Abstract
The use of carbon nanotubes (CNTs) to reinforce cemented rockfill is attracting considerable interest due to the remarkable improvement in performance and the extremely low dose of the added nanomaterial. To reveal the enhancement mechanism of the CNTs on cemented rockfill, the acoustic emission (AE) characteristics of cemented rockfill specimens during the Brazilian split test were investigated. The results demonstrated that CNTs improved tensile strength by 17.2% and decreased the AE count. The nucleation and micropore-filling effects of the CNTs promoted the cement hydration reaction and formation of a denser structure, thereby improving resistance to loads. Meanwhile, finer pores avoid stress concentration, resulting in AE activity becoming more sparse. Finally, the AE b-value increased by 14.8%, which further indicated that the overall failure process was at a lower intensity.
You have full access to this open access chapter, Download conference paper PDF
Keywords
1 Introduction
Carbon nanomaterials, including carbon nanotubes (CNTs), graphene oxide and carbon nanosheets, have been widely recognized for their enhancement of cement-based composites [1, 2]. The strengthening mechanism of CNTs in cement-based composites has been the focus in recent decades [3, 4], and it is though physical properties such as extremely high mechanical strength and large specific surface area that CNTs fill microscopic pores in cement matrix and promote the development of hydration products [5]. The resulting compact microstructure greatly optimizes the macroscopic mechanical properties of cement-based composites, including compressive strength, impermeability and corrosion resistance [6, 7]. At the same time, the addition of CNTs is potentially a way to reduce CO2 emissions from cement production [8].
In construction and mining projects, cemented rockfill with higher mechanical properties is significant for structural stability and production safety. CNTs improve the mechanical strength of cemented rockfill materials [9], but due to the lack of sensitivity of current monitoring systems, the effect of CNTs on failure patterns during the loading process needs further research. Acoustic emission (AE) technology is a nondestructive testing method widely used in the study of the mechanical properties of rock materials [10]. During the failure process, the gradual development of microfractures will cause acoustic signals, which can be monitored by the AE system. The waveform of the AE signal reflects the microscopic failure pattern. For example, the RA (Rise time to Amplitude ratio) and AF (AE counts to Duration ratio) can be used as criteria for the type of failure [11]. Therefore, the AE technique is effective for studying the destruction mode of the cemented rockfill.
In this study, we add a very low content of CNTs with fly ash (FA) to partially replace cement in the cemented rockfill. The tensile failure strength of the specimens was measured by the Brazilian split test and simultaneously the AE system collected signals during the destruction process. Combing the AE activity, and the stress–-strain curve, the distribution and intensity of the failure events in each loading stage of the CNT-enhanced specimens were analyzed. The failure event accumulation of the specimen is discussed according to the peak and growth rate of the cumulative AE counts curve. The b-value in AE technology is calculated to characterize the severity of the overall failure process. The findings in this study promote the engineering application of CNTs and we discuss the enhancement mechanism of CNTs in cemented rockfill materials.
2 Methods
Waste coal gangue extracted from a coal mine in Shanxi province, China, was selected as the solid particles in cement rockfill. The composition of coal gangue does not react chemically with the cement. Ordinary Portland cement (PO. 42.5), conforming to the Chinese Standard GB-175-2007 [12], was the binder material. Multiwall CNTs (MWCNTs; manufactured by Nanjing XFNANO Materials Tec. Co., Nanjing City, Jiangsu Province, China) were added to the rockfill materials. Polycarboxylate superplasticizer was added to promote CNT dispersion in the suspension.
The preparation of CNT-enhanced cement rockfill samples mainly comprised the preparation of CNT–cement slurry and mixing of the slurry with solid particles. The process is detailed in our previous report [13]. A Ref-group and CNT-group were set in this study, and a 0.4 water-to-cement ratio was applied in both groups. In the CNT-group mortar, there was 20% FA with 0.05 wt% CNTs to replace 20% cement. The other preparation processes of the two groups were consistent.
We chose 28-day-old standard-cured disc samples with a diameter of 50 mm and a thickness of 25 mm for the Brazilian split tests. The loading rate was 0.10 mm/min. To avoid the influence of errors in the test and improve accuracy, three samples were selected for each group. During the loading process, the AE signals were monitored by a Micro-II AE system (developed by the American Physical Acoustic Corporation), as shown in Fig. 1. The AE threshold and frequency were set at 30 dB and 10 Msps, respectively.
3 Results
3.1 Mechanical Properties of Cemented Rockfill
After curing for 28 days, the peak tensile strength of the specimens is shown in Fig. 2. The peak strength of the CNT-group was 3.4 MPa, an increase of 17.2% compared with the Ref-group, indicating that CNTs significantly enhanced the ability of the sample to resist tensile stress, which was consistent with previous studies [14]. Higher tensile strength can reduce the risk of sudden failure and improve engineering safety.
The increase in tensile strength was attributed to the strengthening effect of CNTs in the cement matrix. CNTs show a bridging effect between microfractures in the cement matrix [15]. When the sample is under tensile stress, the high tensile strength of CNTs can help the cement matrix resist external stress and avoid microcrack development [16]. As the sample’s hydration reaction continued, the hydration products became more closely connected with the CNTs and the resultant compact internal structure enabled the specimen to resist failure and deformation.
3.2 Analysis of AE Activity During the Failure Process
The stress–strain curve and real-time AE signals of the samples are shown in Fig. 3. As the stress gradually increased, the stress–strain curve divided into four failure stages. In the initial compaction stage and elastic deformation stage, there was almost no fracture inside the sample, accompanied by sparse AE signals. During the plastic deformation stage, cracks gradually developed and the AE activity gradually became denser. When peak strength was reached, the samples suddenly produced a lot of AE counts, corresponding to the development of major fractures. In the post-peak stage, cracks continue to expand.
With the addition of CNTs to the cemented rockfill, the AE activity became sparse and AE counts decreased significantly during the failure process. The cumulative counts of the Ref-group reached 20(×103), much higher than in the CNT-group. At the peak strength point, the Ref-group showed a single and high-count AE event, whereas the CNT-group showed multiple peaks of AE activity. The reason for this phenomenon is the promotion of a dense microstructure by CNTs. The defect area is smaller, reducing the severity of failure, resulting in fewer counts and lower frequency of AE events, which leads to more gradual macro disruption.
The b-value reflects the ratio of the number of lower and higher grade AE events during the rock failure process, and can be calculated by the following equation [17]:
where A is the amplitude of the AE event, N(A/20) is the cumulative frequency of AE events with an amplitude ≥ A, and b represents the b-value.
According to Eq. 1, the b-value of the CNT-group reached 1.27, increasing 14.8% more than the Ref-group (Fig. 4), which reflects the AE activity being mostly concentrated at lower energy levels during the failure of the sample. The reason behind this phenomenon is that CNTs promote the development of hydration products to reduce the size of micropores, further avoiding the high energy release of cracks during loading.
4 Discussion and Conclusions
In this study, CNTs and FA were added to a cemented rockfill mix to investigate the production of environmentally friendly and high-workability materials. The tensile properties of the three specimens in each group were tested by the Brazilian split test and AE signals were monitored by a PCI-2 system. The failure mode pattern of the CNT-reinforced cement rockfill material was studied by the stress–strain curve and AE waveform.
In the Brazilian split experiment, the CNT-reinforced sample showed increased peak tensile strength by 17.2%. At the same time, the AE events became sparser and the count decreased, indicating that the intensity of destruction decreased. Finally, the addition of CNTs increased the b-value by 14.8%, which indicated that CNT-reinforced cemented rockfill material will have fewer high energy release destruction events, thereby making it a safer option.
References
Gao Y, Jing HW, Chen SJ, Du MR, Chen WQ, Duan WH (2019) Influence of ultrasonication on the dispersion and enhancing effect of graphene oxide–carbon nanotube hybrid nanoreinforcement in cementitious composite. Compos B 164:45–53
Yao X, Shamsaei E, Wang W, Zhang S, Sagoe-Crentsil K, Duan W (2020) Graphene-based modification on the interface in fibre reinforced cementitious composites for improving both strength and toughness. Carbon 170:493–502
Morsy M, Alsayed S, Aqel M (2011) Hybrid effect of carbon nanotube and nano-clay on physico-mechanical properties of cement mortar. Constr Build Mater 25(1):145–149
Li GY, Wang PM, Zhao X (2007) Pressure-sensitive properties and microstructure of carbon nanotube reinforced cement composites. Cem Concr Compos 29(5):377–382
Konsta-Gdoutos MS, Metaxa ZS, Shah SP (2010) Highly dispersed carbon nanotube reinforced cement based materials. Cem Concr Res 40(7):1052–1059
Liu C, Huang X, Wu Y-Y, Deng X, Zheng Z (2021) The effect of graphene oxide on the mechanical properties, impermeability and corrosion resistance of cement mortar containing mineral admixtures. Constr Build Mater 288:123059
Gao Y, Jing H, Zhou Z, Shi X, Li L, Fu G (2021) Roles of carbon nanotubes in reinforcing the interfacial transition zone and impermeability of concrete under different water-to-cement ratios. Constr Build Mater:272
de Souza FB, Yao X, Gao W, Duan W (2022) Graphene opens pathways to a carbon-neutral cement industry. Sci Bull 67:5–8
Wu J, Jing H, Gao Y, Meng Q, Yin Q, Du Y (2022) Effects of carbon nanotube dosage and aggregate size distribution on mechanical property and microstructure of cemented rockfill. Cem Concr Compos 127:104408
Zhao ZL, Jing HW, Wu JY, Shi XS, Gao Y, Yin Q (2020) Experimental investigation on damage characteristics and fracture behaviors of granite after high temperature exposure under different strain rates. Theor Appl Fract Mech 110:102823
Tragazikis IK, Dassios KG, Exarchos DA, Dalla PT, Matikas TE (2016) Acoustic emission investigation of the mechanical performance of carbon nanotube-modified cement-based mortars. Constr Build Mater 122:518–524
Standard C (2007) Common portland cement (text of document is in Chinese). GB 175. Standards Press of China, Beijing
Gao Y, Jing H, Yu Z, Li L, Wu J, Chen W (2022) Particle size distribution of aggregate effects on the reinforcing roles of carbon nanotubes in enhancing concrete ITZ. Constr Build Mater 327:126964
Siddique R, Mehta A (2014) Effect of carbon nanotubes on properties of cement mortars. Constr Build Mater 50:116–129
Tyson BM, Abu Al-Rub RK, Yazdanbakhsh A, Grasley Z (2011) Carbon nanotubes and carbon nanofibers for enhancing the mechanical properties of nanocomposite cementitious materials. J Mater Civ Eng 23(7):1028
Naqi A, Abbas N, Zahra N, Hussain A, Shabbir SQ (2019) Effect of multi-walled carbon nanotubes (MWCNTs) on the strength development of cementitious materials. J Mater Res Technol 8(1):1203–1211
Colombo IS, Main I, Forde M (2003) Assessing damage of reinforced concrete beam using “b-value” analysis of acoustic emission signals. J Mater Civ Eng 15(3):280–286
Acknowledgements
This study was supported by Yunlong Lake Laboratory of Deep Underground Science and Engineering Project (No. 104023002), National Natural Science Foundation of China (No. 52074259), Assistance Program for Future Outstanding Talents of China University of Mining and Technology (No. 2022WLJCRCZL050) and Postgraduate Research & Practice Innovation Program of Jiangsu Province (No. KYCX22_2580).
Funding
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Author information
Authors and Affiliations
Contributions
The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript.
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Open Access This chapter is licensed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license and indicate if changes were made.
The images or other third party material in this chapter are included in the chapter's Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the chapter's Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
Copyright information
© 2023 The Author(s)
About this paper
Cite this paper
Yu, Z., Jing, H., Gao, Y., Wei, X., Wang, A. (2023). Effect of Carbon Nanotubes on the Acoustic Emission Characteristics of Cemented Rockfill. In: Duan, W., Zhang, L., Shah, S.P. (eds) Nanotechnology in Construction for Circular Economy. NICOM 2022. Lecture Notes in Civil Engineering, vol 356. Springer, Singapore. https://doi.org/10.1007/978-981-99-3330-3_54
Download citation
DOI: https://doi.org/10.1007/978-981-99-3330-3_54
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-99-3329-7
Online ISBN: 978-981-99-3330-3
eBook Packages: EngineeringEngineering (R0)