Abstract
Advances in cluster science have enabled the preparation of atomically precise metal clusters with one to a hundred atoms under controllable expansion conditions. After introducing typical gas-phase cluster preparation and reaction apparatuses, this work summarized recent progress in preparing pure metal clusters of single-atom resolution, including neutral and ionic ones, with typical examples of Al, V, Nb, Fe, Co, Ni, Rh, Pt, Ag, Cu, and Pb. With the development of soft-landing deposition technology, the size-selective pure metal clusters with strict atomic precision and predictive property will benefit nanomanufacturing down to atomic and near-atomic scales. This work serves as a modest motivation to stimulate the interest of scientists focusing on interdisciplinary subjects.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Atomic clusters are a new type of matter that bridges the gap between atoms and the nanoscale and exhibits well-defined structures and atomically precise size and composition. Cluster investigations help further understand the micro-mechanisms of nano-catalysis and the structure–function relationship of nanomaterials. Significant research was performed to explore the potential applications of these materials, such as in catalysis, chemo-sensing, bioimaging, biomedicine, optics, quantum computing, and solid-state memory [1,2,3,4,5,6,7,8]. Over the past decades, extensive progress has been made in the preparation of naked metal clusters [9,10,11,12,13,14] and ligand-protected metal clusters [15,16,17,18,19,20,21]. Advances have also been achieved in probing their structural stability, reactivity, and properties [22,23,24,25,26,27]. Studies on the structural stability of clusters and the preparation of condensed-phase metallic nanomaterials or quantum dots with highly tunable properties by cluster assembly or soft-landing deposition [28] for various applications [29, 30] are of great importance.
Micro-dispensing, electrospray deposition, robotic printing, stamping, ink jet deposition, and ion soft-landing are the main techniques for the preparation of solid-supported metal clusters. Among these, the soft-landing deposition of selected metal clusters onto various supports has made substantial progress in the past decades and provided a new way to elucidate interface interactions and improve the selectivity and efficiency of catalytic reactions [31,32,33,34,35,36,37,38,39]. For example, Cooks et al. [40,41,42,43,44] prepared protein microarrays by soft-landing mass-selected ions on specific spots of a moveable target [45]. Palmer et al. [46] studied the physical vapor deposition of metal atoms onto cryogenically cooled supports with simultaneous co-condensing argon and developed a preparation method for the colloidal suspensions of the physically deposited clusters. Vajda and coworkers [47,48,49,50] and Laskin, Johnson, and coworkers [51] conducted many investigations to determine the size effect of supported clusters for chemical reactions [24]. Heiz [52,53,54,55] and Landman [56] revealed a dramatic size dependence in the deposition of mass-selected gold clusters on supports for hydrogenation and oxygen reduction reactions. Nakajima [57] studied the deposition of silicon and metal-doped silicon metal clusters. Song and Wang [58, 59] dedicated efforts to improve the preparation process at the macro scale and examined the size-dependent properties of supported clusters. The development of soft-landing technologies helps further understand the mechanisms of nanomaterials and nanomanufacturing down to atomic and near-atomic scales.
Controllable preparation is the prerequisite for well-resolved metal clusters. However, this condition is challenging because naked nanometals are often reactive in the presence of trace contamination, which largely affects the formation of pure metal clusters (instead of metal oxides or carbides). In general, cluster sources based on magnetron sputtering (MagS) and laser vaporization (LaVa) are dominantly applied for the efficient preparation of gas-phase metal clusters. For these cluster sources, nucleation and growth can be controlled by adjusting the buffer gas pressure and monomer concentration that depends on the ablation laser density or MagS power. In particular, the local space (namely, the waiting room) preceding the nozzle plays a key role in cluster formation.
In addition to its effective preparation, mass spectrometry is one of the most common and powerful tools that can analyze clusters simply by measuring the ion abundance relative to mass-to-charge ratios [60,61,62]. Mass spectrometry techniques, including customized quadrupole mass spectrometry, time-of-flight mass spectrometry (TOFMS), ion-trap mass spectrometry, tandem quadrupole TOFMS (Q-TOFMS), and Fourier transform ion cyclotron resonance system, have been widely used for gas-phase metal cluster studies. Here we summarized the efforts devoted to preparing gas-phase pure metal clusters based on the two source types. We also present several examples of the well-resolved mass spectra of a few typical metals, including Al, V, Nb, Fe, Co, Ni, Rh, Pt, Ag, Cu, and Pb, and the prospect of nanomanufacturing micro materials down to atomic and near-atomic scales.
2 Experimental Methods
Figure 1a displays the diagram of the customized Re-TOFMS system with a self-developed deep ultraviolet (DUV) laser system (abbreviated as DUV-TOFMS) for the optional ionization of neutral species. This instrument involves a self-made LaVa source coupled with a downstream flow tube reactor (~ 60 mm), which allows for efficient cluster preparation and multiple gas collisions [63,64,65,66]. The reactants and product ions pass through a skimmer and are then directed into the second chamber where they are orthogonally accelerated by five plate-electrodes woven with gold wires. The materials are pushed back by a multiplate reflector and collected by a microchannel plate detector. The ion signal is recorded by a digital storage oscilloscope. This integrated system is efficient for the preparation of neutral and ionic clusters and for the study of their gas-phase reactivity with high-resolution mass spectrometry.
A MagS source has the advantages of high efficiency and continuous flow [67,68,69] and operates under highly controllable parameters to achieve tunable cluster size distribution. Figure 1b shows a MagS source in combination with a customized triple quadrupole mass spectrometer (TQMS) and a 1-m-long multiple-ion laminar flow tube (MIFT) reactor [70, 71]. Pure metal clusters can be formed with the MagS source under proper sputtering conditions and are driven out of the source chamber due to the pressure difference in the flow tube (e.g., ~ 0.7 vs. ~ 3 Torr) controlled by a large Roots blower (490 rpm, 510 m3/h). In the absence of electric field constraint, sufficient gas collisions under such a system provide a reliable strategy for probing stable and unstable species. The whole instrument is mounted on a moveable aluminum–alloy shelf, and all the chambers can be separated independently.
3 Results and Discussion
3.1 Main Group Metal Clusters
Figure 2 presents the typical mass spectra of anionic, cationic, and neutral aluminum clusters produced by the LaVa source. Aninion aluminum clusters Aln− (n = 7–37) that will fit with a Gaussian distribution (e.g., centered at Al19−/Al20−) are relatively easy to prepare at proper experimental conditions. By comparison, neutral clusters often show high mass abundance for n = 1, 2. This finding is consistent with previous studies [72, 73]. In addition to mass distribution, the formed clusters are subjected to size-dependent stability. In particular, Al7+, Al13−, and Al23− magically correspond to the closed electronic shells of 40 and 70 valence electrons [74, 75]. This phenomenon is rationalized using the Clemenger–Nilsson ellipsoidal shell model, which considers an effective single-particle potential based on a harmonic oscillator (valid for small clusters). In this model, 2, 8, 20, 40, 70, and 112 correspond to magic numbers. The magic numbers of stable aluminum clusters differ from those of the sodium clusters. Early experimental studies on sodium clusters identified 8, 20, 40, and 58 to be the magic numbers that simply fit with the energy-level occupation for square-well potentials (with 2, 8, 20, 40, 58, 68, 90, and 92 at a sequence of closed shells for 1s, 1p, 1d|2s, 1f|2p, 1g, 2d, 1h, and 3s, respectively) [76]. As an intermediate of these two potentials, a phenomenological Woods–Saxon potential (identical to the self-consistent Kohn–Sham potential) has been widely applied for the empirical jellium model [76,77,78] and successfully predicted the magic numbers in diverse metal clusters.
In the past decades, the structure and stability of heavy metal clusters have been widely studied. The global annual production of lead has reached a few thousand million tons, and lead chemistry study is important for battery application. For this metal, we prepared pure cationic clusters Pbn+ (n = 1–13) with a MagS source and studied the gas-phase reactivity with CH3I. As shown in Fig. 3, the nascent Pbn+ clusters displayed a near-Gaussian distribution, and the reactivity of these cationic Pbn+ clusters with CH3I exhibited strong size dependence [79]. PbnI+ was the dominant product for Pb1-4+, but this material was not observed for Pbn>4+. Relative to the Pb-I bonding, the Pb-Pb interatomic interactions were strengthened with the increasing number of Pb atoms. In contrast to those of Pb1-4+ clusters, the reactions of Pbn>4+ with CH3I showed insurmountable transition state energy barriers.
3.2 Platinum Group Metal Clusters
Platinum group metals are widely used as catalysts for many reactions. Figures 4a–c present the typical mass spectra of Rhn±,0 clusters [80] produced by the laser ablation of a rotating and moving rhodium disk under a helium atmosphere. The abundances of anionic rhodium clusters Rhn–(n = 5–33) and neutral Rhn (n = 4–22) fitted well with Gaussian distribution, and the cations Rhn+ (n = 3–31) fitted well with Rayleigh distribution. We also obtained clean and well-resolved clusters for the other Pt group metals. Figure 4d shows an example of the anionic Ptn− (n = 3–25) clusters, which can also be fitted by a Gaussian curve. By reacting Ptn− with different gas molecules and conducting comprehensive theoretical calculations, we discovered the unexpected stability of Pt10− (insert of Fig. 4d). This feature is associated with the all-metal β-aromaticity and superatom–atom bonding nature (Pt6@Pt4–) in mimicking methane [81].
3.3 Magnetic Metal Clusters
Cobalt, iron, and nickel are the most important metals used as magnetic materials. We studied the size-dependent stability and reactivity of cationic Fe, Co, and Ni clusters using the DUV TOFMS instrument. Figure 5 shows the typical mass spectra of the cationic Fen+ (n = 1–35), Con+ (n = 1–33), and Nin+ (n = 4–50) clusters produced by the LaVa source. Most of these clusters readily reacted with oxygen to produce diverse oxides but displayed competitive multiple reaction channels when reacting with acetylene. At the relatively low partial pressure of the acetylene gas, the Fen+, Con+, and Nin+ clusters reacted with acetylene and were dominated by dehydrogenation; however, at high acetylene concentrations, the cyclotrimerization of acetylene to benzene became the dominant reaction channel [82].
For these metals, we also prepared the anionic clusters and compared their reactivity with that of a few chemicals. The neutral and anionic ones appeared relatively inert while reacting with nitrogen, and the cationic Con+ clusters reacted with multiple N2 to form diverse adducts. One exception is the octahedral superatom Co6+, which survived the reactions with dinitrogen due to its unique stability. In addition, a few cobalt cluster complexes showed significant mass abundances. One of them is Co5N6+, which was identified as a typical superatomic complex. These superatoms and superatomic complexes embody the previously proposed concept of special and general superatoms [83].
Taking advantage of our self-made DUV TOFMS that has ps-pulsed laser ionization and is free of fragmentation, we prepared well-resolved neutral Con (n = 1–30) metal clusters as shown in Fig. 6a. Given that the ionization energies of the neutral Con clusters are smaller than the single-photon energy of 177.3-nm-deep ultraviolet laser (except Co atoms), the ps-pulsed laser bears unique advantages for efficient single-photon ionization. For these well-resolved Con (n ≤ 30) clusters, we comprehensively studied their reactions with oxygen (Fig. 6b). An extremely stable cluster Co13O8 emerged in the spectra and showed dominant mass abundance upon the introduction of sufficient oxygen reactant (Fig. 6c). Furthermore, this Co13O8 cluster showed a cubic structure with remarkable cubic aromaticity. We also studied the reactions of pure Nin± clusters with O2 and found magic clusters Ni13O8± with a body-centered cubic structure similar to that of Co13O8 [84]. This class of oxygen-passivated metal clusters contain a perovskite-like cubic structure and are named “metalloxocubes,” which are an ideal candidate for genetic materials due to the advantages of the cubic building blocks and the stability within inorganic aromaticity [85, 86].
3.4 VB Group Metal Clusters
Extensive studies have illustrated the chemistry of group VB transition metals. Figure 7 plots the mass spectra of neutral vanadium and anionic niobium clusters produced and detected by DUV TOFMS. Taking advantage of the DUV laser ionization and our experiences in preparing metal clusters, we observed the well-resolved mass distribution of neutral Vn (n = 1–42) clusters, as shown in Fig. 7a. The reactions of neutral Vn clusters with water revealed the prominent stability of superatomic V10 (insert of Fig. 7a) and V16 [87]. We also prepared niobium clusters, with the typical spectrum of anionic Nbn− (n = 5–64) clusters displayed in Fig. 7b. Owing to its unique electron configuration ([Kr]4d45s1), Nb is more active than other VB transition metals V ([Ar]3d34s2) and Ta ([Xe]4f145d36s2). Niobium shows diverse oxidation states ranging from − 1 to + 5; however, the Nb-Nb bond energy is up to 513 kJ/mol (V-V bond at 269.3 kJ/mol), which is convenient for the formation of niobium clusters. As shown in Fig. 7b, the Nbn− clusters generated from the LaVa source exhibited a Gaussian-like curve with n up to 60.
We investigated the reactions of the Nbn− clusters with oxygen in the flow tube reactor and found concentration-dependent reaction channels that involve the addition of oxygen, which coexists with O2 etching and growth channels to form various NbnOm− products [88]. We also observed a highly selective product, Nb11O15−, which dominated the mass spectra under the suitable gas flow rate of intermediate O2. DFT calculations unveiled the special stability of Nb11O15− cluster within D5h symmetry and under protection by 15 Nb–O–Nb bridges. Despite being a cluster anion, the cluster shell of Nb11O15− is almost electronically neutral. However, the net atomic charge on the center Nb atom is around − 1, and the shielding effect consequently restricts the electrostatic interactions with other molecules. Meanwhile, the delocalized 11c-2e multicenter bonds endowed remarkable superatomic characteristics to the Nb@Nb10 core, as shown in Fig. 8 [88], accompanied by an extremely large energy release in Nb11O15 formation. The HOMO–LUMO gap (142.8 kJ/mol) is appropriately smaller than that of Nb2O5, thus further indicating its potential application as cluster-genetic materials for Nb-related semiconductors.
3.5 Coinage Metal Clusters
In recent years, coinage metal (Au, Ag, and Cu) nanoclusters have been widely studied, and a variety of ligand-protected metal nanoclusters with high catalytic activity and photoluminescence have been synthesized [89,90,91]. The features of the s-band of coinage metals are close to the density of states of Group IA metals, indicating their comparable electronic structures with group alkali metals; however, these transition metals exhibit properties related to d-d electronic activity [92]. The general principles of the formation of coinage metal clusters and their stabilization mechanism in the gas phase must be studied. Despite their small bond energy (Cu-Cu bond at 201 kJ/mol; Ag–Ag at 162.9 kJ/mol; Au–Au at 226 kJ/mol), coinage metals bear relatively high sputtering rates and readily form metal clusters. Figure 9a presents the mass spectrum of cationic Agn+ (n = 1–27) clusters prepared with a MagS source. In this image, regular odd–even alternation can be observed, and Ag9+ exhibits prominent mass abundance due to its eight-electron shell closure visualized using the jellium model. In addition, we prepared anionic Agn− (n = 10–34) clusters using the LaVa source (Fig. 9b) and studied their reactions with O2 under multiple-collision conditions. A few clusters, such as Ag13− and Ag17-19−, displayed prominent inertness during the reactions with oxygen [93]. First-principles calculation revealed that the ground state Ag17− shows a D4d symmetric structure (inset Fig. 9b) and well-organized superatomic orbitals pertaining to electronic shell closure [94]. Using the same LaVa source and method, we prepared pure copper cluster anions Cun− (n = 7–37) as shown in Fig. 9c. Cu17-19− clusters appeared similarly inert while reacting with a few small molecules such as NO, CO, and O2. The results highlighted the remarkable stability of the open-shell cluster Cu18–, which is comparable with that of the closed-shell clusters Cu17– and Cu19–[95]. The unpaired electron on the SOMO of Cu18– is mainly contributed by the copper atom in the central Cu atom with a charge of − 1.06 |e|, thus implying the endohedral structure (Cu–@Cu17) with electrostatic shielding and electron transfer restriction during the reaction with the chemicals of electron acceptor.
4 Summary and Perspective
Gas-phase naked metal clusters provide an ideal model for studying catalytic activity, electronic and magnetic properties, and atomically precise reaction mechanisms. Although the preparation of pure metal clusters of tunable size distribution has been elucidated, challenges remain in this field, especially for some metals with a weak metal–metal bonding or readily reacting with trace amounts of contamination. Metal cluster studies revealed the possibility of tailoring the unique properties of subnano metals, thus prompting the development of precise chemistry and benefiting atomically precise nanomanufacturing. In the future, the importance of metal cluster catalysis and cluster-genetic materials will be recognized. As a result, cluster soft-landing deposition, assembly, and printing will be adopted for the design of catalysts and functional materials at atomic and near-atomic scales.
Surface spectroscopy has been applied to study the electron transfer between the support and metal clusters (e.g., gold clusters on MgO) [55] and will progress with further research on supported metal clusters, especially the development of extended X-ray absorption fine structure spectroscopy [96]. In addition, the rapid development of electron microscopes, such as spherical aberration microscopes and cryo-electron microscopes, could bring significant contributions to cluster characterization. Advancements on cluster theory from the viewpoints of physics and chemistry [97], including superatom theory [98,99,100,101,102,103,104], will provide insights into the most primitive mechanism of nucleation and cluster formation and serve as a scientific basis for cluster-genetic materials and atomically precise manufacturing.
Change history
23 November 2022
A Correction to this paper has been published: https://doi.org/10.1007/s41871-022-00174-2
References
Luo ZX, Castleman AW, Khanna SN (2016) Reactivity of metal clusters. Chem Rev 116:14456–14492
Tao Y, Li MQ, Ren JS, Qu XG (2015) Metal nanoclusters: novel probes for diagnostic and therapeutic applications. Chem Soc Rev 44:8636–8663
Jin RC, Zeng CJ, Zhou M, Chen YX (2016) Atomically precise colloidal metal nanoclusters and nanoparticles: fundamentals and opportunities. Chem Rev 116:10346–10413
Sun CF, Teo BK, Deng CL, Lin JQ, Luo GG, Tung CH, Sun D (2021) Hydrido-coinage-metal clusters: rational design, synthetic protocols and structural characteristics. Coord Chem Rev 427:213576
Tejada J, Chudnovsky EM, Del Barco E, Hernandez JM, Spiller TP (2001) Magnetic qubits as hardware for quantum computers. Nanotechnology 12:181–186
Busche C, Laia VN, Yan J, Miras HN, Long DL, Georgiev VP, Asenov A, Pedersen RH, Gadegaard N, Mirza MM, Paul DJ, Poblet JM, Cronin L (2014) Design and fabrication of memory devices based on nanoscale polyoxometalate clusters. Nature 515:545–549
Zheng KY, Setyawati MI, Leong DT, Xie JP (2018) Antimicrobial silver nanomaterials. Coord Chem Rev 357:1–17
Chakraborty I, Pradeep T (2017) Atomically precise clusters of noble metals: emerging link between atoms and nanoparticles. Chem Rev 117:8208–8271
Kapiloff E, Ervin KM (1997) Reactions of cobalt cluster anions with oxygen, nitrogen, and carbon monoxide. J Phys Chem A 101:8460–8469
Ervin KM (2001) Metal-ligand interactions: gas-phase transition metal cluster carbonyls. Int Rev Phys Chem 20:127–164
Sakurai M, Watanabe K, Sumiyama K, Suzuki K (1999) Magic numbers in transition metal (Fe, Ti, Zr, Nb, and Ta) clusters observed by time-of-flight mass spectrometry. J Chem Phys 111:235–238
Wang T, Ma J, Yin B, Xing X (2018) Adsorption of O2 on anionic gold clusters in the 0–1 nm size range: an insight into the electron transfer dynamics from kinetic measurements. J Phys Chem A 122:3346–3352
Xing X, Tian Z, Liu H, Tang Z (2003) Magic bimetallic cluster anions of m/Pb (M = Au, Ag and Cu) observed and analyzed by laser ablation and time-of-flight mass spectrometry. Rapid Commun Mass Spectrom 17:1411–1415
Hou GL, Farago E, Buzsaki D, Nyulaszi L, Holtzl T, Janssens E (2020) Observation of the reaction intermediates of methanol dehydrogenation by cationic vanadium clusters. Angew Chem Int Ed Engl 60:4759–4763
Takano S, Hirai H, Nakashima T, Iwasa T, Taketsugu T, Tsukuda T (2021) Photoluminescence of doped superatoms m@Au12 (M = Ru, Rh, Ir) homoleptically capped by (ph2)pch2p(ph2): Efficient room-temperature phosphorescence from Ru@Au12. J Am Chem Soc 143:10560–10564
Zhao Y, Zhuang SL, Liao LW, Wang CM, Xia N, Gan ZB, Gu WM, Li J, Deng HT, Wu ZK (2020) A dual purpose strategy to endow gold nanoclusters with both catalysis activity and water solubility. J Am Chem Soc 142:973–977
Wu ZN, Yao QF, Chai OJH, Ding N, Xu W, Zang SQ, Xie JP (2020) Unraveling the impact of gold(i)-thiolate motifs on the aggregation-induced emission of gold nanoclusters. Angew Chem Int Ed 59:9934–9939
Cao YT, Guo JH, Shi R, Waterhouse GIN, Pan JH, Du ZX, Yao QF, Wu LZ, Tung CH, Xie JP, Zhang TR (2018) Evolution of thiolate-stabilized Ag nanoclusters from Ag-thiolate cluster intermediates. Nat Commun 9:2379
Huang RW, Wei YS, Dong XY, Wu XH, Du CX, Zang SQ, Mak TCW (2017) Hypersensitive dual-function luminescence switching of a silver-chalcogenolate cluster-based metal-organic framework. Nat Chem 9:689–697
Bootharaju MS, Lee S, Deng G, Malola S, Baek W, Häkkinen H, Zheng N, Hyeon T (2021) Ag44(EBT)26(TPP)4 nanoclusters with tailored molecular and electronic structure. AngewChem Int Ed 60:9038–9044
Yan J, Malola S, Hu CY, Peng J, Dittrich B, Teo BK, Hakkinen H, Zheng LS, Zheng NF (2018) Co-crystallization of atomically precise metal nanoparticles driven by magic atomic and electronic shells. Nat Commun 9:1–8
Wang Z, Su HF, Gong YW, Qu QP, Bi YF, Tung CH, Sun D, Zheng LS (2020) A hierarchically assembled 88-nuclei silver-thiacalix[4]arene nanocluster. Nat Commun 11:1–8
Zhou M, Higaki T, Hu GX, Sfeir MY, Chen YX, Jiang DE, Jin RC (2019) Three-orders-of-magnitude variation of carrier lifetimes with crystal phase of gold nanoclusters. Science 364:279–282
Lei Y, Mehmood F, Lee S, Greeley J, Lee B, Seifert S, Winans RE, Elam JW, Meyer RJ, Redfern PC, Teschner D, Schlögl R, Pellin MJ, Curtiss LA, Vajda S (2010) Increased silver activity for direct propylene epoxidation via subnanometer size effects. Science 328:224–228
Yao QF, Chen TK, Yuan X, Xie JP (2018) Toward total synthesis of thiolate-protected metal nanoclusters. Acc Chem Res 51:1338–1348
Du YX, Sheng HT, Astruc D, Zhu MZ (2020) Atomically precise noble metal nanoclusters as efficient catalysts: A bridge between structure and properties. Chem Rev 120:526–622
Kang X, Zhu MZ (2019) Tailoring the photoluminescence of atomically precise nanoclusters. Chem Soc Rev 48:2422–2457
Claridge SA, Castleman AW, Khanna SN, Murray CB, Sen A, Weiss PS (2009) Cluster-assembled materials. ACS Nano 3:244–255
Zhang WJ, Liu Z, Song KP, Aikens CM, Zhang SS, Wang Z, Tung CH, Sun D (2021) A 34-electron superatom Ag78 cluster with regioselective ternary ligands shells and its 2D rhombic superlattice assembly. Angew Chem Int Ed 60:4231–4237
Bi Y, Wang Z, Liu T, Sun D, Godbert N, Li H, Hao J, Xin X (2021) Supramolecular chirality from hierarchical self-assembly of atomically precise silver nanoclusters induced by secondary metal coordination. ACS Nano 15:15910–15919
Dai Y, Gorey TJ, Anderson SL, Lee S, Lee S, Seifert S, Winans RE (2016) Inherent size effects on xanes of nanometer metal clusters: Size-selected platinum clusters on silica. J Phys Chem C 121:361–374
Weber AV, Anderson SL (2016) Electrocatalysis by mass-selected Ptn clusters. Acc Chem Res 49:2632–2639
Timoshenko J, Halder A, Yang B, Seifert S, Pellin MJ, Vajda S, Frenkel AI (2018) Subnanometer substructures in nanoassemblies formed from clusters under a reactive atmosphere revealed using machine learning. J Phys Chem C 122:21686–21693
Negreiros FR, Halder A, Yin CR, Singh A, Barcaro G, Sementa L, Tyo EC, Pellin MJ, Bartling S, Meiwes-Broer KH, Seifert S, Sen P, Nigam S, Majumder C, Fukui N, Yasumatsu H, Vajda S, Fortunelli A (2018) Bimetallic Ag-Pt sub-nanometer supported clusters as highly efficient and robust oxidation catalysts. Angew Chem Int Ed 57:1209–1213
Bentley CL, Kang M, Unwin PR (2018) Nanoscale surface structure-activity in electrochemistry and electrocatalysis. J Am Chem Soc 141:2179–2193
Wang HW, Gu XK, Zheng XS, Pan HB, Zhu JF, Chen S, Cao LN, Li WX, Lu JL (2019) Disentangling the size-dependent geometric and electronic effects of palladium nanocatalysts beyond selectivity. Sci Adv 5:eaat6413
Zhou M, Bao S, Bard AJ (2019) Probing size and substrate effects on the hydrogen evolution reaction by single isolated Pt atoms, atomic clusters, and nanoparticles. J Am Chem Soc 141:7327–7332
Cui CN, Luo ZX, Yao JN (2019) Enhanced catalysis of Pt3 clusters supported on graphene for N-H bond dissociation. CCS Chem 1:215–225
Zhang HC, Cui CN, Luo ZX (2020) MoS2-supported Fe2 clusters catalyzing nitrogen reduction reaction to produce ammonia. J Phys Chem C 124:6260–6266
Cyriac J, Wleklinski M, Li G, Gao L, Cooks RG (2012) In situ Raman spectroscopy of surfaces modified by ion soft landing. Analyst 137:1363–1369
Laskin J, Wang P, Hadjar O, Futrell JH, Alvarez J, Cooks RG (2007) Charge retention by peptide ions soft-landed onto self-assembled monolayer surfaces. Int J Mass Spectrom 265:237–243
Habibpour V, Song MY, Wang ZW, Cookson J, Brown CM, Bishop PT, Palmer RE (2012) Novel powder-supported size-selected clusters for heterogeneous catalysis under realistic reaction conditions. J Phys Chem C 116:26295–26299
Peng WP, Johnson GE, Fortmeyer IC, Wang P, Hadjar O, Cooks RG, Laskin J (2011) Redox chemistry in thin layers of organometallic complexes prepared using ion soft landing. Phys Chem Chem Phys 13:267–275
Miller SA, Luo H, Pachuta SJ, Cooks RG (1997) Soft-landing of polyatomic ions at fluorinated self-assembled monolayer surfaces. Science 275:1447–1450
Ouyang Z, Taka Z, Blake TA, Gologan B, Guymon AJ, Wiseman JM, Oliver JC, Davisson VJ, Cooks RG (2003) Preparing protein microarrays by soft-landing of mass-selected ions. Science 301:1351–1354
Cai R, Jian N, Murphy S, Bauer K, Palmer RE (2017) A new method to prepare colloids of size-controlled clusters from a matrix assembly cluster source. APL Materials 5:053405
Yin CR, Negreiros FR, Barcaro G, Beniya A, Sementa L, Tyo EC, Bartling S, Meiwes-Broer KH, Seifert S, Hirata H, Isomura N, Nigam S, Majumder C, Watanabe Y, Fortunelli A, Vajda S (2017) Alumina-supported sub-nanometer Pt10 clusters: amorphization and role of the support material in a highly active CO oxidation catalyst. J Mater Chem A 5:4923–4931
Yang B, Liu C, Halder A, Tyo EC, Martinson AB, Seifer S, Zapol P, Curtiss LA, Vajda S (2017) Copper cluster size effect in methanol synthesis from CO2. J Phys Chem C 121:10406–10412
Halder A, Liu C, Liu Z, Emery JD, Pellin MJ, Curtiss LA, Zapol P, Vajda S, Martinson AB (2018) Water oxidation catalysis via size-selected iridium clusters. J Phys Chem C 122:9965–9972
Halder A, Curtiss LA, Fortunelli A, Vajda S (2018) Perspective: Size selected clusters for catalysis and electrochemistry. J Chem Phys 148:110901
Laskin J, Johnson GE, Warneke J, Prabhakaran V (2018) From isolated ions to multilayer functional materials using ion soft landing. Angew Chem Int Ed Engl 57:16270–16284
Nesselberger M, Roefzaad M, Hamou RF, Biedermann PU, Schweinberger FF, Kunz S, Schloegl K, Wiberg GK, Ashton S, Heiz U, Mayrhofer KJ, Arenz M (2013) The effect of particle proximity on the oxygen reduction rate of size-selected platinum clusters. Nat Mater 12:919–924
Wettergren K, Schweinberger FF, Deiana D, Ridge CJ, Crampton AS, Rotzer MD, Hansen TW, Zhdanov VP, Heiz U, Langhammer C (2014) High sintering resistance of size-selected platinum cluster catalysts by suppressed Ostwald ripening. Nano Lett 14:5803–5809
Rondelli M, Zwaschka G, Krause M, Rötzer MD, Hedhili MN, Högerl MP, D’Elia V, Schweinberger FF, Basset JM, Heiz U (2017) Exploring the potential of different-sized supported subnanometer Pt clusters as catalysts for wet chemical applications. ACS Catal 7:4152–4162
Yoon B, Hakkinen H, Landman U, Worz AS, Antonietti JM, Abbet S, Judai K, Heiz U (2005) Charging effects on bonding and catalyzed oxidation of CO on Au8 clusters on MgO. Science 307:403–407
Sanchez A, Abbet S, Heiz U, Schneider WD, Häkkinen H, Barnett RN, Landman U (1999) When gold is not noble: nanoscale gold catalysts. J Phys Chem A 103:9573–9578
Mitsui M, Nagaoka S, Matsumoto T, Nakajima A (2006) Soft-landing isolation of vanadium-benzene sandwich clusters on a room-temperature substrate using n-alkanethiolate self-assembled monolayer matrixes. J Phys Chem B 110:2968–2971
Qin Y, Han J, Guo G, Du Y, Li Z, Song Y, Pi L, Wang X, Wan X, Han M, Song F (2015) Enhanced quantum coherence in graphene caused by Pd cluster deposition. Appl Phys Lett 106:023108
Kwon G, Ferguson GA, Heard CJ, Tyo EC, Yin C, DeBartolo J, Seifert S, Winans RE, Kropf AJ, Greeley J, Johnston RL, Curtiss LA, Pellin MJ, Vajda S (2013) Size-dependent subnanometer Pd cluster (Pd4, Pd6, and Pd17) water oxidation electrocatalysis. ACS Nano 7:5808–5817
Luo ZX (2017) Deep ultraviolet single-photon ionization mass spectrometry. InTech, London
Gross J (2013) Mass spectrometry. Springer, Heidelberg
Luo ZX, Khanna SN (2020) Metal clusters and their reactivity. Springer, Singapore
Yuan CQ, Liu XH, Zeng CH, Zhang HY, Jia MY, Wu YS, Luo ZX, Fu HB, Yao JN (2016) All-solid-state deep ultraviolet laser for single-photon ionization mass spectrometry. Rev Sci Instrum 87:024102
Zhang HY, Wu HM, Jia YH, Geng LJ, Luo ZX, Fu HB, Yao JN (2019) An integrated instrument of DUV-IR photoionization mass spectrometry and spectroscopy for neutral clusters. Rev Sci Instrum 90:073101
Long Y, Song SY, Li J, Wu LL, Wang QS, Liu Y, Jin RC, Zhang HJ (2018) Pt/CeO2@MOF core@shell nanoreactor for selective hydrogenation of furfural via the channel screening effect. ACS Catal 8:8506–8512
Fang J, Zhang B, Yao Q, Yang Y, Xie J, Yan N (2016) Recent advances in the synthesis and catalytic applications of ligand-protected, atomically precise metal nanoclusters. Coord Chem Rev 322:1–29
Zhang C, Tsunoyama H, Akatsuka H, Sekiya H, Nagase T, Nakajima A (2013) Advanced nanocluster ion source based on high-power impulse magnetron sputtering and time-resolved measurements of nanocluster formation. J Phys Chem A 117:10211–10217
Dai HQ, Xu H, Zhou YN, Lu F, Fu ZW (2012) Electrochemical characteristics of Al2O3-doped ZnO films by magnetron sputtering. J Phys Chem C 116:1519–1525
Zhao J, Baibuz E, Vernieres J, Grammatikopoulos P, Jansson V, Nagel M, Steinhauer S, Sowwan M, Kuronen A, Nordlund K, Djurabekova F (2016) Formation mechanism of Fe nanocubes by magnetron sputtering inert gas condensation. ACS Nano 10:4684–4694
Wilson DJ, Konermann L (2005) Ultrarapid desalting of protein solutions for electrospray mass spectrometry in a microchannel laminar flow device. Anal Chem 77:6887–6894
Ouyang T, Ye YQ, Wu CY, Xiao K, Liu ZQ (2019) Heterostructures composed of n-doped carbon nanotubes encapsulating cobalt and β-Mo2C nanoparticles as bifunctional electrodes for water splitting. Angew Chem Int Ed 131:4977–4982
Woodward WH, Eyet N, Shuman NS, Smith JC, Viggiano AA, Castleman AW (2011) Aluminum cluster anion reactivity with singlet oxygen: evidence of Al9- stability. J Phys Chem C 115:9903–9908
Jia YH, Luo ZX (2019) Thirteen-atom metal clusters for genetic materials. Coordin Chem Rev 400:1–17
Leuchtner RE, Harms AC, Castleman AW (1989) Thermal metal cluster anion reactions-behavior of aluminum clusters with oxygen. J Chem Phys 91:2753–2754
Cox DM, Trevor DJ, Whetten RL, Rohlfing EA, Kaldor A (1986) Aluminum clusters: magnetic properties. J Chem Phys 84:4651–4656
De Heer WA (1993) The physics of simple metal clusters: experimental aspects and simple models. Rev Mod Phys 65:611–676
Brack M (1993) The physics of simple metal clusters: self-consistent jellium model and semiclassical approaches. Rev Mod Phys 65:677–732
Knight WD, Clemenger K, de Heer WA, Saunders WA, Chou MY, Cohen ML (1984) Electronic shell structure and abundances of sodium clusters. Phys Rev Lett 52:2141–2143
Yang M, Wu H, Huang B, Luo Z, Hansen K (2020) Iodization threshold in size-dependent reactions of lead clusters Pbn+ with iodomethane. J Phys Chem A 124:2505–2512
Jia Y, Wu H, Zhao X, Zhang H, Geng L, Zhang H, Li S, Luo Z, Hansen K (2021) Interactions between water and rhodium clusters: molecular adsorption versus cluster adsorption. Nanoscale 13:11396–11402
Jia Y, Yu X, Zhang H, Cheng L, Luo Z (2021) Tetrahedral Pt10- cluster with unique beta aromaticity and superatomic feature in mimicking methane. J Phys Chem Lett 12:5115–5122
Gan W, Geng L, Yin B, Zhang H, Luo Z, Hansen K (2021) Cyclotrimerization of acetylene on clusters Con+/Fen+/Nin+ (n = 1–16). J Phys Chem A 125:10392–10400
Geng LJ, Cui CN, Jia YH, Yin BQ, Zhang HY, Sun ZD, Luo ZX (2021) Reactivity of cobalt clusters Con±/0 with dinitrogen: superatom Co6+ and superatomic complex Co5N6+. J Phys Chem A 125:2130–2138
Geng LJ, Yin BQ, Zhang HY, Sun ZD, Luo ZX (2021) Spin accommodation and reactivity of nickel clusters with oxygen: aromatic and magnetic metalloxocube Ni13O8±. Nano Res 14:4822–4827
Geng LJ, Weng MY, Xu CQ, Zhang HY, Cui CN, Wu HM, Chen X, Hu MY, Lin H, Sun ZD, Wang X, Hu HS, Li J, Zheng JX, Luo ZX, Pan F, Yao JN (2020) Co13O8-metalloxocubes: A new class of perovskite-like neutral clusters with cubic aromaticity. Natl Sci Rev 201:1–8
Jia Y, Li J, Huang M, Geng L, Zhang H, Cheng S-B, Yi Y, Luo Z (2022) Ladder oxygenation of group VIII metal clusters and the formation of metalloxocubes M13O8+. J Phys Chem Lett 13:733–739
Zhang HY, Zhang MZ, Jia YH, Geng LJ, Yin BQ, Li SN, Luo ZX, Pan F (2021) Vanadium cluster neutrals reacting with water: Superatomic features and hydrogen evolution in a fishing mode. J Phys Chem Lett 12:1593–1600
Lei X, Zhang HY, Jia YH, Luo ZX (2021) Gas-phase preparation and the stability of superatomic Nb11O15−. Phys Chem Chem Phys 23:15766–15773
Anumula R, Xiao P, Cui C, Wu H, Cui G, Fang W, Luo Z, Yao J (2020) A small bimetallic Ag3Cu2 nanocluster with dual emissions within and against Kasha’s rule. Nanoscale 12:7864–7869
Anumula R, Reber AC, An P, Cui C, Guo M, Wu H, Luo Z, Khanna SN (2020) Ligand accommodation causes the anti-centrosymmetric structure of Au13Cu4 clusters with near-infrared emission. Nanoscale 12:14801–14807
Wu HM, Fang YG, Anumula R, Andrew GN, Cui GL, Fang WH, Luo ZX, Yao JN (2021) A mono-copper doped undeca-gold cluster with up-converted and anti-stokes emissions of fluorescence and phosphorescence. Nanoscale 13:5300–5306
Yin BQ, Luo ZX (2021) Coinage metal clusters: From superatom chemistry to genetic materials. Coord Chem Rev 429:213643
Luo Z, Gamboa GU, Smith JC, Reber AC, Reveles JU, Khanna SN, Castleman AW (2012) Spin accommodation and reactivity of silver clusters with oxygen: the enhanced stability of Ag13-. J Am Chem Soc 134:18973–18978
Yin BQ, Du QY, Geng LJ, Zhang HY, Luo ZX, Zhou S, Zhao JJ (2021) Superatomic signature and reactivity of silver clusters with oxygen: Double magic Ag17- with geometric and electronic shell closure. CCS Chem 3:219–229
Yin BQ, Du QY, Geng LJ, Zhang HY, Luo ZX, Zhou S, Zhao JJ (2020) Anionic copper clusters reacting with NO: An open-shell superatom Cu18-. J Phys Chem Lett 11:5807–5814
An P, Anumula R, Cui C, Liu Y, Zhan F, Tao Y, Luo Z (2019) A facile method to synthesize water-soluble Pd8 nanoclusters unraveling the catalytic mechanism of p-nitrophenol to p-aminophenol. Nano Res 12:2589–2596
Luo Z, Khanna S (2020) Metal clusters and their reactivity. Springer, Singapore
Luo Z, Castleman AW (2014) Special and general superatoms. Acc Chem Res 47:2931–2940
Jia Y, Luo Z (2019) Thirteen-atom metal clusters for genetic materials. Coord Chem Rev 400:213053
Yin B, Luo Z (2021) Coinage metal clusters: From superatom chemistry to genetic materials. Coord Chem Rev 429:213643
Reber AC, Khanna SN (2017) Superatoms: electronic and geometric effects on reactivity. Acc Chem Res 50:255–263
Zhao J, Du Q, Zhou S, Kumar V (2020) Endohedrally doped cage clusters. Chem Rev 120:9021–9163
Jena P, Sun Q (2018) Super atomic clusters: Design rules and potential for building blocks of materials. Chem Rev 118:5755–5870
Liu Z, Wu X, Zhu Y, Wang R, Yu F, Wang Z (2021) Superatomic Rydberg state excitation. J Phys Chem Lett 12:11766–11771
Acknowledgements
We thank Prof. Jiannian Yao and Prof. Fengzhou Fang for their guidance and communication. This work was financially supported by the Ministry of Science and Technology of the People's Republic of China (No. 2020YFA0714602), the National Natural Science Foundation of China (Grant No. 21722308 and 22003072), the Key Research Program of CAS Frontier Sciences (CAS Grant QYZDBSSWSLH024), the National Project Development of Advanced Scientific Instruments Based on Deep Ultraviolet Laser Source (Y31M0112C1), and the CAS Instrument Development Project (Y5294512C1).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no conficts of interest.
Additional information
The original online version of this article was revised: The declaration text was missing.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wu, H., Zhang, H., Geng, L. et al. Pure Metal Clusters with Atomic Precision for Nanomanufacturing. Nanomanuf Metrol 5, 230–239 (2022). https://doi.org/10.1007/s41871-022-00139-5
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41871-022-00139-5