyl-substituted imidazole moiety, N,N-diphenyl-4′-(1,4,5-triphenyl-1H-imidazol-2-yl)-[1,1′-biphenyl]-4-amine (TPA-PIM, 1–12), were studied by Yang et al.31. A fully twisted TPA-PIM showed highly suppressed vibration splitting and narrow emission spectra in the solid state. TPA-PIM devices with a configuration of ITO/PEDOT:PSS/NPB/TCTA/TPA-PIM/TPBi/LiF/Al showed an extraordinarily narrow EL emission at 420 nm with an FWHM of 35 nm and an external quantum efficiency (EQE) of 3.28% with CIE coordinates of (0.161, 0.046) (Fig. 4a). Gong et al. also reported a series of deep-blue-emissive materials based on a spiro[fluorene-7,9′-benzofluorene] core, including N,N,N,N′-tetraphenylspiro[fluorene-7,9′-benzofluorene] (SFBF)-5,9-diamine (BD-6DPA, 1–13), N,N′-di-(2-naphthyl)-N,N′-diphenyl-SFBF-5,9-diamine (BD-6NPA, 1–14), N,N′-diphenyl-N,N′-di-m-tolyl-SFBF-5,9-diamine (BD-6MDPA, 1–15), and N,N′-diphenyl-N,N′-bis(4-(trimethylsilyl)phenyl)-SFBF-5,9-diamine (BD-6TMSA, 1–16)32. Spiro compounds with specific steric configurations can prevent intermolecular interactions with amorphous morphology and high PLQY, even in films. The corresponding EL devices showed narrow EL bands at 460 nm (FWHM = 46–56 nm) with EQEs of 6.54–8.16%. In addition, a blue-emissive indenofluorenyl core with two spiro-linked xanthenyl units, dispiro[xanthene-9,6-indeno[1,2-b]fluorene-12,9′-xanthene] (DSX-IF, 1–17), was reported by Rault-Berthelot et al.33. Owing to the highly rigid spiro structures, DSX-IF suppressed excimer formation in the solid state with improved solubility and narrow PL (in cyclohexane) and EL spectra with FWHM values of ~30 and 40 nm, respectively.
In 2018, Park et al. designed four different kinds of narrow blue-emitting fluorophores based on a pyrene moiety by varying diphenylamine (DPA) side groups34. To hinder intermolecular packing, they introduced different kinds of alkyl side chains onto the DPA moiety and synthesized N,N,N′,N′-tetraphenyl-pyrene-1,6-diamine (TPPDA, 1–18), N,N,N′,N′-tetra-o-tolylpyrene-1,6-diamine (2Me-TPPDA, 1–19), N,N’-bis(4-(tert-butyl)phenyl)-N,N’-di-o-tolylpyrene-1,6-diamine (1Me-1Bu-TPPDA, 1–20), and N,N′-bis(5-(tert-butyl)-2-methylphenyl)-N,N′-bis(2,4-dimethylphenyl)-pyrene-1,6-diamine (3Me-1Bu-TPPDA, 1–21). In toluene, the PL maxima (FWHM) of TPPDA, 2Me-TPPDA, 1Me-1Bu-TPPDA, and 3Me-1Bu-TPPDA were 458 (38), 452 (39), 462 (39), and 461 nm (41 nm), respectively. A higher PLQY was measured for 1Me-1Bu-TPPDA (89%) and 3Me-1Bu-TPPDA (91%) than for TPPDA (87%) and 2Me-TPPDA (79%) because bulky tert-butyl substituents can prevent intermolecular aggregation. All EL devices with a configuration of ITO/2-TNATA/NPB/α,β-ADN: 4% dopant/Alq3/LiF/Al showed a narrow emission with FWHM = ~40 nm. In particular, 3Me-1Bu-TPPDA showed the highest EQE of 9.25% with a small y value for the CIE coordinate (0.133, 0.145). Kwon et al. also synthesized a pyrene-based blue fluorophore, N,N′-bis-dibenzofuran-4-yl-N,N′-bis-(2,5-dimethyl-phenyl)-pyrene-1,6-diamine (BPPyA, 1–22), and reported a TADF host-sensitization system using the BPPyA emitter and 9,9-dimethyl-2,7-di(10H-spiro[acridine-9,9′-fluoren]-10-yl)-9H-thioxanthene-10,10-dioxide (SPAC-DMT) as a TADF sensitizer, showing λEL = 455 nm with a FWHM of 43 nm and an EQE of 7%35.
Fused aromatic compounds with structural symmetry
Symmetrically structured fused aromatic compounds without ICT character have demonstrated narrow emission with similar molecular geometry in the S0 and S1 states. For example, flavanthrone is a well-known anthraquinone-type fluorophore with a rigid planar backbone, and several flavanthrone derivatives have been investigated in OLEDs where a dominant LE emission was observed with a high oscillator strength. Based on the flavanthrone core, Monkman et al. synthesized a series of 8,16-dialkoxybenzo[h]-benz[5,6]acridino[2,1,9,8-klmna]acridines (FCs) with various alkoxy side chains (-OC4H9 (FC-4, 1–23), -OC6H13 (FC-6), -OC8H17 (FC-8, 1–24), -OC10H21 (FC-10), and -OC12H25 (FC-12, 1–25))36. All FC derivatives showed similar optical properties (λPL of 521 nm in chloroform) because of the identical core structure. In particular, a Stokes shift of only 9 nm was observed for FC-8 in chloroform, suggesting a negligible geometrical distortion between the ground and excited states. When FC-4, FC-8, and FC-12 OLEDs were fabricated with a configuration of ITO/PEDOT:PSS/PVK/CBP:1 wt% FC-4, 8, or 12/TPBi/LiF/Al, remarkably narrow EL spectra were measured with an EL maximum wavelength (λEL) of 535 nm and an extremely small FWHM (21–22 nm) (Fig. 4b).
A series of rigid anthanthrene derivatives were synthesized by Neckers et al. with various phenyl substituents, including 4,10-diphenylanthanthrene (1–26) and p-tert-butylphenyl-4,6,10,12-tetraphenylanthanthrene (1–27)37. Compounds 1–26 showed a remarkably small FWHM of 14 nm with a λPL of 442 nm and a PLQY of 33% in dichloromethane (DCM). Because anthanthrene in DCM had almost isoenergetic S1 and T2 states, nonradiative relaxation pathways via intersystem crossing (ISC) decreased the PL efficiency. However, in the solid state, the T2 state had a slightly higher energy than the S1 state, making the nonradiative ISC process far less likely to occur and yielding blueshifted emission with a higher PLQY compared to that in solution. OLED devices using compounds 1–26 and 1–27 with a structure of ITO/NPB/TBADN:1.1% 1–26 or 1–27 /Alq3/MgAg exhibited narrow EL emission at a λEL of 446 nm (FWHM = 42 nm) and 472 nm (FWHM = 46 nm), respectively.
A red fluorophore, tetraphenyldibenzoperiflanthene (DBP, 1–28), was also synthesized by Bard et al.; this fluorophore had a narrow PL spectrum (λPL = 596 nm, FWHM = 22 nm in benzene), and its solution-processed, TADF-sensitized red-emitting OLED (ITO/PEDOT:PSS/2 wt% DBP:15 wt% DC-TC:CBP/TmPyPB/LiF/Al) was successfully fabricated by Su, showing λEL = 610 nm with a FWHM of 25 nm, an EQE of 8%, and a CIE coordinate of (0.61, 0.38)38,39. In 2020, Lee et al. reported an N-fused polyaromatic fluorophore (tDIDCz, 1–29) that exhibited violet emission at 393 nm in THF with a small FWHM (20 nm)40. In particular, the multiple resonance (MR) effect (discussed in detail in chapter 4) was achieved without any boron or ketone groups. The MR effect was generated by two nitrogen atoms enclosed in three aromatic rings with the LUMO distributed along the adjacent carbon atoms. The device employing tDIDCz showed a pure-violet EL emission at λEL = 401 nm with a remarkably small FWHM (14 nm).
Quinacridone derivatives
Various quinacridone derivatives based on a core structure consisting of five fused rings have proven to be green OLED emitters with great potential, showing intense fluorescence, high carrier mobility, and inherently narrow emission. However, the rigid and planar core structures readily form strong π–π stacking and intermolecular hydrogen bonding interactions in concentrated or aggregated conditions, which significantly quenches their fluorescence. Wang et al. studied the light-emitting characteristics of several quinacridone derivatives with various substituents to reduce intermolecular aggregation. For example, the quinacridone derivatives N,N-di(n-butyl)quinacridone (1–30) and N,N-di(n-butyl)-1,3,8,10-tetramethylquinacridone (1–31) showed narrow PL spectra in chloroform with a PLQY of over 90% at λPL = 538 and 532 nm, respectively (FWHM < 30 nm)41. EL devices fabricated with these molecules showed only a slight increase in the FWHM (28 and 36 nm for 1–30 and 1–31, respectively). Fluorine substituents were subsequently introduced to yield N,N′-di(n-butyl)-2,9-difluoroquinacridone (C4-DFQA, 1–32)42. Similar to the non-fluorinated compounds 1–30, C4-DFQA showed a remarkably narrow (FWHM = 21 nm) and highly efficient green PL emission in THF at 535 nm with a PLQY of 97%. The introduction of strongly electron-withdrawing fluorine atoms decreased the HOMO and LUMO energy levels, resulting in efficient electron injection and transport to improve the OLED performance. As shown in Fig. 4c, the EL spectra of the ITO/NPB/C4-DFQA/Alq3/LiF/Al device exhibited a yellowish-green emission at 553 nm with a small FWHM of 30 nm and CIE coordinates of (0.42, 0.56). The authors also attempted to extend the conjugation of the core to tune the emission properties of quinacridone derivatives43. The indole-fused quinacridone structure 5,8,15,18-tetraoctyl-5,8,15,18-tetrahydroindolo[3,2-a]indole[3′,2′:5,6]quinacridone (IDQA, 1–33) in toluene showed a slightly red-shifted PL maximum at 568 nm compared to that of quinacridone itself due to increased conjugation. In dilute solution, narrowband PL with an FWHM of 25 nm and a PLQY of 91% was measured, while a redshifted broadened PL spectrum with decreased PLQY was observed in concentrated solutions due to aggregation. The ITO/NPB/Alq3:IDQA (1 wt%)/Alq3/LiF/Al EL device exhibited a narrow emission at λEL = 588 nm with an FWHM of 45 nm.
BODIPY derivatives
BODIPY derivatives are efficient fluorescent materials with sharp absorption and emission spectra with high PLQY values close to unity. The emission wavelength of BODIPY derivatives can be modulated by functionalizing different positions with different substituents and/or controlling π-conjugation. For example, Baryshnikov et al. reported 1,7-diphenyl-substituted-BODIPY derivatives such as 2-carbethoxy-3-methyl-7-butyl-1,9-diphenyl-4,4-difluoro-3a,4a,7-triaza-4-bora-cyclopenta[b]-fluoren-8-on (1–34)44,45. Because of the unique nature of BODIPY structures, the geometrical distortion in the excited state is limited upon electronic transition between the HOMO and LUMO, resulting in a small Stokes shift. Compounds 1–34 showed a bright red emission in DCM with a λPL = 618 nm, a PLQY of 86%, a Stokes shift of 30 nm, and an FWHM of 48 nm. Narrow-emission spectra (FWHM of 45 nm) were also obtained from EL devices (ITO/CuI/CBP:20% 1–34/Bphen/Ca/Al). A new phenyl amide-substituted-BODIPY structure (1–35) was designed by Ziessel et al.46. Compounds 1–35 showed a PL maximum at 540 nm with an FWHM of 31 nm in DCM, while its PL spectra in film exhibited a strong secondary emission at 633 nm by forming dimers via hydrogen bonding. When the BODIPY-based emitters were dispersed into host materials (Alq3), an EL device with the structure ITO/α-NPD/Alq3: 1–35/BCP/Al achieved narrow EL emission. Interestingly, OLEDs doped with 7 and 18 mol% of 1–35 showed a narrow EL emission with FWHM < 40 nm at λEL = 550 (monomer emission) and 635 nm (dimer emission), respectively, providing the opportunity to adjust the emission color from yellow to red without damaging the color purity (Fig. 4d, left). By attaching a naphthalene or pyrene substituent at the C-8 position, Pushkarev et al. synthesized new BODIPY derivatives with extended π-conjugation, 4,4-difluoro-8-naphthyl-1,3,5,7-tetramethyl-2,6-diethyl-4-boron-3a,4a-diaza-s-indacene (1–36) and 4,4-difluoro-8-pyrryl-1,3,5,7-tetramethyl-2,6-diethyl-4-boron-3a,4a-diaza-s-indacene (1–37)47. Both BODIPY derivatives showed PL emission at 541–544 nm, regardless of the surrounding environment (DCM, ethanol, and poly(methyl methacrylate) (PMMA)). The ITO/PVK: 1–36 or 1–37 (5 wt%)/BPhen/Alq3/Yb EL devices also showed narrow emission at λEL = 542 and 540 nm, respectively, with an FWHM of 36 nm. However, a significant excimer emission was also observed in the devices doped with 10 wt% BODIPY derivatives. To reduce fluorescence quenching via π–π stacking, Ahn et al. designed a difluoroboron complex based on 2-(benzothiazol-2-yl)phenol (1–38) in which the boron is bound to O and N atoms in the bidentate ligand48. Compounds 1–38 showed a narrow and efficient PL emission at 463 nm with a PLQY of 61% and an FWHM of 38 nm even in the aggregated state, confirming that the π–π stacking interactions were effectively suppressed. In addition, Zhan et al. demonstrated that the TADF-sensitized hyperfluorescence from 10-(4,4′-di-tert-butyl[1,1:3,1′-terphenyl]-5-yl)-5,5-difluoro-1,3,7,9-tetramethyl-5H-4λ4,5λ4-dipyrrolo[1,2-c:2,1-f][1,3,2]diazaborinine (tPhBODIPY, 1–39) showed narrow EL spectra and a high EQE49. A hyperfluorescence device with DCzDCN as a host and 4CzIPN as a TADF assistant dopant displayed a bright green emission at an λEL of 520 nm (FWHM of 32 nm) with EQE = 19% and CIE coordinates of (0.26, 0.67) (Fig. 4d, right).
Cyclometalated complex-based phosphorescent materials with narrow emission
Cyclometalated complexes containing Ir, Pt, Pd, Eu, and Tb in their core surrounded by π-conjugated ligands show intense phosphorescence even at room temperature50,51. Through efficient ISC from S1 to T1, these phosphorescent emitters can achieve internal EL quantum efficiencies close to unity via strong spin-orbit coupling (SOC) between the emitting triplet state and high-lying singlet states, demonstrating their great potential as emitters in phosphorescent OLEDs (PhOLEDs)52,53,54.
Figure 5a shows a simplified molecular orbital (MO) diagram for organo-transition metal compounds55. The electrons in most cyclometalated complexes are populated in the ligand-centered (LC) and metal-to-ligand charge transfer (MLCT) states upon excitation, yielding mainly four excited electronic states of the singlet and triplet MLCT (1MLCT and 3MLCT) and LC (1LC and 3LC) states. Subsequently, the low-lying 3MLCT and 3LC states can be occupied by excited carriers via internal conversion (IC) and ISC. In many phosphorescent cyclometalated complexes, the lowest excited T1 state can be described as a combination (or intermixing) of 3MLCT and 3LC, forming the LUMO of a hybrid triplet state. MLCT-dominant phosphorescence is common in phosphorescent Ir and Ru coordination complexes and is characterized by broad, structureless emission with pronounced solvatochromism and rigidochromism originating from strong CT characteristics. The MLCT-dominant emission in various Ir complexes has a relatively short phosphorescence lifetime (τp on the order of ns to μs) because of the efficient SOC with a singlet excited state such as 1MLCT. By differentiating the central metal and organic ligands, cyclometalated complexes can also form various excited states, such as metal-centered (MC) and ligand-to-metal charge transfer (LMCT) states, as shown in Fig. 5b56. LMCT is the charge transfer from an MO with ligand-like character to that with metal-like character, which is an opposite process of MLCT from an MO with metal-like character to that with ligand-like character. Thus, LMCT reduces the metal center, while MLCT undergoes oxidation of the metal center. Unlike homoleptic phosphorescent complexes with identical ligand structures, heteroleptic complexes with incorporated ancillary ligands (L′) have additional transition states induced by the ligands, i.e., L′C, ML′CT, and ligand to ligand charge transfer (LL′CT) states, facilitating fine modulation of phosphorescence color tuning.
The emitting T1 state splits into three substates via zero-field splitting (ZFS) depending on the SOC54. The ZFS values correlate with the relative contribution of the 3MLCT and 3LC states to the LUMO of cyclometalated complexes. As shown in Fig. 5c, the octahedral Ir(4,6-dFppy)2(pic) complex exhibits a larger ZFS and a shorter emission decay time (ΔE(ZFS, Ir) = 67 cm−1 and τ(Ir) = 0.4 μs) compared to the square planar Pt(4,6-dFppy)(acac) complex (ΔE(ZFS, Pt) = 8 cm−1 and τ(Pt) = 3.6 μs)57. The emitting T1 state in Pt(4,6-dFppy)(acac) is largely LC, showing a better resolvable emission compared to that of Ir(4,6-dFppy)2(pic). Large ΔE(ZFS) values over 50 cm−1 in quasi-octahedral structures indicate significant 3MLCT character in the emitting T1 state, showing favorable radiative emission from the triplet substates to the ground S0 state via efficient SOC. The smaller ΔE(ZFS) from the emitting triplet state in Pt complexes originates from the weaker SOC between the lowest 3LC (3ππ*) and 1MLCT (1dπ*) states. In this case, indirect SOC mixing can occur if the 1MLCT state interacts with the 3MLCT state, which couples with 3LC by a configuration interaction (CI)54. Compounds with ΔE(ZFS) smaller than 1 cm−1 show favorable 3LC emitting states. Cyclometalated complexes, which have a T1 state with dominant 3MLCT character, show a short phosphorescence lifetime with high quantum yield; however, structureless broad emissions are commonly observed, originating from the strong CT character of these states. To induce 3LC-dominant narrow phosphorescent emission, it is necessary to design phosphorescent molecules with a 3LC state that is lower than the 3MLCT by modifying the structure of the organometallic complex. Vibrational coupling to the ground state in the 3LC-dominant emission can be effectively suppressed by employing rigid ligand frameworks without intra- or interligand CT interactions. In this chapter, we review cyclometalated complexes with narrow emission and discuss the correlation between the molecular structure and intermixing of the 3LC and 3MLCT states and the resulting light-emitting characteristics (Table 2).
Ir-based phosphorescent cyclometalated complexes
Since the Thompson and Forrest group developed fac-tris(2-phenylpyridine)iridium (fac-Ir(ppy)3) in the late 1990s58, heavy metal-based phosphorescent emitters have been extensively studied with the aim of exploiting their strong SOC and triplet excitons. Ir(III) complexes have shown good photo- and thermal stabilities, high quantum efficiencies, and short lifetimes. For example, fac-Ir(ppy)3 is a representative green-emissive triplet emitter (λPL = 519 nm) with a high PLQY of ~100% at room temperature. However, it shows a broad emission spectrum due to its strong MLCT character at ambient temperature59. Therefore, cyclometalated Ir complexes with a variety of ligands have been synthesized to improve emission color purity by modulating the energy level and spatial geometry (Fig. 6). Bejoymohandas developed a series of Ir complexes (Ir1 (2-1), Ir2 (2-2), Ir3, and Ir4) by attaching electron-donating and electron-withdrawing substituents to the quinoline moiety in (benzo[b]thiophen-2-yl)quinoline cyclometalating ligands60. The HOMO and LUMO of Ir1-Ir4 are localized primarily in the cyclometalating ligands rather than the Ir center, resulting in an electronic transition with reduced MLCT character. As a result, the electron-donating methyl-substituted Ir1 and unsubstituted Ir2 showed narrow PL spectra at 655 nm in DCM with FWHM < 44 nm, while Ir3 and Ir4, which had strong electron-withdrawing trifluoromethyl and ethyl ester substituents, showed prominent CT character, resulting in a broad emission spectrum with a smaller emissive bandgap. The light-emitting properties of phosphorescent metal complexes can also be modulated by changing the ancillary ligand. Because of their higher triplet energy, nonchromophoric ancillary ligands do not influence the emission process directly, but different ligand field strengths can alter the SOC efficiency and structural distortion. Bejoymohandas developed new Ir complexes (Ir1-pic (2-3) and Ir2-pic (2-4)) by replacing the flexible thenoyltrifluoroacetylacetonate (tta) ancillary ligand of Ir1 and Ir2 (hereafter called Ir1-tta and Ir2-tta) with a rigid picolinate (pic) moiety61. As shown in Fig. 7a, the change in ancillary ligands had a negligible influence on the shape of the PL spectrum and FWHM (< 44 nm), but a slight blueshift in the PL spectra of the Ir1-pic and Ir2-pic was observed because of the stronger ligand field of the ancillary pic ligand compared to the tta moiety. The quantum efficiencies of Ir1-pic (49%) and Ir2-pic (37%) were significantly higher than their tta analogs (2–8%) because the rigid picoline ligand reduces the extent of the geometrical deformation of the excited state and thereby suppresses nonradiative relaxation. With the device architecture ITO/PEDOT:PSS/PVK/CBP:TPBi:Ir1-pic (15%) or Ir2-pic (10%)/TPBi/LiF/Al, EQEs of 5.03% and 3.41% were obtained for Ir1-pic and Ir2-pic-based devices with EL maxima at 657 and 664 nm, respectively.
Huang reported a spiro aromatic ligand-based homoleptic Ir complex that demonstrated both narrow emission and color tunability62. Bulky 2-(spiro[fluorene-9,9′-xanthene])-pyridine (SFXpy) acts as a multifunctional ligand. Its steric bulkiness not only reduces intermolecular π–π aggregation at high doping levels but also helps charge injection/transport. Because of its extended conjugation, fac-Ir(SFXpy)3 (2–5) showed a redshifted (compared to fac-Ir(ppy)3) emission at 542 nm, but no emission from the aggregates or excimers was observed (Fig. 7b). In addition, the fact that emission from the LC transition was predominant ensured a narrow PL emission with an FWHM of approximately 27 nm. The PhOLED was fabricated with a common host (CBP) by varying the doping concentration of fac-Ir(SFXpy)3 (5–18 wt%) and showed narrow EL spectra at λEL = 542 nm (FWHM = 29 nm) with a peak EQE of 12.1% in devices with a doping concentration of 15 wt%. Using combinatorial chemistry methods, König et al. studied the photophysical properties of a series of Ir complexes (2–6~2–9) and was able to achieve narrow PL (FWHM < 49 nm) and PLQY ranging from 54%–85% through modification of the ligand structure63. Hwang reported a solution-processable Ir complex, bis(2-(4-methoxynaphthalen-1-yl)benzo[d]thiazole)iridium(III)acetylacetonate ((BTMN)2Ir(acac), 2–10)64. In DCM solution, (BTMN)2Ir(acac) had a remarkably narrow PL spectrum with an FWHM of ~25 nm at λPL = 599 nm (PLQY of 29%). However, the (BTMN)2Ir(acac)-based red-emissive EL device (ITO/PEDOT:PSS/PVK:(BTMN)2Ir(acac)/TPBi/CsF/Al) showed a significantly broadened emission at 598 nm with an FWHM in the range of 74–76 nm, reinforcing the need for additional structural modifications to narrow the EL bandwidth to achieve high color purity.
Pt- and Pd-based phosphorescent cyclometalated complexes
The T1 state of most octahedral Ir complexes is primarily determined by the 3MLCT state, which induces broad PL emission with high PLQY because of the strong SOC between the triplet and singlet states. In contrast, square planar Pt and Pd complexes typically have narrowband emission, but longer phosphorescence lifetimes and lower PLQYs than those found in Ir complexes were observed because of weak SOC in the square planar complexes (Fig. 8). Li et al. modified the ligand structure of the PtON1 structure that had a bridging oxygen between the phenyl-pyrazole (ppz)-based cyclometalating ligand and the carbazolyl pyridine ancillary ligand by incorporating electron-donating substituents (methyl (PtON1-Me, 3–1), tert-butyl (PtON1-tBu, 3–2), and N,N-dimethylamino (PtON1-NMe2, 3–3)) at the 4-position of the pyridyl ring, resulting in narrow deep-blue emissions (FWHM 15–20 nm) at 445 nm with high PLQYs (80~95%) (Fig. 9)65,66. These results can be explained by the fact that the 1MLCT/3MLCT character in the original PtON1 was thermally accessible at room temperature, while the addition of an electron-donating group increased the energy levels of MLCT states, suppressing the MLCT character in the T1 state51,67. In contrast, the addition of a 9-carbazolyl substituent (PtON1-Cz) caused broad CT emission due to the decreased MLCT energy level, which enhanced the MLCT character of the T1 state. A similar strategy was successfully employed with 4-phenyl-pyrazole and carbene-based tetradentate Pt complexes (PtON6-tBu (3–4), PtON7-tBu, and PtON7-dtb (3–5)) by incorporating a tert-butyl substituent, resulting in an FWHM of 19–20 nm and a PLQY > 80%. Li et al. also developed PtN1N (3–6), which included a pyrazolylcarbazole group as the emitting ligand and a pyridylcarbazole moiety as an ancillary ligand68. At 77 K, the PL spectra of PtN1N and its analogs (PtN1pyCl (3–7) and PtN1(acac)) were similar, with each having a dominant single emission. At room temperature, PtN1N still showed little color contamination from v0-1 and v0-2 transitions (S = 0.3) with FWHM < 20 nm, while PtN1pyCl had an S value >0.5 and PtN1(acac) exhibited a structureless broad emission, whose appearance was dependent on the relative MLCT:LC character of the T1 state. Most importantly, a narrow EL emission (FWHM 20 nm) and an EQE of 26.1% were obtained from a device with a structure of ITO/PEDOT:PSS/NPD/TAPC/7% PtN1N:26mCPy/PO15/BmPyPB/LiF/Al. Because the excimer was absent due to the breaking of its planar geometry, a high EQE (25.6%) was observed even with a high dopant concentration (14%). Additionally, the blue-emissive PtON7-tBu (3–8) and orange-emissive PtN8ppy (3–9) showed narrow PL spectra in DCM at 446 nm with FWHM = 20 nm (PLQY = 83%) and 573 nm with FWHM = 26 nm (PLQY = 40%), respectively. By modifying the number and position of methyl substituents, a series of narrow-emissive Pt complexes, Pt(ppzOczpy) (3–10), Pt(ppzOczpy-m) (3–11), Pt(ppzOczpy-2m) (3–12), and Pt(ppzOczpy-4m) (3–13), were synthesized by Huang et al., in which the intermixing of 3MLCT and 3LC in the T1 state could be finely modulated69. Compared to a PtON1 reference material, the introduction of a methyl group to the para-position of the pyridine moieties enhances the electron distribution in the carbazole moieties to yield a 3ππ* dominated T1 state, resulting in a dominant LC contribution. Consequently, all four compounds had narrow PL spectra with remarkably low FWHM values of approximately 20 nm in PMMA films. PhOLEDs doped with 20% Pt(ppzOczpy-4m) in the device with a structure of ITO/PEDOT:PSS/CzSi:CzAcSF:Pt(ppzOczpy-4m) (80:20:20)/DPEPO/TmPyPB/Liq/Al showed the best EQE of 19.5% with CIE coordinates of (0.159, 0.166) and a FWHM of 53 nm.
Pt complexes with porphyrin ligands were also studied as narrowband phosphorescent emitters. In 1998, Forrest et al. first reported the utilization of Pt-porphyrin complexes in efficient PhOLEDs by doping the host Alq3 with 2,3,7,8,12,13,17,18-octaethyl-21H,23H-porphine platinum(II) (PtOEP, 3–14)70. Although porphyrin is known to have a long-lived triplet state, PtOEP showed a decreased phosphorescence lifetime (91 μs) and 50% PLQY due to strong SOC. The Alq3:PtOEP-based PhOLED device has an emission spectrum similar to that of its porphyrin ligand and exhibits strong phosphorescence at 650 nm with a small FWHM of 19 nm, which is thought to originate from the dominant LC character of the emitting T1 state. Thompson also reported another type of Pt-porphyrin complex; the two representative examples, PtOX (3–15) and PtDPP (3–16) had octaalkylporphyrin and arylporphyrin ligands, respectively71. PtOX showed a narrow emission peak at 648 nm with FWHM = 26 nm in polystyrene films, and PtDPP also displayed a narrow PL spectrum at λPL = 630 nm (FWHM = 33 nm). The rotation of the phenyl group in PtDPP promoted nonradiative relaxation, making the PLQY of PtDPP (16%) lower than that of PtOX (44%). However, the spin-coated PtDPP:PS thin film showed an improved PLQY similar to that of PtOX because the rotation of the phenyl group was restricted. Narrow EL spectra of ITO/α-NPD/Alq3:PtOX and PtDPP/Alq3/Mg:Ag/Ag were observed at λEL = 650 nm (FWHM of 25 nm) and 640 nm (FWHM of 50 nm) with CIE coordinates of (0.69, 0.30) and (0.67, 0.31), respectively. This result demonstrates the potential utility of PtOX- and PtDPP-based PhOLEDs as red emitters with satisfactory CIE criteria (0.55 ≤ x ≤ 0.74 and 0.25 ≤ y ≤ 0.35).
Despite the fact that Pt and Pd are both group 10 transition metals (and would therefore be expected to have similar properties), there are fewer studies on phosphorescent emitters based on Pd than on their Pt counterparts because their lowest-lying excited states are usually depleted by the thermally accessible MC states that deactivate radiative decay at room temperature72. Zhu et al. designed a Pd complex ((Phpy)Pd(Pery-q), 3–17) with a 2-phenylpyridine and hydroxyquinoline-substituted perylene bisimide as an asymmetric ligand73. Introducing perylene bisimide can prevent the localization of electrons in the thermally accessible MC state by causing the ligand localized (intraligand) excited state to be below the 3MLCT state. Consequently, once the singlet excited state of perylene bismide is populated, it acts as a phosphorescent sensitizer and undergoes ISC to the triplet state of the hydroxyquinoline ligand. Finally, narrow phosphorescence spectra were measured at 635 nm (FWHM = 27 nm) in DCM and 625 nm (FWHM = 18 nm) in poly(9-vinylcarbazole) film at room temperature.
New Pd-containing phosphorescent blue emitters, PdN1N (3–18), PdN1N-dm (3–19), and PdN6N (3–20), were prepared by introducing pyridylcarbazole and pyrazolylcarbazole-based tetradentate ligands to achieve narrow emission with S < 0.5 (FWHM 18~22 nm) at λPL = 470–476 nm in DCM74. Borisov et al. reported the Pd-phorphyrin type complexes PdNTBP (3–21) and PdTPTBP (3–22), which showed strong room temperature red phosphorescence in deoxygenated toluene with a narrow-bandwidth (FWHM = 32 nm and 47 nm, respectively)75. Additionally, Niedermair et al. synthesized a series of Pd porphyrin complexes by fusing an additional benzene ring onto at least one of the benzo groups in tetrabenzoporpyrin76. Extension of the aromaticity in the porphyrin framework provided emission maxima in Pd complexes in the near infrared region (849–882 nm). In particular, cis-palladium(II)-meso-tetra-(4-fluorophenyl)dibenzodinaphthoporphyrin (Pd2NF, 3–23) exhibited PL at 868 nm with a small FWHM of 41 nm in toluene. Similar to those of Pt porphyrins, the optical properties of Pd porphyrins are determined by the degree of similarity between the ground and excited states of the porphyrin ligands.
In addition, industries have also tried to develop narrowband emitters; for example, deep red-emitting phosphorescent OLEDs with suppressed first vibronic transition in their EL spectra (molecular structure was not disclosed, λE = 640 nm with a FWHM of 43 nm) were reported by Universal Display Co. and Beijing Summer Sprout Technology Co., Ltd. at the Society for Information Display (SID) conference in 2019 and 2020, respectively77,78.
Eu- and Tb-based phosphorescent cyclometalated complexes
Owing to their sharp emission, trivalent lanthanide (Ln) metal complexes, including those with Eu3+ and Tb3+ ions, have attracted attention as red- and green-emissive phosphorescent materials (Fig. 10)79. The luminance of Eu and Tb complexes is mainly caused by f → f transitions in the metal and shows an extremely sharp emission (FWHM < 10 nm). Because the direct population of the excited emitting state in Ln3+ is prohibited, the organic ligands in the Ln complex were first excited, and then the T1 state was formed. Subsequently, Dexter-type electron exchange between the T1 state of the ligand and the Ln ion induces the indirect population of the 4f level of Ln3+ complexes, yielding sensitized luminescence80,81,82. In Ln metal complexes, ligands determine the sensitization phenomenon; therefore, the resulting PL intensity of the Ln ion is different depending on the structure of the ligand83. In Eu complexes, β-diketonate-type structures have been widely used as ligands to sensitize Eu3+ ions, where control of the precise energy of the ligand T1 energy level is important to ensure that it has a higher energy than the emissive level of Eu3+ (5D0) and to optimize the sensitization. Martín-Gil et al. synthesized Eu(cbtfa)3(bath) (4–1), which has a halogenated β-diketonate-based ligand and a rigid bathophenanthroline ancillary ligand (bath)84. Upon excitation at 365 nm, the Eu(cbtfa)3(bath) powder, solution (in chloroform), and thin film showed almost identical PL spectra with a sharp red emission at 613 nm with a 5 nm FWHM. As shown in Fig. 11a, a strong electric dipole transition (5D0-7F2) causes intense emission at 613 nm due to the highly polarizable ligand field around the Eu3+ ion and has five satellite peaks corresponding to intraconfigurational f → f transitions. The EL spectra of the EL (ITO/PEDOT:PSS/Eu(cbtfa)3(bath)/Ca/Al) device were similar to the PL spectra with a dominant emission at 613 nm. Because only one crystal field line is possible for a complex with D3h symmetry79, emission from most Eu complexes occurs from a narrow 5D0 → 7F2 transition, regardless of the external environment or ligand structures. Sivakumar et al. synthesized Eu(TTA)3Phen-Fl-TPA (4–2), in which the tta ligand acts as an optical antenna with efficient energy transfer to Eu3+ ions, exhibiting a sharp emission at 612 nm in both solution and film samples85. Borisov et al. reported a series of Eu complexes, Eu(HPhN)3phen (4–3), Eu(HPhN)3dpp (4–4), and Eu(HPhN)3DDXPO (4–5), containing 9-hydroxy-1H-phenalen-1-one (HPhN) as a sensitizing ligand and different ancillary ligands86. S1 and T1 excited states of the ancillary ligands with a higher energy than those of HPhN improved the sensitization process, and similar PL spectra at ~611 nm were observed for all structures, showing ~20% PLQY in polystyrene films. Similar results were reported by Vaidyanathan et al., who showed that all Eu-β-diketonate complexes had similar PL data with a sharp emission at 612 nm both in film and in chloroform solution, regardless of the ancillary ligand (4–6~4–10), indicating efficient energy transfer from the T1 state of the β-diketonate ligand to the excited state of Eu3+ (Fig. 11b) 87.
Similarly, various Tb complexes with different ligands also exhibit similar PL spectra arising from the 5D4 → 7F6 transition (Fig. 11c)88. Huang et al. reported a Tb complex, Tb(PMIP)3DPPOC (4–11), whose optical and electrical properties were comparable to those of Tb(PMIP)3(H2O)2 (4–12) and Tb(PMIP)3(TPPO)2 (4–13) (Fig. 11d)89. Fig. 11d also shows that similar emission spectra were observed for all Tb complexes with sharp Tb3+ emission at 548 nm (5D4 → 7F5) with multiple satellite peaks. Since the energy level of the triplet state of DPPOC is closer to the 5D4 level of Tb, Tb(PMIP)3DPPOC showed a higher PLQY (16.7%) than the other Tb complexes. When the Tb(PMIP)3DPPOC-based EL device was fabricated with an architecture of ITO/NPB/Tb(PMIP)3/co-deposited Tb(PMIP)3DPPOC/BCP/Alq3/Mg0.9Ag0.1/Ag, strong green emission from the Tb ions was observed with a maximum brightness of 2256 cd m−2 and power efficiency of 16.1 lm W−1 (at 5 V). Raithby et al. synthesized a new Tb complex, Tb(tfac)3DPEPO (4–14), with neutral bidentate ligands, trifluoroacetylacetone, and DPEPO90. Both the PL and EL spectra of Tb(tfac)3DPEPO were very similar, with emission maxima at ~545 nm.
TADF-based light-emitting materials
TADF, which was pioneered by Parker and Hatchard, is a phenomenon whereby triplet excitons are converted to singlet excitons by thermal activation and consequently undergo fluorescence91. Theoretically, 100% internal quantum efficiency (IQE) is possible via an efficient upconversion process called reverse intersystem crossing (RISC). Adachi’s group successfully developed a new generation of TADF-based OLEDs92. The design of TADF emitters involves spatial separation of the electron-rich (donor) and electron-deficient (acceptor) moieties to separate the HOMO and LUMO distributions and create a small energy gap (ΔEST) between the S1 and T1 states (Fig. 12a)93. This design strategy has resulted in a significant improvement in EL efficiency, but it also enhances the structural relaxation in the excited states via ICT, resulting in broad CT emission (FWHM of 70–100 nm) with a large Stokes shift in TADF OLED devices (Fig. 12b)94.
To achieve both high-performance and narrowband emission in TADF OLEDs, Hatakeyama et al. designed new TADF materials in which a rigid molecular framework with regular arrangements of boron and nitrogen atoms shows an MR effect; the HOMO is localized on the nitrogen atoms and at the meta-position with respect to the boron atom, whereas the LUMO is localized on the boron atom and at the ortho- and para-positions (Fig. 12c)94. Thus, the boron and nitrogen atoms in the MR-TADF structures have the opposite resonance effect, and the HOMO and LUMO are separated onto different atoms without the need for electron-rich or electron-deficient substituents. The MR-TADF compounds shown in Fig. 13 undergo a limited amount of reorganization in the excited state and maintain their oscillating strength due to effective overlap of the electron and hole wavefunctions, ensuring narrow PL and EL spectra with high luminescence efficiency. In addition, the MR effect minimizes the bonding/antibonding characteristics of the HOMO and LUMO, and the resulting nonbonding MOs minimize the vibronic coupling and vibrational relaxation in the material, resulting in emission peaks with an extremely small FWHM95. In this chapter, various MR-TADF- and conventional D-A-type molecules are summarized, and strategies to achieve narrow emission are discussed (Table 3).
Multiple resonance (MR) TADF emitters
In 2015, Hatakeyama et al. first reported a series of TADF dopants, 5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracene (5-1), 2,12-phenyl-5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracene (5-2), 3,11-diphenyl-5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracene (5-3), and 6,8-diphenyl-5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracene (5-4)96. In compound 5-1, separation of the localized HOMO and LUMO suppresses the exchange interaction between MOs, enhancing the resonance effects of boron and oxygen atoms in the excited state. As a result, compounds 5-1~3 showed strong and narrow PL profiles at 398~410 nm with FWHM < 33 nm in DCM, while 5-4 showed a slightly broader emission (FWHM = 49 nm) attributed to ICT. Based on the observed structure-property relationships, the Hatakeyama group further developed various narrow-emissive blue TADF emitters with rigid boron-containing polycyclic aromatic hydrocarbons (PAHs). In particular, 5,9-diphenyl-5,9-diaza-13b-boranaphtho[3,2,1-de]anthracene (DABNA1, 5–5) and 9-([1,1′-biphenyl]-3-yl)-N,N,5,11-tetraphenyl-5,9-dihydro-5,9-diaza-13b-boranaphtho[3,2,1-de]anthracen-3-amine (DABNA2, 5–6) are considered to be representative narrow-emissive TADF materials94. Unlike those of conventional TADF emitters, the HOMO and LUMO of DABNA1 and DABNA2 are well-distributed over the whole boron-based molecular framework by the MR effect. DABNA1 and DABNA2 both have a small ΔEST (0.20 eV) and bright blue emission at λPL = 460–470 nm with a small FWHM (28–36 nm) in an mCBP film and even in a polar solvent (ethanol). Additionally, the small Stokes shifts of DABNA1 and DABNA2 (25 and 26 nm, respectively) are attributed to the rigid, conjugated core. A DABNA-based OLED with a device structure of ITO/NPD/TCTA/mCP/mCBP:1 wt% DABNA1 or 2/TSPO1/LiF/Al showed a narrower EL spectrum at λEL = 459 nm (DABNA1) and λEL = 467 nm (DABNA2, FWHM = 28 nm for both devices) compared to their PL spectra, with well-matched blue CIE coordinates (BT 2020) (Fig. 14a, b). However, the device doped with 1 wt% DABNA faced severe efficiency roll-off owing to the charge imbalance and bimolecular quenching process. Although the efficiency roll-off improved at a higher emitter doping concentration (5 wt%), the EL spectrum of DABNA2 was redshifted (467 nm). The study highlighted the importance of substituents on rigid B/N cores to localize the HOMO and LUMO at the core and thereby maintain their emission color purities.
Following Oi et al.’s report of a triangulene-shaped planaroborane compound, 4,8,12-trioxa-12c-boradibenzo[cd,mn]pyrene (5–7), which showed a narrow PL emission at λPL = 386 nm with an FWHM of 47 nm in toluene97, Hatakeyama modified the triangulene core by replacing the bridging oxygen atoms with nitrogen. This modification resulted in a small PL bandwidth (FWHM = 26 nm) at λPL = 399 nm for 5–8 in the PMMA film together with a small ΔEST of 0.21 eV98. In the presence of N atoms, X-ray crystallography showed that the B-C bond of 5–8 is shorter (1.478–1.480 Å) than that of triphenyl boron (1.571–1.589 Å), emphasizing that the planarity is strongly enhanced by the bridging N atoms. This planar polycyclic B/N skeleton was further developed to form B/N-doped nanographene structures, B2 (5–9), B3 (5–10), and B4 (5–11), extending the π conjugation of the PAHs with an increased number of boron atoms99. B2, B3, and B4 all showed narrow blue emissions with FWHM = 32, 34, and 38 nm in PMMA films, respectively. In particular, high-purity blue emissions with CIE coordinates of (0.13, 0.11), λE = 460 nm, and a maximum EQE of 18.3% at 1 cd m−2 were observed from B2 OLEDs. Concurrently, DABNA structures were modified by switching the positions of the boron and nitrogen atoms, yielding 5,9-bis(2,6-dimethylphenyl)-3,7,11-trimethyl-5,9-dihydro-13b-aza-5,9-diboranaphtho[3,2,1-de]anthracene (ADBNA-Me-Mes, 5–12) and 3,7,11-trimethyl-5,9-bis(2,4,6-triisopropylphenyl)-5,9-dihydro-13b-aza-5,9-diboranaphtho[3,2,1-de]anthracene (ADBNA-Me-Tip, 5–13)100. When doped into the DOBNA-OAr film, both ADBNA derivatives showed narrow emission (FWHM ~34 nm) in the sky blue region (λPL = 482 and 479 nm for ADBNA-Me-Mes and ADBNA-Me-Tip, respectively). In particular, fabricated ADBNA-Me-Tip devices with a structure of ITO/HATCN/NPB/TCTA/mCP/DOBNA-OAr:1 wt% ADBNA-Me-Tip/TSPO1/LiF/Al showed narrow EL spectra with FWHM = 33 nm and maximum EQE = 21.4% with ΔEST = 0.20 eV and efficient RISC (kRISC = 9.0×103 s−1) (Fig. 14c). Although efficiency roll-off was still observed for the boron-containing ADBNA-Me-Tip-based device, the EQE was sufficiently high (15.4%) even at high luminance (100 cd m−2). In 2019, Hatakeyama developed a new pseudo-linear TADF molecule, (N7,N7,N13,N13,5,9,11,15-octaphenyl-5,9,11,15-tetrahydro-5,9,11,15-tetraaza-19b,20b-diboradinaphtho[3,2,1-de:1′,2′,3′-jk]pentacene-7,13-diamine) (ν-DABNA, 5–14)95. Through the electronic interaction of two boron atoms and six nitrogen atoms, this compound exhibited a well-distributed HOMO and LUMO and showed narrow PL emission with FWHM = 14 nm at 468 nm with 74% PLQY in toluene. In addition, remarkably reduced vibronic coupling was observed in the PL emission of ν-DABNA compared to that of the fluorescent emitter perylene due to the MR effect (Fig. 14d). Employing an MR-TADF-type host (DOBNA-OAr) based on structure 5-1 caused the PLQY to improve remarkably up to 90% (FWHM = 18 nm). The OLEDs fabricated with ν-DABNA (ITO/NPD/TCTA/mCP/DOBNA-OAr:1 wt% ν-DABNA/TSPO1/LiF/Al) achieved a sharp blue emission at 469 nm with FWHM = 18 nm (Fig. 14e), which is comparable to that of QDs or perovskite-LEDs. The ν-DABNA-based blue OLED exhibited not only the smallest FWHM but also the highest EQE (34.4%) among the MR-TADF emitters reported thus far owing to its small ∆EST (0.017 eV) and efficient RISC.
The B/N frameworks designed by Hatakeyama have been extensively modified by other research groups. Lee et al. newly synthesized 2,12-di-tert-butyl-5,9-bis(4-(tert-butyl)phenyl)-5,9-dihydro-5,9-diaza-13b-boranaphtho[3,2,1-de]anthracene (t-DABNA, 5–15) by modifying DABNA1 with tert-butyl groups to hinder intermolecular packing101. In this study, they reported a ternary emitting system based on the TADF-assisted TADF (TATADF) strategy by incorporating an additional TADF assistant dopant. To fabricate the TATADF device (ITO/PEDOT:PSS/TAPC/mCP/t-DABNA/TSPO1/TPBi/LiF/Al), a TADF assistant dopant (DMAC-DPS) was introduced into the emitting layer (1 wt% t-DABNA in DPEPO) to decrease the PL lifetime and improve kRISC via efficient upconversion. The fabricated t-DABNA-based TATADF device showed a narrow EL emission at 450 nm (FWHM of 31 nm) and a remarkably high EQE of 31.4% (Fig. 14f). Huang et al. synthesized a new MR-TADF molecule, 2,12-di-tert-butyl-5,9-bis(4-(tert-butyl)phenyl)-7-(3,6-di-tert-butyl-9H-carbazol-9-yl)-5,9-dihydro-5,9-diaza-13b-boranaphtho[3,2,1-de]anthracene, by introducing t-butyl substituents and a carbazole moiety to the DABNA1 structure (TBN-TPA, 5–16; the molecular structure was corrected to 5–16′ by Hatakeyama based on its 1H NMR spectrum)102,103. The electron-donating group at the para-position relative to boron enhanced the oscillator strength, achieving a high PLQY (97.48%) in toluene. A narrow PL emission at 470 nm (FWHM 26 nm) and extremely small Stokes shift (10 nm) were measured; these were attributed to the structural rigidity of the molecule. A similar EL spectrum was also observed at 474 nm with FWHM = 27 nm and high EQE up to 32.1%.
Narrowband green-emissive MR-TADF emitters have also been developed by extending the conjugation of boron-containing rigid molecular backbones. Wang et al. reported two types of MR-TADF molecules, sky blue-emitting DtBuCzB (5–17) and green-emitting DtBuPhCzB (5–18), based on the dicarbazolylphenylene framework104. In toluene, DtBuCzB and DtBuPhCzB exhibited PL spectra at 481 and 496 nm with FWHMs of 22 and 21 nm, respectively. The extended conjugation (compared to the blue-emissive MR-TADF structures discussed above) causes a bathochromic shift in the emission, but a small FWHM was maintained owing to their structural rigidity, with a small Stokes shift of 14–15 nm for both compounds. With the device structure of ITO/TAPC/TCTA/mCBP:1 wt% DtBuCzB or DtBuPhCzB/TmPyPB/LiF/Al, EL devices based on DtBuCzB and DtBuPhCzB showed narrow EL spectra (FWHM 29 nm) at 488 and 504 nm, respectively. To achieve a further shift in the emission maximum to a longer wavelength, the DtBuCzB core was modified by incorporating di-tert-butylcarbazole into the para- or meta-positions relative to the boron atom, yielding p-Cz-BNCz (5–19) and m-Cz-BNCz (5–20), respectively (Fig. 15a)105. In p-Cz-BNCz, an identical HOMO/LUMO distribution and similar optical properties to those of DtBuCzB were observed (Fig. 15b). In contrast, the meta-substituted carbazole moiety in m-Cz-BNCz upshifted the HOMO with a decreased bandgap to yield green emission. Because of the twisted structure of the meta-substituted carbazole and boron-substituted phenyl ring in m-Cz-BNCz, a narrow PL was observed with FWHM = 38 nm and without ICT character. Devices fabricated with different concentrations of m-Cz-BNCz (1–50 wt%) exhibited similar green EL spectra at 520–528 nm with small FWHM (all <48 nm) (Fig. 15c). Weak intermolecular interactions caused by structural distortion helped to achieve a high EQE (31%), even with dopant concentrations of 10 wt%. In particular, the device with 3 wt% m-Cz-BNCz achieved exceptionally pure green emission with CIE coordinates of (0.23, 0.69). Another strategy to induce green emission is the introduction of an electron-withdrawing moiety onto the para-position with respect to boron in DtBuCzB. By introducing a fluorine-substituted phenyl unit, Duan et al. synthesized a series of green-emissive TADF emitters, 2F-BN (5–21), 3F-BN (5–22), and 4F-BN (5–23)106. When these emitters were doped into a 9-(3-(9H-carbazol-9-yl)phenyl)-9H-3,9′-bicarbazole (mCPBC) film, emission maxima were observed at 501~503 nm with FWHM = 31~33 nm and high PLQYs of ~90%, regardless of the positions of the fluorine substituents. With a device architecture of ITO/HAT-CN/NPB/BCzPh/2F-, 3F-, or 4F-BN/9Cz46Pm/DPPyA:Liq (1:1)/LiF/Al, narrowband green EL spectra were observed at 501, 499 and 493 nm (with FWHM of 40, 38 and 31 nm) for 2F-BN, 3F-BN, and 4F-BN, respectively. Duan also developed another type of B/N framework, 8,11,14,17-tetra-tert-butyl-21-butyl-5b,19b,20-triaza-12b-borabenzo[a]fluorantheno[1,2,3-fg]indeno[1,2,3-mn]tetracene (AZA-BN, 5–24), which has extended conjugation with isoquinoline fused to the central benzene ring107. The PL spectrum of the 4 wt% AZA-BN-doped mCBP film showed pure green emission at λPL = 526 nm with a small FWHM (36 nm) and a high PLQY (94%). In particular, when AZA-BN was utilized as a phosphorescence-sensitized TADF dopant in iridium-based PhOLEDs, a narrowband EL spectrum at 527 nm (FWHM 30 nm) was obtained with high EQE (28.2%) and color purity with CIE coordinates of (0.27, 0.69).
Hatakeyama also reported a series of carbazole‐based MR-TADF DABNA analogs (5–25~5–33) via regioselective one-shot borylation (Fig. 16a)103. Among them, CzB2-M/P showed a green PL emission at 504 nm in a PMMA film with a high PLQY (87%), and its EL device exhibited a narrow emission at 497 nm (FWHM of 29 nm) (Fig. 16b) with a maximum EQE of 26.7% (Fig. 16c) and a long operational lifetime of 74 h. They also designed another solution-processable green-emitting MR-TADF material, OAB-ABP-1 (5–34)108. By delicate modulation of HOMO and LUMO separation, the oscillator strength of OAB-ABP-1 was sufficiently high (f = 0.3231), with minimized vibronic coupling in the S0–S1 transitions. As a result, a narrow green PL peak with a small FWHM was observed at 506 nm (34 nm) in the PMMA film, and the solution-processed OLED device using a bipolar polymer host (Fig. 16d) was demonstrated to successfully show a narrow EL spectrum at 505 nm with FWHM = 33 nm (Fig. 16e).
Recently, Yasuda et al. reported four different kinds of MR-TADF molecules based on B/N-fused PAH structures (5–35~5–38) covering full-color emissions in the visible range109. Importantly, BBCz-R successfully demonstrated MR-TADF-based red emission for the first time. By differentiating the substituent positions of B and N atoms, the donating and accepting abilities were finely controlled. For instance, the donor strength of the N atoms bound in central benzene is depressed in BBCz-DB due to the para-positioned B atom, leading to deeper blue emission (466 nm) in toluene compared to that of BBCz-SB (481 nm) (Fig. 16f). In contrast, the symmetrical substitution of N or B atoms in BBCz-R strengthens the polar effect, leading to a bathochromic shift in the PL emission. The OLED devices fabricated with BBCz-DBA, BBCz-G, BBCz-Y, and BBCz-R exhibited narrowband and full-color EL spectra (λEL = 469, 515, 549, and 615 nm, respectively) (Fig. 16g). All the fabricated devices showed sufficiently high EQEs (22.0~31.8%) owing to the spontaneous horizontal orientation of molecules (Fig. 16h). Despite the broader bandwidth of EL spectra compared to that of red- and blue-emitting BBCz-R and BBCz-DB devices, BBCz-G and BBCz-Y showed less EQE roll-off owing to their relatively larger ICT character and faster RISC.
Inspired by the MR effects of B/N structures, other structures with different electron-withdrawing groups replacing boron atoms have been reported. For instance, Jiang et al. reported quinolino[3,2,1-de]acridine-5,9-dione (QAO, 5–39), which is composed of two carbonyl groups and one nitrogen atom fused together and exhibits a similar resonance effect110. QAO exhibited narrow PL emission at 466 nm with a FWHM of 32 nm in toluene; this emission is attributed to the rigid framework with well-separated HOMO and LUMO distributions. The EL spectrum of the QAO-based device was similar to its PL emission spectrum, showing an emission maximum at 468 nm with an FWHM of 39 nm and CIE coordinates of (0.13, 0.18), demonstrating another type of MR system without boron. Two new types of MR-TADF molecules, 3-phenylquinolino[3,2,1-de]acridine-5,9-dione (3-PhQAD, 5–40) and 7-phenylquinolino[3,2,1-de]acridine-5,9-dione (7-PhQAD, 5–41), were developed based on the QAO framework111. 3-PhQAD and 7-PhQAD exhibited narrowband emissions at 466 nm and 464 nm, respectively, with small FWHM values (<30 nm). Asymmetric 3-PhQAD showed a higher EQE (19.1%) and maximum current efficiency (33.5 cd A−1) than 7-PhQAD (EQE of 18.7% and current efficiency of 28.8 cd A−1), and both devices showed severe efficiency roll-off due to the loss of excitons via triplet-triplet annihilation (TTA) at low driving voltages and singlet-polaron annihilation (SPA) at higher driving voltages. Colman et al. also modified the QAO structure to synthesize 3,7,11-trimesitylquinolino[3,2,1-de]acridine-5,9-dione (Mes3DiKTa, 5–42) with three orthogonal mesityl groups that reduced intermolecular aggregation and emission quenching112. The PL maximum of Mes3DiKTa in toluene was 468 nm with a small FWHM (27 nm), and redshifted emission at 480 nm (FWHM = 36 nm) was obtained in the film. Although the Mes3DiKTa-based device showed a higher EQE (21.1% at 25 cd m-2) than the QAO-based device, it also suffered from severe efficiency roll-off. Colman’s group also reported dimeric QAO, [3,3′-biquinolino[3,2,1-de]acridine]-5,5′,9,9′-tetraone (DDiKTa, 5–43), which showed PL emission at λPL = 470 nm (FWHM of 47 nm) in toluene113. Among the devices fabricated with different DDiKTa dopant concentrations (3–12 wt%) in DPEPO, the 9 wt% doped device achieved the highest EQE (19%) with green emission at 500 nm and CIE coordinates of (0.18, 0.53).
Ma et al. also reported a series of MR-TADF-based QAO derivatives of QA-PF (5–44), QA-PCN (5–45), QA-PMO (5–46), and QA-PCz (5–47)114. A design strategy to yield narrow emission was proposed by enhancing the low-frequency vibronic coupling strength while simultaneously reducing the high-frequency vibronic coupling strength of the commonly involved stretching modes. The fluorophenyl groups in QA-PF suppressed the high-frequency stretching vibrations coupled to the structural reorganization between S0 and S1, resulting in a decrease in the overall reorganization energy. Based on this approach, all the QAO-based derivatives showed a narrower PL emission in toluene (FWHM = 23–29 nm) compared to that of QAO. The EL devices also showed narrow spectra (FWHM = 27–30 nm); however, the EQEs were still lower than those of the B/N core structures and suffered from severe efficiency roll-off originating from TTA and SPA. The close intermolecular packing was suggested as one reason for the EQE roll-off.
Conventional D-A type TADF emitters
Narrow-emissive TADF materials adopting a conventional TADF structure with spatially separated donor-acceptor substituents have also been studied (Fig. 17). Lee et al. designed and synthesized 4,4,6,6-tetra(9H-carbazol-9-yl)-[1,1-biphenyl]-3,3-dicarbonitrile (CzBPCN, 5–48) as a narrowband TADF emitter without the MR effect115. An isomeric structure of CzBPCN, 4,4,5,5-tetra(9H-carbazol-9-yl)-[1,1-biphenyl]-2,2-dicarbonitrile (CNBPCz), was also synthesized for comparison. Designed by differentiating the position of the donor (carbazole) and acceptor (nitrile) on the biphenyl central core, interlocked donor groups of CzBPCN restricted its molecular motion, resulting in narrow emission at 453 nm (FWHM of 51 nm) in toluene, while CNBPCz, which does not exhibit this interlocking effect, had an FWHM of over 70 nm at λPL = 458 nm. In addition, the rigid interlocked architecture of CzBPCN resulted in a higher PLQY of 94% compared to that of CNBPCz (37%). The OLED device fabricated with CzBPCN showed deep blue EL emission at 460 nm with FWHM = 48 nm and CIE coordinates of (0.14, 0.12), demonstrating the successful operation of narrow-emissive TADF OLEDs without an MR effect. Based on the 5-1 structure as an acceptor, Kwon’s group designed two new TADF molecules, 10-(2,12-di-tert-butyl-5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracen-7-yl)-9,9-dimethyl-9,10-dihydroacridine (TDBA-AC) (5–49) and 5-(2,12-di-tert-butyl-5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracen-7-yl)-10,15-diphenyl-10,15-dihydro-5H-diindolo[3,2-a:3,2-c]carbazole (TDBA-DI) (5–50), which incorporate dimethylacridine and diindolocarbazole as a donating group116. The mutually orthogonal conformation between the donating and accepting moieties reduced ΔEST, showing enhanced PLQYs of 93 and 99% in the DBFPO film. The strong donating ability of the diindolocarbazole in TDBA-DI resulted in a high PLQY (99%), but its stronger ICT interaction also increased the bandwidth (FWHM of 55 nm in toluene) compared to that of TDBA-AC (50 nm). OLEDs fabricated with TADF emitters doped in electron-transporting DBFPO (ITO/HATCN/TAPC/DCDPA/DBFPO:20 wt% TDBA-AC or TDBA-DI/DBFPO/TPBi/LiF/Al) showed high EQEs for both emitters (25.7% and 38.15%, respectively) via efficient RISC owing to the mutually orthogonal conformation of the donating and accepting moieties in their structures. Kwon also developed two blue-emitting TADF molecules, 9′-(2,12-di-tert-butyl-5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracen-7-yl)-9,9″-diphenyl-9H,9′H,9″H-3,3′:6′,3″-tercarbazole (3CzTB, 5–51) and 9′-(5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracen-7-yl)-6,6″-dimethyl-9,9″-diphenyl-9H,9′H,9″H-3,3′:6′,3″-tercarbazole (M3CzB, 5–52), with diphenyltercarbazoles as donating groups117. Modification of the alkyl substituent structure and position allows the CT character to be fine controlled. The addition of tert-butyl substituents at the 2 and 12 positions of the B/O framework (3CzTB) or methyl substituents of a donor moiety (M3CzB) yielded narrowband emission at 433 and 445 nm (FWHM ~50 nm) in toluene, respectively. Blue OLEDs fabricated with 3CzTB and M3CzB showed high EQEs (29–30%) and long operational lifetimes of over 81 h with a slightly larger FWHM (56 and 54 nm, respectively) compared to the MR-TADF emitters.
Summary and outlook
In this review, fluorescent, phosphorescent, and TADF emitters with narrowband emission were summarized, and the structure-property relationships were discussed. The development of narrow-emission OLED materials is of great importance to meet the new BT 2020 color standard for wide-gamut displays118,119. Recently, molecular design strategies and the underlying mechanisms for controlling the emission bandwidth have been studied extensively to achieve narrow PL and EL.
π-Conjugated organic fluorophores normally suffer from limited color purity with broad emission owing to their intrinsic vibronic coupling between the S0 and S1 states as well as structural relaxation in the excited state. Twisted or rigid structures with fused aromatic backbones have shown narrow emissions with a dominant 0–0 transition caused by inhibition of CT interactions and intermolecular aggregation in the solid state. For example, a narrow EL spectrum (FWHM of 35 nm) was observed in TPA-PIM (1–9), which has suppressed vibrational splitting due to its fully twisted donor-acceptor structure, achieving the smallest CIEy of 0.046 ever reported at that time31. The rigid planar flavanthrone-based dyes (compounds 1–15~17) showed extremely small FWHM values of ~22 nm at 535 nm in their EL spectra36. The quinacridone or BODIPY-based structures also exhibited a small FWHM ≤ ~50 nm in the green to red region.
The emitting T1 state in cyclometalated phosphorescent emitters is often determined by intermixing the 3MLCT and 3LC states. Ir-based octahedral complexes have short phosphorescence lifetimes with high PLQYs due to strong SOC, but their MLCT-dominant emissions result in broad spectra. Several square planar Pt- and Pd-based structures have shown narrow phosphorescence, where the T1 state is mainly determined by the 3LC state. By modifying the ligand structures in the cyclometalated Pt/Pd complexes, the emission bandwidth can be further decreased, increasing the color purity. Li et al. modified the rigid tetradentate pyridyl ring of carbazolyl pyridine ancillary ligands to further suppress the vibrational coupling, resulting in improved phosphorescence quantum yield and achieving an FWHM of <20 nm with >80% PLQY (compounds 3–1~5). In particular, the PtON7-dtb (3–5)-based EL device exhibited a high EQE of 24.8% with dominant emission at 451 nm (FWHM of 29 nm).
TADF molecules can achieve 100% IQE through efficient upconversion via the RISC process; however, these emitters are often designed by spatial separation of the HOMO and LUMO distributions to decrease the ΔEST between the S1 and T1 states. This strategy enhances the structural relaxation in the excited states via ICT, resulting in a broad CT emission with FWHM values of 70–100 nm and large Stokes shifts. Recently, new MR-based TADF molecules with rigid skeletons and regular arrangements of boron and nitrogen atoms have been investigated extensively by Hatakeyama et al. Owing to the MR effects between the electron-accepting boron and electron-donating nitrogen atoms, the strategic separation of the HOMO and LUMO localized around the individual atoms could achieve not only high EQE but also narrow emission bandwidth. For example, MR-TADF OLEDs based on ν-DABNA (5–14) demonstrated extremely narrow emission with an FWHM of 18 nm and a remarkably high EQE of 31.4% 95.
Although many promising results for the development of singlet and triplet emitters with narrow emission have been reported, several challenges remain. To further decrease the emission bandwidth, the 0–0 vibronic transition should be intensified with higher 0–n (n = 1, 2, 3…) vibronic transitions suppressed. Thus far, it is not clearly understood how the 0–n vibronic transitions can be efficiently suppressed or controlled by the molecular design of fluorophores. The vibrational normal modes coupled with the electronic S1 to S0 transition need to be studied to understand how to control their Huang–Rhys factors and minimize the 0–n vibronic transition. The number of green- and red-emitting singlet fluorescent emitters is very limited, with most of the reported narrowband fluorophores being blue-emitting materials. Molecules are often designed to exploit the ICT interaction to extend the effective conjugation with a reduced bandgap; however, the CT character induces undesirable broad emission. Given these limitations, the development of efficient green- and red-emitting fluorescent materials with small FWHM values is of paramount importance. Hyperfluorescent OLEDs made by combining TADF sensitizers and narrow-emitting fluorescent dopants can be an effective strategy to achieve both high EQE and color purity. In the case of phosphorescent triplet emitters, the structural optimization of square planar organometal complexes is still needed. For instance, rigid tetradentate ligands without intraligand or interligand CT interactions can reduce vibronic coupling with decreased emission bandwidth. Similar to the case of fluorescent materials, the investigation of the vibrational normal modes coupled with the LC S1 to S0 transition to decrease their Huang–Rhys factors may suggest an affordable solution to intensify the 0–0 transition with reduced 0–n vibronic peaks. The compound library of phosphorescent emitters showing narrow emission and high PLQY needs to be further expanded. As shown in Fig. 1d, blue- and green-MR-TADF emitters have been widely studied to achieve narrow emission and high EQE. However, the development of red-emitting MR-TADF molecules is still far behind, and extending the conjugation of these molecules without broadening the emission bandwidth remains challenging. In addition, the efficiency roll-off in MR-TADF OLEDs that occurs at a high current density remains a significant barrier to the industrialization of MR-TADF OLEDs. To overcome the EQE and its roll-off that originates from TTA, SPA, aggregation quenching, etc., the optimization of emitter structures and the optimization of the device architecture should be considered together. For instance, Adachi recently reported an MR-TADF OLED employing ν-DABNA as an emitter by combining a TADF sensitizer, showing a maximum EQE of 41% with suppressed efficiency roll-off120. Monkman also adopted ν-DABNA as a hyperfluorescent emitter, suppressing efficiency roll-off by decreasing the excimer quenching with optimization of its doping ratio121. In addition, the enhancement of outcoupling efficiency by controlling the molecular orientation of MR-TADF emitters needs to be studied to further improve the EQE and roll-off. As discussed, the underlying mechanism needs to be further clarified, and fine optimization of the host, TADF dopants, and charge injection/transport layers is necessary to improve the charge balance and efficiency roll-off. In particular, special attention should be given to the design of narrowband green emitters because their CIE coordinates need to be further optimized to a further degree than those of blue and red emitters to satisfy the BT 2020 standards. Despite the current challenges, narrowband emissive OLEDs have great potential to become an efficient and extensively adopted display technology in the next generation of high-resolution and wide-color gamut displays if both the resolution and color chromaticity are considered.
References
Tang, C. W. & Vanslyke, S. A. Organic electroluminescent diodes. Appl Phys. Lett. 51, 913–915 (1987).
Shirota, Y. & Kageyama, H. Charge carrier transporting molecular materials and their applications in devices. Chem. Rev. 107, 953–1010 (2007).
Hong, G. et al. A brief history of OLEDs-emitter development and industry milestones. Adv. Mater. 33, 2005630 (2021).
Broadbent, A. D. A critical review of the development of the CIE1931 RGB color-matching functions. Color Res. Appl 29, 267–272 (2004).
International Telecommunication Union (ITU), BT.2020. Parameter Values for Ultra-High Definition Television Systems for Production and International Programme Exchange. https://www.itu.int/rec/R-REC-BT.2020-1-201406-S/en (2014).
Ye, Y., He, Y. W. & Xiu, X. Y. Manipulating ultra-high definition video traffic. IEEE Multimed. 22, 73–81 (2015).
Qian, G. et al. Band gap tunable, donor-acceptor-donor charge-transfer heteroquinoid-based chromophores: near infrared photoluminescence and electroluminescence. Chem. Mater. 20, 6208–6216 (2008).
Wang, S. P. et al. Highly efficient near-infrared delayed fluorescence organic light emitting diodes using a phenanthrene-based charge-transfer compound. Angew. Chem. Int Ed. 54, 13068–13072 (2015).
Gierschner, J., Mack, H. G., Luer, L. & Oelkrug, D. Fluorescence and absorption spectra of oligophenylenevinylenes: vibronic coupling, band shapes, and solvatochromism. J. Chem. Phys. 116, 8596–8609 (2002).
Zhang, B., Wu, H. Z., Wang, Z. M., Qin, A. J. & Tang, B. Z. Planarized intramolecular charge transfer on triphenylamine-modified pyrazine and its application in organic light-emitting diodes. J. Mater. Chem. C 8, 4754–4762 (2020).
Liu, B. Q. et al. Monocationic iridium(III) complexes with far-red charge-transfer absorption and near-ir emission: synthesis, photophysics, and reverse saturable absorption. Eur. J. Inorg. Chem. 2019, 2208–2215 (2019).
Yang, Z. W. et al. Recent advances in quantum dot-based light-emitting devices: challenges and possible solutions. Mater. Today 24, 69–93 (2019).
Steckel, J. S., Ho, J. & Coe-Sullivan, S. QDs generate light for next-generation. Disp. Photonic Spectra 48, 55–61 (2014).
Lee, E. et al. "Greener" quantum-dot enabled LCDs with BT.2020 color gamut. SID 41-1, 549–551 (2016).
Cho, Y., Choi, Y. K. & Sohn, S. H. Optical properties of neodymium-containing polymethylmethacrylate films for the organic light emitting diode color filter. Appl. Phys. Lett. 89, 051102 (2006).
Frobel, M. et al. Three-terminal RGB full-color OLED pixels for ultrahigh density displays. Sci. Rep. 8, 9684 (2018).
Lee, K. T., Han, S. Y., Li, Z. J., Baac, H. W. & Park, H. J. Flexible high-color-purity structural color filters based on a higher-order optical resonance suppression. Sci. Rep. 9, 14917 (2019).
de Jong, M., Seijo, L., Meijerink, A. & Rabouw, F. T. Resolving the ambiguity in the relation between Stokes shift and Huang-Rhys parameter. Phys. Chem. Chem. Phys. 17, 16959–16969 (2015).
Li, K. et al. Highly phosphorescent platinum(II) emitters: photophysics, materials and biological applications. Chem. Sci. 7, 1653–1673 (2016).
Li, W. J. et al. A hybridized local and charge-transfer excited state for highly efficient fluorescent OLEDs: molecular design, spectral character, and full exciton utilization. Adv. Opt. Mater. 2, 892–901 (2014).
Lin, J. Y. et al. Ultrastable supramolecular self-encapsulated wide-bandgap conjugated polymers for large-area and flexible electroluminescent devices. Adv. Mater. 31, 1804811 (2019).
Kim, Y. H. et al. Novel blue emitting material with high color purity. Adv. Mater. 13, 1690–1693 (2001).
Park, H. et al. Highly rigid and twisted anthracene derivatives: a strategy for deep blue OLED materials with theoretical limit efficiency. J. Mater. Chem. 22, 2695–2700 (2012).
Odom, S. A., Parkin, S. R. & Anthony, J. E. Tetracene derivatives as potential red emitters for organic LEDs. Org. Lett. 5, 4245–4248 (2003).
Park, Y. et al. New blue-violet emitters based on an indenopyrazine core for OLEDs: effects of the position of m-terphenyl side group substitution on optical and electroluminescence properties. Org. Electron 11, 864–871 (2010).
Park, Y. I. et al. Synthesis and electroluminescence properties of novel deep blue emitting 6,12-dihydro-diindeno[1,2-b: 1′,2′-e] pyrazine derivatives. Chem. Commun. 2008, 2143–2145 (2008).
Park, Y. et al. An aromatic imine group enhances the EL efficiency and carrier transport properties of highly efficient blue emitter for OLEDs. J. Mater. Chem. 20, 5930–5936 (2010).
Wang, Z. M. et al. Phenanthro[9,10-d]imidazole as a new building block for blue light emitting materials. J. Mater. Chem. 21, 5451–5456 (2011).
Gao, Z. et al. High-efficiency violet-light-emitting materials based on phenanthro[9,10-d]imidazole. Chem. Eur. J. 19, 2602–2605 (2013).
Gao, Z. et al. Highly efficient deep blue light emitting devices based on triphenylsilane modified phenanthro[9, 10-d]imidazole. Laser Photonics Rev. 8, L6–L10 (2014).
Li, W. J. et al. Highly efficient deep-blue OLED with an extraordinarily narrow FHWM of 35 nm and a y coordinate < 0.05 based on a fully twisting donor-acceptor molecule. J. Mater. Chem. C 2, 4733–4736 (2014).
Jeon, Y. M., Lee, J. Y., Kim, J. W., Lee, C. W. & Gong, M. S. Deep-blue OLEDs using novel efficient spiro-type dopant materials. Org. Electron 11, 1844–1852 (2010).
Cocherel, N., Poriel, C., Vignau, L., Bergamini, J. F. & Rault-Berthelot, J. Dispiroxanthene-indenofluorene: a new blue emitter for nondoped organic light emitting diode applications. Org. Lett. 12, 452–455 (2010).
Jung, H. et al. High efficiency and long lifetime of a fluorescent blue-light emitter made of a pyrene core and optimized side groups. ACS Appl Mater. Interfaces 10, 30022–30028 (2018).
Ahn, D. H., Jeong, J. H., Song, J., Lee, J. Y. & Kwon, J. H. Highly efficient deep blue fluorescent organic light-emitting diodes boosted by thermally activated delayed fluorescence sensitization. ACS Appl Mater. Interfaces 10, 10246–10253 (2018).
Kotwica, K. et al. Soluble flavanthrone derivatives: synthesis, characterization, and application to organic light-emitting diodes. Chem. Eur. J. 22, 7978–7986 (2016).
Shah, B. K., Neckers, D. C., Shi, J. M., Forsythe, E. W. & Morton, D. Anthanthrene derivatives as blue emitting materials for organic light-emitting diode applications. Chem. Mater. 18, 603–608 (2006).
Chen, D. J. et al. Efficient solution-processed red all-fluorescent organic light-emitting diodes employing thermally activated delayed fluorescence materials as assistant hosts: molecular design strategy and exciton dynamic analysis. J. Mater. Chem. C 5, 5223–5231 (2017).
Debad, J. D., Morris, J. C., Lynch, V., Magnus, P. & Bard, A. J. Dibenzotetraphenylperiflanthene: synthesis, photophysical properties, and electrogenerated chemiluminescence. J. Am. Chem. Soc. 118, 2374–2379 (1996).
Lee, H., Chung, W. J. & Lee, J. Y. Narrowband and pure violet organic emitter with a full width at half maximum of 14 nm and gamma color coordinate of below 0.02. Small 16, 1907569 (2020).
Ye, K. Q. et al. Supramolecular structures and assembly and luminescent properties of quinacridone derivatives. J. Phys. Chem. B 109, 8008–8016 (2005).
Bi, H. et al. Fluorinated quinacridone derivative based organic light-emitting device with high power efficiency. Org. Electron 11, 1180–1184 (2010).
Wang, C. G. et al. Polymorph, assembly, luminescence and semiconductor properties of a quinacridone derivative with extended pi-conjugated framework. J. Mater. Chem. C 1, 5548–5556 (2013).
Ivaniuk, K. et al. BODIPY-core 1,7-diphenyl-substituted derivatives for photovoltaics and OLED applications. Dyes Pigm. 175, 108123 (2020).
Zatsikha, Y. V., Yakubovskyi, V. P., Shandura, M. P., Dubey, I. Y. & Kovtun, Y. P. An efficient method of chemical modification of BODIPY core. Tetrahedron 69, 2233–2238 (2013).
Bonardi, L. et al. Fine-tuning of yellow or red photo- and electroluminescence of functional difluoro-boradiazaindacene films. Adv. Funct. Mater. 18, 401–413 (2008).
Merkushev, D. A. et al. BODIPY associates in organic matrices: Spectral properties, photostability and evaluation as OLED emitters. Mater. Chem. Phys. 187, 104–111 (2017).
Santra, M. et al. Dramatic substituent effects on the photoluminescence of boron complexes of 2-(benzothiazol-2-yl)phenols. Chem. Eur. J. 18, 9886–9893 (2012).
Song, X. Z., Zhang, D. D., Zhang, Y. W., Lu, Y. & Duan, L. Strategically modulating carriers and excitons for efficient and stable ultrapure-green fluorescent OLEDs with a sterically hindered BODIPY dopant. Adv. Opt. Mater. 8, 2000483 (2020).
Lamansky, S. et al. Synthesis and characterization of phosphorescent cyclometalated iridium complexes. Inorg. Chem. 40, 1704–1711 (2001).
Brooks, J. et al. Synthesis and characterization of phosphorescent cyclometalated platinum complexes. Inorg. Chem. 41, 3055–3066 (2002).
Adachi, C., Baldo, M. A., Thompson, M. E. & Forrest, S. R. Nearly 100% internal phosphorescence efficiency in an organic light-emitting device. J. Appl. Phys. 90, 5048–5051 (2001).
Tsuboyama, A. et al. Homoleptic cyclometalated iridium complexes with highly efficient red phosphorescence and application to organic light-emitting diode. J. Am. Chem. Soc. 125, 12971–12979 (2003).
Yersin, H. Highly Efficient OLEDs with Phosphorescent Materials (Wiley‐VCH, Weinheim, Germany, 2007).
Howarth, A. J., Majewski, M. B. & Wolf, M. O. Photophysical properties and applications of coordination complexes incorporating pyrene. Coord. Chem. Rev. 282, 139–149 (2015).
Heine, J. & Muller-Buschbaum, K. Engineering metal-based luminescence in coordination polymers and metal-organic frameworks. Chem. Soc. Rev. 42, 9232–9242 (2013).
Rausch, A., Homeier, H., Djurovich, P., Thompson, M. & Yersin, H. Spin-orbit coupling routes and OLED performance: studies of blue-light emitting Ir(III) and Pt (II) complexes. In Proc. SPIE 6655, Organic Light Emitting Materials and Devices XI 66550F (2007).
Baldo, M. A., Lamansky, S., Burrows, P. E., Thompson, M. E. & Forrest, S. R. Very high-efficiency green organic light-emitting devices based on electrophosphorescence. Appl. Phys. Lett. 75, 4–6 (1999).
Hofbeck, T. & Yersin, H. The triplet state of fac-Ir(ppy)(3). Inorg. Chem. 49, 9290–9299 (2010).
Kim, H. U. et al. Substituents engineered deep-red to near-infrared phosphorescence from tris-heteroleptic iridium(III) complexes for solution processable red-NIR organic light-emitting diodes. J. Mater. Chem. C 6, 10640–10658 (2018).
Kim, H. U. et al. Ancillary ligand-assisted robust deep-red emission in iridium(iii) complexes for solution-processable phosphorescent OLEDs. J. Mater. Chem. C 7, 4143–4154 (2019).
Ren, B. Y. et al. A yellow-emitting homoleptic iridium(III) complex constructed from a multifunctional spiro ligand for highly efficient phosphorescent organic light-emitting diodes. Inorg. Chem. 56, 8397–8407 (2017).
Hohenleutner, A. et al. Rapid combinatorial synthesis and chromatography based screening of phosphorescent iridium complexes for solution processing. Adv. Funct. Mater. 22, 3406–3413 (2012).
Jang, J. H. et al. Red phosphorescent naphthalene-based iridium(III) complex for solution-processed single-emissive-layer white organic light-emitting diodes. J. Nanosci. Nanotechnol. 16, 8580–8584 (2016).
Fleetham, T., Li, G. J., Wen, L. L. & Li, J. Efficient “pure” blue OLEDs employing tetradentate Pt complexes with a narrow spectral bandwidth. Adv. Mater. 26, 7116–7121 (2014).
Li, G. J., Wolfe, A., Brooks, J., Zhu, Z. Q. & Li, J. Modifying emission spectral bandwidth of phosphorescent platinum(II) complexes through synthetic control. Inorg. Chem. 56, 8244–8256 (2017).
Li J., Turner E. & Huang L. Metal compounds and methods and uses thereof. USA patent WO 2014031977 A1 (2014).
Li, G. J., Fleetham, T., Turner, E., Hang, X. C. & Li, J. Highly efficient and stable narrow-band phosphorescent emitters for OLED applications. Adv. Opt. Mater. 3, 390–397 (2015).
Ma, H. L. et al. High-color-purity and efficient solution-processable blue phosphorescent light-emitting diodes with Pt(ii) complexes featuring 3pi pi* transitions. Mater. Chem. Front. 3, 2448–2454 (2019).
Baldo, M. A. et al. Highly efficient phosphorescent emission from organic electroluminescent devices. Nature 395, 151–154 (1998).
Kwong, R. C. et al. Efficient, saturated red organic light emitting devices based on phosphorescent platinum(II) porphyrins. Chem. Mater. 11, 3709–3713 (1999).
La Deda, M. et al. Organometallic emitting dyes: palladium(II) nile red complexes. J. Organomet. Chem. 690, 857–861 (2005).
Zhu, W. H. & Fan, L. Q. Room temperature phosphorescence of a palladium(II) complex sensitized by unsymmetric perylene bisimide. Dyes Pigm. 76, 663–668 (2008).
Zhu, Z. Q., Park, C. D., Klimes, K. & Li, J. Highly efficient blue OLEDs based on metal-assisted delayed fluorescence Pd(II) complexes. Adv. Opt. Mater. 7, 1801518 (2019).
Borisov, S. M., Zenkl, G. & Klimant, I. Phosphorescent platinum(II) and palladium(II) complexes with azatetrabenzoporphyrins-new red laser diode-compatible indicators for optical oxygen sensing. ACS Appl. Mater. Interfaces 2, 366–374 (2010).
Niedermair, F. et al. Tunable phosphorescent NIR oxygen indicators based on mixed benzo- and naphthoporphyrin complexes. Inorg. Chem. 49, 9333–9342 (2010).
Pang, H. et al. 83-1: Invited paper: optimization of high performance deep red OLEDs using tandem structure for automotive lighting application. SID 51, 1247–1250 (2020).
Margulies, E. A. et al. 65-1: Invited paper: narrow spectrum deep red emitters for OLED lighting and display. SID 50, 911–913 (2019).
Binnemans, K. Interpretation of europium(III) spectra. Coord. Chem. Rev. 295, 1–45 (2015).
Binnemans, K. Lanthanide-Based Luminescent hybrid materials. Chem. Rev. 109, 4283–4374 (2009).
Hasegawa, Y., Kitagawa, Y. & Nakanishi, T. Effective photosensitized, electrosensitized, and mechanosensitized luminescence of lanthanide complexes. Npg Asia Mater. 10, 52–70 (2018).
Vázquez-Ibar, J. L., Weinglass, A. B. & Kaback, H. R. Engineering a terbium-binding site into an integral membrane protein for luminescence energy transfer. Proc. Natl Acad. Sci. USA 99, 3487–3492 (2002).
Li, H. R. et al. Preparation and luminescence properties of hybrid materials containing europium(III) complexes covalently bonded to a silica matrix. Chem. Mater. 14, 3651–3655 (2002).
Martins, J. P. et al. Highly luminescent pure-red-emitting fluorinated beta-diketonate europium(III) complex for full solution-processed OLEDs. J. Lumin. 159, 17–25 (2015).
Rajamouli, B., Sood, P., Giri, S., Krishnan, V. & Sivakumar, V. A dual-characteristic bidentate ligand for a ternary mononuclear europium(III) molecular complex - synthesis, photophysical, electrochemical, and theoretical study. Eur. J. Inorg. Chem. 2016, 3900–3911 (2016).
Borisov, S. M., Fischer, R., Saf, R. & Klimant, I. Exceptional oxygen sensing properties of new blue light-excitable highly luminescent europium(III) and gadolinium(III) complexes. Adv. Funct. Mater. 24, 6548–6560 (2014).
Devi, R. & Vaidyanathan, S. Narrow band red emitting europium complexes and their application in smart white LEDs and vapoluminescent sensors. Dalton Trans. 49, 6205–6219 (2020).
Yu, G. et al. Highly efficient terbium(III)-based organic light-emitting diodes obtained by exciton confinement. J. Mater. Chem. C 4, 121–125 (2016).
Chen, Z. Q. et al. A highly efficient OLED based on terbium complexes. Org. Electron 10, 939–947 (2009).
Ilmi, R. et al. A single component white electroluminescent device fabricated from a metallo-organic terbium complex. J. Mater. Chem. C 7, 13966–13975 (2019).
Parker, C. A. & Hatchard, C. G. Triplet-singlet emission in fluid solutions - phosphorescence of eosin. Trans. Faraday Soc. 57, 1894–1904 (1961).
Endo, A. et al. Efficient up-conversion of triplet excitons into a singlet state and its application for organic light emitting diodes. Appl. Phys. Lett. 98, 083302 (2011).
Uoyama, H., Goushi, K., Shizu, K., Nomura, H. & Adachi, C. Highly efficient organic light-emitting diodes from delayed fluorescence. Nature 492, 234–238 (2012).
Hatakeyama, T. et al. Ultrapure blue thermally activated delayed fluorescence molecules: efficient HOMO-LUMO separation by the multiple resonance effect. Adv. Mater. 28, 2777–2781 (2016).
Kondo, Y. et al. Narrowband deep-blue organic light-emitting diode featuring an organoboron-based emitter. Nat. Photonics 13, 678–682 (2019).
Hirai, H. et al. One-step borylation of 1,3-diaryloxybenzenes towards efficient materials for organic light-emitting diodes. Angew. Chem. Int. Ed. 54, 13581–13585 (2015).
Kitamoto, Y. et al. The first synthesis and X-ray crystallographic analysis of an oxygen-bridged planarized triphenylborane. Chem. Commun. 52, 7098–7101 (2016).
Nakatsuka, S., Gotoh, H., Kinoshita, K., Yasuda, N. & Hatakeyama, T. Divergent synthesis of heteroatom-centered 4,8,12-triazatriangulenes. Angew. Chem. Int. Ed. 56, 5087–5090 (2017).
Matsui, K. et al. One-shot multiple borylation toward BN-doped nanographenes. J. Am. Chem. Soc. 140, 1195–1198 (2018).
Oda, S., Kawakami, B., Kawasumi, R., Okita, R. & Hatakeyama, T. Multiple resonance effect-induced sky-blue thermally activated delayed fluorescence with a narrow emission band. Org. Lett. 21, 9311–9314 (2019).
Han, S. H., Jeong, J. H., Yoo, J. W. & Lee, J. Y. Ideal blue thermally activated delayed fluorescence emission assisted by a thermally activated delayed fluorescence assistant dopant through a fast reverse intersystem crossing mediated cascade energy transfer process. J. Mater. Chem. C 7, 3082–3089 (2019).
Liang, X. et al. Peripheral amplification of multi-resonance induced thermally activated delayed fluorescence for highly efficient OLEDs. Angew. Chem. Int. Ed. 57, 11316–11320 (2018).
Oda, S. et al. Carbazole-based DABNA analogues as highly efficient thermally activated delayed fluorescence materials for narrowband organic light-emitting diodes. Angew. Chem. Int. Ed. 60, 2882–2886 (2021).
Xu, Y. C. et al. Molecular-structure and device-configuration optimizations toward highly efficient green electroluminescence with narrowband emission and high color purity. Adv. Opt. Mater. 8, 1902142 (2020).
Xu, Y. C. et al. Constructing charge-transfer excited states based on frontier molecular orbital engineering: narrowband green electroluminescence with high color purity and efficiency. Angew. Chem. Int. Ed. 59, 17442–17446 (2020).
Zhang, Y. W. et al. Multi-resonance induced thermally activated delayed fluorophores for narrowband green OLEDs. Angew. Chem. Int. Ed. 58, 16912–16917 (2019).
Zhang, Y. W. et al. Achieving pure green electroluminescence with CIEy of 0.69 and EQE of 28.2% from an aza-fused multi-resonance emitter. Angew. Chem. Int. Ed. 59, 17499–17503 (2020).
Ikeda, N. et al. Solution-processable pure green thermally activated delayed fluorescence emitter based on the multiple resonance effect. Adv. Mater. 32, 2004072 (2020).
Yang, M. L., Park, I. S. & Yasuda, T. Full-color, narrowband, and high-efficiency electroluminescence from boron and carbazole embedded polycyclic heteroaromatics. J. Am. Chem. Soc. 142, 19468–19472 (2020).
Yuan, Y. et al. The design of fused amine/carbonyl system for efficient thermally activated delayed fluorescence: novel multiple resonance core and electron acceptor. Adv. Opt. Mater. 7, 1801536 (2019).
Li, X. et al. Thermally activated delayed fluorescence carbonyl derivatives for organic light-emitting diodes with extremely narrow full width at half-maximum. ACS Appl. Mater. Interfaces 11, 13472–13480 (2019).
Hall, D. et al. Improving processability and efficiency of resonant TADF emitters: a design strategy. Adv. Opt. Mater. 8, 1901627 (2020).
Sun, D. M. et al. The design of an extended multiple resonance TADF emitter based on a polycyclic amine/carbonyl system. Mater. Chem. Front. 4, 2018–2022 (2020).
Qiu, X. et al. Narrowband emission from organic fluorescent emitters with dominant low-frequency vibronic coupling. Adv. Opt. Mater. 9, 2001845 (2021).
Cho, Y. J., Jeon, S. K., Lee, S. S., Yu, E. & Lee, J. Y. Donor interlocked molecular design for fluorescence-like narrow emission in deep blue thermally activated delayed fluorescent emitters. Chem. Mater. 28, 5400–5405 (2016).
Ahn, D. H. et al. Highly efficient blue thermally activated delayed fluorescence emitters based on symmetrical and rigid oxygen-bridged boron acceptors. Nat. Photonics 13, 540–546 (2019).
Karthik, D. et al. Highly efficient blue thermally activated delayed fluorescence organic light emitting diodes based on tercarbazole donor and boron acceptor dyads. J. Mater. Chem. C 8, 2272–2279 (2020).
Masaoka, K., Nishida, Y. & Sugawara, M. Designing display primaries with currently available light sources for UHDTV wide-gamut system colorimetry. Opt. Express 22, 19069–19077 (2014).
Fukagawa, H., Oono, T., Iwasaki, Y., Hatakeyama, T. & Shimizu, T. High-efficiency ultrapure green organic light-emitting diodes. Mater. Chem. Front. 2, 704–709 (2018).
Chan, C. Y. et al. Stable pure-blue hyperfluorescence organic light-emitting diodes with high-efficiency and narrow emission. Nat. Photonics 15, 203–207 (2021).
Stavrou, K., Danos, A., Hama, T., Hatakeyama, T. & Monkman, A. Hot vibrational states in a high-performance multiple resonance emitter and the effect of excimer quenching on organic light-emitting diodes. ACS Appl. Mater. Interfaces 13, 8643–8655 (2021).
Acknowledgements
This work was supported by the National Research Foundation (NRF) of Korea (Grants NRF-2019R1A2C2085290, 2019R1A6A1A11044070, 2016M1A2A2940911, NRF2020M3H4A3081814). This work was supported by the Korea University Grant and LG Display.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ha, J.M., Hur, S.H., Pathak, A. et al. Recent advances in organic luminescent materials with narrowband emission. NPG Asia Mater 13, 53 (2021). https://doi.org/10.1038/s41427-021-00318-8
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41427-021-00318-8
- Springer Japan KK
This article is cited by
-
Highly efficient pure-blue organic light-emitting diodes based on rationally designed heterocyclic phenophosphazinine-containing emitters
Nature Communications (2024)
-
Exploring Dual Solvatochromic Traits in Novel Fluorescent Benzanthrone Ethynyl Derivatives
Journal of Solution Chemistry (2024)
-
Photoluminescence properties of CaMgB2O5: RE3+ (RE = Dy, Eu, Sm) environmental friendly phosphor for solid state lighting
Indian Journal of Physics (2024)
-
Highly Fluorescent π-Conjugated Azomethines and Divalent Metal Complexes as Antibacterial and Antibiofilm Nominees
Journal of Fluorescence (2024)
-
Theoretical investigations on electronic structure and optoelectronic properties of vinyl fused monomeric and oligomeric benzimidazole derivatives using DFT and TDDFT techniques
Journal of Molecular Modeling (2024)