Highlights
-
The theoretical knowledge in the field of microwave absorption is summarized in detail.
-
The recent progress of metal–organic frameworks-derived porous carbon-based nanocomposites as microwave absorption materials is reviewed.
Abstract
The development of microwave absorption materials (MAMs) is a considerable important topic because our living space is crowed with electromagnetic wave which threatens human’s health. And MAMs are also used in radar stealth for protecting the weapons from being detected. Many nanomaterials were studied as MAMs, but not all of them have the satisfactory performance. Recently, metal–organic frameworks (MOFs) have attracted tremendous attention owing to their tunable chemical structures, diverse properties, large specific surface area and uniform pore distribution. MOF can transform to porous carbon (PC) which is decorated with metal species at appropriate pyrolysis temperature. However, the loss mechanism of pure MOF-derived PC is often relatively simple. In order to further improve the MA performance, the MOFs coupled with other loss materials are a widely studied method. In this review, we summarize the theories of MA, the progress of different MOF-derived PC‑based MAMs, tunable chemical structures incorporated with dielectric loss or magnetic loss materials. The different MA performance and mechanisms are discussed in detail. Finally, the shortcomings, challenges and perspectives of MOF-derived PC‑based MAMs are also presented. We hope this review could provide a new insight to design and fabricate MOF-derived PC-based MAMs with better fundamental understanding and practical application.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
The rapid development of science and technology made many kinds of electronic devices become irreplaceable role in human’s daily life [1,2,3,4,5,6,7]. However, the electronic devices make the space rife with electromagnetic waves (EMWs) [8,9,10,11,12,13,14]. The EMWs become a new and more hazardous source of pollution as water, air and noise pollution [15,16,17]. On the one hand, the undesirable EMW may make strong interference to the nearby instruments, causing their malfunctioning and signal interruption. On the other hand, EMW may harm human’s health which cause some disease such as cancer and endocrine disorder [18, 19]. Besides, plants can be inactive, variation and even die with the strong EMW radiation [20, 21]. It is urgently need for human to solve the problem of EMW pollution, while in the field of military, many advanced weapons such as warcraft are the key target of the enemy. EMW stealth technology of military equipment is a crucial solution to evade detection and attack. Coating of MAMs on military equipment is an effective anti-detection method [22]. Therefore, the exploration of high-performance MAMs is of great significance in both civil and military fields.
Recently, MAMs have received much attention because they have the ability to attenuate EMW. They can convert EMW into thermal energy or other forms of energy to dissipate [23, 24]. The ideal MAMs are often multiple loss mechanisms and they required to have lightweight, thin thickness, wide absorption bandwidth and strong absorption characteristics [25, 26].
Metal–organic frameworks (MOFs) are a kind of crystalline porous material with periodic network structure, which is composed of inorganic metal center (metal ion or metal cluster) and organic ligand connected by self-assembly [27,28,29,30]. Due to large amounts of organic ligands that could be used, MOFs have various of compositions and structures. As we know, more than 20,000 MOFs have been reported so far [31, 32]. MOFs have attracted lots of research interest due to their performance diversity, which are potential to extensive uses in many fields, such as electrochemical energy storage [33, 34], catalysis [35, 36], purification [37, 38] and sensing [39, 40]. Moreover, with MOFs as the precursor, carbon and metal-based compounds can be generated in situ by high-temperature pyrolysis in an inert atmosphere [28, 41, 42]. Fortunately, the morphologies of MOFs are still well preserved after pyrolysis [43, 44]. The MOF-derived PC nanocomposites also possess the desirable properties from MOFs [45] such as their tunable chemical structures, large specific surface area, uniform pore distribution, diverse morphology and chemical stability, which enable MOF-derived PC to be an ideal candidate for MA.
MOF-derived PC-based nanocomposites have been widely studied in the field of MAMs, but the attenuation mechanism may be relatively simple. In order to improve the attenuation performance, they usually coupled with other lossy materials. Based on the above views, how to design and prepare MOF-derived PC-based MAMs is now a hot research topic [46, 47]. In this review, we summarize the recent progress of several MOF-derived PC-based nanocomposites as MAMs such as Co, Ni, Fe, Zn, Cu, Ti, Zr and rare-earth (RE) MOF-derived PC-based nanocomposites. Besides the pure MOF, multi-metal MOF or tunable chemical composition incorporated with other loss material had also been fabricated as MAMs. Furthermore, MAMs with different morphology had been reviewed. Finally, we put forward some personal insights into the current status and perspectives in the future research direction.
2 Theories of Microwave Absorption
When the incident EMW contacts with the surface of the MAMs, as shown in Fig. 1, three situations may happen. Part of the incident EMW reflects on the surface of the MAMs (reflected EMW), part of it goes to the interior of the MAMs and absorbed by the MAMs (adsorbed EMW), and the rest of the EMW goes through the MAMs (transmitted EMW) [48]. When designing MAMs, researchers expect the incident EMW to be dissipated as much as possible inside the MAMs to reduce reflected EMW and transmitted EMW. Therefore, a good MAM usually needs to meet two conditions: good impedance matching and strong EMW attenuation ability [49, 50]. The good impedance matching requires incident EMW goes into the MAMs as much as possible and reduces the reflection on the material surface [51]. The ideal impedance matching requires that the complex permittivity (ɛr= ɛ′ − jɛ″) is equal to the complex permeability (μr= μ′ − jμ″). In the formula, ɛ′ and μ′ represent the ability to store electrical and magnetic energy, while ε″ and µ″ refer to the loss of electrical and magnetic energy [52, 53]. It is not easy to meet this requirement. We can artificially adjust electromagnetic parameters (ɛ and μ) to improve the impedance matching. The EMW attenuation ability means the loss capacity of the EMW which enters into the interior of MAMs [24, 54, 55].
Reflection loss (RL) is often used to evaluate the EMW absorption ability. For example, the RL value of − 10 dB is comparable to 90% of MA, and the RL value of − 20 dB is comparable to 99% of MA. The RL is calculated by the transmission line theory, which is shown as follows [56,57,58,59,60]:
Z0 is the impedance of free space (377 Ω), Zin is the input impedance of MAMs, f is the frequency of EMW, d is the thickness of the MAMs, and c is velocity of light, respectively. When Z = 1, the wave impedance of the MAMs is exactly the same as that of the free space. The incident EMW can enter the MAMs completely without reflected wave. Therefore, Z = 1 is an ideal situation. When the value of Z is equal or close to 1, it is beneficial for improving MA ability [61, 62]. The delta-function is another method to evaluate the EM impedance matching degree. The equation is shown as follows [63,64,65]:
The small delta value and close to zero indicate good impedance matching. If |Δ| tends to far away from zero, it gives poor microwave absorption.
The MAMs can be roughly divided into three types according to their loss mechanisms including dielectric loss materials, magnetic loss materials and multiple loss materials, as shown in Table 1. Dielectric loss materials are represented by carbon materials [66, 67], non-magnetic metal powder [68, 69], polymers [70, 71], non-magnetic metal oxides [72, 73], non-oxygen ceramics [74, 75] and so on. They possess features such as high strength, resistance to high temperature, excellent electrical conductivity and low density, but effective absorption bandwidth (EAB) and the MA performance may be not sufficient [76, 77]. Magnetic loss materials are represented by magnetic metal powder and compounds [78, 79], ferrite [80,81,82,83,84,85,86,87], carbonyl iron [88,89,90] and so on. However, their high density and poor stability limit their practical application [91]. The dielectric and magnetic loss factors, defined as \(\tan \delta_{E} = \varepsilon^{\prime \prime } /\varepsilon^{\prime }\) and \(\tan \delta_{M} = \mu^{\prime \prime } /\mu^{\prime }\), are suggested to evaluate on dielectric and magnetic losses [92,93,94].
The dielectric loss ability mainly stems from electrical conductivity loss and polarization relaxation loss [95, 96]. The electrical conductivity loss is that when the EMWs enters into the MAMs, the charge carriers would form a current under the action of the electric field, and then, the electric energy converts to the thermal energy or other form of energy and dissipated out [97, 98], thus increasing EMW attenuation. However, if the conductivity is too high, the incident EMW will be reflected by a large amount, resulting in impedance mismatch and poor EMW attenuation. The polarization relaxation loss is split into ionic polarization, electronic polarization, dipoles relaxation polarization and interfacial polarization (spatial polarization) [55, 99]. Ion polarization is caused by the relative displacement of cations and anions. Electron polarization is caused by position change of the constituent atoms relative to the nucleus, and thus, the dipole moment is generated. Ion polarization and electron polarization usually occur in the frequency range of ultraviolet, visible and infrared light, which is much higher than the microwave frequency range (2-18 GHz), so they are excluded [100, 101]. Dipoles relaxation polarization refers to the polarization caused by the rotation of the dipole moment in the direction of the electric field, and it can greatly influence the dielectric loss [41, 102]. The relaxation loss can be analyzed by Debye equation [103,104,105]:
We can deduce an equation from Eqs. (3) and (4) as follows:
where \(\varepsilon_{S}\) is the static dielectric constant, \(\varepsilon_{\infty }\) is the dielectric constant of infinite frequency, and τ is the time of relaxation. The circle of this equation is called Cole–Cole semicircle [106, 107]. Each Cole–Cole semicircle represents a polarization relaxation process [108, 109]. The points on the semicircle correspond to the values of the real and imaginary parts of the dielectric constant at a certain frequency calculated by the Debye equation. Interfacial polarization usually appears at the interface of heterogeneous medium, which is caused by the accumulation of electrons or ions at the interface under the action of the external electric field [110]. Generally speaking, dielectric materials can be wideband absorption. However, the disadvantage is that the low-frequency absorption effect is poor and it is difficult to achieve the thin coating wideband absorption.
Magnetic loss refers to the phenomenon that the work is done by the outside world to a magnetic material and then the work is converted into heat during the process of magnetization or demagnetization [111]. It includes hysteresis loss, eddy current loss and residual loss [112, 113]. The hysteresis loss is due to the hysteresis loop relationship between the magnetic perceptual strength and the magnetic field strength. Normally, the hysteresis loss often occurred in the weak field can be excluded [114]. When a conductor moves in an inhomogeneous magnetic field or is in a time-varying magnetic field, the energy loss caused by the induced current in the conductor is called eddy current loss. It can be defined as [115,116,117]:
where δ is the electrical conductivity of material, and d is the thickness of the MAMs. From the equation, C0 is a constant at a certain thickness of the MAMs with the change of frequency. This is one of the ways to determine whether EMW loss only results from the eddy current loss [118]. The residual loss refers to other losses except hysteresis loss and eddy current loss [77, 101].
The multiple loss material is not just a single loss mechanism, and it combined the advantages of various losses.
We all know that the synergistic effects between the dielectric loss and magnetic loss contribute to the excellent EMW absorption ability, which result in the good impedance matching and strong EM wave attenuation of the MAMs. However, the conflict between the two sides is still exist. In order to get the EMW into the material as much as possible, it will inevitably reduce the attenuation ability of the MAMs to the EMW. Therefore, it is necessary to coordinate impedance matching and EMW attenuation in practical application. The attenuation constant α can be defined as [119, 120]:
Dissipation of reflected EMW through the interference of MAMs is another key factor to attenuate the EMW, which can be described by the quarter-wavelength matching mechanism (λ/4) as follows [46, 109]:
In the formula, λ is the wavelength of EMW, dm and fm are the thickness and corresponding frequency of maximum RL values, and |μr| and |εr| are the modulus of complex permeability and permittivity at fm, respectively.
3 MOF-Derived PC-Based Nanocomposites as MAMs
As we know, MOFs are composed of inorganic metal center (metal ion or metal cluster) and organic ligand [121, 122]. Through direct pyrolysis of MOFs, they can be converted into metal-doped carbon, and the structure does not change significantly. We can simple and fast synthesis of MAMs by pyrolysis. However, the pure MOF-derived PC-based nanocomposites have not been functionalized, the absorption loss mechanism is simple and MA performance may be not exciting. By incorporated with materials with different absorbing loss mechanisms, impedance matching can be improved and the MA performance can be enhanced.
3.1 Magnetic Single-Metal MOF-Derived PC-Based Nanocomposites as MAMs
Common magnetic metals are Fe, Co and Ni. They often act as inorganic metal centers to synthesize MOF. When they are directly pyrolyzed, the MA performance may not be very good because the simple loss mechanism may lead to impedance mismatch. They often coupled with dielectric loss material to improve impedance matching and rational design on the microstructure to introduce multiple loss mechanisms.
3.1.1 Co-MOF-Derived PC-Based Nanocomposites as MAMs
The most widely studied MOF-derived PC-based nanocomposites as MAMs are the Co-MOF. The typical Co-MOF is ZIF (zeolitic imidazolate framework)-67, which is prepared through the self-assembly of Co2+ and 2-methylimidazole. In Kuang’s work, they pyrolyze Co-based MOFs (Co-MOF, ZIF-67) to synthesize porous Co/C composite under inert atmosphere with different pyrolysis temperature [123]. The morphology before and after sintering has not changed much, just the surface was wrinkled, as shown in Fig. 2. The sample pyrolysis at 500 °C shows better MA performance. The maximum RL of Co/C-500 reached − 35.3 dB at 5.8 GHz with a thickness of 4 mm, and the EAB was 5.80 GHz (8.40–14.20 GHz) corresponding to a thickness of 2.5 mm. The magnetic loss of Co, the large dielectric loss value of carbon and the porous structure result in the MA performance, but the RL and EAB are not very satisfactory.
Since the tunable of inorganic metal center and organic ligand, MOFs have various of compositions and structures. Co-MOF-derived PC-based nanocomposites as MAMs have been reported by many groups. Kong synthesized Co/C pyrolysis from the cubic [Co(INA)2]MOF by isonicotinic acid as organic ligand [124]. Wang’s group constructed Co/C composites via pyrolysis a new Co-based MOF named [Co2O(cptpy)2(DMF)] (CPT-1-Co, Hcptpy = 4′-(4-carboxyphenyl)-4,2′:6′,4′′-terpyridine, DMF = N,N-dimethylformamide), by reacting a multi-dentate ligand, 4′-(4-carboxyphenyl)-4,2′:6′,4′′-terpyridine (Hcptpy), with Co(OAc)2 salt [125]. More works of Co/C synthesized from pure Co-MOF have also been reported [126, 127]. However, the MA performance of pure Co-MOF-derived PC-based nanocomposites is not quite satisfying. The reason may be the low relatively complex permittivity, and high relatively complex permeability leads to poor impedance matching performance, thus limiting their application in MAMs. So, Co-MOF coupled with other loss material, especially dielectric loss material, is a better solution to improve the MA performance.
When they coupled with MOF-derived PC, they would show unexpected performance. The MOF-derived PC/dielectric loss material nanocomposites have many advantages, such as low cost, easy preparation and low density. Moreover, the additional loss mechanisms are created, and electrical loss, polarization loss, the interfacial and multiple scattering may lead to the good MA performance.
Carbon materials such as graphene, carbon nanotube (CNT) and carbon nanofiber (CNF) have aroused wide attention as MAMs due to their excellent physical and chemical properties, including their lightweight, high specific surface area, mechanical strength, thermal stability, corrosion resistance, electric conductivity and dielectric properties. Graphene, composed of sp2-bonded carbon atoms, has a lot of advantages such as electrical, thermal and mechanical properties. Graphene has functional groups and some defects on its surface. The impedance matching of graphene can be improved, and the dipole polarization relaxation can also be generated to improve the MA performance. Graphene can also form a multilayer structure, which can increase the number of reflections and propagation distance of EMW. Dong had synthesized MOF/RGO hybrids by two steps including in situ growth of Co-based MOF on GO nanosheets and a controlled calcination process [128], which is shown in Fig. 3. The maximum RL of the sample reached − 52 dB at 9.6 GHz with a thickness of 4.1 mm. The EAB of this MOF/RGO hybrid can reach 7.72 GHz only under a thickness of 3.2 mm, which surpasses most reported MOF and RGO-based MAMs. It is worthy to point out that the enhanced effect of MOF/RGO interface, improved match between dielectric loss and magnetic loss should be considered as the factor of the high MA performance.
Chen’s group synthesized CoC–rGO obtained by calcination of ZIF-67–GO hybrids [129]. The introduction of high conductivity of rGO may lead to strong eddy current loss and reduce the permeability. The impedance matching is determined by the additive amount of rGO. The RLmax value reached up to -44.77 dB at thickness of 2.1 mm, and the EAB reached 5.2 GHz at thickness of 1.8 mm, which showed evident advantages compared to CoC or rGO alone with single loss mechanism. Zhang’s group synthesized MOF-derived carbonaceous Co3O4/Co/RGO composite at 600 °C in Ar [130]. The sample displays RLmax − 52.8 dB at 13.12 GHz with thickness which is only 2.0 mm. The EAB is up to 10.72 GHz in the thicknesses range of 2.0–4.0 mm. Since the unique porous structure, the dielectric and magnetic tangent losses of the sample are in the middle levels, it is beneficial for the impedance match and thus results in the higher MA performances. CNTs can be divided into single-walled carbon nanotubes (SCNTs) and multi-walled carbon nanotubes (MCNTs). They have a very large aspect ratio, so a conductive network can be formed. The dielectric constant is large, and its permeability is small, so its impedance matching is poor. Therefore, it is often combined with other magnetic loss materials to improve the MA performance. Dong et al. had prepared a 3D Co/C-MCNTs hybrid network using MCNTs as wires and Co-based MOFs as junctions [131]. The multiple components synergistic effect leads to the good MA performance. The purpose of introducing MCNTs may promote the formation of a conductive network, increasing interfacial polarization. The RLmax of the sample Co/C-MCNTs is -33.4 dB at the frequency of 3.6 GHz with the thickness of 6 mm. And the EAB is 4.08 GHz at 1.8 mm. Yu had also fabricated Co–C/MWCNTs composites, and the RLmax is − 48.9 dB at 2.99 mm [132]. Tan synthesized ultra-small Co/CNTs nanohybrid via the pyrolysis of ZIF-67 and (catalytic chemical vapor deposition) CCVD method. It achieves the RLmax of − 49.16 dB and the in EAB of 4.2 GHz (12.4–16.6 GHz) [133]. Chen synthesized MWCNTs@carbonaceous CoO composites with good MA properties [134]. When the annealing temperature is 500 and 600 °C, the carbonaceous Co3O4 can be obtained. When the annealing temperature is 700 °C, Co3O4 was all reduced to CoO. The value of RLmax is up to − 50.2 dB with 1.84 mm thickness. CNF has high dielectric constant, so the impedance match may be not very good, and we usually improve the MA performance by combining with magnetic loss materials. Zhang et al. reported necklace-like CNFs@MOF-based carbonaceous Co/CoO composite, which was synthesized by wet and pyrolysis method [135]. The optimum RL value is − 53.1 dB at 6.56 GHz with the thickness 3.54 mm, and EAB is up to 13.52 GHz with the thickness range of 2.0–5.0 mm. The unique structure will form many defects, which can generate much interfacial polarization, which lead to more dielectric loss. The small-sized nanoparticle can improve dipole polarization. And impedance matching is also optimized to improve the MA performance.
Polymer has the advantages of low density, anti-corrosion and adjustable conductivity, and the electric conductivity and dielectric constant are high. So, it has shown promising prospect in the field of MAMs. In Wang’s report, a chain-like PPy (Polypyrrole) aerogel decorated with MOF-based nanoporous Co/C (Co/C@PPy) has been successfully prepared by a self-assembled polymerization method [136]. The composite Co/C@PPy can reach the optimal RL value of − 44.76 dB at 17.32 GHz with the thickness of 2.0 mm. And the EAB of 6.56 GHz (11.04–17.60 GHz) is achieved with the thickness of 2.5 mm. The performance is attributed to a proper impedance matching and a high dielectric loss highly enhanced by the PPy aerogel. Besides, the unique chain-like PPy aerogel and the porous feature of Co/C itself can induce more multiple reflection and scattering of EMW.
Non-magnetic metal oxide is a common dielectric loss material and coupled with magnetic loss material to regulate impedance matching which is an effective strategy to solve the absorption problems. Zinc oxide (ZnO), as an important semiconductor with a wide band gap, has been extensively investigated as MAMs, due to its excellent dielectric properties and lightweight [137]. Hu’s group constructed a novel 3D hetero-structured Co/NPC@ZnO/rGO by the direct pyrolysis of ZIF-67@ZnO NPs wrapped on rGO nanosheets [138]. ZnO can be utilized to regulate the complex permittivity over the measured frequency range and upgrade the impedance matching property of the sample. The RLmax can reach up to − 45.4 dB at only 2 mm, and the EAB achieved 5.4 GHz (from 11.9 to17.3 GHz). Vanadium sesquioxide (V2O3), with relatively high electrical conductivity at room temperature and superior dielectric loss, is usually used in the field of MAMs. Yan’s group designed and synthesized Co/C@V2O3 hollow spheres with an RL of − 40.1 dB and the EAB of 4.64 GHz at a small thickness of only 1.5 mm [139]. The sample exhibits both excellent impedance matching and light weight due to the rational combination of hollow V2O3 spheres and porous Co/C. One-dimensional chain-like MnO@Co/C composite derived from MnOx@ZIF-67 has also been reported [140]. Similar work was also reported by Co/N/C@MnO2 sample [141]. Hierarchical MnO2 sheets are used to decrease the excessive complex permittivity of Co/N/C and improving impedance match, and polydopamine (PDA) is carbon source. The sample with a filler loading of 15 wt% shows the RLmax of − 58.9 dB and EAB of 5.5 GHz. The excellent MA performance of Co/N/C@MnO2 composites is attributed to synergetic effects of excellent impedance match, and dramatical EM attenuation ability arises from multiple helpful constituents, abundant interfaces and extraordinary hollow structure.
Non-oxygen ceramics presents high strength, good thermal stability and chemical resistivity. But the MA performance is not very good. In order to improve the MA performance, we usually combine non-oxygen ceramics with magnetic loss materials. Dong constructed kebab-like nanocomposites composed of SiC stringing polyhedral Co-MOF [142]. The excellent MA performance attributed to the reduced dielectric constant, enlarged aspect ratio and enhanced interface polarization. Under the thickness of 3 mm, the RLmax attained − 47 dB at the frequency of 9.32 GHz, and the EAB achieved 5.92 GHz in a frequency range 12.08–18 GHz with the sample thickness of 2.0 mm.
Rational design on the microstructure of MOFs-derived PC-based nanocomposites is an effective strategy to prepare high-performance MAMs, through designing some special structures such as foam structure, core–shell structure and hollow structure, which improve the multiple reflections and interfacial polarization so as to enhance MA performance. Zheng’s group successfully synthetized NRGO (nitrogen-doped)/MWCNT composite foams by hydrothermal and high-temperature calcination strategy [143]. The 3D networks were well constructed by overlapped flaky RGO in the composite foams, and the calcination temperature showed notable effects on the micromorphology. The RLmax is − 69.6 dB at 12.5 GHz, and EAB achieved 4.3 GHz (13.2–17.5 GHz) at a low thickness of 1.5 mm, as shown in Fig. 4. The excellent MA performance of the foams was derived from a well-constructed 3D network structure, nitrogen doping, polarization relaxation and conduction loss. Wu and his workmates designed a 3D hybrid carbon sponge composite with a hierarchical micro/nanostructure and hollow skeleton [144]. The conductive network, diverse interface, porous and tubular structures, as well as the synergistic effect between metallic Co nanocrystals and carbon species, resulting in the RLmax is − 51.2 dB with a ultrathin thickness of 1.6 mm and EAB is 5.4 GHz. MOFs-derived hollow Co/C microspheres were produced by Li’s group [145]. They use cetyltrimethylammonium bromide (CTAB) as self-sacrificing template to make hollow microstructures well preserved in the resultant carbon matrix. The hollow microstructures improve the dielectric loss, magnetic loss and enhancing attenuation ability. So rational design on the microstructure of MOFs-derived PC nanocomposites is an effective strategy to develop high-performance MAMs.
3.1.2 Ni-MOF-Derived PC-Based Nanocomposites as MAMs
Magnetic metal Ni-based MOF is also often used in MAMs. Zou and his workmates synthesized Ni@C composites by thermal decomposition of pure Ni-MOF [146]. The sample which calcinated at temperature 800 °C showed a RLmax of − 55.7 dB, and the EAB is 6.0 GHz at a thickness of 1.85 mm. The excellent MA performance is related to the hollow structure and the synergistic effect between carbon and nickel nanoparticles. Ji had fabricated Ni nanoparticles-embedded nanoporous carbon (NPC/Ni), and the sample prepared at 700 °C exhibits nice MA performance with the RLmax value of -39.4 dB and EAB of 4.2 GHz [147]. In Yang’s report, they synthesized Ni-based MOF hollow spheres with various surface morphologies via a simple hydrothermal method [148]. The surface morphologies are controlled by the hydrothermal reaction time. The surface morphologies are smooth, hair-like and rod-like corresponding to the reaction time which is 6, 8, and 10 h, respectively. The RLmax of the 10 h sample reached − 58 dB at 6 GHz with a thickness of 1.5 mm, and the EAB was 6.2 GHz (5–11.2 GHz) with a thickness of 4.6 mm, as shown in Fig. 5. The difference in the surface morphologies results in variation of the magnetic anisotropy, which leads to multi-resonance behavior of the permeability. Liu’s group synthesized two kinds of Ni@C derived from the Ni-based MOFs with two kinds of organic ligands (dimethylimidazole as a ligand named as Ni-ZIF and trimesic acid as a ligand named as Ni-BTC) [149]. The RLmax of the Ni@C-ZIF microspheres is − 86.8 dB with the thickness of 2.7 mm, and the EAB was 7.4 GHz (4–11.4 GHz) with the thickness ranging from 1.5 to 4.0 mm. The impedance matching, multiple reflection, interfacial polarization among Ni and C and the N-doping were beneficial to the excellent MA performance.
The dielectric loss material is also usually introduced to Ni-MOF to improve impedance matching. Chen’s group fabricated multi-component composite SiC/Ni/NiO/C by annealing SiC NPs and the Ni-MOF in argon [150]. The maximum RL is − 50.52 dB at 13 GHz for a film thickness of 4.0 mm, and the EAB is 2.96 GHz (14.76–17.72 GHz) with thickness of 2.5 mm. The high permittivity of the SiC/Ni/NiO/C nanocomposites is expected to enhance absorption of EMW, as shown in Fig. 6. The excellent MA performance also stems from the multi-interface structure which provides interfacial polarization and plasmon resonance.
Structure design is also very important to improve the MA performance of Ni-MOF-derived PC. Du synthesized hierarchical yolk–shell nanostructure (NiO/Ni/GN@Air@NiO/Ni/GN) derived from Ni-MOF by solvothermal reactions [151]. This special structure can effectively enhance the MA performance. And it can also tune the dielectric properties of the NiO/Ni/GN@Air@NiO/Ni/GN composites to achieve good impedance matching. The RLmax of − 34.5 dB is obtained at 17.2 GHz with the thin thickness of 1.7 mm. And the EAB can be obtained in the frequency range 7.8–18 GHz with absorber thicknesses of 1.7–5.0 mm. The 3D porous flower-like Ni/C composites were prepared by Zou’s group through the pyrolysis of Zn-doped Ni-MOF under N2 atmosphere [152]. These 3D flower-like structures have massive porous and large spacing flakes, which increases the EMW scatter. The RLmax is − 52.4 dB with a thickness of 1.6 mm, and EAB is 5 GHz.
3.1.3 Fe-MOF-Derived PC-Based Nanocomposites as MAMs
Because of the good chemical stability, high saturation magnetization and simple preparation, metal iron and ferrite are often used to enhance magnetic loss in MA. So dielectric loss material is also introduced to improve impedance matching. Xu et al. reported Fe/C nanocubes, which are prepared through an in situ derivation from Prussian blue MOF by controlled high-temperature pyrolysis [153]. The maximum RL of the sample obtained at 650 °C reached − 22.6 dB at 4 GHz with a thickness of 5 mm, and the EAB was 7.2 GHz (10.8–18.0 GHz) corresponding to a thickness of 2 mm, as shown in Fig. 7. The good MA performance of the Fe/C nanocubes results in the synergetic effect of dielectric loss and magnetic loss.
Hu’s group successfully fabricated magnetic Fe3C/C (denoted as FC-650) and Fe3C/Fe/C (denoted as FC-700) carbon-matrix composites via carbonization of Material Institute Lavoisier (MIL)-101(Fe) [154]. Both Fe3C/C and Fe3C/Fe/C owned flower-like structures formed by 2D flakes. Fe3C/C possessed RLmax of − 39.43 dB at 14.00 GHz, at the thickness of 2.00 mm. And the EAB is 14.32 GHz (from 3.68 to 18.00 GHz). The impedance matching and the well-designed structures lead to the excellent MA performance.
The morphology usually had significant effect on the MA performance. Kong pyrolyzed two MOFs with different topologies (MOFs: MIL-101-Fe and MIL-88B-Fe) under same pyrolysis condition, identical chemical composition and microstructure [155]. The RLmax is − 59.2 dB with a thickness of 4.32 mm, and the EAB is 6.5 GHz with a thickness of 2 mm which are achieved by Fe/C-700@101 (700: pyrolysis temperature; 101: MIL-101 precursor) and Fe/Fe3C/C-800@101, respectively. This article reveals the significant impact of morphology on MA performance.
In order to improve the impedance matching, dielectric loss material is usually introduced to the Fe-MOF. Hu’s group reported the synthesis of novel MOF (Fe)/PANI (polyaniline) core–shell composite via hydrothermal and in situ chemical polymerization methods [156]. The RLmax of the composite can reach − 41.4 dB at 11.6 GHz, and the EAB is up to 5.5 GHz with only 2 mm. The loss mechanism is due to the enhanced interfacial polarization, dipole polarization and charge transfer and attenuation constant. The introduction of PANI enlarges the dielectric constant. Meanwhile, the higher dielectric constant of MOF (Fe)/PANI may be attributed to the improved interfacial polarization and appearance of localized defects as bipolaron/polaron, and the multiple reflection and scattering in the pores of the samples, dielectric loss, magnetic loss, good impedance matching also beneficial for EMW absorption. Lu’s group reported Fe3O4 @ carbon (Fe3O4@NPC) composites by a simple one-pot synthesis method and subsequent in situ formation under thermal decomposition conditions [157]. The Fe3O4@NPC composites exhibited MA performance with a maximum RL of -65.5 dB at 9.8 GHz with a thickness of 3 mm and the EAB of 4.5 GHz, as shown in Fig. 8. The tan δm value was higher than tan δε value, which indicated that magnetic loss contributed more than dielectric loss to the EMW attenuation. Thus, the improvement of the absorption performance was mainly originated from the magnetic loss. The synergistic effects of the dielectric loss and the magnetic loss are effective in enhancing the MA performance.
3.2 Non-magnetic Single-Metal MOF-Derived PC-Based Nanocomposites as MAMs
Non-magnetic single-metal MOF-derived PC-based nanocomposites usually act as dielectric performance but have negative characteristics in attenuation and impedance matching. Therefore, selecting a high dielectric candidate to combine with non-magnetic single-metal MOF or magnetic loss material is critical.
3.2.1 Zn-MOF-Derived PC-Based Nanocomposites as MAMs
Ji’s group fabricated ZnO/nanoporous carbon (NPC)/reduced graphene oxide (RGO) materials through a simple and valid hydrothermal method derived from Zn-MOF [158]. The RLmax is − 50.5 dB with a thickness of 2.4 mm, and the EAB is 7.4 GHz with a thickness of 2.6 mm, which is shown in Fig. 9. The dielectric constant of ZnO/NPC/RGO samples could be modulated by regulating the combination ratio. Too high or too low permittivity can hardly satisfy an ideal absorber. They had also prepared novel ZnO/carbon porous nanofibers derived from Zn-MOF and polyacrylonitrile (PAN) nanofibers [159]. Xie reported polypyrrole (PPy)/Zn-MOF nanocomposites show tunable electrical conductivity as well as a tunable MA performance [160]. The EAB reaches 7.24 GHz with the thickness of 2.6 mm, and the RLmax is -49 dB with the thickness of 2.9 mm. The MA performance is attributed to the electrical conduction loss and interfacial polarization relaxation.
3.2.2 Ti-MOF-Derived PC-Based Nanocomposites as MAMs
Ji’s group had also synthesized a novel nanoporous carbon material (TiO2/C) by annealing titanium-based MOFs (MIL-125 (Ti); MIL stands for Material from Institute Lavoisier) [161]. The RLmax is -49.6 dB, and the EAB is 4.6 GHz (13.4-18 GHz) with the thickness of 1.6 mm. The outstanding MA performance may be due to the high tan δε, α and polarization loss.
3.2.3 Cu-MOF-Derived PC-Based Nanocomposites as MAMs
Zeng’s group synthesized Ni/NiO/Cu@C composites by using Cu MOFs as the precursor [162]. The RLmax value is − 38.1 dB at a layer thickness of 3.2 mm. The introduction of Ni offers magnetic loss, and interfacial polarization is changed by increasing the interface area and electrical conductivity.
3.2.4 Zr-MOF-Derived PC-Based Nanocomposites as MAMs
Liu’s group developed cobalt-decorated porous ZrO2/C hybrid octahedrons by pyrolysis of Co(NO3)2 impregnated NH2-UIO-66(Zr-MOF) [44]. The sample results in RLmax of − 57.2 dB at 15.8 GHz, corresponding to a matching thickness of 3.3 mm. The EAB reaches 11.9 GHz (6.1–18 GHz). The excellent MA performance of Co/ZrO2/C can be ascribed to the strong interface polarization and the suitable impedance matching, and the synergistic effect among the components. Wang had also synthesized ZrO2/C octahedra from UIO-66 [163]. The RLmax value of − 58.7 dB (16.8 GHz, 1.5 mm) has been achieved. And the EAB could cover 91.3% (3.4–18.0 GHz) of the measured frequency within the thickness range of 1.0–5.0 mm.
3.2.5 Rare-Earth MOF-Derived PC-Based Nanocomposites as MAMs
Li’s group had reported the synthesis of a series of rare-earth MOFs based on MH (maleic hydrazide) ligands [13]. RE-MOFs have many advantages such as hierarchical porous structures, low density and large pore volume. These properties will meet the requirements of MAMs. They successfully synthesized four novel RE-MOFs [Y2(MH)6]n·DMF (1), [Er2(MH)6]n (2), [Yb2(MH)6]n (3) and [La(MH)3]n (4) by the traditional hydrothermal method. Different MA performances can be attributed to different structures and different central ions. The maximum RL values of MOF 1, MOF 2, MOF 3 and MOF 4 are − 22.78 dB at 5 mm, − 19.99 dB at 4.5 mm, − 28.14 dB at 2 mm and − 13.07 GHz at 2 mm, respectively. And the effective absorption bandwidth is 2.24 GHz (6.8–9.04 GHz), 2.12 GHz (from 6.8 to 8.72 GHz), 0.96 GHz (15.76–16.72 GHz) and 0.32 GHz (16.72–17.04 GHz) for MOF 1, MOF 2, MOF 3 and MOF 4. The property may be resulted in the synergetic effects of permittivity and permeability.
3.3 Multi-metal MOF-Derived PC-Based Nanocomposites as MAMs
The MA performance of multi-metal MOF-derived PC-based nanocomposite is often better than single-metal MOF because the multi-metal MOF combines the advantages of two or more materials, endows the mixture with new chemical and physical properties and effectively regulates the electromagnetic parameters of the MAMs.
3.3.1 Multi-magnetic Metal MOF-Derived PC-Based Nanocomposites as MAMs
NiCo nanoparticles/nanoporous carbon (NiCo/NPC) composites with multilayered structure were synthesized through in situ pyrolysis of the bimetallic NiCo-MOF by Lu’s group [164]. The synergistic interactions of magnetic loss and dielectric loss among NiCo NPs, graphitized carbon layer and NPC were beneficial to the optimization of the impedance matching and the enhancement of EMW attenuation. The multilayered nanoporous carbon matrix leads to the multiple reflection and scatterings, interface and dipole polarization as well as the natural resonance and exchange resonance. The RLmax value is − 51 dB at 17.9 GHz with EAB of 4.5 GHz (13.5–18 GHz) and a thickness of 1.5 mm at 600 °C. Dong had also fabricated porous and hollow CoNi@C microspheres derived from CoNi-MOFs [165]. The RLmax can reach − 44.8 dB at 10.7 GHz, and the EAB can reach up to 13.3 GHz (4.7–18.0 GHz) with the thickness of 1.6–4.0 mm, as shown in Fig. 10. The simultaneous enhancement of attenuation ability and impedance matching together contribute to the improved MA performance. The attenuation ability comes from interfacial polarization, eddy current loss, multiple reflection and scattering. The impedance matching stems from magnetic CoNi alloy and dielectric graphitized carbon. Liu had also reported CoNi/C nanocomposites derived from bimetallic CoNi-MOF [166]. The RLmax of − 74.7 dB could be achieved with a thickness of 1.8 mm at 15.6 GHz. The EAB ranged from 2.9 GHz to 18 GHz. The porous Co–Ni/C nanocomposites combined advantages of excellent impedance matching and strong interfacial loss between metallic NPs and porous carbon composites. Similarly, FeCo alloy/carbon composites [167] and Fe3Ni/C composites [168] had also shown the excellent MA performance. Hollow sphere trimetallic FeCoNi@C MAMs via high-temperature carbonization were obtained using FeCoNi-based MOF-74 (FeCoNiMOF) as the precursor [169].
Other multi-magnetic metal MOF-derived PC-based nanocomposites as MAMs had also been reported. In order to further improve impedance matching, the dielectric loss is often introduced to the multi-magnetic metal MOF such as FeCo@C@CNGs(carbon nanocages) [170], NiCo alloy/carbon nanorod@CNT [171], Fe–Co/NC/rGO [172], FeNi@CNT/CNRs(carbon nanorods) [173] and CoFe@C@MnO2 [174]. All of these samples show good impedance matching and outstanding EMW attenuation capability.
3.3.2 Magnetic and Non-magnetic Metal MOF-Derived PC-Based Nanocomposites as MAMs
Non-magnetic metal MOFs play the role of dielectric loss. Zn is most widely used in this occasion. Since the unique evaporation character of Zn metal under high pyrolysis temperature, the porous low-dielectric amorphous carbon/Zn shell derived from Zn-MOF was formed to decrease the permittivity for a better impedance match. Zheng’s group fabricated nitrogen-doped CoO/Co/C nanocomposites by high-temperature pyrolysis of Co/Zn-ZIFs [175]. Zn was evaporated during the high-temperature pyrolysis process at 700 °C. The RLmax reached − 66.7 dB at 7.2 GHz with a thickness of 3.3 mm, and the EAB is 5.1 GHz (12.6–17.7 GHz) with thickness of 1.8 mm, as shown in Fig. 11. The excellent MA performance ascribed to the enhanced polarization relaxation, and synergistic effects of dielectric loss, conduction loss and magnetic loss.
Jiang had fabricated CoZn-MOF and then calcined it at different high temperatures to gain the metal Co embedded in porous and N-doped graphitized carbon matrix (Co@pNGC) [176]. Zn species was also evaporated at high temperature. The RLmax is − 50.7 dB at 11.3 GHz, and the EAB reaches 5.5 GHz (12.3–17.8 GHz), corresponding to a thickness of 2.0 mm. The strong dielectric loss is derived from interfacial polarization, migration, hopping of electrons and the magnetic loss from the Co nanoparticles.
4 Comparison of MA Performance of Different MOF-Derived PC-Based Nanocomposites
As is mentioned above, many MOF-derived PC-based nanocomposites exhibited the appreciable MA performance. In Table 2, we sum up the performance of the MAMs mentioned above. As is described, there are many kinds of MOF-derived PC-based materials used in the MAMs. Most of the MOF-derived PC-based MAMs have better MA performance than the comparison MAMs. The MA performance of pure Ni, Co, Fe-MOF-derived PC-based is not satisfactory. When they coupled with dielectric loss material, the MA performance will be significantly improved. Non-magnetic metal MOF-derived PC-based MAMs such as Zn, Ti, Cu, Zr and RE are usually coupled with magnetic loss material to get impedance matching, while the multiple metal MOF-derived PC-based MAMs have shown excellent MA performance. They usually have multiple loss mechanism, so the synergistic effect between each part will be beneficial to impedance matching and electromagnetic wave attenuation. The structure of MOF also has a significant effect on the MA performance. Through design of MOF with different structures such as foam structure, core–shell structure, hollow structure, etc., the multiple reflections and interfacial polarization can be achieved. Therefore, MOF-derived PC-based nanocomposite is a promising material in the field of high-performance MAMs in the future.
5 Conclusion
The recent progress of MOF-derived PC-based nanocomposites as MAMs has been systematically summarized by this review. In view of these studies, we find that MOF-derived PC-based MAMs from in situ pyrolysis of MOFs will be a promising method for the development of lightweight and highly effective MAMs. After pyrolysis, the PC-based MAMs from the MOFs exhibit porosity, low density, good electrical conductivity and dielectric loss. And the inorganic metal center can result in magnetic loss (magnetic metal) or dielectric loss (non-magnetic metal). To further improve the MA performance, the MOF-derived PC-based nanocomposites often coupled with other loss material. The well-designed nanocomposites with multiple advantages will show good impedance matching and strong EM attenuation capability because of the multiple loss mechanism and synergistic effect of the multi-components. Therefore, the MOF-derived PC-based nanocomposites coupled with multiple loss material are an attractive development direction of MAMs in the future.
Many achievements have been made in MOF-derived PC-based nanocomposites as MAMs, but most are just at the research stage, far away from the practical use. The EAB and the maximum RL values are not enough to meet the actual needs. We can rationally design the MAMs with the suitable preparation conditions to realize the special microstructure, which can improve the scattering of EM, and the multiple loss mechanism is realized by the synergistic effect of multiple components. As more than 20,000 kinds of MOFs have been used in various fields, we only review the common Ni, Co, Fe, Zn, Ti, Cu, Zr and RE metal as the central elements, and they have shown considerable MA performance. But they are just the tip of the iceberg of the big family of MOFs. We should also pay more attention to other metal elements. Through the modulation of inorganic metal center and organic ligand, different kinds of MOFs are constructed to achieve the optimal MA performance. The “thin, wide, light, strong” is the goal to develop MAMs, but most of the studies merely focus on the EAB and the maximum RL values, while the thickness and the weight of the MAMs have been usually ignored. In fact, low density is also an important parameter to evaluate the MAMs. One of the pyrolysis products of MOFs is carbon; therefore, MOFs are promising materials to employ new lightweight MAMs, especially in military applications. In conclusion, MOF-derived PC-based nanocomposites had already shown its great potential as MAMs. We firmly believe that the MOF-derived PC-based nanocomposites will be widely used in the field of MAMs in the future.
References
N. Wu, D. Xu, Z. Wang, F. Wang, J. Liu et al., Achieving superior electromagnetic wave absorbers through the novel metal-organic frameworks derived magnetic porous carbon nanorods. Carbon 145, 433–444 (2019). https://doi.org/10.1016/j.carbon.2019.01.028
H. Lv, X. Liang, G. Ji, H. Zhang, Y. Du, Porous three-dimensional flower-like Co/CoO and its excellent electromagnetic absorption properties. ACS Appl. Mater. Interfaces. 7(18), 9776–9783 (2015). https://doi.org/10.1021/acsami.5b01654
S. Xie, Z. Ji, L. Zhu, J. Zhang, Y. Cao et al., Recent progress in electromagnetic wave absorption building materials. J. Build. Eng. 27, 100963 (2020). https://doi.org/10.1016/j.jobe.2019.100963
L. Heng, Z. Zhang, X. Chen, S. Wang, Z. Wu et al., Fe/nanoporous carbon hybrid derived from metal-organic framework for highly effective microwave absorption. Appl. Organomet. Chem. 33(8), e4991 (2019). https://doi.org/10.1002/aoc.4991
S.U. Rehman, J. Wang, Q. Luo, M. Sun, L. Jiang et al., Starfish-like C/CoNiO2 heterostructure derived from ZIF-67 with tunable microwave absorption properties. Chem. Eng. J. 373, 122–130 (2019). https://doi.org/10.1016/j.cej.2019.05.040
M. Qiao, X. Lei, Y. Ma, L. Tian, X. He et al., Application of yolk–shell Fe3O4@N-doped carbon nanochains as highly effective microwave-absorption material. Nano Res. 11(3), 1500–1519 (2018). https://doi.org/10.1007/s12274-017-1767-0
B. Shen, W. Zhai, M. Tao, J. Ling, W. Zheng, Lightweight, multifunctional polyetherimide/graphene@Fe3O4 composite foams for shielding of electromagnetic pollution. ACS Appl. Mater. Interfaces. 5(21), 11383–11391 (2013). https://doi.org/10.1021/am4036527
J.L. Liu, H.S. Liang, Y. Zhang, G.L. Wu, H.J. Wu, Facile synthesis of ellipsoid-like MgCo2O4/Co3O4 composites for strong wideband microwave absorption application. Compos. Part B Eng. 176, 12 (2019). https://doi.org/10.1016/j.compositesb.2019.107240
X.F. Zhou, Z.R. Jia, A.L. Feng, X.X. Wang, J.J. Liu et al., Synthesis of fish skin-derived 3D carbon foams with broadened bandwidth and excellent electromagnetic wave absorption performance. Carbon 152, 827–836 (2019). https://doi.org/10.1016/j.carbon.2019.06.080
P. Liu, Y. Huang, J. Yan, Y. Yang, Y. Zhao, Construction of CuS nanoflakes vertically aligned on magnetically decorated graphene and their enhanced microwave absorption properties. ACS Appl. Mater. Interfaces. 8(8), 5536–5546 (2016). https://doi.org/10.1021/acsami.5b10511
M.-M. Lu, M.-S. Cao, Y.-H. Chen, W.-Q. Cao, J. Liu et al., Multiscale assembly of grape-like ferroferric oxide and carbon nanotubes: a smart absorber prototype varying temperature to tune intensities. ACS Appl. Mater. Interfaces. 7(34), 19408–19415 (2015). https://doi.org/10.1021/acsami.5b05595
D. Ding, Y. Wang, X. Li, R. Qiang, P. Xu et al., Rational design of core-shell Co@C microspheres for high-performance microwave absorption. Carbon 111, 722–732 (2017). https://doi.org/10.1016/j.carbon.2016.10.059
L.W. Zhu, N. Liu, X.H. Jiang, L.M. Yu, X. Li, Four novel 3D RE-MOFs based on maleic hydrazide: syntheses, structural diversity, efficient electromagnetic wave absorption and antibacterial activity properties. Inorg. Chim. Acta 501, 119291 (2020). https://doi.org/10.1016/j.ica.2019.119291
Y. Zhang, X. Wang, M. Cao, Confinedly implanted NiFe2O4-rGO: cluster tailoring and highly tunable electromagnetic properties for selective-frequency microwave absorption. Nano Res. 11(3), 1426–1436 (2018). https://doi.org/10.1007/s12274-017-1758-1
P. Saini, M. Arora, G. Gupta, B.K. Gupta, V.N. Singh et al., High permittivity polyaniline-barium titanate nanocomposites with excellent electromagnetic interference shielding response. Nanoscale 5(10), 4330–4336 (2013). https://doi.org/10.1039/c3nr00634d
L. Huang, J. Li, Z. Wang, Y. Li, X. He et al., Microwave absorption enhancement of porous C@CoFe2O4 nanocomposites derived from eggshell membrane. Carbon 143, 507–516 (2019). https://doi.org/10.1016/j.carbon.2018.11.042
Z. Xu, Y. Du, D. Liu, Y. Wang, W. Ma et al., Pea-like Fe/Fe3C nanoparticles embedded in nitrogen-doped carbon nanotubes with tunable dielectric/magnetic loss and efficient electromagnetic absorption. ACS Appl. Mater. Interfaces. 11(4), 4268–4277 (2019). https://doi.org/10.1021/acsami.8b19201
X.-X. Wang, T. Ma, J.-C. Shu, M.-S. Cao, Confinedly tailoring Fe3O4 clusters-NG to tune electromagnetic parameters and microwave absorption with broadened bandwidth. Chem. Eng. J. 332, 321–330 (2018). https://doi.org/10.1016/j.cej.2017.09.101
Z. Jia, D. Lan, K. Lin, M. Qin, K. Kou et al., Progress in low-frequency microwave absorbing materials. J. Mater. Sci.: Mater. Electron. 29(20), 17122–17136 (2018). https://doi.org/10.1007/s10854-018-9909-z
H. Zhao, Y. Cheng, W. Liu, L. Yang, B. Zhang et al., Biomass-derived porous carbon-based nanostructures for microwave absorption. Nano-Micro Lett. 11(1), 24 (2019). https://doi.org/10.1007/s40820-019-0255-3
H. Zhao, Y. Cheng, H. Lv, G. Ji, Y. Du, A novel hierarchically porous magnetic carbon derived from biomass for strong lightweight microwave absorption. Carbon 142, 245–253 (2019). https://doi.org/10.1016/j.carbon.2018.10.027
S. Ghosh, S. Remanan, S. Mondal, S. Ganguly, P. Das et al., An approach to prepare mechanically robust full IPN strengthened conductive cotton fabric for high strain tolerant electromagnetic interference shielding. Chem. Eng. J. 344, 138–154 (2018). https://doi.org/10.1016/j.cej.2018.03.039
K. Srogi, Microwave-assisted sample preparation of coal and coal fly ash for subsequent metal determination. Anal. Lett. 40(2), 199–232 (2007). https://doi.org/10.1080/00032710600867713
X. Zhang, J. Qiao, F. Wang, L. Lv, D. Xu et al., Tailoring electromagnetic absorption performances of TiO2/Co/carbon nanofibers through tuning graphitization degrees. Ceram. Int. 46(4), 4754–4761 (2020). https://doi.org/10.1016/j.ceramint.2019.10.207
B. Zhao, G. Shao, B. Fan, W. Zhao, Y. Xie et al., Synthesis of flower-like CuS hollow microspheres based on nanoflakes self-assembly and their microwave absorption properties. J. Mater. Chem. A 3(19), 10345–10352 (2015). https://doi.org/10.1039/c5ta00086f
A. Munir, Microwave radar absorbing properties of multiwalled carbon nanotubes polymer composites: a review. Adv. Polym. Tech. 36(3), 362–370 (2017). https://doi.org/10.1002/adv.21617
M. Safaei, M.M. Foroughi, N. Ebrahimpoor, S. Jahani, A. Omidi et al., A review on metal-organic frameworks: synthesis and applications. Trac-Trends Anal. Chem. 118, 401–425 (2019). https://doi.org/10.1016/j.trac.2019.06.007
X. Xu, F. Ran, Z. Fan, H. Lai, Z. Cheng et al., Cactus-inspired bimetallic metal-organic framework-derived 1D-2D hierarchical Co/N-decorated carbon architecture toward enhanced electromagnetic wave absorbing performance. ACS Appl. Mater. Interfaces. 11(14), 13564–13573 (2019). https://doi.org/10.1021/acsami.9b00356
Y. Wang, X. Gao, C. Lin, L. Shi, X. Li et al., Metal organic frameworks-derived Fe-Co nanoporous carbon/graphene composite as a high-performance electromagnetic wave absorber. J. Alloys Compd. 785, 765–773 (2019). https://doi.org/10.1016/j.jallcom.2019.01.271
Y. Ye, Z. Ma, R.-B. Lin, R. Krishna, W. Zhou et al., Pore space partition within a metal-organic framework for highly efficient C2H2/CO2 separation. J. Am. Chem. Soc. 141(9), 4130–4136 (2019). https://doi.org/10.1021/jacs.9b00232
H. Zhang, X. Liu, Y. Wu, C. Guan, A.K. Cheetham et al., MOF-derived nanohybrids for electrocatalysis and energy storage: current status and perspectives. Chem. Commun. 54(42), 5268–5288 (2018). https://doi.org/10.1039/c8cc00789f
Z.-X. Cai, Z.-L. Wang, J. Kim, Y. Yamauchi, Hollow functional materials derived from metal–organic frameworks: synthetic strategies, conversion mechanisms, and electrochemical applications. Adv. Mater. 31(11), 1804903 (2019). https://doi.org/10.1002/adma.201804903
Z. Liang, C. Qu, W. Guo, R. Zou, Q. Xu, Pristine metal-organic frameworks and their composites for energy storage and conversion. Adv. Mater. (2018). https://doi.org/10.1002/adma.201702891
X. Wei, Y. Li, H. Peng, M. Zhou, Y. Ou et al., Metal-organic framework-derived hollow CoS nanobox for high performance electrochemical energy storage. Chem. Eng. J. 341, 618–627 (2018). https://doi.org/10.1016/j.cej.2018.02.032
J. Li, W. Huang, M. Wang, S. Xi, J. Meng et al., Low-crystalline bimetallic metal-organic framework electrocatalysts with rich active sites for oxygen evolution. ACS Energy Lett. 4(1), 285–292 (2019). https://doi.org/10.1021/acsenergylett.8b02345
B. Zhu, R. Zou, Q. Xu, Metal-organic framework based catalysts for hydrogen evolution. Adv. Energy Mater. (2018). https://doi.org/10.1002/aenm.201801193
R.-B. Lin, S. Xiang, H. Xing, W. Zhou, B. Chen, Exploration of porous metal-organic frameworks for gas separation and purification. Coord. Chem. Rev. 378, 87–103 (2019). https://doi.org/10.1016/j.ccr.2017.09.027
X. Jiang, S. Li, Y. Bai, L. Shao, Ultra-facile aqueous synthesis of nanoporous zeolitic imidazolate framework membranes for hydrogen purification and olefin/paraffin separation. J. Mater. Chem. A 7(18), 10898–10904 (2019). https://doi.org/10.1039/c8ta11748a
J. Chang, X. Wang, J. Wang, H. Li, F. Li, Nucleic acid-functionalized metal-organic framework-based homogeneous electrochemical biosensor for simultaneous detection of multiple tumor biomarkers. Anal. Chem. 91(5), 3604–3610 (2019). https://doi.org/10.1021/acs.analchem.8b05599
Y. Li, M. Xie, X. Zhang, Q. Liu, D. Lin, C. Xu, F. Xie, X. Sun, Co-MOF nanosheet array: a high-performance electrochemical sensor for non-enzymatic glucose detection. Sens. Actuat. B Chem. 278, 126–132 (2019). https://doi.org/10.1016/j.snb.2018.09.076
W. Liu, S. Tan, Z. Yang, G. Ji, Enhanced low-frequency electromagnetic properties of MOF-derived cobalt through interface design. ACS Appl. Mater. Interfaces. 10(37), 31610–31622 (2018). https://doi.org/10.1021/acsami.8b10685
H. Xu, X. Yin, M. Zhu, M. Li, H. Zhang et al., Constructing hollow graphene nano-spheres confined in porous amorphous carbon particles for achieving full X band microwave absorption. Carbon 142, 346–353 (2019). https://doi.org/10.1016/j.carbon.2018.10.056
Y. Zhang, S. Gao, H. Xing, H. Li, In situ carbon nanotubes encapsulated metal Nickel as high-performance microwave absorber from Ni-Zn metal-organic framework derivative. J. Alloys Compd. 801, 609–618 (2019). https://doi.org/10.1016/j.jallcom.2019.06.164
X. Zhang, J. Qao, J. Zhao, D. Xu, F. Wang et al., High-efficiency electromagnetic wave absorption of cobalt decorated NH2-UIO-66-derived porous ZrO2/C. ACS Appl. Mater. Interfaces. 11(39), 35959–35968 (2019). https://doi.org/10.1021/acsami.9b10168
W. Yang, X. Li, Y. Li, R. Zhu, H. Pang, Applications of metal-organic-framework-derived carbon materials. Adv. Mater. 31(6), 1804740 (2019). https://doi.org/10.1002/adma.201804740
W. Liu, L. Liu, Z. Yang, J. Xu, Y. Hou et al., A versatile route toward the electromagnetic functionalization of metal–organic framework-derived three-dimensional nanoporous carbon composites. ACS Appl. Mater. Interfaces. 10(10), 8965–8975 (2018). https://doi.org/10.1021/acsami.8b00320
Q. Wu, H. Jin, W. Chen, S. Huo, X. Chen et al., Graphitized nitrogen-doped porous carbon composites derived from ZIF-8 as efficient microwave absorption materials. Mater. Res. Express 5(6), 065602 (2018). https://doi.org/10.1088/2053-1591/aac67e
F. Meng, H. Wang, F. Huang, Y. Guo, Z. Wang et al., Graphene-based microwave absorbing composites: a review and prospective. Compos. Part B Eng. 137, 260–277 (2018). https://doi.org/10.1016/j.compositesb.2017.11.023
R. Shu, J. Zhang, C. Guo, Y. Wu, Z. Wan et al., Facile synthesis of nitrogen-doped reduced graphene oxide/nickel-zinc ferrite composites as high-performance microwave absorbers in the X-band. Chem. Eng. J. 384, 123266 (2020). https://doi.org/10.1016/j.cej.2019.123266
Y. Wu, R. Shu, X. Shan, J. Zhang, J. Shi et al., Facile design of cubic-like cerium oxide nanoparticles decorated reduced graphene oxide with enhanced microwave absorption properties. J. Alloys Compd. 817, 152766 (2020). https://doi.org/10.1016/j.jallcom.2019.152766
J. Yan, Y. Huang, C. Chen, X. Liu, H. Liu, The 3D CoNi alloy particles embedded in N-doped porous carbon foams for high-performance microwave absorbers. Carbon 152, 545–555 (2019). https://doi.org/10.1016/j.carbon.2019.06.064
Z. Wu, K. Tian, T. Huang, W. Hu, F. Xie et al., Hierarchically porous carbons derived from biomasses with excellent microwave absorption performance. ACS Appl. Mater. Interfaces. 10(13), 11108–11115 (2018). https://doi.org/10.1021/acsami.7b17264
N. Wu, C. Liu, D. Xu, J. Liu, W. Liu et al., Enhanced electromagnetic wave absorption of three-dimensional porous Fe3O4/C composite flowers. ACS Sustain. Chem. Eng. 6(9), 12471–12480 (2018). https://doi.org/10.1021/acssuschemeng.8b03097
M. Zeng, Q. Cao, J. Liu, B. Guo, X. Hao et al., Hierarchical cobalt selenides as highly efficient microwave absorbers with tunable frequency response. ACS Appl. Mater. Interfaces. 12(1), 1222–1231 (2020). https://doi.org/10.1021/acsami.9b15172
L.J. Yang, H.L. Lv, M. Li, Y. Zhang, J.C. Liu et al., Multiple polarization effect of shell evolution on hierarchical hollow C@MnO2 composites and their wideband electromagnetic wave absorption properties. Chem. Eng. J. 392, 10 (2020). https://doi.org/10.1016/j.cej.2019.123666
Z. Wang, R. Wei, J. Gu, H. Liu, C. Liu et al., Ultralight, highly compressible and fire-retardant graphene aerogel with self-adjustable electromagnetic wave absorption. Carbon 139, 1126–1135 (2018). https://doi.org/10.1016/j.carbon.2018.08.014
K. Wang, Y. Chen, R. Tian, H. Li, Y. Zhou et al., Porous Co-C core-shell nanocomposites derived from Co-MOF-74 with enhanced electromagnetic wave absorption performance. ACS Appl. Mater. Interfaces. 10(13), 11333–11342 (2018). https://doi.org/10.1021/acsami.8b00965
R. Shu, G. Zhang, X. Wang, X. Gao, M. Wang et al., Fabrication of 3D net-like MWCNTs/ZnFe2O4 hybrid composites as high-performance electromagnetic wave absorbers. Chem. Eng. J. 337, 242–255 (2018). https://doi.org/10.1016/j.cej.2017.12.106
Y. Zhang, Y. Huang, H. Chen, Z. Huang, Y. Yang et al., Composition and structure control of ultralight graphene foam for high-performance microwave absorption. Carbon 105, 438–447 (2016). https://doi.org/10.1016/j.carbon.2016.04.070
J. Zhang, R. Shu, Y. Wu, Z. Wan, M. Zheng, Facile fabrication and enhanced microwave absorption properties of reduced graphene oxide/tin dioxide binary nanocomposites in the X-band. Synth. Met. 257, 116157 (2019). https://doi.org/10.1016/j.synthmet.2019.116157
Q. Song, F. Ye, L. Kong, Q. Shen, L. Han et al., Graphene and MXene nanomaterials: toward high-performance electromagnetic wave absorption in gigahertz band range. Adv. Funct. Mater. 30(31), 2000475 (2020). https://doi.org/10.1002/adfm.202000475
G. Shao, J. Liang, W. Zhao, B. Zhao, W. Liu et al., Co decorated polymer-derived SiCN ceramic aerogel composites with ultrabroad microwave absorption performance. J. Alloys Compd. 813(15), 152007 (2020). https://doi.org/10.1016/j.jallcom.2019.152007
S. Dong, P. Hu, X. Li, C. Hong, X. Zhang et al., NiCo2S4 nanosheets on 3D wood-derived carbon for microwave absorption. Chem. Eng. J. 398, 125588 (2020). https://doi.org/10.1016/j.cej.2020.125588
X. Wang, F. Pan, Z. Xiang, Q. Zeng, K. Pei et al., Magnetic vortex core-shell Fe3O4@C nanorings with enhanced microwave absorption performance. Carbon 157, 130–139 (2020). https://doi.org/10.1016/j.carbon.2019.10.030
S. Dong, W. Zhang, X. Zhang, P. Hu, J. Han, Designable synthesis of core-shell SiCw@C heterostructures with thickness-dependent electromagnetic wave absorption between the whole X-band and Ku-band. Chem. Eng. J. 354, 767–776 (2018). https://doi.org/10.1016/j.cej.2018.08.062
L. Liu, S. Yang, H. Hu, T. Zhang, Y. Yuan et al., Lightweight and efficient microwave-absorbing materials based on loofah-sponge-derived hierarchically porous carbons. ACS Sustain. Chem. Eng. 7(1), 1228–1238 (2019). https://doi.org/10.1021/acssuschemeng.8b04907
H. Wang, F. Meng, F. Huang, C. Jing, Y. Li et al., Interface modulating CNTs@PANi hybrids by controlled unzipping of the walls of CNTs to achieve tunable high-performance microwave absorption. ACS Appl. Mater. Interfaces. 11(12), 12142–12153 (2019). https://doi.org/10.1021/acsami.9b01122
J. Kuang, P. Jiang, F. Ran, W. Cao, Conductivity-dependent dielectric properties and microwave absorption of Al-doped SiC whiskers. J. Alloys Compd. 687, 227–231 (2016). https://doi.org/10.1016/j.jallcom.2016.06.168
X. Qi, Y. Yang, W. Zhong, C. Qin, Y. Deng et al., Simultaneous synthesis of carbon nanobelts and carbon/Fe–Cu hybrids for microwave absorption. Carbon 48(12), 3512–3522 (2010). https://doi.org/10.1016/j.carbon.2010.05.047
H. Xu, X. Yin, X. Li, M. Li, S. Liang et al., Lightweight Ti2CTx MXene/Poly(vinyl alcohol) composite foams for electromagnetic wave shielding with absorption-dominated feature. ACS Appl. Mater. Interfaces. 11(10), 10198–10207 (2019). https://doi.org/10.1021/acsami.8b21671
C.G. Jayalakshmi, A. Inamdar, A. Anand, B. Kandasubramanian, Polymer matrix composites as broadband radar absorbing structures for stealth aircrafts. J. Appl. Polym. Sci. (2019). https://doi.org/10.1002/app.47241
J. Jiang, D. Li, D. Geng, J. An, J. He et al., Microwave absorption properties of core double-shell FeCo/C/BaTiO3 nanocomposites. Nanoscale 6(8), 3967–3971 (2014). https://doi.org/10.1039/c3nr04087a
P. Liu, Y. Huang, J. Yan, Y. Zhao, Magnetic graphene@PANI@porous TiO2 ternary composites for high-performance electromagnetic wave absorption. J. Mater. Chem. C 4(26), 6362–6370 (2016). https://doi.org/10.1039/c6tc01718e
W. Duan, X. Yin, Q. Li, L. Schlier, P. Greil et al., A review of absorption properties in silicon-based polymer derived ceramics. J. Eur. Ceram. Soc. 36(15), 3681–3689 (2016). https://doi.org/10.1016/j.jeurceramsoc.2016.02.002
W. Zhou, R.-M. Yin, L. Long, H. Luo, W.-D. Hu et al., Enhanced high-temperature dielectric properties and microwave absorption of SiC nanofibers modified Si3N4 ceramics within the gigahertz range. Ceram. Int. 44(11), 12301–12307 (2018). https://doi.org/10.1016/j.ceramint.2018.04.017
H. Lv, X. Liang, Y. Cheng, H. Zhang, D. Tang et al., Coin-like alpha-Fe2O3@CoFe2O4 core-shell composites with excellent electromagnetic absorption performance. ACS Appl. Mater. Interfaces. 7(8), 4744–4750 (2015). https://doi.org/10.1021/am508438s
B. Quan, X. Lang, G. Ji, J. Ma, P. Ouyang et al., Strong electromagnetic wave response derived from the construction of dielectric/magnetic media heterostructure and multiple interfaces. ACS Appl. Mater. Interfaces. 9(11), 9964–9974 (2017). https://doi.org/10.1021/acsami.6b15788
C. Zhou, X. Wang, H. Luo, L. Deng, S. Wang et al., Interfacial design of sandwich-like CoFe@Ti3C2Tx composites as high efficient microwave absorption materials. Appl. Surf. Sci. 494, 540–550 (2019). https://doi.org/10.1016/j.apsusc.2019.07.208
N. Li, X. Xie, H. Lu, B. Fan, X. Wang et al., Novel two-dimensional Ti3C2Tx/Ni-spheres hybrids with enhanced microwave absorption properties. Ceram. Int. 45(17), 22880–22888 (2019). https://doi.org/10.1016/j.ceramint.2019.07.331
Z. Lou, C. Yuan, Y. Zhang, Y. Li, J. Cai et al., Synthesis of porous carbon matrix with inlaid Fe3C/Fe3O4 micro-particles as an effective electromagnetic wave absorber from natural wood shavings. J. Alloys Compd. 775, 800–809 (2019). https://doi.org/10.1016/j.jallcom.2018.10.213
T. Wu, Y. Liu, X. Zeng, T. Cui, Y. Zhao et al., Facile hydrothermal synthesis of fe3o4/c core-shell nanorings for efficient low-frequency microwave absorption. ACS Appl. Mater. Interfaces. 8(11), 7370–7380 (2016). https://doi.org/10.1021/acsami.6b00264
M.A. Almessiere, Y. Slimani, H. Güngüneş, V.G. Kostishyn, S.V. Trukhanov et al., Impact of Eu3+ ion substitution on structural, magnetic and microwave traits of Ni–Cu–Zn spinel ferrites. Ceram. Int. (2020). https://doi.org/10.1016/j.ceramint.2020.01.132
D.S. Klygach, M.G. Vakhitov, D.A. Vinnik, A.V. Bezborodov, S.A. Gudkova et al., Measurement of permittivity and permeability of barium hexaferrite. J. Magn. Magn. Mater. 465, 290–294 (2018). https://doi.org/10.1016/j.jmmm.2018.05.054
D.A. Vinnik, D.S. Klygach, V.E. Zhivulin, A.I. Malkin, M.G. Vakhitov et al., Electromagnetic properties of BaFe12O19: Ti at centimeter wavelengths. J. Alloys Compd. 755, 177–183 (2018). https://doi.org/10.1016/j.jallcom.2018.04.315
A.V. Trukhanov, M.A. Almessiere, A. Baykal, S.V. Trukhanov, Y. Slimani et al., Influence of the charge ordering and quantum effects in heterovalent substituted hexaferrites on their microwave characteristics. J. Alloys Compd. 788, 1193–1202 (2019). https://doi.org/10.1016/j.jallcom.2019.02.303
L.Y. Matzui, A.V. Trukhanov, O.S. Yakovenko, L.L. Vovchenko, V.V. Zagorodnii et al., Functional magnetic composites based on hexaferrites: correlation of the composition. Magnetic and high-frequency properties. Nanomaterials 9(12), 1720 (2019). https://doi.org/10.3390/nano9121720
O.S. Yakovenko, L.Y. Matzui, L.L. Vovchenko, A.V. Trukhanov, I.S. Kazakevich et al., Magnetic anisotropy of the graphite nanoplatelet–epoxy and MWCNT–epoxy composites with aligned barium ferrite filler. J. Mater. Sci. 52(9), 5345–5358 (2017). https://doi.org/10.1007/s10853-017-0776-4
Y. Qing, D. Min, Y. Zhou, F. Luo, W. Zhou, Graphene nanosheet- and flake carbonyl iron particle-filled epoxy-silicone composites as thin-thickness and wide-bandwidth microwave absorber. Carbon 86, 98–107 (2015). https://doi.org/10.1016/j.carbon.2015.01.002
O. Khani, M.Z. Shoushtari, K. Ackland, P. Stamenov, The structural, magnetic and microwave properties of spherical and flake shaped carbonyl iron particles as thin multilayer microwave absorbers. J. Magn. Magn. Mater. 428, 28–35 (2017). https://doi.org/10.1016/j.jmmm.2016.12.010
S. Yan, C. Cao, J. He, L. He, Z. Qu, Investigation on the electromagnetic and broadband microwave absorption properties of Ti3C2 Mxene/flaky carbonyl iron composites. J. Mater. Sci.: Mater. Electron. 30(7), 6537–6543 (2019). https://doi.org/10.1007/s10854-019-00959-0
Q. Li, Z. Zhang, L. Qi, Q. Liao, Z. Kang et al., Toward the application of high frequency electromagnetic wave absorption by carbon nanostructures. Adv. Sci. (2019). https://doi.org/10.1002/advs.201801057
C. Fu, D. He, Y. Wang, X. Zhao, Enhanced microwave absorption performance of RGO-modified Co@C nanorods. Synth. Met. 257, 116187 (2019). https://doi.org/10.1016/j.synthmet.2019.116187
Y. Du, W. Liu, R. Qiang, Y. Wang, X. Han et al., Shell thickness-dependent microwave absorption of core-shell Fe3O4@C composites. ACS Appl. Mater. Interfaces. 6(15), 12997–13006 (2014). https://doi.org/10.1021/am502910d
Y. Zhang, Y. Huang, T. Zhang, H. Chang, P. Xiao et al., Broadband and tunable high-performance microwave absorption of an ultralight and highly compressible graphene foam. Adv. Mater. 27(12), 2049–2053 (2015). https://doi.org/10.1002/adma.201405788
H.-B. Zhao, J.-B. Cheng, J.-Y. Zhu, Y.-Z. Wang, Ultralight CoNi/rGO aerogels toward excellent microwave absorption at ultrathin thickness. J. Mater. Chem. C 7(2), 441–448 (2019). https://doi.org/10.1039/c8tc05239e
H. Zhang, B. Wang, A. Feng, N. Zhang, Z. Jia et al., Mesoporous carbon hollow microspheres with tunable pore size and shell thickness as efficient electromagnetic wave absorbers. Compos. Part B Eng. 167, 690–699 (2019). https://doi.org/10.1016/j.compositesb.2019.03.055
B. Wen, M.-S. Cao, Z.-L. Hou, W.-L. Song, L. Zhang et al., Temperature dependent microwave attenuation behavior for carbon-nanotube/silica composites. Carbon 65, 124–139 (2013). https://doi.org/10.1016/j.carbon.2013.07.110
B. Quan, W. Shi, S.J.H. Ong, X. Lu, P.L. Wang et al., Defect engineering in two common types of dielectric materials for electromagnetic absorption applications (Funct. Mater, Adv, 2019). https://doi.org/10.1002/adfm.201901236
H. Lv, H. Zhang, G. Ji, Z.J. Xu, Interface strategy to achieve tunable high frequency attenuation. ACS Appl. Mater. Interfaces. 8(10), 6529–6538 (2016). https://doi.org/10.1021/acsami.5b12662
G. Sun, B. Dong, M. Cao, B. Wei, C. Hu, Hierarchical dendrite-like magnetic materials of Fe3O4, gamma-Fe2O3, and Fe with high performance of microwave absorption. Chem. Mater. 23(6), 1587–1593 (2011). https://doi.org/10.1021/cm103441u
M.-S. Cao, X.-X. Wang, M. Zhang, J.-C. Shu, W.-Q. Cao et al., Electromagnetic response and energy conversion for functions and devices in low-dimensional materials. Adv. Funct. Mater. 29(25), 1807398 (2019). https://doi.org/10.1002/adfm.201807398
X. Liang, B. Quan, Z. Man, B. Cao, N. Li et al., Self-assembly three-dimensional porous carbon networks for efficient dielectric attenuation. ACS Appl. Mater. Interfaces. 11(33), 30228–30233 (2019). https://doi.org/10.1021/acsami.9b08365
Q. Liu, X. Liu, H. Feng, H. Shui, R. Yu, Metal organic framework-derived Fe/carbon porous composite with low Fe content for lightweight and highly efficient electromagnetic wave absorber. Chem. Eng. J. 314, 320–327 (2017). https://doi.org/10.1016/j.cej.2016.11.089
N. Li, G.-W. Huang, Y.-Q. Li, H.-M. Xiao, Q.-P. Feng et al., Enhanced microwave absorption performance of coated carbon nanotubes by optimizing the Fe3O4 nanocoating structure. ACS Appl. Mater. Interfaces. 9(3), 2973–2983 (2017). https://doi.org/10.1021/acsami.6b13142
Y. Cheng, J.Z.Y. Seow, H. Zhao, Z.J. Xu, G. Ji, A flexible and lightweight biomass-reinforced microwave absorber. Nano-Micro Lett. 12(1), 125 (2020). https://doi.org/10.1007/s40820-020-00461-x
Y. Yang, L. Xia, T. Zhang, B. Shi, L. Huang et al., Fe3O4@LAS/RGO composites with a multiple transmission-absorption mechanism and enhanced electromagnetic wave absorption performance. Chem. Eng. J. 352, 510–518 (2018). https://doi.org/10.1016/j.cej.2018.07.064
N. Zhang, Y. Huang, M. Zong, X. Ding, S. Li et al., Synthesis of ZnS quantum dots and CoFe2O4 nanoparticles co-loaded with graphene nanosheets as an efficient broad band EM wave absorber. Chem. Eng. J. 308, 214–221 (2017). https://doi.org/10.1016/j.cej.2016.09.065
H. Lv, Y. Guo, G. Wu, G. Ji, Y. Zhao et al., Interface polarization strategy to solve electromagnetic wave interference issue. ACS Appl. Mater. Interfaces. 9(6), 5660–5668 (2017). https://doi.org/10.1021/acsami.6b16223
Y. Lin, J. Dai, H. Yang, L. Wang, F. Wang, Graphene multilayered sheets assembled by porous Bi2Fe4O9 microspheres and the excellent electromagnetic wave absorption properties. Chem. Eng. J. 334, 1740–1748 (2018). https://doi.org/10.1016/j.cej.2017.11.150
T. Hanai, Theory of the dielectric dispersion due to the interfacial polarization and its application to emulsions. Kolloid-Zeitschrift 171(1), 23–31 (1960). https://doi.org/10.1007/BF01520320
J.B. Goodenough, Summary of losses in magnetic materials. IEEE Trans. Magn. 38(5), 3398–3408 (2002). https://doi.org/10.1109/TMAG.2002.802741
M.-S. Cao, J.-C. Shu, X.-X. Wang, X. Wang, M. Zhang et al., Electronic structure and electromagnetic properties for 2D electromagnetic functional materials in gigahertz frequency. Ann. Phys. 531(4), 1800390 (2019). https://doi.org/10.1002/andp.201800390
B. Zhao, W. Zhao, G. Shao, B. Fan, R. Zhang, Morphology-control synthesis of a core-shell structured NiCu alloy with tunable electromagnetic-wave absorption capabilities. ACS Appl. Mater. Interfaces. 7(23), 12951–12960 (2015). https://doi.org/10.1021/acsami.5b02716
J. Carrey, B. Mehdaoui, M. Respaud, Simple models for dynamic hysteresis loop calculations of magnetic single-domain nanoparticles: application to magnetic hyperthermia optimization. J. Appl. Phys. 109(8), 083921 (2011). https://doi.org/10.1063/1.3551582
C.-L. Zhu, M.-L. Zhang, Y.-J. Qiao, G. Xiao, F. Zhang et al., Fe3O4/TiO2 core/shell nanotubes: synthesis and magnetic and electromagnetic wave absorption characteristics. J. Phys. Chem. C 114(39), 16229–16235 (2010). https://doi.org/10.1021/jp104445m
D. Xu, X. Xiong, P. Chen, Q. Yu, H. Chu et al., Superior corrosion-resistant 3D porous magnetic graphene foam-ferrite nanocomposite with tunable electromagnetic wave absorption properties. J. Magn. Magn. Mater. 469, 428–436 (2019). https://doi.org/10.1016/j.jmmm.2018.09.019
X. Liang, Z. Man, B. Quan, J. Zheng, W. Gu et al., Environment-stable CoxNiy encapsulation in stacked porous carbon nanosheets for enhanced microwave absorption. Nano-Micro Lett. 12(1), 102 (2020). https://doi.org/10.1007/s40820-020-00432-2
R. Shu, Y. Wu, Z. Li, J. Zhang, Z. Wan et al., Facile synthesis of cobalt-zinc ferrite microspheres decorated nitrogen-doped multi-walled carbon nanotubes hybrid composites with excellent microwave absorption in the X-band. Compos. Sci. Technol. 184, 107839 (2019). https://doi.org/10.1016/j.compscitech.2019.107839
Z. Li, X. Li, Y. Zong, G. Tan, Y. Sun et al., Solvothermal synthesis of nitrogen-doped graphene decorated by superparamagnetic Fe3O4 nanoparticles and their applications as enhanced synergistic microwave absorbers. Carbon 115, 493–502 (2017). https://doi.org/10.1016/j.carbon.2017.01.036
Y. Wu, R. Shu, J. Zhang, Z. Wan, J. Shi et al., Oxygen vacancies regulated microwave absorption properties of reduced graphene oxide/multi-walled carbon nanotubes/cerium oxide ternary nanocomposite. J. Alloys Compd. 819, 152944 (2020). https://doi.org/10.1016/j.jallcom.2019.152944
X. Zhao, Y. Wang, D.S. Li, X. Bu, P. Feng, Metal-organic frameworks for separation. Adv. Mater. (2018). https://doi.org/10.1002/adma.201705189
R. Zhao, Z. Liang, R. Zou, Q. Xu, Metal-organic frameworks for batteries. Joule 2(11), 2235–2259 (2018). https://doi.org/10.1016/j.joule.2018.09.019
Y. Lu, Y. Wang, H. Li, Y. Lin, Z. Jiang et al., MOF-derived porous Co/C nanocomposites with excellent electromagnetic wave absorption properties. ACS Appl. Mater. Interfaces. 7(24), 13604–13611 (2015). https://doi.org/10.1021/acsami.5b03177
J. Li, P. Miao, K.-J. Chen, J.-W. Cao, J. Liang et al., Highly effective electromagnetic wave absorbing prismatic Co/C nanocomposites derived from cubic metal-organic framework. Compos. Part B Eng. 182, 107613 (2020). https://doi.org/10.1016/j.compositesb.2019.107613
B.-Y. Zhu, P. Miao, J. Kong, X.-L. Zhang, G.-Y. Wang et al., Co/C composite derived from a newly constructed metal-organic framework for effective microwave absorption. Cryst. Growth Des. 19(3), 1518–1524 (2019). https://doi.org/10.1021/acs.cgd.9b00064
H. Wang, L. Xiang, W. Wei, J. An, J. He et al., Efficient and lightweight electromagnetic wave absorber derived from metal organic framework-encapsulated cobalt nanoparticles. ACS Appl. Mater. Interfaces. 9(48), 42102–42110 (2017). https://doi.org/10.1021/acsami.7b13796
R. Qiang, Y. Du, D. Chen, W. Ma, Y. Wang et al., Electromagnetic functionalized Co/C composites by in situ pyrolysis of metal-organic frameworks (ZIF-67). J. Alloys Compd. 681, 384–393 (2016). https://doi.org/10.1016/j.jallcom.2016.04.225
K. Zhang, A. Xie, M. Sun, W. Jiang, F. Wu et al., Electromagnetic dissipation on the surface of metal organic framework (MOF)/reduced graphene oxide (RGO) hybrids. Mater. Chem. Phys. 199, 340–347 (2017). https://doi.org/10.1016/j.matchemphys.2017.07.026
H. Qiu, X. Zhu, P. Chen, S. Yang, X. Guo et al., Magnetic dodecahedral CoC-decoratedreduced graphene oxide as excellent electromagnetic wave absorber. J. Electron. Mater. 49(2), 1204–1214 (2020). https://doi.org/10.1007/s11664-019-07837-9
J. Yuan, Q. Liu, S. Li, Y. Lu, S. Jin et al., Metal organic framework (MOF)-derived carbonaceous Co3O4/Co microframes anchored on RGO with enhanced electromagnetic wave absorption performances. Synth. Met. 228, 32–40 (2017). https://doi.org/10.1016/j.synthmet.2017.03.020
K. Zhang, F. Wu, J. Li, M. Sun, A. Xie et al., Networks constructed by metal organic frameworks (MOFs) and multiwall carbon nanotubes (MCNTs) for excellent electromagnetic waves absorption. Mater. Chem. Phys. 208, 198–206 (2018). https://doi.org/10.1016/j.matchemphys.2018.01.008
Y. Yin, X. Liu, X. Wei, Y. Li, X. Nie et al., Magnetically aligned Co-C/MWCNTs composite derived from MWCNT-interconnected zeolitic imidazolate frameworks for a lightweight and highly efficient electromagnetic wave absorber. ACS Appl. Mater. Interfaces. 9(36), 30850–30861 (2017). https://doi.org/10.1021/acsami.7b10067
X. Xiao, W. Zhu, Z. Tan, W. Tian, Y. Guo et al., Ultra-small Co/CNTs nanohybrid from metal organic framework with highly efficient microwave absorption. Compos. Part B Eng. 152, 316–323 (2018). https://doi.org/10.1016/j.compositesb.2018.08.109
S. Lu, Y. Meng, H. Wang, F. Wang, J. Yuan et al., Great enhancement of electromagnetic wave absorption of MWCNTs@ carbonaceous CoO composites derived from MWCNTs-interconnected zeolitic imidazole framework. Appl. Surf. Sci. 481, 99–107 (2019). https://doi.org/10.1016/j.apsusc.2019.03.018
H. Chen, R. Hong, Q. Liu, S. Li, F. Huang et al., CNFs@carbonaceous Co/CoO composite derived from CNFs penetrated through ZIF-67 for high-efficient electromagnetic wave absorption material. J. Alloys Compd. 752, 115–122 (2018). https://doi.org/10.1016/j.jallcom.2018.04.142
X. Sun, X. Lv, M. Sui, X. Weng, X. Li et al., Decorating MOF-derived nanoporous Co/C in chain-like polypyrrole (PPy) aerogel: a lightweight material with excellent electromagnetic absorption. Materials 11(5), 781–793 (2018). https://doi.org/10.3390/ma11050781
X. Liu, L.-S. Wang, Y. Ma, Y. Qiu, Q. Xie et al., Facile synthesis and microwave absorption properties of yolk-shell ZnO-Ni-C/RGO composite materials. Chem. Eng. J. 333, 92–100 (2018). https://doi.org/10.1016/j.cej.2017.09.139
S. Kang, W. Zhang, Z. Hu, J. Yu, Y. Wang et al., Porous core-shell zeolitic imidazolate framework-derived Co/NPC@ZnO-decorated reduced graphene oxide for lightweight and broadband electromagnetic wave absorber. J. Alloys Compd. 818, 152932 (2020). https://doi.org/10.1016/j.jallcom.2019.152932
C. Zhou, C. Wu, D. Liu, M. Yan, Metal-organic framework derived hierarchical Co/C@V2O3 hollow spheres as a thin, lightweight, and high-efficiency electromagnetic wave absorber. Chem. Eur. J. 25(9), 2234–2241 (2019). https://doi.org/10.1002/chem.201805565
M. Liu, R. Tian, H. Chen, S. Li, F. Huang et al., One-dimensional chain-like MnO@Co/C composites for high-efficient electromagnetic wave absorbent. J. Magn. Magn. Mater. 499, 166289 (2020). https://doi.org/10.1016/j.jmmm.2019.166289
R. Wang, M. He, Y. Zhou, S. Nie, Y. Wang et al., Metal-organic frameworks self-templated cubic hollow Co/N/C@MnO2 composites for electromagnetic wave absorption. Carbon 156, 378–388 (2020). https://doi.org/10.1016/j.carbon.2019.09.063
K. Zhang, F. Wu, A. Xie, M. Sun, W. Dong, In situ stringing of metal organic frameworks by SiC nanowires for high-performance electromagnetic radiation elimination. ACS Appl. Mater. Interfaces. 9(38), 33041–33048 (2017). https://doi.org/10.1021/acsami.7b11592
R. Shu, Z. Wan, J. Zhang, Y. Wu, Y. Liu et al., Facile design of three-dimensional nitrogen-doped reduced graphene oxide/multi-walled carbon nanotube composite foams as lightweight and highly efficient microwave absorbers. ACS Appl. Mater. Interfaces. 12(4), 4689–4698 (2020). https://doi.org/10.1021/acsami.9b16134
N. Yang, Z.-X. Luo, G.-R. Zhu, S.-C. Chen, X.-L. Wang et al., Ultralight three-dimensional hierarchical cobalt nanocrystals/N-doped CNTs/carbon sponge composites with a hollow skeleton toward superior microwave absorption. ACS Appl. Mater. Interfaces. 11(39), 35987–35998 (2019). https://doi.org/10.1021/acsami.9b11101
Z. Li, X. Han, Y. Ma, D. Liu, Y. Wang et al., MOFs-derived hollow Co/C microspheres with enhanced microwave absorption performance. ACS Sustain. Chem. Eng. 6(7), 8904–8913 (2018). https://doi.org/10.1021/acssuschemeng.8b01270
Z. Zhang, Q. Zhu, X. Chen, Z. Wu, Y. He et al., Ni@C composites derived from Ni-based metal organic frameworks with a lightweight, ultrathin, broadband and highly efficient microwave absorbing properties. Appl. Phys. Express 12(1), 011001 (2019). https://doi.org/10.7567/1882-0786/aaeedc
B. Quan, G. Xu, H. Yi, Z. Yang, J. Xiang et al., Enhanced electromagnetic wave response of nickel nanoparticles encapsulated in nanoporous carbon. J. Alloys Compd. 769, 961–968 (2018). https://doi.org/10.1016/j.jallcom.2018.08.069
Z. Yang, Y. Zhang, M. Li, L. Yang, J. Liu et al., Surface architecture of Ni-based metal organic framework hollow spheres for adjustable microwave absorption. ACS Appl. Nano Mater. 2(12), 7888–7897 (2019). https://doi.org/10.1021/acsanm.9b01881
J. Yan, Y. Huang, Y. Yan, L. Ding, P. Liu, High-performance electromagnetic wave absorbers based on two kinds of nickel-based MOF-derived Ni@C microspheres. ACS Appl. Mater. Interfaces. 11(43), 40781–40792 (2019). https://doi.org/10.1021/acsami.9b12850
R. Yang, J. Yuan, C. Yu, K. Yan, Y. Fu et al., Efficient electromagnetic wave absorption by SiC/Ni/NiO/C nanocomposites. J. Alloys Compd. 816, 152519 (2020). https://doi.org/10.1016/j.jallcom.2019.152519
X. Liang, B. Quan, Y. Sun, G. Ji, Y. Zhang et al., Multiple interfaces structure derived from metal-organic frameworks for excellent electromagnetic wave absorption. Part. Part. Syst. Char. 34(5), 1700006 (2017). https://doi.org/10.1002/ppsc.201700006
Z. Zhang, Y. Lv, X. Chen, Z. Wu, Y. He et al., Porous flower-like Ni/C composites derived from MOFs toward high-performance electromagnetic wave absorption. J. Magn. Magn. Mater. 487, 165334 (2019). https://doi.org/10.1016/j.jmmm.2019.165334
R. Qiang, Y. Du, H. Zhao, Y. Wang, C. Tian et al., Metal organic framework-derived Fe/C nanocubes toward efficient microwave absorption. J. Mater. Chem. A 3(25), 13426–13434 (2015). https://doi.org/10.1039/C5TA01457C
S. Peng, S. Wang, G. Hao, C. Zhu, Y. Zhang et al., Preparation of magnetic flower-like carbon-matrix composites with efficient electromagnetic wave absorption properties by carbonization of MIL-101(Fe). J. Magn. Magn. Mater. 487, 165306 (2019). https://doi.org/10.1016/j.jmmm.2019.165306
P. Miao, R. Zhou, K. Chen, J. Liang, Q. Ban et al., Tunable Electromagnetic Wave Absorption Of Supramolecular Isomer-Derived Nanocomposites With Different Morphology. Adv. Mater. Interfaces 7(4), 1901820 (2020). https://doi.org/10.1002/admi.201901820
Y. Wang, W. Zhang, X. Wu, C. Luo, Q. Wang et al., Conducting polymer coated metal-organic framework nanoparticles: facile synthesis and enhanced electromagnetic absorption properties. Synth. Met. 228, 18–24 (2017). https://doi.org/10.1016/j.synthmet.2017.04.009
Z. Xiang, Y. Song, J. Xiong, Z. Pan, X. Wang et al., Enhanced electromagnetic wave absorption of nanoporous Fe3O4 @ carbon composites derived from metal-organic frameworks. Carbon 142, 20–31 (2019). https://doi.org/10.1016/j.carbon.2018.10.014
X. Liang, B. Quan, G. Ji, W. Liu, H. Zhao et al., Tunable dielectric performance derived from the metal-organic framework/reduced graphene oxide hybrid with broadband absorption. ACS Sustain. Chem. Eng. 5(11), 10570–10579 (2017). https://doi.org/10.1021/acssuschemeng.7b02565
W. Gu, J. Lv, B. Quan, X. Liang, B. Zhang et al., Achieving MOF-derived one-dimensional porous ZnO/C nanofiber with lightweight and enhanced microwave response by an electrospinning method. J. Alloys Compd. 806, 983–991 (2019). https://doi.org/10.1016/j.jallcom.2019.07.334
Y. Jiao, J. Li, A. Xie, F. Wu, K. Zhang et al., Confined polymerization strategy to construct polypyrrole/zeolitic imidazolate frameworks (PPy/ZIFs) nanocomposites for tunable electrical conductivity and excellent electromagnetic absorption. Compos. Sci. Technol. 174, 232–240 (2019). https://doi.org/10.1016/j.compscitech.2019.03.003
J. Ma, W. Liu, X. Liang, B. Quan, Y. Cheng et al., Nanoporous TiO2/C composites synthesized from directly pyrolysis of a Ti-based MOFs MIL-125(Ti) for efficient microwave absorption. J. Alloys Compd. 728, 138–144 (2017). https://doi.org/10.1016/j.jallcom.2017.08.274
L. Huang, C. Chen, X. Huang, S. Ruan, Y.-J. Zeng, Enhanced electromagnetic absorbing performance of MOF-derived Ni/NiO/Cu@C composites. Compos. Part B Eng. 164, 583–589 (2019). https://doi.org/10.1016/j.compositesb.2019.01.081
X. Zhang, J. Qiao, C. Liu, F. Wang, Y. Jiang et al., A MOF-derived ZrO2/C nanocomposite for efficient electromagnetic wave absorption. Inorg. Chem. Front. 7(2), 385–393 (2020). https://doi.org/10.1039/c9qi01259a
J. Xiong, Z. Xiang, J. Zhao, L. Yu, E. Cui et al., Layered NiCo alloy nanoparticles/nanoporous carbon composites derived from bimetallic MOFs with enhanced electromagnetic wave absorption performance. Carbon 154, 391–401 (2019). https://doi.org/10.1016/j.carbon.2019.07.096
Y. Liu, Z. Chen, W. Xie, F. Qiu, Y. Zhang et al., Enhanced microwave absorption performance of porous and hollow CoNi@C microspheres with controlled component and morphology. J. Alloys Compd. 809, 151837 (2019). https://doi.org/10.1016/j.jallcom.2019.151837
C. Liu, J. Qiao, X. Zhang, D. Xu, N. Wu et al., Bimetallic MOF-derived porous CoNi/C nanocomposites with ultra-wide band microwave absorption properties. New J. Chem. 43(42), 16546–16554 (2019). https://doi.org/10.1039/c9nj04115j
D. Liu, R. Qiang, Y. Du, Y. Wang, C. Tian et al., Prussian blue analogues derived magnetic FeCo alloy/carbon composites with tunable chemical composition and enhanced microwave absorption. J. Colloid Interface Sci. 514, 10–20 (2018). https://doi.org/10.1016/j.jcis.2017.12.013
W. Liu, S. Tan, Z. Yang, G. Ji, Hollow graphite spheres embedded in porous amorphous carbon matrices as lightweight and low-frequency microwave absorbing material through modulating dielectric loss. Carbon 138, 143–153 (2018). https://doi.org/10.1016/j.carbon.2018.06.009
J. Ouyang, Z. He, Y. Zhang, H. Yang, Q. Zhao, Trimetallic FeCoNi@C nanocomposite hollow spheres derived from metal-organic frameworks with superior electromagnetic wave absorption ability. ACS Appl. Mater. Interfaces. 11(42), 39304–39314 (2019). https://doi.org/10.1021/acsami.9b11430
F. Wang, N. Wang, X. Han, D. Liu, Y. Wang et al., Core-shell FeCo@carbon nanoparticles encapsulated in polydopamine-derived carbon nanocages for efficient microwave absorption. Carbon 145, 701–711 (2019). https://doi.org/10.1016/j.carbon.2019.01.082
L. Wang, B. Wen, X. Bai, C. Liu, H. Yang, NiCo alloy/carbon nanorods decorated with carbon nanotubes for microwave absorption. ACS Appl. Nano Mater. 2(12), 7827–7838 (2019). https://doi.org/10.1021/acsanm.9b01842
S. Wang, Y. Xu, R. Fu, H. Zhu, Q. Jiao et al., Rational construction of hierarchically porous Fe-Co/N-doped carbon/rGO composites for broadband microwave absorption. Nano-Micro Lett. 11(1), 76 (2019). https://doi.org/10.1007/s40820-019-0307-8
X. Xu, F. Ran, H. Lai, Z. Cheng, T. Lv et al., In Situ confined bimetallic metal-organic framework derived nanostructure within 3D interconnected bamboo-like carbon nanotube networks for boosting electromagnetic wave absorbing performances. ACS Appl. Mater. Interfaces. 11(39), 35999–36009 (2019). https://doi.org/10.1021/acsami.9b14754
Y. Zhang, Z. Yang, M. Li, L. Yang, J. Liu et al., Heterostructured CoFe@C@MnO2 nanocubes for efficient microwave absorption. Chem. Eng. J. 382, 123039 (2020). https://doi.org/10.1016/j.cej.2019.123039
R. Shu, W. Li, Y. Wu, J. Zhang, G. Zhang et al., Fabrication of nitrogen-doped cobalt oxide/cobalt/carbon nanocomposites derived from heterobimetallic zeolitic imidazolate frameworks with superior microwave absorption properties. Compos. Part B Engn. 178, 107518 (2019). https://doi.org/10.1016/j.compositesb.2019.107518
S. Wang, X. Ke, S. Zhong, Y. Lai, D. Qian, Y. Wang, Q. Wang, W. Jiang, Bimetallic zeolitic imidazolate frameworks-derived porous carbon-based materials with efficient synergistic microwave absorption properties: the role of calcining temperature. RSC Adv. 7(73), 46436–46444 (2017). https://doi.org/10.1039/c7ra08882e
X. Qi, J. Xu, Q. Hu, Y. Deng, R. Xie et al., Metal-free carbon nanotubes: synthesis, and enhanced intrinsic microwave absorption properties. Sci. Rep. 6, 28310–28310 (2016). https://doi.org/10.1038/srep28310
C. Wang, X. Han, P. Xu, X. Zhang, Y. Du et al., The electromagnetic property of chemically reduced graphene oxide and its application as microwave absorbing material. Appl. Phys. Lett. 98(7), 072906 (2011). https://doi.org/10.1063/1.3555436
H. Chen, Z. Huang, Y. Huang, Y. Zhang, Z. Ge et al., Synergistically assembled MWCNT/graphene foam with highly efficient microwave absorption in both C and X bands. Carbon 124, 506–514 (2017). https://doi.org/10.1016/j.carbon.2017.09.007
S.K. Singh, M.J. Akhtar, K.K. Kar, Hierarchical carbon nanotube-coated carbon fiber: ultra lightweight, thin, and highly efficient microwave absorber. ACS Appl. Mater. Interfaces. 10(29), 24816–24828 (2018). https://doi.org/10.1021/acsami.8b06673
A. Xie, F. Wu, M. Sun, X. Dai, Z. Xu et al., Self-assembled ultralight three-dimensional polypyrrole aerogel for effective electromagnetic absorption. Appl. Phys. Lett. 106(22), 222902 (2015). https://doi.org/10.1063/1.4921180
P. Zhang, X. Han, L. Kang, R. Qiang, W. Liu et al., Synthesis and characterization of polyaniline nanoparticles with enhanced microwave absorption. RSC Adv. 3(31), 12694–12701 (2013). https://doi.org/10.1039/C3RA40973B
M. Cai, A. Shui, X. Wang, C. He, J. Qian et al., A facile fabrication and high-performance electromagnetic microwave absorption of ZnO nanoparticles. J. Alloys Compd. 842, 155638 (2020). https://doi.org/10.1016/j.jallcom.2020.155638
M. Green, Z. Liu, R. Smedley, H. Nawaz, X. Li et al., Graphitic carbon nitride nanosheets for microwave absorption. Mater. Today Phys. 5, 78–86 (2018). https://doi.org/10.1016/j.mtphys.2018.06.005
C. Liang, Z. Wang, L. Wu, X. Zhang, H. Wang et al., Light and strong hierarchical porous SiC foam for efficient electromagnetic interference shielding and thermal insulation at elevated temperatures. ACS Appl. Mater. Interfaces. 9(35), 29950–29957 (2017). https://doi.org/10.1021/acsami.7b07735
R.B. Yang, W.F. Liang, C.W. Lou, J.H. Lin, Electromagnetic and microwave absorption properties of magnetic stainless steel powder in 2–18 GHz. J. Appl. Phys. 111(7), 07A338 (2012). https://doi.org/10.1063/1.3693764
F. Wang, C. Long, T. Wu, W. Li, Z. Chen et al., Enhancement of low-frequency magnetic permeability and absorption by texturing flaky carbonyl iron particles. J. Alloys Compd. 823, 153827 (2020). https://doi.org/10.1016/j.jallcom.2020.153827
Acknowledgements
The authors gratefully acknowledge financial support from Ministry of Science and Technology of China (MoST, 2016YFA0200200), the National Natural Science Foundation of China (NSFC, 21875114, 51373078, and 51422304) and NSF of Tianjin City (15JCYBJC17700).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, Z., Cai, Z., Wang, Z. et al. A Review on Metal–Organic Framework-Derived Porous Carbon-Based Novel Microwave Absorption Materials. Nano-Micro Lett. 13, 56 (2021). https://doi.org/10.1007/s40820-020-00582-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-020-00582-3