Abstract
Magnetic topological insulators (MTIs) offer a combination of topologically nontrivial characteristics and magnetic order and show promise in terms of potentially interesting physical phenomena such as the quantum anomalous Hall (QAH) effect and topological axion insulating states. However, the understanding of their properties and potential applications have been limited due to a lack of suitable candidates for MTIs. Here, we grow two-dimensional single crystals of Mn(SbxBi(1-x))2Te4 bulk and exfoliate them into thin flakes in order to search for intrinsic MTIs. We perform angle-resolved photoemission spectroscopy, low-temperature transport measurements, and first-principles calculations to investigate the band structure, transport properties, and magnetism of this family of materials, as well as the evolution of their topological properties. We find that there exists an optimized MTI zone in the Mn(SbxBi(1-x))2Te4 phase diagram, which could possibly host a high-temperature QAH phase, offering a promising avenue for new device applications.
Similar content being viewed by others
Introduction
Recently, research on topological phases has created a surge of interest and some fruitful outcomes for condensed matter physics and material science. Different combinations of topology and magnetism reveal more interesting topological phases, in which various quasiparticles with or without counterpart particles in the universe can be simulated in condensed matter; for example, quantum anomalous Hall states, topological superconducting states, topological axion insulating states, and Weyl semimetallic states1,2,3,4,5,6,7,8,9,10,11,12. Despite intense efforts, this research is still in its early stages due to obstacles in the material platforms. In particular, magnetic topological insulators (MTIs), which are expected to reveal both quantum anomalous Hall effects (QAHEs) and topological axion insulating states, are extremely rare. Previous efforts have been made to study the doping of magnetic impurities in topological materials or the proximity effect in magnetic heterostructures of topological materials and magnetic insulators13,14,15,16,17,18,19,20,21, in which the magnetic effect is weak. Generally, increased levels of dopants may increase the exchange field but can reduce sample quality and decrease electronic mobility22,23,24,25,26,27,28,29. Therefore, most exotic topological quantum states including QAHE are either only observable at extremely low temperatures or have yet to be observed experimentally13,16,27. These drawbacks have dragged behind the pace of development of these materials for practical applications. Hence it is a key priority to search for more intrinsic MTIs, with less stringent requirements for the quantum effects mentioned above. The recently discovered MnBi2Te4 is found to be a possible intrinsic MTI with spontaneous antiferromagnetic (AFM) magnetization30,31,32. Theoretical calculations show that QAHE states may arise in MnBi2Te4 thin film and that the QAHE gap is almost 50–80 meV, which is much larger than that of magnetically doped topological insulators30,33, pointing to the possibility that QAHE could be observed at elevated temperatures. MnBi2Te4 also offers a promising platform for topological axion insulators and Weyl semimetals30,31. However, according to recent reports of angle-resolved photoemission spectroscopy (ARPES)34,35,36,37,38, synthesized crystals of MnBi2Te4 always show heavy n-type doping, and the Fermi level lies in the bulk conduction bands34,35,36,37,38. Thus, for undoped MnBi2Te4 with bulk carrier dominated transport, there is less likely to be evidence of exotic magnetic topological properties, including QAHE.
In this work, we grow a serial single crystals of the Mn(SbxBi(1 − x))2Te4 family, and search for intrinsic MTIs in this family. By combining ARPES, low-temperature transport measurements, and first-principles calculations, we reveal several physical transitional processes, including n–p carrier transition, magnetic transition, and topological phase transition in this family of materials. We reveal that the Fermi level of Mn(SbxBi(1 − x))2Te4 can be tuned from the conduction bands to the valence bands by adjusting the atomic ratio x. Specifically, for bulk crystals, the Fermi level lies near the bulk gap when x ~ 0.3, the sample with x ~ 0.3 displays the highest resistivity, and an n–p carrier transition occurs near this atomic ratio. For thin-film devices, less substitution of antimony, with x ~ 0.1, is required because chemical potential shifting occurs during device fabrication. Theoretical calculations reveal that the inverted bandgap in Mn(SbxBi(1 − x))2Te4 holds when x < 0.55. We find an optimized zone in the Mn(SbxBi(1 − x))2Te4 phase diagram, thereby achieving an intrinsic MTI combining topological non-triviality, spontaneous magnetization, and bulk carrier suppression. This provides an ideal platform for the realization of novel topological phases such as high-temperature QAHE and topological axion states.
Results
Topological nontrivial states in the crystals at x = 0
We investigate the whole family of Mn(SbxBi(1 − x))2Te4 materials, starting from crystals with x = 0. They have a layered rhombohedral crystal structure with the space group \(R\overline 3 m\)39, composed of stacking septuple layers (SLs) Te–X–Te–Mn–Te–X–Te (X = Bi/Sb) as displayed in Fig. 1a. The magnetic moments of each manganese atom in a SL are in parallel with each other and form a ferromagnetic (FM) order with the out-of-plane easy axis, while the magnetizations of the neighboring SLs are the opposite, forming an AFM order34,35. Single crystals of MnBi2Te4 are grown using the flux method. Plate-like single crystals with sizes larger than 5 × 5 mm2 are obtained, which can easily be exfoliated mechanically along the c axis. The cleavage surfaces are flat and shiny, and suitable for ARPES measurements.
We conduct ARPES measurements on the x = 0 samples. Figure 1b shows the ARPES intensity plot around the center of the Brillouin zone, with a photon energy of 7.25 eV at 8 K. In this plot, one can see the parabolic bulk conduction band (BCB) and valence band (BVB), of which the dispersions are broadened and unclear due to bulk projections (marked by the orange arrows). In addition, a clearer Dirac-cone-like feature with linear dispersions can also be seen in the bulk bandgap (marked by the red arrows), with a crossing point at k∥ = 0 and a binding energy of −0.27 eV, which can be identified as the topological surface states (TSSs). Considering the range of the Dirac-cone-like dispersions, as shown in the magnified view in Fig. 1c and the corresponding constant energy contours in Fig. 1d, the isotropic circular Dirac-cone shaped dispersion formed by the two linear TSS bands can be seen more clearly. Although an exchange gap should open at the Dirac point30,31,33, we note that the linear dispersion of these two bands seems well maintained at the crossing point and no observable gap opening feature can be observed. According to the momentum distribution curves (MDCs) displayed in Fig. 1e, there is still a finite spectral weight near the Dirac point (bold line), and the intensity of the energy distribution curve (EDC) near the Dirac point changes almost linearly with no obvious ‘U’ shaped gap opening features in Fig. 1f. Considering the resolution limit of our ARPES, we believe that the gap opening size in real synthesized MnBi2Te4 crystals is much smaller (<25 meV) than calculations (~80 meV)33 and cannot be identified by our ARPES measurements, the smaller value being consistent with the transport measurements40. The difference between the theoretical calculations and experimental measurements possibly comes from the complex magnetic moment distributions at the surface of the MnBi2Te4 crystals, where the moments may not be arranged strictly like the A-type AFM order in the bulk. In order to identify further characteristics of bulk band dispersions, we also perform ARPES measurements under various photon energies. We note that the band dispersions of the crystal vary dramatically under different photon energies. Clear surface states can only be detected under low photon energies. When increasing the photon energy, ARPES signals are dominated by the bulk contributions (Fig. 1g). One possible reason for this is the difference between photoemission matrix elements for surface states and bulk states.
Tuning the n–p carrier compensation by increasing x
In the data presented above, we note that the position of the Fermi level of MnBi2Te4 is far from the bulk gap. This is because heavy n-type doping is induced during crystal synthesis, and the Fermi level lies in the bulk conduction band. Such an unintentional doping effect also occurs in the samples grown by molecular beam epitaxy and the melting method35,36,37, preventing the material (x = 0) from being an ideal MTI for QAHE measurements. Encouraged by some previous successes41,42,43,44,45, we investigate the whole family of Mn(SbxBi(1 − x))2Te4 by increasing the value of x in the search for the ideal bulk-insulating MTI. Shiny plate-like Mn(SbxBi(1 − x))2Te4 crystals could still be obtained following a similar growth process (inset of Fig. 2a). The X-ray diffraction (XRD) patterns for single crystals with corresponding x value are shown in Fig. 2a. The positions of the (00n) diffraction peaks reveal the c axis of ~ 41 Å in all four samples, consistent with the crystals with x = 0. Figure 2b displays the energy dispersive spectra (EDS) for samples with different amounts of antimony substitution. The ratio of Mn:(Bi + Sb):Te is nearly 1:2:4, indicating a stoichiometric atomic ratio of Mn(SbxBi(1 − x))2Te4. After normalizing each EDS curve by the amplitude of the peaks from the tellurium, the intensity of the bismuth and antimony peaks clearly evolves as expected, indicating the successful control of the atomic ratio of these two elements.
In order to identify the Fermi levels of the different samples in the Mn(SbxBi(1 − x))2Te4 family, we perform ARPES measurements on samples with different antimony ratios. We note that the signals of the antimony-substituted samples are less clear when the photon energy is lower than 10 eV, and following extensive measurements, we choose hv = 14 eV for the detections. Even though the ARPES signals at this photon energy are dominated by the bulk contributions, this is sufficient for verifying the evolution of the shifting chemical potential in the different samples. Figures 2c-f show the dispersions detected on the cleaved surface of Mn(SbxBi(1-x))2Te4 for x from 0 to 0.4. The offset of the Fermi level in the different samples is significant. At x = 0, the band gap is below the Fermi level at the binding energy of approximately −200 meV, illustrating heavy n-type doping (Fig. 2c). In the sample for x = 0.2, the bulk conduction band is still observable in Fig. 2d but the Fermi level is much closer to the band gap than the one shown in Fig. 2c. By increasing the Sb substitution ratio slightly to x = 0.3, a dramatic shift in Fermi level is observed (Fig. 2e). The Fermi level of the samples with x = 0.3 lies near the edge of the valence band. The sudden change in Fermi level may be caused by the low carrier density near the bulk gap, and the introduction of a small amount of carrier has a dramatic effect on the chemical potential. When the Sb ratio is increased further to x = 0.4, the Fermi level continuously penetrates deep into the valence band, as expected (Fig. 2f). Substituting antimony for bismuth gives rise to the monotonic shifting of the Fermi level from the conduction band to the valence band, indicating an n–p carrier transition in the vicinity of x ~ 0.3.
In order to confirm the n–p carrier evolution further, we measure the transport properties of these four samples (bulk crystals with thicknesses of 50–200 μm) at low temperatures. The Hall resistivities ρxy as a function of the magnetic field B of samples with different substituting ratios when the temperature is higher and lower than TN are shown in Fig. 2g, h, respectively. The slope of ρxy changes signs from negative to positive when x increases from 0.25 to 0.3, confirming the n–p transition for the changing Sb ratio, which is consistent with the ARPES measurements. One can further extract the carrier density of each sample by RH = 1/ne, where RH is the Hall coefficient. Figure 2i displays the calculated carrier density of each sample extracted from Fig. 2h. The carrier density in the sample with x = 0.3 is 1.85 × 1018 cm−3, which is almost 40 times lower than the values for the x = 0 sample (7.05 × 1019 cm−3), indicating a successful suppression of the bulk carriers by controlling the Sb:Bi ratio in Mn(SbxBi(1-x))2Te4. Bulk carrier suppression can also be identified from the curves of resistivity against temperature for samples with different values of x (Fig. 2j). The resistivity of the sample with x = 0.3 is highest among all five samples over the whole temperature ranging from 2 to 300 K. In addition, most of the samples show metallic behavior except for the sample of x = 0.3, in which the resistivity increases when cooling near 200 K. This increase in resistivity could possibly originate from bulk carrier suppression by fine tuning the ratio of antimony substitution. It may also be a spin-related feature that emerges when the bulk metallic behavior is suppressed, given that considerable spin fluctuation in MnBi2Te4 is reported even at room temperature36, and the resistivity could be affected. It is reasonable to suppose that there is an electrical neutral point for minimum bulk conductivity contributions, which can be achieved between x = 0.25 and 0.35 when the Fermi level aligns with the QAHE gap.
Magnetism in bulk crystals and thin film devices
Apart from bulk carrier suppression, another precondition for QAHE is spontaneous magnetization, thus it is necessary to investigate systematically the magnetism of this material family. We use a vibrating sample magnetometer to measure the magnetization of bulk crystals with different values of x. Figure 3a shows the field-cooled (FC) and zero-field-cooled (ZFC) curves of four samples for x = 0 to 0.5. The FC and ZFC curves of each sample perfectly overlap with each other and a peak near 25 K can be identified, indicating an AFM transition in all four samples from x = 0 to 0.5. In the curves of magnetization versus B field displayed in Fig. 3b and the transport magnetoresistances (Fig. 3c) of the samples with different x values (as well as in ρxy discussed above in Fig. 2g), two types of “kink” feature (marked by the arrows and triangles in Fig. 3b, c, respectively) can be identified near B = 3T and 7T in all four samples. This can be explained by an AFM to canted-AFM (CAFM) transition (Hc1 ~ 3T) and a CAFM to FM transition (Hc2 ~ 7T) caused by the external magnetic field36. One further phenomenon of interest is that when increasing the magnetic field, the magnetoresistance of the sample with x = 0.25 jumps upwards at the first kink near Hc1 ~ 3T, as shown in Fig. 3c, which is the opposite of the case for the other three samples. The reasons for this are worthy of further study and may be attributable to the different magnetic coupling mechanisms between the sample with strong metallic behavior and that with the Fermi level near the band gap46,47,48. Figure 3d summarizes the results of Néel temperature extracted from the magnetization data in Fig. 3a and the corresponding critical field for the kink (Hc1, Hc2) in Fig. 3b, c. Both TN and the critical field decrease with increasing x, indicating the weaker AFM coupling in samples with higher x. However, the increase in antimony does not much affect the order of AFM because TN only decreases by 2.6 K in the sample for x = 0.5 compared with the one for x = 0. We therefore believe that there is no magnetic transition from AFM to paramagnetism and the spontaneous magnetization is maintained in Mn(SbxBi1 − x)2Te4 within the range of x < 0.5. In fact, spontaneous AFM order still maintains when x = 1, i. e. in pure MnSb2Te449.
The synthesized Mn(SbxBi(1 − x))2Te4 crystals can also be mechanically exfoliated into thin films. The thickness of the thin films is identified by an atomic force microscope (Fig. 4a, b), followed by a standard electron beam lithography process to fabricate the mesoscopic devices (Fig. 4c). Figure 4d shows a high resolution transmission electron microscopy (HR-TEM) photograph and the fast Fourier transformation (FFT) pattern collected on the exfoliated (001) surface of a typical thin film, in which the hexagonal atomic fringes from the (110) lattice plane with a spacing of 0.217 nm are clearly shown, indicating the high quality of the exfoliated thin film crystals. During the transport measurement, we are surprised to discover that the fabrication process of the thin-film device causes the Fermi level to shift downwards. In other words, the Fermi level of thin films is closer to the Dirac point than bulk crystals for n-type samples. Thus, the optimized x value for thin devices is < 0.3. After a large number of measurements, we find that x ~ 0.1 is a more appropriate substitution ratio for thin-film devices (Supplementary Fig. 1). Due to the A-type antiferromagnetism in Mn(SbxBi(1 − x))2Te4, the magnetizations of neighboring SLs are opposite, and there should be oscillations in magnetic properties between thin films with even and odd SLs. Figure 4e displays the Hall resistances of several devices with x = 0.1 with different thicknesses. Each curve is measured at 2 K under a certain back gate voltage (Vg) to reach the maximum longitudinal resistance of the corresponding device. One can see that the devices with odd SLs (5, 7, 9 SLs) show obvious AHE with a coercive field around 0.5 to 1T. Although hysteresis loops can also be observed in samples with even SLs (6, 8 SLs), the coercive fields of these samples are much smaller than the ones with odd SLs and the remnant magnetic signals are believed to result from the canting or disorder of the AFM configurations.35 Since the Fermi level is close to the charge neutral point, the reversal of AHE signals in Fig. 4e may come from competition between the intrinsic Berry curvature and Dirac-gap enhanced extrinsic skew scattering in this material.50 Figure 4f summarizes the coercive fields for devices with different thicknesses, and the expected oscillation between even and odd SLs is clearly demonstrated.
The phase diagram of the multiple transition processes
As shown above, the bulk carrier contributions of the Mn(SbxBi(1 − x))2Te4 family can be suppressed and the crystals have similar antiferromagnetic interlayer coupling. However, special attention should be focused on the fact that a higher value of x reduces the strength of the spin orbital coupling (SOC) of the materials, which is the origin of the topological transition and the band inversion.
To verify our observations, we calculate the band structures of Mn(SbxBi(1 − x))2Te4 using first-principles calculations. Figures 5a–d display the band calculations along with the evolution of the Wannier charge centers (WCCs) in MnBi2Te4 (x = 0) and MnSb2Te4 (x = 1) respectively. According to our calculations, MnBi2Te4 is an intrinsic MTI with an inverted bulk band gap of ~ 0.2 eV, while MnSb2Te4 is a topologically trivial magnetic insulator with a bulk band gap of 34 meV, indicating a topological phase transition in Mn(SbxBi(1 − x))2Te4 when the amount of antimony is increased. Figure 5e shows its phase diagram with the topological phase transition, as well as the n–p carrier transition. The purple curves indicate the calculated bulk bandgap in Mn(SbxBi(1 − x))2Te4. The closing and reopening of the bandgap clearly show that the topological transition point lies at x = 0.55, which exceeds the value of x = 0 to 0.5 in our samples as discussed above. Therefore, our calculations support the fact that the topologically nontrivial characteristics are maintained in the samples considered in this work. For bulk crystals in particular, the electrical neutral point is close to x ~ 0.3, while a lower amount of Sb substitution with x ~ 0.1 is appropriate in thin-film devices due to the unexpected shift in Fermi level. A peak in the bandgap curve at around x = 0.9 can also be observed and we believe this originates from the competition between the SOC effect and the chemical bonding effect (Supplementary Fig. 2).
Discussion
The three basic requirements for the realization of QAHE, i.e., topological non-triviality, spontaneous magnetization, and bulk carrier suppression, are all satisfied in the sample of Mn(SbxBi(1 − x))2Te4 with the optimized substitution ratio x both in bulk crystals and thin films (shown by the dashed ellipse in Fig. 5e), promising an ideal platform for the realization of high-temperature QAHE and other predicted topological effects. In addition, Mn(SbxBi(1 − x))2Te4 is a material family hosting rich physical phenomena, including topological phase transition, metallic-insulating transition, n–p type carrier transition, and different magnetisms including AFM, CAFM, and FM. With such potentially physical properties in mind, we believe that this material family is worthy of further study and could offer a wide range of potential applications in the future.
Methods
Crystal growth
High quality single crystals are synthesized using the flux method. For the crystal with x = 0, raw materials of MnTe and Bi2Te3 are mixed in the molar ratio of 1:5.85 in an alumina crucible, which need to be sealed inside a quartz ampule. The ampule is placed in a furnace and heated to 950 °C over a period of one day. After maintaining it at 950 °C for 12 h, the ampule is cooled to 580 °C at a rate of 10 °C/h. Large-sized MnBi2Te4 crystals are obtained after centrifuging in order to remove the excess Bi2Te3 flux. For other crystals with different values of x, different amounts of Sb2Te3 are used to substitute for Bi2Te3. The growth process is similar but the temperatures for centrifugation differ slightly depending on the ratio of Sb:Bi used. It is noteworthy that the melting temperatures of MnBi2Te4 and Bi2Te3 are very close. The actual temperatures of each furnace require careful monitoring and calibration before growth. During the centrifugation, there is a requirement to take the ampule out of the furnace and place it into the centrifuge as soon as possible (normally < 5 s afterwards) because the temperature of the mixture drops fast in an ambient environment.
ARPES measurements
ARPES experiments are performed at the BL13U beamline at the Hefei National Synchrotron Radiation Laboratory, and the BL03U beamline at the Shanghai Synchrotron Radiation Facility. Photon energies ranging from 7 to 30 eV are applied in the experiments. The samples are cleaved and measured in an ultrahigh-vacuum chamber at a pressure below 10−10 Torr.
Transport measurements on bulk crystals
The electrical resistivity is measured using a physical property measurement system. (Quantum Design PPMS-14T). The lowest temperature and highest magnetic field are 2 K and 14 T, respectively. The samples used here are plate-like bulk crystals with thicknesses of 50–200 μm and are cleaved by a knife, and the sizes of these plates are 0.5–2 mm. Standard hall-bar contacts are fabricated using silver paste or indium pressing on the cleaved sample surface.
Magnetic measurements
A vibrating sample magnetometer equipped in a physical property measurement system (Quantum Design) is used to measure the magnetization of bulk crystals. The measured crystals are about 0.5–1 mm in thickness and 2–3 mm in side length. Standard copper sample holders are used during the measurement. The lowest temperature and highest magnetic field are 2 K and 9 T, respectively.
Thin device fabrication
Thin films of Mn(SbxBi(1 − x))2Te4 samples are obtained by mechanical exfoliation using scotch-tapes. Silicon wafers with 300 nm silica layers are used as the substrates. An atomic force microscope is used first to determine the film thickness, and thin films with uniform thickness and appropriate size (normally 5–30 μm in length and 3–20 μm in width) are chosen for the next step of device fabrication. Electron beam lithography is used to fabricate Hall-bar electrodes on the thin films.
First-principles calculations
First-principles calculations are performed by the Vienna Ab-initio Simulation Package51 with the local density approximation (LDA) + U functional. Parameters U = 3 eV and J = 0 eV are used for Mn d orbitals. The virtual crystal approximation52 is used for Mn(SbxBi(1 − x))2Te4. A cut-off energy of 450 eV and 8 × 8 × 8 k-points are adopted for self-consistent calculation. Experimental lattice constants are fixed and inner atoms in the unit cell are fully relaxed with a total energy tolerance of 10−5 eV. The spin-orbit coupling is self-consistently included. Maximally localized Wannier functions53 are used to calculate the surface states.
Data availability
The datasets that support the findings of this study are available from the corresponding author upon reasonable request.
References
Yu, R. et al. Quantized anomalous Hall effect in magnetic topological insulators. Science 329, 61–64 (2010).
Nomura, K. & Nagaosa, N. Surface-quantized anomalous Hall current and the magnetoelectric effect in magnetically disordered topological insulators. Phys. Rev. Lett. 106, 166802 (2011).
He, K., Wang, Y. & Xue, Q.-K. Quantum anomalous Hall effect. Natl. Sci. Rev. 1, 38–48 (2013).
Liu, C.-X., Zhang, S.-C. & Qi, X.-L. The quantum anomalous Hall effect: theory and experiment. Annu. Rev. Condens. Matter Phys. 7, 301–321 (2016).
Wang, J., Lian, B. & Zhang, S.-C. Quantum anomalous Hall effect in magnetic topological insulators. Phys. Scr. T164, 014003 (2015).
Liu, Q. et al. Magnetic impurities on the surface of a topological insulator. Phys. Rev. Lett. 102, 156603 (2009).
Qi, X.-L. et al. Inducing a magnetic monopole with topological surface states. Science 323, 1184–1187 (2009).
Li, R. et al. Dynamical axion field in topological magnetic insulators. Nat. Phys. 6, 284 (2010).
Wan, X. et al. Topological semimetal and Fermi-arc surface states in the electronic structure of pyrochlore iridates. Phys. Rev. B 83, 205101 (2011).
Lv, B. Q. et al. Experimental discovery of Weyl semimetal TaAs. Phys. Rev. X 5, 031013 (2015).
Xu, S.-Y. et al. Discovery of a Weyl fermion semimetal and topological Fermi arcs. Science 349, 613–617 (2015).
Ruan, J. et al. Symmetry-protected ideal Weyl semimetal in HgTe-class materials. Nat. Commun. 7, 11136 (2016).
Chang, C.-Z. et al. Experimental observation of the quantum anomalous Hall effect in a magnetic topological insulator. Science 340, 167–170 (2013).
Luo, W. & Qi, X.-L. Massive Dirac surface states in topological insulator/magnetic insulator heterostructures. Phys. Rev. B 87, 085431 (2013).
Jiang, H. et al. Quantum anomalous Hall effect with tunable chern number in magnetic topological insulator film. Phys. Rev. B 85, 045445 (2012).
Chang, C.-Z. et al. High-precision realization of robust quantum anomalous Hall state in a hard ferromagnetic topological insulator. Nat. Mater. 14, 473 (2015).
Vobornik, I. et al. Magnetic proximity effect as a pathway to spintronic applications of topological insulators. Nano Lett. 11, 4079–4082 (2011).
Xiao, D. et al. Realization of the axion insulator state in quantum anomalous Hall sandwich heterostructures. Phys. Rev. Lett. 120, 056801 (2018).
Chen, Y. L. et al. Massive Dirac fermion on the surface of a magnetically doped topological insulator. Science 329, 659–662 (2010).
Fan, Y. et al. Magnetization switching through giant spin–orbit torque in a magnetically doped topological insulator heterostructure. Nat. Mater. 13, 699 (2014).
Eremeev, S. V. et al. Magnetic proximity effect at the three-dimensional topological insulator/magnetic insulator interface. Phys. Rev. B 88, 144430 (2013).
Mogi, M. et al. Magnetic modulation doping in topological insulators toward higher-temperature quantum anomalous Hall effect. Appl. Phys. Lett. 107, 182401 (2015).
Bestwick, A. J. et al. Precise quantization of the anomalous Hall effect near zero magnetic field. Phys. Rev. Lett. 114, 187201 (2015).
Lang, M. et al. Proximity induced high-temperature magnetic order in topological insulator—ferrimagnetic insulator heterostructure. Nano Lett. 14, 3459–3465 (2014).
Ou, Y. et al. Enhancing the quantum anomalous Hall effect by magnetic codoping in a topological insulator. Adv. Mater. 30, 1703062 (2018).
Kou, X. et al. Scale-invariant quantum anomalous Hall effect in magnetic topological insulators beyond the two-dimensional limit. Phys. Rev. Lett. 113, 137201 (2014).
Checkelsky, J. G. et al. Trajectory of the anomalous Hall effect towards the quantized state in a ferromagnetic topological insulator. Nat. Phys. 10, 731 (2014).
Feng, X. et al. Thickness dependence of the quantum anomalous Hall effect in magnetic topological insulator films. Adv. Mater. 28, 6386–6390 (2016).
Li, W. et al. Origin of the low critical observing temperature of the quantum anomalous Hall effect in V-doped (Bi, Sb)2Te3 film. Sci. Rep. 6, 32732 (2016).
Li, J. et al. Intrinsic magnetic topological insulators in van der Waals layered MnBi2Te4-family materials. Sci. Adv. 5, eaaw5685 (2019).
Zhang, D. et al. Topological axion states in the magnetic insulator MnBi2Te4 with the quantized magnetoelectric effect. Phys. Rev. Lett. 122, 206401 (2019).
Otrokov, M. M. et al. Highly-ordered wide bandgap materials for quantized anomalous Hall and magnetoelectric effects. 2D Mater. 4, 025082 (2017).
Otrokov, M. et al. Unique thickness-dependent properties of the van der waals interlayer antiferromagnet MnBi2Te4 films. Phys. Rev. Lett. 122, 107202 (2019).
Otrokov, M. M. et al. Prediction and observation of the first antiferromagnetic topological insulator. Preprint at https://arxiv.org/abs/1809.07389 (2018).
Gong, Y. et al. Experimental realization of an intrinsic magnetic topological insulator. Chin. Phys. Lett. 36, 076801 (2019).
Lee, S. H.et al. Spin scattering and noncollinear spin structure-induced intrinsic anomalous Hall effect in antiferromagnetic topological insulator MnBi2Te4. Phys. Rev. Res. 1, 012011 (2019).
Zeugner, A. et al. Chemical Aspects of the candidate antiferromagnetic topological insulator MnBi2Te4. Chem. Mater. 31, 2795–2806 (2019).
Yan, J. Q. et al. Crystal growth and magnetic structure of MnBi2Te4. Phys. Rev. Materials 3, 064202 (2019).
Lee, D. S. et al. Crystal structure, properties and nanostructuring of a new layered chalcogenide semiconductor, Bi2MnTe4. CrystEngComm 15, 5532–5538 (2013).
Deng, Y. et al. Magnetic-field-induced quantized anomalous Hall effect in intrinsic magnetic topological insulator MnBi2Te4. Preprint at https://arxiv.org/abs/1904.11468 (2019).
Hong, S. S. et al. Ultra-low carrier concentration and surface-dominant transport in antimony-doped Bi2Se3 topological insulator nanoribbons. Nat. Commun. 3, 757 (2012).
Zhang, J. et al. Band structure engineering in (Bi1−xSbx)2Te3 ternary topological insulators. Nat. Commun. 2, 574 (2011).
Souma, S. et al. Topological surface states in lead-based ternary telluride Pb(Bi1-xSbx)2Te4. Phys. Rev. Lett. 108, 116801 (2012).
Zhao, B. et al. Electronic interference transport and its electron–phonon interaction in the Sb-doped Bi2Se3 nanoplates synthesized by a solvothermal method. J. Phys. Condens. Matter 27, 465302 (2015).
Arakane, T. et al. Tunable Dirac cone in the topological insulator Bi2-xSbxTe3-ySey. Nat. Commun. 3, 636 (2012).
Li, M. et al. Experimental verification of the van vleck nature of long-range ferromagnetic order in the vanadium-doped three-dimensional topological insulator Sb2Te3. Phys. Rev. Lett. 114, 146802 (2015).
Zyuzin, A. A. & Loss, D. RKKY interaction on surfaces of topological insulators with superconducting proximity effect. Phys. Rev. B 90, 125443 (2014).
Litvinov, V. I. Magnetic exchange interaction in topological insulators. Phys. Rev. B 89, 235316 (2014).
Yan, J.-Q. et al. Evolution of structural, magnetic and transport properties in MnBi2-xSbxTe4. Phys. Rev. B 100, 104409 (2019).
Zhang, S. et al. Experimental observation of the gate-controlled reversal of the anomalous Hall effect in the intrinsic magnetic topological insulator MnBi2Te4 device. Preprint at https://arxiv.org/abs/1905.04839 (2019).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Bellaiche, L. & Vanderbilt, D. Virtual crystal approximation revisited: Application to dielectric and piezoelectric properties of perovskites. Phys. Rev. B 61, 7877–7882 (2000).
Souza, I., Marzari, N. & Vanderbilt, D. Maximally localized Wannier functions for entangled energy bands. Phys. Rev. B 65, 035109 (2001).
Acknowledgements
We gratefully acknowledge the financial support of the National Key R&D Program of China (2017YFA0303203 and 2018YFA0306800), the National Natural Science Foundation of China (91622115, 11522432, 11574217, 11674165, 11774154, 61822403, 11874203, 11904165, 11904166, U1732273, and U1732159), the Natural Science Foundation of Jiangsu Province (BK20160659, BK20190286), the Fundamental Research Funds for the Central Universities, Users with Excellence Program of Hefei Science Center CAS (2019HSC-UE007), and the opening Project of the Wuhan National High Magnetic Field Center. Part of this research used Beamline 03U of the Shanghai Synchron Radiation Facility, which is supported by ME2 project under contract No. 11227902 from National Natural Science Foundation of China. We thank Professor Donglai Feng and Rui Peng from Fudan University for helping with the ARPES measurements. We also thank Professor Ke He from Tsinghua University for some stimulating discussions.
Author information
Authors and Affiliations
Contributions
B.C. and F.F. took charge of crystal growth and characterization. B.C., F.F., B.Z., P.W., W.L., Y.Z., J.G., Q.L., Z.W., X.W., J.Z., X.X., W.C., Z.S., D.S., S.W. and Y.Z. carried out the ARPES measurements. B.C. and F.F. measured the transport and magnetism properties. S.Z. and B.W. fabricated the devices and performed the device measurements. Z.Z. measured the HR-TEM images. D.Z. and H.Z. performed the first-principles calculations. F.F. and F.S. wrote the paper and Y.Z., M.Z., X.W., H.Z. and B.W. participated in discussions on this paper. F.S. was responsible for overall project planning and direction.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Shik Shin and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Chen, B., Fei, F., Zhang, D. et al. Intrinsic magnetic topological insulator phases in the Sb doped MnBi2Te4 bulks and thin flakes. Nat Commun 10, 4469 (2019). https://doi.org/10.1038/s41467-019-12485-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-12485-y
- Springer Nature Limited
This article is cited by
-
Fabrication-induced even-odd discrepancy of magnetotransport in few-layer MnBi2Te4
Nature Communications (2024)
-
Quantum geometry quadrupole-induced third-order nonlinear transport in antiferromagnetic topological insulator MnBi2Te4
Nature Communications (2024)
-
Revealing Fermi surface evolution and Berry curvature in an ideal type-II Weyl semimetal
Nature Communications (2024)
-
On the half-quantized Hall conductance of massive surface electrons in magnetic topological insulator films
Science China Physics, Mechanics & Astronomy (2024)
-
Antiferromagnetic topological insulator with selectively gapped Dirac cones
Nature Communications (2023)