Abstract
Non-spherical Cu@CuS yolk–shell structures are successfully obtained using Cu2O cube templates in a process combining rapid surface sulfidation followed by disproportionation of the Cu2O core upon treatment with a hydrochloric acid solution. By employing the above method, Cu@CuS yolk–shell structures with different morphologies, including octahedral, truncated octahedral, and cuboctahedral shapes, can be synthesized. The void space within the hollow structures provides a unique confined space, where the metallic copper present in the core of a shell can be protected from agglomeration and oxidation. Furthermore, the presence of metal copper in these hollow structures contributes to improvement in the photocatalytic properties of these materials. The application of these Cu@CuS structures indeed shows clearly improved photocatalytic performance.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Highlights
-
Non-spherical Cu@CuS yolk–shell structures with different morphologies, including octahedral, truncated octahedral, and cuboctahedral shapes, are successfully obtained using a strategy combining shell sulfidation and core disproportionation reaction.
-
The as-prepared Cu@CuS structures exhibited clearly remarkable photocatalytic performance.
2 Introduction
Photocatalytic technology can be used to convert solar energy into chemical energy and constitutes a promising approach to combat both environmental pollution and the global energy shortage [1–4]. Metal sulfides have been drawing attention as new photocatalytic materials owing to their narrow band gap, good light adsorption properties, and excellent photocatalytic performance [5, 6]. In particular, copper sulfides (Cu x S with x = 1–2) are transition metal chalcogenides that have been found to be potentially useful materials for application in photocatalysis due to their low cost, high stability, and low cytotoxicity [7]. Recently, many varieties of copper sulfides micro-/nanostructures have been synthesized to improve their photocatalytic efficiency, including nanotubes [8], nanowires [9], nanorods [10], nanoplates [11], ball-flower [12], and hollow cages [13]. However, the photocatalytic activity of pure copper sulfides under visible light irradiation is not high enough for practical applications due to drawbacks associated with their narrow band gap, which results in the easy recombination of the photogenerated charges.
To address this issue, various methods have been developed, such as a controllable synthesis by doping with different ions [14, 15], sensitization by absorbed molecules or quantum dots [16, 17], and coupling with different band-gap semiconductors [18]. Among these, the modification of a photocatalyst with noble metals such as Pt, Au, and Ag is a meaningful and efficient strategy, since these metals can act as electron sinks to effectively transfer the photogenerated electrons, thus improving the corresponding photocatalytic performance [19–21]. Compared to noble metals, copper is particularly interesting due to its high conductivity combined with a much lower cost. However, deposition of copper on a photocatalyst surface is not always useful in photocatalysis since copper particles have a strong tendency to agglomerate and can be easily oxidized during the preparation and utilization processes [22].
Compared to other dense structures of the same size, yolk–shell nanostructures with a void space between the interior core and the mesoporous outer shell have attracted a great deal of attention due to their special structure and properties, such as low density, large surface area, and high loading capacity [23–28]. The void space within the yolk–shell structures provides a unique confined space, where a metal present as the yolk in the core of a shell can be protected from agglomeration and oxidation [29]. In general, various yolk–shell nanoparticles (NPs) have been synthesized by selectively scarifying the core/shell layer or converting the core materials via a disproportionation reaction [30], galvanic reaction [31, 32], or the Kirkendall effect [33]. However, most of the studies on the preparation of yolk–shell NPs focus on a noble metal, such as Au, Ag, and Pt, as the core and a metal oxide as the shell. Investigations on nanostructures using copper as the core and metal sulfides as the shell have been relatively limited. Therefore, it is still desirable to develop new efficient strategies to fabricate Cu@metal sulfides with high-performance photocatalytic activity.
Herein, we developed a strategy combining a shell sulfidation and core disproportionation reaction to synthesize uniform, non-spherical Cu@CuS yolk–shell structures. When evaluated as photocatalytic materials, the Cu@CuS structures showed a clear improvement in their photocatalytic performance.
3 Experimental
3.1 Chemicals
Copper(II) sulfate pentahydrate (CuSO4·5H2O), cupric acetate monohydrate [Cu(CH3COO)2·H2O], trisodium citrate dihydrate (Na3C6H5O7·2H2O), sodium hydroxide (NaOH), ascorbic acid (C6H8O6), sodium sulfide (Na2S·9H2O), hydrochloric acid (HCl), ammonia (NH3·H2O), and d-glucose (C6H12O6) were all purchased from Sinopharm Chemical Reagent Co., Ltd.
3.2 Synthesis of the Materials
3.2.1 Synthesis of Cu2O Solid Cubes
In a typical synthesis, CuSO4·5H2O (0.375 g, 1.5 mmol) was dissolved in 100 mL of distilled water under vigorous stirring treatment to form solution 1. Subsequently, Na3C6H5O7·2H2O (0.15 g, 0.51 mmol) and NaOH (1 g, 25 mmol) were added to the above solution 1. Ascorbic acid (0.264 g 1.5 mmol) was dissolved in 50 mL of distilled water under ultrasonic treatment to form solution 2. Solution 2 was mixed with solution 1 at room temperature (25 °C), and the resulting mixture was stirred for 40 min at room temperature. A red product was obtained by centrifugation and washed with deionized water and ethanol. The product was dried in oven at 60 °C.
3.2.2 Preparation of Cu2O Solid Octahedrons
In a typical experiment, Cu(CH3COO)2·H2O (3 g, 15 mmol) was dissolved in deionized water (20 mL) under a constant stirring at 70 °C for 2 min. When a sodium hydroxide solution (10 mL, 9 M) was added to the above solution, a dark precipitate was produced. After stirring for 5 min, d-glucose powder (0.6 g) was then added with constant stirring at 70 °C for 60 min. A red product was obtained by centrifugation, washed with deionized water and ethanol, and then dried in oven at 60 °C. The preparation of Cu2O solid truncated octahedrons is similar to that of Cu2O solid octahedrons, except for the concentration and volume of the Cu(CH3COO)2·H2O (50 mL, 0.3 M) and sodium hydroxide (30 mL, 3 M) solutions. Cuboctahedral particles were also produced by a similar method, but the reaction time was reduced from 60 to 20 min.
3.2.3 Preparation of Cu2O@CuS Yolk–Shell Structures
In a typical synthesis, the Cu2O solid sample (70 mg) was added into distilled water to form solution 3, and then a sodium sulfide solution (1 mL, 0.6 M) was added to the above solution, and stirred for 5 min at room temperature. The black products were collected by centrifugation, washed with distilled water, and then dried at 60 °C for further characterization.
3.2.4 Preparation of Cu@CuS Yolk–Shell Structures
The above-synthesized black products (70 mg) were dissolved in 10 mL of distilled water under ultrasonic treatment to form solution 4. Hydrochloric acid (1 mL) was then added to solution 4 at 80 °C. After stirring for 2 h, the products were collected by centrifugation, washed, and dried at 60 °C for further characterization.
3.2.5 Preparation of CuS Hollow Structures
CuS particles were also prepared by a similar method together with Cu@CuS box structures, and ammonia was added to the black solution 4 instead of hydrochloric acid.
3.3 Characterization
The composition and phase of the as-prepared products were acquired by powder X-ray diffraction (XRD) using a Panalytical X-pert diffractometer with CuKα radiation. The morphology and crystal structure of the as-prepared products were observed by scanning electron microscopy (SEM, SU8010) and high-resolution transmission electron microscopy (HRTEM, JEM-2100) with an acceleration voltage of 200 kV. All TEM samples were prepared by depositing a drop of the diluted suspensions in ethanol on a carbon-film-coated copper grid.
3.4 Photocatalysis
The photodegradation efficiency of methylene blue (MB) in aqueous solution was measured under sunlight irradiation (300 W xenon lamp). All experiments were carried out at the temperature of 25 ± 2 °C. Typically, 15 mg of Cu@CuS yolk–shell sample was dispersed in 50 mL of MB aqueous solution (0.02 M) under ultrasonic irradiation to form a suspension, which was magnetically stirred for 30 min in the dark. At regular irradiation time intervals, the dispersion was sampled and centrifuged to separate the residue. The photodegradation efficiency was monitored by measuring the absorbance of the centrifuged solutions at the maximum absorption wavelength of 664 nm using UV–Vis spectroscopy (SHIMADZU, UV-2100) at room temperature.
4 Results and Discussion
Our strategy for the formation of Cu@CuS yolk–shell structures is shown in Fig. 1a. In the first step, the Cu2O cubes used as precursors were prepared by a facile solvothermal method. The XRD pattern (Fig. S1) of the obtained products corresponds to the cubic Cu2O phase (JCPDS card no. 00-034-1354, α = 0.4217 nm), indicating that Cu2O was successfully synthesized. As shown in Fig. 1b, the synthesized uniform Cu2O cubes exhibit a smooth surface and have a mean size of about 1 μm. The Cu2O cubes can be easily converted into Cu2O@CuS yolk–shell structures by a simple surface sulfidation process using Na2S as sulfur source. XRD analysis was used to elucidate the composition and crystal phase of the as-prepared products. As shown in Fig. 2a, most of the diffraction peaks can be ascribed to hexagonal CuS (JCPDS card no. 01-078-0876), while a part of the peaks (marked with a star) corresponds to the primitive cubic Cu2O (JCPDS card no. 00-034-1354). Therefore, the as-prepared products are composite of CuS and Cu2O phases, and the reaction equation can be described as: 2Cu2O + 4S2− + O2 + 4H2O → 4CuS + 8OH− [34]. The morphologies of the products were analyzed by FESEM and TEM. As shown in Fig. 1c, the morphologies of the products still retain uniform cubes after the sulfidation process. The TEM images (inset of Fig. 1c) confirm the formation of yolk–shell structures by the obvious contrast between the cavity and the shell, which has a thickness of approximately 50 nm. The formation process of the yolk–shell structures can be divided into a sulfidation step and the Kirkendall effect. Firstly, the sulfide ions released from Na2S in the aqueous solution react with the metal ions on the surface of the Cu2O cubes to form a thin layer of Cu sulfides, and then the outward diffused metal ions become dominant compared to the inward diffusion of S2− based on the Kirkendall effect, leading to the formation of a well-defined gap between the shell and the Cu2O core. Cuprous compounds can go through a disproportionation reaction to form Cu metal and Cu2+ ions under acidic conditions. Therefore, the cubic Cu2O core encapsulated in this system can be used to synthesize spatially confined Cu particles by a disproportionation reaction. When the Cu2O@CuS particles were added to a hydrochloric acid solution, the color of the solution turned blue-green (Fig. S2), indicating that the Cu2+ ions generated from the disproportionation reaction can diffuse to the solution through the CuS shell. The SEM and TEM images (Fig. 1d) reveal that the Cu2O core disappeared and the corresponding hollow cubes could be generated after acidic treatment, suggesting the conversion of Cu2O cubes to Cu crystals. However, no diffraction peaks corresponding to Cu were found in the XRD pattern (Fig. 2b), most likely due to its low content and poor crystalline. Actually, the Cu2O core of the Cu2O@CuS particles could be completely dissolved by ammonia complexation reaction to form [Cu(NH3)4]+ and hollow CuS boxes. The composition and morphology of the products were examined by XRD (Fig. 2c), SEM, and TEM analyses (Fig. S3).
In order to further confirm the composition and structural information of the Cu@CuS structures, the products were characterized by HRTEM and selected-area electron diffraction (SAED). In agreement with the FESEM findings, a high uniformity of the hollow cubes can be seen in the TEM images (Fig. 3a). Moreover, the inner cavities are clearly revealed by the sharp contrast between shells and hollow interiors. The TEM images at higher magnifications depict the inner cavities of the hollow cubes (Fig. 3b). Interestingly, it appears that some small particles with a size of several nanometers are present in the cavities (Fig. 3c). The SAED pattern corresponding to the square shell is displayed in Fig. 3e, and it shows that the square shell has a single crystalline characteristic, and it can be indexed to a primitive hexagonal phase of CuS viewed along the \([000\overline{1} ]\) zone axis. Moreover, some additional spots correspond well to the (200) reflections of the face-centered cubic Cu. The detailed microstructure of the square shell was further investigated by HRTEM. As shown in Fig. 3d, the corresponding lattice spacing is 0.27 nm, which is in good agreement with the d value of the \((60\overline{6} 0)\) facets of the hexagonal phase of CuS. The electron diffraction and HRTEM results further confirm that the as-prepared products are comprised of CuS and Cu.
This shell sulfidation and core disproportionation strategy can also be used to synthesize Cu@CuS yolk–shell structures with different morphologies (octahedral, truncated octahedral, and cuboctahedral). Figure 4 shows the SEM images of the different morphologies of Cu2O before and after the sulfidation and disproportionation processes. Firstly, different shapes of the Cu2O particles with a smooth surface were synthesized by changing the reaction conditions (Fig. 4a1–c1). After the sulfidation treatment, the surface of the particles became rough (Fig. 4a2–c2). Selecting the octahedral shape as example XRD analysis (Fig. S4) was carried out to determine the structure and composition of the obtained samples. The diffraction peaks can be ascribed to hexagonal CuS and cubic Cu2O, indicating that the as-prepared products are composites of CuS and Cu2O phases. According to the above strategy, Cu2O can be used to synthesize spatially confined Cu particles by a disproportionation reaction. From the SEM images (Fig. 4a3–c3), the products still retain the original morphologies and the interior cavity is formed after the disproportionation reaction. The TEM images (Fig. 5a–c) of Cu2O octahedrons depict the inner cavities, and some small Cu particles appear in the cavities. The color of the solution turned blue-green (Fig. S5), which indicates that the Cu2O in the core has disappeared. Therefore, Cu@CuS yolk–shell structures with different morphologies can be synthesized utilizing this disproportionation method (Fig. 4b, c).
The photocatalytic activity of the Cu@CuS cubes was evaluated by MB degradation under sunlight irradiation. As shown in Fig. 6a, when the Cu@CuS cubes were used as photocatalyst, the degradation could be finished within 200 min, and the photographs indicate that the solution became colorless after 200 min (inset Fig. 6a). The normalized temporal concentration changes (C t/C 0) of MB during the photocatalytic process are proportional to the normalized maximum absorbance (A t/A 0), which can be derived from the change in the MB absorption profile at a given time interval. Figure 4b clearly shows that the photocatalytic activity of the Cu@CuS cubes is higher than that of the CuS cubes. A linear relation of ln(C t/C 0) versus reaction time is observed, implying that the photocatalytic reaction can be considered as a pseudo-first-order reaction (Fig. 4c). The cubic Cu@CuS yolk–shell catalysts showed the fastest reaction rate, and the apparent kinetic rate constant was estimated to be 1.18 × 10−2 min−1, which is higher than that of the CuS cubes (3.65 × 10−3 min−1). In order to evaluate the catalytic stability, we carried out the cycle performance of double-shell structure Cu@CuS cubic catalysts for the degradation of MB under solar light irradiation (Fig. 4d). The results reveal that the Cu@CuS cubic structures possess an outstanding catalytic stability, which remains above 90% in the photodegradation of MB after five cycle tests.
The enhanced photocatalytic activity of Cu@CuS cubes might be mainly ascribed to a reduced electron–hole pair recombination owing to the Cu/CuS hybrid nanostructures, as confirmed by EIS measurements (Fig. 7). The low charge-transfer resistance (R ct) indicates that the coupled system of semiconductors decreases the layer resistance in the solid-state interface and the charge-transfer resistance on the surface. Therefore, the above results indicate that the present copper can act as an electron sink to effectively transfer the photogenerated electrons of the photocatalyst (Cu2S), which may slow down the recombination of photogenerated electrons and holes to provide a high photocatalytic activity [35, 36].
5 Conclusions
In summary, we have developed a new and efficient shell sulfidation and core disproportionation strategy for the synthesis of non-spherical Cu@CuS yolk–shell structures. This method can be used to fabricate Cu@CuS yolk–shell structures with different morphologies (cubic, octahedral, and cuboctahedral). The void space in the hollow structures provides a unique confined space, where a metal copper present in the core of a shell can be protected from agglomeration and oxidation. Furthermore, due to the presence of metal copper and hollow structures, the Cu@CuS yolk–shell structures manifest excellent photocatalytic activity and stability under sunlight irradiation.
References
A. Fujishima, K. Honda, Three-dimensional structure of thermolysin. Nature 238, 37–41 (1972). doi:10.1038/newbio238037a0
X.B. Chen, S.H. Shen, L.J. Guo, S.S. Mao, Semiconductor-based photocatalytic hydrogen generation. Chem. Rev. 110, 6503–6570 (2010). doi:10.1021/cr1001645
Z.G. Yi, J.H. Ye, N. Kikugawa, T. Kako, S.X. Ouyang et al., An orthophosphate semiconductor with photooxidation properties under visible-light irradiation. Nat. Mater. 9, 559–564 (2010). doi:10.1038/nmat2780
P. Zhang, L. Wang, X. Zhang, C. Shao, J. Hu, G. Shao, Three-dimensional porous networks of ultra-long electrospun SnO2 nanotubes with high photocatalytic performance. Nano-Micro Lett. 7(1), 86–95 (2015). doi:10.1007/s40820-014-0022-4
J.S. Hu, L.L. Ren, Y.G. Guo, H.P. Liang, A.M. Cao, L.J. Wan, C.L. Bai, Mass production and high photocatalytic activity of ZnS nanoporous nanoparticles. Angew. Chem. Int. Ed. 117, 1295–1299 (2005). doi:10.1002/ange.200462057
H.F. Cheng, B.B. Huang, X.Y. Qin, X.Y. Zhang, Y. Dai, A controlled anion exchange strategy to synthesize Bi2S3 nanocrystals/BiOCl hybrid architectures with efficient visible light photoactivity. Chem. Commun. 48, 97–99 (2012). doi:10.1039/C1CC15487G
Q.W. Tian, J.Q. Hu, Y.H. Zhu, R.J. Zou, Z.G. Chen et al., Sub-10 nm Fe3O4@Cu2−x S core–shell nanoparticles for dual-modal imaging and photothermal therapy. J. Am. Chem. Soc. 135(23), 8571–8577 (2013). doi:10.1021/ja4013497
J.F. Mao, Q. Shu, Y.Q. Wen, H.Y. Yuan, D. Xiao, M.F. Choi, Facile fabrication of porous cus nanotubes using well-aligned [Cu(tu)]Cl·1/2H2O nanowire precursors as self-sacrificial templates. Cryst. Growth Des. 9(6), 2546–2548 (2009). doi:10.1021/cg8006052
F. Pan, S.M. Niu, Y. Ding, L. Dong, R.M. Yu, Y. Liu, G. Zhu, Z.L. Wang, Enhanced Cu2S/CdS coaxial nanowire solar cells by piezo-phototronic effect. Nano Lett. 12(6), 3302–3307 (2012). doi:10.1021/nl3014082
Z.J. Sun, X. Liu, Q.D. Yue, H.X. Jia, P.W. Du, Cadmium sulfide nanorods decorated with copper sulfide via one-step cation exchange approach for enhanced photocatalytic hydrogen evolution under visible light. Chemcatchem 8, 157–162 (2016). doi:10.1002/cctc.201500789
H.B. Wu, W. Chen, Synthesis and reaction temperature-tailored self-assembly of copper sulfide nanoplates. Nanoscale 3, 5096–5102 (2011). doi:10.1039/c1nr10829h
Z.G. Chen, S.Z. Wang, Q. Wang, B.Y. Geng, A facile solution chemical route to self-assembly of CuS ball-flowers and their application as an efficient photocatalyst. CrystEngComm 12, 144–149 (2010). doi:10.1039/B914902C
H. Kuo, Y.T. Chu, Y.F. Song, M.H. Huang, Cu2O nanocrystal-templated growth of Cu2S nanocages with encapsulated au nanoparticles and in situ transmission X-ray microscopy study. Adv. Funct. Mater. 21, 792–797 (2011). doi:10.1002/adfm.201002108
J. Reszczynska, T. Grzyb, J.W. Sobczak, W. Lisowski, M. Gazda, B. Ohtani, A. Zaleska, Visible light activity of rare earth metal doped (Er3+, Yb3+ or Er3+/Yb3+) titania photocatalysts. Appl. Catal. B-Environ. 163, 40–49 (2015). doi:10.1016/j.apcatb.2014.07.010
J.Z. Bloh, R. Dillert, D.W. Bahnemann, Designing optimal metal-doped photocatalysts: correlation between photocatalytic activity, doping ratio, and particle size. J. Phys. Chem. C 116(48), 25558–25562 (2012). doi:10.1021/jp307313z
J.Y. Qin, J.P. Huo, P.Y. Zhang, J. Zeng, T.T. Wang, H.P. Zeng, Improving the photocatalytic hydrogen production of Ag/g-C3N4 nanocomposites by dye-sensitization under visible light irradiation. Nanoscale 8, 2249–2259 (2016). doi:10.1039/C5NR06346A
K. Kim, M.J. Kim, S. Kim, J.H. Jang, Towards visible light hydrogen generation: quantum dot-sensitization via efficient light harvesting of hybrid-TiO2. Sci. Rep. 3, 3330 (2013). doi:10.1038/srep03330
S.S. Chen, Y. Qi, T. Hisatomi, Q. Ding, T. Asai et al., Efficient visible-light-driven z-scheme overall water splitting using a MgTa2O6–xNy/TaON heterostructure photocatalyst for H2 evolution. Angew. Chem. Int. Ed. 127, 8618–8621 (2015). doi:10.1002/ange.201502686
J. Jiang, H. Li, L.Z. Zhang, New insight into daylight photocatalysis of AgBr@Ag: synergistic effect between semiconductor photocatalysis and plasmonic photocatalysis. Chem. Eur. J. 18, 6360–6369 (2012). doi:10.1002/chem.201102606
W. Ding, K. Liu, S.N. He, C.B. Gao, Y.D. Yin, Ligand-exchange assisted formation of Au/TiO2 schottky contact for visible-light photocatalysis. Nano Lett. 14(11), 6731–6736 (2014). doi:10.1021/nl503585m
S.N. Xiao, P.J. Liu, W. Zhu, G.S. Li, D.Q. Zhang, H.X. Li, Copper nanowires: a substitute for noble metals to enhance photocatalytic H2 generation. Nano Lett. 15(8), 4853–4858 (2015). doi:10.1021/acs.nanolett.5b00082
Y. Li, W.N. Wang, Z.L. Zhan, M.H. Woo, C.Y. Wu, P. Biswas, Photocatalytic reduction of CO2 with H2O on mesoporous silica supported Cu/TiO2 catalysts. Appl. Catal. B-Environ. 100, 386–392 (2010). doi:10.1016/j.apcatb.2010.08.015
X. Lai, J.E. Halpert, D. Wang, Recent advances in micro-/nano-structured hollow spheres for energy applications: from simple to complex systems. Energy Environ. Sci. 5, 5604–5618 (2012). doi:10.1039/C1EE02426D
N. Liu, H. Wu, M.T. McDowell, Y. Yao, C.M. Wang, Y. Cui, A yolk–shell design for stabilized and scalable li-ion battery alloy anodes. Nano Lett. 12(6), 3315–3321 (2012). doi:10.1021/nl3014814
H. Hu, B.Y. Guan, B.Y. Xia, X.W. Lou, Sub-10 nm Fe3O4@Cu2−x S core–shell nanoparticles for dual-modal imaging and photothermal therapy. J. Am. Chem. Soc. 135(23), 8571–8577 (2013). doi:10.1021/ja4013497
L.L. Wang, H.M. Dou, Z. Lou, T. Zhang, Encapsuled nanoreactors (Au@SnO2): a new sensing material for chemical sensors. Nanoscale 5, 2686–2691 (2013). doi:10.1039/c2nr33088a
L.L. Wang, Z. Lou, J.N. Deng, R. Zhang, T. Zhang, Ethanol gas detection using a yolk–shell (core–shell) α-Fe2O3 nanospheres as sensing material. ACS Appl. Mater. Interfaces 7, 13098–13104 (2015). doi:10.1021/acsami.5b03978
L.L. Wang, W.B. Ng, J.A. Jackman, N.J. Cho, Graphene-functionalized natural microcapsules: modular building blocks for ultrahigh sensitivity bioelectronic platforms. Adv. Funct. Mater. 26, 2097–2103 (2016). doi:10.1002/adfm.201504940
Y.R. Wang, W.L. Yang, L. Zhang, Y. Hu, X.W. Lou, Formation of MS–Ag and MS (M = Pb, Cd, Zn) nanotubes via microwave-assisted cation exchange and their enhanced photocatalytic activities. Nanoscale 5, 10864–10867 (2013). doi:10.1039/c3nr03909a
S.H. Ye, X.J. He, L.X. Ding, Z.W. Pan, Y.X. Tong, M.M. Wu, G.R. Li, Cu2O template synthesis of high-performance PtCu alloy yolk–shell cube catalysts for direct methanol fuel cells. Chem. Commun. 50, 12337–12340 (2014). doi:10.1039/C4CC04108A
L. Kuai, B.Y. Geng, S.Z. Wang, Y. Sang, A general and high-yield galvanic displacement approach to AuM (M = Au, Pd, and Pt) core–shell nanostructures with porous shells and enhanced electrocatalytic performances. Chem. Eur. J. 18, 9423–9429 (2012). doi:10.1002/chem.201200893
Y. Lu, Y. Zhao, L. Yu, L. Dong, C. Shi, M.J. Hu, Y.J. Xu, L.P. Wen, S.H. Yu, Hydrophilic Co@Au yolk/shell nanospheres: synthesis, assembly, and application to gene delivery. Adv. Mater. 22, 1407–1411 (2010). doi:10.1002/adma.200903298
Z.H. Wei, Z.J. Zhou, M. Yang, C.H. Lin, Z.H. Zhao, D.T. Huang, Z. Chen, J.H. Cao, Multifunctional Ag@Fe2O3 yolk–shell nanoparticles for simultaneous capture, kill, and removal of pathogen. J. Mater. Chem. 21, 16344–16348 (2011). doi:10.1039/c1jm13691g
S.D. Sun, X.P. Song, C.C. Kong, S.H. Liang, B.J. Ding, Z.M. Yang, Unique polyhedral 26-facet CuS hollow architectures decorated with nanotwinned, mesostructural and single crystalline shells. CrystEngComm 13, 6200–6205 (2011). doi:10.1039/c1ce05563a
Q.P. Luo, X.Y. Yu, B.X. Lei, H.Y. Chen, D.B. Kuang, C.Y. Su, Reduced graphene oxide-hierarchical zno hollow sphere composites with enhanced photocurrent and photocatalytic activity. J. Phys. Chem. C 116(14), 8111–8117 (2012). doi:10.1021/jp2113329
X.W. Zou, H.Q. Fan, Y.M. Tian, M.G. Zhang, X.Y. Yan, Microwave-assisted hydrothermal synthesis of Cu/Cu2O hollow spheres with enhanced photocatalytic and gas sensing activities at room temperature. Dalton Trans. 44, 7811–7821 (2015). doi:10.1039/C4DT03417A
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Grant Nos. 21671085, 21473081, 21201088), the Natural Science Foundation of Jiangsu Province (BK20161160), the Qing Lan Project and the Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions.
Author information
Authors and Affiliations
Corresponding author
Additional information
Qiuyan Li and Fan Wang have contributed equally to this work.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Li, Q., Wang, F., Sun, L. et al. Design and Synthesis of Cu@CuS Yolk–Shell Structures with Enhanced Photocatalytic Activity. Nano-Micro Lett. 9, 35 (2017). https://doi.org/10.1007/s40820-017-0135-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-017-0135-7