The current issues and recent advances in polymer/inorganic composite electrolytes are reviewed.
-
The molecular interaction between different components in the composite environment is highlighted for designing high-performance polymer/inorganic composite electrolytes.
-
Inorganic filler properties that affect polymer/inorganic composite electrolyte performance are pointed out.
-
Future research directions for polymer/inorganic composite electrolytes compatible with high-voltage lithium metal batteries are outlined.
Solid-state electrolytes (SSEs) are widely considered the essential components for upcoming rechargeable lithium-ion batteries owing to the potential for great safety and energy density. Among them, polymer solid-state electrolytes (PSEs) are competitive candidates for replacing commercial liquid electrolytes due to their flexibility, shape versatility and easy machinability. Despite the rapid development of PSEs, their practical application still faces obstacles including poor ionic conductivity, narrow electrochemical stable window and inferior mechanical strength. Polymer/inorganic composite electrolytes (PIEs) formed by adding ceramic fillers in PSEs merge the benefits of PSEs and inorganic solid-state electrolytes (ISEs), exhibiting appreciable comprehensive properties due to the abundant interfaces with unique characteristics. Some PIEs are highly compatible with high-voltage cathode and lithium metal anode, which offer desirable access to obtaining lithium metal batteries with high energy density. This review elucidates the current issues and recent advances in PIEs. The performance of PIEs was remarkably influenced by the characteristics of the fillers including type, content, morphology, arrangement and surface groups. We focus on the molecular interaction between different components in the composite environment for designing high-performance PIEs. Finally, the obstacles and opportunities for creating high-performance PIEs are outlined. This review aims to provide some theoretical guidance and direction for the development of PIEs.
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
The ever-increasing energy consumption sparks widespread interest in energy-efficient storage and flexible conversion. Lithium-ion batteries (LIBs) have been heavily marketed in consumer electronics and traffic electrification owing to their eco-friendliness, high energy density and working voltage [1,2,3]. Currently, the energy density of LIBs has approached 260 Wh kg−1 and is challenging to break through [4, 5]. Meanwhile, LIBs have repeatedly experienced catastrophic failure in recent years, resulting in severe property damage and raising public concern. Developing LIBs with high energy density and safety has become unremitting pursuit. Organic liquid electrolyte frequently employed in commercial LIBs is blamed for thermal runaway [6]. It has volatility and flammability, posing safety issues about leakage and fire. The constituent solvents such as ethylene carbonate have strong reactivity with lithium metal anodes (LMAs) known as “holy grail” anodes, causing dendrite growth and continual side reactions [7,8,9]. Solid-state electrolytes (SSEs) can effectively enhance safety by eliminating the flammable liquid electrolyte. They can inhibit the dissolution of transition metal ions of the cathode materials and block the by-product cross talk between the electrodes [10]. SSEs can also limit the shuttle effect of polysulfide in lithium–sulfur batteries and reduce the cross talk of O2 and H2O as well as the nucleophilic attack of reduced oxygen in lithium-oxygen batteries [11, 12]. Some SSEs exhibit thermodynamic/electrochemical compatibility on the interfaces of LMAs, which further broaden the electrochemical window and enhance the energy density [13].
SSEs can be categorized into two groups: polymer solid-state electrolytes (PSEs) and inorganic solid-state electrolytes (ISEs). Single PSEs and ISEs are challenging to fulfill general requirements, such as adequate ionic conductivity (> 10–4 S cm−1), high operating voltage (up to 4–5 V vs. Li/Li+), appropriate mechanical strength (> 6 GPa) and excellent interfacial contact (Fig. 1) [14, 15]. PSEs exhibit good elasticity and adaptability to volume variations, which are widely used for flexible batteries. However, the polymers crystallize easily at ambient temperature, resulting in limited ionic conductivity [16]. The thermodynamic instability of the interface restricts their compatibility with high-voltage cathode materials and the inferior mechanical properties cannot suppress dendrite growth [17, 18]. ISEs own acceptable ionic conductivity, extensive electrochemical window and satisfactory mechanical strength, while their brittleness and fragility cause poor machinability and large contact resistance. Recently, researchers have been committed to integrating inorganic fillers into PSEs to form polymer/inorganic composite electrolytes (PIEs) and realize the synergistic effect of different materials. Inorganic fillers not only increase the mechanical strength of the polymer matrix but also act as plasticizers, preventing polymer crystallization and boosting the ionic conductivity of the electrolyte [19,20,21]. The interaction of the fillers with the polymer increases the redox stability of the electrolyte, hence extending the electrochemical window [22]. PIEs with sufficient ionic conductivity, electrochemical stability and outstanding mechanical strength represent tremendous potential for the next generation of LIBs.
Numerous inorganic fillers have emerged to enhance the performance of PIEs, including metal oxides, ceramic Li+ conductors and novel porous materials like metal–organic frameworks (MOFs). Despite extensive researches asserting that certain fillers have the potential to dramatically enhance PIE performance, the mechanism underlying these improvements lacks in-depth understanding and sortation. This review provides a comprehensive summary of the existing challenges and current advancements in PIEs. The properties of the PIEs are profoundly influenced by the nature of ceramic fillers including content, morphology, arrangement and surface groups. The molecular interaction in different phases and interface regions are highlighted to understand the improvement. The major purpose of this review is to propose alternative solutions to overcome the defects of PIEs and inspire the engaged contributors and new entrants to explore scalable strategies for the industrialization of PIEs.
2 Key Issues in the Development of PIEs
The key issues in the development of PIEs are illustrated in Fig. 2. PIEs must be engineered to be thin (thickness < 30 μm) and have fast Li+ transport capability to compete with the available commercial liquid LIBs [23]. Besides, PIEs should match the electrodes with high loading, specific capacity and working voltage to gain advantages in energy density and power capability. Combining SSEs with 4 V-class cathode and LMAs can increase the energy density, which also poses a significant challenge since it may cause performance deterioration due to high reactivity between electrolyte and charged electrodes [24]. The poor point-to-point contact generates a substantial interface resistance and uneven distribution of local current density, driving dendritic growth. Periodic volume changes of the electrode lead to the formation and accumulation of structural stress, which will deteriorate the ion transport on the electrode/electrolyte interface [25]. Improving the voltage window and developing a stable interface of PIEs are crucial challenges for achieving high-performance all-solid-state batteries (ASSBs).
2.1 Lithium-Ionic Conductivity
Ionic conductivity is a critical metric for accessing the migratory ability of Li+ in electrolytes. It is proportional to carrier concentration and transference number (t+). The ionic conductivity of commercial liquid organic electrolytes can approach 10–3–10–2 S cm−1, while the ionic conductivity of PSEs is less than 10–4 S cm−1 at room temperature [26]. PSEs with conductivity less than 5 × 10–4 S cm−1 are incapable of meeting the operational requirements of thick electrodes (thickness > 70 μm) [27], and gain no advantage in terms of energy density. According to the free-volume model, polymer matrix transfers Li+ ions through the polar sites and local segmental motions in amorphous regions [28, 29]. The ion diffusion kinetics in crystalline region is negligible. Reducing the crystallinity of polymer matrix at normal temperature is a crucial method for enhancing conductivity. However, lowering crystallinity reduces polymer strength, causing the polymer behaves as a viscous liquid and incapable of forming a self-supporting membrane. The balance between conductivity and mechanical strength raises concerns regarding polymers as hosts. Given that the reported ionic conductivity of certain ISEs has reached 10–3 S cm−1 and they feature great mechanical strength, the development of polymer/ceramic composite electrolytes should be a viable solution to enhance ion conductivity to some extent (Fig. 3a) [30, 31]. Ionic conductivity of PIEs is primarily influenced by interactions between Li+, anions, polymers and fillers [32]. The ion–dipole interaction between ions and the polymer matrix impacts the concentration of free Li+. The Lewis acid–base interaction generated by inorganic fillers influences polymer segment motion, lithium salt solubility and Li+ ion diffusion behavior. Making full use of the interaction between different components to optimize ionic conductivity has emerged as a primary focus for developing PIE.
The t+ quantifies the contribution of Li+ to the transport charge. Since anions do not engage in reversible electrochemical reactions, their migration cannot transfer effective charges [34]. Nevertheless, for anions with a large volume and mass, their transfer number is always bigger than that of Li+; hence, the t+ of PSEs is always less than 0.5 [35]. t+ is determined by the ability of polymer to dissociate lithium salt, and thus polymer with a high dielectric constant and lithium salt with a low lattice energy can achieve high t+ [36, 37]. Besides, the transport of Li+ strongly depends on the segmental movement of the amorphous region in the polymer matrix. Polymer with a low glass transition temperature (Tg) can facilitate the segment movement and enhance t+. Adding fillers in polymer can change the local environment of Li+ ions. Especially, the strong interaction between fillers and anions results in the dissociation of lithium salts and an increase in t+. Fixing anions with fillers to increase t+ can reduce the concentration polarization on the electrode and inhibits fractal dendrites caused by the depletion of Li+ on the anode.
2.2 Electrochemical Stability
The electrolyte decomposes when the working potential of the battery exceeds its redox potential window [38, 39]. To achieve high-voltage stability, PIEs require every component has a HOMO energy level less than the Fermi energy of cathode. The HOMO values of most polymers are greater than those of lithium salts, indicating that the polymers preferentially undergo interfacial side reactions (Fig. 3b) [32]. Furthermore, adding lithium salt reduces the oxidation stability of polymers because the anions shield positive charges on the chains [40]. Electrolytes based on PEO are typically utilized for 3 V-grade cathode materials due to the labile lone pairs on the ether-oxygen atoms in the PEO chains [41]. Yu et al. found that the C-H bonds became weak after partially oxidizing the ether-oxygen atoms, causing the H protons to be carried away by the TFSI− and generate hydrogenated HTFSI. As a potent acid, it can impair interface and produce H2 on the anode [42]. In addition, the cathodes such as LiNiO2, LiCoO2 and LiNixCoyMn1−x−yO2 possess large specific surface areas and show strong catalytic ability, due to the transition metal ions or conductive carbon, hence accelerating electrolyte degradation [43, 44]. The molecule interaction of the components changes the chemical environment of the polymers, which consequently affects their HOMO value. Incorporating inorganic fillers can improve the oxidative stability of polymers via Lewis acid–base interaction, hydrogen-bonding or dipolar interactions between the lone pairs of polymers and the surface groups of fillers [32, 45]. Cui et al. reported that the ether-oxygen segments in the polymer matrix can interact with the P atoms in the Li6PS5Cl fillers, thereby reducing the HOMO energy level of the polymer and widening the electrochemical window [46]. Chen et al. found that the strong Lewis acid–base interaction between anions and the surface groups of Li7La3Zr2O12 fillers can decrease the oxidation of anions [47]. Meanwhile, combining anions with the fillers can diminish the shielding effect of anions on the positive charges of polymers and effectively stabilize the polymers at high voltage. Furthermore, rational design of polymer and inorganic Li+ conductors can inhibit the direct contact of unstable interface and improve the compatibility with Li and high-voltage cathode [48]. Specifically, most polymers are stable at the Li anode but poor at the high-voltage cathode, whereas certain inorganic oxides and sulfides are the exact reverse. Properly designing PIEs with two or more layers of vertical heterostructure provides a viable option for concurrently meeting cathode and anode requirements, exploring a new pathway for high-voltage ASSBs.
2.3 Dendrite Inhibition
LMA possesses unique superiority in energy density because it owns the lowest molar mass and reduction potential among metallic elements [49, 50]. However, notorious dendrite propagation gives rise to large volume expansion, low reversibility and potential safety hazards [51]. In polymer electrolytes, heterogeneous interface, limited ion transport and low mechanical strength are the primary reasons driving dendrite growth [52]. Firstly, solid electrolyte interface (SEI) realizes the dynamic passivation of the electrode, which expands the electrochemical window of LMBs to a certain extent [53]. However, the heterogeneous SEI induces uneven Li+ flux on the anode, triggering the propagation of mossy and whiskery dendrites (Fig. 4a) [7, 54]. Isotropic inert interface with uniform ionic conductivity can effectively homogenize lithium flux; thus, dendrite growth can be effectively alleviated by constructing a stable electrolyte layer on the anode. Furthermore, the limited transport results in local ion depletion on the interface, creating a space charge layer (SCL) [55]. The large electric field in the SCL leads to electric convection and rapid growth of fractal dendrites. Fixing anions to enhance t+ and prevent SCL formation is regarded as an effective method for inhibiting dendrites [56]. Additionally, enhancing mechanical strength can regulate Li nucleation and growth by altering the surface energy at the Li top surface [57]. According to the theoretical model proposed by Monroe and Newman, lithium dendrites can be eliminated when the surface shear modulus is at least 2–3 times that of metallic lithium (4.5 GPa) [58]. The polymer electrolytes have a low shear modulus (typically < 0.1 GPa) and are incapable of inhibiting Li dendrites (Fig. 4b). Viswanathan et al. further established a universal criterion for stable electroplating using the shear modulus ratio of SSEs and lithium anode (\(G_{{{\text{SSE}}}}\)/\(G_{{{\text{Li}}}}\)) and the molar volume ratio of Li+ ions and lithium anode (\(V_{{{\text{Li}}^{ + } }} /V_{{{\text{Li}}}}\)) [59]. They concluded stable electroplating necessitated the use of SSEs with a high (low) Li molar volume and high (low) shear modulus. PSEs have soft texture and low shear modulus, while the formation of Li+ solvated “cages” leads to high volume expansion and high \(V_{{{\text{Li}}^{ + } }}\), causing they cannot inhibit dendrites. To verify the feasibility of this criterion, Helms et al. prepared nano-LiF@polymer PIEs by in situ cation metathesis [60]. The modified PIEs had minimally reconfigurable, ceramic-like, ion-conducting domains contained in a soft, polymer-like matrix with a low shear modulus, which can inhibit the growth of dendrites.
2.4 Contact Stability
During reciprocating charge and discharge, the electrode materials may undergo lattice and phase changes, causing volume fluctuation and particle pulverization [61, 62]. Inadequate contact between the electrode and PIEs leads to high contact resistance even complete loss of electric disconnection (Fig. 4c). Besides, the uneven plating/stripping behavior of metallic lithium reduces the effective contact area, hence exacerbating the inhomogeneous distribution of Li+ flux. A decent electrolyte design requires a compromise between the appropriate modulus and surface adhesion [63].
In addition to the typical issues listed above, PIEs face additional challenges with some specific energy storage systems. Lithium–sulfur batteries have an overwhelming advantage in energy density (500–600 Wh kg−1), which partly attributes to the reduction of S to Li2S yields a high specific capacity of 1675 mAh g−1. However, the shuttle effect of soluble polysulfide intermediates (Li2Sn, 3 ≤ n ≤ 8) results in the rapid attenuation of capacity and low coulombic efficiency [64]. Some polymers such as PEO have a strong solvation effect on polysulfides at high temperatures, causing polysulfides to dissolve in polymers and trigger side reactions [65]. The polysulfides on the anode induce uneven plating/stripping behavior of lithium and further deterioration of interface contact [66]. As physical barriers, inorganic fillers can reduce the contact with polymers [67]. Meanwhile, they can adsorb polysulfides and mitigate the shuttle effect by forming chemical bonds with polysulfides [68]. Li–O2 (air) batteries also have a much higher energy density (~ 950 Wh kg−1) than the existing graphite||layered ternary cathode system. Polymers with non-toxic, non-combustible and nonvolatile characteristics provide feasible solutions to solve safety problems. However, most routinely used polymers, including PAN, PVDF, PVDF-HFP and PEO, are reactive to reduction products such as Li2O2 [69, 70]. Fortunately, Lewis acid base interaction between inorganic fillers and polymers can improve the electrochemical stability of the polymers [71, 72]. The charge transfer of Li–O2 batteries using liquid electrolyte occurs at the solid–liquid-gas interface, while that of Li–O2 batteries using PIEs occurs at the solid–gas interface. Due to the increased contact resistance, the reaction rate would be drastically slowed down. It is essential to develop catalysts to accelerate the kinetics of conversion reaction.
3 Fillers of PIEs
3.1 Components of PIEs
PIEs are made up of polymer matrix, lithium salt and ceramic filler. Wright et al. proposed that alkali metal salts mixed with polyethylene oxide (PEO) could conduct ions in 1973 [73]. And then Armand used the composite as electrolyte in batteries [74]. Subsequently, a broad array of polymers, including polyvinylidene fluoride (PVDF), polymethyl methacrylate (PMMA), polyacrylonitrile (PAN) and poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP), emerged as matrices [73, 75]. It is challenging for a single polymer to satisfy all the requirements as electrolyte material (Table 1). By combining the benefits of several hosts, polymer/polymer cooperation offers the chance to create superior polymer matrices. Copolymerization, cross-linking, interpenetration and blending are the most explored techniques in this field [22]. These polymer segments typically include polar groups to dissolve lithium salts and transfer Li+ ions, such as C=O, –O–, –N–, C=N and –P– [37]. Li+ ions coordinate with polar groups on the polymer chains at certain places and generate free volume by local segment movement of the polymer chains, allowing Li+ to be transmitted within and between the chains [26] (Fig. 5a). Table 1 lists the fundamental characteristics of typical polymer matrices in terms of Tg and melting point (Tm). These two parameters govern the conductivity of Li+ ions. Specifically, Tg is crucial for the phase transition of polymer electrolytes since most studies hold that Li+ ion transport only takes place in the amorphous zone above Tg.
Ordinary lithium salts usually contain the characteristics of large anionic radius and delocalization charge, such as LiPF6, LiFSI, LiTFSI and LiClO4, which have high solubility in polymers and easily generate stable SEI [26, 80] (Fig. 5b). Ceramic fillers can be classified as either inert or active fillers depending on whether they can conduct Li+ ions. The inert fillers include SiO2, ZrO2, Al2O3, Y2O3, LiAlO2, and the active fillers include garnet, NASICON, perovskite, sulfide, Li3N, etc. [71, 81,82,83,84]. Both inert and active fillers can be utilized as plasticizers to diminish the crystallization, hence facilitating the movement of Li+ ions. As fast ion conductors, active fillers can also promote Li+ diffuse through the defects or vacancies in the crystal structure, such as Schottky defects and Flenker defects, thus enhancing the ionic conductivity. If the active fillers are highly concentrated, Li+ ions can diffuse through the permeation network provided by continuous filler particles [85]. In this case, the polymer matrix only acts as a flexible host and is not responsible for Li+ ion diffusion. Therefore, high ion conductivity and t+ can also be achieved without lithium salts [86,87,88].
3.2 Inert Fillers
The thermal and mechanical strength of the polymer matrix can be improved by inert fillers. Moreover, fillers dispersed in the polymer matrix typically have tiny particle sizes and large specific surface areas, creating abundant interface with massive defects and high reactivity, which easily interact with other components [89]. Interaction between components affects the ionic conductivity and electrochemical stable window (ESW). Precisely regulating the intermolecular force is essential for achieving PIEs with high performance [89].
Inert fillers can weaken the interaction among the chains and increase free volume in the polymer matrix, which speeds up segmentation dynamics and delays polymer crystallization. Furthermore, fillers with Lewis acidic surface can interact with the anions [90]. As a result, the newly established hydrogen bonds make the fillers become cross-linking centers between polymer and anions, further disrupting the crystallinity (Fig. 6a) [32, 91, 92]. Instead, the fillers with Lewis basic surface can interact with Li+, causing the decrease of t+. Neutral fillers interact weakly with lithium salts and polymer, hence having a negligible effect on the transport characteristics. Therefore, fillers with Lewis acidic surface are more favorable to Li+ ion diffusion. The inert fillers can also facilitate salt dissociation and increase Li+ ion concentration. Fixing anions on fillers can prevent anion–polymer interaction to increase the oxidation stability of PIEs [45, 93]. Meanwhile, most inorganic fillers are stable at high voltages. Well-designed PIEs can broaden ESW by inhibiting the direct contact of thermodynamically unstable components to realize compatibility with LMAs and high-voltage cathode. The recent research on PIEs with inert fillers and their properties is presented in Table 2.
3.2.1 Oxide Materials
Al2O3 is inexpensive and widely available with robust thermal stability and is one of the earliest materials used as filler [126,127,128]. Pereira et al. reported that the addition of Al2O3 did not change the Tg of PEO-LiClO4, but increased amorphous regions, thereby promoting the segment mobility and the transport of Li+ ions [129]. Wieczorek and Chen used Al2O3 with two distinct properties as fillers to demonstrate the validity of Lewis acid–base theory in elucidating the modification of ionic conductivity [130, 131]. Fourier transform infrared spectroscopy (FTIR) showed that Al2O3 with acidic groups enhanced the interaction with ClO4−, thus promoting the dissolution of LiClO4. Therefore, O atoms on Al2O3 with basic groups can interact with Li+, which increased free anions and diminished the t+.
SiO2 is easily accessible and rich in reserves and is commonly utilized as filler material [132,133,134]. Zhang et al. constructed a three-dimensional network of PEO-LiClO4@SiO2 by in situ hydrolysis reaction (Fig. 6b) [94]. SiO2 promoted the segmental motion by the synergistic effect of Lewis acid–base and hydrogen bond. In addition, the enhanced interfacial stability allowed for an ESW of up to 4.8 V at 90 °C. Lu et al. created Li2SO4-modified SiO2 nanofibers through electrospinning and calcination (Fig. 6c) [95]. The doping of Li2SO4 enhanced the ionic conductivity of SiO2 and the wettability to the polymer. Meanwhile, the created mesopores encouraged anion absorption. After integrating PEO-LiTFSI matrix, the nanofiber networks can produce rapid and continuous Li+ diffusion routes. The sturdy 3D network served as a solid skeleton, reinforcing the entire membrane and inhibiting dendrite growth.
TiO2 has a high dielectric constant (ε > 180) and strong Lewis acid–base action, making it a popular choice as a filler for PIEs. Ghosh et al. explored the impact of TiO2 nanoparticles on the characteristics of the PMMA-LiClO4 [135]. 1 wt% addition of TiO2 raised the ionic conductivity of the PIEs to 3 × 10–4 S cm−1 at room temperature. It contributed to that the strong interaction between TiO2 nanoparticles and ClO4− inhibited ion pair formation and increased free carriers. Lithium-ion poly (ethyl citrate) embedded with TiO2 nanoparticles was in situ produced by thermal-initiated polymerization [136]. Polymer esterification catalyzed in situ hydrolysis of titanium alkoxide, leading to the production of nano-TiO2. As the increase in TiO2 concentration, polymerization of PIEs decreased and the thermal stability improved marginally. The addition of 20 wt% TiO2 to the PIEs increased ionic conductivity by two orders of magnitude (1.74 × 10–4 S cm−1).
ZrO2 has good chemical and thermal stability. In addition, ZrO2 nanoparticles have Lewis acidity, which can attract anions and encourage lithium salt dissociation [137]. Jing et al. fabricated polypropylene oxide (PPO)-based PIEs by combining the bis[3-(methyldimethoxysilyl)]-terminated PPO (BSPPO) oligomers with ZrO2 nanofillers, succinonitrile (SN) plasticizer and cellulose membrane (CM) framework. LiBOB was used to trigger the cross-linking of BSPPO oligomers. ZrO2 nanofillers decreased the Tg of the polymer and promoted the dissociation of LiTFSI. The ionic conductivity was further increased by the SN, which was an efficient ionizer. The prepared PPO-LiTFSI@ ZrO2 had good flexibility, high ionic conductivity (9.62 × 10–4 S cm−1), excellent thermal and electrochemical stability (5 V) [138]. Cui et al. employed Y2O3-doped ZrO2 to tailor the PAN-LiClO4 (Fig. 6d). High concentration of oxygen vacancies in ZrO2 can be created by doping with Y3+ with a low oxidation state. The positively charged oxygen vacancies as Lewis acid sites can combine with ClO4− to liberate additional Li+ ions, which increased the conductivity to 1.07 × 10–5 S cm−1 and the t+ rose to 0.56 [96].
3.2.2 Ferroelectric Materials
Ferroelectric materials with permanent dipoles have strong Lewis acid–base characteristics, which are also employed as fillers [97, 139]. Due to their unique crystal structure, ferroelectric materials exhibit spontaneous polarization. They can effectively alleviate the generation of SCL formed by Li+ depletion due to the large chemical potential difference at the electrode/electrolyte interface [140, 141]. Sohn et al. incorporated BaTiO3, PbTiO3 and LiNbO3 into the PEO polymer [98]. The fillers decreased the contact resistance between the LMAs and the electrolyte, increasing the mechanical strength and Li+ ionic conductivity.
3.2.3 Porous Materials
Porous materials, such as zeolite and MOFs, provide an adaptable pore structure and large specific surface area, hence generating abundant contact sites [142]. In addition, the channel structure has a nanoscale effect that allows for the effective regulation of charged particle adsorption. Moreover, these materials possess excellent thermal stability and mechanical properties which have been extensively explored as inorganic fillers.
Zeolites are widely available from nature and possess ultra-high structural stability. Kim et al. treated the surface of aluminosilicate zeolite (SSZ-13) with polyacrylic acid (Fig. 7a) [143]. SSZ-13 with a hydrophobic surface enhanced the dispersion of LiTFSI in PEO and provided continuous channels for Li+ diffusion. It increased dissociation of LiTFSI and liberation of Li+ ions. The conductivity of PEO-LiTFSI@SSZ-13 was increased to 5.34 × 10–2 cm S−1 (70 °C) with a t+ of 0.85. The ASSBs assembled with Li and LiFePO4 delivered capacity retention of 94.1% after 80 cycles at 60 °C. Additionally, they employed YNa zeolite as a ceramic filler and combined it with PEO-LiFSI to create PIEs (PEO-LiFSI@YNa) (Fig. 7b) [99]. The ionic conductivity was elevated to 1.66 × 10–2 S cm−1 and t+ was significantly increased to 0.84. Li||Li symmetric cells maintained a stable overpotential of ~ 60 mV for 1500 h, revealing the PIEs can inhibit dendrite growth.
MOFs are comprised of inorganic clusters containing center metal ions and organic ligands [144]. In addition to sharing some characteristics with zeolites, including great thermal stability, large specific surface area and Lewis acidic surface, MOFs also contain their own distinct organic functional groups, which allow for the flexible control of surface properties [145, 146]. Unsaturated metal sites in MOFs can interact with anions to facilitate Li+ ion transport, hence enhancing ionic conductivity [147]. The periodic crystal structure and organized channels in MOFs provide uniform Li+ flux, ensuring uniform Li+ plating behavior and inhibiting dendrite growth. Stephan et al. enhanced the ionic conductivity of PEO-LiTFSI by two orders of magnitude with aluminum benzenetricarboxylate (Al-BTC) as filler [117]. The obtained PIEs exhibited excellent thermal stability and cycle stability to LMAs. They also reported that the insertion of aluminum terephthalate (Al-TPA) can reduce the migration of polysulfides in lithium–sulfur batteries and realize a stable cycle performance [118]. Zheng et al. constructed a 3D MOF network (Zirconium benzenedicarboxylate MOF, UIO-66) by electrospinning and then filled it with PAN/PEO-LiTFSI to obtain PIEs@UIO-66 (Fig. 7c) [100]. Density functional theory (DFT) demonstrated that UIO-66 had strong adsorption to Li+ ions. The interconnected particles offered continuous pathways for the rapid transport of Li+ ions, efficiently enhancing the ionic conductivity (2.89 × 10–4 S cm−1) and promoting the homogeneous distribution of Li+ flux. The PIEs@UIO-66 had high t+ (0.52), wide ESW (4.7 V), remarkable ability to suppress lithium dendrites and high mechanical strength. Guo et al. produced a novel cationic MOF (CMOF) by grafting pyridine onto UiO-66 and dispersed it in PEO-LiTFSI to form PIEs (Fig. 8a) [101]. CMOF fixed anions through electrostatic interaction and its large specific surface area further enhanced the adsorption of anions, making its t+ reach 0.72. Moreover, CMOF grafted with -NH2 groups protected the ether-oxygen on the polymer chains by hydrogen bonding, extending the electrochemical window to 4.97 V. After 300 cycles at 1C, the ASSBs combined with LMAs and LiFePO4 retained 85.4% of their initial capacity. Zhang et al. grafted polyethylene glycol diacrylate chain (PEGDA) onto vinyl-functionalized MOF nanoparticles (UIO66-NH2) through UV photopolymerization and formed PIEs with LiTFSI (Fig. 8b) [148]. The PIEs have a fivefold increase in ionic conductivity over PEGDA-LiTFSI, reaching 10–5 S cm−1.
3.2.4 Other Inert Fillers
Other inert inorganic materials, such as mixed metal oxides, phosphates, layered clay materials, are also widely used as fillers. Stephan et al. incorporated MgAl2O4 into PEO-LiPF6 to create PIEs by hot press [149]. The addition of MgAl2O4 improved the Tg and ionic conductivity of the polymer, which attributed to Lewis acid properties of MgAl2O4, can compete with Li+ ions and form complexes with PEO chains, thus decreasing polymer crystallization. Nanosized Ca3(PO4)2 was reported to produce a similar effect on the performance of PEO-LiTFSI and PEO-LiClO4 [150]. Nano-layered clays, such as montmorillonite and kaolinite, were utilized as inorganic fillers due to their high dielectric characteristics and specific surface area, which were conducive to the dissociation of lithium salts [151,152,153].
In summary, whereas inert fillers are unable to transport Li+ ions, numerous surface groups can interact with polymers and lithium salts to prevent polymer crystallization and promote lithium salt dissociation. Additionally, inert fillers can improve the mechanical and thermal stability of polymers. The interaction between inorganic fillers and anions can inhibit the continuous oxidative decomposition of anions and widen the ESW of the PIEs.
3.3 Active Fillers
Active fillers allow efficient conduction of Li+ ions. Li+ ions exhibit different migration patterns in different regions of the PIEs with active fillers: (1) segment movement within the polymer, (2) vacancy or interstitial migration in the active fillers (Fig. 9a) and (3) interfacial migration between the fillers and polymer (Fig. 9b) [28, 154, 155]. Debates still exist regarding the migration paths of Li+ ions in PIEs containing active fillers, which will be described in depth in the following section. Based on the type of solid-state electrolyte used as fillers, they can be classified as garnet-type, NASICON-type, perovskite-type and sulfide-type PIEs (Fig. 9c) [156].
3.3.1 Garnet-Type PIEs
Thangadurai et al. reported the garnet-type Li5La3M2O12 (M = Nb, Ta) with an ionic conductivity of 10–6 S cm−1 at room temperature for the first time in 2003 [160]. By inserting more lithium atoms into the framework, a series of SSEs with garnet structure were created. Li6.4La3Zr1.4Ta0.6O12 has the highest bulk ionic conductivity of 10–3 S cm−1 at 25 °C among the known Li-rich garnets [161]. Garnet-type SSEs have the advantages of excellent ionic conductivity (~ 10–4–10–3 S cm−1), oxidation resistance under high voltage, stability to lithium metal and superior mechanical strength. Nevertheless, they also have the issue of significant interfacial resistance brought by inadequate contact with the rough interface [162]. Composited with polymer can accomplish robustness and flexibility, minimize interfacial contact impedance and overcome the poor processability of powder ceramics. The recent research on PIEs filled with garnet-type fillers and their properties is summarized in Table 3.
Gerbaldi et al. added Li7La3Zr2O12 (LLZO) fillers and a photoinitiator to the PEO-tetra (ethylene glycol dimethyl ether) (G4)-LiTFSI and then induced cross-linking under ultraviolet light to generate PIE films. The PIEs had good flexibility and exhibited an ionic conductivity more than 1 × 10–4 S cm−1 and a t+ greater than 0.5 at 20 °C. The Li||LiFePO4 cells with the PIEs demonstrated a remarkable specific capacity for 400 cycles [175]. The relationship between ion mobility, transport pathways and activity concentration in PEO-LiTFSI@LLZO was determined by solid-state nuclear magnetic resonance (NMR) [157]. The results demonstrated that when the LLZO content in the PIEs was less than 20 wt%, Li+ ions were mainly conducted through PEO (Fig. 9d). Once the concentration of LLZO reached a threshold level, the particles joined together, forming an infiltration network. Li+ ions migrated through the network rather than the PEO matrix. The critical concentration depended on several factors such as particle size, morphology as well as the dispersity of the fillers. The effects of LLZO fillers on ionic conductivity of PIEs are mainly manifested in the following aspects: (1) LLZO fillers reduced the crystallinity of polymer matrix; (2) Li+ ion channels in PEO could be blocked by LLZO particles and reduced the mobility of Li+ ions; (3) LLZO contributed as an extra source of Li+ ions to the conductivity. The trade-off between three competing effects determined whether the fillers increased or decreased ionic conductivity at a given concentration.
Chan et al. improved the ionic conductivity of PAN-LiClO4 by incorporating 5 wt% LLZO nanowires [158]. NMR revealed that LLZO nanowires changed the local environment in the polymer matrix and Li+ ion transport preferentially happened at the LLZO/polymer interface (Fig. 9e). The total ionic conductivity of PIEs adding LLZO nanoparticles (1.13 × 10–5 S cm−1) was much lower than that of PIEs adding LLZO nanowires (1.31 × 10–4 S cm−1). This indicated that the morphology and continuous conduction pathways provided by fillers were essential for the improvement of ionic conductivity.
Percolation effect may contribute significantly to the ionic conductivity of PIEs [157]. Wei et al. observed the space charge regions at the interface of PEO/Li6.25Ga0.25La3Zr2O12 (LLZO-Ga) nanoparticles by transmission electron microscope (TEM) [159]. Phase-field simulation demonstrated the chemical potential difference between LLZO-Ga and PEO drove the Li+ to migrate to the surface sites, leading to the enrichment of Li+ ions and low concentration of vacancies. As soon as the space charge region and phase distribution satisfied the criteria for establishing the percolation, percolation effect occurred, creating successive rapid transport routes and increasing ionic conductivity dramatically. Meanwhile, the space charge region surrounding isolated fillers barely impacted the ionic conductivity (Fig. 9f). Hu et al. tracked the Li+ diffusion paths in PEO-LiClO4@LLZO combining isotope labeling and Li NMR. By detecting that 6Li in the LMAs replaced 7Li in the PEO-LiClO4@LLZO, they found that Li+ ions diffused mainly through LLZO particles rather than through the interface or the polymer matrix (Fig. 10a) [176]. The aforementioned results imply that the observed Li+ diffusion path is closely related to the prepared PIEs inherently tied to the morphology, content, dispersion and properties of fillers.
Shen et al. suggested that Li6.75La3Zr1.75Ta0.25O12 (LLZTO) fillers can induce structure changes in PVDF [163]. La atoms of LLZTO can complex with N atoms and C=O groups of N, N-dimethylformamide (DMF) coupled with electron enrichment at the N atoms. The electron-rich N atoms acted as Lewis bases donated electron pairs and caused the partial dehydrofluorination of PVDF. The C=C on the modified PVDF enhanced the acid–base interaction with different components. LLZTO particles as Lewis acid promoted the dissociation of lithium salt and increased the concentration of Li+ ions. Partially dehydrofluorinated PVDF enhanced the interaction with LLZTO and further reduced the crystallinity of PVDF, resulting in enhanced comprehensive performance of the PIEs.
Wang et al. suggested that Li6.75La3Zr1.75Nb0.25O12 (LLZN) nanowires can interact with C=O and O=C–N, which were left by the solvent (DMF) [165]. The interaction reinforced the connection between fillers and polymer thus creating abundant amorphous regions and large free volume for segment movement. The surface group of ceramic filler had strong adsorption for ClO4−, hence facilitating the dissociation of the salt. Moreover, the vacancies of the LLZN nanowires provided special conductive channels for ion transportation. The multiple Li+ conduction forms significantly increased the ionic conductivity of PIEs (Fig. 10b).
3.3.2 NASICON-Type PIEs
The primary NASICON-type SSEs are derived from LiGe2(PO4)3 and LiTi2(PO4)3. The ionic conductivity can be further enhanced by partial replacement of tetravalent Ge4+ and Ti4+ with trivalent cations such as Ga3+, Al3+ and Fe3+. The ionic conductivity of Li1.3Al0.3Ti1.7(PO4)3 (LATP) can reach 10–3 S cm−1 and satisfy the requirements of SSEs [177]. Moreover, they are resistant to air and water, enabling large-scale synthesis and battery assembly in an air atmosphere, which decreases processing challenge and cost [178]. While they have an issue with instability to lithium since Ti4+ and Ge4+ are easily reduced, generating high-impedance interfacial phases [179, 180]. Composited with polymer electrolyte owning electronic insulation and flexibility can improve electrochemical and contact stability on the interface of NASICON-type SSEs. The recent research on PIEs filled with NASICON-type ISEs and their properties is summarized in Table 4.
Rational structural design can help ceramic and polymer electrolytes overcome their drawbacks and exploit their full potential. Yang et al. constructed PIEs with vertically aligned Li1.5Al0.5Ge1.5(PO4)3 (LAGP) and flexible PEO/PEG polymer (Fig. 11a) [181]. The vertical arranged LAGP created successive pathways for rapid ion diffusion and the PEO/PEG matrix made the PIEs flexible. The ionic conductivity of the PIEs reached 1.67 × 10–4 S cm−1 at 25 °C. After 300 cycles, the ASSBs built with LiFePO4 and LMAs retained 93.3% of the initial capacity. Jiang et al. adopt Janus interface modification strategy to improve the electrochemical stability at LAGP/electrodes interface. They sandwiched LAGP disks between in situ cross-linked PMMA and poly(cyclic carbonate urethane methacrylate)-based polymer electrolytes (Fig. 11b). Polymer electrolyte coatings not only kept PIEs in contact with the electrode, accelerating the interfacial ion transport kinetics, but also built stable CEI and SEI layers. The PIEs enabled the Li||LiNi0.8Mn0.1Co0.1O2 cells to have outstanding cycle stability at 4.5 V [196]. Yang et al. developed PIEs with “brick–mortar” microstructures (Fig. 11c) [182]. They prepared multilayer PEO-LiTFSI@LAGP by stacking and sintering at 850 °C. Then, the stack was immersed in polymer electrolyte under vacuum, and compressed at 80 °C to break into thin sheet and enable polymer to plug all gaps. The obtained PIEs exhibited extremely high ultimate bending strength and remarkable toughness. The ASSBs assembled with LiFePO4 and LMAs can retain 92% of their initial capacity at 0.5C after 300 cycles at 60 °C. Xiong et al. embedded silane functionalized LATP nanoparticles into the PVDF framework by electrospinning to form nanofiber membranes and then carried out thermal initiation polymerization of vinylene carbonate-based precursors in the composite network (Si@LATP/PVDF/PVC) [183]. Silane functionalization increased the affinity of Si@LATP with the PVDF skeleton and fully exposed the Lewis acid sites on LATP. The -NH3+ in poly-siloxane further increased the anion adsorption. The PIEs possessed high electrochemical stability to lithium and the ASSBs coupled with LiNi0.5Co0.2Mn0.3O2 exhibited excellent cycle performance and rate capability. Fan et al. created porous interconnected LATP networks with NaCl as a sacrificial template and introduced PEO-LiTFSI into the networks (Fig. 11d). The PIEs not only served as rapid transport routes for Li+ ions, but also as physical barriers to prevent the growth of Li dendrites [184].
3.3.3 Perovskite-Type PIEs
Perovskite-type SSEs include Li3xLa2/3−xTiO3 and (Li, Sr)(M, M') O3 (M = Ti, Hf, Zr, Ga, Sn, etc., M' = Ta, Nb, etc.) [197, 198]. They process high ionic conductivity at room temperature (10–3 S cm−1) as well as outstanding mechanical strength and electrochemical oxidation potential (> 8 V). But they are vulnerable to reduction by the LMAs (Ti4+ + Li → Ti3+ + Li+). It is effective in overcoming defects by compositing with polymers. The recent research on PIEs filled with perovskite-type ISEs and their properties is summarized in Table 5.
Hu et al. reported flexible PIEs made of PEO-LiFSI and Li3/8Sr7/16Ta3/4Zr1/4O3 (PEO-LiFSI@LSTZ). The increased bonding of Ta5+ to F atoms in anions accelerated the release of Li+ ions and improved ionic conductivity (Fig. 12a) [199]. Concurrently, the SEI layer formed on LMAs increased the interfacial stability and inhibited lithium dendrites. The symmetrical Li||Li cells with PEO-LiFSI@LSTZ exhibited long-life stripping/plating behavior over 700 h. ASSBs matched with LiFePO4 or LiNi0.8Co0.1Mn0.1O2 exhibited high cycle stability and rate performance.
The alignment of the fillers in the polymer matrix has a significant effect on ionic conductivity and cell performance. Yu et al. compared randomly distributed Li0.35La0.55TiO3 (LLTO) fillers with 3D interconnection network on the performance of PIEs (Fig. 12b) [200]. In the random distribution structure, the agglomeration of nanoparticles generated discontinuous Li+ conductive paths which reduced the percolation behavior and ionic conductivity. LLTO with a 3D interconnection structure provided a continuous interface phase for Li+ conduction, which can significantly improve the ionic conductivity of PIEs. Zhao et al. fabricated PIEs with a vertically aligned LLTO framework embedded in a PEO-LiTFSI matrix [201]. The vertically aligned structure provided a rapid and continuous network for Li+ transport, obtaining ionic conductivity of 0.13 × 10–3 S cm−1, which was 2.4 times more than that of PIEs with randomly scattered LLTO (Fig. 12c). Cui et al. investigated the impact of Li0.33La0.557TiO3 nanowire orientation on the ionic conductivity of PIEs. Compared to the nanowires that were randomly scattered, well-aligned nanowires had a ten-fold increase in ionic conductivity (6.05 × 10–5 S cm−1 at 30 °C) [203] (Fig. 12d). Cui et al. compared the effect of Li0.33La0.557TiO3 nanoparticles with nanowires on the performance of PAN-LiClO4. Nanowires allowed for continuous ion transport channels, which shortened the transport distance and increased ionic conductivity compared to nanoparticle packing, where Li+ ions must cross several particle–particle junctions [202]. Therefore, developing continuous conduction paths is crucial for achieving high ionic conductivity of PIEs.
3.3.4 Sulfide-Type PIEs
The ionic conductivity of sulfide-type SSEs can reach ~ 10–2 S cm−1, while the electrochemical stability and interfacial stability are poor (Fig. 13a) [209]. The sensitivity of sulfides to air necessitates treatment in inert gas environment, which impedes their large-scale utilization. Sulfide-type SSEs are classified as binary or ternary based on their compositions. Binary sulfide SSEs comprise P2S5 and Li2S including Li7P3S11 and Li3PS4, while ternary sulfide electrolytes comprise P2S5, Li2S and MS2 (M = Si, Ge, Sn) including Li10GeP2S12 (LGPS) and Li6PS5X (X = Cl, Br, I) [210]. Combining sulfide-type SSEs with polymers can increase interfacial stability and improve processability. The recent research on PIEs filled with sulfide-type ISEs and their properties is summarized in Table 6.
Nan et al. prepared ultra-thin and flexible PIEs with Li6PS5Cl (LPSCl) and poly(vinylidene fluoride-co-trifluoroethylene) (P(VDF-TrFE)) by electrospinning-permeation-hot pressing method (Fig. 13b) [88]. The TrFE groups allowed P(VDF-TrFE) to exhibit dominant-phase with an all-trans conformation, resulting in a higher dielectric constant and greater flexibility than PVDF. The strong polarity of the polymer promoted the interaction with LSPSCl. The P(VDF-TrFE) network enabled the complete infiltration of LPSCl particles to generate interpenetrating P(VDF-TrFE)@LPSCl films. The PIEs had an ionic conductivity of up to 1.2 × 10–3 S cm−1 and enabled Li-In||LiNi0.8Co0.1Mn0.1O2 cells to maintain 71% capacity after 20,000 cycles at 1.0 mA cm−2. PEO-LiTFSI@LSPSCl PIEs were developed by solution casting method (Fig. 13c) [211]. The Li||S batteries assembled by the PIEs retained 97.8% of their initial capacity at 0.1 Ag−1. Cryo-TEM revealed that LSPSCl facilitated the decomposition of TFSI− and enhanced ionic conductivity. Li2O, LiF and Li2S-rich SEI formed by anionic decomposition hindered dendrite growth and enhanced interfacial stability. PEO-LiTFSI@LSPSCl also suppressed the shuttling of phosphorus and sulfur specie. By employing PEO-LiTFSI@Li3.25Ge0.25P0.75S4, Bieker et al. reduced the interfacial contact impedance and increased ionic conductivity (0.42 × 10–3 S cm−1) and t+ (0.87). The cells made of vulcanized polyacrylonitrile and LMAs exhibited outstanding rate performance and cycle stability (Fig. 13d) [212].
3.4 Synthesis of PIEs
The preparation methods of PIEs are mainly based on the synthesis of polymers involved solution casting, phase inversion, electrospinning and in situ polymerization. Solution casting entails dispersing the polymer, lithium salts and fillers in solvents, thoroughly agitating and then casting the mixture onto a flat substrate [224]. After removing the solvents, PIEs are obtained. This procedure is straightforward to implement; however, it cannot precisely regulate the porosity and thickness of PIEs. Phase inversion and solution casting share similar beginning steps; however in the former, the mixture coated on the substrate is soaked in a nonsolvent to replace the solvent. The exchange process causes phase transitions in the polymer. After drying at a high temperature, porous PIEs are created. Electrospinning is commonly used to fabricate one-dimensional nanomaterials and nanofiber-woven 3D networks. It can produce PIEs with adjustable porosity, pore size, thickness and excellent elasticity. Long fibers can offer continuous routes for ion transport [16]. In situ polymerization is the process of solidifying procurers containing curable monomers (e.g., tetrahydrofuran, 1,3-dioxolane, etc.), initiators (e.g., PF5, BF3, AlCl3, etc.), lithium salts and inorganic fillers under specific conditions (e.g., heat, UV radiation) [225]. Inorganic fillers shall be uniformly dispersed in the polymer during the process. Grafting allows fillers to covalently join on the polymer to avoid agglomeration of nanoparticles [226].
When solvent treatment is performed, the compatibility between solvents and fillers must be evaluated. In the presence of sulfides, the polarity index of the solvent must be less than 3.1 [227]. Physical and chemical properties of different PIE components, such as reactivity and toxicity with wet air and oxygen, must be thoroughly accounted for. For example, sulfides exhibit strong reactivity in humid air, leading to the creation of hazardous H2S [228]. PIEs composed of sulfides must be treated in a dry environment or even an inert gas atmosphere [229].
Generally, active fillers can conduct Li+ ions and the interface generated by their contact with polymers can provide transport routes for Li+ ions. Establishing continuous conduction routes is critical to improving ionic conductivity. The fillers’ type, particle size, shape, arrangement and interaction with other components will influence performance. Vertical heterostructures possess asymmetrical features, which can enrich the design strategies and show great potential in the practical application of ASSBs.
4 Summary and Perspective
This review presents recent progress on PIEs with inorganic fillers and focuses on the influence of inert and active fillers on the characteristics of the PIEs (Fig. 14). Especially, composite with active fillers can effectively overcome defects of the single component and improve the comprehensive performance of the electrolyte. The characteristics of PIEs are influenced by the type, content, morphology, arrangement and surface groups of the fillers. Proper design of fillers can significantly improve the ionic conductivity, mechanical strength and interfacial stability of the PIEs. Given their superior integrative performance, PIEs have been extensively investigated in ASSBs assembled with high-energy-density cathode and anode including S, O2 and LMAs. Even though PIEs have made significant strides, fundamental scientific questions remain and widespread implementation confronts substantial obstacles.
-
1.
Even though ionic conductivity of PIEs has greatly increased compared to traditional PSEs, it is still much lower than that of conventional liquid electrolytes, which is detrimental to develop LIBs with high energy density and power capability. Precisely regulating the characteristics and arrangement of fillers are expected to break through the ionic conductivity limit of PIEs. Understanding the Li+ migration routes and interactions between different components can provide crucial theoretical direction for enhancing ionic conductivity. Furthermore, it is essential to develop advanced in situ characterization techniques and theoretical computation methods to conduct mechanistic investigations in PIEs.
-
2.
It is critical for realizing the interfacial stability between PIEs and electrodes. Although the flexible polymer matrix can improve the contact with the rough electrode, the frequent expansion and contraction of the electrodes would degrade the contact during the charging/discharging processes. Especially when matching LMAs, the uneven plating/stripping behavior may cause the loss of electrical connection of active lithium. Regulating the electrochemical behavior of LMAs and adding minuscule ionic liquid or liquid electrolyte can considerably optimize surface contact.
-
3.
Increasing the operating voltage is a potential avenue for developing high-energy–density batteries. By crafting the arrangement of the fillers and polymer, we can increase the stability on the high-voltage cathode and reduce dendritic growth and side reactions on the anode. Coatings that can withstand high voltages and reduction are expected to encourage the widespread use of PIEs.
-
4.
At present, the thickness of PIEs is still significantly higher than that of commercial polyolefin separators. Developing ultra-thin PIEs with moderate rigidity and flexibility is conducive to improving the energy density of batteries. The uniform dispersion of inorganic fillers in polymer matrix facilitates to construct continuous and uniform Li+ transport channels. And the efficient dispersion of fillers is critical in the manufacture of PIEs. Meanwhile, processing compatibility with electrodes or other internal components must be guaranteed throughout synthesis and operation.
Generally, solving these problems still requires the joint efforts of multidisciplinary fields. The assessment of advanced research and outlook for future research in this paper is expected to benefit the next generation of all-solid-state lithium metal batteries.
References
M. Armand, J.M. Tarascon, Building better batteries. Nature 451, 652–657 (2008). https://doi.org/10.1038/451652a
J.M. Tarascon, M. Armand, Issues and challenges facing rechargeable lithium batteries. Nature 414, 359–367 (2001). https://doi.org/10.1038/35104644
Y. Wang, Y. Xue, C. Zhang, Electrochemical product engineering towards sustainable recovery and manufacturing of critical metals. Green Chem. 23, 6301–6321 (2021). https://doi.org/10.1039/D1GC01462E
J. Janek, W.G. Zeier, A solid future for battery development. Nat. Energy 1, 16141 (2016). https://doi.org/10.1038/nenergy.2016.141
W. Li, B. Song, A. Manthiram, High-voltage positive electrode materials for lithium-ion batteries. Chem. Soc. Rev. 46, 3006–3059 (2017). https://doi.org/10.1039/C6CS00875E
J. Hou, L. Lu, L. Wang, A. Ohma, D. Ren et al., Thermal runaway of lithium-ion batteries employing LiN(SO2F)2-based concentrated electrolytes. Nat. Commun. 11, 5100 (2020). https://doi.org/10.1038/s41467-020-18868-w
Y. He, X. Ren, Y. Xu, M. Engelhard, X. Li et al., Origin of lithium whisker formation and growth under stress. Nat. Nanotechnol. 14, 1042–1047 (2019). https://doi.org/10.1038/s41565-019-0558-z
F. Shi, A. Pei, A. Vailionis, J. Xie, B. Liu et al., Strong texturing of lithium metal in batteries. Proc. Nat. Acad. Sci. 114(46), 12138–12143 (2017). https://doi.org/10.1073/pnas.1708224114
W. Wu, Y. Bo, D. Li, Y. Liang, J. Zhang et al., Safe and stable lithium metal batteries enabled by an amide-based electrolyte. Nano-Micro Lett. 14, 44 (2022). https://doi.org/10.1007/s40820-021-00780-7
J. Langdon, A. Manthiram, Crossover effects in lithium-metal batteries with a localized high concentration electrolyte and high-nickel cathodes. Adv. Mater. 34(41), 2205188 (2022). https://doi.org/10.1002/adma.202205188
S.A. Freunberger, Y. Chen, N.E. Drewett, L.J. Hardwick, F. Bardé et al., The lithium-oxygen battery with ether-based electrolytes. Angew. Chem. Int. Ed. 50(37), 8609–8613 (2011). https://doi.org/10.1002/anie.201102357
J. Betz, J.P. Brinkmann, R. Nölle, C. Lürenbaum, M. Kolek et al., Cross talk between transition metal cathode and Li metal anode: unraveling its influence on the deposition/dissolution behavior and morphology of lithium. Adv. Energy Mater. 9(21), 1900574 (2019). https://doi.org/10.1002/aenm.201900574
J. Leng, H. Liang, H. Wang, Z. Xiao, S. Wang et al., A facile and low-cost wet-chemistry artificial interface engineering for garnet-based solid-state Li metal batteries. Nano Energy 101, 107603 (2022). https://doi.org/10.1016/j.nanoen.2022.107603
M. Falco, S. Ferrari, G.B. Appetecchi, C. Gerbaldi, Managing transport properties in composite electrodes/electrolytes for all-solid-state lithium-based batteries. Mol. Syst. Des. Eng. 4, 850–871 (2019). https://doi.org/10.1039/C9ME00050J
X. Fu, D. Yu, J. Zhou, S. Li, X. Gao et al., Inorganic and organic hybrid solid electrolytes for lithium-ion batteries. CrystEngComm 18, 4236–4258 (2016). https://doi.org/10.1039/C6CE00171H
D.K. Maurya, R. Dhanusuraman, Z. Guo, S. Angaiah, Composite polymer electrolytes: progress, challenges, and future outlook for sodium-ion batteries. Adv. Compos. Hybrid Mater. 5, 2651–2674 (2022). https://doi.org/10.1007/s42114-021-00412-z
A. Gurung, J. Pokharel, A. Baniya, R. Pathak, K. Chen et al., A review on strategies addressing interface incompatibilities in inorganic all-solid-state lithium batteries. Sustain. Energy Fuels 3, 3279–3309 (2019). https://doi.org/10.1039/C9SE00549H
T. Zhang, W. He, W. Zhang, T. Wang, P. Li et al., Designing composite solid-state electrolytes for high performance lithium ion or lithium metal batteries. Chem. Sci. 11, 8686–8707 (2020). https://doi.org/10.1039/D0SC03121F
S. Tang, W. Guo, Y. Fu, Advances in composite polymer electrolytes for lithium batteries and beyond. Adv. Energy Mater. 11(2), 2000802 (2021). https://doi.org/10.1002/aenm.202000802
S. Ferrari, J.R. Nair, Y. Zhou, C. Wan, 10: polymer nanocomposites for lithium battery applications, in Polymer-Based Nanocomposites for Energy and Environmental Applications. ed. by M. Jawaid, M.M. Khan (Elsevier, Amsterdam, 2018), pp.283–313. https://doi.org/10.1016/B978-0-08-102262-7.00010-6
P. Arunachalam, 6: polymer-based nanocomposites for energy and environmental applications, in Polymer-Based Nanocomposites for Energy and Environmental Applications. ed. by M. Jawaid, M.M. Khan (Elsevier, Amsterdam, 2018), pp.185–203. https://doi.org/10.1016/B978-0-08-102262-7.00006-4
S.J. Tan, X.X. Zeng, Q. Ma, X.W. Wu, Y.G. Guo, Recent advancements in polymer-based composite electrolytes for rechargeable lithium batteries. Electrochem. Energy Rev. 1, 113–138 (2018). https://doi.org/10.1007/s41918-018-0011-2
L.Z. Fan, H. He, C.W. Nan, Tailoring inorganic-polymer composites for the mass production of solid-state batteries. Nat. Rev. Mater. 6, 1003–1019 (2021). https://doi.org/10.1038/s41578-021-00320-0
Z. Chang, H. Yang, X. Zhu, P. He, H. Zhou, A stable quasi-solid electrolyte improves the safe operation of highly efficient lithium-metal pouch cells in harsh environments. Nat. Commun. 13, 1510 (2022). https://doi.org/10.1038/s41467-022-29118-6
J. Pan, P. Zhao, N. Wang, F. Huang, S. Dou, Research progress in stable interfacial constructions between composite polymer electrolytes and electrodes. Energy Environ. Sci. 15, 2753–2775 (2022). https://doi.org/10.1039/D1EE03466A
Z. Xue, D. He, X. Xie, Poly(ethylene oxide)-based electrolytes for lithium-ion batteries. J. Mater. Chem. A 3(38), 19218–19253 (2015). https://doi.org/10.1039/C5TA03471J
A. Bielefeld, D.A. Weber, J. Janek, Modeling effective ionic conductivity and binder influence in composite cathodes for all-solid-state batteries. ACS Appl. Mater. Interfaces 12(11), 12821–12833 (2020). https://doi.org/10.1021/acsami.9b22788
Y. Zheng, Y. Yao, J. Ou, M. Li, D. Luo et al., A review of composite solid-state electrolytes for lithium batteries: fundamentals, key materials and advanced structures. Chem. Soc. Rev. 49(23), 8790–8839 (2020). https://doi.org/10.1039/D0CS00305K
R. Chen, W. Qu, X. Guo, L. Li, F. Wu, The pursuit of solid-state electrolytes for lithium batteries: from comprehensive insight to emerging horizons. Mater. Horiz. 3(6), 487–516 (2016). https://doi.org/10.1039/C6MH00218H
K. Nie, S. Wu, J. Wang, X. Sun, Z. Yan et al., Reaction mechanisms of Ta-substituted cubic Li7La3Zr2O12 with solvents during storage. ACS Appl. Mater. Interfaces 13(32), 38384–38393 (2021). https://doi.org/10.1021/acsami.1c10373
J.F. Wu, B.W. Pu, D. Wang, S.Q. Shi, N. Zhao et al., In situ formed shields enabling Li2CO3-free solid electrolytes: a new route to uncover the intrinsic lithiophilicity of garnet electrolytes for dendrite-free Li-metal batteries. ACS Appl. Mater. Interfaces 11(1), 898–905 (2019). https://doi.org/10.1021/acsami.8b18356
Q. Zhou, J. Ma, S. Dong, X. Li, G. Cui, Intermolecular chemistry in solid polymer electrolytes for high-energy-density lithium batteries. Adv. Mater. 31(50), 1902029 (2019). https://doi.org/10.1002/adma.201902029
R. Chen, Q. Li, X. Yu, L. Chen, H. Li, Approaching practically accessible solid-sate batteries: stability issues related to solid electrolytes and interfaces. Chem. Rev. 120(14), 6820–6877 (2020). https://doi.org/10.1021/acs.chemrev.9b00268
P. Fan, H. Liu, V. Marosz, N.T. Samuels, S.L. Suib et al., High performance composite polymer electrolytes for lithium-ion batteries. Adv. Funct. Mater. 31(23), 2101380 (2021). https://doi.org/10.1002/adfm.202101380
Y. Lu, M. Tikekar, R. Mohanty, K. Hendrickson, L. Ma et al., Stable cycling of lithium metal batteries using high transference number electrolytes. Adv. Energy Mater. 5(9), 1402073 (2015). https://doi.org/10.1002/aenm.201402073
P. Yao, H. Yu, Z. Ding, Y. Liu, J. Lu et al., Review on polymer-based composite electrolytes for lithium batteries. Front. Chem. 7, 522 (2019). https://doi.org/10.3389/fchem.2019.00522
H. Wang, L. Sheng, G. Yasin, L. Wang, H. Xu et al., Reviewing the current status and development of polymer electrolytes for solid-state lithium batteries. Energy Storage Mater. 33, 188–215 (2020). https://doi.org/10.1016/j.ensm.2020.08.014
J. Li, Y. Ji, H. Song, S. Chen, S. Ding et al., Insights into the interfacial degradation of high-voltage all-solid-state lithium batteries. Nano-Micro Lett. 14, 191 (2022). https://doi.org/10.1007/s40820-022-00936-z
J. Xu, Critical review on cathode-electrolyte interphase toward high-voltage cathodes for Li-ion batteries. Nano-Micro Lett. 14, 166 (2022). https://doi.org/10.1007/s40820-022-00917-2
C.F.N. Marchiori, R.P. Carvalho, M. Ebadi, D. Brandell, C.M. Araujo, Understanding the electrochemical stability window of polymer electrolytes in solid-state batteries from atomic-scale modeling: the role of Li-ion salts. Chem. Mater. 32(17), 7237–7246 (2020). https://doi.org/10.1021/acs.chemmater.0c01489
K. Yoshida, M. Nakamura, Y. Kazue, N. Tachikawa, S. Tsuzuki et al., Oxidative-stability enhancement and charge transport mechanism in glyme-lithium salt equimolar complexes. J. Am. Chem. Soc. 133(33), 13121–13129 (2011). https://doi.org/10.1021/ja203983r
K. Nie, X. Wang, J. Qiu, Y. Wang, Q. Yang et al., Increasing poly(ethylene oxide) stability to 4.5 V by surface coating of the cathode. ACS Energy Lett. 5(3), 826–832 (2020). https://doi.org/10.1021/acsenergylett.9b02739
S. Kaboli, H. Demers, A. Paolella, A. Darwiche, M. Dontigny et al., Behavior of solid electrolyte in Li-polymer battery with NMC cathode via in-situ scanning electron microscopy. Nano Lett. 20(3), 1607–1613 (2020). https://doi.org/10.1021/acs.nanolett.9b04452
L. Yang, J. Zhang, W. Xue, J. Li, R. Chen et al., Anomalous thermal decomposition behavior of polycrystalline LiNi0.8Mn0.1Co0.1O2 in PEO-based solid polymer electrolyte. Adv. Funct. Mater. 32(23), 2200096 (2022). https://doi.org/10.1002/adfm.202200096
M.A.C. Martínez, N. Boaretto, A.J. Naylor, F. Alcaide, G.D. Salian et al., Are polymer-based electrolytes ready for high-voltage lithium battery applications? An overview of degradation mechanisms and battery performance. Adv. Energy Mater. 12(32), 2201264 (2022). https://doi.org/10.1002/aenm.202201264
Y. Wang, J. Ju, S. Dong, Y. Yan, F. Jiang et al., Facile design of sulfide-based all solid-state lithium metal battery: in situ polymerization within self-supported porous argyrodite skeleton. Adv. Funct. Mater. 31(28), 2101523 (2021). https://doi.org/10.1002/adfm.202101523
F. Chen, D. Yang, W. Zha, B. Zhu, Y. Zhang et al., Solid polymer electrolytes incorporating cubic Li7La3Zr2O12 for all-solid-state lithium rechargeable batteries. Electrochim. Acta 258, 1106–1114 (2017). https://doi.org/10.1016/j.electacta.2017.11.164
F. He, Z. Hu, W. Tang, A. Wang, B. Wen et al., Vertically heterostructured solid electrolytes for lithium metal batteries. Adv. Funct. Mater. 32(25), 2201465 (2022). https://doi.org/10.1002/adfm.202201465
T. Liu, J. Wang, Y. Xu, Y. Zhang, Y. Wang, Dendrite-free and stable lithium metal battery achieved by a model of stepwise lithium deposition and stripping. Nano-Micro Lett. 13, 170 (2021). https://doi.org/10.1007/s40820-021-00687-3
H. Liang, L. Wang, L. Sheng, H. Xu, Y. Song et al., Focus on the electroplating chemistry of Li ions in nonaqueous liquid electrolytes: toward stable lithium metal batteries. Electrochem. Energy Rev. 5, 23 (2022). https://doi.org/10.1007/s41918-022-00158-2
S. Ye, X. Chen, R. Zhang, Y. Jiang, F. Huang et al., Revisiting the role of physical confinement and chemical regulation of 3D hosts for dendrite-free Li metal anode. Nano-Micro Lett. 14, 187 (2022). https://doi.org/10.1007/s40820-022-00932-3
J. Kang, N. Deng, Y. Liu, Z. Yan, L. Gao et al., Recent advances of anode protection in solid-state lithium metal batteries. Energy Storage Mater. 52, 130–160 (2022). https://doi.org/10.1016/j.ensm.2022.07.037
Y. Wang, Separator wettability enhanced by electrolyte additive to boost the electrochemical performance of lithium metal batteries. Nano-Micro Lett. 13, 210 (2021). https://doi.org/10.1007/s40820-021-00731-2
K.J. Harry, D.T. Hallinan, D.Y. Parkinson, A.A. MacDowell, N.P. Balsara, Detection of subsurface structures underneath dendrites formed on cycled lithium metal electrodes. Nat. Mater. 13, 69–73 (2014). https://doi.org/10.1038/nmat3793
J.N. Chazalviel, Electrochemical aspects of the generation of ramified metallic electrodeposits. Phys. Rev. A 42(12), 7355–7367 (1990). https://doi.org/10.1103/PhysRevA.42.7355
R. Messer, F. Noack, Nuclear magnetic relaxation by self-diffusion in solid lithium: T1-frequency dependence. Appl. Phys. 6, 79–88 (1975). https://doi.org/10.1007/BF00883553
C. Fang, B. Lu, G. Pawar, M. Zhang, D. Cheng et al., Pressure-tailored lithium deposition and dissolution in lithium metal batteries. Nat. Energy 6(10), 987–994 (2021). https://doi.org/10.1038/s41560-021-00917-3
C. Monroe, J. Newman, The impact of elastic deformation on deposition kinetics at lithium/polymer interfaces. J. Electrochem. Soc. 152(2), A396–A404 (2005). https://doi.org/10.1149/1.1850854
Z. Ahmad, V. Viswanathan, Stability of electrodeposition at solid-solid interfaces and implications for metal anodes. Phys. Rev. Lett. 119(5), 056003 (2017). https://doi.org/10.1103/PhysRevLett.119.056003
C. Fu, V. Venturi, J. Kim, Z. Ahmad, A.W. Ells et al., Universal chemomechanical design rules for solid-ion conductors to prevent dendrite formation in lithium metal batteries. Nat. Mater. 19, 758–766 (2020). https://doi.org/10.1038/s41563-020-0655-2
X. Ke, Y. Wang, G. Ren, C. Yuan, Towards rational mechanical design of inorganic solid electrolytes for all-solid-state lithium ion batteries. Energy Storage Mater. 26, 313–324 (2020). https://doi.org/10.1016/j.ensm.2019.08.029
X. Yu, A. Manthiram, Electrode-electrolyte interfaces in lithium-sulfur batteries with liquid or inorganic solid electrolytes. Acc. Chem. Res. 50(11), 2653–2660 (2017). https://doi.org/10.1021/acs.accounts.7b00460
M. Keller, A. Varzi, S. Passerini, Hybrid electrolytes for lithium metal batteries. J. Power Sources 392, 206–225 (2018). https://doi.org/10.1016/j.jpowsour.2018.04.099
L. Zhou, D.L. Danilov, F. Qiao, J. Wang, H. Li et al., Sulfur reduction reaction in lithium-sulfur batteries: mechanisms, catalysts, and characterization. Adv. Energy Mater. (2022). https://doi.org/10.1002/aenm.202202094
H. Zhang, U. Oteo, X. Judez, G.G. Eshetu, M. Martinez-Ibañez et al., Designer anion enabling solid-state lithium-sulfur batteries. Joule 3(7), 1689–1702 (2019). https://doi.org/10.1016/j.joule.2019.05.003
Y. Liu, H. Liu, Y. Lin, Y. Zhao, H. Yuan et al., Mechanistic investigation of polymer-based all-solid-state lithium/sulfur battery. Adv. Funct. Mater. 31(41), 2104863 (2021). https://doi.org/10.1002/adfm.202104863
X. Tao, Y. Liu, W. Liu, G. Zhou, J. Zhao et al., Solid-state lithium-sulfur batteries operated at 37 °C with composites of nanostructured Li7La3Zr2O12/carbon foam and polymer. Nano Lett. 17(5), 2967–2972 (2017). https://doi.org/10.1021/acs.nanolett.7b00221
S. Li, S.Q. Zhang, L. Shen, Q. Liu, J.B. Ma et al., Progress and perspective of ceramic/polymer composite solid electrolytes for lithium batteries. Adv. Sci. 7(5), 1903088 (2020). https://doi.org/10.1002/advs.201903088
J.R. Harding, C.V. Amanchukwu, P.T. Hammond, Y. Shao-Horn, Instability of poly(ethylene oxide) upon oxidation in lithium-air batteries. J. Phys. Chem. C 119(13), 6947–6955 (2015). https://doi.org/10.1021/jp511794g
E. Nasybulin, W. Xu, M.H. Engelhard, Z. Nie, X.S. Li et al., Stability of polymer binders in Li–O2 batteries. J. Power Sources 243, 899–907 (2013). https://doi.org/10.1016/j.jpowsour.2013.06.097
B. Kumar, L.G. Scanlon, Polymer-ceramic composite electrolytes. J. Power Sources 52(2), 261–268 (1994). https://doi.org/10.1016/0378-7753(94)02147-3
J. Yi, S. Guo, P. He, H. Zhou, Status and prospects of polymer electrolytes for solid-state Li–O2 (air) batteries. Energy Environ. Sci. 10(4), 860–884 (2017). https://doi.org/10.1039/C6EE03499C
D.E. Fenton, J.M. Parker, P.V. Wright, Complexes of alkali metal ions with poly(ethylene oxide). Polymer 14(11), 589 (1973). https://doi.org/10.1016/0032-3861(73)90146-8
M. Armand, Polymer solid electrolytes: an overview. Solid State Ion. 9–10, 745–754 (1983). https://doi.org/10.1016/0167-2738(83)90083-8
M. Armand, The history of polymer electrolytes. Solid State Ion. 69(3–4), 309–319 (1994). https://doi.org/10.1016/0167-2738(94)90419-7
H. Yue, J. Li, Q. Wang, C. Li, J. Zhang et al., Sandwich-like poly(propylene carbonate)-based electrolyte for ambient-temperature solid-state lithium ion batteries. ACS Sustain. Chem. Eng. 6(1), 268–274 (2018). https://doi.org/10.1021/acssuschemeng.7b02401
C.Y. Hsu, R.J. Liu, C.H. Hsu, P.L. Kuo, High thermal and electrochemical stability of PVDF-graft-PAN copolymer hybrid PEO membrane for safety reinforced lithium-ion battery. RSC Adv. 6(22), 18082–18088 (2016). https://doi.org/10.1039/C5RA26345J
N.K. Jyothi, K.K. Venkataratnam, P.N. Murty, K.V. Kumar, Preparation and characterization of PAN-KI complexed gel polymer electrolytes for solid-state battery applications. Bull. Mater. Sci. 39(4), 1047–1055 (2016). https://doi.org/10.1007/s12034-016-1241-8
Z. Xiao, T. Long, L. Song, Y. Zheng, C. Wang, Research progress of polymer-inorganic filler solid composite electrolyte for lithium-ion batteries. Ionics 28, 15–26 (2022). https://doi.org/10.1007/s11581-021-04340-2
X. Chen, Q. Zhang, Atomic insights into the fundamental interactions in lithium battery electrolytes. Acc. Chem. Res. 53(9), 1992–2002 (2020). https://doi.org/10.1021/acs.accounts.0c00412
H. Yang, B. Zhang, M. Jing, X. Shen, L. Wang et al., In situ catalytic polymerization of a highly homogeneous PDOL composite electrolyte for long-cycle high-voltage solid-state lithium batteries. Adv. Energy Mater. 12(39), 2201762 (2022). https://doi.org/10.1002/aenm.202201762
N. Zhang, J. He, W. Han, Y. Wang, Composite solid electrolyte PEO/SN/LiAlO2 for a solid-state lithium battery. J. Mater. Sci. 54(13), 9603–9612 (2019). https://doi.org/10.1007/s10853-019-03535-3
N.T.K. Sundaram, A. Subramania, Nano-size LiAlO2 ceramic filler incorporated porous PVDF-co-HFP electrolyte for lithium-ion battery applications. Electrochim. Acta 52(15), 4987–4993 (2007). https://doi.org/10.1016/j.electacta.2007.01.066
L. Wang, X. Li, W. Yang, Enhancement of electrochemical properties of hot-pressed poly(ethylene oxide)-based nanocomposite polymer electrolyte films for all-solid-state lithium polymer batteries. Electrochim. Acta 55(6), 1895–1899 (2010). https://doi.org/10.1016/j.electacta.2009.11.003
W. Zhang, J. Nie, F. Li, Z.L. Wang, C. Sun, A durable and safe solid-state lithium battery with a hybrid electrolyte membrane. Nano Energy 45, 413–419 (2018). https://doi.org/10.1016/j.nanoen.2018.01.028
B. Tang, Y. Zhao, Z. Wang, S. Chen, Y. Wu et al., Ultrathin salt-free polymer-in-ceramic electrolyte for solid-state sodium batteries. eScience 1(2), 194–202 (2021). https://doi.org/10.1016/j.esci.2021.12.001
J. Zhang, N. Zhao, M. Zhang, Y. Li, P.K. Chu et al., Flexible and ion-conducting membrane electrolytes for solid-state lithium batteries: dispersion of garnet nanoparticles in insulating polyethylene oxide. Nano Energy 28, 447–454 (2016). https://doi.org/10.1016/j.nanoen.2016.09.002
S. Liu, L. Zhou, J. Han, K. Wen, S. Guan et al., Super long-cycling all-solid-state battery with thin Li6PS5Cl-based electrolyte. Adv. Energy Mater. 12(25), 2270105 (2022). https://doi.org/10.1002/aenm.202270105
S. Sen, E. Trevisanello, E. Niemöller, B.X. Shi, F.J. Simon et al., The role of polymers in lithium solid-state batteries with inorganic solid electrolytes. J. Mater. Chem. A 9(35), 18701–18732 (2021). https://doi.org/10.1039/D1TA02796D
A.M. Stephan, K.S. Nahm, Review on composite polymer electrolytes for lithium batteries. Polymer 47(16), 5952–5964 (2006). https://doi.org/10.1016/j.polymer.2006.05.069
D. Xie, M. Zhang, Y. Wu, L. Xiang, Y. Tang, A flexible dual-Ion battery based on sodium-ion quasi-solid-state electrolyte with long cycling life. Adv. Funct. Mater. 30(5), 1906770 (2020). https://doi.org/10.1002/adfm.201906770
F. Croce, L. Persi, B. Scrosati, F. Serraino-Fiory, E. Plichta et al., Role of the ceramic fillers in enhancing the transport properties of composite polymer electrolytes. Electrochim. Acta 46(16), 2457–2461 (2001). https://doi.org/10.1016/S0013-4686(01)00458-3
O. Borodin, X. Ren, J. Vatamanu, A.W. Cresce, J. Knap et al., Modeling insight into battery electrolyte electrochemical stability and interfacial structure. Acc. Chem. Res. 50(12), 2886–2894 (2017). https://doi.org/10.1021/acs.accounts.7b00486
Z. Xu, T. Yang, X. Chu, H. Su, Z. Wang et al., Strong lewis acid-base and weak hydrogen bond synergistically enhancing ionic conductivity of poly(ethylene oxide)@SiO2 electrolytes for a high rate capability Li-metal battery. ACS Appl. Mater. Interfaces 12(9), 10341–10349 (2020). https://doi.org/10.1021/acsami.9b20128
J. Yu, C. Wang, S. Li, N. Liu, J. Zhu et al., Li+-containing, continuous silica nanofibers for high Li+ conductivity in composite polymer electrolyte. Small 15(44), 1902729 (2019). https://doi.org/10.1002/smll.201902729
W. Liu, D. Lin, J. Sun, G. Zhou, Y. Cui, Improved lithium ionic conductivity in composite polymer electrolytes with oxide-ion conducting nanowires. ACS Nano 10(12), 11407–11413 (2016). https://doi.org/10.1021/acsnano.6b06797
T. Itoh, Y. Miyamura, Y. Ichikawa, T. Uno, M. Kubo et al., Composite polymer electrolytes of poly(ethylene oxide)/BaTiO3/Li salt with hyperbranched polymer. J. Power Sources 119–121, 403–408 (2003). https://doi.org/10.1016/S0378-7753(03)00261-1
H.Y. Sun, Y. Takeda, N. Imanishi, O. Yamamoto, H.J. Sohn, Ferroelectric materials as a ceramic filler in solid composite polyethylene oxide-based electrolytes. J. Electrochem. Soc. 147(7), 2462–2467 (2000). https://doi.org/10.1149/1.1393554
H. Jamal, F. Khan, H.R. Si, J.H. Kim, Enhanced compatibility of a polymer-based electrolyte with Li-metal for stable and dendrite-free all-solid-state Li-metal batteries. J. Mater. Chem. A 9(48), 27304–27319 (2021). https://doi.org/10.1039/D1TA06886E
Z. Li, S. Wang, J. Shi, Y. Liu, S. Zheng et al., A 3D interconnected metal-organic framework-derived solid-state electrolyte for dendrite-free lithium metal battery. Energy Storage Mater. 47, 262–270 (2022). https://doi.org/10.1016/j.ensm.2022.02.014
H. Huo, B. Wu, T. Zhang, X. Zheng, L. Ge et al., Anion-immobilized polymer electrolyte achieved by cationic metal-organic framework filler for dendrite-free solid-state batteries. Energy Storage Mater. 18, 59–67 (2019). https://doi.org/10.1016/j.ensm.2019.01.007
Y. Shi, Z. Fan, B. Ding, Z. Li, Q. Lin et al., Atomic-scale Al2O3 modified PEO-based composite polymer electrolyte for durable solid-state Li–S batteries. J. Electroanal. Chem. 881, 114916 (2021). https://doi.org/10.1016/j.jelechem.2020.114916
B. Liang, S. Tang, Q. Jiang, C. Chen, X. Chen et al., Preparation and characterization of PEO-PMMA polymer composite electrolytes doped with nano-Al2O3. Electrochim. Acta 169, 334–341 (2015). https://doi.org/10.1016/j.electacta.2015.04.039
W. Xiao, Z. Wang, Y. Zhang, R. Fang, Z. Yuan et al., Enhanced performance of P(VDF-HFP)-based composite polymer electrolytes doped with organic-inorganic hybrid particles PMMA-ZrO2 for lithium ion batteries. J. Power Sources 382, 128–134 (2018). https://doi.org/10.1016/j.jpowsour.2018.02.012
S. Hua, J.L. Li, M.X. Jing, F. Chen, B.W. Ju et al., Effects of surface lithiated TiO2 nanorods on room-temperature properties of polymer solid electrolytes. Int. J. Energy Res. 44(8), 6452–6462 (2020). https://doi.org/10.1002/er.5379
C. Li, Y. Huang, C. Chen, X. Feng, Z. Zhang, High-performance polymer electrolyte membrane modified with isocyanate-grafted Ti3+ doped TiO2 nanowires for lithium batteries. Appl. Surf. Sci. 563, 150248 (2021). https://doi.org/10.1016/j.apsusc.2021.150248
R. Premila, C. Subbu, S. Rajendran, K.S. Kumar, Experimental investigation of nano filler TiO2 doped composite polymer electrolytes for lithium ion batteries. Appl. Surf. Sci. 449, 426–434 (2018). https://doi.org/10.1016/j.apsusc.2017.11.272
S. Hua, M.X. Jing, C. Han, H. Yang, H. Chen et al., A novel titania nanorods-filled composite solid electrolyte with improved room temperature performance for solid-state Li-ion battery. Int. J. Energy Res. 43(13), 7296–7305 (2019). https://doi.org/10.1002/er.4758
V. Aravindan, P. Vickraman, Effects of TiO2 and ZrO2 nanofillers in LiBOB based PVdF/PVC composite polymer electrolytes (CPE). J. Phys. D 40(21), 6754–6759 (2007). https://doi.org/10.1088/0022-3727/40/21/040
F. Croce, L. Settimi, B. Scrosati, Superacid ZrO2-added, composite polymer electrolytes with improved transport properties. Electrochem. Commun. 8(2), 364–368 (2006). https://doi.org/10.1016/j.elecom.2005.12.002
N.T.K. Sundaram, T. Vasudevan, A. Subramania, Synthesis of ZrO2 nanoparticles in microwave hydrolysis of Zr(IV) salt solutions-Ionic conductivity of PVdF-co-HFP-based polymer electrolyte by the inclusion of ZrO2 nanoparticles. J. Phys. Chem. Solids 68(2), 264–271 (2007). https://doi.org/10.1016/j.jpcs.2006.11.005
V. Aravindan, P. Vickraman, T.P. Kumar, ZrO2 nanofiller incorporated PVC/PVdF blend-based composite polymer electrolytes (CPE) complexed with LiBOB. J. Membr. Sci. 305(1–2), 146–151 (2007). https://doi.org/10.1016/j.memsci.2007.07.044
O. Sheng, C. Jin, J. Luo, H. Yuan, H. Huang et al., Mg2B2O5 nanowire enabled multifunctional solid-state electrolytes with high ionic conductivity, excellent mechanical properties, and flame-retardant performance. Nano Lett. 18(5), 3104–3112 (2018). https://doi.org/10.1021/acs.nanolett.8b00659
Y. Lin, X. Wang, J. Liu, J.D. Miller, Natural halloysite nano-clay electrolyte for advanced all-solid-state lithium-sulfur batteries. Nano Energy 31, 478–485 (2017). https://doi.org/10.1016/j.nanoen.2016.11.045
K. Zhu, Y. Liu, J. Liu, A fast charging/discharging all-solid-state lithium ion battery based on PEO-MIL-53(Al)-LiTFSI thin film electrolyte. RSC Adv. 4(80), 42278–42284 (2014). https://doi.org/10.1039/C4RA06208F
J.F. Wu, X. Guo, MOF-derived nanoporous multifunctional fillers enhancing the performances of polymer electrolytes for solid-state lithium batteries. J. Mater. Chem. A 7(6), 2653–2659 (2019). https://doi.org/10.1039/C8TA10124H
C. Gerbaldi, J.R. Nair, M.A. Kulandainathan, R.S. Kumar, C. Ferrara et al., Innovative high performing metal organic framework (MOF)-laden nanocomposite polymer electrolytes for all-solid-state lithium batteries. J. Mater. Chem. A 2(26), 9948–9954 (2014). https://doi.org/10.1039/C4TA01856G
S. Suriyakumar, S. Gopi, M. Kathiresan, S. Bose, E.B. Gowd et al., Metal organic framework laden poly(ethylene oxide) based composite electrolytes for all-solid-state Li–S and Li-metal polymer batteries. Electrochim. Acta 285, 355–364 (2018). https://doi.org/10.1016/j.electacta.2018.08.012
Y.W. Chen-Yang, Y.T. Chen, H.C. Chen, W.T. Lin, C.H. Tsai, Effect of the addition of hydrophobic clay on the electrochemical property of polyacrylonitrile/LiClO4 polymer electrolytes for lithium battery. Polymer 50(13), 2856–2862 (2009). https://doi.org/10.1016/j.polymer.2009.04.023
M.Y.A. Rahman, A. Ahmad, L.H.C. Ismail, M.M. Salleh, Fabrication and characterization of a solid polymeric electrolyte of PAN-TiO2–LiClO4. J. Appl. Polym. Sci. 115(4), 2144–2148 (2010). https://doi.org/10.1002/app.31299
W. Jia, Z. Li, Z. Wu, L. Wang, B. Wu et al., Graphene oxide as a filler to improve the performance of PAN-LiClO4 flexible solid polymer electrolyte. Solid State Ion. 315, 7–13 (2018). https://doi.org/10.1016/j.ssi.2017.11.026
L. TianKhoon, N.H. Hassan, M.Y.A. Rahman, R. Vedarajan, N. Matsumi et al., One-pot synthesis nano-hybrid ZrO2–TiO2 fillers in 49% poly(methyl methacrylate) grafted natural rubber (MG49) based nano-composite polymer electrolyte for lithium ion battery application. Solid State Ion. 276, 72–79 (2015). https://doi.org/10.1016/j.ssi.2015.03.034
S. Wang, J. Hu, X. Gui, S. Lin, Y. Tu, A promising PMMA/m-MgO all-solid-state electrolyte for lithium-oxygen batteries. J. Electrochem. Soc. 168(2), 020514 (2021). https://doi.org/10.1149/1945-7111/abdfa6
S. Ramesh, S.C. Lu, Effect of nanosized silica in poly(methyl methacrylate)-lithium bis(trifluoromethanesulfonyl)imide based polymer electrolytes. J. Power Sources 185(2), 1439–1443 (2008). https://doi.org/10.1016/j.jpowsour.2008.07.055
S. Ramesh, L.C. Wen, Investigation on the effects of addition of SiO2 nanoparticles on ionic conductivity, FTIR, and thermal properties of nanocomposite PMMA-LiCF3SO3–SiO2. Ionics 16(3), 255–262 (2010). https://doi.org/10.1007/s11581-009-0388-3
J.E. Weston, B.C.H. Steele, Effects of inert fillers on the mechanical and electrochemical properties of lithium salt-poly(ethylene oxide) polymer electrolytes. Solid State Ion. 7(1), 75–79 (1982). https://doi.org/10.1016/0167-2738(82)90072-8
B.R. Cai, J.H. Cao, W.H. Liang, L.Y. Yang, T. Liang et al., Ultraviolet-cured Al2O3-polyethylene terephthalate/polyvinylidene fluoride composite separator with asymmetric design and its performance in lithium batteries. ACS Appl. Energy Mater. 4(5), 5293–5303 (2021). https://doi.org/10.1021/acsaem.1c00804
S.J. Kwon, B.M. Jung, T. Kim, J. Byun, J. Lee et al., Influence of Al2O3 nanowires on ion transport in nanocomposite solid polymer electrolytes. Macromolecules 51(24), 10194–10201 (2018). https://doi.org/10.1021/acs.macromol.8b01603
C.C. Tambelli, A.C. Bloise, A.V. Rosário, E.C. Pereira, C.J. Magon et al., Characterisation of PEO- Al2O3 composite polymer electrolytes. Electrochim. Acta 47(11), 1677–1682 (2002). https://doi.org/10.1016/S0013-4686(01)00900-8
W. Wieczorek, P. Lipka, G. Żukowska, H. Wyciślik, Ionic interactions in polymeric electrolytes based on low molecular weight poly(ethylene glycol)s. J. Phys. Chem. B 102(36), 6968–6974 (1998). https://doi.org/10.1021/jp981397k
Z. Wang, X. Huang, L. Chen, Understanding of effects of nano-Al2O3 particles on ionic conductivity of composite polymer electrolytes. Electrochem. Solid-State Lett. 6(11), E40–E44 (2003). https://doi.org/10.1149/1.1615352
Y.L. Ni’mah, Z.H. Muhaiminah, S. Suprapto, Increase of solid polymer electrolyte ionic conductivity using nano-SiO2 synthesized from sugarcane bagasse as filler. Polymers 13(23), 4240 (2021). https://doi.org/10.3390/polym13234240
Y.L. Yap, A.H. You, L.L. Teo, Preparation and characterization studies of PMMA-PEO-blend solid polymer electrolytes with SiO2 filler and plasticizer for lithium ion battery. Ionics 25(7), 3087–3098 (2019). https://doi.org/10.1007/s11581-019-02842-8
Y. Hu, Y. Zhong, L. Qi, H. Wang, Inorganic/polymer hybrid layer stabilizing anode/electrolyte interfaces in solid-state Li metal batteries. Nano Res. 13(12), 3230–3234 (2020). https://doi.org/10.1007/s12274-020-2993-4
P. Pal, A. Ghosh, Influence of TiO2 nano-particles on charge carrier transport and cell performance of PMMA-LiClO4 based nano-composite electrolytes. Electrochim. Acta 260, 157–167 (2018). https://doi.org/10.1016/j.electacta.2017.11.070
F. Pignanelli, M. Romero, J. Castiglioni, R. Faccio, A.W. Mombrú, Novel synergistic in situ synthesis of lithium-ion poly(ethylene citrate)-TiO2 nanocomposites as promising fluorine-free solid polymer electrolytes for lithium batteries. J. Phys. Chem. Solids 135, 109082 (2019). https://doi.org/10.1016/j.jpcs.2019.109082
C. Chavan, R.F. Bhajantri, V. Cyriac, Ismayil, S. Bulla et al., Exploration of free volume behavior and ionic conductivity of PVA: x (x = 0, Y2O3, ZrO2, YSZ) ion-oxide conducting polymer ceramic composites. J. Non-Cryst. Solids 590, 121696 (2022). https://doi.org/10.1016/j.jnoncrysol.2022.121696
H.M. Xu, M.X. Jing, J. Li, Z.H. Huang, T.F. Wang et al., Safety-enhanced flexible polypropylene oxide-ZrO2 composite solid electrolyte film with high room-temperature ionic conductivity. ACS Sustain. Chem. Eng. 9(33), 11118–11126 (2021). https://doi.org/10.1021/acssuschemeng.1c02886
T. Itoh, Y. Ichikawa, T. Uno, M. Kubo, O. Yamamoto, Composite polymer electrolytes based on poly(ethylene oxide), hyperbranched polymer, BaTiO3 and LiN(CF3SO2)2. Solid State Ion. 156(3), 393–399 (2003). https://doi.org/10.1016/S0167-2738(02)00682-3
B.K. Park, H. Kim, K.S. Kim, H.S. Kim, S.H. Han et al., Interface design considering intrinsic properties of dielectric materials to minimize space-charge layer effect between oxide cathode and sulfide solid electrolyte in all-solid-state batteries. Adv. Energy Mater. 12(37), 2201208 (2022). https://doi.org/10.1002/aenm.202201208
Y.F. Huang, T. Gu, G. Rui, P. Shi, W. Fu et al., A relaxor ferroelectric polymer with an ultrahigh dielectric constant largely promotes the dissociation of lithium salts to achieve high ionic conductivity. Energy Environ. Sci. 14(11), 6021–6029 (2021). https://doi.org/10.1039/D1EE02663A
Q. Liu, Y. Xu, J. Wang, B. Zhao, Z. Li et al., Sustained-release nanocapsules enable long-lasting stabilization of Li anode for practical Li-metal batteries. Nano-Micro Lett. 12, 176 (2020). https://doi.org/10.1007/s40820-020-00514-1
H. Jamal, F. Khan, S. Hyun, S.W. Min, J.H. Kim, Enhancement of the ionic conductivity of a composite polymer electrolyte via surface functionalization of SSZ-13 zeolite for all-solid-state Li-metal batteries. J. Mater. Chem. A 9(7), 4126–4137 (2021). https://doi.org/10.1039/D0TA11218F
G. Zhang, J. Shu, L. Xu, X. Cai, W. Zou et al., Pancake-like MOF solid-state electrolytes with fast ion migration for high-performance sodium battery. Nano-Micro Lett. 13, 105 (2021). https://doi.org/10.1007/s40820-021-00628-0
J.C. Barbosa, R. Gonçalves, C.M. Costa, V.Z. Bermudez, A. Fidalgo-Marijuan et al., Metal-organic frameworks and zeolite materials as active fillers for lithium-ion battery solid polymer electrolytes. Mater. Adv. 2(12), 3790–3805 (2021). https://doi.org/10.1039/D1MA00244A
Z. Ye, Y. Jiang, L. Li, F. Wu, R. Chen, Rational design of MOF-based materials for next-generation rechargeable batteries. Nano-Micro Lett. 13, 203 (2021). https://doi.org/10.1007/s40820-021-00726-z
S. Bai, Y. Sun, J. Yi, Y. He, Y. Qiao et al., High-power Li-metal anode enabled by metal-organic framework modified electrolyte. Joule 2(10), 2117–2132 (2018). https://doi.org/10.1016/j.joule.2018.07.010
Z. Wang, S. Wang, A. Wang, X. Liu, J. Chen et al., Covalently linked metal-organic framework (MOF)-polymer all-solid-state electrolyte membranes for room temperature high performance lithium batteries. J. Mater. Chem. A 6(35), 17227–17234 (2018). https://doi.org/10.1039/C8TA05642K
N. Angulakshmi, K.S. Nahm, J.R. Nair, C. Gerbaldi, R. Bongiovanni et al., Cycling profile of MgAl2O4-incorporated composite electrolytes composed of PEO and LiPF6 for lithium polymer batteries. Electrochim. Acta 90, 179–185 (2013). https://doi.org/10.1016/j.electacta.2012.12.003
A.M. Stephan, T.P. Kumar, S. Thomas, P.S. Thomas, R. Bongiovanni et al., Calcium phosphate incorporated poly(ethylene oxide)-based nanocomposite electrolytes for lithium batteries. I. Ionic conductivity and positron annihilation lifetime spectroscopy studies. J. Appl. Polym. Sci. 124(4), 3245–3254 (2012). https://doi.org/10.1002/app.35219
R. Prasanth, N. Shubha, H.H. Hng, M. Srinivasan, Effect of nano-clay on ionic conductivity and electrochemical properties of poly(vinylidene fluoride) based nanocomposite porous polymer membranes and their application as polymer electrolyte in lithium ion batteries. Eur. Polym. J. 49(2), 307–318 (2013). https://doi.org/10.1016/j.eurpolymj.2012.10.033
M. Deka, A. Kumar, Electrical and electrochemical studies of poly(vinylidene fluoride)-clay nanocomposite gel polymer electrolytes for Li-ion batteries. J. Power Sources 196(3), 1358–1364 (2011). https://doi.org/10.1016/j.jpowsour.2010.09.035
J.W. Gilman, C.L. Jackson, A.B. Morgan, R. Harris, E. Manias et al., Flammability properties of polymer-layered-silicate nanocomposites. Polypropylene and polystyrene nanocomposites. Chem. Mater. 12(7), 1866–1873 (2000). https://doi.org/10.1021/cm0001760
X. Yu, J. Ma, C. Mou, G. Cui, Percolation structure design of organic-inorganic composite electrolyte with high lithium-ion conductivity. Acta Phys. Chim. Sin. 38(3), 1912061 (2022). https://doi.org/10.3866/PKU.WHXB201912061
L. Chen, Y. Li, S.P. Li, L.Z. Fan, C.W. Nan et al., PEO/garnet composite electrolytes for solid-state lithium batteries: from “ceramic-in-polymer” to “polymer-in-ceramic.” Nano Energy 46, 176–184 (2018). https://doi.org/10.1016/j.nanoen.2017.12.037
J.C. Bachman, S. Muy, A. Grimaud, H.H. Chang, N. Pour et al., Inorganic solid-state electrolytes for lithium batteries: mechanisms and properties governing ion conduction. Chem. Rev. 116(1), 140–162 (2016). https://doi.org/10.1021/acs.chemrev.5b00563
J. Zheng, Y.Y. Hu, New insights into the compositional dependence of Li-ion transport in polymer-ceramic composite electrolytes. ACS Appl. Mater. Interfaces 10(4), 4113–4120 (2018). https://doi.org/10.1021/acsami.7b17301
T. Yang, J. Zheng, Q. Cheng, Y.Y. Hu, C.K. Chan, Composite polymer electrolytes with Li7La3Zr2O12 garnet-type nanowires as ceramic fillers: mechanism of conductivity enhancement and role of doping and morphology. ACS Appl. Mater. Interfaces 9(26), 21773–21780 (2017). https://doi.org/10.1021/acsami.7b03806
Z. Li, H.M. Huang, J.K. Zhu, J.F. Wu, H. Yang et al., Ionic conduction in composite polymer electrolytes: case of PEO:Ga-LLZO composites. ACS Appl. Mater. Interfaces 11(1), 784–791 (2019). https://doi.org/10.1021/acsami.8b17279
V. Thangadurai, H. Kaack, W.J.F. Weppner, Novel fast lithium ion conduction in garnet-type Li5La3M2O12 (M = Nb, Ta). J. Am. Ceram. Soc. 86(3), 437–440 (2003). https://doi.org/10.1111/j.1151-2916.2003.tb03318.x
V. Thangadurai, S. Narayanan, D. Pinzaru, Garnet-type solid-state fast Li ion conductors for Li batteries: critical review. Chem. Soc. Rev. 43(13), 4714–4727 (2014). https://doi.org/10.1039/C4CS00020J
W. Lu, M. Xue, C. Zhang, Modified Li7La3Zr2O12 (LLZO) and LLZO-polymer composites for solid-state lithium batteries. Energy Storage Mater. 39, 108–129 (2021). https://doi.org/10.1016/j.ensm.2021.04.016
X. Zhang, T. Liu, S. Zhang, X. Huang, B. Xu et al., Synergistic coupling between Li6.75La3Zr1.75Ta0.25O12 and poly(vinylidene fluoride) induces high ionic conductivity, mechanical strength, and thermal stability of solid composite electrolytes. J. Am. Chem. Soc. 139(39), 13779–13785 (2017). https://doi.org/10.1021/jacs.7b06364
Z. Wan, D. Lei, W. Yang, C. Liu, K. Shi et al., Low resistance-integrated all-solid-state battery achieved by Li7La3Zr2O12 nanowire upgrading polyethylene oxide (PEO) composite electrolyte and PEO cathode binder. Adv. Funct. Mater. 29(1), 1805301 (2019). https://doi.org/10.1002/adfm.201805301
J. Sun, Y. Li, Q. Zhang, C. Hou, Q. Shi et al., A highly ionic conductive poly(methyl methacrylate) composite electrolyte with garnet-typed Li6.75La3Zr1.75Nb0.25O12 nanowires. Chem. Eng. J. 375, 121922 (2019). https://doi.org/10.1016/j.cej.2019.121922
M. Wu, D. Liu, D. Qu, Z. Xie, J. Li et al., 3D coral-like LLZO/PVDF composite electrolytes with enhanced ionic conductivity and mechanical flexibility for solid-state lithium batteries. ACS Appl. Mater. Interfaces 12(47), 52652–52659 (2020). https://doi.org/10.1021/acsami.0c15004
K. Fu, Y. Gong, J. Dai, A. Gong, X. Han et al., Flexible, solid-state, ion-conducting membrane with 3D garnet nanofiber networks for lithium batteries. Proc. Natl. Acad. Sci. 113(26), 7094–7099 (2016). https://doi.org/10.1073/pnas.1600422113
Y. Zhao, J. Yan, W. Cai, Y. Lai, J. Song et al., Elastic and well-aligned ceramic LLZO nanofiber based electrolytes for solid-state lithium batteries. Energy Storage Mater. 23, 306–313 (2019). https://doi.org/10.1016/j.ensm.2019.04.043
D.H. Kim, M.Y. Kim, S.H. Yang, H.M. Ryu, H.Y. Jung et al., Fabrication and electrochemical characteristics of NCM-based all-solid lithium batteries using nano-grade garnet Al-LLZO powder. J. Ind. Eng. Chem. 71, 445–451 (2019). https://doi.org/10.1016/j.jiec.2018.12.001
J. Zagórski, J.M.L. del Amo, M.J. Cordill, F. Aguesse, L. Buannic et al., Garnet-polymer composite electrolytes: new insights on local Li-ion dynamics and electrodeposition stability with Li metal anodes. ACS Appl. Energy Mater. 2(3), 1734–1746 (2019). https://doi.org/10.1021/acsaem.8b01850
C.Z. Zhao, X.Q. Zhang, X.B. Cheng, R. Zhang, R. Xu et al., An anion-immobilized composite electrolyte for dendrite-free lithium metal anodes. Proc. Natl. Acad. Sci. 114(42), 11069–11074 (2017). https://doi.org/10.1073/pnas.1708489114
J. Zhang, X. Zang, H. Wen, T. Dong, J. Chai et al., High-voltage and free-standing poly(propylene carbonate)/Li6.75La3Zr1.75Ta0.25O12 composite solid electrolyte for wide temperature range and flexible solid lithium ion battery. J. Mater. Chem. A 5(10), 4940–4948 (2017). https://doi.org/10.1039/C6TA10066J
J.H. Choi, C.H. Lee, J.H. Yu, C.H. Doh, S.M. Lee, Enhancement of ionic conductivity of composite membranes for all-solid-state lithium rechargeable batteries incorporating tetragonal Li7La3Zr2O12 into a polyethylene oxide matrix. J. Power Sources 274, 458–463 (2015). https://doi.org/10.1016/j.jpowsour.2014.10.078
R. Li, S. Guo, L. Yu, L. Wang, D. Wu et al., Morphosynthesis of 3D macroporous garnet frameworks and perfusion of polymer-stabilized lithium salts for flexible solid-state hybrid electrolytes. Adv. Mater. Interfaces 6(10), 1900200 (2019). https://doi.org/10.1002/admi.201900200
M. Falco, L. Castro, J.R. Nair, F. Bella, F. Bardé et al., UV-cross-linked composite polymer electrolyte for high-rate, ambient temperature lithium batteries. ACS Appl. Energy Mater. 2(3), 1600–1607 (2019). https://doi.org/10.1021/acsaem.8b02185
J. Zheng, M. Tang, Y.Y. Hu, Lithium ion pathway within Li7La3Zr2O12-polyethylene oxide composite electrolytes. Angew. Chem. Int. Ed. 55(40), 12538–12542 (2016). https://doi.org/10.1002/anie.201607539
H. Aono, E. Sugimoto, Y. Sadaoka, N. Imanaka, G.Y. Adachi, Ionic conductivity of solid electrolytes based on lithium titanium phosphate. J. Electrochem. Soc. 137(4), 1023–1027 (1990). https://doi.org/10.1149/1.2086597
E. Dashjav, Q. Ma, Q. Xu, C.L. Tsai, M. Giarola et al., The influence of water on the electrical conductivity of aluminum-substituted lithium titanium phosphates. Solid State Ion. 321, 83–90 (2018). https://doi.org/10.1016/j.ssi.2018.04.010
Q. Liu, Q. Yu, S. Li, S. Wang, L. Zhang et al., Safe LAGP-based all solid-state Li metal batteries with plastic super-conductive interlayer enabled by in-situ solidification. Energy Storage Mater. 25, 613–620 (2020). https://doi.org/10.1016/j.ensm.2019.09.023
P. Hartmann, T. Leichtweiss, M.R. Busche, M. Schneider, M. Reich et al., Degradation of NASICON-type materials in contact with lithium metal: formation of mixed conducting interphases (MCI) on solid electrolytes. J. Phys. Chem. C 117(41), 21064–21074 (2013). https://doi.org/10.1021/jp4051275
X. Wang, H. Zhai, B. Qie, Q. Cheng, A. Li et al., Rechargeable solid-state lithium metal batteries with vertically aligned ceramic nanoparticle/polymer composite electrolyte. Nano Energy 60, 205–212 (2019). https://doi.org/10.1016/j.nanoen.2019.03.051
A. Li, X. Liao, H. Zhang, L. Shi, P. Wang et al., Nacre-inspired composite electrolytes for load-bearing solid-state lithium-metal batteries. Adv. Mater. 32(2), 1905517 (2020). https://doi.org/10.1002/adma.201905517
Y. Jin, X. Zong, X. Zhang, Z. Jia, H. Xie et al., Constructing 3D Li+-percolated transport network in composite polymer electrolytes for rechargeable quasi-solid-state lithium batteries. Energy Storage Mater. 49, 433–444 (2022). https://doi.org/10.1016/j.ensm.2022.04.035
G. Wang, H. Liu, Y. Liang, C. Wang, L.Z. Fan, Composite polymer electrolyte with three-dimensional ion transport channels constructed by NaCl template for solid-state lithium metal batteries. Energy Storage Mater. 45, 1212–1219 (2022). https://doi.org/10.1016/j.ensm.2021.11.021
Q. Guo, Y. Han, H. Wang, S. Xiong, Y. Li et al., New class of LAGP-based solid polymer composite electrolyte for efficient and safe solid-state lithium batteries. ACS Appl. Mater. Interfaces 9(48), 41837–41844 (2017). https://doi.org/10.1021/acsami.7b12092
J. Lee, T. Howell, M. Rottmayer, J. Boeckl, H. Huang, Free-standing PEO/LiTFSI/LAGP composite electrolyte membranes for applications to flexible solid-state lithium-based batteries. J. Electrochem. Soc. 166(2), A416–A422 (2019). https://doi.org/10.1149/2.1321902jes
G. Piana, F. Bella, F. Geobaldo, G. Meligrana, C. Gerbaldi, PEO/LAGP hybrid solid polymer electrolytes for ambient temperature lithium batteries by solvent-free, “one pot” preparation. J. Energy Storage 26, 100947 (2019). https://doi.org/10.1016/j.est.2019.100947
J. Cheng, G. Hou, Q. Sun, Z. Liang, X. Xu et al., Cold-pressing PEO/LAGP composite electrolyte for integrated all-solid-state lithium metal battery. Solid State Ion. 345, 115156 (2020). https://doi.org/10.1016/j.ssi.2019.115156
C. Wang, Y. Yang, X. Liu, H. Zhong, H. Xu et al., Suppression of lithium dendrite formation by using LAGP-PEO (LiTFSI) composite solid electrolyte and lithium metal anode modified by PEO (LiTFSI) in all-solid-state lithium batteries. ACS Appl. Mater. Interfaces 9(15), 13694–13702 (2017). https://doi.org/10.1021/acsami.7b00336
Z.H. Huang, J. Li, L.X. Li, H.M. Xu, C. Han et al., Boosting lithium-ion transport capability of LAGP/PPO composite solid electrolyte via component regulation from ‘ceramics-in-polymer’ to ‘polymer-in-ceramics.’ Ceram. Int. 48(18), 25949–25957 (2022). https://doi.org/10.1016/j.ceramint.2022.05.274
L. Wang, S. Hu, J. Su, T. Huang, A. Yu, Self-sacrificed interface-based on the flexible composite electrolyte for high-performance all-solid-state lithium batteries. ACS Appl. Mater. Interfaces 11(45), 42715–42721 (2019). https://doi.org/10.1021/acsami.9b12112
H. Zhai, P. Xu, M. Ning, Q. Cheng, J. Mandal et al., A flexible solid composite electrolyte with vertically aligned and connected ion-conducting nanoparticles for lithium batteries. Nano Lett. 17(5), 3182–3187 (2017). https://doi.org/10.1021/acs.nanolett.7b00715
Y. Li, H. Wang, Composite solid electrolytes with NASICON-type LATP and PVdF-HFP for solid-state lithium batteries. Ind. Eng. Chem. Res. 60(3), 1494–1500 (2021). https://doi.org/10.1021/acs.iecr.0c05075
S. Bonizzoni, C. Ferrara, V. Berbenni, U. Anselmi-Tamburini, P. Mustarelli et al., NASICON-type polymer-in-ceramic composite electrolytes for lithium batteries. Phys. Chem. Chem. Phys. 21(11), 6142–6149 (2019). https://doi.org/10.1039/C9CP00405J
Y. Jin, X. Zong, X. Zhang, C. Liu, D. Li et al., Interface regulation enabling three-dimensional Li1.3Al0.3Ti1.7(PO4)3-reinforced composite solid electrolyte for high-performance lithium batteries. J. Power Sources 501, 230027 (2021). https://doi.org/10.1016/j.jpowsour.2021.230027
Z. Chen, H. Zhang, H. Xu, S. Dong, M. Jiang et al., In situ generated polymer electrolyte coating-based Janus interfaces for long-life LAGP-based NMC811/Li metal batteries. Chem. Eng. J. 433, 133589 (2022). https://doi.org/10.1016/j.cej.2021.133589
Y. Sun, P. Guan, Y. Liu, H. Xu, S. Li et al., Recent progress in lithium lanthanum titanate electrolyte towards all solid-state lithium ion secondary battery. Crit. Rev. Solid State 44(4), 265–282 (2019). https://doi.org/10.1080/10408436.2018.1485551
J. Lu, Y. Li, Perovskite-type Li-ion solid electrolytes: a review. J. Mater. Sci. Mater. 32(8), 9736–9754 (2021). https://doi.org/10.1007/s10854-021-05699-8
H. Xu, P.H. Chien, J. Shi, Y. Li, N. Wu et al., High-performance all-solid-state batteries enabled by salt bonding to perovskite in poly(ethylene oxide). Proc. Natl. Acad. Sci. 116(38), 18815–18821 (2019). https://doi.org/10.1073/pnas.1907507116
J. Bae, Y. Li, J. Zhang, X. Zhou, F. Zhao et al., A 3D nanostructured hydrogel-framework-derived high-performance composite polymer lithium-ion electrolyte. Angew. Chem. Int. Ed. 57(8), 2096–2100 (2018). https://doi.org/10.1002/anie.201710841
K. Liu, M. Wu, L. Wei, Y. Lin, T. Zhao, A composite solid electrolyte with a framework of vertically aligned perovskite for all-solid-state Li-metal batteries. J. Membr. Sci. 610, 118265 (2020). https://doi.org/10.1016/j.memsci.2020.118265
W. Liu, N. Liu, J. Sun, P.C. Hsu, Y. Li et al., Ionic conductivity enhancement of polymer electrolytes with ceramic nanowire fillers. Nano Lett. 15(4), 2740–2745 (2015). https://doi.org/10.1021/acs.nanolett.5b00600
W. Liu, S.W. Lee, D. Lin, F. Shi, S. Wang et al., Enhancing ionic conductivity in composite polymer electrolytes with well-aligned ceramic nanowires. Nat. Energy 2(5), 17035 (2017). https://doi.org/10.1038/nenergy.2017.35
K. Liu, R. Zhang, J. Sun, M. Wu, T. Zhao, Polyoxyethylene (PEO)|PEO-perovskite|PEO composite electrolyte for all-solid-state lithium metal batteries. ACS Appl. Mater. Interfaces 11(50), 46930–46937 (2019). https://doi.org/10.1021/acsami.9b16936
L. Zhu, P. Zhu, S. Yao, X. Shen, F. Tu, High-performance solid PEO/PPC/LLTO-nanowires polymer composite electrolyte for solid-state lithium battery. Int. J. Energy Res. 43(9), 4854–4866 (2019). https://doi.org/10.1002/er.4638
P. Zhu, C. Yan, M. Dirican, J. Zhu, J. Zang et al., Li0.33La0.557TiO3 ceramic nanofiber-enhanced polyethylene oxide-based composite polymer electrolytes for all-solid-state lithium batteries. J. Mater. Chem. A 6(10), 4279–4285 (2018). https://doi.org/10.1039/C7TA10517G
X. Wang, Y. Zhang, X. Zhang, T. Liu, Y.H. Lin et al., Lithium-salt-rich PEO/Li0.3La0.557TiO3 interpenetrating composite electrolyte with three-dimensional ceramic nano-backbone for all-solid-state lithium-ion batteries. ACS Appl. Mater. Interfaces 10(29), 24791–24798 (2018). https://doi.org/10.1021/acsami.8b06658
P. Zhu, C. Yan, J. Zhu, J. Zang, Y. Li et al., Flexible electrolyte-cathode bilayer framework with stabilized interface for room-temperature all-solid-state lithium-sulfur batteries. Energy Storage Mater. 17, 220–225 (2019). https://doi.org/10.1016/j.ensm.2018.11.009
Q. Zhang, D. Cao, Y. Ma, A. Natan, P. Aurora et al., Sulfide-based solid-state electrolytes: synthesis, stability, and potential for all-solid-state batteries. Adv. Mater. 31(34), 1901131 (2019). https://doi.org/10.1002/adma.201901131
J. Wu, S. Liu, F. Han, X. Yao, C. Wang, Lithium/sulfide all-solid-state batteries using sulfide electrolytes. Adv. Mater. 33(6), 2000751 (2021). https://doi.org/10.1002/adma.202000751
Y. Su, X. Zhang, C. Du, Y. Luo, J. Chen et al., An all-solid-state battery based on sulfide and PEO composite electrolyte. Small 18(29), 2202069 (2022). https://doi.org/10.1002/smll.202202069
M. Li, J.E. Frerichs, M. Kolek, W. Sun, D. Zhou et al., Solid-state lithium-sulfur battery enabled by Thio-LiSICON/polymer composite electrolyte and sulfurized polyacrylonitrile cathode. Adv. Funct. Mater. 30(14), 1910123 (2020). https://doi.org/10.1002/adfm.201910123
Y. Zhang, R. Chen, S. Wang, T. Liu, B. Xu et al., Free-standing sulfide/polymer composite solid electrolyte membranes with high conductance for all-solid-state lithium batteries. Energy Storage Mater. 25, 145–153 (2020). https://doi.org/10.1016/j.ensm.2019.10.020
J. Li, H. Chen, Y. Shen, C. Hu, Z. Cheng et al., Covalent interfacial coupling for hybrid solid-state Li ion conductor. Energy Storage Mater. 23, 277–283 (2019). https://doi.org/10.1016/j.ensm.2019.05.002
Y. Li, W. Arnold, A. Thapa, J.B. Jasinski, G. Sumanasekera et al., Stable and flexible sulfide composite electrolyte for high-performance solid-state lithium batteries. ACS Appl. Mater. Interfaces 12(38), 42653–42659 (2020). https://doi.org/10.1021/acsami.0c08261
H. Liu, P. He, G. Wang, Y. Liang, C. Wang et al., Thin, flexible sulfide-based electrolyte film and its interface engineering for high performance solid-state lithium metal batteries. Chem. Eng. J. 430, 132991 (2022). https://doi.org/10.1016/j.cej.2021.132991
J. Zheng, P. Wang, H. Liu, Y.Y. Hu, Interface-enabled ion conduction in Li10GeP2S12-poly(ethylene oxide) hybrid electrolytes. ACS Appl. Energy Mater. 2(2), 1452–1459 (2019). https://doi.org/10.1021/acsaem.8b02008
F.J. Simon, M. Hanauer, F.H. Richter, J. Janek, Interphase formation of PEO20:LiTFSI-Li6PS5Cl composite electrolytes with lithium metal. ACS Appl. Mater. Interfaces 12(10), 11713–11723 (2020). https://doi.org/10.1021/acsami.9b22968
S. Luo, Z. Wang, A. Fan, X. Liu, H. Wang et al., A high energy and power all-solid-state lithium battery enabled by modified sulfide electrolyte film. J. Power Sources 485, 229325 (2021). https://doi.org/10.1016/j.jpowsour.2020.229325
C. Lai, C. Shu, W. Li, L. Wang, X. Wang et al., Stabilizing a lithium metal battery by an in situ Li2S-modified interfacial layer via amorphous-sulfide composite solid electrolyte. Nano Lett. 20(11), 8273–8281 (2020). https://doi.org/10.1021/acs.nanolett.0c03395
J. Yi, D. Zhou, Y. Liang, H. Liu, H. Ni et al., Enabling high-performance all-solid-state lithium batteries with high ionic conductive sulfide-based composite solid electrolyte and ex-situ artificial SEI film. J. Energy Chem. 58, 17–24 (2021). https://doi.org/10.1016/j.jechem.2020.09.038
X. Li, D. Wang, H. Wang, H. Yan, Z. Gong et al., Poly(ethylene oxide)-Li10SnP2S12 composite polymer electrolyte enables high-performance all-solid-state lithium sulfur battery. ACS Appl. Mater. Interfaces 11(25), 22745–22753 (2019). https://doi.org/10.1021/acsami.9b05212
J. Zhang, C. Zheng, J. Lou, Y. Xia, C. Liang et al., Poly(ethylene oxide) reinforced Li6PS5Cl composite solid electrolyte for all-solid-state lithium battery: enhanced electrochemical performance, mechanical property and interfacial stability. J. Power Sources 412, 78–85 (2019). https://doi.org/10.1016/j.jpowsour.2018.11.036
L. Han, M. Lehmann, J. Zhu, T. Liu, Z. Zhou et al., Recent developments and challenges in hybrid solid electrolytes for lithium-ion batteries. Front. Energy Res. 8, 202 (2020). https://doi.org/10.3389/fenrg.2020.00202
F.Q. Liu, W.P. Wang, Y.X. Yin, S.F. Zhang, J.L. Shi et al., Upgrading traditional liquid electrolyte via in situ gelation for future lithium metal batteries. Sci. Adv. 4(10), eaat5383 (2018). https://doi.org/10.1126/sciadv.aat5383
S. Li, J. Huang, Y. Cui, S. Liu, Z. Chen et al., A robust all-organic protective layer towards ultrahigh-rate and large-capacity Li metal anodes. Nat. Nanotechnol. 17, 613–621 (2022). https://doi.org/10.1038/s41565-022-01107-2
D.H.S. Tan, A. Banerjee, Z. Chen, Y.S. Meng, From nanoscale interface characterization to sustainable energy storage using all-solid-state batteries. Nat. Nanotechnol. 15(3), 170–180 (2020). https://doi.org/10.1038/s41565-020-0657-x
K. Kerman, A. Luntz, V. Viswanathan, Y.M. Chiang, Z. Chen, Review-practical challenges hindering the development of solid state Li ion batteries. J. Electrochem. Soc. 164(7), A1731–A1744 (2017). https://doi.org/10.1149/2.1571707jes
J. Schnell, T. Günther, T. Knoche, C. Vieider, L. Köhler et al., All-solid-state lithium-ion and lithium metal batteries: paving the way to large-scale production. J. Power Sources 382, 160–175 (2018). https://doi.org/10.1016/j.jpowsour.2018.02.062
Acknowledgements
The work was supported by the National Natural Science Foundation of China (Nos. 22279070, U21A20170 and 22175106), the Ministry of Science and Technology of China (Nos. 2019YFA0705703, 2021YFB2501900 and 2019YFE0100200), the Tsinghua University Initiative Scientific Research Program (20223080001) and the Tsinghua-Foshan Innovation Special Fund (2021THFS0216).
Funding
Open access funding provided by Shanghai Jiao Tong University.
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liang, H., Wang, L., Wang, A. et al. Tailoring Practically Accessible Polymer/Inorganic Composite Electrolytes for All-Solid-State Lithium Metal Batteries: A Review. Nano-Micro Lett. 15, 42 (2023). https://doi.org/10.1007/s40820-022-00996-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-022-00996-1