Abstract
The interests in the biomedical impact of tannic acid (TA) targeting production of various types of biomaterials, such as digital microfluids, chemical sensors, wound dressings, or bioimplants constantly increase. Despite the significant disadvantage of materials obtained from natural-based compounds and their low stability and fragility, therefore, there is an imperative need to improve materials properties by addition of stabilizing formulas. In this study, we performed assessments of thin films over TA proposed as a cross-linker to be used in combination with polymeric matrix based on chitosan (CTS), i.e. CTS/TA at 80:20 or CTS/TA at 50:50 and poly(ethylene glycol) (PEG) at the concentration of 10% or 20%. We evaluated their mechanical parameters as well as the cytotoxicity assay for human bone marrow mesenchymal stem cells, human melanotic melanoma (MNT-1), and human osteosarcoma (Saos-2). The results revealed significant differences in dose-dependent of PEG regarding the maximum tensile strength (σmax) or impact on the metabolic activity of tissue culture plastic. We observed that PEG improved mechanical parameters prominently, decreased the hemolysis rate, and did not affect cell viability negatively. Enclosed data, confirmed also by our previous reports, will undoubtedly pave the path for the future application of tannic acid-based biomaterials to treat wound healing.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Polymers have multiple capabilities to be used in targeting production of various types of biomaterials, for instance, digital microfluids, chemical sensors, wound dressings, or bioimplants (Jayaprakash et al. 2015; Kang et al. 2011; Sarvothaman et al. 2015). They are known to possess excellent film-forming abilities and are miscible with different types of synthetic and natural compounds (Lewandowska et al. 2016). Biopolymers exert high biocompatibility and show adverse effects, thereby they are commonly applied to obtain wide types of materials for their biomedical purposes. Nevertheless, the significant disadvantage of materials obtained from natural-based compounds and their low stability and fragility (Bassyouni et al. 2017; Kamoun et al. 2017; Pandit et al. 2018); therefore, there is an imperative to introduce to improve materials’ properties by addition of stabilizing compounds (Kaczmarek et al. 2017; Lee et al. 2018; Lima et al. 2018a, b).
Polyphenols (as tannic acid) are natural compounds recently considered for the wide medical applications. They may act as polysaccharides cross-linkers that consist of many hydroxyl (–OH) groups in the structure, thereby they are able to interact with hydrophilic functional groups from polymeric chain and form strong hydrogen interactions. For instance, tannic acid has been studied concomitantly with chitosan (Kaczmarek et al. 2019a). To date, mainly phenolic acids are used as additives to polymeric materials, such as ferulic acid (Cirillo et al. 2018), ellagic acid (Karaseva et al. 2019), gallic acid (Xie et al. 2018) as well as tannic acid (Buono et al. 2018). They also provide new active biological properties as antibacterial or antioxidant (de Dicastillo et al. 2016; Kadzinska et al. 2019). Moreover, scaffolds containing tannic acid were implanted into the rabbits’ bone where the healing processes were significantly elevated (Gentile et al. 2017). The presence of tannic acid also has improved the blood vessels formation what is essential for tissue regeneration. The blood compatibility of polymeric material is the key feature that determines its application in contact with blood. It should be tested whether the presence of material causes the hemolysis. If the hemolysis exceeds 5%, material cannot be applied as wound dressing. It should be emphasized that water vapor permeability is an important factor in materials’ research. It allows maintaining moisturized environment around the healing wound. Thus, dry conditions may delay the healing processes and are unwanted while wound dressing materials are considered. The results presented recently by Kaczmarek et al. (2018) prompted us to elucidate the potential role of tannic acid in biomedicine and regenerative medicine. Herein, we additionally propose poly(ethylene glycol) (PEG) as a modifier that improves its properties. Thus, it was earlier presented that additives, such as cellulose (Faradilla et al. 2019) collagen/chitosan (Kozłowska et al. 2018), or sodium alginate (Sun et al. 2019), exert developing capacities of designed biomaterials. Herein, our results confirm the enhancement of materials’ physicochemical properties after the addition of PEGs emphasizing that its supplement as a stabilizer component for chitosan/tannic acid films still remain as not entirely described issue. The aim of the study is the novel approach regarding preparation and characterization of materials based on chitosan with tannic acid and poly(ethylene glycol) bringing the new insights into the future treatment of wound healing. On one side, we present the results of maximum tensile strength, water vapor permeation rate assessment and we elucidate the material properties in contact with blood determined as hemolysis, and platelet adhesion studies on the other side. We tested three human cell lines including bone marrow mesenchymal stem cells (BMSC), melanotic melanoma (MNT-1), and osteosarcoma (Saos-2). Altogether with previous reports listed above, enclosed results can be principal studies for further investigations of chitosan/tannic acid-based materials modified by PEG addition for wound dressings.
Materials and methods
Reagents
Dulbecco’s Modified Eagle’s Medium (DMEM) with high glucose (4500 mg/L), Minimal Essential Medium Eagle (MEM), 1% penicillin–streptomycin solution (10,000 units of penicillin and 10 mg of streptomycin in 1 mL 0.9% NaCl), acetic acid, calcium chloride, chitosan (CTS) (DD 77%), ethanol (EtOH), glutaraldehyde, HEPES (1 M), non-essential amino acids (NEAA) (100 ×), poly(ethylene glycol) (PEG); PEG1: high molecular weight (Mv 8000 g/mol), PEG2: low molecular weight (Mv 200 g/mol), sodium pyruvate (1 mM), and tannic acid (TA) were purchased from Sigma (St. Louis, MO, USA). Fetal bovine serum, 0.05% trypsin/0.53 mM EDTA solution, 1 × PBS (pH 7.4), l-glutamine (200 mM) were supplied by Thermo Fisher Scientific (Waltham, MA, USA).
Samples preparation
CTS and TA were dissolved separately to the final concentration of 2% (w/v) in 0.1 M acetic acid while PEG was prepared in dd H2O (final concentration: 1% by w/v). Subsequently, CTS and TA were mixed in different proportions, i.e. 80:20 or 50:50, along the previous studies (Kaczmarek et al. 2019b), and then 10% and 20% (w/w) of PEG solutions were added based on CTS content as film modifier. Afterwards, the prepared mixture was poured on the plastic holder (10 cm × 10 cm) to allow evaporating the solvent. Tested materials were sterilized prior to cell biological characterization in the form of thin films at the bottom of tissue culture plastic (TCP) in presence of 75% EtOH for 10 min followed by rinsing twice using sterile 1 × PBS (pH 7.4) to remove remnants of alcohol.
Cell culture
Human melanoma MNT-1 cell line was cultured in DMEM medium supplemented with 10% (v/v) heat-inactivated fetal bovine serum, 1% (v/v) l-glutamine, 1% (v/v) HEPES, 1% (v/v) NEAA, 1% (v/v) sodium pyruvate, 1% (v/v) streptomycin–penicillin solution. BMSC and Saos-2 cells were maintained in MEM medium supplemented with 10% (v/v) heat-inactivated fetal bovine serum and 1% (v/v) streptomycin–penicillin solution. All cell lines in the logarithmic growth phase were used prior to the assessments.
Maximum tensile strength
Mechanical properties are very important for the materials as thin films. Thus, the maximum tensile strength (σmax) was determined for each type of film by the Z.05 testing machine (Zwick/Roell, Germany) with the initial force 0.1 MPa and the velocity of 5 mm/min. To perform mechanical testing, samples were immersed for 2 h in 1 × PBS (pH 7.4) prior to the measurement.
Water vapor permeation rate (WVPR)
The WVPR of films was investigated using the method described earlier with slight modifications (Phaechamud et al. 2016). Briefly, calcium chloride as a desiccant was placed into the plastic container (40 mm diameter) and dried out for 24 h at 105 °C prior to further use (m0). Films were placed on top of the containers, sealed tightly, and compared afterwards with the containers without covers considered as control samples. After 24 h at 37 °C (mt), the samples were removed and the weight gain was determined as described before (Michalska-Sionkowska et al. 2018) along the enclosed formula:
Blood compatibility
Blood compatibility assignment was prepared using contact methods as described earlier by Zhou et al. (2011). Anti-coagulated sheep blood (0.2 mL) was added to 10 mL of physiological saline solution containing different specimens (1 cm2). Positive ([OD]positive) and negative ([OD]negative) samples were prepared by adding 0.2 mL of fresh blood to water and physiological saline, respectively, and tubes were incubated at 37 °C for 1 h. Next, the suspension was centrifuged at 1000 rpm for 10 min, and the absorbance of the supernatant was measured by the microplate reader Multiscan FC (Thermo Fisher Scientific, Waltham, USA) at λ = 540 nm. Hemolysis rate was calculated using the equation:
Tannic acid release
Materials were immersed in simulated body fluid (SBF; pH 7.4). Tannic acid concentration was determined by the Folin–Ciocalteu method with the use of standard curve. Briefly, the Folin–Ciocalteu (0.5 mL) reagent was mixed with Na2CO3 (1 mL), sample (1 mL), and distilled water to the final volume of 10 mL. The solution was then stored in 40 °C for 30 min and assessed by the UV–Vis spectrophotometer (UV-1800, Shimadzu, Switzerland) at λ = 725 nm to determine the concentration of released tannic acid.
Platelet adhesion studies
For preparing platelet-rich plasma (PRP), the centrifugation of blood was conducted at 1000 rpm for 10 min. The samples were sterilized and equilibrated in 1 × PBS for 6 h at room temperature (RT). Subsequently, PBS was replaced with PRP and samples were incubated further at 37 °C for 90 min. Afterwards, the samples were washed three times with 3 mL 1 × PBS to remove the non-adherent platelets, and the adhered platelets were fixed in 2.5% glutaraldehyde for 60 min. Then, samples were washed again with 1 × PBS followed by dehydration in gradient ethanol–water solutions (15 min each), and imaged using the scanning electron microscope (LEO Electron Microscopy Ltd, England).
Establishing cell cultures on the experimental films
BMSC were obtained from a 56-year-old male patient along the protocol (Institutional Review Board; No. 1072.6120.254.2017). BMSC, MNT-1 and Saos-2 cells were seeded directly onto material films or tissue culture plastic at a density of 1 × 104/cm2 in 1 mL of culture medium exchanged every 48 h. The cell proliferation MTS assay was carried out for 6 days. Briefly, cells were rinsed once with 1 × PBS and further maintained in respective culture medium mixed with MTS reagent (Cell Titer 96® AQueous One Solution Cell Proliferation Assay, Promega, Madison, WI, USA) (1:10) in the final volume of 200 μL/well, and cultured in a humidified atmosphere of 5% CO2 at 37 °C. The reactions were developed until color change of the MTS reagent in culture wells versus control sample (cell-free well). Next, the MTS solutions were transferred to individual wells into 96-well plates and absorbance was measured at λ = 492 nm using a microplate reader (SpectraMax iD3 Molecular Devices, San Jose, CA, USA).
Statistical analysis
Experiments were performed at least three times, with results expressed in each case as the mean + standard deviation (SD). Significant differences between results were determined by the univariate analysis of variance (ANOVA) or the Student’s t test and appropriate post hoc analysis using GraphPad Prism 7.05 software (La Jolla, CA, USA). Obtained data were normalized and are presented as percentage of the control sample. A P value of less than 0.05 was considered statistically significant.
Results
Mechanical properties
The maximum tensile strength values (σmax) for chitosan/tannic acid films without PEGs equaled to 3.27 MPa and 22.31 MPa (P < 0.001) for CTS/TA at 80:20 and CTS/TA at 50:50, respectively Fig. 1. Furthermore, two PEG concentrations were tested where σmax was significantly elevated (P < 0.001) in case of CTS/TA at 80:20 + 10% PEG1 and 20% PEG1 compared to CTS/TA at 80:20 alone, reaching the value of 4.38 and 5.98, respectively. Similar pattern of regulation was observed in case of CTS/TA at 50:50. The presence of 20% PEG1 enhanced prominently (P < 0.001) σmax compared to CTS/TA at 50:50 alone reaching the value of 30.46 for CTS/TA at 50:50 + 20% PEG1. On the other hand, the addition of PEG2 did not enhance the mechanical properties of films neither in case of CTS/TA at 80:20 nor CTS/TA at 50:50.
Water vapor permeation rate (WVPR) and blood compatibility
Enclosed WVPR parameters for all assessed combinations of CTS/TA at 80:20 or CTS/TA at 50:50 were listed in Table 1. In our case, the WVPR of proposed films based on chitosan or tannic acid modified by PEGs ranged as follows: 4143 (CTS/TA at 80:20 + 20% PEG2) and 4498 (CTS/TA at 80:20 alone) or 3499 (CTS/TA at 50:50 + 20% PEG2) and 5697 g/m2/h (CTS/TA at 50:50 alone). It should be added that the control sample (container without film) reached the WVPR of 8390 g/m2/h. On the other hand, the addition of PEGs, either PEG1 or PEG2, triggers decrease of WVPR as seen in Table 1; however, the decrease is lower in case of PEG1 than PEG2.
Second, the PEG addition increased hemocompatibility of our materials compared to CTS/TA at 80:20 or CTS/TA at 50:50 alone (Table 2). Our experiment showed films with 10% PEG1 of their rate of hemolysis at 0.20% for CTS/TA at 80:20 mixtures or 0.09% for CTS/TA at 50:50. Similar trend was observed from PEG2 where 10% addition showed the rate of hemolysis 0.71% for CTS/TA at 80:20 specimen and 0.32% for CTS/TA at 50:50. Also, hemolysis rate slightly decreased with increasing PEG2 content. Thus, all the tested films with PEG addition showed the hemolysis rate below 1% indicating that materials are non-hemolytic.
Tannic acid release and platelet adhesion studies
The concentration of tannic acid released was detected after films’ immersion in three simulated body fluid (SBF; pH 7.4) and depicted in Fig. 2. The burst effect was noticed in the first period of time. Then, concentration of released tannic acid decreases for each type of film, and after 4 h of immersion the increase of tannic acid concentration was noticed resulting of films welling. As a consequence, regular increase of phenolic acid concentration was observed indicating that presence of PEG massively decreases tannic acid release what is seen particularly after extended incubation time (48 or 72 h).
An assessment of platelet adhesion is a critical issue which has to be performed because it leads to activation of coagulation pathways eliciting blood clot formation (Fig. 3a–c). The addition of PEG1 and PEG2 caused no apparent platelet adhesion as compared to the chitosan/tannic acid films. Also, round morphology with no signs of activation with extended filopodia may be observed.
Establishing cell cultures on the experimental films
Tested cell lines investigated within this report revealed significant enhancement of metabolic activity of TCP compared of 5CTS/TA at 50:50 to CTS/TA at 80:20 alone for human MNT-1 melanoma, human bone marrow mesenchymal stem cells (BMSC) and human osteosarcoma (Saos-2) by 127% (P < 0.001; Fig. 4a), 45% (P < 0.01; Fig. 4b) and 48% (P < 0.01; Fig. 4c), respectively. These results indicate the higher cell compatibility with the increase of tannic acid content in the biomaterial. Furthermore, either PEG1- or PEG2-supplemented CTS/TA at 80:20 did not show any changes in cell viability what is in contrast to the increased content of TA, i.e. CTS/TA at 50:50. What is interesting, addition of PEG2, in both concentrations, such as 10% or 20%, revealed increased metabolic activity of TCP compared to CTS/TA at 50:50 alone by 123% (P < 0.001; Fig. 4a), 200% (P < 0.001; Fig. 4b), and 86% (P < 0.001; Fig. 4c) for CTS/TA at 50:50 + 10% PEG2 and by 89% (P < 0.01; Fig. 4a), 104% (P < 0.001; Fig. 4b), and 79% (P < 0.001; Fig. 4c) for CTS/TA at 50:50 + 20% PEG2.
Discussion
The behavior of the films in the swelling state is an important factor for considering the material as a potential wound dressing since they are in direct contact with body fluids; therefore, they should be durable after soaking. We assume that only high-molecular-weight poly(ethylene glycol) improves the mechanical properties of chitosan/tannic acid-based films. Our results enclosed in this report and this statement are in line with Lima et al. (2018a; b) who noticed that the chitosan’s physical properties of the blends were improved by PEG addition depending on its molecular weight. Similarly, the correlation between PEG and its weight was noticed, i.e. the higher weight of investigated PEG, the increased mechanical parameters (Sun et al. 2008 ), and these observations are in line with our data, additionally confirmed by Xu et al. (2016). Altogether with previous reports, we claim that the higher PEG’s molecular weight is tested, e.g. ranging from 400 to 4000, the more molecular entanglements or electrostatic hindrance of mixture is seen. Next issue is about the optimal characteristics of biomaterial assessed regarding the wound management water vapor that plays the crucial role in efficacy boosting wound healing. Thus, WVPR is an essential factor for the materials to be considered as dressings since the moist environment of a wound is a highly desired condition to maintain the healing processes which is consistent with previous report showed by Michalska-Sionkowska et al. (2018). On the other hand, lower values of WVTR are responsible for accumulation of exudates which might retard the healing progress and increase the risk of bacterial contamination. The increasing amount of tannic acid is connected to the water vapor permeation rate. It is induced by “massive” presence of hydroxyl (–OH) groups in chemical formula which is able to bind water. It is desired that the moisture environment is more suitable for the wound healing; however, it may lead to the skin dehydration and scars formation (Morgado et al. 2015). On the one hand, we claim that increased amount of tannic acid correlates to enhanced WVPR while, on the other hand, the presence of PEG decreases this parameter. The reason for this was mentioned earlier, that the –OH functional groups within the formula of tannic acid triggering the ability to bind water in the environment. We know that PEG is soluble in water; however, as it is used as chitosan/tannic acid additive, it interacts with –OH groups of both compounds acting as cross-linkers by stabilizing the polymer structure. Thus, the presence of strong hydrogen bonds improves material stability; therefore, the mixture of CTS/TA together with PEG has different properties from that of pure PEG. Furthermore, the explanation for PEG-mediated dropped WVPR could be that poly(ethylene glycol) with high molecular weight presumably induces chains' conformation, subsequently structural changes, and finally affecting the WVPR.
Since the hemocompatibility is one of the key factors to consider material for potential biomedical application, we also assessed this parameter. As previously described by Weber et al. (2018), erythrocytes are sensitive to the hemolysis due to the shear stress and this is in line with our results where rate of erythrocytes hemolysis decreases proportionally with increasing concentration of both, PEG1 or PEG2. We compared our results with the ASTM F756-00 standard materials. Thus, hemolytic index ranging between 0 and 2% are considered as non-hemolytic while ranging 2–5% are slight hemolytic, and < 5% are classified as hemolytic ones (Pires et al. 2018). Similar results were obtained by Kameneva et al. (2003) where the PEG contact (any molecular weight) reduced the hemolysis rate of erythrocytes. Shih et al. (2011) also reported that PEG addition to the poly(hexa-methylene-urethane) resulted the lowering of hemolysis as the compatibility with blood is improved. This may suggest that the supplementation with PEG decreases of hemolysis rate indicating in parallel its high safety profile targeting for future application in regenerative medicine. Poly(ethylene glycol) improves material stability what was also proven earlier by Fu and Kao (2009). Thus, the released concentration of different compounds, e.g. silver sulfadiazine and bupivacaine hydrochloride, decreased with increasing amount of PEG added to gelatin acting as cross-linker. De Lima et al. (2018a; b) reported that the release of another phenolic acid–ferulic acid from chitosan-based material was rapidly released due to weak interactions between the phenolic acid and polymer, characterizing a burst effect. Such response was also detected in our experiments where burst effect was initially noticed with subsequent spontaneous increase of material degradation. The release of tannic acid from films obtained by our group showed decreases in concentration with increasing PEG amount. We claim that these differences are caused by the presence of interactions between PEG and tannic acid which inhibit the phenolic acid release from material. In fact, the influence of combinational content of PEG with chitosan on insulin released concentration was noticed by Sadhasivam et al. (2015) where the rate of insulin release was aided by presence of PEG. The addition of poly(ethylene glycol) resulted in repulsion to platelet adhesion and ensuing reduced platelet activation. This larger amount of resistance towards platelet attachment by water molecules can be attributed to the presence of a large number of hydrogen bonds between film components and water molecules. It has been previously reported by Deible et al. (1999) where platelet adhesion onto collagen was observed; however, the incorporation of PEG shows dramatic decrease in platelet adherence when contacted modified protein. This indicates that PEG is forming a type of coating which inhibits the platelets deposited onto the films surface. This observation was also reported by Sagnella and Mai-Ngam (2005) where PEG addition to the chitosan causes the significant decrease in platelet adhesion to the film as well as it decreases the density of surface charge.
Comparatively, our results with the ones obtained by the others listed above, it should be briefly mentioned that the optimal parameters of materials applied as dressings regarding the WVPR range from 1800 to 2300 g/m2/24 h (Xu et al. 2016) and hemolysis rate should not be higher as 5% (according to the ASTM F756-00 standard). In other words, as the WVPR is higher than the optimal conditions, there would be a need to moisture the wound surrounding; therefore, probability of the use of hydrogel form of material would be more desired. Similarly, the low platelet adhesion should be obtained in material contact with blood as it improves thromboresistance (Uchida et al. 2005). Indeed, dressing materials should not inhibit the proliferation of human cells; therefore, it is essential to study the cells’ behavior in contact with the designed material surface. Thus, our studies revealed that cells’ viability was significantly elevated compared to TCP, and this may suggest that materials proposed by us do not affect negatively the proliferation rate of cutaneous cells.
Besides, we supported our studies by cell assessments where our results are consistent with previous reports. For instance, chitosan grafting by PEG improved the L929 cells proliferation compared to materials without PEG (Mao et al. 2005). The presence of PEG in a mixture with chitosan influenced the breast cancer cells, which resulted in the inhibition of their proliferation (Chang et al. 2016), or finally PEG did not show any significant influence on the BMSC cells (Oda et al. 2014). These observations together with our results prompted us to make the statement that poly(ethylene glycol) may be also used in future for treatment of post-operation wounds in dermatology; however, further and prudent studies are strongly desired.
Conclusion
The poly(ethylene glycol) addition may act as cross-linker for materials based on chitosan and tannic acid, and depending on the molecular weight of PEG their properties were changed. High-molecular-weight PEG improved mechanical properties of films, decreased the hemolysis rate, and it reduced the platelet adhesion to the material surface. Moreover, the addition of PEG1 or PEG2 in concentrations of either 10% or 20% to the materials containing CTS/TA at 80:20 does not affect cell viability in comparison to the control materials. On the other side, a statistically significant decrease of viability of MNT-1 cells was observed cultured on CTS/TA at 50:50 + 20% PEG1. Contrary, a prominent increase of viability was revealed for all types of cells cultured on the CTS/TA at 50:50 materials with the addition of both 10% and 20% PEG2. Chitosan/tannic acid thin films modified by PEGs may be potentially used as dressing materials, where those with high-molecular-weight PEG addition showed the inhibition of cancer cells viability and may be further studies for anticancer treatment.
References
Bassyouni M, Javaid U, Hasan SW (2017) Bio-based hybrid polymer composites: a sustainable high performance material. In: Hybrid polymer composite materials, pp 23–70
Buono P, Duval A, Averous L, Habibi Y (2018) Clicking biobased polyphenols: a sustainable platform for aromatic polymeric materials. Chemsuschem 11:2472–2491
Chang FC, Tsao CT, Lin A, Zhang M, Levengood SL (2016) PEG–chitosan hydrogel with tunable stiffness for study of drug response of breast cancer cells. Polymers 8:112
Cirillo G, Curcio M, Spataro T, Picci N, Restuccia D, Iemma F, Spizzirri UG (2018) Antioxidant polymers for food packaging. In: Academic Press (ed) Food Packaging and Preservation, Handbook of Food Bioengineering, pp 213–238.
de Dicastillo CL, Rodríguez F, Guarda A, Galotto MJ (2016) Antioxidant films based on cross-linked methyl cellulose and native Chilean berry for food packaging applications. Carbohydr Polym 136:1052–1060
de Lima IA, Khalil NM, Tominaga TT, Lechanteur A (2018a) Mucoadhesive chitosan-coated PLGA nanoparticles for oral delivery of ferulic acid. Artif Cells Nanomed B 46:993–1002
Deible CR, Petrosko P, Johnson PC, Beckman EJ, Russell AJ, Wagner WR (1999) Molecular barriers to biomaterial thrombosis by modification of surface proteins with polyethylene glycol. Biomaterials 20:101–109
Faradilla RF, Lee G, Sivakumar O, Stenzel M, Arcot J (2019) Effect of polyethylene glycol (PEG) molecular weight and nanofillers on the properties of banana pseudostem nanocellulose films. Carbohydr Polym 205:330–339
Fu Y, Kao WJ (2009) Drug release kinetics and transport mechanisms from semi-interpenetrating networks of gelatin and poly(ethylene glycol) diacrylate. Pharm Res 26:2115–2124
Gentile P, Ferreira AM, Callaghan JT, Miller CA, Atkinson J, Freeman C, Hatton PV (2017) Multilayer nanoscale encapsulation of biofunctional peptides to enhance bone tissue regeneration in vivo. Adv Healthc Mater 6:1601182
Jayaprakash N, Vijaya JJ, Kennedy LJ, Priadharsini K, Palani P (2015) Antibacterial activity of silver nanoparticles synthesized from serine mater. Sci Eng C Mater Biol Appl 49:316–322
Kaczmarek B, Sionkowska A, Osyczka AM (2017) The comparison of physic-chemical properties of chitosan/collagen/hyaluronic acid composites with nano-hydroxyapatite cross-linked by dialdehyde starch and tannic acid. Polym Test 62:171–176
Kaczmarek B, Sionkowska A, Otrocka-Domagała I, Polkowska I (2018) In vivo studies of novel scaffolds with tannic acid addition. Polym Degrad Stab 158:26–30
Kaczmarek B, Nadolna K, Owczarek A, Michalska-Sionkowska M, Sionkowska A (2019a) The characterization of thin films based on chitosan and tannic acid mixture for potential applications as wound dressings. Polym Test 78:106007
Kaczmarek B, Owczarek A, Nadolna K, Sionkowska A (2019b) The film-forming properties of chitosan with tannic acid addition. Mater Lett 245:22–24
Kadzinska J, Janowicz M, Kalisz S, Brys J, Lenart A (2019) An overview of fruit and vegetable edible packaging materials. Packag Technol Sci 32:483–495
Kameneva MV, Repko BM, Krasik EF, Perricelli BC, Borovetz HS (2003) Polyethylene glycol additives reduce hemolysis in red blood cell suspensions exposed to mechanical stress. ASAIO J 49:537–542
Kamoun EA, Kenawy ERS, Chen X (2017) A review on polymeric hydrogel membranes for wound dressing applications: PVA-based hydrogel dressings. J Adv Res 8:217–233
Kang K, Choi IS, NamY, (2011) A biofunctionalization scheme for neural interfaces using polydopamine polymer. Biomaterials 32:6374–6380
Karaseva V, Bergeret A, Lasoste C, Fulcrand H, Ferry L (2019) New biosourced flame retardant agents based on gallic and ellagic acids for epoxy resins. Molecules 24:4305
Kozłowska J, Stachowiak N, Sionkowska A (2018) Preparation and characterization of collagen/chitosan poly(ethylene glycol)/nanohydroxyapatite composite scaffolds. Polym Adv Technol 30:799–803
Lee J, Yeo M, Kim W, Koo Y, Kim G (2018) Development of a tannic acid cross-linking process for obtaining 3D porous cell-laden collagen structure. Int J Biol Macromol 110:497–503
Lewandowska K, Sionkowska A, Grabska S, Kaczmarek B, Michalska M (2016) The miscibility of collagen/hyaluronic acid/chitosan blends investigated in dilute solutions and solids. J Mol Liq 220:726–730
Lima DB, Almeida RD, Pasquali M, Borges SP, Fook ML, Lisboa HM (2018b) Physical characterization and modeling of chitosan/peg blends for injectable scaffolds. Carbohydr Polym 189:238–249
Mao S, Shuai X, Unger F, Wittmar M, Xie X, Kissel T (2005) Synthesis, characterization and cytotoxicity of poly(ethylene glycol)-graft-trimethyl chitosan block copolymers. Biomaterials 26:6343–6356
Michalska-Sionkowska M, Kaczmarek B, Walczak M, Sionkowska A (2018) Antimicrobial activity of new materials based on the blends of collagen/chitosan/hyaluronic acid with gentamicin sulfate addition. Mater Sci Eng C 86:103–108
Morgado PI, Aguiar-Ricardo A, Correia IJ (2015) Asymmetric membranes as ideal wound dressings: an overview on production methods, structure, properties and performance relationship. J Membr Sci 490:139–151
Oda Y, Tani K, Isozaki A, Haraguchi T, Itamoto K, Nakazawa H, Taura Y (2014) Effects of polyethylene glycol administration and bone marrow stromal cell transplantation therapy in spinal cord injury mice. J Vet Med Sci 76:415–421
Pandit P, Nadathur GT, Maiti S, Regubalan B (2018) Functionality and properties of bio-based materials. In: Bio-based materials for food packaging, pp 81–103
Phaechamud T, Issarayungyuen P, Pichayakorn W (2016) Gentamicin sulfate-loaded porous natural rubber films for wound dressing. Int J Biol Macromol 85:634–644
Pires ALR, Motta LA, Dias AMA, de Sousa HC, Moraes AM, Braga MEM (2018) Towards wound dressings with improved properties: effects of poly(dimethylsiloxane) on chitosan-alginate films loaded with thymol and beta-carotene. Mater Sci Eng C 93:595–605
Sadhasivam L, Dey N, Francis AP, Devasena T (2015) Transdermal patches of chitosan nanoparticles for insulin delivery. Int J Pharm Pharm Sci 7:84–88
Sagnella S, Mai-Ngam K (2005) Chitosan based surfactants polymers designed to improve blood compatibility on biomaterials. Colloids Surf B Biointerfaces 42:147–155
Sarvothaman MK, Kim KS, Seale B, Brodersen PM, Walker GC, WheelerAR, (2015) Dynamic fluoroalkyl polyethylene glycol co-polymers: a new strategy for reducing protein adhesion in lab-on-a-chip devices. Adv Funct Mater 25:506–515
Shih MF, Shau MD, Hsieh CC, Cherng JY (2011) Synthesis and evaluation of poly(hexamethylene-urethane) and peg-poly(hexamethylene-urethane) and their cholesteryl oleyl carbonate composites for human blood biocompatibility. Molecules 16:8181–8197
Sun G, Zhang X, Chu C (2008) Effect of the molecular weight of polyethylene glycol (PEG) on the properties of chitosan–PEG–poly(N-isopropylacrylamide) hydrogels. J Mater Sci Mater Med 19:2865–2872
Sun F, Guo J, Liu Y, Yu Y (2019) Preparation, characterizations and properties of sodium alginate grafted acrylonitrile/polyethylene glycol electrospun nanofibers. Int J Biol Macromol 137:420–425
Uchida M, Ito A, Furukawa KS, Nakamura K, Onimura Y, Oyane A, Ushida T, Yamane T, Tamaki T, Tateishi T (2005) Reduced platelet adhesion to titanium metal coated with apatite, albumin-apatite composite or laminin–apatite composite. Biomaterials 26:6924–6931
Weber M, Steinle H, Golombek S, Hann L, Schlensak C, Wendel HP, Avci-Adali M (2018) Blood-contacting biomaterials: in vitro evaluation of the hemocompatibility. Front Bioeng Biotechnol 6:99
Xie C, Song J, Wu H, Hu Y, Liu H, Yang Y, Zhang Z, Chen B, Han B (2018) Naturally occurring gallic acid derived multifunctional porous polymers for highly efficient CO2 conversion and I2 capture. Green Chem 20:4655–4661
Xu R, Xia H, He W, Li Z, Zhao J, Liu B et al (2016) Controlled water vapor transmission rate promotes wound-healing via wound re-epithelialization and contraction enhancement. Sci Rep 6:24596
Zhou HY, Zhang YP, Zhang WF, Chen XG (2011) Biocompatibility and characteristics of injectable chitosan-based thermosensitive hydrogel for drug delivery. Carbohydr Polym 83:1643–1651
Acknowledgements
The present study was partly supported by the grant from the National Science Centre (NCN, Poland) to A. M. O. (UMO-2016/21/B/NZ5/00217) and to some degree from the German Research Foundation (Deutsche Forschungsgemeinschaft [DFG]) to K. K. (KL2900/2-1).
Funding
Open Access funding enabled and organized by Projekt DEAL. This study was supported by the National Science Centre (NCN, Poland) to A. M. O. (UMO-2016/21/B/NZ5/00217) and to some degree from the German Research Foundation (Deutsche Forschungsgemeinschaft [DFG]) to K. K. (KL2900/2-1).
Author information
Authors and Affiliations
Contributions
BK conceived, designed the experiments, analyzed the obtained data, and prepared the first draft of the manuscript. OM carried out the mechanical assessment, the WVPR analysis, platelet adhesion, and tannic release studies while MMS conducted the blood compatibility assays. AMO designed the conditions for the experiments regarding cell biology part; OM carried out the experimental part, and together with AMO evaluated obtained data. KK supported the interpretation of all the results and together with BK drafted the final version of the manuscript.
Corresponding author
Ethics declarations
Conflict of interest
The authors report that they have no conflicts of interest.
Ethical approval
This article does not contain any studies with human participants or animals performed by any of the authors.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Kaczmarek, B., Mazur, O., Miłek, O. et al. Development of tannic acid-enriched materials modified by poly(ethylene glycol) for potential applications as wound dressing. Prog Biomater 9, 115–123 (2020). https://doi.org/10.1007/s40204-020-00136-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40204-020-00136-1