Abstract
The article describes the measurements results of the thermal properties of cross-linked blends of butadiene–acrylonitrile rubber (XNBR, Krynac X.7.50) and chlorosulfonated polyethylene containing different quantity of combined chlorine (CSM24—Hypalon 48, CSM29—Hypalon 20, CSM35—Hypalon 40, and CSM43—Hypalon 30) under inert gas (DSC) and in air (derivatography). The blends were non-conventionally cross linked at a temperature of 150 °C by means of MgO in the presence of stearic acid. The thermal curves obtained were interpreted from the point of view of phase transitions and chemical reactions of the macromolecular components used. It has been found that the elastomers investigated show a good compatibility brought about by the formation of both interpolymeric covalent bonds and interpolymeric and intrapolymeric ionic bridges, which play the role of a chemical compatibilizer. The results of the examinations performed show that the non-conventional cross-linked XNBR/CSM blends prove very good mechanical properties and are self-extinguished in air. Their flammability defined with the value of OI and combustion time in air clearly depends on the type of CSM.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Imperfections in the processes of elastomers synthesis and cross linking cause that it is still the point at issue to seek alternative methods of producing new elastic materials showing sometimes specific properties, which would meet consumers’ expectations. One of such methods of modifying high-molecular compounds consists in preparing polymer blends [1–11]. The properties of elastomeric materials obtained by non-conventional cross-linking elastomer blends have been examined for a long time at the Technical University of Łódź [1].
In earlier published papers [1, 12–14], we have found that the heating of the blends composed of carboxylated acrylonitrile-butadiene rubber (XNBR) and chlorosulfonated polyethylene (CSM) containing incorporated selected metal oxides or hydroxides [MeO, Me(OH)2] leads to formation of both interelastomer covalent and ionic cross links and thus to the unconventional interelastomer curing in the blends studied. The cross-linking rate, the cross-linking degree, and the properties of the cured blends prepared in this way depend on XNBR/CSM ratio, the kind and amount of CSM used, and the kind and amount of metal compound incorporated into the blend as well. Further it has been found [15, 16] that the incorporation of different amount of magnesium oxides (8–32 wt%) into the XNBR/CSM blend (70/30 by weight, CSM containing 43 wt% of bound Cl) reduced combustibility of the prepared materials comparing to XNBR cured with MgO. These phenomena are connected both with the total Cl-content in the system and the specific action of MgO incorporated into the blends studied. The obtained results are the different thermal properties and the combustibility of CSM of different bound Cl-content [17, 18] and its different thermodynamic affinity to XNBR (XNBR solubility parameter δ = 20.5 MPa1/2 [19], CSM solubility parameter δ = 18.3–19.9 MPa1/2 depending on the total bound Cl-content in CSM [10]) which indicate that the XNBR/CSM blends containing different kinds of CSM (total bound Cl-content in the range: 24–43 wt%, potential flame-retardant agent) and cured with selected amount of MgO should exhibit the differentiated thermal properties and combustibility as well. Hence, the aim of this study is to investigate the effect of different kinds of CSM on the thermal properties and combustibility of the XNBR/CSM blends cured and filled with selected amount of MgO. MgO has been chosen and used due to its high crosslinking ability [13, 15, 16] and observed flame-retarding activity in the blends investigated [16].
Experimental
Materials
The subject of the present investigations concerned blends containing 70 parts by weight of carboxylated butadiene–acrylonitrile rubber (XNBR, Krynac X.7.50, a product from Bayer Lanxess, containing 7% by weight of combined acid and 27.5% by weight of combined acrylonitrile) and 30 parts by weight of chlorosulfonated polyethylene [CSM24 (Hypalon 48), CSM29 (Hypalon 20), CSM35 (Hypalon 40), and CSM43 (Hypalon 30), products from Du Pont Dow Elastomers, containing 24, 29, 35, and 43% by weight of chlorine totally combined and ~1.1% by weight of chlorine combined in –SO2Cl groups and ~1% by weight of combined sulfur].
Methods and analysis
The XNBR/CSM blends prepared at room temperature by means of a laboratory rolling mill were cross linked at a temperature of 150 °C using a cross-linking agent including 24 parts by weight of magnesium oxide (MgO from Ancor-P) in the presence of two parts by weight of fatty acid (stearin from POCh) per 100 parts by weight of the elastomer blend. The excessive content of MgO in investigation blends in relation to the twice as high stoichiometric quantity, in terms of the content of carboxyl groups, fulfills the function of filler in them. The blends were, respectively, designated with the following symbols: XNBR/CSM24, XNBR/CSM29, XNBR/CSM35, and XNBR/CSM43.
The cross-linking durations of particular XNBR/CSM blends were consistent in an electrically heated hydraulic press with the values of τ90 determined from the results of the cross-linking kinetic measurements obtained by means of a WG-02 vulcameter with an oscillating rotor according to standard PN-ISO 3417:1994 [16].
The cross-linking degree of XNBR/CSM blends (α = 1/Q w), taking into account both crosswise ionic bonds and crosswise covalent bonds, was determined on the basis of the results of equilibrium swelling (Q w) in toluene. The cross-linking degree (α′ = 1/Q w,a), taking into account crosswise covalent bonds was determined from the results of equilibrium swelling (Q w,a) in toluene after the action of ammonia vapors [16].
The measurements of equilibrium swelling were performed also in the case of samples heated in the derivatograph furnace up to appropriate temperatures determined from DTA curves [16].
The determinations of elasticity constants were carried out with dumbbell samples with a measurement section length of 20 mm and a width of 4 mm. The length of measurement sections before and after loading was determined by means of a cathetometer. The measurement was performed 30 min after each sample loading, and the weights were selected so that the sample elongation increment was each time up to 20% of the measurement section length. The measurement was carried out until 120% of the initial measurement section value was obtained. Elasticity constants were determined from Mooney–Rivlin’s equation [20, 21].
The mechanical properties of cross-linked XNBR/CSM blends were tested according to standard PN-ISO 37:1998 by means of a Zwick tensile testing machine, model 1435, cooperating with a properly programmed computer. Dumbbells with a measurement section width of 4 mm were used to determine tensile strength (TS b) and elongation at break (E b) [16].
The thermal analysis of cross-linked blends was performed under both air and nitrogen atmospheres. 90 mg of samples were heated under air in a Paulik, Paulik Erdey derivatograph furnace at a rate of 7.9 °C/min within the temperature range 25–800 °C using Al2O3 as a reference substance. Thermal curve sensitivities were as follows: TG = 100, DTA = 1/5, and DTG = 1/20.
Under nitrogen atmosphere, 5–7 mg of samples were heated in a DSC-204 furnace from Netzsch at a rate of 10 °C/min within the temperature range from −100 to 500 °C.
The flammability of the cross-linked XNBR/CSM blends was determined by the method of oxygen index using an apparatus of our own construction [22]. The flammability of XNBR/CSM was also assessed on the basis of sample combustion time under air or time, after which the sample was extinguished. The sample shape and dimensions, its arrangement, and flame treatment time were the same as in the case of the oxygen index method [16].
Results and discussion
The thermal properties of high-molecular components of XNBR/CSM blends were the object of our earlier studies [16]. From them it follows that in the atmosphere of a neutral gas, the thermal stability of XNBR, determined by the range of temperature, at which the polymer maintains its elastic properties, is ∆T = −31 ÷ 263 °C, where T = −31 °C is its glass transition temperature (T g) and T = 263 °C is the temperature of the beginning of its cross-linking (T c) (Table 1; Fig. 2). The range of temperature, at which XNBR maintains its elastic properties in the atmosphere of air is ∆T = −31 ÷ 180 °C, since its thermooxidative cross-linking processes begin at T = 180 °C [16]. The range of thermal stability of the chlorosulfonated polyethylene (CSM) under investigation can assume different values depending on the type of CSM. The upper limit of their thermal stability is determined by the temperature, at which the dehydrochlorination processes begin and bring about the thermal modification of polymer chains. This temperature, 190 °C, is independent of the type of CSM and the atmosphere of the examinations performed. The lower limit of the thermal stability of CSMs is determined by their glass transition temperature and in the case of CSM24, their crystallization temperature [18]. In this connection, the lowest ∆T is shown by CSM43 which has the highest temperature of the transition from glassy to elastic state (Table 1).
The comparative analysis of vulcametric results leads to a conclusion that the increase in the content of chemically combined chlorine in the macromolecules of CSM does not exert any systematic influence on the optimal vulcanization time (τ90) of the XNBR/CSM blends at T = 150 °C (Table 2). On the other hand, it brings about an increase in the cross-linking degree of the blends investigated resulting from the presence of the interpolymeric covalent crosswise bonds of XNBR–CSM (~SO2–O–CO~) as well as the interpolymeric crosswise ionic bonds (2C 1, α; Table 2). It is the difference in the cross-linking degrees (α–α′) (Table 2) that testifies to the presence of the intrapolymeric ionic bonds of XNBR–XNBR (–CO–O(−)(+)Mg(+)(−)O–OC–) and the interpolymeric ionic bonds of XNBR–CSM (–CO–O(−)(+)Mg(+)(−)O–SO2–) containing magnesium ions [16]. The crosswise bonds formed during vulcanization fulfill the role of a chemical compatibilizer of the blends investigated [16]. Owing to the presence of crosswise ionic bonds, the XNBR/CSM blends are characterized by very good mechanical properties within a wide range of cross linking as shown by the values of TS b and E b parameters (Table 2). Our findings show that in the case of the XNBR/CSM24, XNBR/CSM29, and XNBR/CSM35 blends cross-linked by means of 24 parts by weight of MgO, the contents of their crosswise bonds are comparable (Table 2). The findings published earlier show that MgO used in the cross linking of the XNBR/CSM blends fulfills the function of both cross linker and filler. It has been also found that the vulcanization of the XNBR/CSM blends results in decreased dimensions of MgO particles dispersed in the elastomeric matrix due to their participation in the formation of crosswise ionic bonds [16].
The similar solubility values of the macromolecular components of the blends investigated, amounting to: δXNBR = 20.51/2; δCSM24 = 18.31/2; δCSM29 = 19.2½; δCSM35 = 19.51/2; δCSM43 = 19.61/2 [19] indicate potential miscibility of the elastomers, which is confirmed by the results obtained by the DSC method (Table 1; Figs. 1, 2, 3). Regardless of the CSM type used, the cross-linked XNBR/CSM blends are characterized by one glass transition temperature being intermediate between the T g values of the elastomer components (Table 3; Figs. 1, 2, 3). From the DSC curve of the cross-linked XNBR/CSM24 blends, it follows that the transition from glassy to elastic state takes place at T = −26 °C. The small endothermic transformation recorded on the thermal curve at T = 55 °C is connected with the melting of crystalline phase in CSM24, whose macromolecules can crystallize due to the lowest content of chemically combined chlorine among all the CSM investigated [18]. The great exothermic transformation of the vulcanized blends recorded on DSC curves, comprising two pronounced peaks in the case of XNBR/CSM24 and XNBR/CSM29 at T = 287 °C and T = 360 °C and three pronounced peaks in the case of XNBR/CSM35 and XNBR/CSM49 at T = 261, 285, and 360 °C, is connected with the processes of their thermal cross linking (Figs. 1, 2, 3). The beginning of the thermal cross linking of XNBR/CSM, which determines the end of their elastic state starts at T = 245 °C in the case of XNBR/CSM24 and shifts towards lower temperatures under the influence of the increase in chemically combined chlorine in the macromolecules of CSM (Table 1; Figs. 1, 2, 3). The comparative analysis of the values of the thermal cross-linking enthalpy (∆H c) of XNBR/CSM blends leads to a conclusion that the increase in chlorine content in the CSM macromolecules increases the yield of these processes (Table 1). The thermal cross-linking processes are accompanied by the destruction of elastomer macromolecules [16]. The temperature of the maximal destruction rate of XNBR and CSM macromolecules clearly increases with the increase in the content of chlorine in CSM (Table 1).
From the derivatographic analysis of the cross-linked blends, it follows that they are decomposed in three stages under the influence of heating (TG, DTG; Fig. 4). Based on the measurement results of the Q w of vulcanized XNBR/CSMs before and after their heating in the derivatograph oven up to T = 245 and 305 °C, it was found that the first two transformations recorded on DTA curves at these temperatures were a symptom of their thermal cross linking in the atmosphere of air. The transformation at T = 305 °C is accompanied by a considerable sample weight loss amounting to 11% (Fig. 4) brought about by the commencing destruction processes of the vulcanized blend components and the evolution of HCl (T DI; Table 3). The violent destruction processes of the cross-linked blends begin at T DII ≥ 355 °C as shown by the two exothermic transformations recorded on DTA curve at T = 405 and 450 °C, respectively (Fig. 4). The thermal decomposition rate of the cross-linked XNBR/CSM (dm/dt II) is considerably lower than the destruction rate of XNBR constituting the polymeric matrix (Table 3), which results from the presence of HCl evolving from the thermal decomposition reactions of the cross-linked blends, owing to which these reactions proceed according to both free-radical and ionic mechanism. This situation facilitates carbonization processes as shown by the considerable increase in the residue after the thermal destruction of the cross-linked XNBR/CSM blends (P w) and the cross-linked elastomer (P e) (Table 3). In the atmosphere of air, the residue after thermal decomposition is burned as indicated by the exothermic peak recorded at T = 515 °C (Fig. 4; Table 3). The high residue after the combustion of the solid residue resulting from the destruction of the cross-linked XNBR/CSM blends (P 800) is significantly influenced by MgO contained in them as cross linker (Table 3).
The results of previously performed tests show that XNBR belongs to polymers extinguishing in air (Table 4). The flammability of the CSMs used depends on the content of chemically combined chlorine [17]. CSM24 and CSM29 belong to the group of self-extinguishing polymers, while CSM35 and CSM43 belong to the group of non-flammable polymers. The XNBR/CSM blends under investigation are self-extinguished in air and their flammability defined by both the value of oxygen index (OI) and the combustion time in air (t) depends of the type of CSM (Table 4). The time, after which the XNBR/CSM blend extinguishes in air, is shortened with the increase in the content of chlorine in CSM (Table 4). The high OI values and the short times, after which the cross-linked XNBR/CSM blends extinguish in air, are due to HCl evolving under the influence of elevated temperature. HCl manifests its active action first of all in the flame to inhibit the chain reactions proceeding in it. At the same time, HCl as non-flammable gas decreases the concentration of gaseous flammable products within the combustion zone and retards the diffusion of oxygen to this zone. From the derivatographic analysis, it follows that HCl shows its active action also in the solid combustion zone where it decreases the thermal destruction rate of the cross-linked elastomers and facilitates their carbonization (Table 3). As a result, a lower quantity of volatile and flammable products of the destruction of the cross-linked polymer blends passes to flame. The structure of the boundary layer between the sample (solid phase) and flame (gaseous phase) is also of great importance in the combustion process. In this case, it is formed of carbonized elastomers. In this connection, this layer shows a high thermal stability and considerably retards the flow of mass and energy between the solid and gaseous phases during combustion. The lowest flammability defined with both the value of OI and the time of combustion in air (t) is shown by the cross-linked XNBR/CSM43 blend (Table 4), which results from its lowest thermal decomposition rate (dm/dt II; Table 3) and the highest yield of carbonization during this process (P w, P e; Table 3). A significant influence on the reduction in the flammability of XNBR/CSM43 is also exerted by the great yield of the thermal cross-linking processes (∆H c; Table 1). The thermal cross linking of elastomers is one of many chemical reactions proceeding in the solid phase of burning polymer that affect the boundary layer structure and consequently also the course of combustion.
Conclusions
Regardless of the type of CSM, its cross-linked blends with carboxylated butadiene–acrylonitrile rubber (XNBR) show one glass transition temperature (T g), which indicates a good miscibility of both polymers. This compatibility results from the presence of interpolymeric crosswise covalent bonds as well as intrapolymeric and interpolymeric ionic bonds containing magnesium ions. The crosswise bonds formed during vulcanization of XNBR/CSM play the role of a chemical compatibilizer.
The thermal decomposition rate of the cross-linked XNBR/CM blends (dm/dt II) is considerably lower than that of XNBR being the elastomeric matrix, which results from the considerable contribution of ionic reactions to the destruction of cross-linked blends.
The non-conventional cross-linked XNBR/CSM blends prove very good mechanical properties and belong to self-extinguishing materials in air. The time, after which the cross-linked blend extinguishes in air, is shortened with the increase in the content of chlorine combined in CSM.
References
Janowska G, Kucharska A, Kawałek J, Rzymski WM. Thermal properties of crosslinked blends of chlorosulfonated polyethylene and styrene–butadiene rubber. Polimery. 2009;54:648–53.
Radhakrishnan CK, Sujith A, Unnikrishnan G. Thermal behaviour of styrene butadiene rubber/poly(ethylene-co-vinyl acetate) blends TG and DTG analysis. J Therm Anal Calorim. 2007;90:191–9.
Rao V, Johns J. Thermal behaviour of chitosan/natural rubber latex blends TG and DSC analysis. J Therm Anal Calorim. 2008;92:801–6.
Rajkumar T, Vijayakumar CT, Sivasamy P, Sreedhar B, Wilkie ChA. Thermal degradation studies on PMMA–HET acid based oligoesters blends. J Therm Anal Calorim. 2010;100:651–60.
Martelli SM, Fernandes EG, Chiellini E. Thermal analysis of soil-buried oxo-biodegradable polyethylene based blends. J Therm Anal Calorim. 2009;97:853–8.
Ciesińska W, Zieliński J, Brzozowska T. Thermal treatment of pitch-polymer blends. J Therm Anal Calorim. 2009;95:193–6.
Rosa DS, Bardi MAG, Machado LDB, Dias DB, Silva LGA, Kodama Y. Starch plasticized with glycerol from biodiesel and polypropylene blends. J Therm Anal Calorim. 2010;102:181–6.
Menyhárd A, Faludi G, Varga J. β-crystallisation tendency and structure of poly-propylene grafted by maleic anhydride and its blends with isotactic polypropylene. J Therm Anal Calorim. 2008;93:937–45.
Ciesińska W. Thermorheological studiem on polymeric blends. J Therm Anal Calorim. 2008;93:747–51.
Dias DS, Crespi MS, Kobelnik M, Ribeiro CA. Calorimetric and SEM studies of PHB–PET polymeric blends. J Therm Anal Calorim. 2009;97:581–4.
Markovic G, Marinovic-Cincovic M, Vodnik V, Radovanovic B, Budinski-Simendic J, Veljkovic O. Thermal stability of acrylonitrile/chlorosulphonated polyethylene rubber blend. J Therm Anal Calorim. 2009;97:999–1006.
Koziol M, Rzymski WM. Curing of blends composed of carboxylated acrylonitrile-butadiene rubber and chlorosulphonated polyethylene. Ann Pol Chem Soc. 2004;3:1015–8.
Koziol M, Rzymski WM. Unconventional crosslinking of the blends of chlorosulfonated polyethylene and carboxylated acrylonitrile–butadiene rubber. Polimery. 2005;50:587–92.
Koziol M, Rzymski WM, Mackowska A. Effect of type and curing condition on the properties of carboxylated acrylonitrile-butadiene rubber. e-Polymers. 2006;P_011:1–6.
Kmiotek M, Rzymski WM. Interelastomer reactions in unconventional elastomer blends. Polimery. 2007;52:511–6.
Janowska G, Kucharska-Jastrząbek A, Kasiczak A, Rzymski WM. Thermal properties and combustibility of crosslinked XNBR/CSM blends. Part I. Influence of the magnesium oxide. J Therm Anal Calorim. doi:10.1007/s10973-011-1328-9.
Janowska G, Rzymski WM, Kmiotek M, Kucharska A, Kasiczak A. Thermal properties and combustibility of chlorosulfonated polyethylene. Polimery. 2009;54:245–9.
Janowska G, Kucharska A, Rzymski WM, Kasiczak A. DSC study of chlorosulphonated polyethylene. J Therm Anal Calorim. 2010;102:1019–24.
Rzymski WM, Srogosz A. The solubility parameter of chlorosulfonated polyethylene. Polimery. 2000;45:41–5.
Mooney M. A theory of large elastic deformation. J Appl Phys. 1940;11:582–92.
Rivlin RS. Torsion of a rubber cylinder. J Appl Phys. 1947;18:444–9.
Patent PRL 129411 (1987).
Open Access
This article is distributed under the terms of the Creative Commons Attribution Noncommercial License which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This is an open access article distributed under the terms of the Creative Commons Attribution Noncommercial License (https://creativecommons.org/licenses/by-nc/2.0), which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.
About this article
Cite this article
Janowska, G., Kucharska-Jastrzabek, A., Rzymski, W.M. et al. Thermal properties and combustibility of cross-linked XNBR/CSM blends. J Therm Anal Calorim 109, 1481–1486 (2012). https://doi.org/10.1007/s10973-011-1953-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10973-011-1953-3