Abstract
We investigated the formation of the conductive network of carbon nanotubes (CNTs) in alkali-activated nanocomposites for sulfate-sensing applications. The matrix was a one-part blend of fly ash and ground granulated blast-furnace slag, activated by sodium silicate and water. Sodium dodecylbenzenesulfonate was used as the surfactant for dispersion of the CNTs in the aqueous media. The nanocomposites were investigated by a laboratory-developed setup to study the electrical and sensing properties of the alkali-activated material. The electrical properties (i.e., conductivity) were calculated and assessed to discover the percolation threshold of the nanocomposites. Furthermore, the sensing behavior of nanocomposites was studied upon sulfate (\({\mathrm{SO}}_{4}^{2-}\)) exposure by introduction of sulfuric acid (\(({\mathrm{H}}_{2}{\mathrm{SO}}_{4})\)) and magnesium sulfate (\({\mathrm{MgSO}}_{4}\)). The sensors were able to preliminarily exhibit a signal difference based on the introduced media (\({\mathrm{H}}_{2}{\mathrm{SO}}_{4} \&\mathrm{ Mg}{\mathrm{SO}}_{4}\)), CNT content and \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\) volumetric quantity. The results of this research demonstrated a sensing potential of CNT alkali-activated nanocomposites and can be applied in the concrete structural health monitoring.
You have full access to this open access chapter, Download conference paper PDF
Keywords
1 Introduction
Aggressive ions such as sulfates (\({\mathrm{SO}}_{4}^{2-}\)) are naturally available in the surrounding aquatic media of concrete infrastructures. Moreover, these anionic species can be liberated from the underground environments or internal sources by moisture ingress (chemical origin) or can be produced through the metabolism of microorganisms (biogenic origin). The main sources of \({\mathrm{SO}}_{4}^{2-}\) anions are sulfuric acid (\({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\)), magnesium sulfate (\({\mathrm{MgSO}}_{4}\)), and sodium sulfate (\({\mathrm{Na}}_{2}{\mathrm{SO}}_{4}\)), which cause severe degradation of concrete material over long-term exposure [1,2,3,4]. An innovative idea regarding prevention of concrete material deterioration is the development of a sensor to distinguish \({\mathrm{SO}}_{4}^{2-}\) species coming from identical [5] or non-identical sources or having different concentrations/quantities.
Therefore, in the present study, carbon nanotube (CNT) alkali-activated sensors are proposed for \({\mathrm{SO}}_{4}^{2-}\) species sensing and discriminating released from \({\mathrm{H}}_{2}{\mathrm{SO}}_{4} \& {\mathrm{MgSO}}_{4}\), for the first time to the best of our knowledge. The sensors were fabricated from a sodium-based fly ash ground granulated blast-furnace slag (GGBS) alkali-activated material and CNTs. As the first step, the percolation threshold of the sensors was determined by measuring the electrical resistance (converted to conductivity) of CNT alkali-activated nanocomposites, incorporating different content of CNTs. To study the \({\mathrm{SO}}_{4}^{2-}\) sensing potential and transitional behavior of the nanocomposites from insulating to conducting mode, the sensors were fabricated to incorporate different CNT concentrations. The assessments were carried out by introducing \({\mathrm{H}}_{2}{\mathrm{SO}}_{4} \&\mathrm{ Mg}{\mathrm{SO}}_{4}\) with identical concentration. Finally, the sensors were fabricated with the percolated CNT concentration and evaluated by introducing different volumetric quantities of \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\).
2 Methods
2.1 Materials
The applied CNTs were TUBALL™, supplied by OCSIAL Europe and their properties can be found in Davoodabadi et al. [5, 6]. The surfactant was a technical grade of sodium dodecylbenzenesulfonate (SDBS) produced by Merck KGaA. The utilized precursors were fly ash (Steag Power Minerals GmbH) and GGBS (Opterra GmbH); their properties are described in Davoodabadi et al. [7]. Sodium disilicate powder (Sikalon; Wöllner GmbH) was used to activate and geopolymerize the blend. Sulfuric acid and magnesium sulfate for the sensing measurements were diluted to 0.1 M from a stock solution of 98% ACS reagent sulfuric acid (Merck KGaA), and anhydrous magnesium sulfate powder (Merck KGaA), respectively.
2.2 Methods
The nanofluids were prepared by ultrasonication of the CNTs and SDBS in ultrapure water according to the procedures in Davoodabadi et al. [5,6,7]. The CNT concentration range spanned from 0.010 to 1.000 wt% of oxide mass and SDBS was added with the same mass as CNTs. The nanocomposites were fabricated with the formulation in Davoodabadi et al. [5,6,7]. The mixed slurries were cast into plastic molds with slot dimensions of 60 × 10 × 10 mm3 for 24 h. After demolding, the nanocomposites were cured in the chemical laboratory ambient conditions. Thereafter, the nanocomposites were heat treated (at 105 °C for 24 h) to eliminate any negative impact of water on the CNTs’ conductive network.
2.3 Characterizations
A programmed setup was used for the electrical properties and sensing measurements composed of a KEYSIGHT B2912A precision source/measure unit (SMU), a computer, and Grafana time-series database [5]. The received data in the form of the resistance \((\mathrm{R})\) in Ω were converted to resistivity (\(\uprho =\mathrm{R}.\mathrm{A}.{\mathrm{L}}^{-1}\)) in Ω.m and conductivity (\(\upsigma ={\uprho }^{-1}\)) in S.m−1 by applying the sensors’ cross-sectional area (A) and length (L). For further analysis, relative resistance \((\mathrm{RR}=100. \left({\mathrm{R}}_{1}-{\mathrm{R}}_{0}\right).{\mathrm{R}}_{0}^{-1})\) was used for sensor evaluations. A GeminiSEM 500 (Carl Zeiss QEC GmbH) was used for scanning electron microscopy imaging of the specimens’ cross section. The FEI Tecnai F30 (ThermoFisher Scientific) was used to conduct high resolution transmission electron microscopy (HRTEM imaging) of the samples.
3 Results and Discussion
3.1 Percolation Threshold
In the available literature, the sensing properties of geopolymers exploited the electrolytic (ionic) conductance of the composites because of their ion-rich structure and pore system [8,9,10,11,12]. However, investigated alkali-activated composites in this study are insulators and exhibit insufficient conductive (electronic) properties to act as a sensor. The measured inherent resistances of these composites were unsteady, in the range of mega ohm (≥10 MΩ). Because measurements are conducted on heat-treated specimens, the electrolytic conductivity of the ion-rich framework is assumed to be negligible. Sufficient inclusion of CNTs causes the resistance range of nanocomposites to descend abruptly from mega ohm (highly insulator character) to hundreds of ohms (highly conductive behavior). This proves that the electronic conductive network of CNTs has been generated, and the nanocomposites are percolated [13].
The correlation curve of the nanocomposites’ conductivity and CNTs’ concentration is depicted in Fig. 1. The observed increasing trend of conductivity corresponded to the required quantity of CNTs for establishing a functional conductive network, mostly in tube-contacting mode rather than the tunneling or hopping mode [13]. This conductive network of CNTs provides the alkali-activated matrix with a percolating transition zone between 0.070 wt% and 0.200 wt% as indicated by the inset in Fig. 1. With respect to percolation theory, such curves can be fitted with power regression models [14,15,16,17]. In addition to the investigated nanocomposites, CNT Portland cement-based nanocomposites have a relatively similar percolation trend, but their documented thresholds exhibit, naturally, non-conclusive values. Some of the documented percolating transition zones of CNT Portland cement-based nanocomposites are shown in Table 1 for comparison.
The most influential parameters on the percolation of nanocomposites are the CNTs’ structure (i.e., chirality, aspect ratio, waviness, and the number of shells) and CNTs’ tunneling resistance/distance. The fabrication methodology (applied surfactant, ultrasonication energy, mixing, and curing), which determines the 3D orientation, configuration, interconnection of CNTs, and geometry of agglomerates, further affects the percolating character of the nanocomposite [15, 16, 18,19,20,21]. Considering the percolation threshold as an outset, the preference of composite researchers is to maintain the nano-additives’ concentration as low as possible (i.e., low or ultra-low percolation thresholds), because high concentrations of nano-additives have a destructive impact on the microstructure and consequently on the mechanical properties of the nanocomposite [14, 22, 23] (Table 1).
Based on these arguments, to achieve a firm conductive network of CNTs, in which the nanocomposite is not so overloaded as to be destroyed by the additives and not too under-loaded to be an insulator, a concentration of 0.1 wt% was considered for the sensor fabrication. In Sect. 3.2. Sulfate discrimination, the selection of CNT concentration of 0.1 wt% as the percolation threshold is further validated. In comparison, a wide concentration range of 0.05–2 wt% was reported in the literature for sensing and smart applications of the Portland cement-based nanocomposites [27,28,29,30,31,32,33,34].
3.2 Sulfate Discrimination
The CNT alkali-activated nanocomposites sensing responses upon exposure to 90 µL (30 µL in each cycle) of 0.1 M \({H}_{2}{SO}_{4} \&\) \({MgSO}_{4}\) with CNT concentration ranging from 0.0 to 1.0 wt% are illustrated in Fig. 2. The response of the sensors upon exposure to different sulfate containing regimens was explored and compared. A range of CNT concentrations were considered to confirm the influence of the generating conductive percolated network of CNTs on the sensing behavior of the nanocomposites with respect to percolation analysis.
The nanocomposites with incorporation of 0.0 and 0.010 wt% exhibited fully insulating behavior (Fig. 2a, b). The responses were highly noisy and stochastic as expected from the ultra-low conductivity of these nanocomposites; the approximate magnitude was 3E-5 S·m–1 as shown in Fig. 1. With CNT incorporation of 0.025 wt% and 0.050 wt%, the conductivity rose sharply to almost 3E-2 and 1 S·m–1, respectively, and the responses were slightly functional but still not accurate (Fig. 2c, d). Considering the onset of the percolating area, at CNT concentration of 0.070 wt% the functional response of the sensors began at 0.075 wt% with sensor conductivity of ≈6 S·m–1 (Fig. 2e). From this point onwards, the CNT signals showed a regular configuration, which corresponded to the normal behavior of pristine p-type CNTs (Fig. 2e–j). The \({\mathrm{H}}_{2}{\mathrm{SO}}_{4} \&\) \({\mathrm{MgSO}}_{4}\) discrimination mechanism in the percolated area was mostly based on the difference in the signal shape and magnitude.
The correlations of maximum relative resistance and CNT concentration are plotted in Fig. 3. The main results to note were (i) the positive relationship of the relative resistance and CNT concentration, and (ii) the higher sensitivity of the nanocomposites towards \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\) exposure than \({\mathrm{MgSO}}_{4}\). Result (ii) means the sensors can discriminate \({\mathrm{SO}}_{4}^{2-}\) species introduced from two different sources (\({\mathrm{H}}_{2}{\mathrm{SO}}_{4} \&\) \({\mathrm{MgSO}}_{4}\)), by means of relative resistance as demonstrated in Fig. 3, and by signal configuration and shape as illustrated in Fig. 2. The CNTs’ signal differentiation was particularly recognizable in the percolating transition zone of the nanocomposites (between 0.075 and 0.250 wt%) shown in Fig. 2e–g.
3.3 Quantity Differentiation
The \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\) quantity differentiation potential of the sensors is shown in Fig. 4. For this purpose, the nanocomposites were fabricated with CNT inclusion of 0.1 wt% based on the percolation and sensing analyses. The same concentration regimen of \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\) (i.e., 0.1 M) was introduced in volumetric quantities of 90, 180, 270 µL (30, 60, and 90 µL, respectively in each cycle) to the sensors to evaluate the responses. The increments of relative resistance were approximately + 140% and + 60% with the volume increasing from 90 µL to 180 µL and afterwards to 270 µL, exhibiting a linear behavior.
3.4 CNTs’ Conductive Network
The CNTs’ network distribution and expansion are shown in Fig. 5. The addition of SDBS as surfactant for the dispersion of CNTs, entrained air bubbles into the alkali-activated microstructure. In addition, SBDS probably had a negative impact on the activating reactions and created a weaker microstructure. Nevertheless, the alkali-activated microstructure exhibited sufficient strength (compressive strength of 40 ± 2.48 MPa for 28-day nanocomposite) and mechanical performance. The main mechanism was the reinforcing effect of the CNTs because of their distribution (Fig. 5a), and crack covering and bridging abilities (Fig. 5b). Furthermore, this mode of interaction by CNTs has a secondary function, which is the formation of a conductive network (Fig. 5c). This network endows the nanocomposites with high electrical conductivity and consequently a sensing ability as explained in previously. The percolated conductive network of CNTs can be seen in the HRTEM images of Fig. 6. The network comprised overlapping CNT agglomerations, which formed directional pathways.
4 Conclusions
The present conceptual study has proposed a structural sensor for assessing the \({\mathrm{SO}}_{4}^{2-}\) sensing potential of CNT alkali-activated nanocomposites. The investigated discrimination criteria were CNT concentration, \({\mathrm{SO}}_{4}^{2-}\) bearing media (\({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\mathrm{ vs}.\mathrm{ Mg}{\mathrm{SO}}_{4}\), and analyte volumetric quantity \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\). The obtained results can be summarized as follows.
-
The percolating zone of the nanocomposites was between 0.07 and 0.20 wt% of CNT content.
-
The sensors can be fabricated by incorporation of 0.1 wt% of CNT into the alkali-activated matrix material based on the percolation threshold study of the nanocomposites.
-
The sensors exhibit differentiation behavior by variation of shape and magnitude of the obtained relative resistance.
-
There was a linear correlation between relative resistance and CNT concentration when the sensors were exposed to 0.1 M \({\mathrm{H}}_{2}{\mathrm{SO}}_{4} \&\mathrm{ Mg}{\mathrm{SO}}_{4}\). Similarly, the relationship between the relative resistance of the sensors and volumetric quantity of 0.1 M \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\) was linear.
-
The sensors exhibited a higher magnitude of relative resistance when exposed to 0.1 M \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\) compared with 0.1 M \({\mathrm{MgSO}}_{4}\).
-
The percolated sensors presented a response curvilinear shape upon \({\mathrm{H}}_{2}{\mathrm{SO}}_{4}\) exposure and a rectangular shape upon \({\mathrm{MgSO}}_{4}\) exposure.
References
Paul A, Rashidi M, Kim J-Y, Jacobs LJ, Kurtis KE (2022) The impact of sulfate- and sulfide-bearing sand on delayed ettringite formation. Cement Concr Compos 125:104323
Wang Y, Cao Y, Zhang Z, Huang J, Zhang P, Ma Y, Wang H (2022) Study of acidic degradation of alkali-activated materials using synthetic C-(N)-A-S-H and N-A-S-H gels. Compos B Eng 230:109510
Grengg C, Gluth GJ, Mittermayr F, Ukrainczyk N, Bertmer M, Guilherme Buzanich A, Radtke M, Leis A, Dietzel M (2021) Deterioration mechanism of alkali-activated materials in sulfuric acid and the influence of Cu: a micro-to-nano structural, elemental and stable isotopic multi-proxy study. Cem Concr Res 142:106373
Kobayashi M, Takahashi K, Kawabata Y (2021) Physicochemical properties of the Portland cement-based mortar exposed to deep seafloor conditions at a depth of 1680 m. Cem Concr Res 142:106335
Davoodabadi M, Liebscher M, Sgarzi M, Riemenschneider L, Wolf D, Hampel S, Cuniberti G, Mechtcherine V (2022) Sulphuric acid sensing of single-walled carbon nanotubes incorporated alkali activated materials. Compos Part B Eng
Davoodabadi M, Vareli I, Liebscher M, Tzounis L, Sgarzi M, Paipetis AS, Yang J, Cuniberti G, Mechtcherine V (2021) Thermoelectric energy harvesting from single-walled carbon nanotube alkali-activated nanocomposites produced from industrial waste materials. Nanomaterials (Basel, Switzerland) 11(5)
Davoodabadi M, Liebscher M, Hampel S, Sgarzi M, Rezaie AB, Wolf D, Cuniberti G, Mechtcherine V, Yang J (2021) Multi-walled carbon nanotube dispersion methodologies in alkaline media and their influence on mechanical reinforcement of alkali-activated nanocomposites. Compos B Eng 209:108559
Biondi L, Perry M, McAlorum J, Vlachakis C, Hamilton A, Lo G (2021) Alkali-Activated Cement Sensors for Sodium Chloride Monitoring. IEEE Sensors J 21(19):21197–21204
Biondi L, Perry M, McAlorum J, Vlachakis C, Hamilton A (2020) Geopolymer-based moisture sensors for reinforced concrete health monitoring. Sens Actuators B Chem 309:127775
McAlorum J, Perry M, Vlachakis C, Biondi L, Lavoie B (2021) Robotic spray coating of self-sensing metakaolin geopolymer for concrete monitoring. Autom Constr 121:103415
Vlachakis C, Perry M, Biondi L, McAlorum J (2020) 3D printed temperature-sensing repairs for concrete structures. Addit Manuf 34:101238
Saafi M, Gullane A, Huang B, Sadeghi H, Ye J, Sadeghi F (2018) Inherently multifunctional geopolymeric cementitious composite as electrical energy storage and self-sensing structural material. Compos Struct 201:766–778
Buroni FC, García-Macías E (2021) Closed-form solutions for the piezoresistivity properties of short-fiber reinforced composites with percolation-type behavior. Carbon 184:923–940
Khan T, Irfan MS, Ali M, Dong Y, Ramakrishna S, Umer R (2021) Insights to low electrical percolation thresholds of carbon-based polypropylene nanocomposites. Carbon 176:602–631
García-Macías E, D’Alessandro A, Castro- Triguero R, Pérez-Mira D, Ubertini F (2017) Micromechanics modeling of the electrical conductivity of carbon nanotube cement-matrix composites. Compos B Eng 108:451–469
Jang S-H, Hochstein DP, Kawashima S, Yin H (2017) Experiments and micromechanical modeling of electrical conductivity of carbon nanotube/cement composites with moisture. Cement Concr Compos 77:49–59
Zhang L, Ding S, Li L, Dong S, Wang D, Yu X, Han B (2018) Effect of characteristics of assembly unit of CNT/NCB composite fillers on properties of smart cement-based materials. Compos A Appl Sci Manuf 109:303–320
Wu D, Wei M, Li R, Xiao T, Gong S, Xiao Z, Zhu Z, Li Z (2019) A percolation network model to predict the electrical property of flexible CNT/PDMS composite films fabricated by spin coating technique. Compos Part B Eng 174:107034
Mahmoodi MJ, Vakilifard M (2019) CNT-volume-fraction-dependent aggregation and waviness considerations in viscoelasticity-induced damping characterization of percolated-CNT reinforced nanocomposites. Compos B Eng 172:416–435
Wang Y, Wang X, Cao X, Gong S, Xie Z, Li T, Wu C, Zhu Z, Li Z (2021) Effect of nano-scale Cu particles on the electrical property of CNT/polymer nanocomposites. Compos A Appl Sci Manuf 143:106325
Doh J, Park S-I, Yang Q, Raghavan N (2021) Uncertainty quantification of percolating electrical conductance for wavy carbon nanotube-filled polymer nanocomposites using Bayesian inference. Carbon 172:308–323
Wang J, Kazemi Y, Wang S, Hamidinejad M, Mahmud MB, Pötschke P, Park CB (2020) Enhancing the electrical conductivity of PP/CNT nanocomposites through crystal-induced volume exclusion effect with a slow cooling rate. Compos B Eng 183:107663
Kim H, Gao S, Hong S, Lee P-C, Kim YL, Ha JU, Jeoung SK, Jung YJ (2019) Multifunctional primer film made from percolation enhanced CNT/Epoxy nanocomposite and ultrathin CNT network. Compos B Eng 175:107107
Liu L, Xu J, Yin T, Wang Y, Chu H (2021) Improved conductivity and piezoresistive properties of Ni-CNTs cement-based composites under magnetic field. Cement Concr Compos 121:104089
Danoglidis PA, Konsta-Gdoutos MS, Shah SP (2019) Relationship between the carbon nanotube dispersion state, electrochemical impedance and capacitance and mechanical properties of percolative nanoreinforced OPC mortars. Carbon 145:218–228
Hong G, Choi S, Yoo D-Y, Oh T, Song Y, Yeon JH (2022) Moisture dependence of electrical resistivity in under-percolated cement-based composites with multi-walled carbon nanotubes. J Market Res 16:47–58
D’Alessandro A, Rallini M, Ubertini F, Materazzi AL, Kenny JM (2016) Investigations on scalable fabrication procedures for self-sensing carbon nanotube cement-matrix composites for SHM applications. Cement Concr Compos 65:200–213
Tian Z, Li Y, Zheng J, Wang S (2019) A state-of-the-art on self-sensing concrete: Materials, fabrication and properties. Compos B Eng 177:107437
Rao RK, Sasmal S (2021) Nanoengineered smart cement composite for electrical impedance-based monitoring of corrosion progression in structures. Cement Concr Compos:104348
Rao R, Sindu BS, Sasmal S (2020) Synthesis, design and piezo-resistive characteristics of cementitious smart nanocomposites with different types of functionalized MWCNTs under long cyclic loading. Cement Concr Compos 108:103517
Kim GM, Yang BJ, Yoon HN, Lee HK (2018) Synergistic effects of carbon nanotubes and carbon fibers on heat generation and electrical characteristics of cementitious composites. Carbon 134:283–292
Konsta-Gdoutos MS, Danoglidis PA, Falara MG, Nitodas SF (2017) Fresh and mechanical properties, and strain sensing of nanomodified cement mortars: the effects of MWCNT aspect ratio, density and functionalization. Cement Concr Compos 82:137–151
Dong W, Li W, Wang K, Han B, Sheng D, Shah SP (2020) Investigation on physicochemical and piezoresistive properties of smart MWCNT/cementitious composite exposed to elevated temperatures. Cement Concr Compos 112:103675
Zhan M, Pan G, Zhou F, Mi R, Shah SP (2020) In situ-grown carbon nanotubes enhanced cement-based materials with multifunctionality. Cement Concr Compos 108:103518
Author information
Authors and Affiliations
Corresponding authors
Editor information
Editors and Affiliations
Rights and permissions
Open Access This chapter is licensed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license and indicate if changes were made.
The images or other third party material in this chapter are included in the chapter's Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the chapter's Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
Copyright information
© 2023 The Author(s)
About this paper
Cite this paper
Davoodabadi, M. et al. (2023). Electrical and Sulfate-Sensing Properties of Alkali-Activated Nanocomposites. In: Duan, W., Zhang, L., Shah, S.P. (eds) Nanotechnology in Construction for Circular Economy. NICOM 2022. Lecture Notes in Civil Engineering, vol 356. Springer, Singapore. https://doi.org/10.1007/978-981-99-3330-3_29
Download citation
DOI: https://doi.org/10.1007/978-981-99-3330-3_29
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-99-3329-7
Online ISBN: 978-981-99-3330-3
eBook Packages: EngineeringEngineering (R0)