Highlights
-
3D Zn-doped CuO framework was designed for aligned distributing high mass loading of MnO2 nanosheets.
-
Zn could be introduced into the CuO crystal lattice to tune the covalency character and thus improve charge transport.
-
A free-standing asymmetric coaxial fiber-shaped supercapacitor based on Zn–CuO@MnO2 core electrode possesses superior performance including higher capacity and better stability under deformation.
Abstract
Coaxial fiber-shaped supercapacitors are a promising class of energy storage devices requiring high performance for flexible and miniature electronic devices. Yet, they are still struggling from inferior energy density, which comes from the limited choices in materials and structure used. Here, Zn-doped CuO nanowires were designed as 3D framework for aligned distributing high mass loading of MnO2 nanosheets. Zn could be introduced into the CuO crystal lattice to tune the covalency character and thus improve charge transport. The Zn–CuO@MnO2 as positive electrode obtained superior performance without sacrificing its areal and gravimetric capacitances with the increasing of mass loading of MnO2 due to 3D Zn–CuO framework enabling efficient electron transport. A novel category of free-standing asymmetric coaxial fiber-shaped supercapacitor based on Zn0.11CuO@MnO2 core electrode possesses superior specific capacitance and enhanced cell potential window. This asymmetric coaxial structure provides superior performance including higher capacity and better stability under deformation because of sufficient contact between the electrodes and electrolyte. Based on these advantages, the as-prepared asymmetric coaxial fiber-shaped supercapacitor exhibits a high specific capacitance of 296.6 mF cm−2 and energy density of 133.47 μWh cm−2. In addition, its capacitance retention reaches 76.57% after bending 10,000 times, which demonstrates as-prepared device’s excellent flexibility and long-term cycling stability.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
The multifunctional portable, wearable devices are a mainstream direction in electronics field and have attracted interesting attention in recent years [1]. These devices, including electrochemical supercapacitors, rechargeable secondary batteries, artificial skin sensors have been widely studied [2,3,4]. However, the conventional planar devices are not suitable for the application of flexible and wearable electronics. Fiber-shaped supercapacitors have a vital position as a new class of flexible power source because of lightweight, small volume, facility in the device application and integration in wearable electronics [5]. Nevertheless, their practical applications are still limited severely since inferior energy density is related to the narrow potential window and low capacitance. Therefore, substantial efforts have been made to improve the energy density via widening the overall potential voltage (V) and improvement of specific capacitance (C) [6].
Fabrication of asymmetric fiber-shaped supercapacitors (AFSC) is an effective strategy to enlarge the voltage window by assembling of two different types of electrode materials [5]. However, AFSC is comprised of two parallel fiber electrodes; it is difficult to realize free-standing because these fibers need to be placed onto substrates [7]. A twisted-type fiber supercapacitor was presented using plastic wire, polymer Kevlar fiber or carbon fiber, but, the effective connective surface area of the two electrodes was limited resulting in low specific capacitance, low energy density, as well as leakage current risk between electrodes during bending or stretchable process [8,9,10]. The asymmetric coaxial fiber-shaped supercapacitor (ACFSC) was designed by assembling two electrodes into a core–shell electrode structure with a fiber electrode core, an film electrode shell and an electrolyte material sandwiched in-between [11]. This coaxial structure provides superior performance including higher capacity and better stability under deformation because of sufficient contact between the electrodes and electrolyte. However, it is still a challenge to coat uniform films on a fiber core and retain the electrochemical stability under deformation.
Furthermore, besides the configuration of the electrodes, the active materials play the important role in improving the electrochemical performance of ACFSC. Among the rich pool of various pseudocapacitive materials, manganese oxide (MnO2) has attracted tremendous attention for its high theoretical specific capacitance, low cost, non-toxicity, wide availability, and environmental friendliness [12, 13]. Unfortunately, its inferior electrical conductivity (10–5 to 10–6 S cm−1) leading to limited specific capacitance and power capability generates an adverse influence in development of ACFSC with excellent electrochemical properties [14]. The prompting studies were boosted to fabricate MnO2 composite electrodes containing graphene, carbon nanotubes, and so on [15, 16]. However, probably because of the severe aggregation of active materials leading to the increasing of “dead” mass which unavoidably hinder the electron transfer, unsatisfied energy density still exists in the carbon/MnO2 hybrid composite structure as ACFSC electrode materials. In addition, the thin film structure or a small active material loading (0.1–0.8 mg cm−2) on the substrates is generally required to achieve satisfactory electrochemical properties because of the redox reaction occurring only in a few nanometers of electrode surface [13]. With the increasing MnO2 mass loading, the capacitive performance was found to deteriorate severely due to slow ion diffusion and inefficient electron transport. Thus, the cycling stability and rate capacity are also impacted seriously resulting in hindering the further application as ACFSC electrode materials. A typical MnO2 mass loading of 8–10 mg cm−2 is required to provide necessary capacitance for commercial SC [17]. Deposition of MnO2 onto three-dimensional conductive scaffold, including carbon, metal oxide or metal nanomaterials, has been proven to be an effective way to obtain larger electroactive surface area and the short diffusion routes for electrons and ions in the electrolyte [18,19,20,21,22]. Carbon nanomaterials, such as carbon nanotube, graphene and porous carbon, were usually used as 3D conductive skeletons which displays the superior electrochemical performance owing to the smart hybrid structure and synergistic effect [23, 24]. However, probably because of the mixture of conductive additive or polymer binder leading to the increasing of “dead” mass which unavoidably hinder the electron transfer, unsatisfied energy density still exists in the carbon/metal oxide/hydroxide hybrid composite structure as fiber-shaped electrode. Metal nanomaterials with high electrical conductivity have been developed as 3D conductive support such as porous gold, copper nanowires, porous Ni, but there is almost no capacitance contributing during electrochemical charge and discharge process [20, 21]. However, there are few reports to design a 3D scaffold with high performance for homogeneous distribution of active materials toward free-standing hybrid electrode for ACFSC.
Herein, we report the rational design and growth of Zn–CuO@MnO2 core–shell nanowire arrays as high-performance positive electrode for ACFSC. In situ Zn-doped CuO nanowires on Cu wire were one-step grown and designed as skeletons for aligned distributing MnO2 nanosheets. The electrical conductivity of Zn doped into the lattice of CuO was improved by several magnitude compared with pristine CuO nanowires, which enables efficient electron transport in the redox reactions of MnO2 nanosheets. Meanwhile, Zn-doped CuO also contributes electrochemical capacitance for MnO2 composite electrode. Zn0.11CuO with MnO2 loading of 12.4 mg cm−2 achieves a high areal capacitance of 4.26 F cm−2 (33.2 F g−1). Zn0.11CuO@MnO2 as core positive electrode could be assessed as a new category of free-standing ACFSC positive electrode associated with high specific capacitance and stability cycling performance. Vanadium nitride (VN) nanowire arrays grown on carbon nanotubes film (CNF) were wrapped uniformly on the core positive electrode as negative electrode to form the coaxial construction devices. The as-prepared ACFSC exhibits a maximum operating voltage window of 1.8 V, a high specific capacitance of 107.95 F cm−3 (296.6 mF cm−2), energy density of 133.5 mWh cm−2 (at a power density of 0.9 mW cm−2) and power density of 8.9 mW cm−2 (at an energy density of 68.7 mWh cm−2), which demonstrates as-prepared device could be a promising candidate for potential uses in high-performance ACFSC.
2 Experimental Section
2.1 Synthesis of Zn–CuO@MnO2 Core–Shell Nanowires on Cu Wires
First, copper wires were cleaned using ethanol and acetone solution with ultrasound for 10 min, respectively. Copper wires were annealed at 600 °C for 30 min in Ar to remove the oxide layer on the surface of copper. The samples were then immersed into Zn(CH3COO)2 aqueous solutions with varied concentration (0.05 ~ 1 M). Then, the samples were put into oven at 60 °C for 30 min to evaporate the moisture. Next, the samples were heated in air from room temperature to 500 °C with 2 °C min−1 and kept at 500 °C for 4 h in tube furnace to grow the Zn-doped CuO nanowires. CuO nanowires grown onto Cu wires were fabricated by the same method without using Zn(CH3COO)2 solutions. MnO2 nanosheets were grown onto the Zn-doped CuO/Cu nanowires via a facile electrodeposition method in a mixed aqueous solution of 0.05 M MnSO4, 0.05 M CH3COONa, and 10% vol ethanol with a current density of 5 mA cm−2.
2.2 Fabrication of All-Solid-State ACFSC Device
VN nanowires array was synthesized on CNT film by our previous method [25]. The Na2SO4/PVA sol–gel electrolyte was firstly prepared by mixing 10 g of PVA and 10 g of Na2SO4 into 100 mL of deionized water under vigorous stirring at 85 °C for 2 h. The Zn–CuO@MnO2 core–shell nanowires on Cu wires electrode were soaked into the Na2SO4/PVA sol–gel electrolyte for 5 min and then maintained at 60 °C for 2 h to evaporate excess moisture. After the gel electrolyte was dried, the aligned VN@CNT film was wrapped around core electrode. The area of the VN@CNT film could be easily adjusted by changing the helical angle. The gel electrolyte was then coated onto the outside of ACFSC.
2.3 Characterization
Scanning electron microscopy (SEM) was carried out using Hitachi S–4800 with an accelerating voltage of 3 kV. X-ray diffraction (XRD) patterns were obtained using a Rigaku D/MAX2500 V with Cu Kα radiation (λ = 1.5418 Å). X-ray photoelectron spectroscopy (XPS) patterns were acquired an ESCALab MKII X-ray photoelectron spectrometer with non-monochromatized Mg Kα X-rays as the excitation source. Inductively coupled plasma emission spectrometer (ICP) data were obtained by Agilent 5100 to confirm the mass of Zn-doped CuO lattice. High-resolution transmission electron microscopy (HRTEM) and energy dispersive X-ray (EDX) elemental mapping images were acquired by a FEI TECNAI G2 20 high resolution TEM (200 kV). Electrochemical measurements were taken on the CHI 760e electrochemical working station.
3 Results and Discussion
The fabrication process of the ACFSC device is schematically displayed in Fig. 1. First, Zn–CuO nanowires were fabricated by annealing Cu wire covering Zn ions in air in tube furnace (Fig. 1a). Then, MnO2 nanosheets were grown onto the Zn–CuO/Cu wire via a facile electrodeposition method in a mixed aqueous solution of MnSO4, CH3COONa, and ethanol with a current density of 5 mA cm−2 (Fig. 1b). The positive core electrode was coated with a thin layer of poly(vinyl alcohol) (PVA) gel electrolyte including Na2SO4 as gel electrolyte and separator (Fig. 1c). VN nanowire arrays were synthesized on the CNT film as negative electrode shown in Fig. 1e. Afterward, it was wrapped around the positive electrode (inner core electrode) whose two ends were immobilized on two motors while the motors were rotating (Fig. 1f). Finally, the second layer of PVA gel electrolyte was coated on the outside of ACFSC. The cross-profile of ACFSC device is illustrated in Fig. 1g, demonstrating that the aligned structure probably favored the rapid charge transport and diffusion of electrolyte ions.
The X-ray diffraction (XRD) patterns of the as-prepared CuO and Zn–CuO with different molar concentration of dopant are displayed in Fig. S1. The pattern of pure CuO phase shows a typical diffraction peaks at 2θ of 35.85, 38.96, 48.89, 61.56, 66.38, and 68.16, corresponding to (\(\overline{1}11\)), (200), (\(\overline{2}02\)), (\(\overline{1}13\)), (\(\overline{3}11\)), and (220) reflection planes of monoclinic crystalline CuO. The pattern of Zn–CuO nanowires shows that there is no trace of Zn or its compounds, indicating dopants are well integrated into CuO lattice structure during the growth process. The peaks of Zn–CuO are found to be wider than those of CuO, indicating the existence of asymmetry crystalline structure after doping. Meanwhile, the position of peaks slightly shifted toward higher angles for Zn0.05CuO, Zn0.08CuO, Zn0.11CuO and slightly shifted toward lower angles with further increasing of Zn dopants for Zn0.15CuO, Zn0.28CuO because Zn substitution generates residual stress that might result in anisotropic shrinkage of lattices and then induce lattice distortion. Tensile stress brings about diffraction planes shift of lower angle, while pressure stress can cause the shift to higher angles [26]. The electric conductive properties of ZnCuO were improved greatly compared with pure CuO. The sample of Zn0.11CuO shows the superior electrical conductivity of compared with other samples (Fig. S2). Therefore, Zn0.11CuO was chosen as conductive skeleton to support the deposition of MnO2 nanosheets. The chemical compositions and valence states of the Zn0.11CuO@MnO2 were investigated using XRD patterns. Compared with the XRD pattern of Zn0.11CuO nanowires, new peaks at 12.8°, 60.2o are attributed to MnO2 (JCPDF No. 44–0141) (Fig. S3).
The XPS data of CuO and Zn–CuO are displayed in Fig. S4. It is found that the intensity of O 1s of 531.5 eV binding energy of Zn–CuO is more than that of CuO sample, demonstrating oxygen vacancies increase after Zn doping into CuO. The main reason is probably that enhances pseudocapacitive charge storage properties of Zn–CuO. The detailed analysis is exhibited in the supporting information. The XPS peaks of Cu 2p at 934.5 and 954.2 eV are assigned to Cu 2p3/2 and Cu 2p1/2, illustrating the presence of the Cu2+ for Zn0.11CuO@MnO2 sample (Fig. 2a) [27,28,29]. The XPS spectrum of Zn 2p displays a peak centered at 1044.21 and 1021.15 eV that is attributed to Zn 2p1/2 and Zn 2p3/2, demonstrating that is present Zn2+ (Fig. 2b) [30]. The Mn 2p XPS spectrum reveals Mn 2p3/2 peak Mn 2p1/2 peak at binding energy of 642.6 and 653.4 eV, indicating the presence of Mn4+ (Fig. 2c) [17, 31]. The O 1s binding energies of 529.8 and 531.5 eV are the main components typical for oxygen in Zn0.11CuO@MnO2 (Fig. 2d).
The morphology and crystalline structure of the CuO nanowire, Zn0.11CuO nanowires and Zn0.11CuO@MnO2 core–shell heterostructure were characterized by SEM and TEM. The different magnification SEM images of the Zn0.11CuO nanowire arrays on the surface of Cu wire in Fig. 3a–c reveal that the uniformly distributed nanowire arrays on the surface of Cu wire when heated at 500 °C for 4 h. The average diameter of Zn0.11CuO nanowire arrays is 100 nm, and lengths are from 100 to 200 nm. The SEM images of MnO2 nanosheets deposited onto the Zn0.11CuO nanowires are shown in Fig. 3d–f. It is found that the plenty of uniform and ultrathin MnO2 nanosheets are aligned distributed on the surface of ZnCuO nanowires, forming the perfect 3D configuration with a reasonable space between the adjacent nanowire arrays. The thickness of MnO2 layer on the Zn0.11CuO increases with the electrodeposition time, as shown in Fig. S5. TEM images provide further insight into detailed structure of CuO, Zn0.11CuO and Zn0.11CuO@MnO2 heterostructure nanowire arrays shown in Fig. S6. Figure 2g clearly displays that internal nanowire structure with the diameter of ~ 80 nm is covered by the interconnected tiny nanosheets. These ultrathin nanosheets increase the specific surface area of electrode materials. EDX elemental mapping images totally confirm the hierarchical core–shell structure in which Cu, Zn, and O are uniformly distributed in the internal structure and Mn and O are distributed in the external structure. The EDX spectrum in Fig. 2h shows several elements such as Cu, Zn, Mn, and O appeared in the hierarchical structure without any impurities. The C is believed from the TEM grid with ultrathin carbon film. These results illustrate the significance of using ZnCuO as skeletons in achieving a uniform coating of MnO2 at high mass loading and verify the successful integration of 3D highly conductive ZnCuO and MnO2 ultrathin nanosheets.
The electrochemical properties of electrodes were investigated in a three-electrode system in 1 M Na2SO4 aqueous electrolyte. The effect of the content of Zn on the capacitive performance of Zn–CuO electrodes is shown in Fig. S7. It is observed that there is no obvious trend for capacitance change of Zn–doped CuO electrodes with increasing contents of Zn. The detailed analysis and charge transfer mechanism are described in Supporting Information. The galvanostatic charge–discharge (GCD) curves of CuO, Zn0.11CuO, CuO@MnO2 and Zn0.11CuO@MnO2 electrodes at a current density of 2 mA cm−2 over a potential range from 0 to 0.6 V are shown in Fig. 4a. Zn0.11CuO nanowires electrode has the longer discharge time than pure CuO, illustrating Zn doping into CuO could effectively reduce the overall resistance and improve electron collection rates and the charge transport during electrochemical reaction. When the deposition time of MnO2 on Zn–CuO is just 5 min with a loading of 1.9 mg cm−2, the discharge time of electrode is significantly increased compared to CuO, Zn–CuO, CuO@MnO2. The specific capacitance was calculated, and the corresponding results of these electrodes are plotted in Fig. 4b, according to Eq. S1. The areal capacitance of Zn0.11CuO@MnO2 electrodes is 2.2 F cm−2 which is larger than that of CuO, Zn0.11CuO, even CuO@MnO2 electrodes at current density of 2 mA cm−2. The internal resistances (IR) of these electrodes are associated with the electrical conductivity of materials, which is proportional to the potential drop of charge and discharge curves. The potential drop of Zn0.11CuO electrode is about 0.0018 V, which is more 30 times lower than that of the CuO electrode (the potential drop is 0.0636 V) at a current density of 2 mA cm−2. Although the potential drop of core–shell electrode is increased slightly after the deposition of MnO2 due to its poor electrical conductivity, it is still much less than CuO@MnO2 electrodes. These results illustrate that ion diffusion and charge transfer in these 3D Zn0.11CuO@MnO2 core–shell electrodes are highly rapid and efficient during charge and discharge process. Different mass loading of MnO2 nanosheets on the Zn0.11CuO was studied by varying deposition time of 5, 10, 15, 20, and 30 min (Fig. S8). It allows precise control of mass loading of MnO2 ultrathin nanosheets on 3D Zn–CuO skeleton, because it is linear relationship between deposition time and mass loading of MnO2 (Fig. 4c). The high loading mass of 12.4 mg cm−2 MnO2 nanosheets was obtained after 30 min deposition. With the increasing of MnO2 loading, the areal capacitance of the Zn0.11CuO@MnO2 electrode also increases at different current densities (Fig. 4d). The capacitance of Zn0.11CuO@MnO2 electrode with the loading mass of 12.4 mg at current density of 10 mA cm−2 (2.88 F cm−2) corresponds to 68% capacitance retention relative to that of 1 mA cm−2, which indicates the superior rate capability of hierarchical 3D core–shell electrode. And when the loading mass of MnO2 increased from 1.9 to 12.4 mg cm−2, the gravimetric capacitances of Zn0.11CuO@MnO2 electrode decrease slightly (Fig. 4e). Therefore, this advanced 3D Zn0.11CuO@MnO2 core–shell electrode supports the long-term cyclic sustainability (Fig. 4f). The 87.6% capacitance of the 3D core–shell electrode is retained after 10,000 cycles at a current density of 10 mA cm−2. When the deposition time of MnO2 was further increased, it rendered to touch each other between the adjacent nanowires to form a dense block area and reducing the effective contactable surface area leading to inferior electrochemical performance; corresponding SEM images and electrochemical properties are shown in Fig. S9. The electrochemical impedance spectroscopy (EIS) studies were conducted and are shown in Fig. S10. These results illustrate that Zn0.11CuO@MnO2 possesses the lowest charge-transfer and series resistances which contribute to its large capacitance and good rate capability.
Then, the ACFSC was successfully assembled by wrapping the VN on CNT film around the positive electrode (inner electrode), which is displayed in Figs. S11 and S12 by corresponding low- and high-magnification SEM images. The potential windows of the VN/CNT film and Zn0.11CuO@MnO2 electrodes were − 1.2 to − 0.2 V and 0 to 0.6 V, respectively (Fig. 5a). Therefore, the maximum voltages window for the asymmetric supercapacitor could reach 1.8 V. The GCD curves were also tested at a current density of 2 mA cm−2 with different potential window from 0.4 to 1.8 V and displayed nearly triangular shape at a potential window as high as 1.8 V, indicating the ideal electrochemical capacitance characteristics and reversible Faradaic reaction (Fig. 5b). A series of CV curves for the asymmetric coaxial device was measured at various scan rates from 5 to 100 mV s− (Fig. 5c) and reveal quasi-rectangular shape of CV shapes without obvious redox peaks when the potential increases to 1.8 V, implying good high-rate performance. The GCD curves of the ACFSC device were measured between 0 and 1.8 V for the current densities from 2 to 10 mA cm−2 (Fig. 5d). These curves are linear that illustrates which this coaxial fiber-shaped device displays ideal capacitive properties and low equivalent series resistance. The areal and volumetric capacitances of as-fabricated ACFSC device were calculated and plotted as a function of current density from 1 to 10 mA cm−2 (Fig. 5e). It is worth noting that the device can achieve a very high volumetric capacitance of 107.9 F cm−3 (296.6 mF cm−2) at a current density of 1 mA cm−2 and 55.6 mF cm−3 (152.7 F cm−2) at 10 mA cm−2, indicating its excellent rate performance. For ACFSC device, the energy density (E) and power density (P) which are two important parameters for evaluating the electrochemical performance, were calculated from GCD curves and plotted on the Ragone diagram (Fig. 5f). Notably, with the volumetric capacitance of 107.95 F cm−3, our ACFSC device illustrates a high volumetric energy density of 48.53 mWh cm−3 and volumetric power density of 327.2 mW cm−3 obtained. These values are much greater than those of some recently reported FSC devices, such as MoS2@rGO@CNT [32], Au-MnO2@CoNi@CNT [33], Ni wire@PPy [34], MnO2@CNT [35], Fe2O3@C [36], and Cu@AuPd@MnO2 [37]. A Ragone plot, representing the relationship between the energy density and power density of the ACFSC device, is shown in Fig. S13, illustrating a high areal energy density of 133.5 µWh cm−2 and an areal power density of 0.9 mW cm−2 obtained at a current density of 2 mA cm−2. These values are much higher than those of some recently reported FSC devices and MnO2 supercapacitors, such as CNT@MnO2 AFSC [32], CNT@NiO@MnOx FSC [38], nickel–cobalt layered double hydroxide FSC [39], carbon fiber@MnO2 supercapacitors [40], carbon fabric@MnO2 micro-supercapacitor [41], zinc–nickel–cobalt ternary oxides AFSC [42], MnO2@PEDOT:PSS@CNT FSC [43], conductive polymer@RuO2 FSC [44], (PEDOT:PSS)/PPy FSC [45], and MnO2 NBs@Ni/CNT coaxial FSC [46].
To further explore their application in flexible electronics, the mechanical stability of the ACFSC devices was investigated under different bending states as shown in Fig. 6a. It is worth noting that all the GCD curves observed at various bending states are no obvious distortion, indicating that the ACFSC device has excellent mechanical stability (Fig. 6b). The long-term cyclic stability and durability of the ACFSC device were further confirmed and are shown in Fig. 6c. It displays that as-prepared ACFSC device retains 76.57% of the initial capacitance after 10,000 charge and discharge cycles at the current density of 10 mA cm−2, which illustrates the excellent bending cycle stability of our ACFSC devices. The capacitances of device gradually decrease because the electrode materials are destroyed after several electrochemical redox reactions. A yellow light-emitting diode (LED) is powered by ACFSC device shown in inset of Fig. 6c, indicating the feasibility and potential application of the device. Accordingly, two full charged ACFSC devices woven into a cloth to light the LED, shown in Fig. 6d; it can give the light continuously for 60 s. These results illustrate that ACFSC device using Zn0.11CuO@MnO2 and VN/CNT film as positive and negative electrodes with high energy storage and good flexible could be applied in wearable electronics as an advanced power source.
4 Conclusions
In summary, we designed Zn–CuO nanowire arrays as 3D skeletons for the coating of MnO2 as core positive electrode. After Zn doped into the lattice of CuO, the electrical conductivity of Zn–CuO nanowire arrays is increased which provides the rapid route for electron transfer during electrochemical charge and discharge process. Benefiting from the nanowire arrays structure of Zn–CuO, it allows the superior high mass loading pseudocapacitive material without decreasing the gravimetric and areal capacitance. Furthermore, VN nanorods fabricated on CNT film were wrapped onto the core positive electrode to form an asymmetric coaxial ACFSC, which increases the connective surface area and decreases the contact resistance between two electrodes. Also, it could be assessed as a new category of free-standing ACFSC electrode associated with high specific capacitance and stability cycling performance. The as-prepared ACFSC exhibits a high specific capacitance of 107.9 F cm−3 (296.6 mF cm−2) and energy density of 48.53 mWh cm−3. In addition, its capacitance retention reaches 88.45% after bending 3000 cycles, which demonstrates excellent flexibility of our prepared device. With the advantage of excellent energy storage performance and flexibility, the ACFSC device designed in this paper is expected to be integrated into wearable electronics systems.
References
A.M. Zamarayeva, A.E. Ostfeld, M. Wang, J.K. Duey, I. Deckman et al., Flexible and stretchable power sources for wearable electronics. Sci. Adv. 3, e1602051 (2017). https://doi.org/10.1126/sciadv.1602051
C. Choi, K.M. Kim, K.J. Kim, X. Lepró, G.M. Spinks, R.H. Baughman, S.J. Kim, Improvement of system capacitance via weavable superelastic biscrolled yarn supercapacitors. Nat. Commun. 7, 13811 (2016). https://doi.org/10.1038/ncomms13811
V. Strauss, K. Marsh, M.D. Kowal, M. El-Kady, R.B. Kaner, A simple route to porous graphene from carbon nanodots for supercapacitor applications. Adv. Mater. 30, 1704449 (2018). https://doi.org/10.1002/adma.201704449
D. Son, J. Kang, O. Vardoulis, Y. Kim, N. Matsuhisa et al., An integrated self-healable electronic skin system fabricated via dynamic reconstruction of a nanostructured conducting network. Nat. Nanotechnol. 13, 1057–1065 (2018). https://doi.org/10.1038/s41565-018-0244-6
X. Wang, Q. Zhang, J. Sun, Z. Zhou, Q. Li et al., Facile synthesis of hierarchical porous manganese nickel cobalt sulfide nanotube arrays with enhanced electrochemical performance for ultrahigh energy density fiber-shaped asymmetric supercapacitors. J. Mater. Chem. A 6, 8030–8038 (2018). https://doi.org/10.1039/C8TA01440J
G. Sun, X. Zhang, R. Lin, J. Yang, H. Zhang, P. Chen, Hybrid fibers made of molybdenum disulfide, reduced graphene oxide, and multi-walled carbon nanotubes for solid-state, flexible, asymmetric supercapacitors. Angew. Chem. Int. Ed. 54, 4651–4656 (2015). https://doi.org/10.1002/anie.201411533
T. Chen, L. Qiu, Z. Yang, Z. Cai, J. Ren et al., An integrated “energy wire” for both photoelectric conversion and energy storage. Angew. Chem. Int. Ed. 51, 11977–11980 (2012). https://doi.org/10.1002/anie.201207023
J. Bae, M.K. Song, Y.J. Park, J.M. Kim, M. Liu, Z.L. Wang, Fiber supercapacitors made of nanowire-fiber hybrid structures for wearable/flexible energy storage. Angew. Chem. Int. Ed. 50, 1683–1687 (2011). https://doi.org/10.1002/anie.201006062
X. Lu, Y. Bai, R. Wang, J. Sun, A high-performance flexible and weavable asymmetric fiber-shaped solid-state supercapacitor enhanced by surface modifications of carbon fibers with carbon nanotubes. J. Mater. Chem. A 4, 18164–18173 (2016). https://doi.org/10.1039/C6TA08233E
X. Dong, Z. Guo, Y. Song, M. Hou, J. Wang, Y. Wang, Y. Xia, Flexible and wire-shaped micro-supercapacitor based on Ni(OH)2-nanowire and ordered mesoporous carbon electrodes. Adv. Funct. Mater. 24, 3405–3412 (2014). https://doi.org/10.1002/adfm.201304001
Q. Zhang, X. Wang, Z. Pan, J. Sun, J. Zhao et al., Wrapping aligned carbon nanotube composite sheets around vanadium nitride nanowire arrays for asymmetric coaxial fiber-shaped supercapacitors with ultrahigh energy density. Nano Lett. 17, 2719–2726 (2017). https://doi.org/10.1021/acs.nanolett.7b00854
Y. Zhang, B. Wang, F. Liu, J. Cheng, X.W. Zhang, L. Zhang, Full synergistic contribution of electrodeposited three-dimensional NiCO2O4@MnO2 nanosheet networks electrode for asymmetric supercapacitors. Nano Energy 27, 627–637 (2016). https://doi.org/10.1016/j.nanoen.2016.08.013
N. Liu, Y. Su, Z. Wang, Z. Wang, J. Xia et al., Electrostatic-interaction-assisted construction of 3D networks of manganese dioxide nanosheets for flexible high-performance solid-state asymmetric supercapacitors. ACS Nano 11, 7879–7888 (2017). https://doi.org/10.1021/acsnano.7b02344
P. Gao, P. Metz, T. Hey, Y. Gong, D. Liu et al., The critical role of point defects in improving the specific capacitance of δ-MnO2 nanosheets. Nat. Commun. 8, 14559 (2017). https://doi.org/10.1038/ncomms14559
J. Zhu, J. He, Facile synthesis of graphene-wrapped honeycomb MnO2 nanospheres and their application in supercapacitors. ACS Appl. Mater. Interfaces 4, 1770–1776 (2012). https://doi.org/10.1021/am3000165
S.W. Lee, J. Kim, S. Chen, P.T. Hammond, Y. Shao-Horn, Carbon nanotube/manganese oxide ultrathin film electrodes for electrochemical capacitors. ACS Nano 4, 3889–3896 (2010). https://doi.org/10.1021/nn100681d
Z.H. Huang, Y. Song, D.-Y. Feng, Z. Sun, X. Sun, X.X. Liu, High mass loading MnO2 with hierarchical nanostructures for supercapacitors. ACS Nano 12, 3557–3567 (2018). https://doi.org/10.1021/acsnano.8b00621
L. Han, P. Tang, L. Zhang, Hierarchical Co3O4@ppy@MnO2 core–shell–shell nanowire arrays for enhanced electrochemical energy storage. Nano Energy 7, 42–51 (2014). https://doi.org/10.1016/j.nanoen.2014.04.014
X. Lu, T. Zhai, X. Zhang, Y. Shen, L. Yuan et al., WO3-x@Au@MnO2 core–shell nanowires on carbon fabric for high-performance flexible supercapacitors. Adv. Mater. 24, 938–944 (2012). https://doi.org/10.1002/adma.201104113
H. Xu, X. Hu, Y. Sun, H. Yang, X. Liu, Y. Huang, Flexible fiber-shaped supercapacitors based on hierarchically nanostructured composite electrodes. Nano Res. 8, 1148–1158 (2015). https://doi.org/10.1007/s12274-014-0595-8
L. Yu, H. Zhou, J. Sun, F. Qin, F. Yu et al., Cu nanowires shelled with NiFe layered double hydroxide nanosheets as bifunctional electrocatalysts for overall water splitting. Energy Environ. Sci. 10, 1820–1827 (2017). https://doi.org/10.1039/C7EE01571B
Z. Pan, Y. Qiu, J. Yang, F. Ye, Y. Xu et al., Ultra-endurance flexible all-solid-state asymmetric supercapacitors based on three-dimensionally coated mnox nanosheets on nanoporous current collectors. Nano Energy 26, 610–619 (2016). https://doi.org/10.1016/j.nanoen.2016.05.053
D. Kong, C. Cheng, Y. Wang, J. Wong, Y. Yang, H. Yang, Three-dimensional Co3O4@C@Ni3S2 sandwich-structured nanoneedle arrays: towards high-performance flexible all-solid-state asymmetric supercapacitors. J. Mater. Chem. A 3, 16150–16161 (2015). https://doi.org/10.1039/c5ta03469h
Z. Zhang, F. Xiao, S. Wang, Hierarchically structured MnO2/graphene/carbon fiber and porous graphene hydrogel wrapped copper wire for fiber-based flexible all-solid-state asymmetric supercapacitors. J. Mater. Chem. A 3, 11215–11223 (2015). https://doi.org/10.1039/c5ta02331a
X. Wang, J. Sun, J. Zhao, Z. Zhou, Q. Zhang, C.P. Wong, Y. Yao, All-solid-state fiber-shaped asymmetric supercapacitors with ultrahigh energy density based on porous vanadium nitride nanowires and ultrathin Ni(OH)2 nanosheet wrapped NiCo2O4 nanowires arrays electrode. J. Phys. Chem. C 123, 985–993 (2019). https://doi.org/10.1021/acs.jpcc.8b05862
R.O. Yathisha, Y. Arthoba Nayaka, Structural, optical and electrical properties of zinc incorporated copper oxide nanoparticles: Doping effect of Zn. J. Mater. Sci. 53, 678–691 (2018). https://doi.org/10.1007/s10853-017-1496-5
Z. Li, M. Shao, L. Zhou, R. Zhang, C. Zhang et al., A flexible all-solid-state micro-supercapacitor based on hierarchical CuO@layered double hydroxide core–shell nanoarrays. Nano Energy 20, 294–304 (2016). https://doi.org/10.1016/j.nanoen.2015.12.030
M. Huang, Y. Zhang, F. Li, Z.A. Wang et al., Merging of kirkendall growth and ostwald ripening: CuO@MnO2 core-shell architectures for asymmetric supercapacitors. Sci. Rep. 4, 4518 (2014). https://doi.org/10.1038/srep04518
T. Wen, X.L. Wu, S. Zhang, X. Wang, A.W. Xu, Core–shell carbon-coated CuO nanocomposites: a highly stable electrode material for supercapacitors and lithium-ion batteries. Chem. Asian J. 10, 595–601 (2015). https://doi.org/10.1002/asia.201403295
A.K. Jyoti, G.D. Srivastava, Varma, highly selective and efficient room temperature NO2 gas sensors based on Zn-doped CuO nanostructure-rGo hybrid. J. Mater. Sci. Mater. E 29, 10640 (2018). https://doi.org/10.1007/s10854-018-9128-7
N. Yu, H. Yin, W. Zhang, Y. Liu, Z. Tang, M.Q. Zhu, High-performance fiber-shaped all-solid-state asymmetric supercapacitors based on ultrathin MnO2 nanosheet/carbon fiber cathodes for wearable electronics. Adv. Energy Mater. 6, 1501458 (2016). https://doi.org/10.1002/aenm.201501458
J. Yu, W. Lu, J.P. Smith, K.S. Booksh, L. Meng et al., A high performance stretchable asymmetric fiber-shaped supercapacitor with a core-sheath helical structure. Adv. Energy Mater. 7, 1600976 (2017). https://doi.org/10.1002/aenm.201600976
Z. Pan, J. Zhong, Q. Zhang, J. Yang, Y. Qiu et al., Ultrafast all-solid-state coaxial asymmetric fiber supercapacitors with a high volumetric energy density. Adv. Energy Mater. 8, 1702946 (2018). https://doi.org/10.1002/aenm.201702946
L. Li, Z. Lou, D. Chen, W. Han, G. Shen, Hollow polypyrrole sleeve based coaxial fiber supercapacitors for wearable integrated photosensing system. Adv. Mater. Technol. 3, 1800115 (2018). https://doi.org/10.1002/admt.201800115
B. Patil, S. Ahn, S. Yu, H. Song, Y. Jeong, J.H. Kim, H. Ahn, Electrochemical performance of a coaxial fiber-shaped asymmetric supercapacitor based on nanostructured MnO2/CNT-web paper and Fe2O3/carbon fiber electrodes. Carbon 134, 366–375 (2018). https://doi.org/10.1016/j.carbon.2018.03.080
Z. Yu, J. Moore, J. Calderon, L. Zhai, J. Thomas, Coil-type asymmetric supercapacitor electrical cables. Small 11, 5289–5295 (2015). https://doi.org/10.1002/smll.201501802
Z. Yu, J. Thomas, Energy storing electrical cables: Integrating energy storage and electrical conduction. Adv. Mater. 26, 4279–4285 (2014). https://doi.org/10.1002/adma.201400440
H. Yuan, G. Wang, Y. Zhao, Y. Liu, Y. Wu, Y. Zhang, A stretchable, asymmetric, coaxial fiber-shaped supercapacitor for wearable electronics. Nano Res. 13, 1686–1692 (2020). https://doi.org/10.1007/s12274-020-2793-x
T.S. Le, T.K. Truong, V.N. Huynh, J. Bae, D. Suh, Synergetic design of enlarged surface area and pseudo-capacitance for fiber-shaped supercapacitor yarn. Nano Energy 67, 104198 (2020). https://doi.org/10.1016/j.nanoen.2019.104198
A. Rafique, A. Massa, M. Fontana, S. Bianco, A. Chiodoni et al., Highly uniform anodically deposited film of MnO2 nanoflakes on carbon fibers for flexible and wearable fiber-shaped Supercapacitors. ACS Appl. Mater. Interfaces 9, 28386 (2017). https://doi.org/10.1021/acsami.7b06311
P. Zhang, Y. Li, G. Wang, F. Wang, S. Yang et al., Zn-ion hybrid micro-supercapacitors with ultrahigh areal energy density and long-term durability. Adv. Mater. 31, 1806005 (2019). https://doi.org/10.1002/adma.201806005
J. Guoa, Q. Zhang, J. Sun, C. Li, J. Zhao et al., Direct growth of vanadium nitride nanosheets on carbon nanotube fibers as novel negative electrodes for high-energy-density wearable fiber-shaped asymmetric supercapacitors. J. Power Sources 382, 122–127 (2018). https://doi.org/10.1016/j.jpowsour.2018.02.034
Q. Zhang, J. Sun, Z. Pan, J. Zhang, J. Zhao et al., Stretchable fiber-shaped asymmetric supercapacitors with ultrahigh energy density. Nano Energy 39, 219–228 (2017). https://doi.org/10.1016/j.nanoen.2017.06.052
Z. Wang, J. Cheng, J. Zhou, J. Zhang, H. Huang et al., All-climate aqueous fiber-shaped supercapacitors with record areal energy density and high safety. Nano Energy 50, 106–117 (2018). https://doi.org/10.1016/j.nanoen.2018.05.029
W. Teng, Q. Zhou, X. Wang, H. Che, P. Hu, H. Li, J. Wang, Hierarchically interconnected conducting polymer hybrid fiber with high specific capacitance for flexible fiber-shaped supercapacitor. Chem. Eng. J. 390, 124569 (2020). https://doi.org/10.1016/j.cej.2020.124569
J. Zhao, L. Li, Y. Zhang, C. Li, Q. Zhang et al., Novel coaxial fiber-shaped sensing system integrated with an asymmetric supercapacitor and a humidity sensor. Energy Storage Mater. 15, 315–323 (2018). https://doi.org/10.1016/j.ensm.2018.06.007
Acknowledgements
The authors thank financial supports from the National Natural Science Foundation of China (Nos. 21975281, 21773293, 21603264), CAS Pioneer Hundred Talents Program, the National Key Research and Development Program of China (2016YFA0203301), Jiangsu Planned Projects for Postdoctoral Research Funds (2019K048), and Suzhou Science and Technology Plan Project (SYG201926).
Author information
Authors and Affiliations
Corresponding authors
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, X., Zhou, Z., Sun, Z. et al. Atomic Modulation of 3D Conductive Frameworks Boost Performance of MnO2 for Coaxial Fiber-Shaped Supercapacitors. Nano-Micro Lett. 13, 4 (2021). https://doi.org/10.1007/s40820-020-00529-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-020-00529-8