Abstract
Topological magnons are emergent quantum spin excitations featured by magnon bands crossing linearly at the points dubbed nodes, analogous to fermions in topological electronic systems. Experimental realisation of topological magnons in three dimensions has not been reported so far. Here, by measuring spin excitations (magnons) of a three-dimensional antiferromagnet Cu3TeO6 with inelastic neutron scattering, we provide direct spectroscopic evidence for the coexistence of symmetry-protected Dirac and triply degenerate nodes, the latter involving three-component magnons beyond the Dirac–Weyl framework. Our theoretical calculations show that the observed topological magnon band structure can be well described by the linear-spin-wave theory based on a Hamiltonian dominated by the nearest-neighbour exchange interaction J1. As such, we showcase Cu3TeO6 as an example system where Dirac and triply degenerate magnonic nodal excitations coexist, demonstrate an exotic topological state of matter, and provide a fresh ground to explore the topological properties in quantum materials.
Similar content being viewed by others
Introduction
By introducing the concept of topology into electronic bands, plenty of novel quantum materials, such as topological insulators1,2 with the edge state existing in the bulk gap, and Dirac3,4,5,6 and Weyl semimetals7,8,9 featured by linear-band crossings at the Dirac and Weyl nodes, respectively, have been discovered. Excitations associated with these topological states are fermions described by the Dirac–Weyl equations10,11. Recently, exotic new fermions12,13,14,15, such as the triply degenerate ones beyond such a classification, have emerged16,17, enriching the family of topological materials and advancing the understanding on band topology. Since topological band structure is independent of the statistics of the constituent quasiparticles, many efforts have been devoted to seeking for nontrivial topological analogues of fermions in bosonic systems, e.g., phononic18,19,20,21,22 and photonic crystals23,24,25,26,27,28,29. In two dimensions, various topological states for magnons (also bosons), which are spin excitations in magnetically ordered systems, have also been proposed. These include topological magnon insulators30,31,32,33,34, and magnonic Dirac35,36,37,38 and Weyl semimetals39,40,41,42,43. Following the successful examples in fermionic systems13,14,16, triply degenerate nodal excitations have been predicted for the magnonic case44,45, extending the topological classification in bosonic systems. Topological magnonic systems exhibit: (i) non-zero Berry curvature which gives rise to the anomalous Hall effect of the heat current carried by the charge-neutral spin excitations33,46,47,48,49,50,51; (ii) edge or surface state that is topologically protected30,32,52,53. These exotic properties make the materials appealing in developing high-efficiency and low-cost spintronic devices47,53,54,55. However, candidate materials to realise topological magnons are scarce. Especially for topological magnons in three dimensions, there has been no experimental report so far. In this regard, Li et al. 56 have predicted Cu3TeO6 to host Dirac magnons, offering an excellent opportunity for experimental investigations into the topological properties of magnons.
In this work, we measure the spin excitations in Cu3TeO6 with inelastic neutron scattering (INS), and compare the INS data with the linear-spin-wave calculations performed based on a Hamiltonian dominated by the nearest-neighbour (NN) exchange interaction J1. From the results, we discover symmetry-protected three-dimensional Dirac and triply degenerate magnons in Cu3TeO6.
Results
Sample characterisations
The crystal structure of Cu3TeO6 with the Ia-3 space group (no. 206) is illustrated in Fig. 1a (ref. 57). Six Cu2+ ions form an almost coplanar hexagon, and each ion is vertex-shared by two hexagons, constituting a three-dimensional spin-web structure57,58,59,60. Neutron powder diffraction has shown that Cu3TeO6 develops a long-range collinear antiferromagnetic order below the transition temperature TN of 61 K, with spins aligned along the [111] direction57,58. Such a magnetic state as illustrated in Fig. 1a, with each up spin related to a down spin by centro-inversion, belongs to a magnetic group with the PT symmetry56, where P and T are space-inversion and time-reversal operations, respectively. Under the protection of this symmetry, magnons are expected to exhibit nontrivial topological properties56. INS is a direct approach to visualise magnon bands in the momentum and energy space, which acts as angle-resolved-photoemission spectroscopy in characterising electronic band structures5,8,17. Below, we present results from INS measurements on well-characterised high-quality single crystals of Cu3TeO6 (see Supplementary Figs. 1 and 2 for details).
Magnetic excitation spectra
We have obtained a rich INS dataset which covers up to eight Brillouin zones in the whole energy range of interest at various temperatures. In Fig. 2a–c, we present the excitation spectra obtained at T = 5 K along three high-symmetry directions [001], [101], and [111], respectively. These directions are illustrated in Fig. 1b. The INS spectra show clear excitations dispersing up from the magnetic Bragg peaks57. More magnetic peaks are shown in Supplementary Fig. 4. These peaks can be almost perfectly indexed with the collinear magnetic structure which respects the PT symmetry57,58. We have performed measurements at higher temperatures up to T = 70 K, above the TN of 61 K, and the results are shown in Supplementary Figs. 3 and 4. We find that the well-defined dispersions at T = 5 K become almost featureless at 70 K (Supplementary Fig. 3g–i), along with the disappearance of the magnetic Bragg peaks (Supplementary Fig. 4e, f). The wave-vector and temperature dependences of the excitations are clearly evidencing that they are spin-wave excitations.
Turning back to the data at 5 K, we can see that the acoustic bands extend up to about 15 meV, and the optical bands are present roughly between 15 and 20 meV. As there are 12 Cu2+ atoms in a primitive unit cell57, there are six doubly degenerate magnon bands due to the PT symmetry56. Since these six bands coexist in such a narrow energy window, band crossings are expected. In fact, by bare visual inspection of Fig. 2a–c, we can already identify various high-symmetry points at which the bands cross each other. Taking Fig. 2a as an example, Γ points at E ≈ 15 meV, and H point at E ≈ 16 and 18.5 meV exhibit as hot spots in the dispersion. At the H point, the interval between the two spots is clearly visible. To better characterise these points, we perform theoretical calculations as described below.
Comparison with linear-spin-wave calculations
The well-defined acoustic modes and quick disappearance of the magnetic order and excitations when approaching TN (Supplementary Fig. 4) indicate that Cu3TeO6 is a three-dimensional antiferromagnet without much frustration, consistent with a small frustration index of f = |ΘCW|/TN ≈ 2.9 in our sample, where ΘCW = −175 K is the Curie–Weiss temperature (Supplementary Fig. 2a). Therefore, we carry out the linear-spin-wave calculation to fit the experimental data. We find that a J1–J2 model with only NN and next-nearest-neighbour (NNN) exchange interactions cannot fit the data, given the apparent discrepancies especially on the optical branches (Supplementary Fig. 3a–f). We have added longer-range exchange interactions and found that at least up to sixth-NN (J6) can we fit the data satisfactorily. The necessity for using terms up to J6 may lie in the highly interconnected three-dimensional spin network and the large number of Cu2+ ions in the unit cell, such that differences between different exchange paths can be small. However, J1 is the only dominant term, which is compatible with the modest frustration of the system as there is no comparable interaction to compete with J1. The calculated spin-wave spectra using these parameters along [001], [101], and [111] directions are presented in Fig. 2d–f, respectively, and the corresponding dispersions are plotted on top of the experimental data in Fig. 2a–c.
The calculated magnetic excitation spectra capture most of the features in the experimental results, as shown in Fig. 2. We note that we can include more longer-range interactions to improve the fittings, mostly for the acoustic branches in the low-energy range where no band crossings occur. But given the present agreement between the theoretical and experimental results, we believe that our Hamiltonian up to J6 is appropriate, since the main purpose for the calculations is to guide our characterisations on the crossing points, which are in the high-energy range. The comparison between the calculated dispersions and experimental data assures that we have observed multiple nodal points along different trajectories in the Brillouin zone in the energy range of 15–18.5 meV. Again, we remind that these nodes are symmetry protected56. The presence of nodes along all these directions indicates that the associated nodal excitations are of three-dimensional nature, similar to those in the fermionic systems5,8. We first identify the four-fold degenerate Dirac nodes, at which two doubly degenerate magnon bands cross each other, for example, the Γ(Γ′) and P points.
In addition to the Dirac nodes predicted in ref. 56, we also observe some double-triply (triply degenerate, hereafter) nodal points at some high-symmetry positions, e.g., the H(H′) points in Fig. 2a, c. At the Γ point, there exist both Dirac and triply degenerate nodes very close in energy. In fact, the triply degenerate nodes are generically expected for a system with a PT plus some point-group symmetry, such as C3 (refs. 13,17,44,45), which is the case in Cu3TeO6 (refs. 56,57).
The existence of above-mentioned nodal points is guaranteed by the symmetry, independent of the Hamiltonian44,45,56. As a demonstration, we show the calculated results using a J1–J2 model in Supplementary Fig. 3a–c—given the apparent failure of this model in describing the experimental data, this model still gives Dirac nodes at P and triply degenerate nodes at H. This further strengthens our conclusion that the unprecedented magnon band structure with coexisting Dirac and triply-degenerate nodes has been discovered in Cu3TeO6. Since the Γ point hosts two types of nodes too close in energy to be resolved experimentally, we pick the P and H points for further elaborations.
Triply degenerate and Dirac nodes
In the dispersions shown in Fig. 2a, we observe two triply degenerate points at H at two energies of E ≈ 16 and 18.5 meV. We first perform a constant-energy (E) cut in the dispersions at an energy interval of ΔE = 18.5 ± 0.5 meV through the H point. The results are plotted in Fig. 3a, where it clearly shows a circle centring at the H point. A cut along the [001] direction through this point yields a peak exactly centring at the H point, as shown in Fig. 3c. Peaks at L = ±2 rlu correspond to H points in the next Brillouin zones. We have also analysed the triply degenerate point at the lower energy of E = 16 meV in Supplementary Fig. 5, which confirms our conclusion on the observation of two triply degenerate nodal points at H.
Results from similar practices for the P points in Fig. 2c at an energy interval of ΔE = 15 ± 0.5 meV are presented in Fig. 3b, from which we observe two Dirac nodes at the P points on top of the ring centring (−2, 0, 1), i.e., the H′ point. Two P and Γ points in other directions are also present in this constant-E contour. We perform a cut through the two P points along the [111] direction, and the results are shown in Fig. 3d, with two peaks centring at the P points.
We have also performed a series of constant-Q (wave-vector) cuts of the dispersions at the Q positions indicated in Fig. 4a, b through the H and P points, respectively. Results of these cuts are shown in Fig. 4c–e. From the linear cuts, we identify two energies around 15 and 18 meV corresponding to these points at q = 0 (Fig. 4c) and ∓0.5 (Fig. 4d, e), evidenced by the sharpest peaks at these Dirac and triply degenerate nodes. We also illustrate the linear dispersions near these nodes in Fig. 4c–e.
To further characterise the triply degenerate points at H, we perform simulations using the effective Hamiltonian derived from our J1, J2…J6 model (Eq. (1)). The results are plotted in Supplementary Fig. 6, which shows that, near each of the H points, there are two linear bands and one flat band. Thus, the magnons can be regarded as three-component bosons44,45, similar to the new fermions13,14,15,16. The two linear bands have a Chern number of 2 and −2, respectively, and the flat band has a Chern number of 0 (refs.13,14,15,22,44,45).
Discussions
By now, we have unambiguously demonstrated the coexistence of Dirac and triply degenerate magnons in Cu3TeO6, and so this material is the first topological system where both Dirac and triply degenerate nodal excitations are present, enabling the investigations into the possible interplay between them and other topological properties of the material. Due to the presence of the nontrivial Berry curvature in topological magnons, the anomalous thermal Hall transport resulting from the spin current is expected33,46,47,48,49,50,51. In Cu3TeO6, under an external magnetic field, a Dirac point should split into two Weyl points carrying a monopole charge of 1 and −1, respectively, which will give rise to the thermal Hall conductivity10,11. Furthermore, the two bands with a Chern number of ±2 crossing with the flat band at the triply degenerate H point are also expected to show a thermal Hall effect under an external magnetic field that opens a gap33. Another important feature of the topological magnons in Cu3TeO6 is the topologically-protected surface arc state56, which may be detected using surface-sensitive probes, such as high-resolution electron energy loss spectroscopy61, or helium atom energy loss spectroscopy62. Recent developments in optical measurements of the spin excitations via the magneto-optical effect may also be helpful63,64,65. Furthermore, spin current flowing on the surface may be directly measured53. Further explorations of these topological properties should lend support to developing spintronics with outstanding performance47,53,54,55. Finally, since the band topology does not rely on the constituent quasiparticles, both the electron and phonon bands of Cu3TeO6 may exhibit topological properties13,14, calling for future theoretical and experimental investigations.
After we finished this work, we became aware of a preprint reporting similar INS results66.
Methods
Single-crystal growth and characterisations
High-quality single crystals of Cu3TeO6 were grown using PbCl2 (4 N) as the flux, following the procedures in ref.59. X-ray diffraction data were collected in an x-ray diffractometer (X′TRA, ARL) using the Cu-Kα edge with a wave length of 1.54 Å. Rietveld refinements on the data were run in the Fullprof. suite. A single-crystal x-ray diffractometer was used to confirm the orientation of the single crystals. Susceptibility and heat capacity were measured in the physical property measurement system (PPMS-9T) from Quantum Design.
INS experiment
Our INS experiment was performed on wide angular-range chopper spectrometer (ARCS) at Spallation Neutron Source (SNS) of Oak Ridge National Laboratory (ORNL). For the experiment, we coaligned 40 pieces of single crystals weighing about 3 g in total using a backscattering Laue x-ray diffractometer. The single crystals glued on an aluminum plate with a sample mosaic of 1.5° were loaded into a closed-cycle refrigerator with the [010] direction aligned in the vertical direction. Data were collected by rotating the sample about the [010] axis with an incident energy Ei = 35 meV and a chopper frequency of 300 Hz resulting in an energy resolution of about 1.4 meV. We collected data at various temperatures. At 5 K, the data were collected by rotating the sample by 90° in a 1.25° step. For other high temperatures, data were collected with a 5° step. We used DAVE67 to analyse the data. The wave vector Q was expressed as Q = (2π/a, 2π/b, 2π/c) reciprocal lattice unit (rlu) with a = b = c = 9.537(3) Å. Data in Fig. 2a–c were obtained by integrating the experimental data along two other orthogonal directions, with a thickness of [H, 0, 0] = [−3.2, −2.8], [0, K, 0] = [−0.2, 0.2]; [−L, 0, L] = [0.8, 1.2], [0, K, 0] = [−0.2, 0.2]; and [−L, 0, L] = [1.3, 1.7], [−K, 2K, −K] = [0.1, 0.2], respectively. Data in Fig. 3a,b were integrated over [H, 0, 0] = [−3.2, −2.8] and [−L, 0, L] = [1.3, 1.7], respectively.
Linear-spin-wave theory
In order to fit the experimental data, we used the Heisenberg model involving exchange interactions up to the sixth nearest neighbour (NN),
where n-NN indicates the nth NN bond and Jn is the magnitude of the nth NN Heisenberg term. Since this material is a collinear antiferromagnet, we performed the calculations with the linear-spin-wave theory. After performing standard Holstein–Primakoff transformation and diagonalizing the quadric Hamiltonian, we obtained the magnon dispersions.
To compare with the experimental data, we calculated the neutron scattering cross section
where Qα = x,y,z is the α component of Q and the Sαβ(Q, E) is the spin–spin correlation function defined by
Here, Si is the effective spin at site i with the coordinate ri.
Data availability
Data supporting the findings of this study are available from the corresponding author J.S.W. (Email: jwen@nju.edu.cn) upon reasonable request.
References
Hasan, M. Z. & Kane, C. L. Colloquium: topological insulators. Rev. Mod. Phys. 82, 3045–3067 (2010).
Qi, X.-L. & Zhang, S.-C. Topological insulators and superconductors. Rev. Mod. Phys. 83, 1057–1110 (2011).
Young, S. M. et al. Dirac semimetal in three dimensions. Phys. Rev. Lett. 108, 140405 (2012).
Wang, Z. et al. Dirac semimetal and topological phase transitions in A3Bi (A = Na, K, Rb). Phys. Rev. B 85, 195320 (2012).
Liu, Z. K. et al. Discovery of a three-dimensional topological Dirac semimetal, Na3Bi. Science 343, 864–867 (2014).
Liu, Z. K. et al. A stable three-dimensional topological Dirac semimetal Cd3As2. Nat. Mater. 13, 677–681 (2014).
Wan, X., Turner, A. M., Vishwanath, A. & Savrasov, S. Y. Topological semimetal and Fermi-arc surface states in the electronic structure of pyrochlore iridates. Phys. Rev. B 83, 205101 (2011).
Xu, S.-Y. et al. Discovery of a Weyl fermion semimetal and topological Fermi arcs. Science 349, 613–617 (2015).
Lv, B. Q. et al. Observation of Weyl nodes in TaAs. Nat. Phys. 11, 724–727 (2015).
Wehling, T., Black-Schaffer, A. M. & Balatsky, A. V. Dirac materials. Adv. Phys. 63, 1–76 (2014).
Bansil, A., Lin, H. & Das, T. Colloquium: topological band theory. Rev. Mod. Phys. 88, 021004 (2016).
Zhu, Z., Winkler, G. W., Wu, Q., Li, J. & Soluyanov, A. A. Triple point topological metals. Phys. Rev. X 6, 031003 (2016).
Bradlyn, B. et al. Beyond Dirac and Weyl fermions: unconventional quasiparticles in conventional crystals. Science 353, aaf5037 (2016).
Bradlyn, B. et al. Topological quantum chemistry. Nature 547, 298–305 (2017).
Tang, P., Zhou, Q. & Zhang, S.-C. Multiple types of topological fermions in transition metal silicides. Phys. Rev. Lett. 119, 206402 (2017).
Ma, J. Z. et al. Three-component fermions with surface Fermi arcs in tungsten carbide. Nat. Phys. 14, 349–354 (2018).
Lv, B. Q. et al. Observation of three-component fermions in the topological semimetal molybdenum phosphide. Nature 546, 627–631 (2017).
Strohm, C., Rikken, G. L. J. A. & Wyder, P. Phenomenological evidence for the phonon Hall effect. Phys. Rev. Lett. 95, 155901 (2005).
Stenull, O., Kane, C. L. & Lubensky, T. C. Topological phonons and Weyl lines in three dimensions. Phys. Rev. Lett. 117, 068001 (2016).
Serra-Garcia, M. et al. Observation of a phononic quadrupole topological insulator. Nature 555, 342 (2018).
Peterson, C. W., Benalcazar, W. A., Hughes, T. L. & Bahl, G. A quantized microwave quadrupole insulator with topologically protected corner states. Nature 555, 346 (2018).
Zhang, T. et al. Double-Weyl phonons in transition-metal monosilicides. Phys. Rev. Lett. 120, 016401 (2018).
Lu, L., Joannopoulos, J. D. & Soljacic, M. Topological photonics. Nat. Photon. 8, 821–829 (2014).
Lu, L. et al. Experimental observation of Weyl points. Science 349, 622–624 (2015).
Zilberberg, O. et al. Photonic topological boundary pumping as a probe of 4D quantum Hall physics. Nature 553, 59 (2018).
Zhou, H. et al. Observation of bulk Fermi arc and polarization half charge from paired exceptional points. Science 359, 1009–1012 (2018).
Yang, B. et al. Ideal Weyl points and helicoid surface states in artificial photonic crystal structures. Science 359, 1013–1016 (2018).
Harari, G. et al. Topological insulator laser: theory. Science 359, eaar4003 (2018).
Bandres, M. A. et al. Topological insulator laser: experiments. Science 359, eaar4005 (2018).
Zhang, L., Ren, J., Wang, J.-S. & Li, B. Topological magnon insulator in insulating ferromagnet. Phys. Rev. B 87, 144101 (2013).
Chisnell, R. et al. Topological magnon bands in a Kagome lattice ferromagnet. Phys. Rev. Lett. 115, 147201 (2015).
Mook, A., Henk, J. & Mertig, I. Edge states in topological magnon insulators. Phys. Rev. B 90, 024412 (2014).
Romhnyi, J., Penc, K. & Ganesh, R. Hall effect of triplons in a dimerized quantum magnet. Nat. Commun. 6, 6805 (2015).
McClarty, P. A. et al. Topological triplon modes and bound states in a Shastry–Sutherland magnet. Nat. Phys. 13, 736 (2017).
Fransson, J., Black-Schaffer, A. M. & Balatsky, A. V. Magnon Dirac materials. Phys. Rev. B 94, 075401 (2016).
Okuma, N. Magnon spin-momentum locking: various spin vortices and Dirac magnons in noncollinear antiferromagnets. Phys. Rev. Lett. 119, 107205 (2017).
Owerre, S. A. Magnonic analogs of topological Dirac semimetals. J. Phys. Commun. 1, 025007 (2017).
Pershoguba, S. S. et al. Dirac magnons in honeycomb ferromagnets. Phys. Rev. X 8, 011010 (2018).
Mena, M. et al. Spin-wave spectrum of the quantum ferromagnet on the pyrochlore lattice Lu2V2O7. Phys. Rev. Lett. 113, 047202 (2014).
Li, F.-Y. et al. Weyl magnons in breathing pyrochlore antiferromagnets. Nat. Commun. 7, 12691 (2016).
Mook, A., Henk, J. & Mertig, I. Tunable magnon Weyl points in ferromagnetic pyrochlores. Phys. Rev. Lett. 117, 157204 (2016).
Su, Y., Wang, X. S. & Wang, X. R. Magnonic Weyl semimetal and chiral anomaly in pyrochlore ferromagnets. Phys. Rev. B 95, 224403 (2017).
Ross, K. A., Savary, L., Gaulin, B. D. & Balents, L. Quantum excitations in quantum spin ice. Phys. Rev. X 1, 021002 (2011).
Owerre, S. A. Weyl magnons in noncoplanar stacked kagome antiferromagnets. Phys. Rev. B 97, 094412 (2018).
Owerre, S. A. Magnonic triply-degenerate nodal points. Eur. Phys. Lett. 120, 57002 (2017).
Katsura, H., Nagaosa, N. & Lee, P. A. Theory of the thermal Hall effect in quantum magnets. Phys. Rev. Lett. 104, 066403 (2010).
Onose, Y. et al. Observation of the magnon Hall effect. Science 329, 297–299 (2010).
Matsumoto, R. & Murakami, S. Theoretical prediction of a rotating magnon wave packet in ferromagnets. Phys. Rev. Lett. 106, 197202 (2011).
Ideue, T. et al. Effect of lattice geometry on magnon Hall effect in ferromagnetic insulators. Phys. Rev. B 85, 134411 (2012).
Zhang, L. Berry curvature and various thermal Hall effects. New J. Phys. 18, 103039 (2016).
Hirschberger, M., Chisnell, R., Lee, Y. S. & Ong, N. P. Thermal Hall effect of spin excitations in a Kagome magnet. Phys. Rev. Lett. 115, 106603 (2015).
Shindou, R., Matsumoto, R., Murakami, S. & Ohe, J.-i Topological chiral magnonic edge mode in a magnonic crystal. Phys. Rev. B 87, 174427 (2013).
Rückriegel, A., Brataas, A. & Duine, R. A. Bulk and edge spin transport in topological magnon insulators. Phys. Rev. B 97, 081106 (2018).
Baltz, V. et al. Antiferromagnetic spintronics. Rev. Mod. Phys. 90, 015005 (2018).
Chumak, A., Vasyuchka, V., Serga, A. & Hillebrands, B. Magnon spintronics. Nat. Phys. 11, 453–461 (2015).
Li, K., Li, C., Hu, J., Li, Y. & Fang, C. Dirac and nodal line magnons in three-dimensional antiferromagnets. Phys. Rev. Lett. 119, 247202 (2017).
Herak, M. et al. Novel spin lattice in Cu3TeO6: an antiferromagnetic order and domain dynamics. J. Phys. Condens. Matter 17, 7667 (2005).
Månsson, M. et al. Magnetic order and transitions in the spin-web compound Cu3TeO6. Phys. Procedia 30, 142–145 (2012).
He, Z. & Itoh, M. Magnetic behaviors of Cu3TeO6 with multiple spin lattices. J. Magn. Magn. Mater. 354, 146–150 (2014).
Norman, M. Copper tellurium oxides - a playground for magnetism. J. Magn. Magn. Mater. 452, 507–511 (2018).
Zhu, X. et al. High resolution electron energy loss spectroscopy with two-dimensional energy and momentum mapping. Rev. Sci. Instrum. 86, 083902 (2015).
Harten, U. & Toennies, J. P. Surface phonons on GaAs(110) measured by inelastic helium atom scattering. Eur. Phys. Lett. 4, 833 (1987).
van Kampen, M. et al. All-optical probe of coherent spin waves. Phys. Rev. Lett. 88, 227201 (2002).
Shen, K. & Bauer, G. E. W. Laser-induced spatiotemporal dynamics of magnetic films. Phys. Rev. Lett. 115, 197201 (2015).
Hashimoto, Y. et al. All-optical observation and reconstruction of spin wave dispersion. Nat. Commun. 8, 15859 (2017).
Yao, W. et al. Topological spin excitations observed in a three-dimensional antiferromagnet. Preprint at https://arxiv.org/abs/1711.00632 (2017).
Azuah, R. T. et al. DAVE: a comprehensive software suite for the reduction, visualization, and analysis of low energy neutron spectroscopic data. J. Res. NIST 114, 341 (2009).
Acknowledgements
Work at Nanjing University was supported by National Natural Science Foundation of China with Grant Nos. 11674157, 11774152, 11374138, 11674158 and 11525417, National Key Projects for Research & Development of the Ministry of Science and Technology of China with Grant No. 2016YFA0300401, and Fundamental Research Funds for the Central Universities with Grant No. 020414380105. The research at Oak Ridge National Laboratory’s Spallation Neutron Source was sponsored by the US Department of Energy, office of Basic Energy Sciences, Scientific User Facilities Division. We thank Jian Sun, S. A. Owerre, Yuan Li, and Ka Shen for stimulating discussions.
Author information
Authors and Affiliations
Contributions
J. S. W. and J. -X. L. conceived the project. S. B. grew the crystals. S. B. and Z. M. carried out the neutron scattering experiments with help from D. L. A. W. W., S. -L. Y., D. W. and X. G. W. performed the theoretical calculations. S. B., J. H. W., Z. W. C. and J. S. W. analysed the data. J. S. W., J. -X. L. and S. B. wrote the paper with inputs from all authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Bao, S., Wang, J., Wang, W. et al. Discovery of coexisting Dirac and triply degenerate magnons in a three-dimensional antiferromagnet. Nat Commun 9, 2591 (2018). https://doi.org/10.1038/s41467-018-05054-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-05054-2
- Springer Nature Limited
This article is cited by
-
Dipolar spin-waves and tunable band gap at the Dirac points in the 2D magnet ErBr3
Communications Physics (2022)
-
Order-by-disorder from bond-dependent exchange and intensity signature of nodal quasiparticles in a honeycomb cobaltate
Nature Communications (2021)
-
Acoustic spin-1 Weyl semimetal
Science China Physics, Mechanics & Astronomy (2020)