Abstract
Ceria (CeO2) nanocubes were synthesized by a hydrothermal method and weak ferromagnetism was observed in room temperature. After ultraviolet irradiation, the saturation magnetization was significantly enhanced from ~3.18 × 10−3 to ~1.89 × 10−2 emu g−1. This is due to the increase of oxygen vacancies in CeO2 structure which was confirmed by X-ray photoelectron spectra. The first-principle calculation with Vienna ab-initio simulation package was used to illustrate the enhanced ferromagnetism mechanism after calculating the density of states (DOSs) and partial density of states (PDOSs) of CeO2 without and with different oxygen vacancies. It was found that the increase of oxygen vacancies will enlarge the PDOSs of Ce 4f orbital and DOSs. Two electrons in one oxygen vacancy are respectively excited to 4f orbital of two Ce atoms neighboring the vacancy, making these electron spin directions on 4f orbitals of these two Ce atoms parallel. This superexchange interaction leads to the formation of ferromagnetism in CeO2 at room temperature. Our work indicates that ultraviolet irradiation is an effective method to enhance the magnetism of CeO2 nanocube, and the first-principle calculation can understand well the enhanced magnetism.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Nanocrystalline ceria (CeO2) has attracted much attention due to its fascinating mechanical and physic-chemical properties, as well as wide applications in various fields, including polishing materials [1, 2], automobile exhaust catalysts [3–5], fuel cell materials [6, 7], gas sensors [8, 9], high temperature superconducting materials [10], ultraviolet ray detectors, etc. [11, 12]. Recently, Zhang et al. [13] reported that CeO2 nanoparticles have great potential for multifunctional therapeutic applications in cancer therapy. Flytzani-Stephanopoulos et al. [14] used different nanostructured CeO2 materials as a support to deposit gold clusters and found that Au/CeO2 catalysts showed a strong support shape effect in the water-gas shift reaction. Most of the properties of cerium oxide was found to be related with oxygen vacancies in the structure [15–18].
It is well known that CeO2 with perfect structure is paramagnetic. When one of oxygen atoms is removed, two electrons will be left and localized strongly at the f-level traps on two Ce atoms. This will cause the formal valence of two neighboring Ce atoms changing from +4 to +3, and therefore resulting in the formation of magnetism. Lee and co-workers [17] examined the localization behavior of CeO2 with various degrees of oxygen deficiency as well as the associated magnetic properties and their origins using first-principles methods in the Vienna ab-initio simulation package (VASP). Choudhury and Choudhury [10] investigated how oxygen vacancies and cationic Ce3+ defects in ceria affect the band gap property by changing its structural regularity and then control its visible luminescence. In addition, vacancies in some other non-magnetic materials can also induce magnetism. Si et al. [19] found that vacancies in hexagonal boron nitride nanosheets (h-BN) could generate magnetic moments and form ferromagnetism, and they conducted some experiments to test their discovery.
Although some methods could generate magnetism change such as spin-reorientation transition (SRT) in ultrathin Ni films grown on Cu (100) [20], few papers report the experimental methods of obtaining oxygen vacancies and changing the valence state. Recently, Qin et al. [21] improved the magnetic properties of semiconductors and found that UV irradiation could significantly enhance the magnetism of the (111) twinned BaTiO3 crystallites. They demonstrated that magnetism might originate from the increase in oxygen vacancies and Ti3+ cations formed by capturing an excited electron from Ti4+ under UV irradiation. Enlightened by this report, we speculate that the valence state might also change (from Ce4+ to Ce3+) under UV irradiation. Herein, the optical and magnetic properties of CeO2 under UV irradiation were investigated and the electron density of states (DOSs) and the electron partial density of states (PDOSs) were calculated via density functional theory for a better understanding of the phenomenon.
2 Experimental Details
2.1 Synthesis of CeO2 Nanocubes
The uniform organic-capping-free CeO2 nanocubes were synthesized using a hydrothermal process [22]. Briefly, 434.3 mg of Ce(NO3)3·6H2O and 1.6 mg of Na3PO4 were mixed in 40 mL deionized water and sonicated for 30 min. The mixed solution was then transferred into a Teflon-lined autoclave with 50 mL capacity. The vessel was sealed and heated at 200 °C for 24 h in an electric furnace. Then the product was collected and cleansed by centrifugation at 10,000 r min−1 for 5 min and re-dispersed twice in ethanol. The precipitate was then calcined at 400 °C for 4 h and collected for further characterization.
2.2 UV Irradiation on CeO2
The dried sample was uniformly distributed in a square crucible and put in a darkroom to irradiate for 24 h under the UV lamp.
2.3 Characterization of CeO2
The powder X-ray diffraction (XRD) patterns were recorded on PANalytical Empyrean equipped with a PIXcel with a 1D detector at 40 kV and 40 mA. Field emission scanning electron microscopy (FESEM) was carried out with a Nova 400 Nano microscope to analyze the morphology and size of the product. Transmission electron microscopy (TEM) was used to analyze the morphology and size of the samples with JEOL-400EX. The X-ray photoelectron spectra (XPS) were conducted by an ESCALab MKI X-ray photoelectron spectrometer, using non-monochromatized Mg Kα X-ray as the excitation source. The reflection spectrum of the sample was measured using UV-3600 (SHIMADZU) UV–VIS–NIR Spectrophotometer. Magnetism measurement was carried out on superconducting quantum interference device (SQUIDs) measurement.
2.4 Computation of Magnetism
First-principles methods, implemented in the Vienna ab-initio simulation package (VASP) [23], were used to study the magnetism of CeO2 without and with oxygen vacancies. Because of the strong Coulomb interaction of the localized Ce 4f electrons, the standard density functional theory (DFT) calculations with the correction of Hubbard U parameter (DFT+U) were employed [24, 25]. We chose U = 7 eV [26] to improve the prediction of the computation. And a 500 eV plane-wave energy cutoff was used to expand the electronic wave functions. The 7 × 7 × 7 Monkhorst–Pack grid was used for the sampling of the Brillouin zone during geometrical optimization. A supercell of 2 × 2 × 2 without any vacancy and with different oxygen vacancies was built to simulate the magnetic properties of CeO2. All the atomic positions and lattice parameters were relaxed and optimized until the convergence of force reaches 0.01 eV Å−1.
3 Results and Discussion
A typical XRD pattern of the sample is shown in Fig. 1a. All the peaks can be indexed to the cubic phase (Fm3m, JCPDS 34-0394) of CeO2 without any impurity peaks. FESEM images of the synthesized CeO2 sample, as shown in Fig. 1b, c, demonstrate that the particles are quite uniform and have regular cube-like morphology with a size of 200 nm. TEM image in Fig. 1d also shows clear cubic shape of CeO2 particle. The inset is the high-resolution TEM image of the selected area, which has lattice planes (100) with d-spacing of 0.27 nm.
Figure 2a, b show UV–Vis reflectance spectra and Kubelka–Munk functions of the CeO2 nanocubes without and with UV irradiation. Extrapolating the linear part of Kubelka–Munk function, which is actually the ratio of the absorption and scattering factors from the optical diffuse reflectance spectrum [27], the energy gap of the CeO2 can be evaluated as 3.13 and 3.04 eV for the CeO2 sample without and with UV irradiation, respectively (Fig. 2a, b) [28, 29]. The reduced band gap can be attributed to the defect energy level, as some previous studies have reported that oxygen deficiencies create additional energy level within the forbidden energy gap [30, 31].
Since the intensity of Ce 4p and Ce 4d is much lower compared to that of Ce 3d, we choose Ce 3d signal in XPS results to analyze further. Figure 3a shows the photoelectron spectrum of Ce 3d core level before UV irradiation, among which V and U are for Ce3+ and Ce4+ states, respectively. The binding energy peaks labeled as V1 and V2 are located at 883.26 eV and 902.81 eV, indicating the Ce3+3d5/2 and Ce3+3d3/2. The peaks (U1, U2 U3, U4, U5, and U6) of Ce4+3d5/2 and Ce4+3d3/2 are respectively shown at binding energy of 881.48, 888.34, 897.73, 899.85, 907.05, and 916.34 eV [32–34]. Compared with the sample after UV irradiation in Fig. 3b, it can be found that positions of Ce 3d peaks are nearly unchanged. However, the content of elements changes and the intensity ratio of Ce3+ to Ce4+ increases from 0.260 to 0.332. This may be ascribed to the increase of Ce3+ ions after UV irradiation. Figure 3c shows the O 2p core level of the sample before UV irradiation, labeled as O1, O2, and O3, which indicates the valence of O is -2. The levels of O 2p peaks at 528.83 and 530.86 eV are ascribed to O2− ions which are related to Ce4+ and Ce3+ ions [33], while the peak of 532.47 eV is attributed to the oxygen absorbed onto the surface of the samples [35, 36]. Same with Ce 3d, the positions of O 2p peaks after UV irradiation do not shift while the relative intensity of these peaks changes (Fig. 3d), which indicates the change of element quantity. In calculation results, the intensity ratio of O2 to O1 increases from 1.183 to 1.291, demonstrating that the O2− ions related to Ce3+ increase, which confirms the increase in oxygen vacancies. All the curve-fitting processes in Fig. 3 use a mixed Gaussian–Lorentzian simulation method with the same full width at half-maximum.
Figure 4 shows the hysteresis loops of sample from −15,000 Oe to +15,000 Oe before and after UV irradiation. The saturation magnetization of the sample before UV irradiation is 3.18 × 10−3 emu g−1, while it was greatly enhanced to 1.89 × 10−2 emu g−1 after UV irradiation. This may relate to the increase of oxygen vacancies caused by UV irradiation.
From the above discussion, we have demonstrated that UV irradiation can generate oxygen vacancies, and oxygen vacancies will induce the enhancement of magnetism. In order to understand the mechanism, electron DOS, projected density of states (PDOS), and the magnetism of the structure were calculated using the first-principle calculation in the VASP. In all calculations, the projector augmented wave method (PAW) [37] with the frozen-core approximation was used for the ion–electron interactions. Exchange correlation interactions were described by the generalized gradient approximation (GGA) [38].
The DOSs and PDOSs of CeO2 without and with one oxygen vacancy and two oxygen vacancies were calculated and the results are shown in Fig. 5. One can see the perfect structure of tetrahedral CeO2 supercell with 32 cerium atoms and 64 oxygen atoms. Each oxygen atom is surrounded by four cerium atoms with the same distance. To simplify the atom orbitals, the f orbitals of Ce 4f are marked as 4f-3 ~ 4f3 and the p orbitals of O 2p are marked as Px ~ Pz as shown in Fig. 5b. From the total DOS of CeO2, all the electron spin-up and spin-down states are symmetric and show no magnetism in the perfect CeO2 cell. Comparing the Ce 4f state with O 2p, we have observed that O 2p contributes more to the total DOS at the top valence band than the Ce 4f. While at the bottom conduction band the majority was formed by Ce 4f. The integrative action of Ce 4f and O 2p makes the CeO2 non-magnetic. When one oxygen is removed, an oxygen vacancy is generated, as shown in Fig. 5c. Several PDOSs of Ce 4f are symmetric except f-3, f-2, and f3, which generate most of the magnetism of CeO2 with one vacancy. From the PDOSs of O 2p, the Px, Py, and Pz states are symmetric at the top valence band constituting most of the valence band of CeO2, as can be seen from Fig. 5d. Meanwhile, at the bottom conduction band, O 2p exhibits slight asymmetry which contributes to the formation of the conduction band of CeO2. With one oxygen vacancy, the calculation of magnetism of the sample is about 1.213 μB. After another oxygen atom is removed, two oxygen vacancies are formed. Herein, we choose two cases to analyze the magnetism as depicted in Fig. 5e, g. Comparing the DOSs and PDOSs of Ce 4f and O 2p in Fig. 5f, h, it is not difficult for us to discover that all their electron spin-up and spin-down in f orbitals of Ce 4f are asymmetric, generating most of the magnetism of CeO2. Same as the situation in Fig. 5b, the electron spin-up and spin-down of O 2p are symmetric at the top valence band and reveal a bit of asymmetry at the bottom conduction band. Since the asymmetry of PDOSs in f orbitals in Fig. 5h is higher than that of PDOSs in f orbitals in Fig. 5f, the magnetizaiton of the sample in Fig. 5h is larger than that in Fig. 5f in accordance with the values in the figure (M 2 = 1.912 μB, M 2′ = 1.968 μB). Moreover, the magnetization of the sample with two oxygen vacancies is obviously larger than that with one oxygen vacancy, which well matches our demonstration that the enhancement of the magnetism of CeO2 after UV irradiation is due to the generation of oxygen vacancies. Since the oxygen vacancy exhibits positive electricity, it attracts nearest oxygen atoms. The blue arrows in Fig. 5c, e, g demonstrate the displacement of the neighboring oxygen atoms. All the structures of CeO2 without and with oxygen vacancies are optimized in the calculations of the DOSs, PDOSs, and magnetism.
Figure 6a shows the schematic of superexchange interaction among 1Ce, 2Ce, and O atoms. The two Ce atoms are respectively reduced by two electrons from the oxygen vacancy, forming a Ce–O–Ce bond together with the neighboring O atom, which favors a 90° superexchange interaction, leading to magnetism [17, 39]. Figure 6b–f display the process of superexchange interaction of Ce–O–Ce. First, one electron on one O 2p orbital is excited by UV irradiation to one 4f orbital of 1Ce atom (Fig. 6c), and its spin direction is parallel to the electron on Ce 4f orbital based on Hund’s rule [40] (Fig. 6d). Since the Ce–O–Ce bond angle is close to 90°, the electron with the same spin direction on another O 2p orbital is exchanged with 4f orbital of 2Ce atom (Fig. 6e), which makes the spin direction of the electron on 2Ce 4f orbital parallel to it (Fig. 6f). Therefore, the magnetic moments of these two Ce atoms have the same direction, generating ferromagnetic coupling. With the increase in oxygen vacancies, the tetrahedral structure of the sample is further destroyed, making the Ce atoms close to the oxygen vacancies, which increases the total magnetic momentum. Back to Fig. 5, as UV irradiation produces more oxygen vacancies in the structure of CeO2, the electron spin on Ce 4f orbitals becomes more complicated, making the PDOSs of Ce 4f more asymmetric. Thus UV irradiation can enhance the magnetism by producing oxygen vacancies.
4 Conclusions
In this work, uniform CeO2 nanocubes were synthesized and oxygen vacancy can be increased and therefore the magnetism was enhanced by UV irradiation. The first-principle calculation was used to explain the magnetism enhancement mechanism. According to the calculation results, the increase of oxygen vacancy which confirmed by XPS measurements will enhance the DOSs of Ce4f orbital, and therefore superexchange interaction of Ce–O–Ce generates magnetism. This work demonstrates an effective route to produce diluted magnetism for CeO2 nanocubes and offers a better understanding of room-temperature magnetism in CeO2 nanocrystals.
References
X.L. Wang, S.Z. Yi, E.W. Liang, Y.Y. Wu, Z.X. Fang, Study on preparation of polishing powder for LCD. Adv. Mater. Res. 785–786, 480–483 (2013). doi:10.4028/www.scientific.net/AMR.785-786.480
Y. Chen, Z.N. Li, N.M. Miao, Polymethylmethacrylate (PMMA)/CeO2 hybrid particles for enhanced chemical mechanical polishing performance. Tribol. Int. 82, 211–217 (2015). doi:10.1016/j.triboint.2014.10.013
M. Ozawa, Role of cerium-zirconium mixed oxides as catalysts for car pollution: a short review. J. Alloy. Compd. 275, 886–890 (1998). doi:10.1016/S0925-8388(98)00477-0
S.Y. Christou, S. Garacia-Rodriguez, J.L.G. Fierro, A.M. Efstathiou, Deactivation of Pd/Ce0.5Zr0.5O2 model three-way catalyst by P, Ca and Zn deposition. Appl. Catal. B: Environ. 111, 233–245 (2012). doi:10.1016/j.apcatb.2011.10.004
Z.X. Yang, X.H. Yu, Z.S. Lu, S.F. Li, K. Hermansson, Oxygen vacancy pairs on CeO2 (110): a DFT+U study. Phys. Lett. A 373(31), 2786–2792 (2009). doi:10.1016/j.physleta.2009.05.055
K.C. Anjaneya, G.P. Nayaka, J. Manjanna, G. Govindaraj, K.N. Ganesha, Preparation and characterization of Ce1-xGdxO2-delta (x = 0.1–0.3) as solid electrolyte for intermediate temperature SOFC. J. Alloy. Compd. 578, 53–59 (2013). doi:10.1016/j.jallcom.2013.05.010
E. Bekyarova, P. Fornasiero, J. Kaspar, M. Graziani, CO oxidation on Pd/CeO2-ZrO2 catalysts. Catal. Today 45(1–4), 179–183 (1998). doi:10.1016/S0920-5861(98)00212-0
H. Yahiro, Y. Baba, K. Eguchi, H. Arai, High-temperature fuel-cell with ceria-yttria solid electrolyte. J. Electrochem. Soc. 135(8), 2077–2080 (1988). doi:10.1149/1.2096212
M.F. Al-Kuhaili, S.M.A. Durrani, I.A. Bakhtiari, Carbon monoxide gas-sensing of CeO2-ZnO thin films. Appl. Surf. Sci. 255(5), 3033–3039 (2008). doi:10.1016/j.apsusc.2008.08.058
B. Choudhury, A. Choudhury, Ce3+ and oxygen vacancy mediated tuning of structural and optical properties of CeO2 nanoparticles. Mater. Chem. Phys. 131(3), 666–671 (2012). doi:10.1016/j.matchemphys.2011.10.032
Y. Taga, Recent progress in coating technology for surface modification of automotive glass. J. Non-Cryst. Solids 218, 335–341 (1997). doi:10.1016/S0022-3093(97)00281-0
S. Zec, S. Boskovic, B. Kaluderovic, Z. Bogdanov, N. Popovic, Chemical reduction of nanocrystalline CeO2. Ceram. Int. 35(1), 195–198 (2009). doi:10.1016/j.ceramint.2007.10.031
L. Zhang, H. Jiang, M. Selke, X.M. Wang, Selective cytotoxicity effect of cerium oxide nanoparticles under UV irradiation. J. Biomed. Nanotechnol. 10(2), 278–286 (2014). doi:10.1166/jbn.2014.1790
R. Si, M. Flytzani-Stephanopoulos, Shape and crystal-plane effects of nanoscale ceria on the activity of Au-CeO2 catalysts for the water-gas shift reaction. Angew. Chem. Int. Edit. 47(15), 2884–2887 (2008). doi:10.1002/anie.200705828
N. Izu, S. Nishizaki, T. Itoh, M. Nishibori, W. Shin, I. Matsubara, Gas response, response time and selectivity of a resistive CO sensor based on two connected CeO2 thick films with various particles sizes. Sens. Actuators B 136(2), 364–370 (2009). doi:10.1016/j.snb.2008.12.018
M. Nolan, Hybrid density functional theory description of oxygen vacancies in the CeO2 (110) and (100). Chem. Phys. Lett. 499(1–3), 126–130 (2010). doi:10.1016/j.cplett.2010.09.016
X.P. Han, J.C. Lee, H.I. Yoo, Oxygen-vacancy-induced ferromagnetism in CeO2 from first principles. Phys. Rev. B 79(10), 100403 (2009). doi:10.1103/PhysRevB.79.100403
S. Phokha, S. Pinitsoontorn, S. Maensiri, Structure and magnetic properties of monodisperse Fe3+-doped CeO2 nanospheres. Nano-Micro Lett. 5(4), 223–233 (2013). doi:10.5101/nml.v5i4.p223-233
M.S. Si, D.Q. Gao, D.Z. Yang, Y. Peng, Z.Y. Zhang, D.S. Xue, Y.S. Liu, X.H. Deng, G.P. Zhang, Intrinsic ferromagnetism in hexagonal boron nitride nanosheets. J. Chem. Phys. 140, 204701 (2014). doi:10.1063/1.4879055
C. Klein, R. Ramchal, A.K. Schmid, M. Farle, Controlling the kinetic order of spin-reorientation transitions in Ni/Cu(100) films by tuning the substrate step structure. Phys. Rev. B 75, 193405 (2007). doi:10.1103/PhysRevB.75.193405
S. Qin, D. Liu, Z. Zuo, Y. Sang, H. Liu, UV-irradiation-enhanced ferromagnetism in BaTiO3. J. Phys. Chem. Lett. 1(1), 238–241 (2010). doi:10.1021/jz900131x
L. Feng, D.T. Hoang, C.K. Tsung, W.Y. Huang, S.H.Y. Lo, J.B. Wood, H. Wang, J.Y. Tang, P.D. Yang, Catalytic properties of Pt cluster-decorated CeO2 nanostructures. Nano Res. 4(1), 61–71 (2011). doi:10.1007/s12274-010-0042-4
G. Kresse, J. Furthmuller, Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54(16), 11169–11186 (1996). doi:10.1103/PhysRevB.54.11169
D.A. Andersson, S.I. Simak, N.V. Skorodumova, I.A. Abrikosov, B. Johansson, Theoretical study of CeO2 doped with tetravalent ions. Phys. Rev. B 76(17), 174119 (2007). doi:10.1103/PhysRevB.76.174119
M. Nolan, S.C. Parker, G.W. Watson, The electron structure of oxygen vacancy defects at the low index surfaces of ceria. Surf. Sci. 595(1–3), 223–232 (2005). doi:10.1016/j.susc.2005.08.015
C. Loschen, J. Carrasco, K.M. Neyman, F. Illas, First-principles LDA+U and GGA+U study of cerium oxides: dependence on the effective U parameter. Phys. Rev. B 75, 035115 (2007). doi:10.1103/PhysRevB.75.035115
J. Li, Z. Chen, X.X. Wang, D.M. Proderpio, A novel two-dimensional mercury antimony telluride: low temperature synthesis and characterization of RbHgSbTe3. J. Alloys Compd. 262, 28–33 (1997). doi:10.1016/S0925-8388(97)00324-1
J. Xu, C.G. Hu, Y. Xi, C. Peng, B.Y. Wan, X.S. He, Synthesis, photoluminescence and magnetic properties of barium vanadate nanoflowers. Mater. Res. Bull. 46(6), 946–950 (2011). doi:10.1016/j.materresbull.2011.02.023
X.A. Huang, D. Kocaefe, Y. Kocaefe, Y. Boluk, A. Pichette, A spectrocolorimetric and chemical study on color modification of heat-treated wood during artificial weathering. Appl. Surf. Sci. 258(14), 5360–5369 (2012). doi:10.1016/j.apsusc.2012.02.005
D.C. Cronemeyer, Infrared absorption of reduced rutile TiO2 single crystals. Phys. Rev. 113(5), 1222–1226 (1959). doi:10.1103/PhysRev.113.1222
D.L. Guo, C.G. Hu, Y. Xi, UV-irradiation-enhanced ferromagnetism of barium vanadate (Ba3V2O8) nanoflowers. J. Alloy. Compd. 550, 389–394 (2013). doi:10.1016/j.jallcom.2012.10.152
X.H. Lu, X. Huang, S.L. Xie, D.Z. Zheng, Z.Q. Liu, C.L. Liang, Y.X. Tong, Facile electrochemical synthesis of single crystalline CeO2 octahedrons and their optical properties. Langmuir 26(10), 7569–7573 (2010). doi:10.1021/la904882t
A. Arumugam, C. Karthikeyan, A.S.H. Hameed, K. Gopinath, S. Gowri, V. Karthika, Synthesis of cerium oxide nanoparticles using Gloriosa superba L. leaf extract and their structural, optical and antibacterial properties. Mater. Sci. Eng. C 49, 408–415 (2015). doi:10.1016/j.msec.2015.01.042
L.N. Wang, F.M. Meng, Oxygen vacancy and Ce3+ ion dependent magnetism of monocrystal CeO2 nanopoles synthesized by a facile hydrothermal method. Mater. Res. Bull. 48(9), 3492–3498 (2013). doi:10.1016/j.materresbull.2013.05.036
Z. Zhang, C. Hu, M. Hashim, P. Chen, Y. Xiong, C. Zhang, Synthesis and magnetic properties of FeMoO4 nanorods. Mater. Sci. Eng. B 176(9), 756–761 (2011). doi:10.1016/j.mseb.2011.02.018
X.Y. Wu, J. Du, H.B. Li, M.F. Zhang, B.J. Fan, Y.C. Zhu, Y.T. Qian, Aqueous mineralization process to synthesize uniform shuttle-like BaMoO4 microcrystals at room temperature. J. Solid State Chem. 180(11), 3288–3295 (2007). doi:10.1016/j.jssc.2007.07.010
G. Kresse, D. Joubert, From ultrasoft pseudopotential to the projector augmented-wave method. Phys. Rev. B 59(3), 1758–1775 (1999). doi:10.1103/PhysRevB.59.1758
J.P. Perdew, K. Burke, M. Ernzerhof, Generalized gradient approximation made simple. Phys. Rev. Lett. 77(18), 3865–3868 (1996). doi:10.1103/PhysRevLett.77.386
J.B. Goodenough, Magnetism and the Chemical Bond (Interscience, New York, 1963)
S. Yamanaka, K. Koizumi, Y. Kitagawa, T. Kawakami, M. Okumura, K. Yamaguchi, Chemical bonding, less screening, and Hund’s rule revisted. Int. J. Quantum Chem. 105(6), 687–700 (2005). doi:10.1002/qua.20784
Acknowledgments
This work is supported by the National High Technology Research and Development Program (863 program) of China (2015AA034801), NSFC (11204388, 51402112), the Fundamental Research Funds for the Central Universities (CQDXWL-2014-001 and CQDXWL-2013-012), and the large-scale equipment sharing fund of Chongqing University.
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Kang, Y., Leng, Q., Guo, D. et al. Room-Temperature Magnetism of Ceria Nanocubes by Inductively Transferring Electrons to Ce Atoms from Nearby Oxygen Vacancy. Nano-Micro Lett. 8, 13–19 (2016). https://doi.org/10.1007/s40820-015-0056-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40820-015-0056-2