Abstract
One-dimensional (1D) CdS@ZnS core-shell nanocomposites were successfully synthesized via a two-step solvothermal method. Preformed CdS nanowires with a diameter of ca. 45 nm and a length up to several tens of micrometers were coated with a layer of ZnS shell by the reaction of zinc acetate and thiourea at 180 °C for 10 h. It was found that uniform ZnS shell was composed of ZnS nanoparticles with a diameter of ca. 4 nm, which anchored on the nanowires without any surface pretreatment. The 1D CdS@ZnS core-shell nanocomposites were confirmed by XRD, SEM, TEM, HR-TEM, ED, and EDS techniques. The optical properties and photocatalytic activities of the 1D CdS@ZnS core-shell nanocomposites towards methylene blue (MB) and 4-chlorophenol (4CP) under visible light (λ > 420 nm) were separately investigated. The results show that the ZnS shell can effectively passivate the surface electronic states of the CdS cores, which accounts for the enhanced photocatalytic activities of the 1D CdS@ZnS core-shell nanocomposites compared to that of the uncoated CdS nanowires.
Avoid common mistakes on your manuscript.
Introduction
One-dimensional (1D) nanocomposites consisting of two important functional materials have attracted significant attention with respect to their fascinating properties and potential applications in the field of nanodevice fabrication [1–3]. Superior or new properties and diverse functions have been realized by assembling different types of constituents into nanocomposites with controlled structure and interface interactions. Recently, considerable research efforts have been directed on the shape and compositional control of 1D semiconductor-included nanocomposites, such as nanowires with superlattice structures [4, 5], core-shell coaxial nanowires [6–13], biaxial or sandwich-like triaxial nanowires [14–18], and anisotropic (e.g., dimer-type and hierarchical composite materials) heterostructures [19–23]. In particular, core-shell nanostructures are reported most often because various mechanisms can be involved in shell growth that do not necessarily relate to epitaxy between the inorganic components, and consequently enhanced or modified properties are resulted from the particular dimensionality. For example, Lieber et al. [24] have reported on the synthesis of Ge/Si core-shell nanowires (NW) and high-performance as field-effect transistors due to the reduced interface scattering. Xu et al. [25] demonstrated that Ni nanowires encapsulated within fullerene cables exhibited enhanced and anisotropic ferromagnetic behavior along the nanowire axes.
The development of new heterostructures is still a challenging subject, for the critical step of this work remains how to modulate the properties by tailoring the nucleation of one phase on the surface of the other. Wurtzite CdS, a direct band gap semiconductor with a gap energy of 2.42 eV at 300 K, is one of the first discovered semiconductors which has promising applications in photochemical catalysis, gas sensor, detectors for laser and infrared, solar cell, nonlinear optical materials, various luminescence devices, and optoelectronic devices [26–28]. On the account of this, various 1D CdS nanostructural materials have been generated through various routes [29–32]. ZnS has a wider band gap (Eg = 3.7 eV) than CdS. The surface modification of a wide band gap semiconducting shell around a narrow band gap core can alter the charge, functionality, and reactivity of the materials and consequently enhance the functional properties due to localization of the electron-hole pairs [33–35]. Up to now, CdS@ZnS core-shell nanostructures with stronger luminescence and electrical properties have been successfully prepared by metal-organic CVD (MOCVD) process or wet–chemical approach [10, 36–38].
In this paper, we try to use preformed CdS nanowires as 1D nanoscale substrates for the growth of ZnS shell by a two-step solution method. No surface pretreatments were needed to introduce new surface functional groups, or additional covalent and/or noncovalent interconnectivity for the growth of ZnS onto CdS nanowires in our experiments. The optical properties and photocatalytic activities of the 1D CdS@ZnS core-shell nanocomposites under visible light (λ > 420 nm) were investigated. The results show that the ZnS shell can effectively passivate the surface electronic states of the CdS cores, which helps to enhance the photocatalytic activities of the 1D CdS@ZnS core-shell nanocomposites.
Experimental Section
The Preparation of 1D CdS@ZnS Core-Shell Nanocomposites was Achieved via a Two-Step Solvothermal Process. All Reagents were Analytical Grade and were Used Without Further Purification
Preparation of CdS Nanowire
In a typical process, Cd(S2CNEt2)2(1.124 g, 0.1 mmol) prepared by precipitation from a stoichiometric mixture of NaS2CNEt2and CdCl2in water, was added to a Teflon-lined stainless steel autoclave with a capacity of 55 mL. Then the autoclave was filled with 40 mL ethylenediamine up to about 70% of the total volume. The autoclave was maintained at 180 °C for 24 h and then allowed to cool to room temperature. A yellowish precipitate was collected and washed with absolute ethanol and distilled water to remove residue of organic solvents. The final products were dried in vacuum at 70 °C for 6 h.
Preparation of 1D CdS@ZnS Core-Shell Nanocomposites
As a general procedure, CdS nanowires (0.03 g, 0.2 mmol) were well-dispersed in 45 mL absolute ethanol under sonication, then Zn(CH3COO)2 · 2H2O (0.022 g, 0.1 mmol) and (NH2)2CS (0.015 g, 0.2 mmol) were added in sequence. The resulting mixture was loaded into a 55 mL-Telfon-lined autoclave and maintained at 180 °C for 12 h. After the reaction was completed, the autoclave was cooled to room temperature naturally, and the resulting solid products were collected, washed with absolute ethanol and distilled water for twice, and then dried in vacuum at 70 °C for 6 h.
Characterization
The crystal structure of the product was determined from the X-ray diffractometer (Bruker D8) with a graphite monochromator and CuK α radiation (λ = 1.5418 Å) in the range of 15–80° at room temperature while the tube voltage and electric current were held at 40 kV and 20 mA. The morphology and microstructure of the products were determined by FESEM (Hitachi S-4800), TEM (JEM-100CXII) with an accelerating voltage of 80 kV, and high-resolution TEM (HR-TEM, JEOL-2100) with an accelerating voltage of 200 kV equipped with an energy-dispersive X-ray spectrometer (EDS). The UV-vis spectra and room photoluminescence (PL) were performed on a TU-1901 UV-vis spectrophotometer and WGY-10 spectrofluorimeter.
Photocatalytic Decomposition of MB and 4CP
To evaluate the photocatalytic activity of the synthesized 1D CdS@ZnS core-shell nanocomposites, the degradation of MB and 4CP were carried out in a jacketed quartz reactor filled with 50 mL of the test solution in the presence of the catalyst (50 mg) by using a 300-W Xe lamp with a cutoff filter (λ > 420 nm) as light source. Prior to illumination, the suspension was stirred for 20 min in the dark to favor the pollutant’s adsorption onto the catalyst surface, followed by determination of the concentration of the pollutants as the initial concentrationC0. The remaining concentration of pollutants in the suspension at given intervals of irradiation was measured on a TU-1901 UV-vis spectrophotometer.
Results and Discussion
Characterizations of the Final Products
The CdS nanowires and 1D CdS@ZnS hybrid nanocomposites were analyzed using XRD, SEM, TEM, and HRTEM to evaluate the structural characteristics. Figure 1a shows the powder XRD pattern from unmodified CdS nanowires, which can be indexed to the wurtzite structure (JCPDS No. 41-1049). Compared with the standard card, the diffraction peaks of (100) and (110) are relatively strong, while the peak of (002) is weak, which can attributed to the fact that CdS nanowires mainly lie on the experimental cell during the XRD measurement process and have a preferential orientation along [001] [39]. After ZnS shells are coated onto the CdS nanowires, additional diffraction peaks marked with “#” appear in the XRD pattern (Fig. 1b) corresponding to the powder diffraction pattern for zinc blende ZnS (JCPDS No. 05-0566).
As seen in a SEM image (Fig. 2a), numerous CdS nanowires with a diameter of ca. 45 nm and a length up to several decades of μm are uniformly distributed on the carbon conductive tape. In Fig. 2b, a representative SEM image of 1D CdS@ZnS hybrid nanocomposites, demonstrated that the diameter of the core-shell nanowires had increased to be about ~60 nm while the thickness of the shell layer was calculated to be 5 ~ 10 nm. After the shell growth, the surface of the nanowires became rough (inset of Fig. 2b). The XRD and SEM results indicate that the as-grown product is a composite material of CdS and ZnS with a 1D morphology. Detailed microstructures of the product were further investigated using TEM, HRTEM, ED, and EDS techniques.
TEM image of neat CdS nanowires with smooth surface are shown in Fig. 3a, and a high-magnified TEM image of the marked region in Fig. 3a shows that the CdS nanowires have a highly crystalline nature with a lattice plane separation of 0.335 nm corresponding to the (002) lattice spacing distance of hexagonal CdS (Fig. 3b), which suggests that the CdS nanowires preferentially grow along the [001] direction. The SAED pattern (inset of Fig. 3a) of a single nanowire is also consistent with the single crystalline nature of CdS indexed as the [010] zone axis. In Fig. 3c, the CdS nanowire is coated with a thin layer of ZnS shell, resulting in increased diameter and a relatively rough surface. Figure 3d is an enlargement of the marked region in Fig. 3c, from which we can see the shell is made up of ZnS nanoparticles of ~4 nm diameter growing along the surface of the CdS nanowires. ZnS nanoparticles mainly show two sets of lattice fringe spacings of 0.27 nm and 0.19 nm that correspond to the (200) and (220) planes of the zinc blende ZnS, respectively. The corresponding select area electron diffraction (SAED) pattern of the CdS@ZnS nanocomposite is mainly composed of two sets of diffraction patterns. The dashed parallelogram is indexed as that of hexagonal CdS along the zone axis and diffraction rings as that of the ZnS layer with polycrystalline nature (Fig. 3f). The measured lattice spacing based on the rings in the diffraction pattern can separately be indexed as correspondinghkl from the PDF database of zinc blende ZnS.
The existence of ZnS layer on the surface of CdS nanowires was further confirmed by EDS data (Fig. 3e). EDS analysis conducted on the central region of a CdS@ZnS core-shell nanowire indicates that the nanowire is mainly composed of Cd, Zn and S with Cd/Zn/S ratio of 0.62:0.36:1 (a stoichiometry close to Cd x Zn1−xS). The Cu peaks were detected from the grid for TEM observation.
Optical Properties and Photocatalytic Activity of 1D CdS@ZnS Core-Shell Nanocomposites
The optical properties of 1D CdS@ZnS core-shell nanocomposites were measured using UV-vis absorption and PL spectroscopy. The UV-vis absorption spectra of the CdS nanowires and CdS@ZnS core-shell nanocomposites are shown in Fig. 4a. The absorption spectra of the nanocomposites is dominated by the CdS core with a slight blue-shift owning to the influence of the ZnS shells [40]. PL spectra recorded with a 300 nm excitation wavelength are shown in Fig. 4b. The PL spectrum of the uncoated CdS nanowires shows an obvious absorption shoulder around 523 nm, and the PL emission of the nanocomposites exhibits a more intense emission positioned at ~520 nm. The nearly unchanged emission peak position mainly suggests the PL behavior of the CdS nanowires, while it is slightly asymmetric indicating the presence of another emission band toward the higher wavelength region [37]. The enhancement in the emission is due to the fact that high band gap ZnS shell material suppresses the tunneling of the charge carriers from the CdS nanowires to the surface atoms of the shell, resulting in more photogenerated electrons and holes confined inside the CdS cores. Consequently, passivated nonradiative recombination sites that exist on the core surfaces lead to high PL efficiency [41, 42].
The photocatalytic activities of as-obtained 1D CdS@ZnS nanocomposites were evaluated by degradation of MB and 4CP molecules under visible light irradiation (λ > 420 nm). MB was used as a test contaminant since it has been extensively used as an indicator for the photocatalytic activities [43, 44]. And its degradation can be easily monitored by optical absorption spectroscopy. Figure 5a shows the photocatalytic activities of the nanocomposites evaluated by degradation of MB. The absorption spectral changes when the MB aqueous solution was degraded with the 1D CdS@ZnS core-shell nanocomposites for 6 h. The intensity of the main absorption peaks decreased or even disappeared due to the degradation of MB, and blue-shifted due to the formation of the demethylated dyes [45]. As a comparison, the photodegradation with CdS nanowires (curve 2 in Fig. 5b), with commercial Anatase TiO2 (curve 3), photolysis in the absence of photocatalyst (curve 4), and with 1D CdS@ZnS nanocomposites in dark (curve 5) were also measured. The y-axis of degradation is referred as C/C0 in which C was the concentration of MB at each irradiated time interval determined at a wavelength of 664 nm while C0 was the starting concentration when adsorption–desorption equilibrium was achieved. From the chart, it can be seen that MB hardly decomposed under the presence of 1D nanocomposites without irradiation (curve 5). However, the absorption of MB disappeared (99.9% decomposed) after 6 h of visible light irradiation for the 1D nanocomposites (curve 1), showing much greater activity than that of CdS nanowires (63% decomposed, curve 2). In the meantime, up to 67.9% (curve 3) and 52.0% (curve 4) of MB was degraded in the presence of Anatase TiO2 or only through photolysis, respectively.
Phenolic compounds are widely used in various fields, most of which are highly toxic and can remain in the environment for a longer time due to their stability and bioaccumulation [46]. Photocatalytic treatment is a preferable approach to treat such wastewaters [47, 48]. Absorption spectral changes of 4CP aqueous solution degraded by 1D CdS@ZnS core-shell nanocomposites with different irradiation time are shown in Fig. 6a. Figure 6b shows the change of concentration of 4CP over time under different conditions (C was the concentration of 4CP determined at a wavelength of 225 nm). Control experiments indicated that the photocatalytic reaction hardly proceeded in the absence of visible light (curve 5). After 12 h irradiation, up to 74.0% (curve 2), 30.0% (curve 3), and 30.1% (curve 4) of 4CP was degraded in the presence of CdS nanowires, anatase TiO2, or only through photolysis, respectively. For the 1D CdS@ZnS nanocomposites, ca. 88.5% of 4CP was degraded under the same conditions (curve 1), showing significantly improved photocatalytic activity than others. The enhanced photocatalytic activity may be due to the surface charge modification and surface electronic states passivation of CdS cores by the ZnS shells.
Conclusion
In summary, 1D CdS@ZnS core-shell nanocomposites were successfully synthesized via a two-step mild solution method. It has been demonstrated that preformed CdS nanowires with a diameter of ca. 45 nm and a length up to several tens of micrometers were coated with a uniform layer of ZnS shell. This shell was composed of ZnS nanoparticles with a diameter of ca. 4 nm, anchoring on the surface of CdS nanowires without any surface pretreatment or functionalization. The optical properties and photocatalytic activities of the 1D nanocomposites under visible light were separately investigated. Compared to the neat CdS nanowires, the as-obtained 1D CdS@ZnS core-shell nanocomposites showed significantly enhanced photocatalytic activities owning to the effective passivation of the surface electronic states by the ZnS shells.
References
Wu Y, Xiang J, Yang C, Lu W, Lieber CM: Nature. 2004, 430: 61. COI number [1:CAS:528:DC%2BD2cXlt1CqtLg%3D]; Bibcode number [2004Natur.430...61W] COI number [1:CAS:528:DC%2BD2cXlt1CqtLg%3D]; Bibcode number [2004Natur.430...61W] 10.1038/nature02674
Gautam UK, Fang X, Bando Y, Zhan J, Golberg D: ACS Nano. 2008, 2: 1015. COI number [1:CAS:528:DC%2BD1cXltFyqtrw%3D] COI number [1:CAS:528:DC%2BD1cXltFyqtrw%3D] 10.1021/nn800013b
Jensen A, Hauptmann JR, Nygrd J, Sadowski J, Lindelof PE: Nano Lett.. 2004, 4: 349. COI number [1:CAS:528:DC%2BD2cXhvFWqtQ%3D%3D] COI number [1:CAS:528:DC%2BD2cXhvFWqtQ%3D%3D] 10.1021/nl0350027
Gudiksen MS, Lauhon LJ, Wang J, Smith DC, Lieber CM: Nature. 2002, 415: 617. COI number [1:CAS:528:DC%2BD38XhsVCjsL4%3D]; Bibcode number [2002Natur.415..617G] COI number [1:CAS:528:DC%2BD38XhsVCjsL4%3D]; Bibcode number [2002Natur.415..617G] 10.1038/415617a
Solanki R, Huo J, Freeouf JL, Miner B: Appl. Phys. Lett.. 2002, 81: 3864. COI number [1:CAS:528:DC%2BD38Xos1Snsro%3D]; Bibcode number [2002ApPhL..81.3864S] COI number [1:CAS:528:DC%2BD38Xos1Snsro%3D]; Bibcode number [2002ApPhL..81.3864S] 10.1063/1.1521570
Zhang Y, Suenaga K, Colliex C, Iijima S: Science. 1998, 281: 973. COI number [1:CAS:528:DyaK1cXlsVeqsrc%3D]; Bibcode number [1998Sci...281..973Z] COI number [1:CAS:528:DyaK1cXlsVeqsrc%3D]; Bibcode number [1998Sci...281..973Z] 10.1126/science.281.5379.973
Han S, Li C, Liu ZQ, Lei B, Zhang DH, Jin W, Liu XL, Tang T, Zhou CW: Nano Lett.. 2004, 4: 1241. COI number [1:CAS:528:DC%2BD2cXksVGqurs%3D] COI number [1:CAS:528:DC%2BD2cXksVGqurs%3D] 10.1021/nl049467o
Kong XY, Ding Y, Wang ZL: J. Phys. Chem. B. 2004, 108: 570. COI number [1:CAS:528:DC%2BD3sXptlOrs7Y%3D] COI number [1:CAS:528:DC%2BD3sXptlOrs7Y%3D] 10.1021/jp036993f
Hu JQ, Li Q, Meng XM, Lee CS, Lee ST: Chem. Mater.. 2003, 15: 305. COI number [1:CAS:528:DC%2BD38Xpt1aitb8%3D] COI number [1:CAS:528:DC%2BD38Xpt1aitb8%3D] 10.1021/cm020649y
Hsu YJ, Lu SY: Chem. Commun. (Camb.). 2004, 18: 2102. 10.1039/b403932g
Mokari T, Banin U: Chem. Mater.. 2003, 15: 3955. 10.1021/cm034173+
Manna L, Scher EC, Li LS, Alivisatos AP: J. Am. Chem. Soc.. 2002, 124: 7136. COI number [1:CAS:528:DC%2BD38XjvFCntb0%3D] COI number [1:CAS:528:DC%2BD38XjvFCntb0%3D] 10.1021/ja025946i
Kar S, Santra S, Heinrich H: J. Phys. Chem. C. 2008, 112: 4036. COI number [1:CAS:528:DC%2BD1cXisVCntbc%3D] COI number [1:CAS:528:DC%2BD1cXisVCntbc%3D] 10.1021/jp800277x
Wang ZL, Dai ZR, Gao RP, Bai ZG, Gole JL: Appl. Phys. Lett.. 2000, 77: 3349. COI number [1:CAS:528:DC%2BD3cXotFGktbs%3D]; Bibcode number [2000ApPhL..77.3349W] COI number [1:CAS:528:DC%2BD3cXotFGktbs%3D]; Bibcode number [2000ApPhL..77.3349W] 10.1063/1.1327281
Hu J, Bando Y, Liu Z, Sekiguchi T, Golberg D, Zhan J: J. Am. Chem. Soc.. 2003, 125: 11306. COI number [1:CAS:528:DC%2BD3sXmsFams7o%3D] COI number [1:CAS:528:DC%2BD3sXmsFams7o%3D] 10.1021/ja030235l
He RR, Law M, Fan R, Kim F, Yang PD: Nano Lett.. 2002, 2: 1109. COI number [1:CAS:528:DC%2BD38Xmt1Gitr4%3D] COI number [1:CAS:528:DC%2BD38Xmt1Gitr4%3D] 10.1021/nl0257216
Zhan JH, Bando Y, Hu JQ, Sekiguchi T, Golberg D: Adv. Mater.. 2005, 17: 225. COI number [1:CAS:528:DC%2BD2MXht12ltbY%3D] COI number [1:CAS:528:DC%2BD2MXht12ltbY%3D] 10.1002/adma.200400585
Teo BK, Li CP, Sun XH, Wong NB, Lee ST: Inorg. Chem.. 2003, 42: 6723. COI number [1:CAS:528:DC%2BD3sXnt1Cjtro%3D] COI number [1:CAS:528:DC%2BD3sXnt1Cjtro%3D] 10.1021/ic034397u
Zheng Y, Zheng L, Zhan Y, Lin X, Zheng Q, Wei K: Inorg. Chem.. 2007, 46: 6980. COI number [1:CAS:528:DC%2BD2sXnvFGnsLk%3D] COI number [1:CAS:528:DC%2BD2sXnvFGnsLk%3D] 10.1021/ic700688f
Lao JY, Wen JG, Ren ZF: Nano Lett. 2002, .2: 1287. 10.1021/nl025753t
Jung Y, Ko DK, Agarwal R: Nano Lett. . 2007, 7: 264. COI number [1:CAS:528:DC%2BD28XhtlehsrzM] COI number [1:CAS:528:DC%2BD28XhtlehsrzM] 10.1021/nl0621847
Bae S, Seo H, Choi H, Park J, Park J: J. Phys. Chem. B. 2004, 108: 12318. COI number [1:CAS:528:DC%2BD2cXlvVOlt74%3D] COI number [1:CAS:528:DC%2BD2cXlvVOlt74%3D] 10.1021/jp048918q
Li YQ, Tang JX, Wang H, Zapien JA, Shan YY, Lee ST: Appl. Phys. Lett. 2007, .90: 093127. Bibcode number [2007ApPhL..90i3127L] Bibcode number [2007ApPhL..90i3127L] 10.1063/1.2710743
Lauhon LJ, Gudiksen MS, Wang DL, Lieber CM: Nature. 2002, 420: 57. COI number [1:CAS:528:DC%2BD38XosVCmu7o%3D]; Bibcode number [2002Natur.420...57L] COI number [1:CAS:528:DC%2BD38XosVCmu7o%3D]; Bibcode number [2002Natur.420...57L] 10.1038/nature01141
Tao F, Liang Y, Yin G, Xu D, Jiang Z, Li H, Han M, Song Y, Xie Z, Xue Z, Zhu J, Xu Z, Zheng L, Wei X, Ni Y: Adv. Funct. Mater.. 2007, 17: 1124. COI number [1:CAS:528:DC%2BD2sXlvVGrsbk%3D] COI number [1:CAS:528:DC%2BD2sXlvVGrsbk%3D] 10.1002/adfm.200600177
Agarwal R, Barrelet C, Lieber CM: Nano Lett.. 2005, 5: 917. COI number [1:CAS:528:DC%2BD2MXis1Ois7Y%3D] COI number [1:CAS:528:DC%2BD2MXis1Ois7Y%3D] 10.1021/nl050440u
Ma R, Dai L, Qin G: Nano Lett. 2007, .7: 868. 10.1021/nl062329+
Jie JS, Zhang WJ, Jiang Y, Meng XM, Li YQ, Lee ST: Nano Lett.. 2006, 6: 1887. COI number [1:CAS:528:DC%2BD28XnsF2ht7w%3D] COI number [1:CAS:528:DC%2BD28XnsF2ht7w%3D] 10.1021/nl060867g
Chen M, Xie Y, Lu J, Xiong Y, Zhang S, Qian Y, Liu X: J. Mater. Chem.. 2002, 12: 748. COI number [1:CAS:528:DC%2BD38XhsVCgur8%3D] COI number [1:CAS:528:DC%2BD38XhsVCgur8%3D] 10.1039/b105652m
Barrelet CJ, Wu Y, Bell DC, Lieber CM: J. Am. Chem. Soc.. 2003, 125: 11498. COI number [1:CAS:528:DC%2BD3sXmvVWisb8%3D] COI number [1:CAS:528:DC%2BD3sXmvVWisb8%3D] 10.1021/ja036990g
Ye C, Meng G, Wang Y, Jiang Z, Zhang L: J. Phys. Chem. B. 2002, 106: 10338. COI number [1:CAS:528:DC%2BD38XmvFWlu7s%3D] COI number [1:CAS:528:DC%2BD38XmvFWlu7s%3D] 10.1021/jp0255785
Wang Y, Meng G, Zhang L, Liang C, Zhang J: Chem. Mater.. 2002, 14: 1773. COI number [1:CAS:528:DC%2BD38Xhs1yitb0%3D] COI number [1:CAS:528:DC%2BD38Xhs1yitb0%3D] 10.1021/cm0115564
Malik MA, O’Brien P, Revaprasadu N: Chem. Mater. 2002, . 14: 2004. 10.1021/cm011154w
Reiss P, Bleuse J, Pron A: Nano Lett. 2002, .2: 781. 10.1021/nl025596y
Danek M, Jensen KF, Murray CB, Bawendi MG: Chem. Mater.. 1996, 8: 173. COI number [1:CAS:528:DyaK2MXhtVSmtrzE] COI number [1:CAS:528:DyaK2MXhtVSmtrzE] 10.1021/cm9503137
Datta A, Panda SK, Chaudhuri S: J. Phys. Chem. C. 2007, 111: 17260. COI number [1:CAS:528:DC%2BD2sXht1WltLvL] COI number [1:CAS:528:DC%2BD2sXht1WltLvL] 10.1021/jp076093p
Hsu YJ, Lu SY, Lin YF: Adv. Funct. Mater.. 2005, 15: 1350. COI number [1:CAS:528:DC%2BD2MXoslGmsL4%3D] COI number [1:CAS:528:DC%2BD2MXoslGmsL4%3D] 10.1002/adfm.200400563
Kim MR, Kang YM, Jang DJ: J. Phys. Chem. C. 2007, 111: 18507. COI number [1:CAS:528:DC%2BD2sXhtlGqtrfL] COI number [1:CAS:528:DC%2BD2sXhtlGqtrfL] 10.1021/jp075218n
Zhan J, Yang X, Wang D, Li S, Xie Y, Xia Y, Qian Y: Adv. Mater. 2000, . 12: 1348. 10.1002/1521-4095(200009)12:18<1348::AID-ADMA1348>3.0.CO;2-X
Hsu YJ, Lu SY: Langmuir. 2004, 20: 194. COI number [1:CAS:528:DC%2BD3sXps1ymsbc%3D] COI number [1:CAS:528:DC%2BD3sXps1ymsbc%3D] 10.1021/la0347410
Xie RG, Kolb U, Li JX, Basche T, Mews A: J. Am. Chem. Soc.. 2005, 127: 7480. COI number [1:CAS:528:DC%2BD2MXjvVSju7g%3D] COI number [1:CAS:528:DC%2BD2MXjvVSju7g%3D] 10.1021/ja042939g
Wang R, Xin JH, Yang Y, Liu H, Xu L, Hu J: Appl. Surf. Sci.. 2004, 227: 312. COI number [1:CAS:528:DC%2BD2cXislyntrw%3D]; Bibcode number [2004ApSS..227..312W] COI number [1:CAS:528:DC%2BD2cXislyntrw%3D]; Bibcode number [2004ApSS..227..312W] 10.1016/j.apsusc.2003.12.012
Lachheb H, Puzenat E, Houas A, Ksibi M, Elaloui E, Guillard C, Hermman JM: Appl. Catal. B Environ.. 2001, 31: 145. 10.1016/S0926-3373(00)00276-9
Yogi C, Kojima K, Wada N, Tokumoto H, Takai T, Mizoguchi T, Tamiaki H: Thin Solid Films. 2008, 516: 5881. COI number [1:CAS:528:DC%2BD1cXmsl2ntbk%3D]; Bibcode number [2008TSF...516.5881Y] COI number [1:CAS:528:DC%2BD1cXmsl2ntbk%3D]; Bibcode number [2008TSF...516.5881Y] 10.1016/j.tsf.2007.10.050
Kieth LH, Telliard WA: Environ. Sci. Technol.. 1979, 13: 416. 10.1021/es60152a601
Shen X, Zhu L, Liu G, Yu H, Tang H: Environ. Sci. Technol.. 2008, 42: 1687. COI number [1:CAS:528:DC%2BD1cXhsVWjtL0%3D] COI number [1:CAS:528:DC%2BD1cXhsVWjtL0%3D] 10.1021/es071788p
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Wang, L., Wei, H., Fan, Y. et al. Synthesis, Optical Properties, and Photocatalytic Activity of One-Dimensional CdS@ZnS Core-Shell Nanocomposites. Nanoscale Res Lett 4, 558 (2009). https://doi.org/10.1007/s11671-009-9280-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11671-009-9280-3