Abstract
This paper presents systematic studies of hydrophilic metal oxide nanoparticles (NPs) dispersed in brine intended to reveal their potential to enhance oil recovery (EOR) in various rock wettability systems. The stability in suspension (nanofluid) of the NPs has been identified as a key factor related to their use as an EOR agent. Experimental techniques have been developed for nanofluid stability using three coupled methods: direct visual observation, surface conductivity and particle size measurements. The use of a dispersant has been investigated and has been shown to successfully improve metal oxide nanofluid stability as a function of its concentration. The dispersant alters the nanofluid properties, i.e. surface conductivity, pH and particle size distribution. A two-phase coreflood experiment was conducted by injecting the stable nanofluids as a tertiary process (nano-EOR) through core plugs with various wettabilities ranging from water-wet to oil-wet. The combination of metal oxide nanofluid and dispersant improved the oil recovery to a greater extent than either silica-based nanofluid or dispersant alone in all wettability systems. The contact angle, interfacial tension (IFT) and effluent were also measured. It was observed that metal oxide-based nanofluids altered the quartz plates to become more water-wet, and the results are consistent with those of the coreflood experiment. The particle adsorption during the transport process was identified from effluent analysis. The presence of NPs and dispersant reduced the IFT, but its reduction is sufficient to yield significant additional oil recovery. Hence, wettability alteration plays a dominant role in the oil displacement mechanism using nano-EOR.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
In recent years, most investigations have shown that nanoparticles (NPs) offer promise for future enhanced oil recovery (EOR) processes in which silica-based NPs are most commonly used (Ju et al. 2006; Miranda et al. 2012; Roustaei et al. 2012; Hendraningrat et al. 2013a). Hydrophilic silica NPs were chosen because they consist of greater than 99 % silicon oxide, which is the main constituent of sandstone reservoirs (Hendraningrat et al. 2012). Moreover, silicon oxide is not a chemical that harms the environment. However, inhalation of dried silica NPs into the human body is harmful over a long period. Miranda et al. (2012) mentioned other benefits of using silica NPs for EOR purposes. Silica NPs are an inorganic material that is easy to manipulate in terms of physical chemistry properties. In addition, silica also can be easily surface functionalised from a hydrophobic to hydrophilic state via silanization with hydroxyl groups or sulphonic acid. If the NPs do not aggregate to a larger size, they have the ability to flow through a pore size (typically measured in microns). Hence, the stability of the nanofluid becomes a critical parameter.
The rapid evolution of nanotechnology has created various types of NPs, i.e. metal oxides for multi-purpose applications in many sectors. Currently, metal oxides play an essential role in many areas of chemistry, physics and materials science (Fernandez-Garcia and Rodriguez 2007). Metal oxide-based nanofluids are frequently used for thermal conductivity and heat transfer (Fedele et al. 2011; Keblinski et al. 2008; Yu et al. 2008). The most widely used nanometals are Al2O3, MgO, ZrO2, CeO2, TiO2, ZnO and Fe2O3, and these metal oxide NPs exhibit unique physical and chemical properties (Fernandez-Garcia and Rodriguez 2007). In the oil and gas industries, the use of metal oxide NPs was recently investigated for trapping and controlling fine migration (Ahmadi et al. 2013; Ogolo et al. 2013) and reducing heavy oil viscosity by acting as a catalyst (Li et al. 2007; Hascakir et al. 2008; Shokrlu and Babadagli 2010).
Because the nanofluid is injected through a typical porous medium with a micron-sized pore throat, it is important to maintain the stability of the nanofluids in terms of nanometer size. Most NPs tend to aggregate once they are hydrated (Keller et al. 2010). The NPs aggregate easily because they have a large ratio of surface area to volume (due to the small particle size); therefore, possess high surface energies and consequently create an aggregate form to minimise these surface energies (Wu et al. 2008). The surface-to-volume ratio is an essential aspect for reactivity, which is defined as the rate at which a chemical reaction will proceed. Materials with a high surface-to-volume ratio react at much faster rates because additional surfaces are available to react. If the NPs create an aggregate form, it may lead to pore throat blocking/plugging and alter the rock properties (Ogolo et al. 2012; Hendraningrat et al. 2013b, c; Ehtesabi et al. 2014).
The classical framework theory used to describe the stability of colloids in suspension (i.e. NPs dispersed in brine as the base fluid) is the DLVO theory (named after Derjaguin, Landau, Verwey and Overbeek). The state of the NPs dispersed in brine is determined by the interactions between the NPs and between the NPs and the base fluid (Rao 2010). This theory primarily addresses the balance between two opposing forces, i.e. van der Waals (VDW) attraction and electrostatic repulsion, to explain why certain colloidal systems agglomerate while others remain discrete and dispersed in suspension. The VDW attraction is the result of forces between individual molecules in each colloid. The electrostatic repulsion becomes significant when two colloids approach each other due to charge interactions, and their double layers begin to interfere. Energy is required to minimise this repulsion by creating an aggregate form. Increasing the repulsive forces by increasing the surface charge between particles provides better stability in the suspension, because it maintains discrete particles and prevents them from gathering into larger sizes in the process known as agglomeration. Each suspension carries the same electrical charge, which produces a force of mutual electrostatic repulsion between adjacent particles. The surface conductivity is closely related to the surface charge. If the charge is sufficiently high, the colloids will remain discrete and dispersed in suspension. Decreasing the charge has the reverse effect. The particle surface charge can be controlled by modifying the suspension liquid, i.e. changing pH, shifting the ionic environment or adding a stabiliser (Rao 2010).
The actual oil reservoirs can be water-, intermediate- or oil-wet. The initial rock wettability will affect oil recovery after waterflooding and plays a vital role in oil production (Morrow 1990). In a water-wet system, the most oil will be produced before water breakthrough after which the rate will decline. Indeed, the water breakthrough will occur earlier in intermediate- or oil-wet systems than in a water-wet system. The wettability affects the relative permeability, which controls the flow and spatial distribution of fluids in a porous medium (Anderson 1987). However, the wettability is not the only parameter that controls the relative permeability curves. Anderson (1987) stated that the relative permeability curves will also be affected by pore geometry, fluid distribution, saturation, and saturation history.
The oil displacement mechanism with use of NPs is not yet clearly understood. Wasan and Nikolov (2003), Chengara et al. (2004), and Wasan et al. (2011) concluded that the structural disjoining pressure is important. The structural disjoining pressure is correlated to the fluid’s ability to spread along the surface of a substrate due to an imbalance of the interfacial forces among the solid, oil and aqueous phases (Chengara et al. 2004). The NPs create ordered structures near the three-phase contact line (wetting wedge) of a drop on a solid surface, which promotes spreading of the nanofluid along the surface as monolayer particles. The zero contact angle of the aqueous phase means that the nanofluid has completely spread and has a notably large surface area. Therefore, the fluid possesses a high surface energy with adsorption and alters the surface energy and wettability of the system (Giraldo et al. 2013).
The use of metal oxide nanofluids for EOR purposes that involve stability analysis as well as coreflood experiments with light crude oil and Berea sandstones in various wettability systems has not yet been reported. This paper describes investigation of metal oxide NPs in various initial rock wettability systems to evaluate these materials as alternative solutions for future EOR. Experimental studies on nanofluid stabilities were performed using three techniques: direct visual observation, surface conductivity measurement and particle size analysis. The use of a dispersant in metal oxide NPs was investigated at various concentrations and temperatures. A two-phase coreflood experiment was conducted by injecting those stable nanofluids as a tertiary process (nano-EOR) through Berea sandstone core plugs with various wettability systems ranging from water- to oil-wet. The reason for using different wettabilities in this research was to identify the most suitable conditions for each type of NPs. Therefore, the relationship between oil recovery, metal oxide NPs, and initial rock wettability could be identified. The fluid–fluid and rock–fluid interactions were analysed via contact angle measurement, interfacial tension (IFT) measurement and effluent analysis to observe possible oil displacement mechanisms.
Experiments
Fluids
Degassed crude oil from a field in the North Sea was used as the oleic phase in this study. This oil has a viscosity of approximately 5.1 cP at 22 °C. For the base aqueous phase, a synthetic reservoir brine was prepared from sodium chloride (NaCl) at 3.0 wt. % (approx. 30,000 ppm) and de-ionised water. The density and viscosity were measured using a pycnometer and a Brookfield rotating viscometer (model LVDV-II + P), respectively. The pH and surface conductivity were measured using a digital pH meter Metroohm (serial 827). This brine was used as the dispersion fluid for the NPs, and the fluid properties are summarised in Table 1. Adding NPs into the brine slightly decreased its density and pH value, whereas the viscosity and surface conductivity were increased.
Nanoparticle preparation and characterisation
Three fumed hydrophilic oxide NPs, i.e. aluminium (Al2O3), titanium (TiO2), and silica (SiO2), were employed in this study. These NPs were selected due to similar specific surface areas (Brunauett–Emmett–Teller/BET) of approximately 45–65 m2/g. The average primary particle sizes of those NPs were declared as 17 nm for Al2O3, 21 nm for TiO2 and 40 nm for SiO2. Table 2 lists the properties of the NPs. Characterisation and elemental analysis of NPs were carried out using a scanning electron microscope (SEM, Hitachi Model S-5500) and integrated energy-dispersive X-ray spectroscopy (EDX), as shown in Figs. 1, 2, 3. The carbon appears because the NPs were placed on carbon conductive tape. Based on this characterisation, the NPs took on a secondary form after aggregation under SEM that is much larger than their primary particle size. As explained in the previous section, the NPs easily aggregate because they have a large surface-to-volume ratio (due to the small particle size) and therefore possess high surface energies. The NPs consequently create an aggregate form to minimise this surface energy. In addition, materials with high surface-to-volume ratios react at much faster rates because additional surfaces are available to react. To obtain a more precise particle size characterisation, the NanoSight instrument was used, which operates based on a conventional optical microscope concept but uses a laser light source to illuminate nano-sized particles within a sample introduced to the viewing unit via a disposable syringe, and the particles subsequently scatter the light. The detector measures the NPs in a particular area (Nanosight 2009).
Nanofluid preparation and characterisation
Each type of NP was synthesised using brine with a weight concentration of 0.05 wt. %. This concentration was selected based on our previous concentration optimisation study of silica NPs (Hendraningrat et al. 2013c). The nanofluids were synthesised using high-speed magnetic stirring and ultra-sonication at 60–100 % amplitude. The fluid properties of the nanofluids are provided in Table 1. Figure 4 shows brine (NaCl 3 wt. %) containing NPs at 0.05 wt. % at the initial condition. Of the group, the TiO2 nanofluid is the milkiest in appearance due to original colour from the particles. The characterisation of NP sizes and distributions dispersed in brine were measured using nanoSight. Figure 5 shows the NP distribution measurements dispersed in brine, ranging from 0 nm to greater than 1,000 nm in particle size. The means of the NP diameters measured from NanoSight are 98 nm for Al2O3, 106 nm for TiO2 and 53 nm for SiO2.
Nanofluid stabilising agent
A polyvinylpyrrolidone (PVP) stabiliser known as Povidone is used in this study. This material has an ultrafine amorphous form, a size of approximately 50–250 μm and a bulk density of 400–600 g/L (Folttmann and Quadir 2008). The molecular form of PVP is (C6H9NO)n, and the chemical structure of PVP is shown in Fig. 6. An advantage of PVP is its universal solubility both in hydrophilic and hydrophobic solvents (Folttmann and Quadir 2008), and it is a non-toxic stabiliser that is safe for the environment. Currently, PVP is widely used as a binder for capsules and granules (especially in pharmaceuticals), a film former in medical plastics, a taste masker in chewable tablets and a toxicity reducer (Folttmann and Quadir 2008). In this study, PVP type K30 was added to avoid earlier NP aggregation by improving the metal oxide nanofluid stability. The K30 refers to the K value of this PVP in the range 27.0–32.4. The K value characterises the mean molecular weight of PVP, and the higher the K values, the higher the molecular weight.
Core preparation and characterisation
All cores used in this study consisted of Berea sandstone, which is commonly used as a sandstone core porous medium in most laboratory research. The core has an average diameter and length of 3.8 and 4.0 cm, respectively. All cores were first cleaned with methanol and dried in a heating cabinet at 80 °C for 2–3 days until no dry weight alteration was observed before and after cleaning based on standard laboratory procedure (Torsæter and Abtahi 2003). The porosities were measured using a helium porosimeter, resulting in values from 15 to 17 %. Selected cores were cut into smaller specimens for characterisation purposes. Others were used in further ageing processes to alter the original wettability from water-wet to intermediate- and oil-wet systems. The pore size of Berea sandstone was observed using SEM, which reported micron-sized pores, as shown in Fig. 7.
The core mineralogy was characterised using two methods: energy-dispersive X-ray (EDX) and X-ray diffraction (XRD). Figure 8 shows the EDX elemental analysis of areas A and B. The only elements present in both locations are Si, O, Al and K. Reactive clays such as ‘Na+’, ‘Ca+2’, ‘Cl−’, or ‘Mg+2’ were not identified based on this analysis, but a minor amount of those elements may be present. Table 3 provides the XRD analysis data from four samples and shows consistent results. The core was dominated by quartz, which is composed of elements Si and O (91–93 %). The potassium (K+) and aluminium (Al+3) may originate from either alkali feldspar (KAlSi3O8) or residues. The minor residue is identified as pyroxene, which has the general formula XYZ2O6, where X = Mg+2, Fe+2, Mn+2, Li+, Ca+2, Na+; Y = Al+3, Fe+3, Cr+3, Cr+3, Ti+4, Mg+2, Fe+2, Mn+2; and Z = Si, Al+3, Fe+3. The XRD results are consistent with the EDX results. Hence, it was assumed that the obtained mineralogy is representative for all core plugs studied in this work.
Quartz plate preparation
A series of rectangular transparent plates of quartz was used as the solid substrates in this study. Each quartz plate has average dimensions of 2.8 cm in length, 1.5 cm in width and 0.19 cm in height. The quartz plates were first cleaned with a detergent solution and rinsed with methanol followed by distilled water. The plates were dried in a heating cabinet at 50–60 °C for 3–5 days. The original wettability of the quartz plate was observed by measuring the contact angle between brine and crude oil and is considered as water-wet (Hendraningrat et al. 2013a).
Nanofluid stability analysis
Nanofluid stability analysis was carried out using three coupled techniques: direct visual observation, surface conductivity measurement and NanoSight. The visual observation was conducted at various temperatures: room temperature, 50 and 80 °C. The dispersant PVP was used and studied to avoid early metal oxide NP aggregation. Three different concentrations of PVP were studied: 0.1, 0.5 and 1.0 wt. %. The surface conductivity of each nanofluid solution was measured using a digital pH meter. Each colloid carries a “like” surface charge that produces a force of mutual electrostatic repulsion between adjacent particles. The surface conductivity is closely related to the surface charge. If the charge is sufficiently high, the colloids will remain in discrete form and exhibit good stability in suspension. Decreasing the surface charge has the reverse effect. The particle stability also can be observed using NanoSight. The nanofluids will be unstable if particles aggregate and create a secondary form that is larger than the primary particle size. NanoSight is a useful technique for identifying the particle size and its distribution in solution.
Wettability alteration via an ageing process
The original wettability of the cores and quartz plates was altered from water-wet to intermediate- and oil-wet via an ageing process. The wettability of porous rock was determined using the Amott test, which combines spontaneous and forced displacement at room conditions with a wettability index (IW) formula as follows:
where Vo describes the oil volume produced from the imbibition process, Vw describes the water volume from the drainage process, subscript ‘1’ denotes a spontaneous displacement process and ‘2’ indicates a forced displacement process.
The wettability index (IW) of a porous medium can be correlated with the contact angle obtained from a smooth surface by the inversed cosine (arccos) of the contact angle. A water-wet system is represented by an IW from +0.25 to +1.0 (contact angle from 0o to 75o), intermediate-wet by an IW from −0.25 to +0.25 (contact angle from 75o to 105o) and oil-wet by an IW from −0.25 to −1.0 (contact angle from 105o to 180o). The original wettabilities of the Berea sandstone cores show an Amott–Harvey wettability index (IW) ranging from +0.7 to +0.9 and are considered as strongly water-wet (Hendraningrat et al. 2013d). Ageing in crude oil altered the Berea core plugs to intermediate-wet. The ageing process took approximately 4 weeks at temperatures of 80–90 °C and altered the core wettability IW to an average of +0.05 (Li et al. 2013). At the same time, a mixture of 70 % (V/V) Pentane (C5–H12) and 30 % (V/V) Surfasil™ (C8–H24–Cl2–O3–Si4) was used to alter the core and quartz plate wettability from water-wet to oil-wet. Surfasil™ can be used for surface treatment purposes. The latter process took approximately 6 days at room temperature. Based on the Amott test, the substrate has an IW in the range from −0.5 to −0.6 and is considered oil-wet.
Contact angle measurement
The contact angle was measured directly on transparent quartz plates using a Goniometry KSV CAM instrument at ambient conditions. The system consists of a quartz plate as the solid, a degassed crude oil from a field in the North Sea as the oleic phase and nanofluids as the aqueous phase, as shown in Fig. 9. The measurement is based on the Young–Laplace formula as follows:
where σ describes the interfacial tension components of phase, indices s and l stand for the solid and liquid phases, respectively, σsl represents the interfacial tension between the two phases and θ is the contact angle corresponding to the angle between vectors σl and σsl.
Treiber et al. (1971) defined the contact angle in a three-phase system (water, oil and rock surface) as follows: water-wet in the range of 0o–75o, intermediate/neutral-wet in the range of 75o–105o and oil-wet in the range of 105o–180o. A zero contact angle indicates that the denser fluid completely wets the solid.
Interfacial tension measurement
The interfacial tension (IFT) of degassed crude oil was measured against brine/nanofluids as the aqueous phase using a SVT20 spinning drop video tensiometer at room temperature, as shown in Fig. 10. This measurement involves crude oil with brine and silica-based and Al2O3-based nanofluids with PVP. Due to poor clarity, the IFT of the TiO2-based NPs with PVP nanofluid could not be measured. The rotational speed was maintained near 5,000–6,000 rpm. The formula used to measure IFT is as follows (Than et al. 1988):
where σ is the interfacial tension (dyn/cm), ∆ρ is the density difference (g/cm3), Ω is the rotational rate of the cylinder (s−1), Dapp is the measured drop diameter (cm), n is the refractive index of the heavy fluid, D is the true diameter of the drop (D = \(\frac{{D_{\text{app}} }}{n}\)), JD is a correction factor and a function of L/D, and L/D is the aspect ratio (e.g. the ratio of the drop length to its diameter).
Coreflood procedure
All cores were fully saturated with brine in a vacuum container for approximately 1–2 days. The liquid (brine) permeability of cores was measured with a range of 100–400 mD. The two-phase oil–water system coreflooding instrument is shown in Fig. 11. The sleeve pressure was set to a constant 20 bar in the Hassler core cell. The drainage process was started by injection of degassed crude oil at a flowrate from 1 to 40 cm3/min with approximately 8–10 of pore volume (PV) until no more brine was produced and thus the initial water saturation was established. As a first forced imbibition process, brine (denoted as WF1) was injected at a constant rate of 0.2 cm3/min with a range of 3–5 PV into the core plugs until no more oil was produced and thus residual oil saturation was established due to waterflooding. The injection rate was chosen to approximate the typical reservoir velocities. Next, the injection was continued at a similar injection rate and pore volume of nanofluids (silica and metal oxides) as a tertiary recovery process (denoted as NF). In the final stage, brine was re-injected (denoted as WF2) in a range of 3–5 PV under the same conditions as those of previous flooding. The recovered oil was accumulated into a gravity-settling separator and calculated based on material balance. A camera was installed to record the oil recovery during the flooding process, and the effluents were collected in a water accumulator. For each sequential flooding process, the effluent was collected at the last PV to analyse its pH and surface conductivity alterations to avoid contamination from the previous sequence. A differential pressure transmitter in the range of 0–30 bar was connected to the inlet and outlet ends of the core holder to measure and record the pressure drop across the core during the flooding process. The data were recorded into a computer in real time. As a comparison, brine with dispersant alone was used in the tertiary flooding and is discussed in the following section.
Results and discussion
Nanofluid stability analysis
Providing a stable nanofluid is challenging, because NPs have a tendency to aggregate due to forces of different natures that interact amongst particles and may lead to agglomeration (Fedele et al. 2011). Decreasing the stability of nanofluids will reduce their advantages. We observed that nanofluid stability has been observed as a critical issue prior to use as EOR agents (Hendraningrat et al. 2013b). The stability of nanofluids is a function of its concentration as dispersed in brine. During the injection process, the tendency of NPs to agglomerate will affect the porosity and impair permeability. It was also observed that oil recovery is not proportional to the nanofluid concentration, which means that oil recovery is enhanced if the nanofluid concentration increases but decreases if the concentration is higher than a critical value. For oil recovery, the critical value seems to be an optimum hydrophilic nanofluid concentration of 0.05 wt. %, and we selected this concentration in this study. The nanofluid stability analysis was developed using three techniques: direct visual observation, surface conductivity measurement and particle size analysis.
Based on our visual observation of stability over 168 h, as shown in Figs. 12, 13, untreated hydrophilic metal oxide NPs (0.05 wt. %) were much easier to precipitate than silica dioxide when dispersed in brine solution. As shown in Fig. 12, these particles began to precipitate in less than 1 h at room conditions. The A2O3-based nanofluid was completely precipitated after approximately 3 h, and the TiO2-based nanofluid agglomerated slightly later (Fig. 13). The SiO2-based nanofluids show much better stability over approximately 24–48 h. Thermal stability was also observed at room temperature, 50 and 80 °C, as shown in Fig. 14, to determine the stability in reservoir temperature conditions. The behaviour appears analogous for metal oxides at room conditions, which means that the higher temperature does not significantly affect the NP aggregation. These visual stability observations are consistent with the surface conductivity measurements, as shown in Table 1. The SiO2-based nanofluid has the highest surface conductivity (49.9 mV) among the nanofluids, whereas the Al2O3-based nanofluid has the lowest (29 mV). The surface conductivity is inversely related to the pH value, and the higher the particle charge potential, the more stable is the nanofluid. The surface conductivity is closely related to the surface charge. If the charge is sufficiently high, the colloids will remain discrete and dispersed in suspension.
Determination of the mean particle size dispersed in brine was carried out using NanoSight, as shown in Fig. 5, and the results are summarised as follows: 98 nm for Al2O3, 106 nm for TiO2 and 53 nm for SiO2. Although the SiO2 nanoparticle has the largest primary particle size (40 nm) among the NPs used in this study (see Table 2), its mean diameter is the smallest when dispersed in brine (Fig. 15). The Al2O3 NPs have the highest degree of aggregation, almost six times larger than the primary particle size. These results are consistent with those from two previous techniques in which Al2O3-based nanofluid precipitated fastest and had the lowest surface conductivity. The development of three coupled techniques was successful in identifying nanofluid stability.
Effect of adding a stabiliser
To improve metal oxide nanofluid stability, PVP (Povidone K30) is added at three different weight concentrations of 0.1, 0.5 and 1.0 wt. % but was not added to the silica-based nanofluid because this suspension was considered stable with a mean particle size distribution close to the average single particle size. Visual stability was observed at 50 °C during a 168-hour period, as shown in Figs. 14, 16. It was observed that PVP provided better stability at particular concentrations. At a low concentration of 0.1 wt. %, PVP does not provide any effect on the metal oxide nanofluid stability. Increasing the PVP concentration to 1.0 wt. % provides better stability, and at 1.0 wt. % of PVP, the nanofluid stability was investigated for more than 96 h for the Al2O3-based nanofluid but over shorter time period for the TiO2-based nanofluid, approximately 48 h. However, both conditions showed good stability at higher temperatures, i.e. 50 °C.
Addition of PVP also altered such nanofluid properties as pH and surface conductivity. Figure 17 shows how PVP significantly changed these nanofluid properties, but density and viscosity were not significantly altered. Higher PVP concentrations caused lower pH values and higher surface conductivities on metal oxide nanofluids, higher than those of SiO2 nanofluids. At higher PVP concentrations (0.5 and 1 wt. %), the surface conductivity of Al2O3 nanofluids exceeded that of TiO2 nanofluids. The highest conductivity of Al2O3 is similar only to that of brine with PVP (1 wt. %). These results are consistent with the visual stability observation in which the Al2O3 nanofluid with PVP showed better stability than TiO2 nanofluids at the given high PVP concentration. For nanofluid stability, it may be of interest to find a suitable dispersant for each metal oxide NP together with its optimum concentration. Fedele et al. (2011) observed that PEG 600 (Alfa Aesar) is a suitable dispersant for TiO2-based nanofluids.
A dispersant (PVP) with 1 wt. % concentration in metal oxide NPs was selected for the particle size distribution study, as shown in Figs. 18 and 19. The presence of PVP successfully increased the intensity of the mean particle diameter, closer to the primary particle size of 26 nm for Al2O3 NPs and 29 nm for TiO2 NPs. Stable nanofluids were identified by increasing the population of small-sized NPs dispersed in brine. The mean particle size grows larger with time (7 days) due to aggregation but their diameter is identified as equal to or a slightly greater than the size of the nanofluid without PVP in the range of 80–150 nm, which is much smaller than the size of the pore throat (typically in micron size). These observations demonstrate the potential for EOR processes in Berea sandstone, because the nanofluid may easily flow through a core pore throat of micron size.
Coreflood experiment
The coreflood experiment results from several Berea core plugs are summarised in Table 4. A dispersant (PVP) at 1 wt. % was added to the metal oxide-based nanofluid based on previous stability analysis. The average oil recoveries after waterflooding with brine (WF1) are in the range of 52–57 % of original oil in place (OOIP) for a water-wet system, 53–60 % of OOIP for an intermediate-wet system and 42–51 % of OOIP for an oil-wet system. Morrow (1985) observed that oil recovery reached a maximum for cores in an intermediate-wet system, which is likely related to disconnection and trapping of the oil phase. After a water cut of 100 %, nanofluids were injected as a tertiary recovery process (nano-EOR, denoted as NF). The nanofluids successfully reduced residual oil saturation. However, as shown Figs. 20, 21, 22, the nanofluids required a certain amount of time to displace additional oil, at least 0.5 PV during NF, likely due to physicochemical interactions between the NPs and the grain surfaces. The additional oil recovery from the NF sequence of both metal oxide-based nanofluids is much greater than that of silica-based nanofluid, especially in a water-wet system. The additional oil recovery (NF) of metal oxide-based nanofluids decreased as the wettability changed from water- to intermediate- and oil-wet systems. However, the TiO2-based nanofluid (with PVP) showed the best performance in this sequence (NF) in all wettability systems. The absence of metal oxide NPs in brine with dispersant solution had no significant impact on the additional oil recovery. Hence, the combination of metal oxides and dispersant shows great potential for EOR. In the last sequence (WF2), brine was re-injected to flush out any remaining particles and might have reduced residual oil in the core. The most interesting result came from the silica-based nanofluid. As shown, the residual oil saturation decreased dramatically from 11 to 19 % points of PV, whereas the oil recovery increased from 19 to 25 % points of OOIP in all wettability systems, and the trend appears identical in all silica-based nanofluid cases. Metal oxide NPS have a greater ability to adsorb into the pore throat than silica NPs, and pH plays significant role in the trapping mechanism (Ogolo et al. 2013). The effectiveness of particle trapping is greater at lower pH. Both metal oxide-based nanofluids (with PVP) provide much lower pH values than the silica-based nanofluid and tend to adsorb inside the pore throat rather than washing out during the NF and WF2 sequences. Silica oxide NPs have a low adsorption capacity and are easily washed-out (due to negative charges) and displace more oil. The NP adsorption during transport in a porous medium involves physicochemical interactions between NPs and grain surfaces (Zhang et al. 2013).
Figure 23 shows the filtration mechanism of NPs in Berea sandstone from observation of the inlet point of cores after the WF2 sequence. It is clear that there were no surface nano-cakes formed during NF flooding in all cases (metal oxides with PVP and silica-based nanofluids). Increasing the injection rate may affect the accumulation of NPs at the core inlet (Hendraningrat et al. 2013d). The particle velocity through the porous medium might be lower than the nanofluid injection rate and will create nano-caking (increasing pressure drop) at an injection rate of 0.8 cm3/min, as shown in Fig. 23d. If the nanofluid remains stable at nanometer size, core plugging could be avoided and a physicochemical adsorption mechanism might occur between the particles and the porous medium.
Displacement mechanism
In this study, several possible measurements, i.e. contact angle, IFT and effluent analyses, were conducted to identify the oil displacement mechanism using metal oxide NPs. Karimi et al. (2012) observed that ZrO2 plays an important role in the wettability alteration of a carbonate reservoir rock, whereas it could also change the wettability of the rock from a strongly oil-wet to strongly water-wet condition. Giraldo et al. (2013) observed that alumina-based nanofluids altered the wettability of cores from an oil-wet to a water-wet condition. Ehtesabi et al. (2014) reported a similar phenomenon in which the rock wettability changed from an oil- to water-wet condition after treatment with TiO2 NPs. Therefore, metal oxide-based nanofluids may change the rock wettability and affect the oil displacement mechanism.
Figure 24 shows the contact angle measurements for different aqueous phases in a water-wet system (a) and an oil-wet system (b). Once the hydrophilic metal oxide (with PVP) is introduced into the brine, it reduces the contact angle from 54o to 21o, which means that metal oxide-based nanofluids have rendered the quartz plate more strongly water-wet. In contrast, PVP alone rendered the quartz weakly water-wet. The highest reduction in contact angle was achieved with the TiO2-based nanofluid, consistent with the oil recovery results obtained from the TiO2-based nanofluid applied as tertiary recovery (NF) in a water-wet system. Due to the poor clarity of the TiO2-based nanofluid in the oil-wet system, the measurements could not be performed in addition to IFT measurements. Similar to the water-wet system, the presence of hydrophilic NPs in brine tends to change the quartz plate to a weakly oil-wet system. However, the silica-based nanofluid is more effective in an oil-wet system than an Al2O3-based nanofluid, a result consistent with the observation that additional oil recovery from SiO2-based nanofluid is greater than with Al2O3-based nanofluid in an oil-wet system.
The IFT was measured at room temperature, as shown in Table 5, and a brine-crude oil system is used with the base value of 19.2 mN/m and a pH value of 6.76. The presence of NPs reduced the IFT between the oleic phase and the aqueous phase as well as the presence of PVP as dispersant. The lowest IFT was achieved with metal oxide NPs, although they do not have the lowest pH. As shown in Fig. 17, the lowest pH was obtained from brine with PVP solution (approx. pH 3.6), and metal oxide-based nanofluids have a pH in the range 4–5. Additional oil recovery due to a silica-based nanofluid is greater than that of a brine with PVP solution, even though silica-based nanofluids have a higher IFT than a brine with PVP solution. It can be concluded that the degree of IFT reduction is not a main parameter in oil displacement in nano-EOR.
In addition, the pH and surface conductivity of the effluent were also analysed, and the results are summarised in Table 6. Based on the measurements, the pH value and surface conductivity of injected brine were altered in all cores before and after injection of NF. The effluent became more acidic (lower pH) and the surface charge increased. This alteration may have occurred due to adsorption of NPs during NPs transport through the porous medium, resulting in wettability alteration. This particle retention during NP transport in porous media has been observed in a previous study (Hendraningrat et al. 2013b). The trend of the pH value of Al2O3-based nanofluids after the WF2 sequence is lower than in the NF sequence and has the highest capacity for adsorption into the pore throat amongst the other nanofluids due to the lowest pH. It is observed that pH plays a significant role in the trapping mechanism, and Al2O3 is identified as one of the most effective NPs for trapping and migrating in fine sand (Ogolo et al. 2013). However, the pH reduction is not the main cause of the displacement mechanism, as demonstrated in the case of brine with PVP alone. This solution has the lowest pH but does not have a significant effect on additional oil recovery for either the NF or WF2 sequences. Although pH induced an IFT reduction, the relationship is not proportional to the additional oil recovery. Hence, wettability alteration plays a dominant role in the oil displacement mechanism using nano-EOR.
Concluding remarks and future work
A systematic study of hydrophilic metal oxide nanoparticles (NPs) for EOR purposes was performed, and the stability of metal oxide-based nanofluids was successfully improved by adding PVP at 1 wt. %. The PVP altered the fluid properties, i.e. pH and surface conductivity, and provided better nanofluid stability. The combinations of metal oxide nanofluids and PVP improved oil recovery to a greater extent than silica-based nanofluid and dispersant alone, and the TiO2-based nanofluid was especially effective for all wettability systems. The additional oil recovery (NF) of metal oxide-based nanofluids decreased as the wettability changed from water- to intermediate- and oil-wet systems. The contact angle, interfacial tension (IFT) and effluent were measured and analysed in the displacement mechanism observations. It was observed that all nanofluids rendered the quartz plate more water-wet, and the TiO2-based nanofluid was the most effective wettability-altering fluid. This result is consistent with and proportional to the additional oil recovery from the coreflood experiment. The particle adsorption during the transport process was identified from the effluent analysis. The presence of NPs reduced the IFT between the oleic phase and aqueous phase as did the presence of PVP as dispersant, but the degree of IFT reduction is not proportional to the additional oil recovery. The lowest IFT was achieved by metal oxide NPs even though this material does not have the lowest pH. The additional oil recovery due to silica-based nanofluid is greater than that of brine with PVP solution, even though the silica-based nanofluid has a higher IFT than the brine with PVP solution. Therefore, wettability alteration plays a dominant role in the oil displacement mechanism using nano-EOR. Finding a suitable stabiliser for each nanofluid and its optimum concentration might be important in future work as well as repeating the experiment with representative formation water at reservoir conditions.
SI metric conversion factors
References
Ahmadi M, Habibi A, Pourafshary P (2013) Zeta-potential investigation and experimental study of nanoparticles deposited on rock surface to reduce fines migrations. SPE J 18(3):534–544 (SPE-142633-PA)
Anderson WG (1987) Wettability literature survey-part 5: the effects of wettability on relative permeability. J Pet Tech 39(11):1453–1468 (SPE-16323-PA)
Chengara A, Nikolov A, Wasan DT, Trokhymchuck A, Henderson D (2004) Spreading of nanofluids driven by the structural disjoining pressure gradient. J Colloid Interface Sci 280:192–201
Ehtesabi H, Ahadian MM, Taghikhani V, Ghazanfari MH (2014) Enhanced heavy oil recovery in sandstone cores using TiO nanofluids. Energy Fuels 28(1):423–430
Fedele L, Colla L, Bobbo S, Barison S, Agresti F (2011) Experimental stability analysis of different water-based nanofluids. Nanoscale Res Lett 6:300
Fernandez-Garcia M, Rodriguez JA (2007) Metal oxide nanoparticles. Brookhaven National Laboratory, New York
Folttmann H, Quadir A (2008) Polyvinylpyrrolidone (PVP)–One of the most widely used excipients in pharmaceuticals: an overview. Drug Deliv Technol 8(6):22–27
Giraldo J, Benjumea P, Lopera S, Cortés FB, Ruiz MA (2013) Wettability alteration of sandstone cores by alumina-based nanofluids. Energy fuel 27:3659–3665
Hascakir B, Babadagli T, Akin S (2008) Experimental and numerical modeling of heavy-oil recovery by electrical heating. Paper SPE/PS/CHOA 117669-MS presented at the international thermal operations and heavy oil symposium, Calgary, Canada, 20–23 October 2008
Hendraningrat L, Shidong L, Torsæter O (2012) A glass micromodel experimental study of hydrophilic nanoparticles retention for EOR project. Paper SPE 159161-MS presented at the SPE Russian oil & gas exploration & production technical conference and exhibition, Moscow, Russia, 16–18 October 2012
Hendraningrat L, Li S, Torsæter O (2013a) A coreflood investigation of nanofluid enhanced oil recovery. J Petrol Sci Eng 111:128–138
Hendraningrat L, Engeset B, Suwarno S, Li S, Torsæter O (2013b) Laboratory investigation of porosity and permeability impairment in Berea sandstones due to hydrophilic nanoparticle retention. Paper SCA2013-062 presented at the international symposium of the society of core analysts held in Napa Valley, California, USA, 16–19 September 2013
Hendraningrat L, Li S, Torsæter O (2013c) A coreflood investigation of nanofluid enhanced oil recovery in low-medium permeability Berea sandstone. Paper SPE 164106-MS presented at SPE international symposium on oilfield chemistry, The Woodlands, Texas, 8–10 April 2013
Hendraningrat L, Li S, Torsæter O (2013d) Effect of some parameters influencing enhanced oil recovery process using silica nanoparticles: an experimental investigation. Paper SPE-165955 presented at SPE Reservoir Characterisation and Simulation Conference and Exhibition, Society of Petroleum Engineers, Abu Dhabi, UAE, 16–18 September 2013
Ju B, Tailiang F, Mingxue M (2006) Enhanced oil recovery by flooding with hydrophilic nanoparticles. China Particuology 4:41–46
Karimi A, Fakhroueian Z, Bahramian A, Khiabani NP, Darabad JB, Azin R, Arya S (2012) Wettability alteration in carbonates using zirconium oxide nanofluids: EOR Implications. Energy Fuels 26(2):1028–1036
Keblinski P, Prasher R, Eapen J (2008) Thermal conductance of nanofluids: is the controversy over? Nanopart Res 10:1089
Keller AA, Wang H, Zhou D, Lenihan HS, Cherr G, Cardinale BJ, Miller R, Ji Z (2010) Stability and aggregation of metal oxide nanoparticles in natural aqueous matrices. Environ Sci Technol 44(6):1962–1967
Li W, Zhu J, Qi J (2007) Application of nano-nickel catalyst in the viscosity reduction of Liaohe extra-heavy oil by aqua-thermolysis. J Fuel Chem 35(2):176–180
Li S, Kaasa AT, Hendraningrat L, Torsæter O (2013). Effect of silica nanoparticles adsorption on the wettability index of Berea sandstone. Paper SCA2013-059 presented at the international symposium of the society of core analysts held in Napa Valley, California, USA, 16–19 September 2013
Miranda CR, De Lara LS, Tonetto BX (2012) Stability and mobility of functionalized silica nanoparticles for enhanced oil recovery application. Paper SPE 157033-MS presented at SPE international oilfield technology conference, Noordwijk, The Netherlands, 12–14 June 2012
Morrow NR (1985) A review of the effects of initial saturation, pore structure, and wettability on oil recovery by waterflooding. In: Proceeding of the north sea oil and gas reservoirs seminar. Graham and Trotman, Ltd: 179-191, Trondheim, Norway, 2–4 December 1985
Morrow NR (1990) Wettability and its effect on oil recovery. J Pet Tech 42(12):1476–1484 (SPE-21621-PA)
Nanosight (2009) Operating manual. NanoSight Ltd., UK
Ogolo NA, Onyekonwu MO Akaranta O (2013) Trapping mechanism of nanofluids on migrating fines in sand. Paper SPE 167502-MS presented at the Nigeria annual international conference and exhibition, Lagos, Nigeria, 30th July–1st August 2013
Ogolo NA, Olafuyi OA, Onyekonwu MO (2012) Enhanced oil recovery using nanoparticles. Paper SPE 160847-MS presented at the SPE Saudi Arabia section technical symposium and exhibition, Al-Khobar, Saudi Arabia, 8–11 April 2012
Rao Y (2010) Nanofluids: stability, phase diagram, rheology and applications. Particuology 8:549–555
Roustaei A, Saffarzadeh S, Mohammadi M (2012) An evaluation of modified silica nanoparticles’ efficiency in enhancing oil recovery of light and intermediate oil reservoirs. Egypt J Petrol 22(3):427–433
Shokrlu YH, Babadagli T (2010) Effects of nano-sized metals on viscosity reduction of heavy oil/bitumen during thermal applications. Paper CSUG/SPE 137540-MS presented at the Canadian unconventional resources and international petroleum conference, Calgary, Canada, 19–21 October 2010
Than P, Preziosi D, Joseph D, Arney M (1988) Measurement of interfacial tension between immiscible liquids with the spinning rod tensiometer. J Colloid Interface Sci 124(2):552–559
Torsæter O, Abtahi M (2003) Experimental reservoir engineering laboratory workbook. Department of Petroleum Engineering and Applied Geophysics, Norwegian University of Science and Technology (NTNU), Trondheim
Treiber LE, Duane LE, Archer L, Owens WW (1971) A laboratory evaluation of the wettability of fifty oil-producing reservoirs. SPE J 12:531–540
Wasan DT, Nikolov A (2003) Spreading of nanofluids on solids. J Nat 423:156–159
Wasan DT, Nikolov A, Kondiparty K (2011) The wetting and spreading of nanofluids on solids: role of the structural disjoining pressure. Curr Opin Colloid Interface Sci 16:344–349
Wu W, He Q, Jiang C et al (2008) Magnetic iron oxide nanoparticles: synthesis and surface functionalization strategies. Nanoscale Res Lett 3:397–415
Yu W, France DM, Routbort JL, Choi SUS (2008) Review and comparison of nanofluid thermal conductivity and heat transfer enhancements. Heat Transfer Eng 29:432
Zhang T, Murphy M, Yu H, Bagaria H, Nielson B, Bielawski C, Johnston K, Huh C, Bryant S (2013) Investigation of nanoparticle adsorption during transport in porous media. Paper SPE 166346-MS presented at the SPE annual technical conference and exhibition, New Orleans, Lousiana, 30th September–2nd October 2013
Acknowledgments
The authors gratefully acknowledge Evonik Industries AG and Elkem Silicon Materials for providing nanoparticles and the Department of Petroleum Engineering and Applied Geophysics, Norwegian University of Science and Technology (NTNU) for financial support necessary to complete this study and permission to publish this article.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution, and reproduction in any medium, provided the original author(s) and the source are credited.
About this article
Cite this article
Hendraningrat, L., Torsæter, O. Metal oxide-based nanoparticles: revealing their potential to enhance oil recovery in different wettability systems. Appl Nanosci 5, 181–199 (2015). https://doi.org/10.1007/s13204-014-0305-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13204-014-0305-6