Abstract
Partially-unzipped multiwalled carbon nanotubes (PUCNTs) combine the chemical structure and basic mechanical properties of multiwalled carbon nanotubes (MWCNTs) and graphene nanoplatelets (GNPs) with exceptionally high graphene-edge content. As a result, PUCNTs can be effectively oxidized for dispersion in aqueous solutions and have a specific surface area that is larger than that of MWCNTs with a comparable aspect ratio. Thus, the incorporation of relatively small concentrations of PUCNTs in cement composites may result in significant physicomechanical enhancements. In the proof-of-concept study presented here, cement paste specimens were manufactured with oxidized PUCNT concentrations of 0, 0.001, and 0.005% in weight of cement (wt%), that is, one order of magnitude smaller than lower-bound concentrations for MWCNTs reported in the literature. Stable dispersion in water was verified through dynamic light scattering analysis. Physicomechanical changes and PUCNT dispersion in the cement matrix were investigated through uniaxial compression tests on 25 × 25 × 76 mm prism specimens, and visual inspection of scanning electron microscopy (SEM) micrographs, respectively. The incorporation of 0.001 wt% and 0.005 wt% of PUCNTs resulted in an average increase in compressive strength of 10% and 29%, respectively, compared with plain cement paste. In both instances, representative SEM micrographs show the preferential formation of cement hydrates in cement paste that accorded with well-dispersed PUCNTs.
You have full access to this open access chapter, Download conference paper PDF
Keywords
1 Introduction
Partially-unzipped multiwalled carbon nanotubes (PUCNTs) are synthesized by longitudinal unzipping of the outer walls of multiwalled carbon nanotubes (MWCNTs) [1, 2], resulting in a portion having a morphology similar to that of graphene nanoplatelets (GNPs). MWCNTs are characterized by a relatively high aspect ratio, which may be beneficial when using these nanoparticles as reinforcement in cement composites [3]. Mechanical enhancements have also been reported for nano-amended cement composites with GNP concentrations between 0.03% [4] and 0.5% [5] in weight of cement (wt%). Related mechanisms may be associated with improved cement hydration through the presence of carboxyl and hydroxyl functional groups on the surface of oxidized MWCNTs and GNPs [6, 7], with a reduction in total porosity [8, 9], pore-size refinement [8, 10], and densification of the cement matrix [11].
PUCNTs have appealing properties compared with their fully-unzipped counterparts; elongated strips of graphene with more functional group-edge sites compared with MWCNTs or GNPs, but also a smaller aspect ratio [12]. Partial unzipping of the outer walls of MWCNTs results in a radical increase in the open surface area [12], and oxidation produces a relatively larger amount of functional groups [1], thus enhancing the chemical affinity with the cement matrix. Through this process, a few outer layers of a given MWCNT are partially unzipped without affecting the inner core walls, resulting in a hybrid graphitic structure together with the inner (intact) carbon nanotubes [13]. Therefore, the resulting PUCNTs exhibit: (a) larger surface area and greater functionality than their precursor MWCNTs, which may enhance dispersibility in aqueous solutions and in the cement matrix, and (b) a relatively high aspect ratio, which may enhance the mechanical properties of the cement composite.
We present a feasibility study of cement paste amended with low concentrations of oxidized PUCNTs, namely, 0.001 and 0.005 wt%, which is one order of magnitude smaller than successful lower-bound concentrations reported in the literature for MWCNTs and GNPs.
2 Methods
2.1 PUCNT Aqueous Suspensions
The PUCNTs were prepared at Savannah River National Laboratory (Aiken, SC, USA) using an oxidative unzipping process modified from Kosynkin et al. [14]. Defects in the pristine MWCNTs were created by soaking in concentrated sulfuric acid and o-phosphoric acid, with potassium permanganate serving as the oxidant. By controlling the amount of oxidant, heating time, and soaking time, the PUCNTs shown in Fig. 1a were produced, and then suspended in deionized (DI) water. Stock solution of 3 g/L of these PUCNTs in DI water was diluted with additional DI water to prepare 0.02 and 0.1 g/L suspensions, to be used for the manufacturing of cement paste specimens with PUCNT concentrations of 0.001 wt% and 0.005 wt%, respectively. A small amount of NaOH (<0.01 mol/L) was added to the suspensions to reach an approximate pH of 12, thereby enhancing the stability of acid-treated (i.e., low pH) PUCNTs in water. The suspensions were ultrasonicated for 15 min using an ultrasonic bath sonicator (model CPX 2008, Branson Ultrasonics Corp., CT, USA).
2.2 Cement Paste Specimens
Prismatic specimens with dimensions 25 × 25 × 76 mm were prepared per ASTM C305 [15] using Type I ordinary Portland cement (OPC) and PUCNT aqueous suspensions, with a water-to-cement ratio of 0.5 (in weight). Plain cement paste specimens to be used as the benchmark were also cast using Type I OPC and DI water. All specimens were cast in acrylic molds from which they were removed after 24 h, and then placed in saturated lime water for 28 days.
2.3 Procedure
The dispersibility of the functionalized PUCNTs in DI water solutions was quantitatively assessed via dynamic light scattering (DLS) testing using a particle and molecular size analyzer (model Zetasizer nano ZS, Malvern Panalytical Ltd.).
For each PUCNT concentration, a suspension sample of 1 mL was used to measure the zeta potential. Each measurement was repeated 10 times to assess the variability of the results. Representative aqueous suspensions used for the manufacturing of cement paste specimens with PUCNTs in concentrations of 0.001 and 0.005 wt% are shown in Fig. 1b.
Uniaxial compression tests were performed on the 28 day cured prism specimens using a servo-hydraulic loading frame. The load was applied in displacement-control mode at a rate of 0.3 mm/min and was measured using a 20-kip load cell. Thin polytetrafluoroethylene inserts were placed between the specimen surfaces and the loading platens to minimize friction. A representative test setup is shown in Fig. 2a. Four specimens were tested for each PUCNT concentration (0, 0.001 and 0.005 wt%).
The fractured specimens were used for scanning electron microscopy (SEM) analysis to investigate the incorporation and dispersion of PUCNTs in the cement paste structure. Specifically, SEM micrographs were used to visually assess the presence of undesirable PUCNT agglomerates as a result of ineffective dispersion. To this end, specimens’ fragments <5 mm in length in any direction were used. Following the compression tests, these samples were extracted from the prisms, air-dried for 24 h, and placed in a vacuum-suction chamber for 1 h to remove the excess moisture. The samples were gold-spattered before being examined under a SEM (Ultraplus Thermal Field Emission Scanning Electron Microscope, Zeiss).
3 Results and Discussion
3.1 Dispersibility in Aqueous Suspension
The effective dispersion of PUCNTs in the aqueous suspensions was assessed by zeta potential measurements made as part of the DLS tests. The zeta potential values obtained were –39.5 ± 1.30 mV and –39.6 ± 1.07 mV for the suspensions used to manufacture cement paste specimens with 0.001 wt% and 0.005 wt% of PUCNT concentration, respectively. Because suspensions characterized by a zeta potential smaller than –30 mV are considered stable [16], and also based on visual inspection (Fig. 1b), it was concluded that the oxidized PUCNTs were effectively dispersed in the aqueous solutions used in this research.
3.2 Compressive Strength
The mean and standard deviation of the 28 day compressive strength were 32.0 ± 3.10 MPa, 34.7 ± 1 0.93 MPa, and 41.4 ± 7.4 MPa for cement paste with PUCNT concentrations of 0, 0.001 and 0.005 wt%, as summarized in Fig. 2b.
Our results showed that the incorporation of very small amounts of PUCNTs resulted in significant compressive strength enhancement, namely 29% on average for a concentration of 0.005 wt%, compared with plain cement paste.
Evidence collected through SEM image analysis was used to better understand plausible strengthening mechanisms. In fact, the micrographs shown in Figs. 3, 4 and 5 suggest that the incorporation of PUCNTs resulted in preferential formation of amorphous (C–S–H) and crystalline (calcium hydroxide) cement hydrates (Figs. 4 and 5), with a less porous structure than plain cement paste (Fig. 3).
In addition, the lack of visible clusters of PUCNTs suggested that the methodology used will produce cement composites with well-dispersed and chemically-affine PUCNTs, and thus with a meso-scale homogeneity comparable to or better than that of plain cement paste. However, the significantly larger standard deviation of the compressive strength results for the 0.005 wt% concentration suggested that larger concentrations of PUCNTs may be more difficult to disperse in the cement matrix.
4 Conclusions
The following conclusions are presented.
-
It is feasible to incorporate well-dispersed and chemically-affine PUCNTs to enhance the physicomechanical properties of cement paste. The unzipping process is similar in chemical approach (and thus cost) to the well-known Hummer’s method used to generate graphite oxide.
-
Due to the morphology and high graphene-edge content of PUCNTs, dispersibility in aqueous solutions was easily achieved.
-
A significant increase in the compressive strength of cement paste occurred with a PUCNT concentration of 0.005 wt%, which is one order of magnitude smaller than lower-bound concentrations reported in the archival literature for MWCNT- and GNP-amended cement pastes.
-
Microscopic inspection of the cement paste nano- and micro-structures suggests that plausible contributing mechanisms for strength enhancement include the preferential and well-distributed formation of cement hydrates in the vicinity of PUCNTs—also resulting in a less porous structure—compared with plain cement paste.
References
Song Y, Feng M, Zhan H (2014) Electrochemistry of partially unzipped carbon nanotubes. Electrochem Commun 45:95–98
Cheng Y, Zhang S, Li J, Sun J, Wang J, Qin C, Dai L (2017) Preparation of functionalized partially unzipped carbon nanotube/polyimide composite fibers with increased mechanical and thermal properties. R Soc Chem Adv 7:21953–21961
Abu Al-Rub RK, Ashour AI, Tyson BM (2012) On the aspect ratio effect of multi-walled carbon nanotube reinforcements on the mechanical properties of cementitious nanocomposites. Constr Build Mater 35:647–655
Lv SH, Deng LJ, Yang WQ, Zhou QF, Cui YY (2016) Fabrication of polycarboxylate/graphene oxide nanosheet composites by copolymerization for reinforcing and toughening cement composites. Cement Concr Compos 66:1–9
Zohhadi N (2014) Functionalized graphitic nano-reinforcement for cement composites. PhD thesis, University of South Carolina, Columbia
Kaur R, Kothiyal NC (2019) Comparative effects of sterically stabilized functionalized carbon nanotubes and graphene oxide as reinforcing agent on physico-mechanical properties and electrical resistivity of cement nanocomposites. Constr Build Mater 202:121–138
Makar JM, Chan GW (2009) Growth of cement hydration products on single-walled carbon nanotubes. J Am Ceram Soc 92(6):1303–1310
Li GY, Wang PM, Zhao X (2005) Mechanical behavior and microstructure of cement composites incorporating surface-treated multi-walled carbon nanotubes. Carbon 43:1239–1245
Nochaiya T, Chaipanich A (2011) Behavior of multi-walled carbon nanotubes on the porosity and microstructure of cement-based materials. Appl Surf Sci 257:1941–1945
Hu Y, Luo D, Li P, Li Q, Sun G, Key S (2014) Fracture toughness enhancement of cement paste with multi-walled carbon nanotubes. Constr Build Mater 70:332–338
Liu J, Wang L, Li Q, Xu S (2019) Reinforcing mechanism of graphene and graphene oxide sheets on cement-based materials. J Mater Civ Eng 31(4):04019014
Jeong YC, Lee K, Kim T, Kim JH, Park J, Cho YS, Yang SJ, Park CR (2016) Partially unzipped carbon nanotubes for high-rate and stable lithium–sulfur batteries. J Mater Chem A 4:819–826
Shende RS, Ramaprabhu S (2016) Thermo-optical properties of partially unzipped multiwalled carbon nanotubes dispersed nanofluids for direct absorption solar thermal energy systems. Sol Energy Mater Sol Cells 157:117–125
Kosynkin DV, Higginbotham AL, Sinitskii A, Lomeda JR, Ayrat DA, Price BK, Tour JM (2009) Longitudinal unzipping of carbon nanotubes to form graphene nanoribbons. Nature 458:872–877
ASTM International (2014) Standard practice for mechanical mixing of hydraulic cement pastes and mortars of plastic consistency. ASTM C305-14. ASTM International, West Conshohocken, PA
Freitas C, Muller RH (1998) Effect of light and temperature on zeta potential and physical stability in solid lipid nanoparticle (SLN™) dispersions. Int J Pharm 168:221–229
Acknowledgements
This material is based on collaborative work supported by the U.S. Department of Energy Office of Science, Office of Basic Energy Sciences, and Office of Biological and Environmental Research, under award number DE-SC0012530; Savannah River National Laboratory; and, the University of South Carolina (USC) Advanced Support for Innovative Research Excellence (ASPIRE) program. Special thanks are extended to Ms. Erika Rengifo (Ph.D.) and Ms. Sarah Riser (undergraduate research assistant) at the UofSC Department of Civil and Environmental Engineering, and personnel of the Center for Environmental Nanoscience and Risk at the Arnold School of Public Health, and the Electron Microscopy Center, for their technical assistance.
Author information
Authors and Affiliations
Contributions
The authors confirm contributions as follows: study conception and design: Iffat S., Matta F., Gaillard J., Baalousha M.; data collection: Iffat S., Levington M., Tinkey S., Meany J.; analysis and interpretation of results: Iffat S., Matta F., Gaillard J., Sikder M., Baalousha M.; draft manuscript preparation: Iffat S., Matta F. All authors reviewed the results and approved the final version of the manuscript.
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Open Access This chapter is licensed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license and indicate if changes were made.
The images or other third party material in this chapter are included in the chapter's Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the chapter's Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
Copyright information
© 2023 The Author(s)
About this paper
Cite this paper
Iffat, S. et al. (2023). Partially-Unzipped Carbon Nanotubes as Low-Concentration Amendment for Cement Paste. In: Duan, W., Zhang, L., Shah, S.P. (eds) Nanotechnology in Construction for Circular Economy. NICOM 2022. Lecture Notes in Civil Engineering, vol 356. Springer, Singapore. https://doi.org/10.1007/978-981-99-3330-3_20
Download citation
DOI: https://doi.org/10.1007/978-981-99-3330-3_20
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-99-3329-7
Online ISBN: 978-981-99-3330-3
eBook Packages: EngineeringEngineering (R0)