Abstract
The ternary plasmonic AgCl/Ag/g-C3N4 photocatalysts were successfully fabricated by a modified deposition–precipitation method, through which Ag/AgCl nanoparticles (5–15 nm in size) were evenly dispersed on the surface of g-C3N4. The AgCl/Ag/g-C3N4 composites exhibited higher photocatalytic activity than Ag/AgCl and g-C3N4. The enhanced photocatalytic performance could be attributed to an efficient separation of electron–hole pairs through a Z-scheme mechanism, in which Ag nanoparticles acted as charge separation centers.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
As a new metal-free semiconductor, polymeric graphitic carbon nitride (g-C3N4) has been developed to cope with environmental pollutants due to its outstanding mechanical, optical, electronic, and catalytic properties as well as its high thermal and chemical stability [1–4]. However, its practical application is quite limited owing to its appreciable drawbacks, including low specific surface area, high photogenerated electron–hole recombination rate, and the limited range of visible light photo-responses [5, 6]. To tackle these issues, many methods have been proposed, such as doping extraneous elements [7–10], designing porous structures [11–15], depositing noble metals [16–19], and coupling with other semiconductors [20–23]. Although some progresses have been achieved, the light harvesting ability and quantum efficiency of these modified g-C3N4 systems are still poor.
Noble metal nanoparticles have attracted considerable attention due to their application as active components for the preparation of various efficient visible light photocatalysts. Logar et al. reported Ag/TiO2 plasmonic photocatalyst that showed high efficiency for degradation of methyl orange (MO) [24]. Parida et al. developed Au/g-C3N4 plasmonic photocatalyst with enhanced photocatalytic activity under irradiation of visible light [17]. Besides, Ag/AgCl [25–27], Ag/AgBr [28], and Ag/AgI [29, 30] have also been used as co-catalysts to enhance the photocatalytic activity of semiconductors under visible light irradiation. It is believed that noble metal nanoparticles can act as active sites and play vital roles in effective visible light absorption and subsequent photocatalytic reactions. The possible reason is that noble metal nanoparticles can strongly absorb visible light because of their localized surface plasmon resonance (LSPR), which can be tuned by varying their size, shape, and surroundings [31].
Recently, two types of Ag/AgCl/g-C3N4 composites were fabricated by Yao et al. [32] and Zhang et al. [33]. The as-prepared products showed efficient photocatalytic degradation activity. However, their precipitation methods not only lack precise control over the morphology and size of final products, but also induce reunion reaction of AgCl [34].
In this work, AgCl/Ag/g-C3N4 composites were fabricated by a modified deposition–precipitation method to overcome the above shortcomings. The photocatalytic activities of the AgCl/Ag/g-C3N4 composites were evaluated by the photocatalytic degradation of Rh B and MO aqueous solution under irradiation of visible light. A plasmonic Z-scheme photocatalytic mechanism was then proposed to explain the enhancement of the photocatalytic activity of the AgCl/Ag/g-C3N4 photocatalysts.
2 Experimental
All reagents supplied by Sinopharm Chemical Reagent co., Ltd. are of analytical grade and used as received without further purification.
2.1 Preparation of Photocatalysts
2.1.1 Preparation of g-C3N4 Powders
The metal-free g-C3N4 powders were fabricated by heating melamine in a muffle furnace. Typically, 5 g of melamine was placed in a semi-closed alumina crucible with a cover. The crucible was heated to 550 °C at a heating rate of 10 °C min−1 and held for 4 h. After the reaction, the alumina crucible was cooled to room temperature. The products were collected and ground into powders.
2.1.2 Preparation of AgCl/Ag/g-C3N4 Hybrid Composites
In a typical preparation process, 0.4 g of g-C3N4 powders and 0.64 g of hexadecyl trimethyl ammonium chloride (CTAC) were added into 200 mL of deionized water, and the suspension was stirred for 30 min and sonicated for 30 min. Then, 4.4 mL of 0.1 M AgNO3 was quickly added to the above mixture. During this process, the excessive surfactant CTAC not only adsorbed onto the surface of g-C3N4 to limit the number of nucleation sites for AgCl to grow, resulting in homogenously dispersed AgCl, but also induced Cl− to precipitate Ag+ in the suspension. The resulting suspension was stirred for 1 h and then placed under irradiation of 300 W Xe lamp for 30 min. The suspension was filtered, washed using deionized water, and dried at 80 °C for 8 h. And then, the gray powder was calcined at 300 °C for 3 h. Different molar ratios of AgCl/Ag/g-C3N4 photocatalysts (3, 5, 10, 15, 20, and 40 at%) were fabricated with the similar procedure.
2.2 Characterization of Photocatalysts
X-ray diffraction (XRD) data were collected on a D-MAX 2500/PC diffractometer (Japan). The surface morphologies of the as-prepared samples were characterized with field emission scanning electron microscopy (FESEM, JEOL JSM-6700F) and transmission electron microscopy (TEM, JEOL JEM-2100F). Photoluminescence (PL) spectra were measured at room temperature on F-4600 fluorescence spectrometer (Hitachi, Japan) with an excitation wavelength of 365 nm. X-ray photoelectron spectroscopy (XPS) analysis was performed on an ESCALAB 250 X-ray photoelectron spectrometer. The Fourier transform infrared spectra (FTIR) of the samples were recorded using IRAffinity-1 spectrometer (Shimadzu, Japan). Ultraviolet visible (UV–Vis) diffuse reflectance spectra (DRS) of the samples were obtained on an UV–vis spectrophotometer (Shimadzu UV-2600, Japan) in the range of 200 to 800 nm and BaSO4 as a standard reference. The Brunauer–Emmett–Teller (BET) surface area (SBET) of the samples were measured by nitrogen adsorption–desorption isotherm measurements on a micromeritics ASAP2020 system. The electron spin resonance (ESR) signals of ·OH and ·O2 − radicals spin-trapped with the spin-trap reagent DMPO (5, 5-dimethyl-1-pyrroline-N-oxide) in water and methanol were examined on an ESR spectrometer (ER200-SCR, Germany), respectively.
2.3 Adsorption Experiment
Adsorption experiments were carried out in the dark. In a typical adsorption procedure, 100 mg of 5 at% AgCl/Ag/g-C3N4 powers mixed with 100 mL 10 mg L−1 Rh B aqueous solution in a glass conical beaker was shaken at ambient temperature. At given time intervals, about 3 mL solution suspension was sampled and immediately centrifuged. The concentration of Rh B solution was analyzed with a UV–Vis spectrophotometer at the maximal absorption wavelength of Rh B, whose characteristic absorption peak was chosen to be 554 nm.
2.4 Test of Photocatalytic Activity
The photocatalytic activities of samples were evaluated by the degradation of Rh B and MO under 300 W Xe lamp with a 420 nm cutoff filter. In brief, 100 mg of photocatalyst was dispersed in 100 mL of a 10 mg L−1 aqueous solution of Rh B or MO in a reactor with a double layer cooled by running water to keep the temperature unchanged. Prior to irradiation, the suspensions were magnetically stirred in the dark for 1 h to ensure the establishment of an adsorption/desorption equilibrium between the photocatalyst and dye molecules. Then, the suspension was illuminated by the Xe lamp combined with magnetic stirring. At given time intervals, about 3 mL solution suspension was sampled and centrifuged. The concentrations of Rh B and MO were measured by UV–Vis spectrophotometer. Additionally, the recycle experiments were performed for five consecutive cycles to test the durability. After each cycle, the catalyst was centrifuged and washed thoroughly with distilled water several times to remove residual dye impurities and then dried at 80 °C for the next test.
3 Results and Discussion
3.1 Characterization of Photocatalysts
The crystal structures of the as-prepared samples were analyzed by the XRD pattern. Figure 1 shows the XRD patterns of the pure g-C3N4 and AgCl/Ag/g-C3N4 hybrid composites with different Ag/AgCl contents. It is observed that two broad peaks around 27.4° and 13.0° in the XRD patterns of the pure g-C3N4 are well ascribed to the (002) and (100) diffraction planes, respectively. The former, which corresponds to the interlayer distance of 0.326 nm, is attributed to the long-range interplanar stacking of aromatic units; the latter, with a much weaker intensity, which corresponds to a distance d = 0.681 nm, is associated with interlayer stacking [35]. It is obvious that the diffraction peaks at 27.7°, 32.2°, 46.2°,54.8°,57.5°,67.4°, 74.5°, and 76.7° gradually appear and the intensity increases with the increase of Ag/AgCl content, and the peaks are assigned to the (111), (200), (220), (311), (222), (400), (331), and (420) planes of AgCl crystal, respectively. A weak diffraction peak at 38.2° is also seen, which corresponds to the (111) plane of Ag crystal. It is difficult to distinguish the characteristic peak of g-C3N4 (27.4°) and the AgCl (111) plane (27.8°) because they are very close to each other. However, with the increase in the amount of Ag/AgCl, the relative intensity of (111)/(200) diffraction of AgCl decreases. This result could be attributed to pure AgCl, the relative intensity of (111) diffraction is about one half of that of (200) diffraction. Therefore, in the XRD analysis, no other crystal phases are observed, which indicated that the AgCl/Ag/g-C3N4 composites were successfully fabricated.
The morphology and microstructure of the as-prepared samples were investigated by SEM and TEM analysis. Figure 2 shows the SEM images of the pure g-C3N4 and the 5 at% AgCl/Ag/g-C3N4 composite. The pure g-C3N4 sample displays an aggregated morphology with a large size and lamellar structure. The surface of the aggregation is very smooth, showing the layer structure of g-C3N4. Figure 2b shows Ag/AgCl nanoparticles which might be deposited on the surface of g-C3N4 and a rough surface was obtained. It is observed from Fig. 3 that the g-C3N4 displays a lamellar shape and has an amorphous structure, whereas the Ag/AgCl exhibits uniform spherical particles. It is also seen that there are dark spherical particles and gray areas. The dark particles can be assigned to Ag/AgCl, whereas the gray areas can be assigned to g-C3N4. The Ag/AgCl particles are evenly dispersed on the surface of g-C3N4, and are approximately 5–15 nm in size. Figure 3c shows that the lattice fringe of 0.236 and 0.277 nm, corresponding to the (111) plane of Ag and (200) plane of AgCl, is clearly observed in the AgCl/Ag/g-C3N4 composite, which verifies the formation of an AgCl/Ag/g-C3N4 heterojunction.
The chemical composition of the as-prepared 5 at% AgCl/Ag/g-C3N4 was analyzed by XPS, as shown in Fig. 4. The survey spectrum of 5 at% AgCl/Ag/g-C3N4 shows peaks of elements of Ag, Cl, C, N, and O. No peaks for other elements is found, indicating that the hybrid composite is primarily composed of Ag, Cl, C, and N elements. To investigate and demonstrate the different chemical states of Ag, C, N, and Cl, the high-resolution XPS peaks of the different elements are provided in Fig. 5. It can be seen from the C1s spectrum that the two C1s peaks are located at 284.7 and 288.0 eV. The former is ascribed to the adventitious contamination and defect-containing sp 2-hybridized carbon atoms present in graphitic domains, whereas the latter one is assigned to C–N–C coordination [35, 36]. In the N1s spectrum, several binding energies can be separated. The main N1s peak at 398.4 eV corresponds to sp 2-hybridized aromatic N bonded to C atoms (C=N–C). The peak at 399.3 eV is assigned to the tertiary N bonded to C atoms in the form of N-(C)3. The peak at 400.7 eV is from the N–H structure. The weak peak at 403.9 eV is attributed to charging effects [4]. The high-resolution XPS spectra of Ag3d are shown in Fig. 5c. The two peaks at approximately 368.3 and 374.2 eV can be ascribed to the binding energies of Ag3d5/2 and Ag3d3/2, respectively. These two peaks can be further deconvoluted into two peaks, at about 367.9/368.6 eV and 373.9/374.6 eV, respectively [37]. The peaks at 367.9 and 373.9 eV are attributed to Ag+ of AgCl, and those at 368.6 and 374.6 eV are ascribed to the metal Ag0. On the basis of XPS peak areas, the mole ratio between Ag0 and Ag+ was calculated to be 2:3. The Cl2p XPS peaks can also be resolved into two typical peaks, 197.9 and 199.5 eV, which are ascribed to AgCl [38]. All of these results further confirm the coexistence of Ag/AgCl and g-C3N4 in the AgCl/Ag/g-C3N4 composite.
The UV–Vis diffuse reflectance spectra of the as-prepared samples are shown in Fig. 6. Pure g-C3N4 has an absorption edge at about 460 nm, which originates from its band gap of 2.7 eV. Compared with the pure g-C3N4, the series of AgCl/Ag/g-C3N4 hybrid composites show a slight red shift of the absorption edge, which is attributed to the surface plasmon resonance (SPR) effect of Ag nanocrystal formed in situ on the surfaces of the AgCl nanoparticles. In addition, the absorption intensities of AgCl/Ag/g-C3N4 composites show a significant enhancement in the visible light regions, which can also be attributed to the SPR effect of Ag nanoparticles.
PL spectra analysis has been widely used to investigate the separation efficiency of photogenerated electrons and holes in semiconductor particles [39]. Figure 7 shows the PL spectra of pure g-C3N4 and AgCl/Ag/g-C3N4 composites. It can be found that the strong emission peak of the pure g-C3N4 centered at 460 nm suggests a high recombination probability of the photogenerated electron–hole pairs, while for AgCl/Ag/g-C3N4 composites, a significant quenching of PL is observed in comparison with g-C3N4, which indicates that these composites have lower recombination rates of photogenerated electrons and holes. This demonstrates that after the formation of a heterojunction between g-C3N4 and Ag/AgCl, the recombination of photogenerated charge carriers is greatly suppressed. Therefore, the photogenerated electron–hole pairs of the AgCl/Ag/g-C3N4 composites can efficiently transfer at the interface of heterostructure, resulting in the higher photocatalytic activity than pure g-C3N4 and Ag/AgCl.
Full nitrogen adsorption isotherms of pure g-C3N4 and 5 at% AgCl/Ag/g-C3N4 composite were measured to gain the information about the specific surface area, as shown in Fig. 8. It is true that the pure g-C3N4 and the 5 at% AgCl/Ag/g-C3N4 composites have type IV isotherms and type H3 hysteresis loops, which indicates the mesoporous structure of the samples. The pore size distribution of the samples shows that most of the pores fall into the size range from 3 to 100 nm. The specific surface area of the 5 at% AgCl/Ag/g-C3N4 composite was calculated to be 11.46 m3 g−1, which is lower than that of pure g-C3N4 (14 m2 g−1). The decrease of the surface area after decoration can be attributed to the disappearance of the small pore, which can be further proved by the pore size distribution shown in the inset of Fig. 8. The results illustrate that the enhanced photocatalytic performance is not a result of the change of the BET surface areas of the samples.
3.2 Adsorption Kinetics
The adsorption kinetics of Rh B on 5 at% AgCl/Ag/g-C3N4 is shown in Fig. 9. The adsorption capacity of Rh B increases firstly and then remains unchanged with time. The adsorption equilibrium is achieved after about 30 min. The adsorption kinetics can be well fitted by a pseudo-second-order model, expressed by Eq. (1)
where k is the rate constant [g (mg min)−1], q e is equilibrium adsorption capacity (mg g−1), and q t is the amount of Rh B (mg g−1) adsorbed at time t. By plotting t/q t versus t, one can determine the values of q e and k from the slope and intercept of the fitted line, respectively. The correlation coefficient (R 2) value of the fitted plot is near unity (0.9999), indicating the applicability of the pseudo-second-order model for the above adsorption kinetics.
3.3 Photocatalytic Activities of the AgCl/Ag/g-C3N4 Hybrid Composites
The photocatalytic activities of the as-prepared AgCl/Ag/g-C3N4 composites were evaluated by monitoring the degradation of Rh B in an aqueous solution under visible light irradiation. For comparison, the performances of pure g-C3N4 and Ag/AgCl photocatalyst were also investigated under same condition. Figure 10 shows the photocatalytic activities of pure g-C3N4, Ag/AgCl, and AgCl/Ag/g-C3N4 composites. It can be clearly observed that the photocatalytic activities of AgCl/Ag/g-C3N4 composites increase firstly and then decrease with the increase of Ag/AgCl content, and the 5 at% AgCl/Ag/g-C3N4 composite exhibits the highest photocatalytic activity. The decreased photocatalytic activity may be attributed to the fact that the higher content of Ag/AgCl may easily result in the agglomeration of Ag/AgCl particles causing a low dispersibility on the surface of g-C3N4. This influences the transfer of photogenerated charge carriers. The degradation efficiency of 5 at% AgCl/Ag/g-C3N4 photocatalyst exceeds 1.14 times more than that of Ag/AgCl and 2.7 times larger than that of g-C3N4.
The photocatalytic activities of pure g-C3N4, Ag/AgCl, and 5 at% AgCl/Ag/g-C3N4 hybrid composite for the degradation of MO were also investigated, as shown in Fig. 11. These results indicate that the photocatalytic activity of 5 at% AgCl/Ag/g-C3N4 hybrid composite toward MO is also much higher than that of either pure g-C3N4 or Ag/AgCl. It suggests that a suitable molar ratio between g-C3N4 and Ag/AgCl is significant for effectively enhancing the photocatalytic activity.
Because renewable catalytic was another important factor for a photocatalyst, the stability of the 5 at% AgCl/Ag/g-C3N4 composite was investigated by a recycling test, as shown in Fig. 12. After five cycles, there was no significant loss of activity, indicating that the photocatalyst was stable during the photocatalytic test.
The excellent stability was further confirmed by the XPS of 5 at% AgCl/Ag/g-C3N4 composite before and after photodegradation. Figure 13 shows that there is no noticeable difference between the sample before and after 5 recycling runs. These results indicated that the chemical states of the AgCl/Ag/g-C3N4 composite surface remained almost unchanged during the photocatalytic degradation of Rh B or MO.
3.4 Photocatalytic Mechanism
To further investigate the photocatalytic mechanism of the AgCl/Ag/g-C3N4 hybrid composites, a series of radicals trapping experiments were performed by using ammonium oxalate (AO), N2 and t-butyl alcohol (TBA) scavengers for holes, ·O2 − and ·OH radicals, respectively. As is clear from Fig. 14, the addition of TBA did not affect the degradation rate of Rh B over 5 at% AgCl/Ag/g-C3N4 composite, suggesting that ·OH was not the main reactive species in the photocatalytic process. On the contrary, the photocatalytic degradation of Rh B was obviously suppressed after the addition of AO and N2 purging. According to these results, it can be clearly seen that h+ and ·O2 − are main reactive species for 5 at% AgCl/Ag/g-C3N4 hybrid composite in the photocatalytic degradation process of Rh B under visible light irradiation.
The g-C3N4 with a band gap of 2.7 eV is a novel metal-free visible light photocatalyst [40]. Under visible light irradiation, the g-C3N4 absorbs visible light photons to produce photogenerated electrons and holes. The photogenerated electrons react with O2 that existed in the photodegradation system, reducing it to superoxide radical anion ·O2 −. The dye molecules are degradated by photogenerated holes and ·O2 −. Ag/AgCl has been demonstrated to be an efficient visible light photocatalyst [31]. As AgCl cannot absorb visible light due to its wide band gap of 3.25 eV, the visible light absorption in Ag/AgCl is attributed to the plasmonic absorption of Ag nanoparticles which can absorb visible light and convert the plasmonic energy into LSPR oscillation. Then, the plasmon-induced electrons from the photoexcited Ag nanoparticles transfer to the CB of AgCl and the electrons on the surface of AgCl are trapped by the adsorbed O2 to form ·O2 − active species, and the plasmon-induced holes stay on the surface of Ag nanoparticles and oxidize the dye molecules [41, 42].
When the Ag/AgCl nanoparticles are coupled with g-C3N4 to form AgCl/Ag/g-C3N4 composites, a heterojunction structure is formed in the interface between g-C3N4 sheets and Ag/AgCl nanoparticles. The improved photocatalytic performances are mainly attributed to the separation efficiency of photogenerated electrons and holes in the composites. On the basis of the above results, a plasmonic Z-scheme mechanism of AgCl/Ag/g-C3N4 composites is proposed and illustrated in Fig. 15. Under visible light irradiation, both Ag and g-C3N4 absorb visible light photons to produce photogenerated electrons and holes. The plasmon-induced electrons of Ag nanoparticles are transported to the CB of AgCl to reduce oxygen, while the holes remain on the Ag nanoparticles. Meanwhile, the photogenerated electrons of g-C3N4 transfer to the Ag nanoparticles to recombine with the plasmon-induced holes produced by plasmonic absorption of Ag nanoparticles, while the VB holes remain on g-C3N4 to oxidize organic substances. Therefore, for the AgCl/Ag/g-C3N4 composites, the reduction active site is on the CB of AgCl while the oxidation active site is on the VB of g-C3N4, it is because Ag nanoparticles act as the charge separation center to form the visible light-driven AgCl/Ag/g-C3N4 Z-scheme system.
The photocatalytic mechanism is further investigated by the ESR technique. DMPO was generally applied to trapping radicals of ·O2 − and ·OH. As shown in Fig. 16, ·O2 − and ·OH radicals could be detected by the ESR under visible light irradiation. The signal of ·O2 − is much stronger than that of ·OH. Considering the band structure of g-C3N4, the VB holes (1.40 eV) from g-C3N4 cannot directly oxidize OH−/H2O into ·OH radicals (1.99 and 2.38 eV for OH−/·OH and H2O/·OH potential). The ·OH radicals should be generated via the ·O2 −→H2O2 → ·OH route [43]. This fact demonstrates that ·O2 − radicals and h + are the main active species which play important roles during the photodegradation process. Based on the result, it demonstrates again that the transport process of the photoexcited carriers of the AgCl/Ag/g-C3N4 composites is in accordance with Fig. 15. Thus, the AgCl/Ag/g-C3N4 composites exhibit excellent photocatalytic performance through Z-Scheme photocatalytic mechanism under visible light.
4 Conclusion
The hybrid AgCl/Ag/g-C3N4 photocatalysts were successfully fabricated by a modified deposition–precipitation method, which was effective for the control of photocatalyst morphology and size. The Ag/AgCl particles with the size of approximately 5–15 nm were evenly dispersed on the surface of g-C3N4. The AgCl/Ag/g-C3N4 composites exhibited the higher photocatalytic performance than Ag/AgCl and g-C3N4 over the degradation of Rh B or MO dyes, which was attributed to Ag nanoparticles act as the charge separation center to form the visible light-driven AgCl/Ag/g-C3N4 Z-scheme system. This study provides new insight into the design of highly efficient and stable g-C3N4-based plasmonic Z-Scheme photocatalysts and facilitates their practical application.
References
C. Wang, K. Maeda, A. Thomas, K. Takanabe, G. Xin, J.M. Carlsson, K. Domen, M. Antonietti, A metal-free polymeric photocatalyst for hydrogen production from water under visible light. Nat. Mater. 8(1), 76–80 (2009). doi:10.1038/nmat2317
X.C. Wang, X.F. Chen, A. Thomas, X.Z. Fu, M. Antonietti, Metal-containing carbon nitride compounds: a new functional organic-metal hybrid material. Adv. Mater. 21(16), 1–4 (2009). doi:10.1002/adma.200802627
Y. Wang, X.C. Wang, M. Antonietti, Polymeric graphitic carbon nitride as a heterogeneous organocatalyst: From photochemistry to multipurpose catalysis to sustainable chemistry. Angew. Chem. Int. Ed. 51(1), 68–89 (2012). doi:10.1002/anie.201101182
T. Are, F. Anna, G. Frederic, A. Markus, M. Jens-Oliver, S. Robert, M.C. Johan, Graphitic carbon nitride materials: variation of structure and morphology and their use as metal-free catalysts. J. Mater. Chem. 18(41), 4893–4908 (2008). doi:10.1039/b800274f
S.W. Zhang, J.X. Li, M.Y. Zeng, G.X. Zhao, J.Z. Xu, W.P. Hu, X.K. Wang, In situ synthesis of water-soluble magnetic graphitic carbon nitride photocatalyst and its synergistic catalytic performance. ACS App. Mater. Interfaces 5(23), 12735–12743 (2013). doi:10.1021/am404123z
S.C. Yan, Z.S. Li, Z.G. Zou, Photodegradation performance of g-C3N4 fabricated by directly heating melamine. Langmuri 25(17), 10397–10401 (2009). doi:10.1021/la900923z
Y. Wang, J.S. Zhang, X.C. Wang, M. Antonietti, H. Li, Boron- and fluorine-containing mesoporous carbon nitride polymers: metal-free catalysts for cyclohexane oxidation. Angew. Chem. Int. Ed. 49(19), 3356–3359 (2010). doi:10.1002/anie.201000120
G. Liu, P. Niu, C.H. Sun, S.C. Smith, Z.G. Chen, Q.G. Lu, H.M. Cheng, Unique electronic structure induced high photoreactivity of sulfur-doped graphitic C3N4. JACS 132(33), 11642–11648 (2010). doi:10.1021/ja103798k
S.C. Yan, Z.S. Li, Z.G. Zou, Photodegradation of rhodamine B and methyl orange over boron-doped g-C3N4 under visible light irradiation. Langmuir 26(6), 3894–3901 (2010). doi:10.1021/la904023j
G.G. Zhang, M.W. Zhang, X.X. Ye, X.Q. Qiu, S. Lin, X.C. Wang, Iodine modified carbon nitride semiconductors as visible light photocatalysts for hydrogen evolution. Adv. Mater. 26(5), 805–809 (2014). doi:10.1002/adma.201303611
J. Xu, Y. Wang, Y. Zhu, Nanoporous graphitic carbon nitride with enhanced photocatalytic performance. Langmuir 29(33), 10566–10572 (2013). doi:10.1021/la402268u
H. Yan, Soft-templating synthesis of mesoporous graphitic carbon nitride with enhanced photocatalytic H2 evolution under visible light. Chem. Commun. 48(28), 3430–3432 (2012). doi:10.1039/c2cc00001f
S.S. Park, S.W. Chu, C.F. Xue, D, Y. Zhao, C.S. Ha, Facile synthesis of mesoporous carbon nitrides using the incipient wetness method and the application as hydrogen adsorbent. J. Mater. Chem. 21(29), 10801–10807 (2011). doi:10.1039/c1jm10849b
Y. Wang, X.C. Wang, M. Antonietti, Y.J. Zhang, Facile one-pot synthesis of nanoporous carbon nitride solids by using soft templates. Chem. Sus. Chem. 3(4), 435–439 (2010). doi:10.1002/cssc.200900284
F. Goettmann, A. Fischer, M. Antonietti, A. Thomas, Chemical synthesis of mesoporous carbon nitrides using hard templates and their use as a metal-free catalyst for Friedel–Crafts reaction of benzene. Angew. Chem. Int. Ed. 45(27), 4467–4471 (2006). doi:10.1002/anie.200600412
N.Y. Cheng, J.Q. Tian, Q. Liu, C.J. Ge, A.H. Qusti, A.M. Asiri, A.O. Al-Youbi, X. Sun, Au-nanoparticle-loaded graphitic carbon nitride nanosheets: green photocatalytic synthesis and application toward the degradation of organic pollutants. ACS Appl. Mater. Interfaces 5(15), 6815–6819 (2013). doi:10.1021/am401802r
S. Subhajyoti, M. Satyabadi, P. Kulamani, Facile synthesis of Au/g-C3N4 nanocomposites: an inorganic/organic hybrid plasmonic photocatalyst with enhanced hydrogen gas evolution under visible-light irradiation. Chem. Cat. Chem. 6, 1453–1462 (2014). doi:10.1002/cctc.201300949
P. Xiao, Y.X. Zhao, T. Wang, Y.Y. Zhan, H.H. Wang, J.L. Li, A. Thomas, J.J. Zhu, Polymeric carbon nitride/mesoporous silica composites as catalyst support for Au and Pt nanoparticles. Chem. Eur. J. 20(10), 2872–2878 (2014). doi:10.1002/chem.201303741
Y.S. Xu, W.D. Zhang, Ag/AgBr-grafted graphite-like carbon nitride with enhanced plasmonic photocatalytic activity under visible light. Chem. Cat. Chem. 5(8), 2343–2351 (2013). doi:10.1002/cctc.201300144
L. Huang, H. Xu, Y. Li, H. Li, X. Cheng, J. Xia, Y. Xu, G. Cai, Visible-light-induced WO3/g- C3N4 composites with enhanced photocatalytic activity. Dalton Trans. 42(24), 8606–8616 (2013). doi:10.1039/c3dt00115f
S. Kumar, T. Surendar, A. Baruah, V. Shanker, Synthesis of a novel and stable g- C3N4-Ag3PO4 hybrid nanocomposite photocatalyst and study of the photocatalytic activity under visible light irradiation. J. Mater. Chem. A 1(17), 5333–5340 (2013). doi:10.1039/c3ta00186e
C. Chang, L. Zhu, S. Wang, X. Chu, L. Yue, Novel mesoporous graphite carbon nitride/BiOI heterojunction for enhancing photocatalytic performance under visible-light irradiation. ACS Appl. Mater. Interfaces 6(7), 5083–5093 (2014). doi:10.1021/am5002597
Y.L. Tian, B.B. Chang, J.L. Lu, J. Fu, F.J. Xi, X.P. Dong, Hydrothermal synthesis of graphitic carbon nitride-Bi2WO6 heterojunctions with enhanced visible light photocatalytic activities. ACS Appl. Mater. Interfaces 5(15), 7079–7085 (2013). doi:10.1021/am4013819
M. Logar, B. Jancar, S. Sturm, D. Suvorov, Weak polyion multilayer-assisted in situ synthesis as a route toward a plasmonic Ag/TiO2 photocatalyst. Langmuir 26(14), 12215–12224 (2010). doi:10.1021/la101124q
X.F. Wang, S.F. Li, Y.Q. Ma, H.G. Yu, J.G. Yu, H2WO4·H2O/Ag/AgCl composite nanoplates: a plasmonic z-scheme visible-light photocatalyst. J. Phys. Chem. C 115(30), 14648–14655 (2011). doi:10.1021/jp2037476
H. Zhang, X.F. Fan, X. Quan, S. Chen, H.T. Yu, Graphene sheets grafted Ag@AgCl hybrid with enhanced plasmonic photocatalytic activity under visible light. Environ. Sci. Technol. 45(13), 5731–5736 (2011). doi:10.1021/es2002919
G. Begum, J. Manna, R.K. Rana, Controlled orientation in a bio-Inspired assembly of Ag/AgCl/ZnO nanostructures enables enhancement in visible-light-induced photocatalytic performance. Chem. Eur. J. 18, 6847–6853 (2012). doi:10.1002/chem.201103760
M.S. Zhu, P.L. Chen, M.H. Liu, Ag/AgBr/graphene oxide nanocomposite synthesized via oil/water and water/oil microemulsions: a comparison of sunlight energized plasmonic photocatalytic activity. Langmuir 28(7), 3385–3390 (2012). doi:10.1021/la204452p
R. Liu, P. Wang, X.F. Wang, H.G. Yu, J.G. Yu, UV- and visible-light photocatalytic activity of simultaneously deposited and doped Ag/Ag(I)-TiO2 photocatalyst. J. Phys. Chem. C 116(33), 17721–17728 (2012). doi:10.1021/jp305774n
C. Hu, T.W. Peng, X.X. Hu, Y.L. Nie, X.F. Zhou, J.H. Qu, H. He, Plasmon-induced photodegradation of toxic pollutants with Ag–AgI/Al2O3 under visible-light irradiation. JACS 132, 857–862 (2010). doi:10.1021/ja907792d
P. Wang, B.B. Huang, Y. Dai, M.H. Whangbo, Plasmonic photocatalysts: harvesting visible light with noble metal nanoparticles. Phys. Chem. Chem. Phys. 14(28), 9813–9825 (2012). doi:10.1039/c2cp40823f
X. Yao, X.H. Liu, X.L. Hu, Synthesis of the Ag/AgCl/g-C3N4 composite with high photocatalytic activity under visible light irradiation. Chem. Cat. Chem. 6(12), 3409–3418 (2014). doi:10.1002/cctc.201402487
S.W. Zhang, J.X. Li, X.K. Wang, Y.S. Huang, M.Y. Zeng, J.Z. Xu, In situ ion exchange synthesis of strongly coupled Ag@AgCl/g-C3N4 porous nanosheets as plasmonic photocatalyst for highly efficient visible-light photocatalysis. ACS Appl. Mater. Interfaces 6(24), 22116–22125 (2014). doi:10.1021/am505528c
S.L. Lin, L. Liu, J.S. Hu, Y.H. Liang, W.Q. Cui, Nano Ag@AgBr surface-sensitized Bi2WO6 photocatalyst: oil-in-water synthesis and enhanced photocatalytic degradation. Appl. Sur. Sci. 324, 20–29 (2015). doi:10.1016/j.apsusc.2014.10.101
H. Katsumata, T. Sakai, T. Suzuki, S. Kaneco, Highly efficient photocatalytic activity of g-C3N4/Ag3PO4 hybrid photocatalysts through z-scheme photocatalytic mechanism under visible light. Ind. Eng. Chem. Res. 53(19), 8018–8025 (2014). doi:10.1021/ie5012036
X.J. Wang, W.Y. Yang, F.T. Li, Y.B. Xue, R.H. Liu, Y.J. Hao, In Situ microwave-assisted synthesis of porous N–TiO2/g-C3N4 heterojunctions with enhanced visible-light photocatalytic properties. Ind. Eng. Chem. Res. 52(48), 17140–17150 (2013). doi:10.1021/ie402820v
H.J. Cheng, J.G. Hou, H.M. Zhu, X.M. Guo, Plasmonic Z-scheme α/β-Bi2O3–Ag–AgCl photocatalyst with enhanced visible-light photocatalytic performance. RSC Adv. 4(78), 41622–41630 (2014). doi:10.1039/C4RA07938H
R.F. Dong, B.Z. Tian, C.Y. Zeng, T.Y. Li, T.T. Wang, J.L. Zhang, Ecofriendly synthesis and photocatalytic activity of uniform cubic Ag@AgCl plasmonic photocatalyst. J. Phys. Chem. C 117(1), 213–220 (2013). doi:10.1021/jp311970k
L.L. Chen, W.X. Zhang, C. Feng, Z.H. Yang, Y.M. Yang, Replacement/etching route to ZnSe nanotube arrays and their enhanced photocatalytic activities. Ind. Eng. Chem. Res. 51(11), 4208–4214 (2012). doi:10.1021/ie202044v
F. Dong, L.W. Wu, Y.J. Sun, M. Fu, Z.B. Wu, S.C. Lee, Efficient synthesis of polymeric g-C3N4 layered materials as novel efficient visible light driven photocatalysts. J. Mater. Chem. 21(39), 15171–15174 (2011). doi:10.1039/c1jm12844b
Y.X. Tang, Z.J. Gui, C. Xing, A. Li, P.D. Kanhere et al., Efficient Ag@AgCl cubic cage photocatalysts profit from ultrafast plasmon-induced electron transfer processes. Adv. Fun. Mater. 23(23), 2932–2940 (2013). doi:10.1002/adfm.201203379
J.G. Hou, Z. Wang, C. Yang, W.L. Zhou, S.Q. Jiao, H.M. Zhu, Hierarchically plasmonic Z-Scheme photocatalyst of Ag/AgCl nanocrystals decorated mesoporous single-crystalline metastable Bi20TiO32 nanosheets. J. Phys. Chem. C 117(10), 5132–5141 (2013). doi:10.1021/jp311996r
Z.Y. Wang, W. Guan, Y.J. Sun, F. Dong, Y. Zhou, W.K. Ho, Water-assisted production of honeycomb-like g-C3N4 with ultralong carrier lifetime and outstanding photocatalytic activity. Nanoscale 7, 2471–2479 (2015). doi:10.1039/C4NR05732E
Acknowledgments
The authors are grateful to the financial aid from the National Natural Science Foundation of China (NSFC No. 51472133).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Bao, Y., Chen, K. AgCl/Ag/g-C3N4 Hybrid Composites: Preparation, Visible Light-Driven Photocatalytic Activity and Mechanism. Nano-Micro Lett. 8, 182–192 (2016). https://doi.org/10.1007/s40820-015-0076-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40820-015-0076-y