Abstract
Complex oxides provide a versatile playground for many phenomena and possible applications, for instance, high-temperature superconductivity, magnetism, ferroelectricity, metal-to-insulator transition, colossal magnetoresistance, and piezoelectricity. The origin of these phenomena is the competition between different degrees of freedom such as charge, orbital, and spin, which are interrelated with the crystal structure, the oxygen stoichiometry, and the doping dependence. Recent developments not only in the epitaxial growth technologies, such as reactive molecular beam epitaxy, but also in the characterization techniques, as aberration-corrected scanning transmission electron microscopy with spectroscopic tools, allow synthesizing and identifying epitaxial systems at the atomic scale. Combination of different oxide layers opens access to interface physics and leads to engineering interface properties, where the degrees of freedom can be artificially modified. In this review, we present different homo- and hetero-epitaxial interfaces with extraordinary structural quality and different functionalities, including high-temperature superconductivity, thermoelectricity, and magnetism.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Complex oxide hetero-structures create a multidirectional platform for the emergence of significant properties stemming from the strong interplay between the lattice, spin, orbital, and charge degrees of freedom [1, 2]. The easily modifiable crystal structure and tailorable oxygen sublattice of the generally studied ABO3 perovskite structure, which is composed of corner-sharing BO6 octahedra and body-centered A-site cations surrounded oxygen anions, bring the advantage of fine-tuning properties through picometer-scale modifications in the lattice [3]. Especially after the discovery of high-temperature superconductivity [4], the epitaxial growth of cuprate-based systems such as La2−xSrxCuO4 (LSCO) [5, 6], YBa2Cu3O7−δ (YBCO) [7,8,9], DyBa2Cu3O7−δ (DBCO) [10], Bi2Sr2Can−1CunO2n + 4 (BSSCO) [11], received a strong interest, together with the other functional oxide compounds with different functionalities [12,13,14]. In addition to the synthesis of single-phase films, the epitaxial growth of such complex oxides in the form of multilayered systems further yields the emergence of novel interfacial phenomena [15,16,17], which are not present in the constituent layers alone. These systems provide not only a wide range of applications with prominent functionalities such as ferroelectricity [18, 19], emergence of 2D electron gas [20], thermoelectricity [21], magnetism [22,23,24], and superconductivity [25], but also understanding the fundamental nature of the underlying complex phenomena. The quality of the multicomponent oxide thin films can be defined as a function of the stoichiometry, the structural quality and the extent of present defects, whereas the interface sharpness has been realized as the most critical factor for novel applications. An intriguing example is the high-temperature interface superconductivity (HT-IS) emerging at the interface between non-superconducting undoped and overdoped copper oxide layers [26], for which the absence of a specific accepted theory of high-temperature superconductors (HTS) fosters the strong interest.
In general, the precision of the epitaxial growth techniques determines the limits of the synthesis and accordingly the control and the understanding of the materials’ properties. Recent technical developments in epitaxial growth technologies pave the way for synthesizing high-quality oxide hetero-structures with atomic layer precision. Different physical deposition techniques, such as pulsed laser deposition (PLD) [27,28,29,30,31], reactive sputtering, and reactive molecular beam epitaxy (MBE) with in situ reflection high-energy electron diffraction (RHEED) [32,33,34,35,36,37], have been comprehensively utilized. The reactive ozone-assisted MBE can be considered as the most powerful technique, since it allows high-quality fabrication with great variability, low-energy of impinging atoms, and layer-precise control of the growth [38], which brings advantages on structural quality and interface sharpness [39]. The combination of such unique deposition methods with at least one foremost characterization technique is an inevitable step for further progress in the field of oxide hetero-structure engineering, especially for interface-focused research. In particular, cuprate-based hetero-interfaces are impressive systems with the possibility to emerge the superconducting state, which is substantially sensitive to material characteristics, e.g., film stoichiometry and the presence of defects (impurities, oxygen vacancies). Complimentary characterization methods such as in situ RHEED [40,41,42,43], atomic force microscopy (AFM), high-resolution X-ray diffraction [44, 45], together with different spectroscopic methods [46,47,48,49,50,51,52,53], identify the crystal quality, the surface roughness, the stoichiometry, and the electronic structure. Additionally, measurements of superconducting transitions via the two-coil mutual inductance [26] or the electrical resistance further reflect the quality of the MBE synthesis. Consequentially, the atomic-layer precise fabrication of these systems requires atomic-resolution identification. In this context, one prominent tool for interface characterization is aberration-corrected scanning transmission electron microscopy (STEM) [54,55,56] with atomic-resolution imaging and spectroscopy capabilities.
In this work, we present a brief overview of different complex oxide hetero-structures fabricated by ozone-assisted MBE (Fig. 1a) with precise atomic layer control, i.e., La2CuO4, La2−xAxCuO4 (A = Ca, Sr, Ba), La2−xSrxNiO4, LaNiO3, and SrMnO3-LaMnO3, in addition to the comprehensive recent achievements in HT-IS in LCO-based systems. The aberration-corrected STEM (Fig. 1b) with the position-sensitive atomic-resolution characterization capability was used to determine the interfacial quality. This review is structured as follows: In Chapter 2, we present the growth and characterization of high-quality single-phase La2CuO4 (LCO) films together with underlining the importance of the oxygen content as well as a way to handle oxygen exchange dynamics through high-temperature consideration of the electrical properties. In Chapter 3, we overview the homo-epitaxial HT-IS including previous results from the Brookhaven group as well as our recent studies focusing on the influence of the cationic radii on the interface sharpness of metal-insulator bilayers and associated physical properties, as well as the asymmetric distribution of the cations across the Sr delta-doped layer in a LCO matrix. The hetero-epitaxial cuprate-nickelate and cuprate-manganite interfaces are described in Chapter 4, with considerations of HT-IS, layer thickness dependence of electrical properties, and the design of superconducting-magnetic individual interfaces, respectively. Finally, the summary and outlook are presented in Chapter 5.
2 Single-Phase Films
The initial challenge in epitaxial complex oxide hetero-structures is to satisfy the sample quality, since various parameters jointly determine the crystal structure, the interface sharpness/roughness, and the correlated properties of these systems. Hence, the first step is to achieve high-quality single-phase epitaxial films. Herewith, we briefly touch on the critical parameters for the oxide thin film growth. The fundamental distinction of the epitaxial films from bulk single crystals is the presence and the explicit involvement of the substrate, which points the structural properties of the epitaxial films. The choice of the substrate can yield different properties by modifying the crystal structure of the thin epitaxial films via inducing small lattice distortions [57, 58]. From one side, the lattice mismatch between the epitaxial film and the substrate should be relatively small and favorable for forming a crystal with the minimum number of defects, for instance, oxygen vacancies [59, 60] and misfit dislocations [61, 62]. On the other side, the substrate-induced strain should be suitable for creating novel functionalities and possible improvements. Furthermore, the oxidation conditions, namely the substrate temperature and the oxidant pressure, which mutually relate with the stoichiometry and/or the composition control, play a crucial role in the correct phase formation as well [63]. The stoichiometry control during the growth is challenging due to the multicomponent composition and requires the management of each atomic flux with high precision to avoid any secondary phase precipitate formation. The initial layer formation at the interface with the substrate and the sequence of the deposited atomic layers should also be taken into consideration in the layer-by-layer MBE growth and for real-time observation of the growth, RHEED has been mainly utilized, which provides primary information about the crystal quality of surface layers and the presence or absence of secondary phase precipitates.
Let us consider the MBE synthesis of hole-doped La2−xAxCuO4 (LACO) epitaxial thin films, which are classical HTS systems with a single CuO2 plane separated by the charge reservoir La-O blocks in the elementary unit cell, where x indicates the concentration of aliovalent A2+ dopant ion. Advantageously, the wide doping range of the system leads to exploring the complete phase diagram from the undoped insulating parent La2CuO4 compound with antiferromagnetic order (AFM) to the overdoped non-superconducting metallic compound [64, 65]. The carrier concentration in this system is regulated by the substitution of La3+ ion by the dopant ions (e.g., Ca2+, Sr2+, Ba2+) and/or by the intercalation of oxygen interstitials. The superconducting dome for Sr- and Ba-doped LCO is obtained within a certain concentration range of hole doping, p, i.e., 0.06 ≤ p ≤ 0.26 and the highest Tc (≈ 35 K) is realized in the optimum-doped compound with the hole concentration of p ≈ 0.16 [66,67,68]. Note that the concentration of the dopant, x, is not exactly equal to the hole carrier concentration, p. The ratio between p and oxygen concentration depends on the corresponding formation energies, and the formation of oxygen vacancies can compensate the increase of the dopant concentration, especially in the overdoped regime [69]. While the doping concentration of Sr and Ba ions can be varied within a wide range (0 ≤ x ≤ 1.4) [70], the solubility limit, x, of Ca as dopant in La2−xCaxCuO4 (bulk polycrystalline) is restricted to x ≈ 0.1 and the maximum superconducting transition temperature achieved is Tc ≤ 20 K [71, 72]. In the case of thin films, for optimal doping (x ≈ 0.16) of Sr- and Ba-doped thin films, the highest Tc ~ 50 K has been reported, when the films are deposited on LaSrAlO4 (LSAO) substrates [6, 73,74,75]. A massive number of reports have been devoted to Sr- and Ba-doped LCO epitaxial films; however, a comprehensive study of Ca-doping in epitaxial LCCO films is still missing, while the only successful initiation of Ca doping in overdoped-undoped (LCCO-LCO) bilayers has been reported [76].
Concerning the substrate-induced strain and Tc relationship, due to the lattice constant mismatch between the LSCO film and the LSAO (001) substrate (aLSAO = 3.755 Å), which is 0.5% smaller than the lattice constant of the Sr optimum-doped bulk LSCO (001) [(aLSCO = 3.777 Å)], the film is under compressive strain that results in the highest Tc ~ 45 K. On the other hand, for instance, SrTiO3 (STO, aSTO = 3.905 Å) substrate, which has a 3% larger in-plane lattice constant, induces tensile strain to the optimum-doped LSCO epitaxial film and Tc is significantly reduced down to ~ 20 K [70, 77]. Another criterion, heavily affecting the final properties of complex oxides, is the contribution of oxygen and related species, e.g., oxygen vacancies and oxygen interstitials [78,79,80,81,82,83]. For example, oxygen interstitials can play the role of dopants and contribute to the conductivity and superconductivity in LCO-based compounds, while the formation of oxygen vacancies suppresses superconductivity. Recently, the experimental evidence of the increase of oxygen vacancies in the apical positions (of MBE-grown LSCO films), after low-temperature vacuum annealing and their variation as a function of Sr doping in highly oxidation environment, has been reported by using confocal Raman spectroscopy [84].
Considering the present understanding and taking the advantage of the atomic-layer precise MBE growth, we have synthesized LCO-based compounds with different dopants (Ca2+, Sr2+, Ba2+) and varying doping concentration on LSAO substrates, which favors the highest Tc. Note that Ca2+, Sr2+, and Ba2+ ions have the same valence state but different ionic radii, i.e., 118 pm, 131 pm, and 147 pm, corresponding to a ninefold coordination [85], respectively. The resultant mismatch with the host La3+ cation having an ionic radius of 121 pm is − 2.47%, + 8.3%, and + 21.5%, which consequently provides different chemical pressures in the crystal structure. In the case of Ba doping, single-phase LBCO epitaxial films grown on LSAO (001) substrates are characterized by rough surfaces with the presence of secondary phase precipitates containing excess Ba, as confirmed by Auger electron spectroscopy (AES), and also the critical thickness of the nucleation exhibits a linear dependency on Ba concentration [76]. The best results obtained for Sr-doped LCO epitaxial films grown by our MBE system are comparable with results from other groups [5, 6, 70, 86]. Furthermore, we have successfully synthesized precipitate-free Ca-doped LCO epitaxial films on LSAO (001) substrates with broad doping range up to x = 0.6 and Tc ≈ 35 K at the optimum doping concentration with x = 0.16. The related report will be published elsewhere. The stabilization of Ca-doped LCO films and the segregation of Ba on the topmost surface result from the interplay between compressive strain induced by the LSAO substrate and the chemical pressure due to the size of dopant ions.
Figure 2a shows an example RHEED image after a completed deposition of a La2CuO4 unit cell showing a characteristic surface reconstruction pattern. Real-time control of RHEED pattern is used for fine control of the growth, in particular the stoichiometry and surface roughness. The transport measurements of a 30 monolayers (MLs) thick optimum-doped LSCO film, i.e., the electrical resistance and the imaginary part of the mutual inductance, as a function of temperature are displayed in Fig. 2b. The superconducting transition (blue) is very sharp, Tc (R = 0) ≈ 43 K and the half width of the imaginary part (black) of the mutual inductance (T ≤ 1 K) confirms the film uniformity. These results (obtained without using a buffer and/or protection layers) are comparable with the results reported by the Bozovic group from the Brookhaven National Laboratory, USA [87]. The high structural quality of the film is confirmed by atomic-resolution STEM-HAADF imaging. The LSCO film (brighter) is distinguished from the LSAO substrate (darker) exhibiting a perfect coherent interface (Fig. 2c).
High-quality LSCO epitaxial films are synthesized in a vastly oxidized environment, which is achieved via the delivery of pure ozone by evaporation of liquid ozone from a distilled system. The typical substrate temperature is ~ 650 °C according to the radiative pyrometer reading and the chamber pressure is ~10−5 Torr. The highest Tc value of the films suggests that most of the oxygen positions in the LSCO crystal structure are occupied by oxygen ions. The undoped LCO thin film grown under these conditions is superconducting with Tc > 40 K due to the intercalation of oxygen interstitials. In the LSCO unit cell, there are three unequal oxygen positions with different binding energies: (i) the oxygen atoms in the CuO2 plane, (ii) the apical oxygen atoms, and (iii) the oxygen interstitial(s). There are different ways to govern the oxygen content such as post-growth annealing in vacuum or oxygen/ozone [88] and post-growth electrochemical doping [78, 83, 89, 90]. Nevertheless, since the thermogravimetric analysis (TGA) is not applicable for such thin films to evaluate the amount of oxygen due to their small volume, another method should be used to qualitatively verify the oxygen concentration. For this, we measure the electrical conductivity of a single LCO film in the temperature interval 300 K < T < 800 K (see Fig. 3) [91]. The decrease of the electrical conductivity at 300 K < T < 500 K (region 1) is ascribed to the loss of non-equilibrium interstitial oxygens, which, accordingly, results in a decrease of the number of holes. Oppositely, in the region 2 (i.e., 500–650 K), the oxygen content in equilibrium increases with increasing temperature similar to what has been reported in Ref. [82], whereas kinetic effects start to disappear as the temperature is increased further (region 3, T > 650 K). However, in the “colder” region for T ≤ 550 K, the oxygen atoms are quenched, and the system gets stable. Herewith, we show that the oxygen concentration of complex oxides, which have a strong influence on transport properties, can be examined through high-temperature conductivity measurements, as we discussed for undoped LCO films. Since examining the electrical properties above room temperature is a promising way to investigate oxygen exchange dynamics, a possible extension of this method can be conducting the experiments under different oxygen/ozone pressure.
3 Diverse Epitaxial Design
Thus far, we have presented high-quality L(S)CO epitaxial films grown by ozone-assisted MBE. Analogously, all other oxide hetero-structures synthesized by our MBE system have similar distinguished characteristics from the point of stoichiometry, crystal structure, and minimal concentration of oxygen defects. Fortunately, with the advantage of atomic-layer precise controlled growth, different deposition schemes can be further constructed utilizing in situ RHEED especially at the distinct layer transitions.
The unit cell of the intrinsically layered LCO structure comprises two molecular layers and each molecular layer is built up of two LaO and one CuO2 atomic layers. Thus, employing the layer-by-layer deposition scheme, this layered oxide compound can be formed by using either in La-La-Cu or in Cu-La-La deposition sequences. However, the deposition of the metals in oxidation conditions and the layer-by-layer regime lead to the formation of nanoscale metal oxides: La2O3 and CuO. The 214–LCO structure is a result of the surface chemical reaction between these elementary oxides, which is derived by the electronegativity of the constituent metals. Therefore, the proper deposition sequence is La-La-Cu (see Fig. 4a) instead of Cu-La-La, as the Cu atoms with the largest electronegativity pick up the oxygen from La2O3 and form CuO2 planes generating the 214 building block. In addition to the alternation of single oxide layers in a single-phase compound, a variety of multilayers, for instance bilayers (Fig. 2b), (or multilayers in the case of more repetitions) or two-dimensional doping (so-called δ-doping), in which a selected single metal oxide atomic layer can be substituted with another metal (i.e., dopant), can be designed as sketched in Fig. 2c.
In the case of multilayer synthesis, one can define the multilayer structure either as homo-epitaxial or as hetero-epitaxial depending on the constituent layers. In case the multilayer is composed of epitaxial layers of the same material with the same crystal structure but different doping levels, the structures are called homo-epitaxial structures. On the other hand, when the multilayer is built up by contacts of different materials, e.g., by stacking of cuprates and nickelates, or cuprates and manganates, or nickelates and manganates, with different chemical formula and crystal structure, the structures are called hetero-epitaxial. Note that for both homo-epitaxy and hetero-epitaxy, the multilayers can be grown on the substrate of different materials, in such a situation the growth of the initial layers is always hetero-epitaxy.
4 Homo-Epitaxy and HT-IS of La2CuO4
A milestone in the field of LCO-based HTS was reached in 2008 by the discovery of interface superconductivity between strongly overdoped metallic (M) LSCO and undoped insulating (I) LCO layers, which are not superconducting when taken alone [26, 94]. It is also shown that the superconducting transition temperature depends on the layer sequence of the M, I, and superconducting (S) layers. Further details can be found in the reviews devoted to this HT-IS phenomenon [86, 95, 96] and the original references therein. Herewith, we summarize the main findings and conclusions:
- i.
I-M bilayers exhibit lower Tc ≤ 15–20 K as Tc for M-I and M-S bilayers, where Tc ≈ 30–36 K and Tc ≈ 51 K can be achieved, respectively. (Note that S indicates the superconducting LCO layer after post-annealing in ozone atmosphere).
- ii.
The thickness of the superconducting interface layer is very thin and confined to a few CuO2 planes. Zn tomography [94] enabled to pinpoint the exact position of the superconducting CuO2 plane with the highest Tc.
- iii.
The possible mechanism due to the nominal La-Sr intermixing at the interface has been ruled out by several independent experiments including in situ time-of-flight ion scattering and recoil spectroscopy during growth (TOF-ISARS) and high-resolution STEM [26]. The cation intermixing is confined within one unit cell from the nominal interface as supported by the real-time in situ RHEED observations during the growth.
- iv.
The importance of the crystal structure in I-M, M-I, and M-S bilayers has been shown by Butko et al. [97] via high-resolution X-ray diffraction studies demonstrating the pseudomorphic growth of the top layer in both M-I and I-M bilayers. Importantly, Tc is linearly dependent on the c-axis lattice parameter. The larger the c-lattice parameter, the higher Tc. A similar relationship between the c-lattice parameter and Cu-O distances has been also reported for single-phase LSCO films [6, 98], and besides, the Coherent Bragg Rod Analysis (COBRA) method for M-I bilayers revealed another structural effect. An increase of the copper-apical oxygen interatomic distances starting from the nominal M-I interface towards the bilayer surface is substantiated [99, 100]. These structural results have been discussed in a frame of a long-range “Madelung strain” effect ascribed to strong Coulomb interaction between the layers, which is mildly screened in growth direction [97, 101].
- v.
Finally, a charge transfer mechanism due to the chemical potential difference between the overdoped and undoped cuprate layers has been proposed for HT-IS in M-I, I-M, and M-S bilayers. The phenomenological model (based on the Poisson equation) for the electrostatic potential is employed to determine the charge profile across the interfaces. Taking the doping dependence of the chemical potential μ(p) for the LSCO compound based on angle-resolved photoemission spectroscopy (ARPES) results [102], the anomalous independence of Tc for HT-IS on the doping level of the M layer in M-I bilayers was supported [103]. The open question is the μ(p) independency in the pseudogap regime (from undoped to optimum doping level), while μ is linearly dependent in the overdoped regime. Several mechanisms have been proposed (e.g., Ref. [104]); however, this is out of the scope of this review.
In addition to above-mentioned research, we further utilized the advantages of the layer-by-layer MBE technique. Bauitti et al. [105] reported a new approach for the design of epitaxially grown HTS of cuprates and showed that when two-dimensional doping, i.e., δ-doping, which is the substitution of a selected La-O layer with a Sr-O layer during the epitaxial growth, is applied to the LCO matrix, an asymmetric distribution of the dopant is present [105, 106]. For such type of doping, the asymmetric dopant distribution profile generates two different types of HTS mechanisms at each side of the interface. While in the growth direction, where the Sr distribution is wide and accompanies to the hole distribution, “conventional doping” is the main mechanism. On the other side of the interface, which has found to be sharper, the dopant, i.e., Sr, and the charge carrier distribution profiles are decoupled, and such decoupling results in a “space-charge” region inducing HTS. Further details can be found in Ref. [105]. The effect of the cation size and the growth temperature on this asymmetric profile has been further studied with atomic-resolution STEM for analogous systems [107], substantiating the fact that although the cation size mildly affects the dopant distribution width in both growth and substrate directions, the asymmetric dopant distribution profile is present and independent of the cation size.
Since the importance of the crystal structure has been demonstrated for HT-IS, the chemical pressure based on the dopant size is expected to perturb the crystal structure and correspondently to modify electronic and superconducting properties. Dopant size effects on the HT-IS were studied by Suyolcu et al. [76], and it has been demonstrated that although HTS can be obtained (Fig. 5a) by employing dopants with different sizes but same valences (i.e., Sr2+, Ba2+, and Ca2+), depending on the interface structure, both “interfacial” and “conventional” HTS can be realized. In particular, although sharp interfaces were achieved via Ca and Sr doping (in M layer) that confined the HTS into 1–2-nm scale, due to the strong surface segregation of Ba (first observed during the growth, Fig. 5b) for Ba-doped M-I bilayers, the HT-IS is hindered as a consequence of the randomly distributed dopants within the entire sample. For the latter case, the bilayer with high epitaxial quality (Fig. 5c) turns into a conventionally doped LCO system and most of the layers were found to be superconducting. Furthermore, when the local octahedral distortions, i.e., apical O-O interatomic distances, are quantitatively investigated and associated with the dopant distributions, the correlation with local Jahn-Teller distortions is enlightened [93]. While in the case of sharp interfaces (i.e., Ca and Sr doping), the O-O interatomic distances increase sharply after the nominal M-I interface, anti-Jahn-Teller distortions dominates the structure for Ba doping due to the wide Ba distribution leading to a reduction of the apical O-O interatomic distances [109]. As an example, a superimposed image of simultaneously acquired STEM high-angle annular dark-field (HAADF) and STEM-ABF images is displayed in Fig. 5d. These recent studies, including the 2D-doped LCO structure and a comparative study of dopant size effects on HT-IS, demonstrated the significant role of intermixing at interfaces, which was neglected in previous studies: The interfacial intermixing has an impact on the local crystal structure and, correspondingly, on the physical properties.
5 Hetero-Epitaxy of La2CuO4
In addition to homo-epitaxial oxide systems, which concern the doping dependency of different physical properties, hetero-epitaxial systems provide a fundamental playground for device fabrication and possible applications. Certainly, to fabricate devices [110, 111], it is a prerequisite to combine several materials, e.g., superlattices, in which apprehending the hetero-epitaxial interfaces is momentous to interpret and improve the underlying structural and physical properties. Hence, one needs to zoom in on the interfaces, not only because of the fact that complex oxides are characterized by ultra-short characteristic length scales such as the Debye screening length or the superconducting coherence length, but also the nanoscopic distortions at interfaces can profoundly affect device properties.
One recent example of hetero-interface engineering by oxide MBE is the HT-IS with a critical temperature up to Tc ≈ 40 K at LCO–La2−xSrxNiO4 (LSNO) multilayers (Fig. 6a) [112]. Note that LCO and LSNO compounds share the same Ruddlesden-Popper 214-crystal structure, and the electronic phase transformation can be achieved by hole-carriers doping by the substitution of the La site with a Sr dopant. It is revealed that Tc of such LCO-LSNO hetero-structures can be tuned by changing the doping level x in the LSNO layer or by varying the LCO thickness. The conditions to emerge HT-IS are the following: The critical doping level in the LSNO layer for a constant LCO layer thickness, N = 2.5, is x > 0.5 and the critical LCO thickness for constant x = 1.3 is N ≥ 1.5 unit cells, while the highest Tc > 30 K was obtained for 2.5 < N < 4.5, with N as the number of unit cells in the crystallographic c direction. For larger N corresponding to larger thicknesses, Tc saturates at around 25 K. Both interfaces, i.e., LCO-LSNO and LSNO-LCO, have been examined by aberration-corrected STEM and the structurally coherent interfaces are substantiated as presented in Fig. 6d, whereas STEM-EELS investigations revealed a certain redistribution of both A-site (La, Sr) and B-site (Cu, Ni) cations. In particular, although the LCO (bottom)–LSNO (top) interface is found to be sharp, an obvious Sr redistribution in the LCO phase in growth direction is detected, which slightly changes depending on the doping level in the LSNO layer. The details are discussed in Ref [112]. Lastly, the broad resistance transition to the superconducting state at such high-onset temperature (similar to optimum-doped LSCO) and the reduced Meissner effect should also be pointed out, since this is an indirect evidence of the inhomogeneous superconducting interface with nanoscale superconducting puddles as a consequence of the interface intermixing.
As discussed earlier in the text, different parameters have a strong impact on the interfacial structure, and an intermixing layer with a thickness of 1–2 unit cells is present at the interfaces of the 214–214 structures. Interfaces of oxide layers with different crystal structures, e.g., 214 pseudo-tetragonal and 113 cubic-perovskite, can be further designed. An intriguing example with contacts of insulating 214-LCO and metallic 113-LaNiO3 (113-LNO) multilayers (Fig. 6b) has been recently studied for examining the thermoelectric and transport properties [91]. The dependency of the transport properties on the thickness of the constituent layers was revealed. As the individual layers’ thicknesses are reduced, the Seebeck coefficient changes the sign and the electrical conductivity is decreased. High-resolution STEM imaging substantiated that a solid solution of La2(Cu,Ni)O4 with 214 crystal structure forms, when the thickness of the 113-LNO layer is decreased down to 2 unit cell. This length scale is comparable with the critical length of elemental intermixing, while for the thick LNO layer, the structural (Fig. 6e) and also the chemical abruptness of the interfaces has been visualized, when the nominal LNO layer thickness is locked to eight unit cells [91].
Another prominent example of 214 and 113 crystal structure junctions is the interface between superconducting LSCO and ferromagnetic manganite La0.66Sr0.33MnO3 (LSMO) layers [114]. Here, we focus on cuprate-manganate heterostructures (Fig. 6c) and present individual superconducting (S) cuprate and ferromagnetic (F) manganate hetero-interfaces. Due to the incompatibility of ferromagnetism and superconductivity, this interface is a playground to study unconventional proximity effects [115, 116]. For similar, i.e., cuprate-manganate, oxide hetero-structures, the antiferromagnetic coupling driven by orbital reconstruction and charge transfer emerging at the interface has been reported [117]. The main challenge of such design is preserving both superconducting and ferromagnetic properties in the multilayers with an appropriate interface quality. Recently, it was shown that the perpendicular exchange bias in L(S)CO-L(S)MO hetero-structures is caused by the antiferromagnetic interaction between copper and manganese ions at the interface. The magnitude of the perpendicular exchange bias was systematically tuned by adjusting the doping level of cuprate layers [113], where all the superlattices were prepared with analogue ferromagnetic layers (i.e., 2 × SrMnO3 (SMO) + 4 × LaMnO3 (LMO) layers) [118, 119]. Additionally, the doping level of LCO layers was varied utilizing the atomic layer-by-layer MBE in order to point the charge transfer scenario. To illustrate the quality of the cuprate-manganate interfaces, a representative high-resolution STEM-HAADF image is presented in Fig. 6f. The sharp and structurally coherent interface between 214 pseudo-tetragonal [92] and 113 cubic structures is discernible. The darker contrast on the image corresponds to the SMO layer due to the weaker Z-contrast stemming from lighter Sr ions compared with the heavier La. The chemical intermixing and physical properties of these interfaces will be published elsewhere.
6 Concluding Remarks and Outlook
During the last decade, significant progress has been achieved in the field of complex oxide hetero-structures, albeit there is still a huge room to explore. Triggered by the continuous development of the atomically precise deposition technologies, the quality of not only the oxide thin films but also the interfaces has improved drastically. In this review, we touch on several examples of epitaxial design including HTS at the interfaces of overdoped and undoped LCO layers, Sr delta-doped LCO structures and heavily Sr-doped LSNO and undoped LCO layers and the realization of abrupt interfaces between different crystal structures, e.g., tetragonal 214 and cubic perovskite 113, are presented.
Utilizing the ozone-assisted layer-by-layer oxide MBE synthesis, one can manipulate the layer sequences with atomic-layer precision and also tune the interface properties, correlatively. Aberration-corrected STEM with atomic-resolution imaging and spectroscopic tools allow the identification of individual atomic columns in the synthesized structures: The crystal structure across the oxide interfaces, where the novel phenomena emerge, is structurally coherent and well defined, while the chemical intermixing is present in most of the cases. Taking into account that the intrinsic physical properties of the complex oxides are a result of the combination of the crystal structure symmetry and doping, the observation of perfect interfaces with confined dopant distribution profiles rises a fundamental question on whether the interface properties are the consequences of only doping profiles or that some other non-trivial mechanisms are involved as well. Independent on the answer of this query, we do have the technologies to fabricate complex oxide hetero-structures with different functional properties that can be used in future applications. Nevertheless, the acceptance of this fundamental question and the accurate answer can provide a further understanding of the physics of complex oxides as well as the impact of the local chemistry and crystal structure distortion. Finally, yet importantly, in spite of the significant progress in thin film technologies and characterization methods, one can see that the limits of the characterization methods still do not allow us to answer this question clearly. Thereby, we believe that further technical improvements and the better integration of high-end characterization techniques to the growth tools will pave the way for more significant scientific achievements.
6.1 Experimental
6.1.1 Growth of the Samples
The LCO-based films were grown in an ozone-assisted MBE system (DCA Instruments) in the layer-by-layer regime, in which the sequence of the evaporation of the constituent layers follows the crystal structure of 214 compounds. In a nominal growth, first, two La-O atomic layers are deposited, and this is followed by the deposition of one Cu-O atomic layer in accordance with the chemical formula of La2CuO4. In the case of Sr-doped LCO compounds, a part of La atoms is replaced by Sr atoms in the co-deposition regime, i.e., simultaneous evaporation of La and Sr atoms is in a proportion corresponding to a doping level. The typical time for formation of one molecular layer of L(S)CO was ~ 3 min. The substrate temperature was measured by the infrared pyrometer and was kept around 650 °C. The total background pressure (ozone (O3), molecular oxygen (O2), and atomic oxygen (O)) was ~ 1.5 × 10−5 Torr provided by continuous evaporation of the distilled ozone.
In-Situ Characterization
An electron beam emanated from the RHEED gun, which is operated at 25 kV, irradiates the substrate surface at an incident angle of 1–2°. The dynamics of the RHEED patterns and the intensities of the diffraction streaks were monitored with a CCD camera and analyzed by using k-Space 400 software.
Structural Characterization and Transport Measurements
Surface morphology, crystal structure characterizations, and AES investigations (at 10 kV) were performed by atomic force microscopy (AFM) (Nanoscope III), high-resolution X-ray diffraction (XRD) (Bruker D8 Cu-Kα1 = 1.5406 Å), and Auger microprobe (JEOL JAMP-7810), respectively. Electrical measurements in a Van der Pauw four-point-probe configuration with alternative DC currents of ± 20 μA were employed. Simultaneously, measurements of the imaginary and real parts of the mutual inductance M(T) were carried out by magnetic susceptibility measurements in a two-coil configuration in parallel geometry with an AC current of 50 μA at a frequency of 1 kHz. The temperature was varied from room temperature to 4.2 K (liquid helium) using a motorized custom-designed dipstick (T change rate < 0.1 K/s).
Scanning Transmission Electron Microscopy
For representative cross-sectional electron transparent specimens, conventional specimen preparation procedures including mechanical thinning (grinding), tripod wedge polishing, and argon-ion thinning (with a liquid nitrogen-cooled stage; PIPS II, Model 695) were performed. For all STEM analyses, a probe-aberration-corrected JEOL JEM-ARM200F STEM equipped with a cold field emission electron source, a probe Cs-corrector (DCOR, CEOS GmbH), and a Gatan GIF Quantum ERS spectrometer was used. STEM imaging and electron energy loss spectroscopy (EELS) analyses were performed at probe semi-convergence angles of 20 mrad and 28 mrad, resulting in probe sizes of 0.8 Å and 1.0 Å, respectively. The collection angles for STEM-HAADF and STEM-ABF images were 75–310 and 11–23 mrad, respectively. A collection semi-angle of 111 mrad was used for EELS investigations [56]. For STEM data process and analyses, different software tools [120,121,122,123] have been used.
References
Dagotto, E.: Complexity in strongly correlated electronic systems. Science. 309, 257–262 (2005). https://doi.org/10.1126/science.1107559
Zubko, P., Gariglio, S., Gabay, M., Ghosez, P., Triscone, J.-M.: Interface physics in complex oxide heterostructures. Ann Rev Condens Matter Phys. 2, 141–165 (2011). https://doi.org/10.1146/annurev-conmatphys-062910-140445
Goodenough, J.B., Zhou, J.-S.: Localized to itinerant electronic transitions in transition-metal oxides with the perovskite structure. Chem. Mater. 10, 2980–2993 (1998). https://doi.org/10.1021/cm980276u
Bednorz, J.G., Müller, K.A.: Possible high Tc superconductivity in the Ba−La−Cu−O system. Z Phys B - Condens Matter. 64, 189–193 (1986). https://doi.org/10.1007/BF01303701
Naito, M., Sato, H., Yamamoto, H.: MBE growth of (La,Sr)2CuO4 and (Nd,Ce)2CuO4 thin films. Physica C. 293, 36–43 (1997). https://doi.org/10.1016/S0921-4534(97)01510-4
Locquet, J.-P., Perret, J., Fompeyrine, J., Mächler, E., Seo, J.W., Van Tendeloo, G.: Doubling the critical temperature of La1.9Sr0.1CuO4 using epitaxial strain. Nature. 394, 453–456 (1998). https://doi.org/10.1038/28810
Oh, B., Naito, M., Arnason, S., Rosenthal, P., Barton, R., Beasley, M.R., et al.: Critical current densities and transport in superconducting YBa2Cu3O7−δ films made by electron beam coevaporation. Appl. Phys. Lett. 51, 852–854 (1987). https://doi.org/10.1063/1.98834
Hellman, E.S., Schlom, D.G., Missert, N., Char Jr., K., Harris, J.S., Beasley, M.R., et al.: Molecular-beam epitaxy and deposition of high-Tc superconductors. J. Vac. Sci. Technol., B: Microelectron. Process. Phenom. 6, 799 (1998). https://doi.org/10.1116/1.584334
Locquet, J., Catana, A., Mächler, E., Gerber, C., Bednorz, J.G.: Block-by-block deposition: a new growth method for complex oxide thin films. Appl. Phys. Lett. 64, 372–374 (1994). https://doi.org/10.1063/1.111151
Schlom, D.G., Eckstein, J.N., Hellman, E.S., Streiffer, S.K., Harris, J.S., Beasley, M.R., et al.: Molecular beam epitaxy of layered Dy-Ba-Cu-O compounds. Appl. Phys. Lett. 53, 1660–1662 (1988). https://doi.org/10.1063/1.100443
Schlom, D.G.: Molecular beam epitaxial growth of layered Bi-Sr-Ca-Cu-O compounds. J. Cryst. Growth. 102, 361–375 (1990). https://doi.org/10.1016/0022-0248(90)90393-Y
Bhattacharya, A., May, S.J.: Magnetic oxide heterostructures. Annu. Rev. Mater. Res. 44, 65–90 (2014). https://doi.org/10.1146/annurev-matsci-070813-113447
Middey, S., Chakhalian, J., Mahadevan, P., Freeland, J.W., Millis, A.J., Sarma, D.D.: Physics of ultrathin films and heterostructures of rare-earth nickelates. Annu. Rev. Mater. Res. 46, 305–334 (2016). https://doi.org/10.1146/annurev-matsci-070115-032057
Sulpizio, J.A., Ilani, S., Irvin, P., Levy, J.: Nanoscale phenomena in oxide heterostructures. Annu. Rev. Mater. Res. 44, 117–149 (2014). https://doi.org/10.1146/annurev-matsci-070813-113437
Mannhart, J., Schlom, D.G.: Oxide interface - an opportunity for electronics. Science. 327, 1607–1611 (2010). https://doi.org/10.1126/science.1181862
Hwang, H.Y., Iwasa, Y., Kawasaki, M., Keimer, B., Nagaosa, N., Tokura, Y.: Emergent phenomena at oxide interfaces. Nat. Mater. 11, 103–113 (2012). https://doi.org/10.1038/nmat3223
Ramesh, R., Schlom, D.G.: Creating emergent phenomena in oxide superlattices. Nat. Rev. Mater. 1, (2019). https://doi.org/10.1038/s41578-019-0095-2
Ahn, C.H., Rabe, K.M., Triscone, J.-M.: Ferroelectricity at the nanoscale: local polarization in oxide thin films and heterostructures. Science. 303, 488–491 (2004). https://doi.org/10.1126/science.1092508.
Bousquet, E., Dawber, M., Stucki, N., Lichtensteiger, C., Hermet, P., Gariglio, S., et al.: Improper ferroelectricity in perovskite oxide artificial superlattices. Nature. 452, 732–736 (2008). https://doi.org/10.1038/nature06817
Ohtomo, A., Hwang, H.Y.: A high-mobility electron gas at the LaAlO3/SrTiO3 heterointerface. Nature. 427, 423–426 (2004). https://doi.org/10.1038/nature02308
Ohta, H., Kim, S., Mune, Y., Mizoguchi, T., Nomura, K., Ohta, S., et al.: Giant thermoelectric Seebeck coefficient of a two-dimensional electron gas in SrTiO3. Nat. Mater. 6, 129–134 (2007). https://doi.org/10.1038/nmat1821
Hepting, M., Green, R.J., Zhong, Z., Bluschke, M., Suyolcu, Y.E., Macke, S., et al.: Complex magnetic order in nickelate slabs. Nat. Phys. 1, 1097 (2018). https://doi.org/10.1038/s41567-018-0218-5
Tokura, Y., Tomioka, Y.: Colossal magnetoresistive manganites. J. Magn. Magn. Mater. 200, 1–23 (1999). https://doi.org/10.1016/S0304-8853(99)00352-2
Brinkman, A., Huijben, M., van Zalk, M., Huijben, J., Zeitler, U., Maan, J.C., et al.: Magnetic effects at the interface between non-magnetic oxides. Nat. Mater. 6, 493–496 (2007). https://doi.org/10.1038/nmat1931
Reyren, N., Thiel, S., Caviglia, A.D., Kourkoutis, L.F., Hammerl, G., Richter, C., et al.: Superconducting interfaces between insulating oxides. Science. 317, 1196–1199 (2007). https://doi.org/10.1126/science.1146006
Gozar, A., Logvenov, G., Kourkoutis, L.F., Bollinger, A.T., Giannuzzi, L.A., Muller, D.A., et al.: High-temperature interface superconductivity between metallic and insulating copper oxides. Nature. 455, 782–785 (2008). https://doi.org/10.1038/nature07293
Dijkkamp, D., Venkatesan, T., Wu, X.D., Shaheen, S.A., Jisrawi, N., Min-Lee, Y.H., et al.: Preparation of Y-Ba-Cu oxide superconductor thin films using pulsed laser evaporation from high Tc bulk material. Appl. Phys. Lett. 51, 619–621 (1987). https://doi.org/10.1063/1.98366
Wu, X.D., Inam, A., Venkatesan, T., Chang, C.C., Chase, E.W., Barboux, P., et al.: Low-temperature preparation of high Tc superconducting thin films. Appl. Phys. Lett. 52, 754–756 (1988). https://doi.org/10.1063/1.99337
Koster, G., Rijnders, G.J.H.M., Blank, D.H.A., Rogalla, H.: Imposed layer-by-layer growth by pulsed laser interval deposition. Appl. Phys. Lett. 74, 3729–3731 (1999). https://doi.org/10.1063/1.123235
Choi, E.-M., Bernardo, A.D., Zhu, B., Lu, P., Alpern, H., Zhang, K.H.L., et al.: 3D strain-induced superconductivity in La2CuO4+δ using a simple vertically aligned nanocomposite approach. Sci. Adv. 5, eaav5532 (2019). https://doi.org/10.1126/sciadv.aav5532
Das, S., Tang, Y.L., Hong, Z., Gonçalves, M.A.P., McCarter, M.R., Klewe, C., et al.: Observation of room-temperature polar skyrmions. Nature. 568, 368 (2019). https://doi.org/10.1038/s41586-019-1092-8
Monkman, E.J., Adamo, C., Mundy, J.A., Shai, D.E., Harter, J.W., Shen, D., et al.: Quantum many-body interactions in digital oxide superlattices. Nat. Mater. 11, 855–859 (2012). https://doi.org/10.1038/nmat3405
King, P.D.C., Wei, H.I., Nie, Y.F., Uchida, M., Adamo, C., Zhu, S., et al.: Atomic-scale control of competing electronic phases in ultrathin LaNiO3. Nat. Nanotechnol. 9, 443–447 (2014). https://doi.org/10.1038/nnano.2014.59
Nair, H.P., Liu, Y., Ruf, J.P., Schreiber, N.J., Shang, S.-L., Baek, D.J., et al.: Synthesis science of SrRuO3 and CaRuO3 epitaxial films with high residual resistivity ratios. APL Mater. 6, 046101 (2018). https://doi.org/10.1063/1.5023477
Mundy, J.A., Brooks, C.M., Holtz, M.E., Moyer, J.A., Das, H., Rébola, A.F., et al.: Atomically engineered ferroic layers yield a room-temperature magnetoelectric multiferroic. Nature. 537, 523–527 (2016). https://doi.org/10.1038/nature19343
Nie, Y.F., Zhu, Y., Lee, C.-H., Kourkoutis, L.F., Mundy, J.A., Junquera, J., et al.: Atomically precise interfaces from non-stoichiometric deposition. Nat. Commun. 5, 4530 (2014). https://doi.org/10.1038/ncomms5530
Ivashko, O., Horio, M., Wan, W., Christensen, N.B., McNally, D.E., Paris, E., et al.: Strain-engineering Mott-insulating La2CuO4. Nat. Commun. 10, 786 (2019). https://doi.org/10.1038/s41467-019-08664-6
Baiutti, F., Wrobel, F., Christiani, G., Logvenov, G.: 3 - Oxide molecular beam epitaxy of complex oxide heterointerfaces. In: Pryds, N., Esposito, V. (eds.) Metal Oxide-Based Thin Film Structures, pp. 53–78. Elsevier (2018). https://doi.org/10.1016/B978-0-12-811166-6.00003-0.
Wrobel, F., Mark, A.F., Christiani, G., Sigle, W., Habermeier, H.-U., van Aken, P.A., et al.: Comparative study of LaNiO3/LaAlO3 heterostructures grown by pulsed laser deposition and oxide molecular beam epitaxy. Appl. Phys. Lett. 110, 041606 (2017). https://doi.org/10.1063/1.4975005
Lagally, M.G., Savage, D.E.: Quantitative electron diffraction from thin films. MRS Bull. 18, 24–31 (1993). https://doi.org/10.1557/S0883769400043414
Bozovic, I., Eckstein, J.N.: Analysis of growing films of complex oxides by RHEED. MRS Bull. 20, 32–38 (1995). https://doi.org/10.1557/S0883769400044870
Herman, M.A., Sitter, H.: Molecular Beam Epitaxy: Fundamentals and Current Status. Springer-Verlag, Berlin Heidelberg (1989)
Kawamura, T., Maksym, P.A.: RHEED from stepped surfaces and its relation to RHEED intensity oscillations observed during MBE. Surf. Sci. 161, 12–24 (1985). https://doi.org/10.1016/0039-6028(85)90724-1
Grazing Incidence Configurations: Thin Film Analysis by X-Ray Scattering, pp. 143–182. John Wiley & Sons, Ltd (2006). https://doi.org/10.1002/3527607595.ch4
Bowen, D.K., Tanner, B.K., Tanner, B.K.: High Resolution X-Ray Diffractometry and Topography. CRC Press (1998). https://doi.org/10.1201/b12575.
Pickett, W.E.: Electronic structure of the high-temperature oxide superconductors. Rev. Mod. Phys. 61, 433–512 (1989). https://doi.org/10.1103/RevModPhys.61.433
Smadici, S., Lee, J.C.T., Wang, S., Abbamonte, P., Logvenov, G., Gozar, A., et al.: Superconducting transition at 38 K in insulating-overdoped La2CuO4-La1.64Sr0.36CuO4 superlattices: evidence for interface electronic redistribution from resonant soft X-ray scattering. Phys. Rev. Lett. 102, 107004 (2009). https://doi.org/10.1103/PhysRevLett.102.107004
Benckiser, E., Haverkort, M.W., Brück, S., Goering, E., Macke, S., Frañó, A., et al.: Orbital reflectometry of oxide heterostructures. Nat. Mater. 10, 189–193 (2011). https://doi.org/10.1038/nmat2958
Ament, L.J.P., van Veenendaal, M., Devereaux, T.P., Hill, J.P., van den Brink, J.: Resonant inelastic x-ray scattering studies of elementary excitations. Rev. Mod. Phys. 83, 705–767 (2011). https://doi.org/10.1103/RevModPhys.83.705
Hepting, M., Minola, M., Frano, A., Cristiani, G., Logvenov, G., Schierle, E., et al.: Tunable charge and spin order in PrNiO3 thin films and superlattices. Phys. Rev. Lett. 113, 227206 (2014). https://doi.org/10.1103/PhysRevLett.113.227206
Gázquez, J., Sánchez-Santolino, G., Biškup, N., Roldán, M.A., Cabero, M., Pennycook, S.J., et al.: Applications of STEM-EELS to complex oxides. Mater. Sci. Semicond. Process. 65, 49–63 (2017). https://doi.org/10.1016/j.mssp.2016.06.005
Damascelli, A., Hussain, Z., Shen, Z.-X.: Angle-resolved photoemission studies of the cuprate superconductors. Rev. Mod. Phys. 75, 473–541 (2003). https://doi.org/10.1103/RevModPhys.75.473
Lanzara, A., Bogdanov, P.V., Zhou, X.J., Kellar, S.A., Feng, D.L., Lu, E.D., et al.: Evidence for ubiquitous strong electron–phonon coupling in high-temperature superconductors. Nature. 412, 510 (2001). https://doi.org/10.1038/35087518
Varela, M., Lupini, A.R., van, B.K., Borisevich, A.Y., Chisholm, M.F., Shibata, N., et al.: Materials characterization in the aberration-corrected scanning transmission electron microscope. Annu. Rev. Mater. Res. 35, 539–569 (2005). https://doi.org/10.1146/annurev.matsci.35.102103.090513
MacLaren, I., Ramasse, Q.M.: Aberration-corrected scanning transmission electron microscopy for atomic-resolution studies of functional oxides. Int. Mater. Rev. 59, 115–131 (2014). https://doi.org/10.1179/1743280413Y.0000000026
Suyolcu, Y.E., Wang, Y., Baiutti, F., Sigle, W., Cristiani, G., Gregori, G., et al.: Aberration-corrected scanning transmission electron microscopy of La2CuO4-based superconducting interfaces at the Stuttgart Center for Electron Microscopy. JEOL News. 53, 8–17 (2018)
Schlom, D.G., Chen, L.-Q., Eom, C.-B., Rabe, K.M., Streiffer, S.K., Triscone, J.-M.: Strain tuning of ferroelectric thin films. Annu. Rev. Mater. Res. 37, 589–626 (2007). https://doi.org/10.1146/annurev.matsci.37.061206.113016
Becher, C., Maurel, L., Aschauer, U., Lilienblum, M., Magén, C., Meier, D., et al.: Strain-induced coupling of electrical polarization and structural defects in SrMnO3 films. Nat. Nanotechnol. 10, 661–665 (2015). https://doi.org/10.1038/nnano.2015.108
Chandrasena, R.U., Yang, W., Lei, Q., Delgado-Jaime, M.U., Wijesekara, K.D., Golalikhani, M., et al.: Strain-engineered oxygen vacancies in CaMnO3 thin films. Nano Lett. 17, 794–799 (2017). https://doi.org/10.1021/acs.nanolett.6b03986
Agrawal, P., Guo, J., Yu, P., Hébert, C., Passerone, D., Erni, R., et al.: Strain-driven oxygen deficiency in multiferroic SrMnO3 thin films. Phys. Rev. B. 94, 104101 (2016). https://doi.org/10.1103/PhysRevB.94.104101
Vailionis, A., Boschker, H., Siemons, W., Houwman, E.P., Blank, D.H.A., Rijnders, G., et al.: Misfit strain accommodation in epitaxial ABO3 perovskites: lattice rotations and lattice modulations. Phys. Rev. B. 83, 064101 (2011). https://doi.org/10.1103/PhysRevB.83.064101
Bagués, N., Santiso, J., Esser, B.D., Williams, R.E.A., McComb, D.W., Konstantinovic, Z., et al.: The misfit dislocation core phase in complex oxide heteroepitaxy. Adv. Funct. Mater. (n.d.). https://doi.org/10.1002/adfm.201704437
Naito, M., Sato, H.: Stoichiometry control of atomic beam fluxes by precipitated impurity phase detection in growth of (Pr,Ce)2CuO4 and (La,Sr)2CuO4 films. Appl. Phys. Lett. 67, 2557–2559 (1995). https://doi.org/10.1063/1.114431
Bozovic, I., Logvenov, G., Verhoeven, M.A.J., Caputo, P., Goldobin, E., Geballe, T.H.: No mixing of superconductivity and antiferromagnetism in a high-temperature superconductor. Nature. 422, 873–875 (2003). https://doi.org/10.1038/nature01544.
Keimer, B., Kivelson, S.A., Norman, M.R., Uchida, S., Zaanen, J.: From quantum matter to high-temperature superconductivity in copper oxides. Nature. 518, 179–186 (2015). https://doi.org/10.1038/nature14165
Radaelli, P.G., Hinks, D.G., Mitchell, A.W., Hunter, B.A., Wagner, J.L., Dabrowski, B., et al.: Structural and superconducting properties of La2-xSrxCuO4 as a function of Sr content. Phys. Rev. B. 49, 4163–4175 (1994). https://doi.org/10.1103/PhysRevB.49.4163
Hashimoto, M., Vishik, I.M., He, R.-H., Devereaux, T.P., Shen, Z.-X.: Energy gaps in high-transition-temperature cuprate superconductors. Nat. Phys. 10, 483–495 (2014). https://doi.org/10.1038/nphys3009
Taillefer, L.: Scattering and pairing in cuprate superconductors. Ann. Rev. Condens. Matter Phys. 1, 51–70 (2010). https://doi.org/10.1146/annurev-conmatphys-070909-104117
Maier, J., Pfundtner, G.: Defect chemistry of the high-Tc superconductors. Adv. Mater. 3, 292–297 (1991). https://doi.org/10.1002/adma.19910030605
Sato, H., Tsukada, A., Naito, M., Matsuda, A.: La2-xSrxCuOy epitaxial thin films (x=0 to 2): structure, strain, and superconductivity. Phys. Rev. B. 61, 12447–12456 (2000). https://doi.org/10.1103/PhysRevB.61.12447
Moodenbaugh, A.R., Sabatini, R.L., Xu, Y., Ochab, J., Huber, J.G.: Solubility of Ca in superconducting La2−xCaxCuO4. Physica C. 198, 103–108 (1992). https://doi.org/10.1016/0921-4534(92)90272-E
Shen, L., Salvador, P., Mason TO, Fueki, K.: High temperature electrical properties and defect chemistry of La2-xCaxCuO4-y superconductors—II. Defect structure modeling. J. Phys. Chem. Solids. 57, 1977–1987 (1996). https://doi.org/10.1016/S0022-3697(95)00324-X
Naito, M., Tsukada, A., Greibe, T., Sato, H.: Phase control in La-214 epitaxial thin films. Int. Soc. Opt. Photon. 4811, 140–155 (2002). https://doi.org/10.1117/12.455498
Sato, H., Tsukada, A., Naito, M., Matsuda, A.: Absence of 1/8 anomaly in strained thin films of La2-xBaxCuO4. Phys. Rev. B. 62, R799–R802 (2000). https://doi.org/10.1103/PhysRevB.62.R799
Bozovic, I., Logvenov, G., Belca, I., Narimbetov, B., Sveklo, I.: Epitaxial strain and superconductivity in La2-xSrxCuO4 thin films. Phys. Rev. Lett. 89, 107001 (2002). https://doi.org/10.1103/PhysRevLett.89.107001
Suyolcu, Y.E., Wang, Y., Baiutti, F., Al-Temimy, A., Gregori, G., Cristiani, G., et al.: Dopant size effects on novel functionalities: high-temperature interfacial superconductivity. Sci. Rep. 7, 453 (2017). https://doi.org/10.1038/s41598-017-00539-4
Kao, H.L., Kwo, J., Fleming, R.M., Hong, M., Mannaerts, J.P.: In situ growth and properties of single-crystalline-like La2-xSrxCuO4 epitaxial films by off-axis sputtering. Appl. Phys. Lett. 59, 2748 (1998). https://doi.org/10.1063/1.105876.
Wells, B.O., Birgeneau, R.J., Chou, F.C., Endoh, Y., Johnston, D.C., Kastner, M.A., et al.: Intercalation and staging behavior in super-oxygenated La2CuO4+δ. Zeitschrift Für Physik B Condens. Matter. 100, 535–545 (1996). https://doi.org/10.1007/s002570050158.
Shen, L., Salvador, P.A., Mason TO: Point defect modeling of La2CuO4-based superconductors. J. Am. Ceram. Soc. 77, 81–88 (1994). https://doi.org/10.1111/j.1151-2916.1994.tb06960.x
Torrance, J.B., Tokura, Y., Nazzal, A.I., Bezinge, A., Huang, T.C., Parkin, S.S.P.: Anomalous disappearance of high-Tc superconductivity at high hole concentration in metallic La2-xSxCuO4. Phys. Rev. Lett. 61, 1127–1130 (1988). https://doi.org/10.1103/PhysRevLett.61.1127
Opila, E.J., Tuller, H.L., Wuensch, B.J., Maier, J.: Oxygen tracer diffusion in La2-xSrxCuO4-y single crystals. J. Am. Ceram. Soc. 76, 2363–2369 (1993). https://doi.org/10.1111/j.1151-2916.1993.tb07778.x
Cordero, F., Cantelli, R.: Interstitial O and O vacancies in La2CuO4+δ during high-temperature treatments. Physica C: Superconductivity. 312, 213–224 (1999). https://doi.org/10.1016/S0921-4534(98)00712-6
Ray, P.J., Andersen, N.H., Jensen, T.B.S., Mohottala, H.E., Niedermayer, C., Lefmann, K., et al.: Staging superstructures in high-Tc Sr/O codoped La2-xSrxCuO4+y. Phys. Rev. B. 96, 174106 (2017). https://doi.org/10.1103/PhysRevB.96.174106
Kim, G., Christiani, G., Logvenov, G., Choi, S., Kim, H.-H., Minola, M., et al.: Selective formation of apical oxygen vacancies in La2-xSrxCuO4. Phys Rev Materials. 1, 054801 (2017). https://doi.org/10.1103/PhysRevMaterials.1.054801
Shannon, R.D.: Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Cryst A. 32, 751–767 (1976). https://doi.org/10.1107/S0567739476001551
Gozar, A., Bozovic, I.: High temperature interface superconductivity. Physica C: Superconductivity and Its Applications. 521–522, 38–49 (2016). https://doi.org/10.1016/j.physc.2016.01.003
Božović, I., He, X., Wu, J., Bollinger, A.T.: Dependence of the critical temperature in overdoped copper oxides on superfluid density. Nature. 536, 309–311 (2016). https://doi.org/10.1038/nature19061
Leng, X., Božović, I.: Controlling superconductivity in La2-xSrxCuO4+δby ozone and vacuum annealing. J. Supercond. Nov. Magn. 28, 71–74 (2015). https://doi.org/10.1007/s10948-014-2888-2
Birgeneau, R.J., Christianson, R.J., Endoh, Y., Kastner, M.A., Lee, Y.S., Shirane, G., et al.: Structures and incommensurate spin excitations in excess oxygen-doped La2CuO4+y. Phys. B Condens. Matter. 237–238, 84–90 (1997). https://doi.org/10.1016/S0921-4526(97)00058-6
Frano, A., Bluschke, M., Xu, Z., Frandsen, B., Lu, Y., Yi, M., et al.: Control of oxygen ordering in cuprate thin-film structures by electrochemistry. Phys. Rev. Mater. (n.d.)
Kaya, P., Gregori, G., Baiutti, F., Yordanov, P., Suyolcu, Y.E., Cristiani, G., et al.: High-temperature thermoelectricity in LaNiO3–La2CuO4 heterostructures. ACS Appl. Mater. Interfaces. 10, 22786 (2018). https://doi.org/10.1021/acsami.8b02153
Jia, C.L., Zeng, X.H., Xi, X.X., Urban, K.: Microstructure and residual strain in La2CuO4 thin films on LaSrAlO4-buffered SrTiO3 substrates. Phys. Rev. B. 64, 075416 (2001). https://doi.org/10.1103/PhysRevB.64.075416
Suyolcu, Y.E., Wang, Y., Sigle, W., Baiutti, F., Cristiani, G., Logvenov, G., et al.: Octahedral distortions at high-temperature superconducting La2CuO4 interfaces: visualizing Jahn–Teller effects. Adv. Mater. Interfaces. 4, 1700737 (2017). https://doi.org/10.1002/admi.201700737
Logvenov, G., Gozar, A., Bozovic, I.: High-temperature superconductivity in a single copper-oxygen plane. Science. 326, 699–702 (2009). https://doi.org/10.1126/science.1178863
Logvenov, G., Gozar, A., Butko, V.Y., Bollinger, A.T., Bozovic, N., Radovic, Z., et al.: Comprehensive study of high-Tc interface superconductivity. J. Phys. Chem. Solids. 71, 1098–1104 (2010). https://doi.org/10.1016/j.jpcs.2010.03.014
Pereiro, J., Bollinger, A.T., Logvenov, G., Gozar, A., Panagopoulos, C., Božović, I.: Insights from the study of high-temperature interface superconductivity. Philos. Trans. R. Soc. A Math. Phys. Eng. Sci. 370, 4890–4903 (2012). https://doi.org/10.1098/rsta.2012.0219
Butko, V.Y., Logvenov, G., Božović, N., Radović, Z., Božović, I.: Madelung strain in cuprate superconductors – a route to enhancement of the critical temperature. Adv. Mater. 21, 3644–3648 (2009). https://doi.org/10.1002/adma.200803850
Sato, H., Naito, M.: Increase in the superconducting transition temperature by anisotropic strain effect in (001) La1.85Sr0.15CuO4 thin films on LaSrAlO4 substrates. Physica C: Superconductivity. 274, 221–226 (1997). https://doi.org/10.1016/S0921-4534(96)00675-2
Zhou, H., Yacoby, Y., Butko, V.Y., Logvenov, G., Božović, I., Pindak, R.: Anomalous expansion of the copper-apical-oxygen distance in superconducting cuprate bilayers. PNAS. 107, 8103–8107 (2010). https://doi.org/10.1073/pnas.0914702107
Yacoby, Y., Zhou, H., Pindak, R., Božović, I.: Atomic-layer synthesis and imaging uncover broken inversion symmetry in La2-xSrxCuO4 films. Phys. Rev. B. 87, 014108 (2013). https://doi.org/10.1103/PhysRevB.87.014108
Radović, Z., Božović, N., Božović, I.: Photoinduced expansion of cuprate superconductors: evidence of strong electron-lattice coupling. Phys. Rev. B. 77, 092508 (2008). https://doi.org/10.1103/PhysRevB.77.092508
Ino, A., Kim, C., Mizokawa, T., Shen, Z.-X., Fujimori, A., Takaba, M., et al.: Fermi surface and band dispersion in La 2-xSrxCuO 4. J. Phys. Soc. Jpn. 68, 1496–1499 (1999). https://doi.org/10.1143/JPSJ.68.1496.
Wu, J., Pelleg, O., Logvenov, G., Bollinger, A.T., Sun, Y.-J., Boebinger, G.S., et al.: Anomalous independence of interface superconductivity from carrier density. Nat. Mater. 12, 877–881 (2013). https://doi.org/10.1038/nmat3719
Radović, Z., Vanević, M., Wu, J., Bollinger, A.T., Božović, I.: Interface superconductivity in cuprates defies Fermi-liquid description. J. Supercond. Nov. Magn. 30, 1–5 (2016). https://doi.org/10.1007/s10948-016-3636-6
Baiutti, F., Logvenov, G., Gregori, G., Cristiani, G., Wang, Y., Sigle, W., et al.: High-temperature superconductivity in space-charge regions of lanthanum cuprate induced by two-dimensional doping. Nat. Commun. 6, 8586 (2015). https://doi.org/10.1038/ncomms9586
Wang, Y., Baiutti, F., Gregori, G., Cristiani, G., Salzberger, U., Logvenov, G., et al.: Atomic-scale quantitative analysis of lattice distortions at interfaces of two-dimensionally Sr-doped La2CuO4 superlattices. ACS Appl. Mater. Interfaces. 8, 6763–6769 (2016). https://doi.org/10.1021/acsami.5b12813
Baiutti, F., Gregori, G., Wang, Y., Suyolcu, Y.E., Cristiani, G., van Aken, P.A., et al.: Cationic redistribution at epitaxial interfaces in superconducting two-dimensionally doped lanthanum cuprate films. ACS Appl. Mater. Interfaces. 8, 27368–27375 (2016). https://doi.org/10.1021/acsami.6b09739.
Suyolcu, Y.E., Wang, Y., Sigle, W., Cristiani, G., Logvenov, G., van, A.P.A.: Linking dopant distribution and interatomic distortions at La1.6M0.4CuO4/La2CuO4 superconducting interfaces. Microsc. Microanal. 22, 308–309 (2016). https://doi.org/10.1017/S1431927616002397
Anisimov, V.I., Korotin, M.A., Zaanen, J., Andersen, O.K.: Spin bags, polarons, and impurity potentials in La2-xSrxCuO4 from first principles. Phys. Rev. Lett. 68, 345–348 (1992). https://doi.org/10.1103/PhysRevLett.68.345
Lorenz, M., Rao, M.S.R., Venkatesan, T., Fortunato, E., Barquinha, P., Branquinho, R., et al.: The 2016 oxide electronic materials and oxide interfaces roadmap. J. Phys. D. Appl. Phys. 49, 433001 (2016). https://doi.org/10.1088/0022-3727/49/43/433001
Coll, M., Fontcuberta, J., Althammer, M., Bibes, M., Boschker, H., Calleja, A., et al.: Towards oxide electronics: a roadmap. Appl. Surf. Sci. 482, 1–93 (2019). https://doi.org/10.1016/j.apsusc.2019.03.312
Baiutti, F., Gregori, G., Suyolcu, E.Y., Wang, Y., Cristiani, G., Sigle, W., et al.: High-temperature superconductivity at the lanthanum cuprate/lanthanum–strontium nickelate interface. Nanoscale. 10, 8712–8720 (2018). https://doi.org/10.1039/C8NR00885J
Kim, G., Khaydukov, Y., Bluschke, M., Suyolcu, Y.E., Cristiani, G., Weschke, E., et al.: Tunable perpendicular exchange bias in oxide heterostructures. Phys. Rev. Mater. 3, 084420 (2019). https://doi.org/10.1103/PhysRevMaterials.3.084420
De Luca, G.M., Ghiringhelli, G., Perroni, C.A., Cataudella, V., Chiarella, F., Cantoni, C., et al.: Ubiquitous long-range antiferromagnetic coupling across the interface between superconducting and ferromagnetic oxides. Nat. Commun. 5, 5626 (2014). https://doi.org/10.1038/ncomms6626
Buzdin, A.I.: Proximity effects in superconductor-ferromagnet heterostructures. Rev. Mod. Phys. 77, 935–976 (2005). https://doi.org/10.1103/RevModPhys.77.935
Efetov, K.B., Garifullin, I.A., Volkov, A.F., Westerholt, K.: Proximity effects in ferromagnet/superconductor heterostructures. In: Zabel, H., Bader, S.D. (eds.) Magnetic Heterostructures: Advances and Perspectives in Spinstructures and Spintransport, pp. 251–290. Springer Berlin Heidelberg, Berlin (2008). https://doi.org/10.1007/978-3-540-73462-8_5.
Frano, A., Blanco-Canosa, S., Schierle, E., Lu, Y., Wu, M., Bluschke, M., et al.: Long-range charge-density-wave proximity effect at cuprate/manganate interfaces. Nat. Mater. 15, 831–834 (2016). https://doi.org/10.1038/nmat4682
May, S.J., Shah, A.B., te Velthuis, S.G.E., Fitzsimmons, M.R., Zuo, J.M., Zhai, X., et al.: Magnetically asymmetric interfaces in a LaMnO3/SrMnO3 superlattice due to structural asymmetries. Phys. Rev. B. 77, 174409 (2008). https://doi.org/10.1103/PhysRevB.77.174409
Shah, A.B., Ramasse, Q.M., May, S.J., Kavich, J., Wen, J.G., Zhai, X., et al.: Presence and spatial distribution of interfacial electronic states in LaMnO3-SrMnO3 superlattices. Phys. Rev. B. 82, 115112 (2010). https://doi.org/10.1103/PhysRevB.82.115112
Bosman, M., Watanabe, M., Alexander, D.T.L., Keast, V.J.: Mapping chemical and bonding information using multivariate analysis of electron energy-loss spectrum images. Ultramicroscopy. 106, 1024–1032 (2006). https://doi.org/10.1016/j.ultramic.2006.04.016
The use of MLLS fitting approach to resolve overlapping edges in the EELS spectrum at the atomic level | Gatan, Inc. n.d. http://www.gatan.com/use-mlls-fitting-approach-resolve-overlapping-edges-eels-spectrum-atomic-level. Accessed 11 Feb 2017
Wang, Y., Salzberger, U., Sigle, W., Eren Suyolcu, Y., van Aken, P.A.: Oxygen octahedra picker: a software tool to extract quantitative information from STEM images. Ultramicroscopy. 168, 46–52 (2016). https://doi.org/10.1016/j.ultramic.2016.06.001
Wang, Y., Suyolcu, Y.E., Salzberger, U., Hahn, K., Srot, V., Sigle, W., et al.: Correcting the linear and nonlinear distortions for atomically resolved STEM spectrum and diffraction imaging. Microscopy (Oxf). 67, i114–i122 (2018). https://doi.org/10.1093/jmicro/dfy002
Acknowledgments
Authors gratefully acknowledge Peter Specht for the technical support on the oxide MBE system and Pinar Kaya and Gideok Kim for fruitful discussions.
Funding
Open access funding provided by Max Planck Society. This project has received funding from the European Union’s Horizon 2020 research and innovation program under grant agreement No. 823717–ESTEEM3.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Suyolcu, Y.E., Christiani, G., van Aken, P.A. et al. Design of Complex Oxide Interfaces by Oxide Molecular Beam Epitaxy. J Supercond Nov Magn 33, 107–120 (2020). https://doi.org/10.1007/s10948-019-05285-4
Received:
Accepted:
Published:
Issue Date: