Abstract
We have performed transport measurements on a gallium phosphide antimonide (GaPSb) film grown on GaAs. At low temperatures (T), transport is governed by three-dimensional Mott variable range hopping (VRH) due to strong localization. Therefore, electron–electron interactions are not significant in GaPSb. With increasing T, the coexistence of VRH conduction and the activated behavior with a gap of 20 meV is found. The fact that the measured gap is comparable to the thermal broadening at room temperature (approximately 25 meV) demonstrates that electrons can be thermally activated in an intrinsic GaPSb film. Moreover, the observed carrier density dependence on temperature also supports the coexistence of VRH and the activated behavior. It is shown that the carriers are delocalized either with increasing temperature or magnetic field in GaPSb. Our new experimental results provide important information regarding GaPSb which may well lay the foundation for possible GaPSb-based device applications such as in high-electron-mobility transistor and heterojunction bipolar transistors.
Avoid common mistakes on your manuscript.
Background
III-V-based alloys and heterostructures have been attracting much interest because of their great device applications as well as their fundamental importance. A major issue of composing III-V-based systems is the miscibility gap in solids[1]. It is known that the mixing enthalpy of the systems, such as GaAs-GaSb and GaP-GaSb, is proportional to the square of the difference in lattice constant of the two end binary components of the system[2]. This reason prohibits the epitaxial growth of most alloys at ordinary growth temperatures[3]. Therefore, the epitaxial growth of these systems was not achieved until the first growth of GaAs-GaSb was done in 1979 by carrying out the growth under a high-supersaturation condition, such as molecular beam epitaxy (MBE)[4]. The ternary alloy gallium phosphide antimonide (GaP1−xSb x ) was grown on GaAs for the first time using the organometallic vapor-phase epitaxy method in 1988[5]. Since then, there has been a lack of work on gallium phosphide antimonide as well as on the transport behavior in such material.
For an intrinsic semiconductor, it usually shows insulating behavior in the sense that the resistance decreases with increasing temperature. At low temperatures (T), when the thermal energy is not high enough to excite carriers to the conduction band, transport is mostly dominated by variable range hopping (VRH)[6, 7], indicating the strong localization of carriers. In the Mott VRH regime, the temperature dependence of the longitudinal resistance Rxx is of the form
with the exponent p = 1/3 for two-dimensional (2D) systems or p = 1/4 for three-dimensional (3D) ones. Here, R0 is a prefactor and T0 is the characteristic temperature related to the localization length. When considering interactions, the suppression of density of states near the Fermi energy would lead to p = 1/2 for both 2D and 3D systems in Equation 1, known as Efros-Shklovskii VRH. Another important phenomenon in the strong localization regime is referred to as negative magnetoresistance (NMR) which results from the suppression of quantum interference between forward scattering hopping paths as the magnetic field (B) is applied[8–11]. On the other hand, at high B where the hopping probability between different sites is significantly reduced due to the shrinkage of wave function, positive magnetoresistance (PMR) occurs[12]. NMR and PMR refer to the case where the resistance decreases and increases, respectively, with increasing B.
At elevated T, activation conduction can contribute to the transport as well, which is usually observed in a doped semiconductor like a Si delta-doped GaAs. In an n-type semiconductor, the Fermi energy is shifted towards the conduction band edge from the mid-gap position. In this activation regime, the resistance as a function of T can be described by
with Boltzmann constant (kB), activation energy (Ea), and a prefactor (Ra). Such a crossover from VRH conduction to an activation one with increasing T has already been observed in Si delta-doped GaAs grown by MBE[13].
Since there is a dearth of work on the transport properties of GaPSb, important physical phenomena such as the type of carriers, the strength of carrier-carrier interactions, transport behavior, and so on require further investigations. In this work, we report extensive transport studies of a GaPSb film grown on a GaAs substrate. Such a device is fully compatible with the existing GaAs-based high-electron-mobility transistor (HEMT) technology. Moreover, the GaPSb-based material system may well be of great device applications in heterojunction bipolar transistor (HBT), high-power devices, and nanoelectronics[14–16]. We shall show that the carriers in GaPSb are electrons. Moreover, at low temperatures, electrons in GaPSb are strongly localized and can be described by 3D Mott VRH. Therefore, electron–electron interactions are negligible in GaPSb. Furthermore, we show that VRH and activation conduction can coexist, which is consistent with the observed peculiar T dependence of n. The measured gap from the observed activated behavior (approximately 20 meV) is comparable to thermal broadening at room temperature (approximately 25 meV). Such a result suggests that electrons are delocalized in nominally undoped GaPSb at room temperature. Our new experimental results provide important information for possible device applications as well as modeling using the GaPSb-based materials.
Methods
The undoped 720-nm-thick GaP0.71Sb0.29 was grown on a 4-in. (100) 2° off-axis toward (110) GaAs substrate by an Aixtron 2600G3 (Aixtron SE, Aachen, Germany) metal organic chemical vapor deposition, using trimethygallium and trimethyantimony as metal organic sources and phosphine (PH3) and arsine (AsH3) as hydride sources. The growth conditions for the GaP0.71Sb0.29 are similar to those published in[17]. We used Vegard's law to determine the averaged Sb composition in this GaP0.71Sb0.29 bulk sample by X-ray diffraction. The reactor was heated up to 700°C to clean the substrate surface with AsH3 before the epitaxial growth and then cooled down to 530°C for the GaPSb growth. The V/III ratio and growth rate were approximately 1 and 1 μm/h, respectively. On top of the GaP0.71Sb0.29 film, a 20-nm GaAs cap was deposited. The Hall bar device was fabricated by standard photolithography and etched by a top-down process with a solution at the mixture ratio of H3PO4/H2O2/H2O = 1:1:10. Four-terminal measurements were performed by standard dc techniques in a top-loading He3 cryostat.
Results and discussion
Figure1a shows the current–voltage measurements V(I) at various temperatures. For T ≦ 20 K, V(I) is highly nonlinear, suggesting that the carriers are strongly localized at low temperatures. With increasing T above 60 K, it shows ohmic behavior over the whole applied current range −2 μA ≦ I ≦ 2 μA. The longitudinal resistance Rxx as a function of T is measured in the ohmic regime with a current I = 1 nA, and the result is shown in Figure1b. The inset in Figure1b illustrates the structure of the device.
In order to further study the transport mechanism in such a highly disordered system, the longitudinal and Hall resistances (Rxx and Rxy) as a function of B at various T were measured, and the results are presented in Figure2a,b, respectively. A current of 100 nA was applied in magnetotransport measurements so as to improve signal-to-noise ratio. As shown in Figure2a, Rxx(B) behaves as an insulator over the whole measurement range. For clarity, we plot Rxx(B)/Rxx(0)−1 against B in Figure2c. With increasing B, a slight decrease of resistance, characteristic of NMR, and subsequent increase of it, characteristic of PMR, can be observed at T = 4.2 K.
Figure2b shows the Hall resistance which is always negative, indicating that electrons are the major carriers in GaPSb. The Hall slope RH = −Rxy/B = 1/(ned) increases with increasing T, and therefore, the estimated carrier concentration n decreases with increasing T, as shown in the inset of Figure2b, where d is the thickness of the measured GaPSb film. It can be observed that n changes rapidly for T < 40 K, while only a slight decrease of n can be seen at higher T. Neither activation of carriers to the conduction band nor electron–electron interaction effects can explain such results as both would tend to decrease the Hall slope with increasing T[18]. As suggested by our previous study on a Si delta-doped GaAs single quantum well[19] and the work performed by Yildiz et al. on Si delta-doped GaAs[13], the observation of non-monotonic T dependence of n, that is, it first decreases and then increases with increasing T, can be regarded as a piece of evidence that there is a crossover from VRH conduction to the activation one with increasing T since the VRH conduction would affect the estimation of Hall slope at low T and results in a reduction of n. According to our results, the decrease of n with increasing T as shown in the inset of Figure2b, we are able to deduce that the VRH conduction coexists with the activation one over the whole measurement range. To further support this argument, the two-band conduction model[20–22] is used to analyze the R(T) results shown in Figure1a. In this model, one can expect that the longitudinal conductance Gxx = 1/Rxx is determined as the combination of VRH and activation conduction and is described by
with prefactors Gc and G0[23]. The other parameters are the same as those used in Equations 1 and 2. As shown by the dotted line in Figure3, there is a good fit to Equation 3, and the parameters are obtained as Gc = 20 μS, Ea = 20 meV, G0 = 10 μS, T0 = 1,409 K, and p = 0.23. The determined exponent p = 0.23 close to the expected value of 0.25 for 3D Mott VRH demonstrates that our GaPSb film is intrinsically three-dimensional and the interactions between electrons is insignificant. Moreover, a transport gap of Ea = 20 meV is found, which is very useful in the fabrication of heterojunction devices since the thermal energy is enough to activate electrons in GaPSb at room temperature, an attractive property for possible HEMT and HBT applications. In the 3D Mott VRH model, kBT0 = 18/(N(EF)ξ3 such that ξ = (18/k B T0/N(E F ))1/3. With the obtained T0 ~ 1,409 K and under the assumption that and m* = me, ξ = 29.5 nm, Rhop ~ 29.5(1,409/T)1/4 nm and the hoping energy whop ~ kBT(1,409/T)1/4 are obtained. Hence, for 4.2 K ≤ T ≤ 80 K, 60 nm ≤ Rhop ≤ 126 nm, and 1.55 meV < whop < 14 meV. From these estimations showing Rhop << sample size and whop< Ea ~ 20 meV over the temperature range of interest, we can learn that VRH transport indeed plays an important role in our system. If the nearest-neighbor-hopping (NNH) conduction plays a role, p ~ 1 should be given. However, we show that p ~ 0.23. Moreover, from the observed unusual temperature dependence of the carrier density, it is expected that the activation conduction would contribute to the conduction at high-enough temperatures. Therefore, we believe that the high-T-activated behavior is predominantly caused by a thermal activation conduction process rather than NNH.
After substituting the obtained parameters into Equation 3, the contributions of VRH and activation conduction are shown separately in Figure4. The blue line denotes the VRH part, and the red one is for the activation conduction in Equation 3. It can be seen clearly that VRH dominate the transport for T < 30 K, consistent with the observations of nonlinear V(I) and the rapid decrease of n at low temperatures, which suggests that the carriers are indeed strongly localized at low T. The deviation from the 3D Mott VRH at high T can be observed clearly by plotting lnG as a function of T−1/4, which can be seen in the inset of Figure4. With increasing T, the activation contribution can compete with the VRH one, and therefore the ohmic behavior can be restored at high T, which can be seen in Figure1a. Such results demonstrate that the carriers are delocalized with increasing T.
For carriers in the conduction band, diffusive motion can dominate the transport, in which nonlinear V(I) does not occur. As inferred from the NMR shown in Figure2a, delocalization of carriers occurs with increasing B as well. However, as known from the nonlinear V(I) at various B for T = 4.2 K shown in Figure3, the carriers are still strongly localized. Therefore, the observed NMR should result from the quantum interference feature in the strong localization regime, which is different from the T-induced delocalization process.
Conclusion
We have performed extensive transport measurements on a GaPSb film grown by MOCVD. At a low T, variable range hopping dominates the transport, and then, a crossover from VRH to activation conduction occurs with increasing T. In the intermediate temperature range, coexistence of the VRH and activation conduction can be found, consistent with the observation of peculiar T dependence of carrier concentration. The observed nonlinear current–voltage relations further support that the carriers are strongly localized at low temperatures. The carriers can be delocalized either with increasing T or increasing B. The measured transport gap of approximately 20 meV is comparable to thermal broadening at room temperature (approximately 25 meV). Therefore, our results show that electrons can be thermally activated even in an intrinsic GaSbP film at room temperature. This interesting result may find applications in designing a transistor with a GaPSb base. Moreover, since our GaPSb film is grown on GaAs, such a device is fully compatible with existing GaAs-based HEMT technology. Our work may be useful for possible applications such as HEMT and HBT devices based on the GaPSb material system.
Authors’ information
STL obtained his B.Sc. degree at National Taiwan University (NTU) in 2010 and is pursuing his Ph.D. degree at the Graduate Institute of Applied Physics, NTU. He won the Dr. An-Tai Chen Scholarship, Mr. Ming Kao Scholarship, and Creative Award for college students participating in special research project provided by the NSC in 2009. HEL obtained his master's degree at NTU in 2011. SWW obtained his master's degree at NTU in 2011. He won the prestigious Lam Research Award in 2012. HDL obtained his B.S. degree at Chinese Culture University, Taiwan, and his Ph.D. degree at Mississippi State University, USA, and currently works as a project engineer at the Electronics Testing Center, Tao-Yuan, Taiwan (ROC). YCC received his B.S. degree in physics from NTU in 1996 and his MSEE degree from National Chiao-Tung University (NCTU) in 2000. He currently is a Ph.D. student studying at the Graduate Institute of Electronics Engineering, NTU. HHL obtained his BSEE, MSEE, and Ph.D. degree at NTU and is currently a professor of the Department of Electrical Engineering, NTU. JCL obtained his master's degree at NTU in 2012. CTL obtained his B.Sc. degree at NTU in 1990 and his Ph.D. degree in physics at Cambridge University, UK, in 1996 and is currently a professor of physics at NTU. He is also a topical editor for Current Applied Physics and an associate editor for the Journal of Nanoscience Letters.
References
Stringfellow GB: Miscibility gaps in quaternary III/V alloys. J Cryst Growth 1982, 58: 194. 10.1016/0022-0248(82)90226-3
Stringfellow GB: Calculation of ternary and quaternary III–V phase diagrams. J Cryst Growth 1974, 27: 21.
Pessetto JR, Stringfellow GB: AlxGa1−xAsySb1−y phase diagram. J Cryst Growth 1983, 62: 1. 10.1016/0022-0248(83)90002-7
Waho T, Ogawa S, Maruyama S: GaAs1-xSbx(0.3<x<0.9) grown by molecular beam epitaxy. Jpn J Appl Phys 1977, 16: 1875. 10.1143/JJAP.16.1875
Jou MJ, Cherng YT, Jen HR, Stringfellow GB: Organometallic vapor phase epitaxial growth of a new semiconductor alloy: GaP1-xSbx. Appl Phys Lett 1988, 52: 549. 10.1063/1.99413
Shlimak I, Friedland KJ, Baranovskii SD: Hopping conductivity in gated δ-doped GaAs: universality of prefactor. Solid State Commun 1999, 112: 21. 10.1016/S0038-1098(99)00286-0
Khondaker SI, Shlimak IS, Nicholls JT, Pepper M, Ritchie DA: Two-dimensional hopping conductivity in a δ-doped GaAs/AlxGa1-xAs heterostructure. Phys Rev B 1999, 59: 4580. 10.1103/PhysRevB.59.4580
Faran O, Ovadyahu Z: Magnetoconductance in the variable-range-hopping regime due to a quantum-interference mechanism. Phys Rev B 1988, 38: 5457. 10.1103/PhysRevB.38.5457
Sivan U, Entin-Wohlman O, Imry Y: Orbital magnetoconductance in the variable-range–hopping regime. Phys Rev Lett 1988, 60: 1566. 10.1103/PhysRevLett.60.1566
Entin-Wohlman O, Imry Y, Sivan U: Orbital magnetoconductance in the variable-range-hopping regime. Phys Rev B 1989, 40: 8342. 10.1103/PhysRevB.40.8342
Tremblay F, Pepper M, Ritchie D, Peacock DC, Frost JEF, Jones GAC: Negative magnetoresistance in the variable-range-hopping regime in n-type GaAs. Phys Rev B 1989, 39: 8059. 10.1103/PhysRevB.39.8059
Raikh ME, Czingon J, Ye Q-y, Koch F, Schoepe W, Ploog K: Mechanisms of magnetoresistance in variable-range-hopping transport for two-dimensional electron systems. Phys Rev B 1992, 45: 6015. 10.1103/PhysRevB.45.6015
Yildiz A, Lisesivdin SB, Altuntas H, Kasap M, Ozcelik S: Electrical conduction properties of Si δ-doped GaAs grown by MBE. Physica B 2009, 404: 4202. 10.1016/j.physb.2009.07.190
Frigeri C, Shakhmin A, Vinokurov D, Zamoryanskaya M: Chemical characterization of extra layers at the interfaces in MOCVD InGaP/GaAs junctions by electron beam methods. Nanoscale Res Lett 2011, 6: 194. 10.1186/1556-276X-6-194
Chin YC, Lin HH, Huang CH, Tseng MN: In0.46Ga0.54P0.98Sb0.02/GaAs: its band offset and application to heterojunction bipolar transistor. IEEE Electron Device Lett 2010, 31: 434.
Chin YC, Lin HH, Huang CH: InGaP/GaAs0.57P0.28Sb0.15/GaAs double HBT with weakly type-II base/collector junction. IEEE Electron Device Lett 2012, 33: 489.
Jou MJ, Cherng YT, Jen HR, Stringfellow GB: OMVPE growth of the new semiconductor alloys GaP1−xSbx and InP1−xSbx. J Cryst Growth 1988, 93: 62. 10.1016/0022-0248(88)90507-6
Simmons MY, Hamilton AR, Pepper M, Linfield EH, Rose PD, Ritchie DA: Weak localization, hole-hole interactions, and the “metal”-insulator transition in two dimensions. Phys Rev Lett 2000, 84: 2489. 10.1103/PhysRevLett.84.2489
Lo S-T, Chen KY, Su Y-C, Liang CT, Chang YH, Kim G-H, Wu JY, Lin S-D: Crossover from negative to positive magnetoresistance in a Si delta-doped GaAs single quantum well. Solid State Commun 2010, 150: 1104. 10.1016/j.ssc.2010.03.030
Look DC, Walters DC, Manasreh MO, Sizelove JR, Stutz CE, Evans KR: Anomalous Hall-effect results in low-temperature molecular-beam-epitaxial GaAs: hopping in a dense EL2-like band. Phys Rev B 1990, 42: 3578. 10.1103/PhysRevB.42.3578
Shklovskii BI, Elfros AL: Electronic Properties of Doped Semiconductors. Berlin: Springer; 1984.
Look DC: Electrical Characterization of GaAs Materials and Devices. New York: Wiley; 1989.
Benzaquen M, Walsh D: Variable-range-hopping conductivity in compensated n-type GaAs. Phys Rev B 1984, 30: 7287. 10.1103/PhysRevB.30.7287
Acknowledgements
This work was funded by the NSC, Taiwan and by the National Taiwan University (grant number: 101R7552-2).
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
STL, HEL, SWW, and JCL performed the measurements. STL and CTL drafted the paper. HDL proposed the theoretical models. HHL coordinated the project. YCC prepared the sample. All authors read and approved the final version of the manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Lo, ST., Lin, H.E., Wang, SW. et al. Electron transport in a GaPSb film. Nanoscale Res Lett 7, 640 (2012). https://doi.org/10.1186/1556-276X-7-640
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-7-640