Abstract
Good thermoelectric performance is being sought to face major problems related to energy, especially in the concern of the usage of energy on environmental impact. In this work, we investigate the underlying mechanism to enhance the thermoelectric performance of bismuth selenide (Bi2Se3) by employing density functional theory (DFT) followed by the Boltzmann transport equation under relaxation time approximation. The structural, electronic, and thermoelectric properties were calculated and analyzed. From the analysis of combined results of thermoelectric properties and electronic properties as the function of the Fermi level, we found that the power factor of Bi2Se3 is improved by increasing electrical conductivity that contributed by the large density of states and light effective mass of charge carriers. The figure of merit, on the other hand, is enhanced by increasing Seebeck coefficient that contributed by heavy effective mass and decreasing thermal conductivity that contributed by low density of states. We also found that both power factor and figure of merit can be improved through n-type doping at 300 K and p-type doping at higher temperature (400 K and 500 K).
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Thermoelectricity has become fascinating prospect for use in generating green energy especially from the processes of waste heat [1,2,3]. The narrow-band gap (0.3 eV) semiconductor such as Bi2Se3 has been recognized as an outstanding thermoelectric material [4,5,6]. Thermoelectric material’s unique properties is that it can convert waste heat to electrical energy directly [7, 8]. It has contributed to the development of many applications such as waste heat recovery, humidity sensors, solid-state generators and radiation sensors [9, 10]. The most attractive application is a sensor that use for internet of things (IoT). There is considerable demand to power these sensors without replacing the batteries. Thermoelectric device is favorable candidate for wireless sensor networks (WSNs) in IoT due to its capability such as no moving part, no maintenance requirement, high reliability, small size and flexible [11]. Thermoelectric material has advantages such as reliable conversion, scalable and compact compared with other technologies of energy conversion and can be the solution to the environmental crisis because no energy waste produced during operation [12,13,14]. In the several crucial markets, thermoelectric devices are in mass production for heating, temperature-control and cooling applications. For future inquiry, if ZT performance of thermoelectric devices has reached 2, commercial solid-state heating, air-cooling systems and ventilating would become available for public to use at home and office [15].
Thermoelectric performance of thermoelectric material is evaluated by the equation \(ZT={S}^{2}\sigma T/\kappa\), where S is Seebeck Coefficient or thermopower, \(\sigma\) is electrical conductivity, T is temperature, \(\kappa\) is thermal conductivity and ZT is dimensionless figure of merit. From the equation, good thermoelectric material is the one that has higher thermopower and electrical conductivity, and a lower thermal conductivity.
Experimental report by Patil et al. shows one of the highest thermopower that Bi2Se3 has ever attained which is 556 μV/K. Due to the lower electrical conductivity (1.877 S/cm), the performance of Bi2Se3 is low as 0.033 [16]. The experimental report by Kulsi et al. shows the same trend which Bi2Se3 has low performance (0.02) due to the lower electrical conductivity (5.200 S/cm) [17]. Many modifications have been done to increase the performance such as doping for instance. Doping by copper, antimony and nickel have increased the ZT value to 0.54, 0.036 and 0.57, respectively [16,17,18]. There are also modification by nano-structuring such as nanoplates and nanosheets of Bi2Se3 that have increased the performance to 0.14 and 0.17, respectively [19, 20]. The advantage of nano-structuring is that the performance can be improved by reducing thermal conductivity without decreasing power factor greatly [13]. Even though there are many high-performance thermoelectric materials that almost reach unity 1.0 figure of merit, these materials could only operate at higher temperature [21,22,23,24]. Bi2Se3, on the other hand, specialized in operating thermoelectricity at room temperature [25, 26].
Study by Peter et al. has made enhancement through optimization of p-doped Bi2Se3 that has significant advantage over Bi2Te3 on thermoelectric properties at the range temperature from 400 to 600 K. The optimization has produced better ZT performance [27]. Study by Leo et al. made further enhancement from optimized doped Bi2Se3 for both n-type and p-type through a tensile in-plain strain and compressive uniaxial strain. The strain has increased Seebeck coefficient that lead to increase of power factor [28]. There have been many fruitful optimized doping predictions for thermoelectric materials such as done on CuFeS2, Cr-doped Bi2Te3 and ZnSb which shows that analyzing in doped configuration could predict good prediction of good thermoelectric performance [29,30,31].
In this study, we attempt to investigate thermoelectric properties of Bi2Se3 as the function of Fermi level to find its optimal doping level and performance by using first-principles study of density functional theory (DFT). According to Xu et al., Fermi level can be controlled and adjusted in topological insulator [32]. Bi2Se3 also exhibit as topological insulator besides thermoelectric material [4, 32,33,34]. Thus, thermoelectric properties are expected can be significantly tuned and optimized. The study involved the investigation on structural, electronic and thermoelectric properties of Bi2Se3. Structural properties are calculated using Cambridge Serial Total Energy Package (CASTEP) as an introduction of the unique structure of Bi2Se3 especially its Van der Waals interaction that gives influence on thermal conductivity of thermoelectric material [35]. Electronic properties that consist of band structure and density of states (DOS) were calculated using full-potential linearized augmented plane wave (FP-LAPW) that implemented in WIEN2K. The contribution of electronic properties on thermoelectric performance was analyzed. Finally, thermoelectric properties were calculated by employing Boltzmann transport equation that implemented in Boltzmann transport properties (BoltzTraP) computer code.
The investigation of enhancement mechanism of thermoelectric performance of Bi2Se3 is done through the contribution of Seebeck coefficient, electrical conductivity, thermal conductivity, DOS, carrier concentration and effective mass to the maximum value of power factor and figure of merit (ZT). We found that, the power factor and ZT have different kind of contribution to attain their maximum point. However, both contributed by n-type doping at their corresponding optimum level to gain maximum value at 300 K. This study could give insight and guideline to narrow down the necessity parameter and region of doping for experiments to improve the thermoelectric performance.
Computational details
Rhombohedral structure of Bi2Se3 with the space group \({D}_{3d}^{5}(R\stackrel{-}{3}m)\) is used [6]. The initial structural parameter was taken from the experimental study by Nakajima [36]. Structural optimization was calculated using DFT that implemented in CASTEP within Materials Studio. For optimization, on-the-fly generation (OTFG) ultrasoft pseudopotential was used to reduce the inaccuracy with respect to completely converged all-electron DFT calculations [37]. Van der Waals (vdW) was considered within Ortmann–Bechstedt–Schmidt (OBS) schemes since Bi2Se3 has vdW interaction in its structure [38, 39]. Generalize gradient approximation for solid (GGA-PBESol) is chosen as functional exchange–correlation [40]. After performed convergence test, cut-off energy 350 eV and k-points 4 × 4 × 1 are chosen. All forces on atoms were converged to less than 0.03 eV/Å, the maximum ionic displacement was set to 0.001 Å and the total stress tensor was decreased to the 0.05 GPa.
After optimization, electronic properties that consist of band structure and density of states (DOS) were calculated using full-potential linearized augmented plane wave (FP-LAPW) that implemented in WIEN2K. The atomic space in FP-LAPW consists of muffin-tin (MT) region and interstitial region. The former is the space throughout atoms occupied by spheres of radius, RMT that is known as MT spheres. The latter is the remaining space region [41]. GGA-PBE has been employed as the exchange–correlation functional [42]. Spin–orbit coupling (SOC) is not considered in the calculation. We use 500 k-points in the first Brillouin zone for the self-consistent calculation. The calculation was converged with respect to the RMTKmax = 7.0 and Gmax = 12.0.
The calculation of thermoelectric properties was executed by using semi-classical Boltzmann transport equation that implemented in BoltzTraP incorporated into WIEN2K computer code within FP-LAPW [43, 44]. The properties can be computed based on calculated band structure on the rigid band approach [44]. The thermoelectric properties consist of thermopower or Seebeck coefficient S, electrical conductivity \(\sigma\), thermal conductivity \(\kappa\) and figure of merit ZT.
Results and discussion
Thermoelectric material operates under the system that based on the equation \(ZT={S}^{2}\sigma T/\kappa\). From the equation, excellent thermoelectric material receives an advantage from higher Seebeck coefficient and electrical conductivity [45]. In addition, the material must have lower thermal conductivity. Higher Seebeck coefficient can be achieved through larger effective mass and smaller carrier concentration [46, 47]. On the contrary, to attain higher electrical conductivity required high carrier concentration and light effective mass [48, 49]. Besides that, thermal conductivity contributed by electronic thermal conductivity and lattice thermal conductivity [50]. Electronic thermal conductivity has a strong relationship with electrical conductivity based on Wiedemann–Franz law which by decreasing electronic thermal conductivity would also decrease electrical conductivity [51]. These contradictory conditions hindered the development towards a higher performance (ZT) for many years.
This work will set forth on structural properties which is the lattice parameter. Then, the result of electronic properties which are band structure and density of states was analyzed. Then, we will explore the transport properties which consist of Seebeck coefficient S, electrical conductivity \(\sigma\), thermal conductivity κ, power factor, and dimensionless figure of merit ZT. Geometrical optimization is done using GGA-PBESol functional together with the corresponding available experimental and theoretical values are listed in Table 1. The structure consists of five-atom layers known as quintuple layers along z-direction as shown in Fig. 1. The layer of the structure arranged with the sequence system of Se1-Bi-Se2-Bi-Se1 [5]. The structure has a strong bond within the quintuple layer. However, the bond is weak between quintuple layers. The weak bond is known as Van der Waals bond and this the reason we included the OBS Van der Waals scheme in the calculation [52, 53]. As can be seen, the optimized lattice parameters concur very well with the experimental works with the small difference around 0.07–0.17% for lattice a = b and 0.38–0.67% for lattice c. The calculated lattice parameter also agrees very well with the other theoretical works. Unlike local density approximation (LDA) due to the treatment limitation, our GGA-PBESol approach is closer to the available experimental values.
After structural optimization was performed, electronic properties which are band structure and density of states were calculated. The calculated band structure was performed using GGA-PBE functional. The calculated band structure is shown in Fig. 2 which has a direct band gap of 0.33 eV at P position. This band gap is overestimated by 9.09% when compared with its typical band gap of 0.30 eV as shown in Table 2 [33, 61, 62]. We find our band gap is in agreement with the other experimental work by LaForge et al. [63] and overestimated by 3.08% when compared with the work of Valla et al. [64].
To understand the origin and orbital contribution to the band structure, the density of states is plotted against the energy as shown in Fig. 3. It shows that total Se orbital is the most contributed at the valence band especially orbital Se-4p when compared with total Bi orbital. The maximum valence band wave vector P is contributed by orbital Se-4p. Orbital Se-4p and Bi-6s are partially hybridized. At the conduction band, both Se and Bi orbital contributed evenly specifically orbital Se-4p and Bi-6p. At the range of energy from 3 to 5 eV, orbital Bi-6p and Se-4p show antibonding states. Minimum conduction band at wave vector Γ and P solely contributed by orbital Bi-6p. Se-4p is fully hybridized with orbital Bi-6p.
Next, thermoelectric properties were calculated using semi-classical Boltzmann transport equation that implemented in BoltzTraP. Under rigid band approximation, the Fermi level can go up or down based on the type of doping (p-type or n-type). However, the fundamental band structure is not allowed to change. Therefore, only one band structure is needed to compute thermoelectric properties at different doping level. This approach has been widely used and helpful for the theoretical investigation of thermoelectric properties based on band structure [44, 65, 66]. The effectiveness of the rigid band model for higher holes or electrons concentration depends the dopant substitution. In our case, Se-4p is the highest contribution in the band structure, specifically at the valence band. Therefore, substituting some of Se atoms at higher concentration would change the band structure, otherwise, the doping does not change the band structure considerably. Thus, for some cases, the rigid band model is effective large concentration [67]. The result of each thermoelectric properties was plotted against the various Fermi level from − 1.0 to 1.0 eV at different temperatures as shown in Fig. 4 to analyze of what gives enhancement to good thermoelectric properties along the Fermi level.
Basically, as the Fermi level reaches band edges, the DOS increases as shown in Fig. 3. From the energy range 10–5 eV, the DOS is very low. The DOS started to increase when the Fermi level reaches 5 eV and band edge at minimum conduction band. Figure 4a shows that the Seebeck coefficient exhibits a high value at the band gap region. It quickly decreases as the Fermi level depart from the band gap and get into band edges. Even though Seebeck coefficient attains high value at the middle gap, for desirable thermoelectric performance, the value of Seebeck coefficient at the band edge is crucial as shown in Fig. 4a. Higher power factor is attained when the Fermi level at the band edge of valence band where Seebeck coefficient is 27.77 μV/K at 300 K, very low when compared with the other reports which has typical values 50–95 μV/K [19, 58, 59, 68,69,70]. However, the power factor attained maximum value mostly through the contribution of electrical conductivity at the Fermi level − 0.42 eV. In addition, large power factor occurred at p-type of doping (corresponding to negative value of Fermi level). The electrical conductivity contributed mainly by the orbital Bi-6s and Se-4p. Large DOS contributed to the large electrical conductivity [71, 72]. The ideal location of Fermi level to attained higher electrical conductivity would be at region − 1.2 to − 0.6 eV. Yet, the Seebeck coefficient is very weak at these regions and that is undesirable.
Besides calculating favorable power factor to attain, we also calculated figure of merit (ZT) to investigate favorable ZT as the function of Fermi level. The results of the calculation are shown in Fig. 4b. Contrary with the highest power factor that occurred at p-type of doping, the highest figure of merit occurred at n-type of doping (corresponding to positive value of Fermi level). In addition, it also occurred exactly at the band edge which is minimum conduction band. Higher figure of merit mostly contributed by the higher Seebeck coefficient with the value − 727 μV/K at 300 K and lower thermal conductivity. However, at 400 K and 500 K, the highest ZT attained occurred at middle gap and mostly contributed by higher Seebeck coefficient and thermal conductivity.
Another particular part of theoretical investigation for thermoelectric material is to discover level of optimal doping at which the power factor and figure of merit accomplish the maximum value. This investigation would deliver a direction in narrowing down doping area in experimental work. To carry out the investigation of discovering level of optimal doping, electrical conductivity with respect to relaxation time and Seebeck coefficient were calculated at wide range of doping concentrations ranging from 1020 to 1021 cm−3 for power factor and included thermal conductivity in the calculation within concentration range from 1016 to 1018 cm−3 for ZT. The result of calculated power factor with respect to the relaxation time and ZT were plotted against carrier concentrations that consist of electron concentrations and hole concentrations as shown in Fig. 5. For each case, the optimal doping was referring to the peak value and all the maximum values are tabulated in Table 3.
The power factor attained a maximum value of 39.487 μW/cm K2 s at 0.654 p-type doping level. The value is increased as the temperature increased. It is clear that Bi2Se3 has higher thermoelectric power factor for p-type doping than n-type doping. The optimum doping level of p-type is higher than the optimum n-type doping level which shows holes contributed more to power factor. However, n-type doping has a higher power factor at 300 K when compared with the p-type doping power factor. Most of the high power factors for p-type doping correspond to carrier concentration ranging from 8 × 1020 to 2 × 1021 cm−3. Power factor contributed by the higher charge carrier instead of thermopower. One of the main reasons power factor has lower value for n-type doping is due to the lower DOS at conduction band region which is lower charge concentration as shown in Fig. 3.
The figure of merit (ZT) attained maximum value at 300 K with n-type of doping 0.000027, very small when compared with the optimum level of doping for power factor. The ZT is decreased as the temperature and doping level increased. Besides 300 K, the ZT has a higher value from p-type doping at 400 K and 500 K when compared with n-type doping. It is clear that electrons contributed more to ZT at 300 K. Lower carrier concentration on contribution to the figure of merit indicates electrical conductivity does not contribute much to the accomplishment of higher ZT. Instead, it is lowering electronic thermal conductivity that plays the main role to achieve high ZT.
Finally, we investigate the reason for the higher power factor and figure of merit based on the band structure. Based on Fig. 2, there are two types of bands that occurred on the structure which are flat and curve bands. Flatter band indicates heavy effective mass, while the curve band indicates light effective. Effective mass was calculated as shown in Table 4.
We calculated effective mass at the wave vector P, L and Γ. It can be seen that, conduction band has higher effective mass when compared with the effective mass at the valence band except at the wave vector Γ which the conduction band lower effective mass by 8.78%. Heavy effective mass contributed to the higher Seebeck coefficient as shown its maximum value occurred at the conduction band. The negative value of Seebeck coefficient indicates electron carrier. Light effective mass, on the other hand, contribute to the charge mobility to improve electrical conductivity as shown higher DOS in valence band.
Conclusion
Our density functional theory calculations show that there are two ways to improve the thermoelectric performance of Bi2Se3 which are through enhancing thermoelectric power factor or figure of merit (ZT). The power factor can be enhanced by increasing electrical conductivity with the price of reducing thermopower. The contribution of increased electrical conductivity can be found through large DOS and light effective mass at the valence band of Bi2Se3. The power factor also can be improved through the optimal n-type doping at the temperature 300 K. However, for the higher temperature (400 K and 500 K), p-type is the optimal type of doping. ZT is improved through the higher thermopower and lower thermal conductivity with the price of reducing electrical conductivity. We found that high Seebeck coefficient contributed by heavy effective mass and low thermal conductivity contributed by low DOS. Furthermore, ZT also can be enhanced through the n-type of doping at 300 K and p-type doping for higher temperatures the same case as the power factor. We hope that our theoretical investigation could give help and provide a guideline to improve thermoelectric performance of Bi2Se3.
References
Innocent, J.-L., et al.: Thermoelectric properties of boron carbide/HfB 2 composites. Mater. Renew. Sustain. Energy 6(2), 6 (2017)
Maki, R.S., Mitani, S., Mori, T.: Effect of spark plasma sintering (SPS) on the thermoelectric properties of magnesium ferrite. Mater. Renew. Sustain. Energy 6(1), 2 (2017)
Maruyama, S., et al.: Microstructure and thermoelectric properties of YxAlyB14 samples fabricated through the spark plasma sintering. Mater. Renew. Sustain. Energy 3(3), 31 (2014)
Fisher, I., Shapiro, M., Analytis, J.: Principles of crystal growth of intermetallic and oxide compounds from molten solutions. Philos. Mag. 92(19–21), 2401–2435 (2012)
Horak, J., Karamazov, S., Lošt'ák, P.: Point defects in Pb-doped Bi2Se3 single crystals. Radiat. Eff. Defects Solids 140(2), 181–196 (1997)
Gao, X., et al.: First-principles study of structural, elastic, electronic and thermodynamic properties of topological insulator Bi2Se3 under pressure. Philos. Mag. 96(2), 208–222 (2016)
Belonogov, E., et al.: Photon treatment effect on the surface and figure of merit of thermoelectric material Bi2Te3−xSex. Mater. Renew. Sustain. Energy 9(1), 1–7 (2020)
Day, T.W., et al.: High-temperature thermoelectric properties of Cu1.97Ag0.03Se1+y. Mater. Renew. Sustain. Energy 3(2), 26 (2014)
Augustine, S., et al.: Effect of Te doping and electron irradiation on thermal diffusivity of Bi2Se3 thin films by photo-thermal technique. J. Phys. D Appl. Phys. 36(8), 994 (2003)
Marques, A., et al.: Synthesis of thermoelectric magnesium-silicide pastes for 3D printing, electrospinning and low-pressure spray. Mater. Renew. Sustain. Energy 8(4), 21 (2019)
Petsagkourakis, I., et al.: Thermoelectric materials and applications for energy harvesting power generation. Sci. Technol. Adv. Mater. 19(1), 836–862 (2018)
Han, C., Li, Z., Dou, S.: Recent progress in thermoelectric materials. Chin. Sci. Bull. 59(18), 2073–2091 (2014)
Yelgel, Ö.C., Srivastava, G.: Thermoelectric properties of Bi2Se3/Bi2Te3/Bi2Se3 and Sb2Te3/Bi2Te3/Sb2Te3 quantum well systems. Phil. Mag. 94(18), 2072–2099 (2014)
Prasad, R., Bhame, S.D.: Review on texturization effects in thermoelectric oxides. Mater. Renew. Sustain. Energy 9(1), 3 (2020)
Bell, L.E.: Cooling, heating, generating power, and recovering waste heat with thermoelectric systems. Science 321(5895), 1457–1461 (2008)
Patil, N., et al.: Effect of Sb doping on thermoelectric properties of chemically deposited bismuth selenide films. Mater. Chem. Phys. 115(1), 47–51 (2009)
Kulsi, C., Kargupta, K., Banerjee, D.: Effect of nickel doping on thermoelectric properties of bismuth selenide. In: AIP Conference Proceedings. AIP Publishing (2017).
Sun, G., et al.: Enhanced thermoelectric performance of n-type Bi2Se3 doped with Cu. J. Alloy Compd. 639, 9–14 (2015)
Ali, Z., et al.: Thermochemically evolved nanoplatelets of bismuth selenide with enhanced thermoelectric figure of merit. AIP Adv. 4(11), 117129 (2014)
Hong, M., et al.: Enhanced thermoelectric performance of ultrathin Bi2Se3 nanosheets through thickness control. Adv. Electron. Mater. 1(6), 1500025 (2015)
Chang, C., et al.: High performance thermoelectrics from earth-abundant materials: Enhanced figure of merit in PbS through nanostructuring grain size. J. Alloy Compd. 664, 411–416 (2016)
He, Y., et al.: High Thermoelectric performance in non-toxic earth-abundant copper sulfide. Adv. Mater. 26(23), 3974–3978 (2014)
Tan, G., et al.: Codoping in SnTe: enhancement of thermoelectric performance through synergy of resonance levels and band convergence. J. Am. Chem. Soc. 137(15), 5100–5112 (2015)
Zhao, L.-D., et al.: High thermoelectric performance via hierarchical compositionally alloyed nanostructures. J. Am. Chem. Soc. 135(19), 7364–7370 (2013)
Liu, H., et al.: Growth of Bi2Se3 nanobelts synthesized through a co-reduction method under ultrasonic irradiation at room temperature. Cryst. Growth Des. 5(5), 1711–1714 (2005)
Choi, J., et al.: Magnetic and transport properties of Mn-doped Bi2Se3 and Sb2Se3. J. Magn. Magn. Mater. 304(1), e164–e166 (2006)
Parker, D., Singh, D.J.: Potential thermoelectric performance from optimization of hole-doped Bi2Se3. Phys. Rev. X 1(2), 021005 (2011)
Luo, X., Sullivan, M.B., Quek, S.Y.: First-principles investigations of the atomic, electronic, and thermoelectric properties of equilibrium and strained Bi2Se3 and Bi2Te3 including van der Waals interactions. Phys. Rev. B 86(18), 184111 (2012)
Takaki, H., et al.: Thermoelectric properties of a magnetic semiconductor CuFeS2. Mater. Today Phys. 3, 85–92 (2017)
Vaney, J.-B., et al.: Magnetism-mediated thermoelectric performance of the Cr-doped bismuth telluride tetradymite. Mater. Today Phys. 9, 100090 (2019)
Berche, A., Jund, P.: Thermoelectric power factor of pure and doped ZnSb via DFT based defect calculations. Phys. Chem. Chem. Phys. 21(41), 23056–23064 (2019)
Xu, N., Xu, Y., Zhu, J.: Topological insulators for thermoelectrics. npj Quantum Mater. 2(1), 51 (2017)
Hasan, M.Z., Moore, J.E.: Three-dimensional topological insulators. Annu. Rev. Condens. Matter Phys. 2(1), 55–78 (2011)
Childres, I., et al.: AFM and Raman studies of topological insulator materials subject to argon plasma etching. Philos Mag. 93(6), 681–689 (2013)
Park, K.H., et al.: Phonon scattering due to van der Waals forces in the lattice thermal conductivity of Bi2Te3 thin films. J. Appl. Phys. 117(1), 015103 (2015)
Nakajima, S.: The crystal structure of Bi2Te3−xSex. J. Phys. Chem. Solids 24(3), 479–485 (1963)
Lejaeghere, K., et al.: Error estimates for solid-state density-functional theory predictions: an overview by means of the ground-state elemental crystals. Crit. Rev. Solid State Mater. Sci. 39(1), 1–24 (2014)
Zhang, W., et al.: First-principles studies of the three-dimensional strong topological insulators Bi2Te3, Bi2Se3 and Sb2Te3. New J. Phys. 12(6), 065013 (2010)
Ortmann, F., Bechstedt, F., Schmidt, W.: Semiempirical van der Waals correction to the density functional description of solids and molecular structures. Phys. Rev. B 73(20), 205101 (2006)
Hohenberg, P., Kohn, W.: Inhomogeneous electron gas. Phys. Rev. 136(3B), B864 (1964)
Rajpoot, P., Rastogi, A., Verma, U.P.: Insights into structural, electronic, optical and thermoelectric properties of WB and WAlB: a first principle study. Philos. Mag. 98(29), 2657–2679 (2018)
Perdew, J.P., Burke, K., Ernzerhof, M.: Generalized gradient approximation made simple. Phys. Rev. Lett. 77(18), 3865 (1996)
Blaha, P., et al.: Computer Code WIEN2K. Vienna University of Technology, Vienna (2001)
Madsen, G.K., Singh, D.J.: BoltzTraP. A code for calculating band-structure dependent quantities. Comput. Phys. Commun. 175(1), 67–71 (2006)
Li, J.-F., et al.: High-performance nanostructured thermoelectric materials. NPG Asia Mater. 2(4), 152 (2010)
Yadav, M.K., Sanyal, B.: First principles study of thermoelectric properties of Li-based half-Heusler alloys. J. Alloy. Compd. 622, 388–393 (2015)
Wei, T., Xu, B., Ji, X.: Enhanced thermoelectric properties of Bi2O2Se ceramics by Bi deficiencies. Eur. Phys. J. B 92(1), 17 (2019)
Qiu, A., Zhang, L., Wu, J.: Crystal structure, electronic structure, and thermoelectric properties of β-Zn4Sb3 from first principles. Phys. Rev. B 81(3), 035203 (2010)
Wu, W., et al.: Doping and temperature dependence of thermoelectric properties of AgGaTe2: first principles investigations. Chem. Phys. Lett. 537, 62–64 (2012)
Harman, T., Walsh, M., Turner, G.: Nanostructured thermoelectric materials. J. Electron. Mater. 34(5), L19–L22 (2005)
Bejan, A., Kraus, A.D.: Heat Transfer Handbook, vol. 1. Wiley, New York (2003)
Li, H., et al.: The van der Waals epitaxy of Bi2Se3 on the vicinal Si (111) surface: an approach for preparing high-quality thin films of a topological insulator. New J. Phys. 12(10), 103038 (2010)
Bludska, J., et al.: Lithium ions in the van der Waals gap of Bi2Se3 single crystals. J. Solid State Chem. 183(12), 2813–2817 (2010)
Xue, L., et al.: First-principles study of native point defects in Bi2Se3. AIP Adv. 3(5), 052105 (2013)
Zhang, H., et al.: Topological insulators in Bi2Se3, Bi2Te3 and Sb2Te3 with a single Dirac cone on the surface. Nat. Phys. 5(6), 438–442 (2009)
Wang, B.-T., Zhang, P.: Phonon spectrum and bonding properties of Bi2Se3: role of strong spin-orbit interaction. Appl. Phys. Lett. 100(8), 082109 (2012)
Cao, H., et al.: Structural and electronic properties of highly doped topological insulator Bi2Se3 crystals. Phys. Status Solidi (RRL) Rapid Res. Lett. 7(1–2), 133–135 (2013)
Janíček, P., et al.: Thermoelectric properties of Tl-doped Bi2Se3 single crystals. Cryst. Res. Technol. 44(5), 505–510 (2009)
Saji, A., et al.: Effects of doping, electron irradiation, H+ and He+ implantation on the thermoelectric properties of Bi2Se3 single crystals. J. Phys. Condens. Matter 17(19), 2873 (2005)
Ahmed, S.: Preparation and thermoelectric power of SnBi4Se7. Philos. Mag. 86(9), 1227–1241 (2006)
Checkelsky, J.G., et al.: Bulk band gap and surface state conduction observed in voltage-tuned crystals of the topological insulator Bi2Se3. Phys. Rev. Lett. 106(19), 196801 (2011)
Hor, Y.S., et al.: p-Type Bi2Se3 for topological insulator and low-temperature thermoelectric applications. Phys. Rev. B 79(19), 195208 (2009)
LaForge, A., et al.: Optical characterization of Bi2Se3 in a magnetic field: infrared evidence for magnetoelectric coupling in a topological insulator material. Phys. Rev. B 81(12), 125120 (2010)
Valla, T., et al.: Photoemission spectroscopy of magnetic and nonmagnetic impurities on the surface of the Bi2Se3 topological insulator. Phys. Rev. Lett. 108(11), 117601 (2012)
Madsen, G.K.: Automated search for new thermoelectric materials: the case of LiZnSb. J. Am. Chem. Soc. 128(37), 12140–12146 (2006)
Chaput, L., et al.: Transport in doped skutterudites: Ab initio electronic structure calculations. Phys. Rev. B 72(8), 085126 (2005)
Lee, M.-S., Mahanti, S.D.: Validity of the rigid band approximation in the study of the thermopower of narrow band gap semiconductors. Phys. Rev. B 85(16), 165149 (2012)
Min, Y., et al.: Synthesis of multishell nanoplates by consecutive epitaxial growth of Bi2Se3 and Bi2Te3 nanoplates and enhanced thermoelectric properties. ACS Nano 9(7), 6843–6853 (2015)
Min, Y., et al.: Surfactant-free scalable synthesis of Bi2Te3 and Bi2Se3 nanoflakes and enhanced thermoelectric properties of their nanocomposites. Adv. Mater. 25(10), 1425–1429 (2013)
Sun, Y., et al.: Atomically thick bismuth selenide freestanding single layers achieving enhanced thermoelectric energy harvesting. J. Am. Chem. Soc. 134(50), 20294–20297 (2012)
Chen, X., et al.: Potential thermoelectric performance of hole-doped Cu2O. New J. Phys. 15(4), 043029 (2013)
Zhang, L., Du, M.-H., Singh, D.J.: Zintl-phase compounds with SnSb4 tetrahedral anions: Electronic structure and thermoelectric properties. Phys. Rev. B 81(7), 075117 (2010)
Acknowledgements
This work was supported by Ministry of Education (MOE) Malaysia under FRGS Grant 600-IRMI/FRGS 5/3 (337/2019). Most appreciated to Universiti Teknologi MARA (UiTM) and Universiti Teknologi Malaysia (UTM) for the facilities provided. The author (Bakhtiar Ul Haq) extends their appreciation to the Deanship of Scientific Research at King Khalid University for funding this work through Research Groups Program under Grand no. R.G.P. 2/21/41.
Funding
This research was supported by Ministry of Education (MOE) Malaysia under FRGS grant 600-IRMI/FRGS 5/3 (337/2019) and by Deanship of Scientific Research at King Khalid University under Grant R.G.P. 2/21/41.
Author information
Authors and Affiliations
Contributions
MZM: conceptualization, formal analysis, investigation, writing—original draft, methodology, data curation, visualization. MFMT: software, validation, resources, supervision, writing—review and editing, project administration, funding acquisition. AR: methodology, software, data curation. MM: supervision. AS: supervision, software. OHH: supervision, review. AMMA: supervision. BUH: supervision, validation, writing—review and editing. MZAY: supervision, validation, writing—review and editing.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mohyedin, M.Z., Taib, M.F.M., Radzwan, A. et al. Enhanced mechanism of thermoelectric performance of Bi2Se3 using density functional theory. Mater Renew Sustain Energy 9, 15 (2020). https://doi.org/10.1007/s40243-020-00176-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40243-020-00176-4