Highlights
-
Controllable and large-scale practical growth of plasmonic Ag-decorated vertically aligned 2D MoS2 nanosheets on graphene.
-
Realization of the synergistic effects of surface plasmon resonance and favorable graphene/MoS2 heterojunction to enhance the photoelectrochemical reactivity of 2D MoS2.
Abstract
A controllable approach that combines surface plasmon resonance and two-dimensional (2D) graphene/MoS2 heterojunction has not been implemented despite its potential for efficient photoelectrochemical (PEC) water splitting. In this study, plasmonic Ag-decorated 2D MoS2 nanosheets were vertically grown on graphene substrates in a practical large-scale manner through metalorganic chemical vapor deposition of MoS2 and thermal evaporation of Ag. The plasmonic Ag-decorated MoS2 nanosheets on graphene yielded up to 10 times higher photo-to-dark current ratio than MoS2 nanosheets on indium tin oxide. The significantly enhanced PEC activity could be attributed to the synergetic effects of SPR and favorable graphene/2D MoS2 heterojunction. Plasmonic Ag nanoparticles not only increased visible-light and near-infrared absorption of 2D MoS2, but also induced highly amplified local electric field intensity in 2D MoS2. In addition, the vertically aligned 2D MoS2 on graphene acted as a desirable heterostructure for efficient separation and transportation of photo-generated carriers. This study provides a promising path for exploiting the full potential of 2D MoS2 for practical large-scale and efficient PEC water-splitting applications.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Photoelectrochemistry (PEC) and photocatalysis of semiconductors have been extensively studied as effective approaches for energy conversion, such as hydrogen gas production by water splitting, and for environmental applications, such as air/water purification, water disinfection, and hazardous waste remediation [1,2,3,4,5,6,7]. Recently, two-dimensional (2D) layered MoS2 has attracted considerable research attention as a promising semiconductor photocatalyst because of its excellent catalytic activity, high chemical stability, eco-friendliness, and abundance in nature [2,3,4]. In particular, few-layer-thick MoS2 nanosheets can be central to exploiting the full potential of 2D MoS2 for solar-light PEC reactions because of the feasibility of mass production and appropriate bandgap energy, which is tunable from ~ 1.2 eV for indirect gap in the bulk form to ~ 1.9 eV for direct gap in the monolayer [8,9,10]. The PEC activity of 2D MoS2, which has strong in-plane covalent bonding of S–Mo–S and weak out-of-plane van der Waals interaction between neighboring S–S layers, is significantly hindered by poor charge transport across basal layers through hopping [2,3,4]. Thus, the ideal architecture configuration comprises 2D MoS2 nanosheets that stand vertically on electrode substrates because the highly conductive edges of MoS2 provide an efficient pathway for photoexcited carriers and good electronic contact with the substrate. In addition, vertically packed 2D sheets offer higher volume than laid sheets for interacting with incoming photon flux on a unit substrate area. He et al. demonstrated that the edge-on structure of MoS2 flakes/TiO2 nanowires improves the photocatalytic hydrogen evolution of MoS2 [11]. Recently, we reported the enhanced PEC activity of few-layer MoS2 nanosheets vertically grown on supporting electrode substrates, such as indium-tin oxide (ITO) and ITO/TiO2 nanowires [12, 13]. However, the synthesis and PEC applications of vertically aligned few-layer MoS2 nanosheets on graphene have not been reported despite its considerable potential.
The support substrate should be made highly conductive and form an appropriate energy band alignment with MoS2 to minimize Ohmic junction losses. Graphene has attracted huge research attention as a promising conducting layer not only because it displays remarkable electron mobility (> 15,000 cm2 V−1 s−1) but also due to its favorable electric contact with MoS2. Chang et al. reported the enhanced photocatalytic hydrogen evolution of MoS2/graphene as a result of the improved charge transport of graphene [14]. Carraro et al. demonstrated the one-pot aerosol synthesis of MoS2 nanoparticles/graphene for enhanced PEC hydrogen production [15]. Biroju et al. also reported that an adequate stacking of 2D MoS2 and graphene exhibited a ΔGH value that is close to zero, which is ideal for hydrogen evolution reactions [16]. However, most MoS2/graphene heterostructures have been synthesized by wet-chemical and mechanical transfer approaches, which are unsuitable for controlled synthesis or vertical stacking of few-layer MoS2 nanosheets on graphene electrode substrates [14,15,16,17,18]. Wet-chemical synthesis methods have yielded a wide range of MoS2 layer thicknesses and produced the randomly assembled structures of 2D MoS2 and graphene [14, 15, 19].
The optical absorption of 2D MoS2 can be remarkably enhanced by employing plasmonic metal nanoparticles (NPs), such as Ag or Au. Plasmonic metals improve the optical absorption over the entire solar spectrum as well as broaden and tune the optical absorption behavior, depending on their composition, size, and shape [20, 21]. Ag and Au have gained research interest because of their strong resonance with ultraviolet (UV) and visible light. Moreover, the surface plasmon resonance (SPR) of metal NPs enhances the intensity of the electric field near the metal NPs, thereby significantly increasing the rate of electron–hole (e–h) pair generation [20, 22]. Plasmonic metal NPs also act as dye sensitizers by absorbing resonant photons and injecting high-energy electrons into the nearby semiconductor [20, 23]. Kang et al. reported the effective injection of SPR-excited electrons, i.e., hot electrons, by Au NPs into the conduction band of MoS2 by overcoming the Schottky barrier (~ 0.8 eV) of Au/MoS2 [24]. Plasmonic effect has been effectively applied to enhance the photocatalytic and PEC performances of various semiconductors, such as TiO2, CdS, ZnO, and BiFeO3 [25,26,27,28,29,30,31,32]. To maximize the SPR effects and enhance the PEC activity, SPR-induced charge carriers should be efficiently transported to the corresponding electrode/water interfaces. Vertically aligned few-layer MoS2 nanosheets on graphene can act as desirable heterostructures to synergistically exploit the SPR effects in terms of energy band diagram and physical nanostructure architecture.
Herein, we report significantly improved PEC efficiency through the synergetic effects of (1) SPR-enhanced optical absorption and photo-generation of charge carriers and (2) efficient separation and transportation of photo-generated e–h pairs through few-layer MoS2 sheets that are vertically aligned on graphene. Few-layer MoS2 sheets were vertically grown on graphene in a controlled manner at relatively low temperatures (250 °C) through metalorganic chemical vapor deposition (MOCVD) to minimize damage to the graphene. For the SPR effect, Ag NPs were formed on 2D MoS2 sheets on graphene through simple thermal evaporation of Ag (Fig. 1). Thermal evaporation is a low-cost and practical method for large-area substrates in comparison with previously reported methods, such as sophisticated metal nanopatterning [21], drop/spin casting of pre-synthesized metal NPs [33], and chemical synthesis [22]. Ag was chosen as plasmonic metal because of its appropriate resonant wavelength range in the UV to near-infrared (IR) band and smaller work function (~ 4.3–4.8 eV) than Au (~ 5.1–5.5 eV) and Pt (~ 5.1–5.9 eV). Thus, Ag/MoS2 forms a low Schottky barrier, which is advantageous for the efficient injection of SPR-excited electrons into the conduction band of MoS2.
2 Experimental
2.1 Preparation of heterostructures of graphene/2D MoS2/Ag NPs
Graphene was synthesized on Cu foils (Alfa Aesar) by using inductively coupled plasma (ICP) CVD with CH4 and H2 gases at 950 °C for 5 min. The ICP power and growth pressure were fixed at 200 W and 1 Torr, respectively. The synthesized graphene on Cu was transferred on an ITO glass substrate (Fig. 1). The CVD growth and transfer procedures of graphene were further described elsewhere [34]. MoS2 was directly grown on ITO and ITO/graphene at 250 °C by using MOCVD with Mo(CO)6 and H2S gas (5 vol% in balance N2) as Mo and S precursors, respectively. Mo(CO)6 was vaporized at 20 °C and transferred into a quartz reaction tube with Ar gas of 25 standard cubic centimeters per minute (SCCM). The flow rate of H2S gas was 75 SCCM. The growth pressure and time were fixed at 1 Torr and 5 min, respectively. Ag NPs were formed on ITO/graphene/MoS2 through thermal evaporation of Ag at room temperature. The size and coverage of Ag NPs on few-layer MoS2 were controlled by various nominal Ag deposition thicknesses of 2, 4, and 8 nm. The Ag contents per electrode area were estimated to be 2.1, 4.2, and 8.4 μg cm−2 for 2, 4, and 8 nm of Ag, respectively.
2.2 Characterization
The morphology of the samples was investigated via scanning electron microscopy (SEM; Hitachi S-4800) and transmission electron microscopy (TEM; Tecnai G2 F30 S-Twin). The structural properties of MoS2 were characterized by TEM and micro-Raman spectroscopy by using an excitation band of 532 nm and a charge-coupled device detector. The chemical states and composition of the samples were characterized by X-ray photoelectron spectroscopy (XPS; Thermo Fisher K-Alpha+). Optical properties were evaluated by UV–visible (UV–Vis; Scinco S-3100) and photoluminescence (PL) spectroscopy (excitation at 532 nm). Photoexcited carrier behavior was investigated by time-resolved PL (TRPL) measurements. The samples were excited using a 467 nm pulsed laser, and the transient signal was recorded using a time-correlated single-photon counting spectrometer (Horiba Fluorolog 3). The energy level of MoS2 was evaluated via UV photoelectron spectroscopy (UPS; Thermo scientific, K-alpha+).
2.3 Photoelectrochemical Measurement
PEC cells were fabricated on 1 × 2 cm2 ITO glass substrates. The working area of the PEC cells was fixed at 0.5 × 0.5 cm2 by using non-conductive epoxy to cover the undesired areas. PEC characterization was performed using a three-electrode system and an electrochemical analyzer (potentiostat/galvanostat 263A). A Pt plate and KCl-saturated calomel (Hg/Hg2Cl2) were used as counter and reference electrodes, respectively. The electrolyte solutions were prepared with 0.3 M KH2PO4 + 0.3 M KOH and 0.5 M Na2SO3 + 0.5 M Na2SO4. The light source was simulated AM 1.5G irradiation of 100 Mw cm−2 delivered by a 150 W Xe arc lamp. The current density–voltage characteristics were recorded using a source meter (Keithley 2400). Electrochemical impedance spectroscopy (EIS) measurement was performed under constant light illumination (100 mW cm−2) at a bias of 0.6 V with varying AC frequencies from 100 kHz to 100 mHz. The incident monochromatic photon-to-current conversion efficiency (IPCE) of the electrode structure was measured using a grating monochromator in the excitation wavelength range of 300–800 nm. The hydrogen gas products were analyzed using a YL 6500 gas chromatograph (Young In Chromass Co., Ltd.) equipped with a flame ionization detector and a thermal conductivity detector. A gas volume of 0.5 mL was injected into columns of 40/60 Carboxen-1000 for GC analysis.
3 Results and Discussion
3.1 Microstructure of AgNP-Decorated MoS2 Nanosheets on Graphene
MoS2 nanosheets with a height of ~ 200 nm and length of ~ 150–250 nm were vertically aligned and densely packed on the ITO/graphene substrate (hereinafter referred to as G/MoS2, Fig. 2a, b). Owing to the low-temperature growth at 250 °C, the graphene layer remained after the MOCVD growth of MoS2, as confirmed by the presence of the characteristic G and 2D band peaks in the Raman spectrum (inset of Fig. 2a, Fig. S1a, b). The pristine CVD-grown graphene layer exhibited a low-intensity ratio of D to G band peaks (> 0.15) and an excellent light transmittance of 96.8% at 550 nm (Fig. S1c), corresponding to approximately one and a half layers of high-quality graphene [34]. The structure of few-layer MoS2 was investigated using TEM and Raman spectroscopy. The planar-view TEM image of G/MoS2 clearly showed the layered structure of MoS2 sheets with edges on graphene (Fig. 2c). The sheets comprised 1–5 layers with an interlayer spacing of 0.63 nm, corresponding to the semiconducting 2H MoS2. The TEM results are consistent with the Raman spectrum of G/MoS2 (Fig. S2a). The \(E^{1}_{{2{\text{g}}}}\) and A1g modes can be attributed to the in-plane vibration of Mo and S atoms and the out-of-plane vibration of S atoms, respectively. The positions and relative frequency difference (RFD) of \(E^{1}_{{2{\text{g}}}}\) and the A1g peaks are strongly correlated with the number of MoS2 layers [12, 35, 36]. For G/MoS2, the RFD value (22.3 cm−1) of \(E^{1}_{{2{\text{g}}}}\) (385.0 cm−1) and A1g peaks (407.3 cm−1) corresponds to a few layers of MoS2. The MoS2 sheets grown on ITO (hereinafter referred to as ITO/MoS2) showed similar size and morphology as the counterpart sample, namely G/MoS2 (Fig. S2b). The RED value of \(E^{1}_{{2{\text{g}}}}\) and A1g peaks of ITO/MoS2 was also similar to that of G/MoS2 (Fig. S2a).
Figure 2d–f shows the TEM images of Ag-decorated G/MoS2 with nominal Ag thicknesses of 2, 4, and 8 nm, respectively (referred to as G/MoS2/Ag-2, G/MoS2/Ag-4, and G/MoS2/Ag-8, respectively). The size of the Ag NPs on MoS2 was successfully manipulated by varying the nominal deposition thickness of Ag through thermal evaporation. For G/MoS2/Ag-2, Ag NPs with a size of ~ 3–5 nm were formed on the MoS2 nanosheet surface (Fig. S3). The NP size increased to ~ 10–20 nm for G/MoS2/Ag-4. By increasing the nominal deposition thickness to 8 nm, the size of Ag NPs increased to ~ 20–40 nm. In addition, large Ag clusters of ~ 60–100 nm were partially formed. The high-resolution TEM lattice image revealed that the NPs were metallic Ag (Fig. 2g). The metallic Ag was also confirmed by XPS. Figure 3a shows two strong peaks in the XPS spectrum of G/MoS2/Ag-4 at 373.9 and 367.9 eV, which can be attributed to the Ag 3d3/2 and Ag 3d5/2 orbitals of metallic Ag, respectively [37].
MoS2 presents two common structure polymorphs, namely semiconducting 2H and metallic 1T phases, which can be converted from each other by surface treatments, such as Ar-plasma bombardment and metal deposition [2, 38, 39]. As shown in Fig. 3b, the XPS spectra of the Mo 3d core level were deconvoluted into only two peaks at 229.1 and 232.2 eV, which can be attributed to the Mo4+ 3d5/2 and Mo4+ 3d3/2 components of the 2H phase of MoS2, respectively [2, 38, 39]. Pristine MoS2 (G/MoS2) and Ag NP-decorated MoS2 (G/MoS2/Ag-4) exhibited nearly identical XPS spectra at the Mo 3d core level, indicating that the single phase of semiconducting 2H MoS2 remained stable after Ag NP decoration. This structural stability is highly advantageous for 2D MoS2 in semiconducting photoelectrode applications. Figure 3c shows the XPS spectra of the S 2p core level of MoS2. The spectra were deconvoluted into two peaks at 163.2 and 162.0 eV, corresponding to the S 2p1/2 and S 2p3/2 orbital of divalent sulfur, respectively [38]. The ratios of the S 2p1/2 and S 2p3/2 peaks of G/MoS2 and G/MoS2/Ag-4 were almost identical, suggesting a single phase of 2H MoS2 for both samples. The 2H phase of both samples was also confirmed by TEM (Fig. 2c). G/MoS2/Ag-4 exhibited a small broad bump near 168 eV, which can be attributed to S4+ due to Ag sulfurization. However, the peak was removed by slight Ar-plasma surface etching, indicating the ultrathin layer of silver sulfide. The XPS result implies that the interface of MoS2/Ag is likely to be an alloy interface.
3.2 Effect of Graphene on the PEC Activity of MoS2 Nanosheets
The G/MoS2 and ITO/MoS2 samples exhibited a PL peak at 676 nm (inset of Fig. 4a), which is consistent with the energy of exciton A. Hence, the dominant electronic transition was the direct bandgap transitions at the Κ point [12]. Notably, G/MoS2 achieved significantly lower PL efficiencies than ITO/MoS2. The PL quenching efficiency indicated that the graphene layer played a crucial role in reducing the e–h recombination in MoS2. TRPL spectroscopy study was conducted to further understand the dynamic behavior of photo-generated carriers (Fig. 4a). The average carrier lifetimes were extracted using the PL decay kinetics fitted by a bi-exponential decay profile [40]. G/MoS2 exhibited a shorter carrier lifetime of 3.1 ns than ITO/MoS2 (4.2 ns). The reduced carrier lifetime can be attributed to the benefits of graphene/MoS2 heterojunction for efficient separation and transportation of photo-generated carriers to the semiconductor/liquid interface [18].
EIS study was conducted to further understand the charge transport property. Figure 4b shows the Nyquist plots of EIS in the dark and under illumination. G/MoS2 exhibited smaller EIS semicircles than ITO/MoS2, whose radius mirrors the charge transfer resistance (Rct). The Nyquist plots were fitted using a simplified Randles circuit (inset of Fig. 4b), consisting of Rct, solution resistance (Rs), constant phase element (Q), and diffusion of species in electrolyte solution represented by Warburg impedance (W). The Rct values are listed in Supporting Information (Table S1). G/MoS2 had Rct values of 3264 and 1959 Ω, whereas ITO/MoS2 exhibited Rct values of 4236 and 2766 Ω in the dark and under illumination, respectively. Moreover, the Rct (dark)-to-Rct (photo) ratio (1.67) of G/MoS2 was greater than that of ITO/MoS2 (1.53), suggesting that the photo-generated e–h pairs were efficiently separated and transported through the graphene/MoS2 heterojunction.
Considering the benefits of graphene/MoS2 heterojunction, G/MoS2 exhibited significantly higher PEC activity through the measured potential range than ITO/MoS2 (Fig. 4c). G/MoS2 yielded approximately nine times higher photocurrent density (1.72 mA cm−2) at 0.4 V (at which the photo-to-dark current ratio (Iph/Idark) was at maximum) than ITO/MoS2 (0.19 mA cm−2). The maximum Iph/Idark value of G/MoS2 was approximately 16 at 0.4 V, whereas that of ITO/MoS2 was approximately 4 at 0.8 V. The water oxidation onset potential (~ 0.13 V), which is generally defined by the potential at the intersection of the dark current and the tangent at the maximum slope of the photocurrent, of G/MoS2 had a cathodic shift of ~ 0.41 V with respect to that (~ 0.54 V) of ITO/MoS2. The rapidly increasing photocurrent density of the samples above 0.6 V resulted from the considerably high dark current, which can be attributed to the electrocatalysis and electro-corrosion of MoS2, in which active S atoms can react with redox species in the solution [12, 14].
3.3 Effect of Plasmonic Ag NPs on the PEC Activity of Graphene/MoS2 Nanosheets
Raman spectroscopy characterization was performed to investigate the interaction of Ag NPs with MoS2. The characteristic \(E^{1}_{{2{\text{g}}}}\) and A1g modes of the Ag-decorated samples were redshifted with respect to those of G/MoS2-250 because of the stiffening of \(E^{1}_{{2{\text{g}}}}\) and A1g vibrations (Fig. 5a). The stiffened lateral vibration between Mo and S atoms through \(E^{1}_{{2{\text{g}}}}\) mode resulted from the p-doping effect of Ag NPs in MoS2 [38]. MoS2/Ag was very likely to form a Schottky junction because of electron transfer from MoS2 to Ag NPs, as shown in Fig. S4. The stiffened vertical vibration of S atoms through A1g mode was also attributed to the interaction between the Ag NPs and MoS2 [23]. Figure 5b shows the UV–Vis absorption spectra of G/MoS2 and the Ag-decorated MoS2 samples. All samples showed two prominent absorption peaks at approximately 607 and 663 nm. The two peaks, known as excitons B and A, respectively, can be attributed to the direct excitonic transitions at the K point of the MoS2 Brillouin zone [12, 41]. In comparison with G/MoS2, the Ag-decorated MoS2 samples exhibited stronger absorption intensity, especially for red light and near-IR regions. Additionally, the absorption edges (~ 800 nm) of Ag-decorated MoS2 samples were redshifted with respect to that (~ 750 nm) of G/MoS2. The enhanced visible light and broadened absorption near the IR region can be attributed to the strong coupling between the excitons and surface plasmons of Ag NPs [20, 21]. The PL spectra also exhibited redshifting behavior with increasing Ag NP sizes (Fig. S5). G/MoS2 showed a PL peak position of 676 nm, corresponding to the energy of the exciton A, representing the direct bandgap transitions at the Κ point of 2D MoS2. With increasing Ag NP sizes, the PL peak was gradually redshifted, reaching 688 nm for G/MoS2/Ag-8.
TRPL study was conducted to investigate the plasmonic effect of Ag NPs on the dynamic carrier behavior. G/MoS2 exhibited the shortest carrier lifetime of 3.1 ns, whereas G/MoS2/Ag-4 and G/MoS2/Ag-8 yielded longer carrier lifetimes of ~ 3.8 ns (Fig. 5c). The carrier lifetime increased with increasing nominal Ag deposition thicknesses. The long carrier lifetimes of Ag-decorated MoS2 samples can be attributed to suppressed e–h recombination by filling the trapping sites of MoS2 by plasmon-excited electrons [23]. Ag-decorated MoS2 samples also exhibited smaller EIS semicircles than G/MoS2 (Fig. 5d, Fig. S5). The Nyquist plots of G/MoS2/Ag-4 yielded the lowest Rct in the dark (~ 2572 Ω) and under illumination (~ 1284 Ω), suggesting the effective assistance of the carrier transfer through the Ag NPs on the MoS2 surface. Moreover, G/MoS2/Ag-4 yielded the highest Rct (dark)/Rct (photo) of 2.00 (inset of Fig. 5d). The increased Rct (dark)/Rct (photo) can result from the SPR-enhanced photo-generation and transfer rate of the charge carriers. In addition, the heterojunction of MoS2/Ag can play a significant role in improving the charge separation and transfer rate [42, 43].
To validate the experimental findings, finite-difference time-domain (FDTD) simulations of the interaction of materials with the incident electromagnetic radiation were performed based on Maxwell’s equations. Ag hemispheres in an open-air environment under the illumination of a plane-wave source were considered (Fig. S7). A 2D periodic orientation of the NPs on a three-layer-thick MoS2 substrate was assumed including the following: (1) 3-nm-diameter NPs with a pitch of 20 nm (referred to as AgNP-3), (2) 15-nm-diameter NPs with a pitch of 30 nm (referred to as AgNP-15), and (3) 60-nm-diameter NPs with a pitch of 65 nm (referred to as AgNP-60). The electric field vector of the source oscillated along the x-axis, while the propagation vector is along the z-axis. Figure 6 shows the simulated UV–Vis absorption spectra and electric field distribution contour plots at the wavelength of SPR (λSPR) for AgNP-3, AgNP-15, and AgNP-60. The simulated UV–Vis absorption spectrum of pristine MoS2 substrate was in good agreement with the corresponding experimental result (Fig. 6a). The light absorption was significantly enhanced in the visible light and IR regions by Ag NP decoration. Notably, the SPR peaks appeared above the absorption edge of pristine MoS2 (~ 700 nm), consistent with the experimentally observed broadened absorption near the IR region. AgNP-15 exhibited the strongest SPR effect, resulting in the highly amplified local electric field intensity in MoS2 (Fig. 6b). The SPR-enhanced electric field can increase the rate of e–h pair generation by a few orders of magnitude [20]. The 15 nm Ag NPs induced an SPR-enhanced electric field in the entire interface region of MoS2/Ag NP. By contrast, the 60 nm Ag NPs showed SPR effect only along the edge of NPs (Fig. 6c), indicating that a significant amount of light was extinguished by big Ag clusters (~ 60–100 nm) of G/MoS2/Ag-8 without photo-generation of e–h pairs in MoS2. The excessive surface coverage of metal NPs can also hinder contact of the electrochemical active surface with the electrolyte solution, resulting in deteriorated PEC activity [44, 45]. In addition, the surface plasmons of small Ag NPs (< 30 nm) undergo decay because of the formation of energetic charge carriers, but those of large Ag NPs (> 50 nm) undergo decay through the radiative scattering of resonant photons [37, 46]. Thus, the Ag NPs of G/MoS2/Ag-4 efficiently injected SPR-excited electrons into the conduction band of MoS2, resulting in the largest Rct (dark)/Rct (photo). Meanwhile, the SPR effect of G/MoS2/Ag-2 was relatively weak because of its low surface coverage of tiny Ag NPs of less than 10 nm (Fig. 6a).
To gain insight into the carrier transport property across the heterojunction of graphene/MoS2, its electronic structure was studied by UPS. The work function of MoS2 (4.82 ± 0.15 eV) was determined based on the difference between the photon energy of excited radiation (21.2 eV) and the spectrum width which is measured from the valence band and secondary edges (16.38 eV, Fig. 7a). The energy difference between the Fermi energy and valence band edge (EF–EVB) was 1.36 eV (Fig. 7b). Considering the bandgap energy of ~ 1.88 eV for MoS2 based on the UV–Vis absorption and PL spectra, the electron affinity of MoS2 was approximately 4.33 eV, which is consistent with the previously reported values (~ 4.3 eV) [47]. This electronic structure suggests the n-type behavior of MoS2, working as a photoanode. As shown in Fig. 7c, the Fermi level (~ 4.6–4.8 eV of work function) of pristine few-layer graphene [48] was appropriately located between the Fermi level of the ITO and the conduction band edge of MoS2 for efficient extraction of electrons to the cathode.
Figure 8a shows the linear sweep voltammograms of G/MoS2, G/MoS2/Ag-2, G/MoS2/Ag-4, and G/MoS2/Ag-8 under illumination. The Ag-decorated MoS2 samples exhibited significantly higher PEC activities than G/MoS2, whereas the dark currents were almost identical (Fig. S8). Subsequently, G/MoS2/Ag-4 yielded 2.5 times higher Iph/Idark value than G/MoS2. In addition, the Ag-decorated MoS2 samples showed a significant cathodic shift of onset potential up to 0.2 V with respect to that of G/MoS2. The Ag-decorated MoS2 samples also did not exhibit any anodic peaks before the onset potential, whereas G/MoS2 yielded minor but noticeable peaks. The anodic peaks can be originated from surface states of 2D MoS2 nanosheets, which can be filled and deactivated by plasmon-excited electrons [23]. Passivating surface states also caused the significant cathodic shift of onset potential [49] and prolonged the carrier lifetimes of the Ag-decorated MoS2 samples (Fig. 5c). Photoconversion efficiency (η) was estimated using the following equation to further quantify PEC performance [50]:
where J is the photocurrent density (mA cm−2) at the applied potential, Eo is the standard reversible potential (1.23 V), Vapp is applied potential, and Plight is the power density of illumination. The photoconversion efficiencies of Ag-decorated MoS2 samples were significantly higher than that (0.8% at − 0.45 V) of G/MoS2 (Fig. 8b). Among the samples, G/MoS2/Ag-4 exhibited the highest photoconversion efficiency of 1.6% at − 0.35 V. The photoconversion efficiency of G/MoS2/Ag-4 further increased to 2.2% at − 0.58 V in 0.5 M Na2SO3 + 0.5 M Na2SO4. The photoconversion efficiency G/MoS2/Ag-4 was comparable with those of previously reported photoanodes, such as Au-decorated MoS2 flakes on carbon fiber cloth (1.27%) [51], MoS2 nanosheets on TiO2 nanorods (0.81%) [52], Ag-embedded MoS2/BiVO4 heterojunctions (2.67%) [53], and MoS2 nanosheets on polydopamine-modified TiO2 nanotubes (1.56%) [54]. Moreover, the photocurrents of G/MoS2 and G/MoS2/Ag-4 did not change significantly after 1 h of illumination, whereas the photocurrent of ITO/MoS2 decreased continuously (Fig. 8c). The photocurrents of G/MoS2 and G/MoS2/Ag-4 decayed initially but saturated shortly above 300 s. The decayed photocurrent was attributed to the recombination of the photo-generated holes with electrons [55]. The photocurrent became stable as the transfer and generation of photo-generated e–h pairs reached equilibrium. The stable photocurrent suggests the effective separation and transfer of the photo-generated e–h pairs in the heterojunction of graphene/MoS2 nanosheets. To examine the PEC stability of Ag-decorated MoS2, the time-dependent PEC measurement of the G/MoS2/Ag-4 was repeated after a month. The time-dependent behavior did not change significantly excepting for slightly reduced photocurrents (Fig. S9). After PEC measurement for 1 h, the MoS2 nanosheets on ITO (ITO/MoS2) were significantly damaged, whereas G/MoS2 and G/MoS2/Ag-4 showed slight morphological changes (Fig. S10). We recently reported that such morphological changes in MoS2 nanosheets were due to the decomposition of MoS2, mainly the loss of S elements [12].
IPCE and H2 evolution studies were carried out to gain insights into the enhanced PEC performance by G/MoS2 heterojunction and SPR effects. Figure 9a shows the IPCE plots of various working electrodes (MoS2, G/MoS2, and G/MoS2/Ag-4). G/MoS2/Ag-4 exhibited significantly improved photoconversion efficiencies over the overall incident-light waveband, suggesting fortified carrier photo-generation and transfer dynamics. Furthermore, a significant IPCE enhancement was observed at the ~ 650–750 nm region, which was associated with the SPR effect of Ag NPs. Hydrogen evolution from dark cathode (Pt) was measured at 0.6 V versus Hg/Hg2Cl2 by using a three-electrode configuration during 15 min. The amount of H2 produced was significantly increased by G/MoS2 heterojunction and SPR effects, suggesting that the photocurrent was attributed to the water-splitting reaction. In addition, the Faradaic efficiency of G/MoS2/Ag-4 was estimated to be approximately 90.4%, implying that few side reactions occurred during water splitting [56].
4 Conclusion
Plasmonic Ag-decorated vertically aligned few-layer MoS2 nanosheets were prepared on graphene in a practical manner through MOCVD of MoS2 and thermal evaporation of Ag. G/MoS2 showed up to four times higher Iph/Idark than ITO/MoS2 because of the efficient separation and transportation of the photo-generated carriers by the graphene/2D MoS2 heterojunction. The PEC activity of G/MoS2 was further enhanced by plasmonic Ag NP decoration. G/MoS2/Ag-4 yielded 10 times higher Iph/Idark value than ITO/MoS2. The maximum photoconversion efficiency of G/MoS2/Ag-4 was 2.2% at − 0.58 V. The significantly improved PEC performance was attributed to the synergetic effects of SPR and graphene/2D MoS2 heterojunction. Plasmonic Ag NPs enhanced visible-light and near-IR absorption of 2D MoS2, resulting in significantly increased the photo-generation rate of e–h pairs. Subsequently, the e–h pairs were efficiently separated and transported to catalytic surfaces across the favorable graphene/2D MoS2 heterojunction and along the highly conductive edges of the vertically aligned 2D MoS2, thereby significantly enhancing the PEC activity. This study offers a practical large-scale approach that combines the potential of SPR and graphene/2D MoS2 heterojunction effects for efficient PEC applications.
References
M.G. Walter, E.L. Warren, J.R. McKone, S.W. Boettcher, Q. Mi, E.A. Santori, N.S. Lewis, Solar water splitting cells. Chem. Rev. 110(11), 6446–6473 (2010). https://doi.org/10.1021/cr1002326
Q. Ding, B. Song, P. Xu, S. Jin, Efficient electrocatalytic and photoelectrochemical hydrogen generation using MoS2 and related compounds. Chem 1(5), 699–726 (2016). https://doi.org/10.1016/j.chempr.2016.10.007
B. Han, Y.H. Hu, MoS2 as a co-catalyst for photocatalytic hydrogen production from water. Energy Sci. Eng. 4(5), 285–304 (2016). https://doi.org/10.1002/ese3.128
B. Chen, Y. Meng, J. Sha, C. Zhong, W. Hu, N. Zhao, Preparation of MoS2/TiO2 based nanocomposites for photocatalysis and rechargeable batteries: progress, challenges, and perspective. Nanoscale 10(1), 34–68 (2018). https://doi.org/10.1039/C7NR07366F
Y.H. Chiu, T.F.M. Chang, C.Y. Chen, M. Sone, Y.J. Hsu, Mechanistic insights into photodegradation of organic dyes using heterostructure photocatalysts. Catalysts 9(5), 430 (2019). https://doi.org/10.3390/catal9050430
Y.H. Chiu, T.H. Lai, M.Y. Kuo, P.Y. Hsieh, Y.J. Hsu, Photoelectrochemical cells for solar hydrogen production: challenges and opportunities. APL Mater. 7(8), 080901 (2019). https://doi.org/10.1063/1.5109785
M.J. Fang, C.W. Tsao, Y.J. Hsu, Semiconductor nanoheterostructures for photoconversion applications. J. Phys. D Appl. Phys. 53(14), 143001 (2020). https://doi.org/10.1088/1361-6463/ab5f25
H. Li, Q. Zhang, C.C.R. Yap, B.K. Tay, T.H.T. Edwin, A. Olivier, D. Baillargeat, From bulk to monolayer MoS2: evolution of raman scattering. Adv. Funct. Mater. 22(7), 1385–1390 (2012). https://doi.org/10.1002/adfm.201102111
K.F. Mak, C. Lee, J. Hone, J. Shan, T.F. Heinz, Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105(13), 136805 (2010). https://doi.org/10.1103/PhysRevLett.105.136805
C. Lee, H. Yan, L.E. Brus, T.F. Heinz, J. Hone, S. Ryu, Anomalous lattice vibrations of single- and few-layer MoS2. ACS Nano 4(5), 2695–2700 (2010). https://doi.org/10.1021/nn1003937
H. He, J. Lin, W. Fu, X. Wang, H. Wang et al., MoS2/TiO2 edge-on heterostructure for efficient photocatalytic hydrogen evolution. Adv. Energy Mater. 6(14), 1600464 (2016). https://doi.org/10.1002/aenm.201600464
T.N. Trung, D.B. Seo, N.D. Quang, D. Kim, E.T. Kim, Enhanced photoelectrochemical activity in the heterostructure of vertically aligned few-layer MoS2 flakes on ZnO. Electrochim. Acta 260, 150–156 (2018). https://doi.org/10.1016/j.electacta.2017.11.089
D.B. Seo, S. Kim, T.N. Trung, D. Kim, E.T. Kim, Conformal growth of few-layer MoS2 flakes on closely-packed TiO2 nanowires and their enhanced photoelectrochemical reactivity. J. Alloys Compd. 770, 686–691 (2019). https://doi.org/10.1016/j.jallcom.2018.08.151
K. Chang, Z. Mei, T. Wang, Q. Kang, S. Ouyang, J. Ye, MoS2/graphene cocatalyst for efficient photocatalytic H2 evolution under visible light irradiation. ACS Nano 8(7), 7078–7087 (2014). https://doi.org/10.1021/nn5019945
F. Carraro, L. Calvillo, M. Cattelan, M. Favaro, M. Righetto et al., Fast one-pot synthesis of MoS2/crumpled graphene p–n nanojunctions for enhanced photoelectrochemical hydrogen production. ACS Appl. Mater. Interfaces 7(46), 25685–25692 (2015). https://doi.org/10.1021/acsami.5b06668
R.K. Biroju, D. Das, R. Sharma, S. Pal, L.P.L. Mawlong et al., Hydrogen evolution reaction activity of graphene–MoS2 van der waals heterostructures. ACS Energy Lett. 2(6), 1355–1361 (2017). https://doi.org/10.1021/acsenergylett.7b00349
Z. Huang, W. Han, H. Tang, L. Ren, D.S. Chander, X. Qi, H. Zhang, Photoelectrochemical-type sunlight photodetector based on MoS2/graphene heterostructure. 2D Mater. 2(3), 035011 (2015). https://doi.org/10.1088/2053-1583/2/3/035011
X. Yu, R. Du, B. Li, Y. Zhanga, H. Liu, J. Qu, X. An, Biomolecule-assisted self-assembly of CdS/MoS2/graphene hollow spheres as high-efficiency photocatalysts for hydrogen evolution without noble metals. Appl. Catal. B 182, 504–512 (2016). https://doi.org/10.1016/j.apcatb.2015.09.003
W. Zhou, K. Zhou, D. Hou, X. Liu, G. Li et al., Three-dimensional hierarchical frameworks based on MoS2 nanosheets self-assembled on graphene oxide for efficient electrocatalytic hydrogen evolution. ACS Appl. Mater. Interfaces 6(23), 21534–21540 (2014). https://doi.org/10.1021/am506545g
S. Linic, P. Christopher, D.B. Ingram, Plasmonic-metal nanostructures for efficient conversion of solar to chemical energy. Nat. Mater. 10, 911–921 (2011). https://doi.org/10.1038/nmat3151
S. Zu, B. Li, Y. Gong, Z. Li, P.M. Ajayan, Z. Fang, Active control of plasmon–exciton coupling in MoS2–Ag hybrid nanostructures. Adv. Opt. Mater. 4(10), 1463–1469 (2016). https://doi.org/10.1002/adom.201600188
A. Ali, F.A. Mangrio, X. Chen, Y. Dai, K. Chen et al., Ultrathin MoS2 nanosheets for high-performance photoelectrochemical applications via plasmonic coupling with Au nanocrystals. Nanoscale 11(16), 7813–7824 (2019). https://doi.org/10.1039/C8NR10320H
Y. Shi, J. Wang, C. Wang, T.-T. Zhai, W.-J. Bao et al., Hot electron of Au nanorods activates the electrocatalysis of hydrogen evolution on MoS2 nanosheets. J. Am. Chem. Soc. 137(23), 7365–7370 (2015). https://doi.org/10.1021/jacs.5b01732
Y. Kang, S. Najmaei, Z. Liu, Y. Bao, Y. Wang et al., Plasmonic hot electron induced structural phase transition in a MoS2 monolayer. Adv. Mater. 26(37), 6467–6471 (2014). https://doi.org/10.1002/adma.201401802
Y.H. Chiu, S.B. Naghadeh, S.A. Lindley, T.H. Lai, M.Y. Kuo et al., Yolk–shell nanostructures as an emerging photocatalyst paradigm for solar hydrogen generation. Nano Energy 62, 289–298 (2019). https://doi.org/10.1016/j.nanoen.2019.05.008
Y.H. Chiu, K.D. Chang, Y.J. Hsu, Plasmon-mediated charge dynamics and photoactivity enhancement for Au-decorated ZnO nanocrystals. J. Mater. Chem. A 6(10), 4286–4296 (2018). https://doi.org/10.1039/C7TA08543E
J.M. Li, H.Y. Cheng, Y.H. Chiua, Y.J. Hsu, ZnO–Au–SnO2 Z-scheme photoanodes for remarkable photoelectrochemical water splitting. Nanoscale 8(34), 15720–15729 (2016). https://doi.org/10.1039/C6NR05605A
Y.L. Huang, W.S. Chang, C.N. Van, H.J. Liu, K.A. Tsai et al., Tunable photoelectrochemical performance of Au/BiFeO3 heterostructure. Nanoscale 8(34), 15795–15801 (2016). https://doi.org/10.1039/C6NR04997D
C.N. Van, W.S. Chang, J.W. Chen, K.A. Tsai, W.Y. Tzeng et al., Heteroepitaxial approach to explore charge dynamics across Au/BiVO4 interface for photoactivity enhancement. Nano Energy 15, 625–633 (2015). https://doi.org/10.1016/j.nanoen.2015.05.024
Y.C. Chen, T.C. Liu, Y.J. Hsu, ZnSe·0.5N2H4 hybrid nanostructures: a promising alternative photocatalyst for solar conversion. ACS Appl. Mater. Interfaces 7(3), 1616–1623 (2015). https://doi.org/10.1021/am507085u
Y.C. Pu, G. Wang, K.D. Chang, Y. Ling, Y.K. Lin et al., Au nanostructure-decorated TiO2 nanowires exhibiting photoactivity across entire UV–visible region for photoelectrochemical water splitting. Nano Lett. 13(8), 3817–3823 (2013). https://doi.org/10.1021/nl4018385
K.H. Chen, Y.C. Pu, K.D. Chang, Y.F. Liang, C.M. Liu et al., Ag-nanoparticle-decorated SiO2 nanospheres exhibiting remarkable plasmon-mediated photocatalytic properties. J. Phys. Chem. C 116(35), 19039–19045 (2012). https://doi.org/10.1021/jp306555j
Y.Y. Li, J.H. Wang, Z.J. Luo, K. Chen, Z.Q. Cheng et al., Plasmon-enhanced photoelectrochemical current and hydrogen production of (MoS2–TiO2)/Au hybrids. Sci. Rep. 7, 7178 (2017). https://doi.org/10.1038/s41598-017-07601-1
L.V. Nang, E.T. Kim, Controllable synthesis of high-quality graphene using inductively-coupled plasma chemical vapor deposition. J. Electrochem. Soc. 159(4), K93–K96 (2012). https://doi.org/10.1149/2.082204jes
J. Jeon, S.K. Jang, S.M. Jeon, G. Yoo, Y.H. Jang, J.-H. Park, S. Lee, Layer-controlled CVD growth of large-area two-dimensional MoS2 films. Nanoscale 7(5), 1688–1695 (2015). https://doi.org/10.1039/C4NR04532G
C. Yim, M. O’Brien, N. McEvoy, S. Winters, I. Mirza, J.G. Lunney, G.S. Duesberg, Investigation of the optical properties of MoS2 thin films using spectroscopic ellipsometry. Appl. Phys. Lett. 104(10), 103114 (2014). https://doi.org/10.1063/1.4868108
L. Bai, X. Cai, J. Lu, L. Li, S. Zhong et al., Surface and interface engineering in Ag2S@MoS2 core–shell nanowire heterojunctions for enhanced visible photocatalytic hydrogen production. ChemCatChem 10(9), 2107–2114 (2018). https://doi.org/10.1002/cctc.201701998
P. Zuo, L. Jiang, X. Li, B. Li, P. Ran et al., Metal (Ag, Pt)–MoS2 hybrids greenly prepared through photochemical reduction of femtosecond laser pulses for SERS and HER. ACS Sustain. Chem. Eng. 6(6), 7704–7714 (2018). https://doi.org/10.1021/acssuschemeng.8b00579
J. Zhu, Z. Wang, H. Yu, N. Li, J. Zhang et al., Argon plasma induced phase transition in monolayer MoS2. J. Am. Chem. Soc. 139(30), 10216–10219 (2017). https://doi.org/10.1021/jacs.7b05765
J.D. Major, M. Al Turkestani, L. Bowen, M. Brossard, C. Li et al., In-depth analysis of chloride treatments for thin-film CdTe solar cells. Nat. Commun. 7, 13231 (2016). https://doi.org/10.1038/ncomms13231
G. Eda, H. Yamaguchi, D. Voiry, T. Fujita, M. Chen, M. Chhowalla, Photoluminescence from chemically exfoliated MoS2. Nano Lett. 11(12), 5111–5116 (2011). https://doi.org/10.1021/nl201874w
W.H. Lin, Y.H. Chiu, P.W. Shao, Y.J. Hsu, Metal-particle-decorated ZnO nanocrystals: photocatalysis and charge dynamics. ACS Appl. Mater. Interfaces 8(48), 32754–32763 (2016). https://doi.org/10.1021/acsami.6b08132
Y.C. Chen, Y.C. Pu, Y.J. Hsu, Interfacial charge carrier dynamics of the three-component In2O3 − TiO2 − Pt heterojunction system. J. Phys. Chem. C 116(4), 2967–2975 (2012). https://doi.org/10.1021/jp210033y
M. Jalali, R.S. Moakhar, T. Abdelfattah, E. Filine, S.S. Mahshid, S. Mahshid, Nanopattern-assisted direct growth of peony-like 3D MoS2/Au composite for nonenzymatic photoelectrochemical sensing. ACS Appl. Mater. Interfaces 12(6), 7411–7422 (2020). https://doi.org/10.1021/acsami.9b17449
K.K. Patra, C.S. Gopinath, Bimetallic and plasmonic Ag–Au on TiO2 for solar water splitting: an active nanocomposite for entire visible-light-region absorption. ChemCatChem 8(20), 3294–3301 (2016). https://doi.org/10.1002/cctc.201600937
C. Burda, X. Chen, R. Narayanan, M.A. El-Sayed, Chemistry and properties of nanocrystals of different shapes. Chem. Rev. 105(4), 1025–1102 (2005). https://doi.org/10.1021/cr030063a
H. Lee, S. Deshmukh, J. Wen, V.Z. Costa, J.S. Schuder et al., Layer-dependent interfacial transport and optoelectrical properties of MoS2 on ultraflat metals. ACS Appl. Mater. Interfaces 11(34), 31543–31550 (2019). https://doi.org/10.1021/acsami.9b09868
Y.J. Yu, Y. Zhao, S. Ryu, L.E. Brus, K.S. Kim, P. Kim, Tuning the graphene work function by electric field effect. Nano Lett. 9(10), 3430–3434 (2009). https://doi.org/10.1021/nl901572a
D. Cao, W. Luo, J. Feng, X. Zhao, Z. Lia, Z. Zou, Cathodic shift of onset potential for water oxidation on a Ti4+ doped Fe2O3 photoanode by suppressing the back reaction. Energy Environ. Sci. 7(2), 752–759 (2014). https://doi.org/10.1039/C3EE42722F
S.U.M. Khan, M. Al-Shahry, W.B. Ingler Jr., Efficient photochemical water splitting by a chemically modified n-TiO2. Science 297(5590), 2243–2245 (2002). https://doi.org/10.1126/science.1075035
X. Xu, G. Zhou, X. Dong, J. Hu, Interface band engineering charge transfer for 3D MoS2 photoanode to boost photoelectrochemical water splitting. ACS Sustain. Chem. Eng. 5(5), 3829–3836 (2017). https://doi.org/10.1021/acssuschemeng.6b02883
Y. Pi, Z. Li, D. Xu, J. Liu, Y. Li et al., 1T-phase MoS2 nanosheets on TiO2 nanorod arrays: 3D photoanode with extraordinary catalytic performance. ACS Sustain. Chem. Eng. 5(6), 5175–5182 (2017). https://doi.org/10.1021/acssuschemeng.7b00518
Q. Pan, C. Zhang, Y. Xiong, Q. Mi, D. Li et al., Boosting charge separation and transfer by plasmon-enhanced MoS2/BiVO4 p–n heterojunction composite for efficient photoelectrochemical water splitting. ACS Sustain. Chem. Eng. 6(5), 6378–6387 (2018). https://doi.org/10.1021/acssuschemeng.8b00170
L. Zeng, X. Li, S. Fan, M. Zhang, Z. Yin, M. Tadé, S. Liu, Photo-driven bioelectrochemical photocathode with polydopamine-coated TiO2 nanotubes for self-sustaining MoS2 synthesis to facilitate hydrogen evolution. J. Power Sources 413, 310–317 (2019). https://doi.org/10.1016/j.jpowsour.2018.12.054
S.J.A. Moniz, S.A. Shevlin, D.J. Martin, Z.-X. Guo, J. Tang, Visible-light driven heterojunction photocatalysts for water splitting—a critical review. Energy Environ. Sci. 8(3), 731–759 (2015). https://doi.org/10.1039/C4EE03271C
C. Jiang, S.J.A. Moniz, A. Wang, T. Zhang, J. Tang, Photoelectrochemical devices for solar water splitting–materials and challenges. Chem. Soc. Rev. 46(15), 4645–4660 (2017). https://doi.org/10.1039/C6CS00306K
Acknowledgements
This work was supported by the National Research Foundation of Korea (NRF) grants funded by the Ministry of Education (2020R1I1A3A04037241 and 2019R1A6A3A13095792) and the Korea Government (MSIT) (2020R1A4A4079397).
Author information
Authors and Affiliations
Corresponding author
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Seo, DB., Trung, T.N., Kim, DO. et al. Plasmonic Ag-Decorated Few-Layer MoS2 Nanosheets Vertically Grown on Graphene for Efficient Photoelectrochemical Water Splitting. Nano-Micro Lett. 12, 172 (2020). https://doi.org/10.1007/s40820-020-00512-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-020-00512-3