Highlights
-
This work starts the research of pseudocapacitive oxide materials for multivalent Zn2+ storage.
-
The constructed RuO2·H2O||Zn systems exhibit outstanding electrochemical performance, including a high discharge capacity, ultrafast charge/discharge capability, and excellent cycling stability.
-
The redox pseudocapacitive behavior of RuO2·H2O for Zn2+ storage is revealed.
Abstract
Rechargeable aqueous zinc-ion hybrid capacitors and zinc-ion batteries are promising safe energy storage systems. In this study, amorphous RuO2·H2O for the first time was employed to achieve fast and ultralong-life Zn2+ storage based on a pseudocapacitive storage mechanism. In the RuO2·H2O||Zn zinc-ion hybrid capacitors with Zn(CF3SO3)2 aqueous electrolyte, the RuO2·H2O cathode can reversibly store Zn2+ in a voltage window of 0.4–1.6 V (vs. Zn/Zn2+), delivering a high discharge capacity of 122 mAh g−1. In particular, the zinc-ion hybrid capacitors can be rapidly charged/discharged within 36 s with a very high power density of 16.74 kW kg−1 and a high energy density of 82 Wh kg−1. Besides, the zinc-ion hybrid capacitors demonstrate an ultralong cycle life (over 10,000 charge/discharge cycles). The kinetic analysis elucidates that the ultrafast Zn2+ storage in the RuO2·H2O cathode originates from redox pseudocapacitive reactions. This work could greatly facilitate the development of high-power and safe electrochemical energy storage.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Novel energy storage systems with the merits of high safety, fast charge–discharge capability, and high energy density are highly demanded with the rapid development of electric vehicles and customer electronics. Recently, multivalent-ion (e.g., Zn2+, Ca2+, Mg2+, and Al3+) storage systems have emerged and exhibited unique electrochemical behaviors [1,2,3,4,5,6]. During various multivalent-ion storage systems, zinc metal anode-based aqueous rechargeable zinc-ion batteries (ZIBs) and zinc-ion hybrid capacitors (ZICs) are particularly attractive [1, 7,8,9,10,11], due to their high safety, low cost, abundant natural resource of zinc, and unique electrochemical features of zinc metal anodes such as low redox potential of − 0.76 V (vs. standard hydrogen electrode) and ultrahigh volumetric capacity of 5845 Ah L−1. Furthermore, the high ionic conductivity of aqueous electrolytes such as ZnSO4 solutions in ZIBs and ZICs is beneficial for achieving high power output. The electrochemical properties of ZIBs and ZICs are strongly dependent on the Zn2+-storage behaviors in cathode materials.
Several cathode materials have been developed for ZIBs and ZICs, including manganese oxides, vanadium oxides, Prussian blue analogs, conductive polymers, and carbon materials. Zn2+ insertion/extraction in manganese oxides, especially tunnel-structured MnO2, creates high specific capacities. However, the poor electrical conductivity of manganese oxides and manganese dissolution issues cause unsatisfactory rate performance and poor cycling stability [12,13,14,15]. Vanadium oxides possess high capacities and fast kinetics for Zn2+ storage [16,17,18,19,20,21,22], whereas their high toxicity impedes their practical applications. Besides, most of the Prussian blue analogs show low capacities of about 50 mAh g−1 when used as cathode materials for ZIBs [23,24,25,26]. Although conductive polymers (e.g., polyaniline and polypyrrole) and carbon materials (e.g., activated carbon, denoted as “AC”) generally have a Zn2+-storage capacity of 100–150 mAh g−1 and better rate performance compared to manganese oxides [11, 27,28,29,30], their low density of about 0.3–1 mg cm−2 is unfavorable for the volumetric energy density of corresponding batteries. Therefore, seeking high-performance Zn2+-storage materials is still a big challenge.
Herein, for the first time, we demonstrate that fast, ultralong-life, and safe Zn2+ storage can be realized in amorphous RuO2·H2O cathode materials based on a pseudocapacitive storage mechanism. The constructed RuO2·H2O||Zn ZICs can reversibly store Zn2+ in a voltage window of 0.4–1.6 V (vs. Zn/Zn2+), delivering a capacity of about 122 mAh g−1, an excellent rate capability and an ultralong cycle life exceeding 10,000 cycles.
2 Experimental
2.1 Electrochemical Measurements
Amorphous ruthenium oxide hydrate (RuO2·xH2O) powder was obtained from Sigma-Aldrich Corporation. To synthesize anhydrous RuO2, the RuO2·xH2O powder was heat-treated in air at 300 °C for 1 h with a heating rate of 5 °C min−1. The amorphous RuO2·xH2O power (or anhydrous RuO2 powder) was mixed with conductive black and polyvinylidene fluoride binder in N-methyl-pyrrolidone solutions, then coated on a stainless steel foil, and finally dried at 100 °C in vacuum to obtain RuO2·xH2O (or RuO2) electrodes. Mass loading of active materials in the prepared cathodes was 2.5–3.0 mg cm−2. Electrochemical performance of these ruthenium oxides for Zn2+ storage was evaluated by assembling CR2032 coin cells, in which RuO2·xH2O (or RuO2) electrode was used as the cathode, commercial Zn foil was used as the anode, air-laid paper was used as separator, and 2 M Zn(CF3SO3)2 or 2 M ZnSO4 aqueous solution served as the electrolyte. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) tests were performed on a Bio-Logic VMP3 electrochemical station. An AC amplitude of 5 mV and a frequency range of 0.1–100 kHz were applied for the EIS test at open-circuit voltage (OCV). For galvanostatic charge–discharge (GCD) measurements, when the applied current was 0.1–3 A g−1, they were performed on a LAND battery testing instrument, and when the current was 5–20 A g−1, the GCD measurements were completed on the Bio-Logic VMP3 electrochemical station. (This is because for fast charge/discharge tests, Bio-Logic VMP3 electrochemical station is more sensitive and accurate.)
2.2 Material and Electrode Characterizations
We used scanning electron microscopy (SEM; model: Zeiss Supra 55VP) and transmission electron microscopy (TEM; model: Tecnai G2 F30) to observe the micromorphologies of samples and used a Brunauer–Emmett–Teller (BET) analyzer to characterize the specific surface area. X-ray diffraction (XRD; model: Bruker D8 Discover Diffractometer) and X-ray photoelectron spectroscopy (XPS; model: MDTC-EQ-M20-01) were applied to analyze the phase and compositions. Thermogravimetric (TG)-differential scanning calorimeter was utilized to determine the water content in amorphous RuO2·xH2O powder. Note that to characterize the electrodes at various charge/discharge states, corresponding cells were charged/discharged, then disassembled, and washed using deionized water five times to remove surface-adsorbed electrolyte.
3 Results and Discussion
Figure 1 shows the physicochemical characteristics of the RuO2·xH2O sample. The RuO2·xH2O is irregular-shaped particles with a size of about 100–500 nm (Fig. 1a). Its selected-area electron diffraction (SAED) image (inset in Fig. 1b) exhibits a characteristic halo ring pattern, revealing the amorphous feature of the RuO2·xH2O. Correspondingly, the high-resolution TEM image does not show clear lattice fringes (Fig. S1). The amorphous feature of the RuO2·xH2O is also confirmed by the XRD result (Fig. 1c), from which only several broad diffraction peaks are observed. To determine the structural water content in the RuO2·xH2O, TG analysis was performed, as shown in Fig. 1d. Mass loss in the temperature range of 100–300 °C originates from the structural water of the RuO2·xH2O [31], which is ~ 12.4 wt%. This means that x in the RuO2·xH2O is 1.0. Therefore, the RuO2·xH2O is denoted as RuO2·H2O. In the XPS spectrum of Ru 3d (Fig. 1e), the Ru 3d3/2 peak at 285.3 eV and Ru 3d5/2 peak at 281.1 eV are observed, corresponding well to the previously reported hydrous RuO2 [32, 33]. Ru 3p XPS spectrum shown in Fig. S2 provides consistent evidence. O 1 s XPS spectrum shown in Fig. 1f is split into three peaks, proving the coexistence of Ru–O–Ru and Ru–O–H bonds in the amorphous RuO2·H2O [32, 33].
The electrochemical performance of the RuO2·H2O for Zn2+ storage was evaluated by assembling the cells with RuO2·H2O cathode, Zn metal anode, and Zn(CF3SO3)2 aqueous electrolyte. The RuO2·H2O||Zn system shows an open-circuit voltage of 1.05 V and can be reversibly charged/discharged in a voltage window of 0.4–1.6 V (Fig. 2a). In such a voltage window, the Zn(CF3SO3)2 and ZnSO4 aqueous electrolytes are stable and water decomposition does not occur (Fig. S3). In the CV curves, there is one pair of broad redox peaks. Even at high scan rates such as 100 mV s−1, the redox peaks remain, suggesting good rate performance of the RuO2·H2O||Zn system. As shown in the GCD profiles (Fig. 2b), the charge curves and discharge curves deviate from linear shapes without flat voltage plateaus. This is consistent with the broad redox peaks observed in the CV curves. At a charge/discharge current of 0.1 A g1, the RuO2·H2O cathode shows a discharge capacity of 122 mAh g−1 with a coulombic efficiency of 86%. When the current increases for 200 times (to 20 A g−1), in which the RuO2·H2O||Zn system is charged/discharged within 36 s, the discharge capacity still reaches 98 mAh g−1. In fact, considering that the coulombic efficiency of the RuO2·H2O||Zn system at low current densities of 0.1–1 A g−1 and high current densities of 3–20 A g−1 is 86–98% and 99–100%, respectively, the RuO2·H2O||Zn system is more suitable for fast charging/discharging. For comparison, rate performance of some typical cathode materials for Zn2+ storage is summarized in Fig. 2c, including MnO2 [15], Zn0.25V2O5·nH2O [16], VS2 [34], polyaniline [28], and AC [11]. Figure 2c intuitively shows the excellent rate capability of the RuO2·H2O cathode, compared with the other cathode materials. It should be noted that the RuO2·H2O exhibits similar superior performance in 2 M ZnSO4 aqueous electrolyte (Fig. S4). Furthermore, according to the Ragone plot shown in Fig. 2d, the RuO2·H2O cathode can provide a maximum energy density of 119 Wh kg−1. More importantly, it keeps a high energy density of 82 Wh kg−1 under the condition of delivering an ultrahigh power output of 16.74 kW kg−1. Such a high power output with considerable energy density is almost impossible for most of the current electrochemical energy storage systems [9, 16, 35]. For instance, the maximum power density of currently reported lithium-ion batteries and aqueous ZIBs is generally smaller than 1–10 kW kg−1.
The kinetic analysis was performed to reveal the mechanisms for the superior electrochemical performance of the RuO2·H2O cathode. Zn2+ storage in the RuO2·H2O cathode was firstly confirmed by the high-resolution Zn 2p XPS spectra shown in Fig. 3. Zn2+ ions were stored in the RuO2·H2O cathode when the cathode was discharged from pristine state to 0.4 V, and almost all Zn2+ ions were extracted from the RuO2·H2O cathode when the cathode was further charged to 1.6 V, implying highly reversible Zn2+ storage in the RuO2·H2O cathode. Besides, H+ from the slightly acid Zn(CF3SO3)2 aqueous electrolyte is also proved to participate in the electrochemical reactions in the RuO2·H2O//Zn system and contributes to a small capacity to the RuO2·H2O cathode (Figs. S5–S7). For the CV curves at various scan rates of the RuO2·H2O||Zn system (Fig. 2a), the relationship between their peak current (i) and scan rate (v) can be depicted through Eq. 1 [36]:
where a and b are variable parameters. Particularly, b values of 0.5 and 1.0 represent a diffusion-controlled process and a complete capacitive process, respectively [33]. As shown in Fig. 4a, the b values for the anodic peaks and cathodic peaks are close to 1.0, suggesting that Zn2+ storage in the RuO2·H2O cathode is dominated by a capacitive process.
We further tested CV curves at low scan rates (Fig. 4b). At 0.2–1 mV s−1, the voltage separation between anodic peaks and cathodic peaks is very small (< 0.08 V), which is a typical feature of pseudocapacitive behavior [37]. As a comparison, ZIB cathode materials such as MnO2 generally possess a large voltage separation (> 0.3 V; Fig. S8). Furthermore, two capacitance differentiation methods were applied to analyze the pseudocapacitive reaction of the RuO2·H2O for Zn2+ storage. According to Dunn’s method (Fig. 4c, d) [37], 79.0–96.4% capacitance originates from the surface-controlled capacitive process, i.e., redox pseudocapacitance and electric double-layer capacitance. Considering that the specific surface area of the RuO2·H2O is only 57 m2 g−1 (Fig. S9), the majority of the capacitance is redox pseudocapacitance, while the electric double-layer capacitance accounts a small fraction. Trasatti’s method analysis in Fig. 4e, f points out that the maximum charge that can be stored in the RuO2·H2O and the charge stored at the so-called outer surface (easily accessible to electrolyte ions) of the RuO2·H2O are 502.5 and 428.4 C g−1, respectively [38]. This means that 85.3% capacity is from the outer surface, which is consistent with the Dunn’s method analysis. Such an energy storage mechanism of redox pseudocapacitive behavior, as well as high conductivity of hydrous ruthenium oxides (higher than 100 S cm−1) [31], benefits for the ultrafast charging/discharging of the RuO2·H2O cathode [37].
It should be emphasized that the structural water in the RuO2·H2O plays a vital role in Zn2+ storage. As a comparison, anhydrous RuO2 sample was synthesized by heat-treating the RuO2·H2O in air (Figs. 5a, b and S10). The TG curve confirms that after heat treatment, structural water content of the sample is negligible. As for the anhydrous RuO2, its redox pseudocapacitive reactions are notably suppressed, corresponding to very low Zn2+-storage capacities of 38–15 mAh g−1 at 0.1–20 A g−1 (Figs. 5c, d and S11, S12), even though anhydrous RuO2 generally possesses a higher electrical conductivity than hydrous RuO2·xH2O [31]. This is because the structural water can facilitate rapid ion transport in the RuO2·H2O [34]. Similarly, hydrous ruthenium oxides perform much better than anhydrous RuO2 in supercapacitors with H2SO4 aqueous electrolytes [31].
Besides the excellent high rate performance, the amorphous RuO2·H2O cathode also exhibits superior long-term cyclic stability, with an 87.5% capacity retention over 10,000 charge/discharge cycles (Fig. 6a). Meanwhile, the coulombic efficiency always maintains ~ 100% during the cycling test (except for the initial tens of cycles). Nyquist plots in Fig. 6b of the RuO2·H2O||Zn hybrid capacitor reveal a small charge-transfer resistance even after the 10,000 charge/discharge cycles. In addition, the long-term cycling test does not cause an obvious change in the phase composition and micromorphology of the amorphous RuO2·H2O cathode (Fig. 6c and S13). These imply the high electrochemical and structural stability of the RuO2·H2O cathode during repeated Zn2+ storage processes.
4 Conclusions
In summary, amorphous RuO2·H2O was employed to achieve fast, ultralong-life, and safe Zn2+ storage. In the RuO2·H2O||Zn zinc-ion hybrid capacitors with aqueous Zn(CF3SO3)2 electrolyte, the RuO2·H2O cathode reversibly stores Zn2+ in a voltage window of 0.4–1.6 V (vs. Zn/Zn2+), displaying a discharge capacity of 122 mAh g−1 and an outstanding high rate performance. The zinc-ion hybrid capacitors can be rapidly charged/discharged within 36 s, in which case a very high power density of 16.74 kW kg−1 and a high energy density of 82 Wh kg−1 are delivered. Such an excellent high rate performance originates from redox pseudocapacitive reactions of the RuO2·H2O by storing Zn2+. Besides, the zinc-ion hybrid capacitors exhibit superior cycling stability with 87.5% capacity retention over 10,000 charge/discharge cycles. This work could greatly facilitate the development of ultrafast and safe aqueous electrolyte-based electrochemical energy storage.
References
C. Xu, B. Li, H. Du, F. Kang, Energetic zinc ion chemistry: the rechargeable zinc ion battery. Angew. Chem. Int. Ed. 51(4), 933–935 (2012). https://doi.org/10.1002/anie.201106307
O. Chusid, Y. Gofer, H. Gizbar, Y. Vestfrid, E. Levi, D. Aurbach, I. Riech, Solid-state rechargeable magnesium batteries. Adv. Mater. 15(7–8), 627–630 (2003). https://doi.org/10.1002/adma.200304415
A.L. Lipson, B. Pan, S.H. Lapidus, C. Liao, J.T. Vaughey, B.J. Ingram, Rechargeable Ca-ion batteries: a new energy storage system. Chem. Mater. 27(24), 8442–8447 (2015). https://doi.org/10.1021/acs.chemmater.5b04027
M. Wang, C. Jiang, S. Zhang, X. Song, Y. Tang, H.M. Cheng, Reversible calcium alloying enables a practical room-temperature rechargeable calcium-ion battery with a high discharge voltage. Nat. Chem. 10, 667–672 (2018). https://doi.org/10.1038/s41557-018-0045-4
N. Jayaprakash, S.K. Das, L.A. Archer, The rechargeable aluminum-ion battery. Chem. Commun. 47, 12610–12612 (2011). https://doi.org/10.1039/C1CC15779E
M.C. Lin, M. Gong, B. Lu, Y. Wu, D.Y. Wang et al., An ultrafast rechargeable aluminium-ion battery. Nature 520, 324–328 (2015). https://doi.org/10.1038/nature14340
L. Dong, W. Yang, W. Yang, Y. Li, W. Wu, G. Wang, Multivalent metal ion hybrid capacitors: a review with a focus on zinc-ion hybrid capacitors. J. Mater. Chem. A 7, 13810–13832 (2019). https://doi.org/10.1039/C9TA02678A
J. Ming, J. Guo, C. Xia, W. Wang, H.N. Alshareef, Zinc-ion batteries: materials, mechanisms, and applications. Mater. Sci. Eng. R 135, 58–84 (2019). https://doi.org/10.1016/j.mser.2018.10.002
M. Song, H. Tan, D. Chao, H.J. Fan, Recent advances in Zn-ion batteries. Adv. Funct. Mater. 28, 1802564 (2018). https://doi.org/10.1002/adfm.201802564
G. Fang, J. Zhou, A. Pan, S. Liang, Recent advances in aqueous zinc-ion batteries. ACS Energy Lett. 3, 2480–2501 (2018). https://doi.org/10.1021/acsenergylett.8b01426
L. Dong, X. Ma, Y. Li, L. Zhao, W. Liu et al., Extremely safe, high-rate and ultralong-life zinc-ion hybrid supercapacitors. Energy Storage Mater. 13, 96–102 (2018). https://doi.org/10.1016/j.ensm.2018.01.003
M.H. Alfaruqi, V. Mathew, J. Gim, S. Kim, J. Song, J.P. Baboo, S.H. Choi, J. Kim, Electrochemically induced structural transformation in a γ-MnO2 cathode of a high capacity zinc-ion battery system. Chem. Mater. 27, 3609–3620 (2015). https://doi.org/10.1021/cm504717p
H. Pan, Y. Shao, P. Yan, Y. Cheng, K.S. Han et al., Reversible aqueous zinc/manganese oxide energy storage from conversion reactions. Nat. Energy 1, 16039 (2016). https://doi.org/10.1038/nenergy.2016.39
H. Li, L. Ma, C. Han, Z. Wang, Z. Liu, Z. Tang, C. Zhi, Advanced rechargeable zinc-based batteries: recent progress and future perspectives. Nano Energy 62, 550–587 (2019). https://doi.org/10.1016/j.nanoen.2019.05.059
K.W. Nam, H. Kim, J.H. Choi, J.W. Choi, Crystal water for high performance layered manganese oxide cathodes in aqueous rechargeable zinc batteries. Energy Environ. Sci. 12, 1999–2009 (2019). https://doi.org/10.1039/C9EE00718K
D. Kundu, B.D. Adams, V. Duffort, S.H. Vajargah, L.F. Nazar, A high-capacity and long-life aqueous rechargeable zinc battery using a metal oxide intercalation cathode. Nat. Energy 1, 16119 (2016). https://doi.org/10.1038/nenergy.2016.119
P. He, Y. Quan, X. Xu, M. Yan, W. Yang, Q. An, L. He, L. Mai, High-performance aqueous zinc-ion battery based on layered H2V3O8 nanowire cathode. Small 13, 1702551 (2017). https://doi.org/10.1002/smll.201702551
B. Tang, G. Fang, J. Zhou, L. Wang, Y. Lei et al., Potassium vanadates with stable structure and fast ion diffusion channel as cathode for rechargeable aqueous zinc-ion batteries. Nano Energy 51, 579–587 (2018). https://doi.org/10.1016/j.nanoen.2018.07.014
N. Zhang, Y. Dong, M. Jia, X. Bian, Y. Wang et al., Rechargeable aqueous Zn-V2O5 battery with high energy density and long cycle life. ACS Energy Lett. 3, 1366–1372 (2018). https://doi.org/10.1021/acsenergylett.8b00565
Y. Yang, Y. Tang, G. Fang, L. Shan, J. Guo et al., Li+ intercalated V2O5·nH2O with enlarged layer spacing and fast ion diffusion as an aqueous zinc-ion battery cathode. Energy Environ. Sci. 11, 3157–3162 (2018). https://doi.org/10.1039/C8EE01651H
W. Zhang, S. Liang, G. Fang, Y. Yang, J. Zhou, Ultra-high mass-loading cathode for aqueous zinc-ion battery based on graphene-wrapped aluminum vanadate nanobelts. Nano-Micro Lett. 11, 69 (2019). https://doi.org/10.1007/s40820-019-0300-2
F. Liu, Z. Chen, G. Fang, Z. Wang, Y. Cai, B. Tang, J. Zhou, S. Liang, V2O5 nanospheres with mixed vanadium valences as high electrochemically active aqueous zinc-ion battery cathode. Nano-Micro Lett. 11, 25 (2019). https://doi.org/10.1007/s40820-019-0256-2
L. Zhang, L. Chen, X. Zhou, Z. Liu, Towards high-voltage aqueous metal-ion batteries beyond: the zinc/zinc hexacyanoferrate system. Adv. Energy Mater. 5, 1400930 (2015). https://doi.org/10.1002/aenm.201400930
Z. Liu, P. Bertram, F. Endres, Bio-degradable zinc-ion battery based on a prussian blue analogue cathode and a bio-ionic liquid-based electrolyte. J. Solid State Electrochem. 21, 2021–2027 (2017). https://doi.org/10.1007/s10008-017-3589-0
R. Trócoli, F.L. Mantia, An aqueous zinc-ion battery based on copper hexacyanoferrate. Chemsuschem 8, 481–485 (2015). https://doi.org/10.1002/cssc.201403143
Z. Jia, B. Wang, Y. Wang, Copper hexacyanoferrate with a well-defined open framework as a positive electrode for aqueous zinc ion batteries. Mater. Chem. Phys. 149–150, 601–606 (2015). https://doi.org/10.1016/j.matchemphys.2014.11.014
H.Y. Shi, Y.J. Ye, K. Liu, Y. Song, X. Sun, A long-cycle-life self-doped polyaniline cathode for rechargeable aqueous zinc batteries. Angew. Chem. Int. Ed. 57, 16359 (2018). https://doi.org/10.1002/ange.201808886
S. Huang, F. Wan, S. Bi, J. Zhu, Z. Niu, J. Chen, A self-healing integrated all-in-one zinc-ion battery. Angew. Chem. Int. Ed. 58, 4357–4361 (2019). https://doi.org/10.1002/ange.201814653
P. Zhang, Y. Li, G. Wang, F. Wang, S. Yang et al., Zn-ion hybrid micro-supercapacitors with ultrahigh areal energy density and long-term durability. Adv. Mater. 31, 1806005 (2018). https://doi.org/10.1002/adma.201806005
G. Sun, H. Yang, G. Zhang, J. Gao, X. Jin, Y. Zhao, L. Jiang, L. Qu, A capacity recoverable zinc-ion micro-supercapacitor. Energy Environ. Sci. 11, 3367–3374 (2018). https://doi.org/10.1039/C8EE02567C
J.P. Zheng, P.J. Cygan, T.R. Jow, Hydrous ruthenium oxide as an electrode material for electrochemical capacitors. J. Electrochem. Soc. 142, 2699–2703 (1995). https://doi.org/10.1149/1.2050077
D. Rochefort, P. Dabo, D. Guay, P.M.A. Sherwood, XPS investigations of thermally prepared RuO2 electrodes in reductive conditions. Electrochim. Acta 48, 4245–4252 (2003). https://doi.org/10.1016/S0013-4686(03)00611-X
D.J. Yun, S. Lee, K. Yong, S.W. Rhee, In situ ultraviolet photoemission spectroscopy measurement of the pentacene-RuO2/Ti contact energy structure. Appl. Phys. Lett. 97, 073303 (2010). https://doi.org/10.1063/1.3481084
P. He, M. Yan, G. Zhang, R. Sun, L. Chen, Q. An, L. Mai, Layered VS2 nanosheet-based aqueous Zn ion battery cathode. Adv. Energy Mater. 7, 1601920 (2017). https://doi.org/10.1002/aenm.201601920
P. Simon, Y. Gogotsi, Materials for electrochemical capacitors. Nat. Mater. 7, 845–854 (2008). https://doi.org/10.1038/nmat2297
J. Wang, J. Polleux, J. Lim, B. Dunn, Pseudocapacitive contributions to electrochemical energy storage in TiO2 (Anatase) nanoparticles. J. Phys. Chem. C 111, 14925–14931 (2007). https://doi.org/10.1021/jp074464w
V. Augustyn, P. Simon, B. Dunn, Pseudocapacitive oxide materials for high-rate electrochemical energy storage. Energy Environ. Sci. 7, 1597–1614 (2014). https://doi.org/10.1039/C3EE44164D
S. Ardizzone, G. Fregonara, S. Trasatti, “Inner” and “outer” active surface of RuO2 electrodes. Electrochim. Acta 35, 263–267 (1989). https://doi.org/10.1016/0013-4686(90)85068-X
Acknowledgements
The authors acknowledge the financial support by the Australian Research Council through the ARC Discovery projects (DP160104340 and DP170100436) and Rail Manufacturing Cooperative Research Centre (RMCRC 1.1.1 and RMCRC 1.1.2 projects). This work was also financially supported by the International Science & Technology Cooperation Program of China (No. 2016YFE0102200) and Shenzhen Technical Plan Project (No. JCYJ20160301154114273).
Author information
Authors and Affiliations
Corresponding authors
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Dong, L., Yang, W., Yang, W. et al. High-Power and Ultralong-Life Aqueous Zinc-Ion Hybrid Capacitors Based on Pseudocapacitive Charge Storage. Nano-Micro Lett. 11, 94 (2019). https://doi.org/10.1007/s40820-019-0328-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-019-0328-3