Highlights
-
The slot-die-coated porous PbI2:CsI film assisted with nitrogen blowing can promote the rapid and complete transformation of perovskite film.
-
The crystallinity and morphology of slot-die-coated perovskite film are significantly improved by controlling substrate temperature.
-
Fully slot-die-coated perovskite solar cells achieve a power conversion efficiency (PCE) of 18.13%, and fully roll-to-roll printed flexible PSCs achieve a PCE of 13.00% in ambient condition.
Abstract
Perovskite solar cells (PSCs) have attracted tremendous attention as a promising alternative candidate for clean energy generation. Many attempts have been made with various deposition techniques to scale-up manufacturing. Slot-die coating is a robust and facile deposition technique that can be applied in large-area roll-to-roll (R2R) fabrication of thin film solar cells with the advantages of high material utilization, low cost and high throughput. Herein, we demonstrate the encouraging result of PSCs prepared by slot-die coating under ambient environment using a two-step sequential process whereby PbI2:CsI is slot-die coated first followed by a subsequent slot-die coating of organic cations containing solution. A porous PbI2:CsI film can promote the rapid and complete transformation into perovskite film. The crystallinity and morphology of perovskite films are significantly improved by optimizing nitrogen blowing and controlling substrate temperature. A power conversion efficiency (PCE) of 18.13% is achieved, which is promising for PSCs fabricated by two-step fully slot-die-coated devices. Furthermore, PSCs with a 1 cm2 area yield a champion PCE of 15.10%. Moreover, a PCE of 13.00% is obtained on a flexible substrate by the roll-to-roll (R2R) coating, which is one of the highest reported cells with all layers except for metal electrode fabricated by R2R process under ambient condition.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
The organic–inorganic hybrid perovskite solar cells (PSCs) are considered one of the promising new-generation solar cells. The certified power conversion efficiency (PCE) has reached a remarkable value of 25.7% since the first report in 2009 [1, 2]. These achievements can be attributed to the intrinsic properties of the perovskite material, such as a large absorption coefficient, high charge mobility, low exciton binding energy and low temperature solution processing ability [3,4,5,6,7,8]. Numerous studies have been attempted to achieve high-quality perovskite films since then, including additives [9,10,11,12], solvent engineering [13,14,15], interface modification [16, 17], and scale-up techniques under ambient fabrication environment [18,19,20,21,22], which would considerably move the development of PSCs to commercialization.
However, most high-performance PSCs are mainly fabricated via spin-coating method due to their accessibility, high repeatability, facile control and suitability for anti-solvent [23, 24]. The major drawback is that spin-coating is unsuitable and difficult to match other scalable printing processes. Recently, growing investigations on PSCs prepared by scalable methods such as blade-coating and slot-die coating have been demonstrated, which are transferable and compatible with the roll-to-roll (R2R) process [25,26,27]. Among various scalable coating techniques, slot-die coating stands out owing to its high reported PCE, fast coating speeds, high material utilization, and matching with the R2R process [28,29,30]. It is well known that perovskite film plays an essential role in the performance of PSCs. Both one-step and two-step deposition methods have been broadly employed in the fabrication of PSCs. In one-step perovskite deposition, it is difficult to modulate the crystal growth for forming a uniform film, especially on a large scale [31]. While in the two-step deposition, PbI2 layer is firstly coated on the substrate by various methods and usually show excellent coverage, which is considered more suitable and reliable for the mass production process. Kim et al. demonstrated a two-step deposition of PSCs with a PCE of 10.9% by fully gravure printing and a PCE of 9.7% by partly R2R process [32]. Later, they adopt tert-butyl alcohol as an anti-solvent to obtain a wide processing window and achieved a PCE of 13.8% for fully R2R processed PSCs [33]. Burkitt et al. used fully R2R process to print p-i-n PSCs with a PCE of 12.2% [34]. Recently, Othman et al. demonstrated that fully R2R slot-die-coated triple-cation PSCs in ambient condition with underlying guanidinium iodide in hole transport layer showed a PCE of 12% [35]. Following the pioneering work by Gratzel group [36], high-performance and stable triple-cation planar heterojunction (PHJ) PSCs have been fabricated successfully via a low temperature sequential solution process [37, 38]. The device with ITO/SnO2/Perovskite/Spiro-OMeTAD/Ag exhibited a PCE of over 20% by spin coating. Meanwhile, devices can sustain about 80% of the initial PCE when stored in air (humidity = 40%) for over 500 h without any encapsulation. Therefore, if the PSCs fabricated by the scalable method can achieve similar PCEs, especially by R2R coating process, it would tremendously accelerate the commercialization process of PSCs.
In this work, we demonstrate the fabrication of fully slot-die-coated PSCs with a n-i-p structure in ambient condition using a two-step process. All layers of PSC devices were prepared by scalable slot-die coating process except the evaporated metal electrode. The initially formed PbI2:CsI film showing porous morphology is able to facilitate the fast and complete conversion of PbI2:CsI film to a pin-hole-free perovskite film which was assisted with heating and N2 blowing, leading to the fully slot-die-coated PSC devices with a max PCE of 18.13%. Furthermore, devices with a 1 cm2 area yielded a champion PCE of 15.10%. Remarkably, R2R processed PSC devices achieved a maximum PCE of 13.00%. The results provide significant and continued inspiration for processing high-performance, large-area flexible PSCs, which is helpful for promoting the potential commercialization of PSCs.
2 Experimental Details
2.1 Materials
All of the chemical materials were used directly without any purification, including tin oxide precursor (SnO2, 15% in H2O colloidal dispersion, Alfa Aesar), lead iodide (PbI2, 99%, Greatcell Solar), cesium iodide (CsI, 99%, Strem Chemicals, inc.), formamidinium iodide (HC(NH2)2I, 99.5%, Greatcell Solar), methylammonium chlorine (CH3NH3Cl, 99.5%, Xi'an Polymer Light Technology Corp.), methylammonium bromide (CH3NH3Br, 99.5%, Greatcell Solar), 2,20,7,70-tetrakis-(N,N-di-4-methoxyphenylamino)-9,90-spirobifluorene (Spiro-OMeTAD, 99%, Xi'an Polymer Light Technology Corp.), lithium bis(trifluoromethanesulfonyl)imide (Li-TFSI, 97%, Sigma-Aldrich), 4-tert-butylpyridine (4-tBP, 98%, Sigma-Aldrich), isopropanol (IPA, 99.5%,Sigma-Aldrich), N,N-dimethylformamide (99.8%, Sigma-Aldrich), chlorobenzene (99.8%, Sigma-Aldrich), and acetonitrile (ACN, 99.95%, Sigma-Aldrich). ITO glass substrates were purchased from Shenzhen Display, China.
2.2 Materials Characterization
UV-Vis spectra were recorded on a Lambda 35 Perkin-Elmer absorption spectrometer. PL spectra were recorded using a fluorescence spectrophotometer (LS55, Perkin-Elmer). XRD patterns were obtained using a Bruker D8 Advance X-ray Diffractometer operating under Cu Kα radiation (40 kV, 40 mA) equipped with a LynxEye detector. The SEM images of the films were taken with a Zeiss Merlin field emission SEM.
2.3 Device Fabrication
2.3.1 Slot-Die Coated Devices on ITO/glass
The ITO/glass substrate was ultrasonically cleaned using detergents/H2O, distilled water, acetone and isopropanol for 5 min sequentially. Then, dried by clean N2 flow and treated by UV-ozone for 15 min at room temperature. For the electron transport layer, the SnO2 nanoparticles solution that was diluted by H2O to half of the original concentration and filtered using a 0.22 μm PVDF filter, was deposited by slot-die coating at a speed of 5 mm s−1 with a 1 µL cm−2 solution in ambient air, and followed by a post-annealing at 150 °C for 30 min. Because SnO2 layer has been extensively used for the slot-die coating for PSCs, and an optimal thickness for perovskite devices has also been obtained [39], thus no further optimization was conducted in this work. After depositing the SnO2 film, the perovskite layer was formed via a two-step slot-die coating deposition in ambient condition. The mixture solution of PbI2:CsI (599.3 mg: 33.8 mg in 900 µL DMF and 100 µL DMSO) was slot-die coated at a head moving speed of 5 mm s−1 with a 1 µL cm−2 solution feed rate on the stationary SnO2 layer, and a gap between the slot-die head and the substrate was controlled at 200 µm. The slot-die coated PbI2:CsI films were heated at 70 °C for 3 min in ambient air. After cooling down of the PbI2:CsI film, the mixture solution of FAI: MABr: MACl in IPA was slot-die coated at a speed of 2 mm s−1 with a 1 µL cm−2 solution feed on the PbI2:CsI film without heating, and then post-annealed at 150 °C for 15 min in air. Subsequently, the Spiro-OMeTAD solution was drop casted or slot-die coated assisted by heating and gas blowing in ambient condition, where 1 mL Spiro-OMeTAD/chlorobenzene (90 mg mL−1) solution was employed with the addition of 10 µL tBP and 45 µl Li-TFSI/ACN (170 mg mL−1). Finally, 100 nm-thick Ag electrode was deposited through thermal evaporation with a mask at a pressure of 8 × 10–6 mbar, resulting in an active area of 0.1 or 1 cm2.
2.3.2 R2R Coated Devices on Flexible ITO/PET
The R2R coating of SnO2 was carried out by the reverse-gravure coating method, using a Mino-Labo™printer (MAHY-1310; Yasui Seiki Co.Ltd). The coating was conducted at 0.16 m min−1 bed speed and 16 rpm of 13 mm wide reverse-gravure roll speed to deposit the 13 mm wide continuous SnO2 layer in the middle of the ITO/PET substrate (width: 25 mm). The coated wet SnO2 film was dried on-line at 135 °C for 10–12 seconds on a hot plate to remove the solvent. A PbI2:CsI solution (599.3 mg: 33.8 mg in 900 μL DMF and 100 μL DMSO) was slot-die coated on top of the SnO2 surface (70 °C) at the feed rate of 18 μL min−1 and the bed speed of 0.3 m min−1. The formed PbI2:CsI film was then annealed at 70 °C assisted with N2 blowing. The perovskite conversion was conducted by slot-die coating of a mixed solution of FAI: MABr: MACl (60 mg: 6 mg: 6 mg in 1 mL IPA) at a bed speed of 0.3 m min−1, solution feed rate of 40 μL min−1 followed by annealing at 135 °C. Finally, Spiro-OMeTAD was slot-die coated at the bed temperature of 60 °C, bed speed of 0.3 m min−1 and feed rate of 40 uL min−1 without further annealing. The completed film was cut into 2.5 cm × 2.5 cm and 100 nm-thick Ag electrode was deposited through thermal evaporation as described in Sect. 2.3.1.
2.4 Device Measurements
Current density–voltage (J-V) curves of the devices were measured by a Keithley 2400 Source Meter under standard solar irradiation (AM 1.5 G, 100 mW cm−2). The light intensity was calibrated using a reference cell (Hamamatsu S1133 with KG5 filter and 2.8 × 2.4 mm2 of photosensitive area), which was calibrated by a certified reference cell (PV Measurements, certified by NREL) under 1000 W m−2 AM 1.5G illumination from a Newport LED lamp source with a ABA grade spectrum.
3 Results and Discussion
3.1 Fabrication of Perovskite Film
Figure 1 shows the fabrication schematic of PSCs using the two-step process with a device structure of ITO glass/SnO2/Perovskite/Spiro-OMeTAD/Ag. Briefly, SnO2 was slot-die coated on glass, followed by PbI2:CsI film. The quality of the PbI2:CsI film was first checked by a dipping process into the cations containing solution. Thereafter, the cation containing was also slot-die coated followed by drop casting of the hole transport layer. Finally, the hole transport layer of Spiro-OMeTAD was also slot-die coated, resulting in fully slot-die coated devices.
The quality and density of the PbI2:CsI film strongly affect the perovskite film quality in a two-step process. Heating is a common way to dry film to reduce the effect of humidity when the wet film is deposited [40,41,42]. The PbI2:CsI film tends to form a dense layer if drying dynamics is not controlled, as shown in Fig. S1a. Hence, an additional slot-die head was attached to channel N2 blowing over the freshly slot-die coated PbI2:CsI wet film as shown in Fig. 1. N2 blowing enables homogenous and porous morphology formation of the PbI2:CsI film, which provides channels facilitating cations to penetrate throughout the bulk of the PbI2:CsI film and enable formation of a pin-hole free and fully converted homogenous perovskite film. PSCs have been demonstrated to be more efficient and stable by combining MA, FA and Cs cations [43,44,45]. Therefore, a similar strategy herein was employed to fabricate perovskite films. For comparison, the PbI2:CsI films were dipped into the FAI/MABr/MACl solution at two different concentrations of 30 and 60 mg mL−1, respectively. The scanning electron microscope (SEM) images of the resulting films are shown in Fig. 2a, b. Clearly, the formed perovskite film at the higher concentration displays a much smoother surface than that one with the lower concentration. Hence, a 60 mg mL−1 FAI/MABr/MACl solution was used for further optimization and translation to slot-die coating, unless otherwise specified. One of the striking advantages of using slot-die coating compared to dipping is that much less perovskite precursor solution is required for each device. Accordingly, slot-die coating was adopted for the deposition of FAI/MABr/MACl solution. As expected, a high-quality perovskite film was achieved through this sequential process (Fig. 2c).
In the two-step fabrication process, the quality and density of PbI2:CsI films are significant keys to facilitating the efficient conversion, leading to the desired perovskite films. The gas blowing and substrate-heating approaches are important factors that can be utilized in tandem with slot-die coating of solution to achieve desired films. Both of them can also minimize the influence of surrounding humidity to improve perovskite crystallization when being processed under an ambient environment [46]. The SnO2-coated substrates were heated at the different bed temperatures, and the PbI2:CsI films were deposited on top of the heated substrates. The morphologies of PbI2:CsI films are well controlled by precise adjustment of the bed temperature and monitored by SEM. As shown in Fig. 3a-c, there are more pin-holes present within the PbI2:CsI film when prepared at 60 °C than that at 70 °C. When the bed temperature was further increased to 80 °C, the PbI2:CsI films tend to become compact, which is attributed to the fact that the solvent evaporates much faster at the higher temperatures, causing PbI2:CsI crystals to precipitate quickly, forming a densely packed film. Figures 3d-f are the SEM images of perovskite films formed on the above-deposited PbI2:CsI films at room temperature via slot-die coating of FAI/MABr/MACl solution. The perovskite grain size is summarized by analyzing the size of 150 grains through Nano Measurer software, as shown in Fig. S2. The grain size increases initially along with the bed temperature changing from 60 to 70 °C, and then decreases when the bed temperature reached 80 °C. This trend can be attributed to the supersaturation of PbI2 crystals at high bed temperature, leading to the excessive incomplete converted PbI2, which will be discussed in detail below. The optimal number of pores would provide enough space for FAI/MABr/MACl to diffuse into PbI2:CsI films, enabling complete conversion to perovskite. On the contrary, too densely packed PbI2:CsI film hinders the solution diffusion into the PbI2:CsI bulk film, inhibiting efficient interaction between PbI2:CsI and FAI/MABr/MACl, causing incomplete conversion to perovskite and negatively impacting device performance. Therefore, the quality of PbI2:CsI films controlled by bed temperature exhibits considerable effects on the fabrication of high-quality perovskite films. Thus, the results suggest that an optimal porous morphology of the PbI2:CsI film is critical to form smooth, homogeneous, fully converted perovskite films with large grains, while a dense PbI2:CsI layer leads to the incomplete conversion into perovskite [47].
3.2 Characterization of Perovskite Film
Figure 4a shows UV–vis absorption spectra of the perovskite films fabricated at different bed temperatures using a standard detector. All the perovskite films exhibit similar absorption as previously reported. The XRD results are displayed in Fig. 4b. When the bed temperature increased to 80 °C, a small peak at 2θ = 12.7° distinctly appeared in the XRD patterns. This typical peak is ascribed to the unreacted excessive PbI2 crystals that primarily reside at the bottom of perovskite film. For investigating the effect of bed temperature on photogenerated charge carriers of the perovskite film, the steady-state photoluminescence (PL) spectra were measured on perovskite films prepared on glass substrate using the same two-step process (Fig. 4c). The perovskite film fabricated at 70 °C presents the highest PL intensity, implying that the nonradiative recombination of perovskite film was significantly suppressed at this bed temperature. The PL peak of perovskite film fabricated at 80 °C has a small redshift, which indicates a higher trap density in perovskite film [48]. Therefore, the increased recombination loss and reduced charge collection of the perovskite film prepared at 80 °C will have a negative influence on the solar cell performance.
The J-V curves and performance parameters of PSC devices fabricated from the above perovskite films prepared at different bed temperatures are shown and summarized in Fig. 4d and Table 1, respectively. Slot-die coating was used for the deposition of SnO2 and perovskite layers, except that Spiro-OMeTAD hole transport layer was coated by drop-casting. The short-circuit current (Jsc) increased when the bed temperature increased from 60 to 70 °C. On the contrary, the Jsc slightly decreased with increasing the bed temperature to 80 °C. The highest Jsc of 22.11 mA cm−2 was achieved at the optimized bed temperature of 70 °C. Meanwhile, the fill factor (FF) was also improved to 75.2%, resulting in the final PCE of 17.96%. The achieved device results comply with the previous result analysis from SEM, PL and XRD. Conspicuously, a suitable bed temperature is crucial in determining PbI2:CsI film morphology and in turn final device performance. The bed temperature at 80 °C accelerates solvent evaporation, resulting in the unavoidable high density of PbI2:CsI film, which causes the incomplete conversion of PbI2:CsI to perovskite. At this point, slot-die coating as an effective way to deposit PbI2:CsI and perovskite film at the certain temperatures range has been demonstrated. This setup is believed to be readily transferred to the R2R continuous process.
3.3 Photovoltaic Performance of Fully Slot-Die Coated PSCs
Notwithstanding the impressive performance parameters were obtained from the slot-die coated perovskite layer on the glass substrate, the industrial compatible process requires all layers to be fabricated with scalable deposition strategies. Figure 5a shows a SEM cross-section of the PSCs, in which all layer but the electrodes, namely SnO2, perovskite layer and Spiro-OMeTAD layer, were slot-die coated. The thickness of the perovskite film reaches about 650 nm. The J-V curves of the best performance of PSCs are shown in Fig. 5b. The champion cell exhibits an open-circuit voltage (Voc) of 1.08 V, a Jsc of 22.09 mA cm−2, an FF of 76.01%, and a PCE of 18.13% in a reverse scan. A steady-state PCE of 17.57% was obtained (Fig. 5c). Extending slot-die coating to large-area fabrication, 1 cm2 device was fabricated via the same process (Fig. S3). J-V curves of 8 PSC devices are presented in Fig. 5d, and the corresponding PCEs are shown in the inset. The champion 1 cm2 device shows a PCE of 15.10%, which demonstrates that large-area PSCs could be effectively fabricated by slot-die coating in ambient conditions.
3.4 Fully R2R Processed PSCs
The slot-die coating was then transferred to R2R coating process (Fig. 6a). The flexible ITO/PET substrate was continuously moved from an unwind roller, passing the coating head and dryer, and finally to the rewind roller. When each coating run was completed, the substrate was collected on the rewind roller. To start, a thin SnO2 film was first coated by micro-gravure printing, followed by slot-die coated of the PbI2:CsI layer which was dried by N2 blowing, and finally converted to the perovskite film by slot-die coating of FAI/MABr/MACl solution. The detailed R2R coating conditions are described in the experimental session. As shown in Fig. 6a, hot plate-1 is employed to heat the wet film during the coating process as a bed temperature, and the hot plate-2 is used to anneal the dried film. The best performance of PSCs using the R2R coating process present a Voc of 1.00 V, a Jsc of 21.45 mA cm−2, an FF of 60.59, and a PCE of 13.00% in a reverse scan (Fig. 6b and Table 2). As shown in Table 2, the hysteresis behavior of R2R coated devices is worse than the slot-die coated ITO/glass substrates. Normally, it is very difficult to control morphology and interface properties of PSCs on flexible substrate using R2R coating process, which would result in more traps in thin film and interface. The trap assisted charge recombination may occur at the interface between the SnO2 layer and the perovskite layer. Thus, both ion movement and traps enhance the hysteresis behavior [49,50,51]. Figure 6c presents the statistical distribution of the PCEs based on 25 PSCs, and the average PCE is about 11.30%.
4 Conclusions
In summary, high-quality perovskite films are successfully prepared in ambient conditions via slot-die coating on ITO/glass substrates and continuous R2R coating on flexible substrates. The influence of bed temperature on the morphology of PbI2:CsI film during the coating was fully investigated. PL and XRD results support the explanation of variable device performances in solar cells when prepared at the different temperatures. Planar n-i-p PSCs with a PCE of 18.13% was achieved by fully slot-die coating. A PCE of 15.10% was achieved for PSCs with an area of 1 cm2. Furthermore, the flexible PSC with a PCE of 13.00% was obtained on ITO/PET substrate by the R2R coating process, which is currently one of the highest perovskite performances for fully R2R fabricated PSCs in ambient air. These results will undoubtedly help further pave the way in improving the performance of the large scale PSCs in ambient conditions and catalyse the pursuit towards low cost mass production in the future.
References
A. Kojima, K. Teshima, Y. Shirai, T. Miyasaka, Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131(17), 6050–6051 (2009). https://doi.org/10.1021/ja809598r
S.P. Dunfield, L. Bills, F. Zhang, J.M. Luther, K. Zhu et al., From defects to degradation: a mechanistic understanding of degradation in perovskite solar cell devices and modules. Adv. Energy Mater. 10(26), 1904054 (2020). https://doi.org/10.1002/aenm.201904054
Z.H. Dai, S. Yadavalli, M. Chen, Y. Qi, N.P. Padture, Interfacial toughening with self-assembled monolayers enhances perovskite solar cell reliability. Science 372(6542), 618–622 (2021). https://doi.org/10.1126/science.abf5602
S.W. Song, S.J. Yang, W. Choi, H. Lee, W. Sung et al., Molecular engineering of organic spacer cations for efficient and stable formamidinium perovskite solar cell. Adv. Energy Mater. 10(42), 2001759 (2020). https://doi.org/10.1002/aenm.202001759
H.Y. Li, C.T. Zuo, A.D. Scully, D. Angmo, J.L. Yang et al., Recent progress towards roll-to-roll manufacturing of perovskite solar cells using slot-die processing. Flex. Print. Elecron. 5, 014006 (2020). https://doi.org/10.1088/2058-8585/ab639e
K.J. Liao, C.B. Li, L.S. Xie, Y. Yuan, S.R. Wang et al., Hot-casting large-grain perovskite film for efficient solar cells: film formation and device performance. Nano-Micro Lett. 12, 156 (2020). https://doi.org/10.1007/s40820-020-00494-2
S. Ngqoloda, C.J. Arendse, T.F. Muller, P.F. Miceli, S. Guha et al., Air-stable hybrid perovskite solar cell by sequential vapor deposition in a single reactor. ACS Appl. Energy Mater. 3(3), 2350–2359 (2020). https://doi.org/10.1021/acsaem.9b01925
D.Q. Bi, X. Li, J.V. Milic, D.J. Kubicki, N. Pellet et al., Multifunctional molecular modulators for perovskite solar cells with over 20% efficiency and high operational stability. Nat. Commun. 9, 4482 (2018). https://doi.org/10.1038/s41467-018-06709-w
H. Min, M. Kim, S.U. Lee, H. Kim, G. Kim et al., Efficient, stable solar cells by using inherent bandgap of α-phase formamidinium lead iodide. Science 336(6466), 749–753 (2019). https://doi.org/10.1126/science.aay7044
M. Kim, G.H. Kim, T.K. Lee, I.W. Choi, Y. Jo et al., Methylammonium chloride induces intermediate phase stabilization for efficient perovskite solar cells. Joule 3(9), 2179–2192 (2019). https://doi.org/10.1016/j.joule.2019.06.014
W.J. Zhao, J. Xu, K. He, Y. Cai, S.M. Yang et al., A special additive enables all cations and anions passivation for stable perovskite solar cells with efficiency over 23%. Nano-Micro Lett. 13, 169 (2021). https://doi.org/10.1007/s40820-021-00688-2
H. Ren, S.D. Yu, L.F. Chao, Y.D. Xia, Y.H. Sun et al., Efficient and stable ruddlesden-popper perovskite solar cell with tailored interlayer molecular interaction. Nat. Photonics 14, 154–163 (2020). https://doi.org/10.1038/s41566-019-0572-6
S. Ghosh, T. Singh, Role of ionic liquids in organic-inorganic metal halide perovskite solar cells efficiency and stability. Nano Energy 63, 103828 (2019). https://doi.org/10.1016/j.nanoen.2019.06.024
K.N. Noel, S.N. Habisreutinger, B. Wenger, M.T. Klug, M.T. Horantner et al., A low viscosity, low boiling point, clean solvent system for the rapid crystallisation of highly specular perovskite films. Energy Environ. Sci. 10(1), 145–152 (2017). https://doi.org/10.1039/c6ee02373h
Z.Q. Lin, H.J. Lian, B. Ge, Z.R. Zhou, H.Y. Yuan et al., Mediating the local oxygen-bridge interactions of oxysalt/perovskite interface for defect passivation of perovskite photovoltaics. Nano-Micro Lett. 13, 177 (2021). https://doi.org/10.1007/s40820-021-00683-7
J. Xiong, B.C. Yang, C.H. Cao, R.S. Wu, Y.L. Huang et al., Interface degradation of perovskite solar cells and its modification using an annealing-free TiO2 NPs layer. Org. Electron. 30, 30–35 (2016). https://doi.org/10.1016/j.orgel.2015.12.010
I.A. Howard, T. Abzieher, I.M. Hossain, H. Eggers, F. Schackmar et al., Coated and printed perovskites for photovoltaic applications. Adv. Mater. 31(26), 1806702 (2019). https://doi.org/10.1002/adma.201806702
J.W. Lee, D.K. Lee, D.N. Jeong, N.G. Park, Control of crystal growth toward scalable fabrication of perovskite solar cells. Adv. Funct. Mater. 29(47), 1807047 (2019). https://doi.org/10.1002/adfm.201807047
F. Huang, M.J. Li, P. Siffalovic, G.Z. Cao, J.J. Tian, From scalable solution fabrication of perovskite films towards commercialization of solar cells. Energy Environ. Sci. 12(2), 518–549 (2019). https://doi.org/10.1039/c8ee03025a
M.L. Xie, H. Lu, L.P. Zhang, J. Wang, Q. Luo et al., Fully solution-processed semi-transparent perovskite solar cells with ink-jet printed silver nanowires top electrode. Sol. RRL 2(2), 1700184 (2018). https://doi.org/10.1002/solr.201700184
J.H. Chang, K. Liu, S.Y. Lin, Y.B. Yuan, C.H. Zhou et al., Solution-processed perovskite solar cells. J. Cent. South Univ. 27, 1104–1133 (2020). https://doi.org/10.1007/s11771-020-4353-7
D. Angmo, G. Deluca, A.D. Scully, A.S.R. Chesman, A. Seeber et al., A lab-to-fab study toward roll-to-roll fabrication of reproducible perovskite solar cells under ambient room conditions. Cell Rep. Phys. Sci. 2(1), 100293 (2021). https://doi.org/10.1016/j.xcrp.2020.100293
F.Z. Li, Y. Zhang, K.J. Jiang, C.S. Zhang, J.H. Huang et al., A novel strategy for scalable high-efficiency planar perovskite solar cells with new precursors and cation displacement approach. Adv. Mater. 30(44), 1804454 (2018). https://doi.org/10.1002/adma.201804454
W.Q. Wu, P.N. Rudd, Q. Wang, Z.B. Yang, J.S. Huang, Blading phase-pure formamidinium-alloyed perovskites for high-efficiency solar cells with low photovoltage deficit and improved stability. Adv. Mater. 32(28), 2000995 (2020). https://doi.org/10.1002/adma.202000995
C.T. Zuo, D. Vak, D. Angmo, L.M. Ding, M. Gao, One-step roll-to-roll air processed high efficiency perovskite solar cells. Nano Energy 46, 185–192 (2018). https://doi.org/10.1016/j.nanoen.2018.01.037
C.D. Gong, S.C. Tong, K.Q. Huang, H.Y. Li, H. Huang et al., Flexible planar heterojunction perovskite solar cells fabricated via sequential roll-to-roll microgravure printing and slot-die coating deposition. Sol. RRL 4(2), 1900304 (2019). https://doi.org/10.1002/solr.201900204
J.E. Kim, S.S. Kim, C.T. Zuo, M. Gao, D. Vak et al., Humidity-tolerant roll-to-roll fabrication of perovskite solar cells via polymer-additive-assisted hot slot die deposition. Adv. Funct. Mater. 29(26), 1809194 (2019). https://doi.org/10.1002/adfm.201809194
Y.J. Heo, J.E. Kim, H. Weerasinhe, D. Angmo, T.S. Qin et al., Printing-friendly sequential deposition via intra-additive approach for rollto-roll process of perovskite solar cells. Nano Energy 41, 443–451 (2017). https://doi.org/10.1016/j.nanoen.2017.09.051
Y.Y. Kim, E.Y. Park, T.Y. Yang, J.H. Noh, T.J. Shin et al., Fast two-step deposition of perovskite via mediator extraction treatment for large-area, high performance perovskite solar cells. J. Mater. Chem. A 6(26), 12447–12454 (2018). https://doi.org/10.1039/c8ta02868k
Y. Li, L. Ji, R.G. Liu, A review on morphology engineering for highly efficient and stable hybrid perovskite solar cells. J. Mater. Chem. A 6(27), 12842–12875 (2018). https://doi.org/10.1039/c8ta04120b
Y.Y. Kim, T.Y. Yang, R. Suhonen, M. Valimaki, T. Maaninen et al., Gravure-printed flexible perovskite solar cells: toward roll-to-roll manufacturing. Adv. Sci. 6(7), 1802094 (2019). https://doi.org/10.1002/advs.201802094
Y.Y. Kim, T.Y. Yang, R. Suhonen, A. Kemppainen, K. Hwang et al., Roll-to-roll gravure-printed flexible perovskite solar cells using eco-friendly antisolvent bathing with wide processing window. Nat. Comm. 11, 5146 (2020). https://doi.org/10.1038/s41467-020-18940-5
D. Burkitt, R. Patidar, P. Greenwood, K. Hooper, J. Mcgettric et al., Roll-to-roll slot-die coated P-I-N perovskite solar cells using acetonitrile based singly step perovskite solvent system. Sustain. Energy Fuels 4(7), 3340–3351 (2020). https://doi.org/10.1039/D0SE00460J
M. Othman, F. Zheng, A. Seeber, A.S.R. Chesman, A.D. Scully et al., Millimeter-sized clusters of triple cation perovskite enables highly efficient and reproducible roll-to-roll fabricated inverted perovskite solar cells. Adv. Funct. Mater. (2021). https://doi.org/10.1002/adfm.202110700
J. Burschka, N. Pellet, S.J. Moon, B.R. Humphry, P. Gao et al., Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–319 (2013). https://doi.org/10.1038/nature12340
C.H. Wang, C.J. Zhang, S.T. Wang, G. Liu, H.Y. Xia et al., Low-temperature processed, efficient, and highly reproducible cesium-doped triple cation perovskite planar heterojunction solar cells. Sol. RRL 2(2), 1700209 (2018). https://doi.org/10.1002/solr.201700209
K.Q. Huang, Y.Y. Peng, Y.X. Gao, J. Shi, H.Y. Li et al., High-performance flexible perovskite solar cells via precise control of electron transport layer. Adv. Energy Mater. 9(44), 1901419 (2019). https://doi.org/10.1002/aenm.201901419
T.L. Bu, J. Li, F. Zheng, W.J. Chen, X.M. Wen et al., Universal passivation strategy to slot-die printed SnO2 for hysteresis-free efficient flexible perovskite solar module. Nat. Commun. 9, 4609 (2018). https://doi.org/10.1038/s41467-018-07099-9
C.T. Zuo, A. Scully, D. Yak, W.L. Tan, X.C. Jiao et al., Self-assembled 2D perovskite layers for efficient printable solar cells. Adv. Energy Mater. 9(4), 1803258 (2019). https://doi.org/10.1002/aenm.201803258
H. Wu, C.J. Zhang, K.X. Ding, L.J. Wang, Y.L. Gao et al., Efficient planar heterojunction perovskite solar cells fabricated by in-situ thermal-annealing doctor blading in ambient condition. Org. Electron. 45, 302–307 (2017). https://doi.org/10.1016/j.orgel.2017.03.017
C.C. Boyd, R. Cheacharoen, K.A. Bush, R. Prasanna, T. Leijtens et al., Barrier design to prevent metal-induced degradation and improve thermal stability in perovskite solar cells. ACS Energy Lett. 3(7), 1772–1778 (2018). https://doi.org/10.1021/acsenergylett.8b00926
F.M. Li, Z.T. Shen, Y.J. Weng, Q. Lou, C. Chen et al., Novel electron transport layer material for perovskite solar cells with over 22% efficiency and long-term stability. Adv. Funct. Mater. 30(45), 2004933 (2020). https://doi.org/10.1002/adfm.202004933
K. Ma, H.R. Atapattu, Q.C. Zhao, Y. Gao, B.P. Finkenauer et al., Multifunctional conjugated ligand engineering for stable and efficient perovskite solar cells. Adv. Mater. 33(32), 2100791 (2021). https://doi.org/10.1002/adma.202100791
M.M. Tavakoli, M. Saliba, P. Yadav, P. Holzhey, A. Hagfeldt et al., Synergistic crystal and interface engineering for efficient and stable perovskite photovoltaics. Adv. Energy Mater. 9(1), 1802646 (2019). https://doi.org/10.1002/aenm.201802646
Q.D. Tai, P. You, H.Q. Sang, Z.K. Liu, C.L. Hu et al., Efficient and stable perovskite solar cells prepared in ambient air irrespective of the humidity. Nat. Commun. 7, 11105 (2016). https://doi.org/10.1038/ncomms11105
T.J. Jacobsson, J.P. Correa, E.H. Anaraki, B. Philippe, S.D. Stranks et al., Unreacted PbI2 as a double-edged sword for enhancing the performance of perovskite solar cells. J. Am. Chem. Soc. 138(32), 10331–10343 (2016). https://doi.org/10.1021/jacs.6b06320
J.J. Tian, Q.F. Xue, X.F. Tang, Y.X. Chen, N. Li et al., Dual interfacial design for efficient CsPbI2Br perovskite solar cells with improved photostability. Adv. Mater. 31(23), 1901152 (2019). https://doi.org/10.1002/adma.201901152
P.Y. Liu, W. Wang, S.M. Liu, H.G. Yang, Z.P. Shao, Fundamental understanding of photocurrent hysteresis in perovskite solar cells. Adv. Energy Mater. 9(13), 1803017 (2019). https://doi.org/10.1002/aenm.201803017
W. Tress, J.P.C. Baena, M. Saliba, A. Abate, M. Graetzel, Inverted current-voltage hysteresis in mixed perovskite solar cells: polarization, energy barriers, and defect recombination. Adv. Energy Mater. 6(19), 1600396 (2016). https://doi.org/10.1002/aenm.201600396
M.F. Ayguler, A.G. Hugnagel, P. Rieder, M. Wussler, W. Jaegermann, Influence of fermi level alignment with tin oxide on the hysteresis of perovskite solar cells. ACS Appl. Mater. Interfaces 10(14), 11414–11419 (2018). https://doi.org/10.1021/acsami.8b00990
Acknowledgements
The authors acknowledge support from the Australian Centre for Advanced Photovoltaics (ACAP) program funded by the Australian Government through the Australian Renewable Energy Agency (ARENA), the Devices & Engineered System Program of CSIRO Manufacturing. HL and JY acknowledge support from the National Natural Science Foundation of China (Grant No. 52173192) and the National Key Research and Development Program of China (Grant No. 2017YFA0206600). HL also acknowledges the support from the Key Innovation Project of Graduate of Central South University (Grant No. 2018ZZTS106) and China Scholarship Council program.
Funding
Open access funding provided by Shanghai Jiao Tong University.
Author information
Authors and Affiliations
Corresponding authors
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, H., Zuo, C., Angmo, D. et al. Fully Roll-to-Roll Processed Efficient Perovskite Solar Cells via Precise Control on the Morphology of PbI2:CsI Layer. Nano-Micro Lett. 14, 79 (2022). https://doi.org/10.1007/s40820-022-00815-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-022-00815-7