Abstract
Enhanced resistive memory characteristics with 10,000 consecutive direct current switching cycles, long read pulse endurance of >105 cycles, and good data retention of >104 s with a good resistance ratio of >102 at 85°C are obtained using a Ti nanolayer to form a W/TiO x /TaO x /W structure under a low current operation of 80 μA, while few switching cycles are observed for W/TaO x /W structure under a higher current compliance >300 μA. The low resistance state decreases with increasing current compliances from 10 to 100 μA, and the device could be operated at a low RESET current of 23 μA. A small device size of 150 × 150 nm2 is observed by transmission electron microscopy. The presence of oxygen-deficient TaO x nanofilament in a W/TiO x /TaO x /W structure after switching is investigated by Auger electron spectroscopy. Oxygen ion (negative charge) migration is found to lead to filament formation/rupture, and it is controlled by Ti nanolayer at the W/TaO x interface. Conducting nanofilament diameter is estimated to be 3 nm by a new method, indicating a high memory density of approximately equal to 100 Tbit/in.2.
Avoid common mistakes on your manuscript.
Background
Resistive switching random access memories (RRAM) with simple metal-insulator-metal stacks are under intensive investigation owing to their great promise for use in next-generation memory applications [1–5]. However, their nonuniformity in switching, low yield, and unclear switching mechanism hinder their practical realization. RRAM devices with simple composition, easy fabrication process, and good 3D integration compatibility will be needed in the future. Methods such as doping, formation polarity control, bottom electrode modification, nanocrystal insertion, and interfacial engineering have recently been investigated to improve the characteristics of resistive switching memory [6–10]. Among other important switching materials such as TiO x [11, 12], NiO x [13–15], HfO x [10, 16–18], ZrO x [19–27], Na0.5Bi0.5TiO3[28], SrTiO3[29], ZnO [30, 31], GeO x [32], and SiO x [33], tantalum oxide (TaO x ) is one of the most promising choices for future RRAM applications. However, TaO x -based RRAM devices are infrequently reported [5, 34–39]. Terai et al. [37] used a TiO2 layer in a Ru/Ta2O5/TiO2/Ru stack with good thermal stability. Ninomiya et al. [38] reported an Ir/Ta2O5−δ/TaO x /TaN structure, and Lee et al. [5] reported a Pt/Ta2O5−x/TaO2−x/Pt crossbar structure with two layers of TaO x and at least one of the inert electrodes such as Ru, Ir, and Pt. Generally, many researchers use one inert electrode to improve the performance of resistive switching memory [5, 39]; however, tungsten (W) as both bottom and top electrodes in a W/TiO x /TaO x /W structure has not yet been reported. Furthermore, the RRAM devices with low current operation (<100 μA) is also a challenging issue. In this work, a resistive switching memory device using a Ti nanolayer at the W/TaO x interface and enhanced memory characteristics such as excellent 10,000 consecutive stable dc switching cycles, long read pulse endurance of >105 cycles, and good data retention of 104 s at 85°C with a large resistance ratio of >102 under a low compliance current (CC) of 80 μA are reported. Furthermore, the device can be operated with a small ‘RESET’ current of 23 μA. For comparison, the W/TaO x /W memory device is also fabricated. The device size of 150 × 150 nm2 is observed using a high-resolution transmission electron microscope (HRTEM). The thicknesses of TiO x and TaO x nanolayers are 3 and 7 nm, respectively. The presence of oxygen-deficient TaO x conducting filaments is investigated by Auger electron spectroscopy (AES) before and after switching of the memory devices. The switching mechanism of the oxygen ion migration owing to a lower barrier height of electrons is investigated, and a filament diameter of approximately equal to 3 nm is calculated using a new method also reported in this work. Considering a small filament diameter, a high memory density of approximately equal to 100 Tbit/in.2 could be designed in the future.
Methods
W/Ti/TaO x /W-structured (device S1) and W/TaO x /W-structured (device S2) resistive switching memory stacks were fabricated. A small via size of 150 × 150 nm2 was etched into the SiO2 on W bottom electrode (BE), which was about 100 nm in thickness. Standard photolithography and dry etching processes were used to open the via holes for the RRAM devices. The photoresist (PR) was coated and opened on active and top electrode (TE) regions for lift-off process. Then, a high-κ Ta2O5 film with a thickness () of approximately equal to 7 nm was deposited by an e-beam evaporator, followed by the sequential deposition of a thin (approximately equal to 3 nm) interfacial layer of titanium (Ti) and approximately equal to 200-nm-thick W layer as a TE by radio-frequency (rf) sputtering. The W and Ti targets were used. Initial vacuum was approximately 10−5 Torr. Argon gas (Ar) with a flow rate of 25 sccm and deposition power of 100 W was used to deposit W. The W deposition rate was 10 nm/min. For Ti deposition, Ar with a flow rate of 15 sccm and deposition power of 150 W were used. The Ti deposition rate was approximately 6.5 nm/min. For device S2, no Ti layer was deposited. The final devices were obtained after a lift-off process. Memory device structure and thicknesses of all layers were observed by transmission electron microscopy (TEM) with an energy of 200 keV. The TaO x material was also confirmed by quadrupole secondary ion mass spectroscopy (SIMS; ATOMIKA SIMS 4500, MA-Tek, Hsinchu, Taiwan) which had a high-depth resolution. Primary beam was O2+ with an energy of 0.5 keV and analysis area of 37.5 × 37.5 μm2. A bias was applied to the TE, and the BE was electrically grounded. Pristine S1 and S2 devices were electroformed by applying positive voltage to the TE before consecutive resistive switching cycle measurements.
Results and discussion
Figure 1a shows a typical cross-sectional TEM image of the W/TiO x /TaO x /W structure. The device size is 150 × 150 nm2. HRTEM images of the S2 and S1 devices are shown in Figure 1b,c. The thicknesses of the TiO x and TaO x layers are approximately 3 and 7 nm, respectively, and both films show an amorphous characteristic. The film deposited by rf sputtering is not a conformal deposition. Therefore, the TiO x layer can be seen clearly on outside and active regions of the via hole (Figure 1a,c); however, this layer is not observed clearly on the sidewall of the via hole. It is also obvious that the switching material on the sidewall is not necessary for switching properties of the RRAM devices because the electrons will find least path to move from TE to BE. This TiO x layer is also confirmed on outside and active region of the device by energy dispersive X-ray spectroscopy (not shown here). Figure 2 shows typical SIMS depth profiles of 16O, 184 W, and 181Ta materials for the S2 sample. The thickness of the TaO x layer is about 15 nm; however, this is higher than the deposited film thickness of 7 nm. This is due to the trail effect and surface roughness of W BE, as we can see from the depth of 57 to 65 nm (or approximately 7 nm) of the 184 W depth profile. The average surface roughness of 200-nm-thick W layer on SiO2/Si substrate is approximately 2.8 nm, which is observed by atomic force microscopy (AFM) with a scan area of 1 × 1 μm2, as shown in Figure 3. Therefore, the remaining thickness of approximately 4.2 nm (=7 to 2.8 nm) is coming from the trail effect of the SIMS depth profile. The depth from 50 to 57 nm is the thickness of the TaO x layer, which is approximately 7 nm, as shown in Figure 2a,c. It is interesting to note that the TaO x /W interface is found to be an oxygen-deficient layer, which makes it a more conducting interface. On the other hand, the conducting filament will be formed after breaking the Ta-O bonds in the bulk Ta2O5 layer rather than the W/TaO x interface. This is because the Ta2O5 layer is more insulating than the W/TaO x interface, so the electric field will drop across the Ta2O5 film rather than the W/TaO x interface which probably results multi-filaments or an uncontrolled nanofilament diameter. As Ti removes oxygen from the Ta2O5 film in the W/TiO x /TaO x /W structure, the TaO x film becomes more oxygen-deficient, which is vital to achieve an improved resistive switching. Considering Gibbs free energies of TiO2, Ta2O5, and WO3 films, which are −887.6, −760.5, and −506.5 kJ/mol, respectively, at 300 K [40], Ti will consume the highest oxygen content owing to its stronger reactivity than those of the other materials, thereby forming a Ta-rich (or defective TaO x ) film. This also prevents oxidation of the W TE at the TaO x /W interface of device S1 owing to the migration of oxygen from the underlying films towards the Ti film, which contributes to the improved resistive switching memory performance as will be described.
The leakage current values of most of the S1 pristine devices at a read voltage (Vread) of 1 V are higher than that of the S2 devices because of the presence of more oxygen vacancies in the TaO x layer owing to the oxygen-getter nature of the TiO x layer (Figure 4a). Typical current-voltage (I-V) curves (inset of Figure 4a) of both devices were asymmetrical with higher current at a negative voltage (≈281 pA for S1 and ≈ 12.6 pA for S2 at Vread = −1 V) compared with that measured at a positive voltage (≈9.8 pA for S1 and ≈ 0.6 pA for S2 at Vread = 1 V). This suggests that the W TE/TaO x interface has more oxygen vacancies than the TaO x /W BE interface, owing to oxygen migration towards W TE during deposition. The ideal leakage current is plotted in Figure 5a and is explained as follows: It is reported that the work function (Фm) of W and bandgap (Eg) of amorphous Ta2O5 and TiO2 are 4.55 [41], 4.2 [42], and 3.3 eV [43], respectively. The conduction band offsets of Ta2O5 and TiO2 with Si are 0.3 [44] and 0.9 eV [45], respectively. Taking the electron affinity of Si as 4.05 eV, the electron affinities of Ta2O5 and TiO2 are calculated to be 3.75 and 3.15 eV, respectively. The corresponding energy diagram is shown in Figure 5a as solid lines. Considering that the Eg of TiO2 for the pristine S1 device will be much lower because of oxygen vacancy creation during the deposition of W TE, the band diagram is shown in dotted lines (Figure 5a). In this case, electron injection dominates rather than hole injection because of a lower barrier height for electrons than for holes (0.8 to 1.4 vs. 3.4 eV). Both S1 and S2 devices show bipolar resistive switching behaviors. The S2 device shows few switching cycles with a higher leakage current of ≈ 10 μA at Vread = 1 V and a higher CC of 300 μA (Figure 4b). In this case, negatively charged oxygen ions (O2−) migrate from the switching material towards W TE, and this has a lesser possibility to form an oxygen-rich layer at the W TE/TaO x interface, leading to the formation of multi-conduction filaments. In the same way, no resistive switching is observed under negative forming voltage for either the S1 or S2 devices because oxygen ions migrate towards the W BE and permanent breakdown is observed (not shown here). The negative forming will lead to high switching current, which is similar to the W/TaO x /W structure, and there is no oxygen-rich interfacial layer at the W/TaO x interface. This interfacial layer will have series resistance and protect from current overshoot effect. However, the insertion of a thin (≈3 nm) Ti layer in between the W and TaO x layers in the S1 device makes a vast difference because Ti can be used as an oxygen reservoir. Moreover, the S1 device exhibits >10,000 consecutive repeatable dc switching cycles with a better resistance ratio of 102 under a low CC of 80 μA (Figure 4c). The transport mechanism follows the trap-charge-controlled space-charge-limited current conduction (not shown here). However, a thicker Ti layer (5 nm) results in unstable switching cycles because it gets more oxygen and behaves as an insulating layer. This may lead to the conducting filament formation/rupture in the TiO x layer rather than the TaO x layer. It is reported that the TiO2 switching layer has a Magneli phase and the memory window is collapsed after a few cycles [46]. That is the reason of having unstable switching using thicker (5 nm) Ti interracial layer. Therefore, thickness optimization is very important and we have chosen those thicknesses of TaO x and TiO x layers here. The thinnest Ti layer of <3 nm is also not to be used because of direct current flow through this layer. Therefore, the thinner (3 nm) Ti layer will control the current overflow as well as will control the filament diameter. The yield of the S1 device is very high (>95%), while that of the S2 device is very low (approximately 10%). In addition, the S2 device cannot be switched below a CC of 300 μA and shows an ohmic behavior, while the S1 device shows switching even at a low CC of 10 μA (discussed later) with non-ohmic current conduction. The average values and standard deviation/average are found to be 39.7 and 0.11, 38.4 kΩ and 0.08 for low-resistance state (LRS) and 1.9 and 2.11, 8.6 MΩ and 0.43 for high-resistance state (HRS) at Vread of 1 V and −1 V, respectively (Figure 4d). This suggests that the LRS has a tighter distribution than the HRS because of the formation of the TiO2 layer, which will have a higher Eg than the pristine one. Similarly, the leakage current at Vread of −1 V is lower than that at +1 V because of the lower electron injection barrier at the TE/TiO2 interface than that at the BE/TaO x interface after switching. Under ‘SET’, O2− will migrate from TaO x towards the TE, resulting in a TiO2 layer which controls the conducting vacancy filament diameter in the TaO x layer by controlling current overflow and producing a tighter distribution of the LRS. Owing to this series resistance, the S1 devices exhibit non-ohmic-simulated (or nonlinear) ideal current, as shown in Figure 5b, whereas an ohmic current is observed for the S2 devices under SET (Figure 5c). It is true that the conducting filament is formed through the TaO x film (Figure 5b,c), which is also confirmed by the AES spectra of the TaO x film for pristine and after-switching of the TaO x -based devices (Figure 6). The differentiated counts with respect to kinetic energy (dC/dE) versus kinetic energy (E) are plotted. The spectrum positions are in the middle of the TaO x switching layer with a typical device size of 0.4 × 0.4 μm2. Different RRAM devices of pristine and switching were used to get the AES spectra. Even though different devices were used, the spectra of both the pristine (blue open square symbols) and switched (yellow solid triangle symbols) devices were maintained from the same depth. Ta-MN (1,737 and 1,680 eV) and O-KL (468, 483, and 503 eV) are observed, which confirms the formation of a TaO x layer. The atomic percentages of Ta-MN3 and O-KL1 are 37.38% and 62.62% for the pristine device and 44.69% and 55.31% for the switched device, respectively. It is believed that the spectra difference is not a variation, and the oxygen ion migration from the TaO x switching layer. Due to a small amount of oxygen migration, the difference of the two spectra will be small. The atomic percentages were calculated by using commercial software for AES spectra. Basically, this decrease in oxygen content and increase in Ta content after switching is of the evidence that an oxygen-deficient filament is formed owing to oxygen ion migration as well as the lower energy gap of the TaO x layer, as shown by the dotted line in Figure 5b. When negative voltage is applied to the TE, oxygen ions are pushed from the TiO2 layer towards the conducting filament where they recombine with oxygen vacancies or oxidize the conducting filament. The device will be in HRS (Figure 5d). Control of oxygen-deficient filament formation and rupture is facilitated by insertion of the thin Ti layer at the TE/TaO x interface, which results in repeatable and reproducible resistive switching characteristics.
The conducting filament diameter is estimated using a new method under a constant current stress of 80 μA (Figure 7). The voltage decreases (or increases) under positive (or negative) current stress after a SET (or RESET) operation. First, it is considered as a parallel plate metal-insulator-metal (MIM) capacitor. Under external constant current stress, the Ta-O bonds break and create the defects due to oxygen ion migration, which results a reducing voltage across the capacitor. The captured cross section of the defects will lead to the diameter of the conducting filament. Assuming a single cylindrical nanofilament, the diameter (D) under SET can be estimated as [47]
where ΔV (changes in the voltage shift under SET and RESET) is found to be 0.98 V (Figure 7), q is the electronic charge (1.602 × 10−19 C), and is the dielectric permittivity of amorphous Ta2O5 film ( ≈20 to 25). Considering all values in Equation 1, the diameter of the nanofilament is approximately 2.9 to 2.6 nm. This suggests that the present resistive switching memory device can be scaled down to <3 nm. Previously reported diameters of 5 to 10 nm for Pt/TiO2/Pt [12], ≈15 nm for Ti/Fe:SrTiO3/Nb:SrTiO3[42], and ≈ 1,000 nm for Pt/CuO/Pt [48] are slightly closer and higher than our calculated values, likely owing to the use of different structures as well as materials. Further study may be needed to clearly understand these results. Figure 8a shows the resistive switching characteristics with different CCs from 10 to 100 μA. The low-resistance state decreases with increasing CCs from 10 to 100 μA (Figure 8a,b), which will be useful for multi-level data storage applications. As the filament diameter increases with higher CCs, the low-resistance state decreases, and the value of RESET current increases. The RESET current can be scaled down to 23 μA at a low CC of 10 μA, which will be useful to a low-power operation RRAM in the near future. Our novel device also has a long read pulse endurance of >105 cycles (Figure 9a) and excellent data retention of >104 s with a good resistance ratio of >102 at 85°C at a low CC of 80 μA (Figure 9b). The HRS is slightly decreased with longer elapsed time; however, it is still high, approximately 10 MΩ. Further study is needed to clarify this issue. A data retention of >103 s is also observed for a low CC of 10 μA (not shown here). This RRAM device shows good program erase endurance of >1,000 cycles with a pulse width of 500 μs (Figure 9c). Considering the obtained nanofilament diameter of approximately 3 nm, a high-density (≈100 Tbit/in.2) nanoscale nonvolatile memory can be achievable in the future.
Conclusions
Improvement in resistive switching performance, particularly 10,000 consecutive switching cycles with tight distribution in HRS/LRS of >102, long read pulse endurance of >105, and good data retention of 104 s at 85°C, have been achieved under a low CC of 80 μA by exploiting the oxygen-getter nature of a Ti nanolayer in a W/TiO x /TaO x /W structure. A small device of 150 × 150 nm2 and a defective TaO x film are confirmed by TEM. O2− ion migration because of lower barrier height for electrons leads to a switching mechanism based on filament formation/rupture. The presence of controllable oxygen-deficient TaO x nanofilament after switching has been investigated by AES. Furthermore, the device could be operated with a small RESET current of 23 μA. A small nanofilament diameter of 3 nm under a low CC of 80 μA has been calculated using a new method, which has a high memory density of ≈ 100 Tbit/in.2, expected to be very useful for future sub-10-nm applications.
References
Waser R, Dittmann R, Staikov G, Szot K: Redox-based resistive switching memories - nanoionic mechanisms, prospects, and challenges. Adv Mater 2009, 21: 2632. 10.1002/adma.200900375
Sawa A: Resistive switching in transition metal oxides. Mater Today 2008, 11: 28.
Liu Q, Sun J, Lv H, Long S, Yin K, Wan N, Li Y, Sun L, Liu M: Real-time observation on dynamic growth/dissolution of conductive filaments in oxide-electrolyte-based ReRAM. Adv Mater 1844, 2012: 24.
Sato Y, Kinoshita K, Aoki M, Sugiyama Y: Reduction in the reset current in a resistive random access memory consisting of NiO x brought about by reducing a parasitic capacitance. Appl Phys Lett 2007, 90: 033503. 10.1063/1.2431792
Lee MJ, Lee CB, Lee D, Lee SR, Chang M, Hur JH, Kim YB, Kim CJ, Seo DH, Seo S, Chung UI, Yoo IK, Kim K: A fast, high-endurance and scalable non-volatile memory device made from asymmetric Ta2O(5−x)/TaO(2−x) bilayer structures. Nat Mater 2011, 10: 625. 10.1038/nmat3070
Yoon J, Choi H, Lee D, Park JB, Lee J, Seong DJ, Ju Y, Chang M, Jung S, Hwang H: Excellent switching uniformity of Cu-doped MoO x /GdO x bilayer for nonvolatile memory applications. IEEE Electron Device Lett 2009, 30: 457.
Prakash A, Maikap S, Lai CS, Lee HY, Chen WS, Chen F, Kao MJ, Tsai MJ: Improvement uniformity of resistive switching parameters by selecting the electroformation polarity in IrO x /TaO x /WO x /W structure. Jpn J Appl Phys 2012, 51: 04DD06. 10.7567/JJAP.51.04DD06
Banerjee W, Maikap S, Lai CS, Chen YY, Tien TC, Lee HY, Chen WS, Chen FT, Kao MJ, Tsai MJ, Yang JR: Formation polarity dependent improved resistive switching memory characteristics using nanoscale (1.3 nm) core-shell IrO x nano-dots. Nanoscale Res Lett 2012, 7: 194. 10.1186/1556-276X-7-194
Yoon JH, Kim KM, Lee MH, Kim SK, Kim GH, Song SJ, Seok JY, Hwang CS: Role of Ru nano-dots embedded in TiO2 thin films for improving the resistive switching behavior. Appl Phys Lett 2010, 97: 232904. 10.1063/1.3525801
Lee HY, Chen PS, Liu WH, Wang SM, Gu PY, Hsu YY, Tsai CH, Chen WS, Chen F, Tsai MJ, Lien C: Robust high-resistance state and improved endurance of HfO x resistive memory by suppression of current overshoot. IEEE Electron Device Lett 2011, 32: 1585.
Choi BJ, Jeong DS, Kim SK, Rohde C, Choi S, Oh JH, Kim HJ, Hwang CS, Szot K, Waser R, Reichenberg B, Tiedke S: Resistive switching mechanism of TiO2 thin films grown by atomic-layer deposition. J Appl Phys 2005, 98: 033715. 10.1063/1.2001146
Kwon DH, Kim KM, Jang JH, Jeon JM, Lee MH, Kim GH, Li XS, Park GS, Lee B, Han S, Kim M, Hwang CS: Atomic structure of conducting nanofilaments in TiO2 resistive switching memory. Nat Nanotechnol 2010, 5: 148. 10.1038/nnano.2009.456
Lee SR, Char K, Kim DC, Jung R, Seo S, Li XS, Park GS, Yoo IK: Resistive memory switching in epitaxially grown NiO. Appl Phys Lett 2007, 91: 202115. 10.1063/1.2815658
Long S, Cagli C, Ielmini D, Liu M, Sune J: Reset statistics of NiO-based resistive switching memories. IEEE Electron Device Lett 2011, 32: 1570.
Long S, Cagli C, Ielmini D, Liu M, Sune J: Analysis and modeling of resistive switching statistics. J Appl Phys 2012, 111: 074508. 10.1063/1.3699369
Yu S, Guan X, Wong HSP: Conduction mechanism of TiN/HfO x /Pt resistive switching memory: a trap-assisted-tunneling model. ApplPhys Lett 2011, 99: 063507. 10.1063/1.3624472
Chen YY, Goux L, Clima S, Govoreanu B, Degraeve R, Kar GS, Fantini A, Groeseneken G, Wouters DJ, Jurczak M: Endurance/retention trade-off on HfO2/ metal cap 1T1R bipolar RRAM. IEEE Trans Electron Devices 2013, 60: 1114.
Long S, Lian X, Ye T, Cagli C, Perniola L, Miranda E, Liu M, Sune J: Cycle-to-cycle intrinsic RESET statistics in HfO2-based unipolar RRAM devices. IEEE Electron Device Lett 2013, 34: 623.
Lin CY, Wu CY, Wu CY, Lee TC, Yang FL, Hu C, Tseng TY: Effect of top electrode material on resistive switching properties of ZrO2 film memory devices. IEEE Electron Device Lett 2007, 28: 366.
Guan W, Long S, Jia R, Liu M: Nonvolatile resistive switching memory utilizing gold nanocrystals embedded in zirconium oxide. Appl Phys Lett 2007, 91: 062111. 10.1063/1.2760156
Liu Q, Guan W, Long S, Liu M, Zhang S, Wang Q, Chen J: Resistance switching of Au-implanted-ZrO2 film for nonvolatile memory application. J Appl Phys 2008, 104: 114514. 10.1063/1.3033561
Liu Q, Guan W, Long S, Jia R, Liu M, Chen J: Resistive switching memory effect of ZrO2 films with Zr+ implanted. Appl Phys Lett 2008, 92: 012117. 10.1063/1.2832660
Guan W, Long S, Liu Q, Liu M, Wang W: Nonpolar nonvolatile resistive switching in Cu doped ZrO2. IEEE Electron Device Lett 2008, 29: 434.
Wang SY, Lee DY, Tseng TY, Lin CY: Effects of Ti top electrode thickness on the resistive switching behaviors of rf-sputtered ZrO2 memory films. Appl Phys Lett 2009, 95: 112904. 10.1063/1.3231872
Wang SY, Lee DY, Huang TY, Wu JW, Tseng TY: Controllable oxygen vacancies to enhance resistive switching performance in a ZrO2-based RRAM with embedded Mo layer. Nanotechnology 2010, 21: 495201. 10.1088/0957-4484/21/49/495201
Li Y, Long S, Lv H, Liu Q, Wang Y, Zhang S, Lian W, Wang M, Zhang K, Xie H, Liu S, Liu M: Improvement of resistive switching characteristics in ZrO2 film by embedding a thin TiO x layer. Nanotechnology 2011, 22: 254028. 10.1088/0957-4484/22/25/254028
Lin CC, Chang YP, Lin HB, Lin CH: Effect of non-lattice oxygen on ZrO2-based resistive switching memory. Nanoscale Res Lett 2012, 7: 187. 10.1186/1556-276X-7-187
Zhang T, Zhang X, Ding L, Zhang W: Study on resistance switching properties of Na0.5Bi0.5TiO3 thin films using impedance spectroscopy. Nanoscale Res Lett 2009, 4: 1309. 10.1007/s11671-009-9397-4
Sun X, Li G, Chen L, Shi Z, Zhang W: Bipolar resistance switching characteristics with opposite polarity of Au/SrTiO3/Ti memory cells. Nanoscale Res Lett 2011, 6: 599. 10.1186/1556-276X-6-599
Chiu FC, Li PW, Chang WY: Reliability characteristics and conduction mechanisms in resistive switching memory devices using ZnO thin films. Nanoscale Res Lett 2012, 7: 178. 10.1186/1556-276X-7-178
Peng CN, Wang CW, Chan TC, Chang WY, Wang YC, Tsai HW, Wu WW, Chen LJ, Chueh YL: Resistive switching of Au/ZnO/Au resistive memory: an in situ observation of conductive bridge formation. Nanoscale Res Lett 2012, 7: 559. 10.1186/1556-276X-7-559
Rahaman SZ, Maikap S, Chen WS, Lee HY, Chen FT, Kao MJ, Tsai MJ: Repeatable unipolar/bipolar resistive memory characteristics and switching mechanism using a Cu nanofilament in a GeO x film. Appl Phys Lett 2012, 101: 073106. 10.1063/1.4745783
Syu YE, Chang TC, Tsai TM, Chang GW, Chang KC, Lou JH, Tai YH, Tsai MJ, Wang YL, Sze SM: Asymmetric carrier conduction mechanism by tip electric field in WSiO x resistance switching device. IEEE Electron Device Lett 2012, 33: 342.
Rahaman SZ, Maikap S, Tien TC, Lee HY, Chen WS, Chen F, Kao MJ, Tsai MJ: Excellent resistive memory characteristics and switching mechanism using a Ti nanolayer at the Cu/TaO x interface. Nanoscale Res Lett 2012, 7: 345. 10.1186/1556-276X-7-345
Prakash A, Maikap S, Lai CS, Tien TC, Chen WS, Lee HY, Chen FT, Kao MJ, Tsai MJ: Bipolar resistive switching memory using bilayer TaO x /WO x films. Solid State Electron 2012, 77: 35.
Chen C, Song C, Yang J, Zeng F, Pan F: Oxygen migration induced resistive switching effect and its thermal stability in W/TaO x /Pt structure. Appl Phys Lett 2012, 100: 253509. 10.1063/1.4730601
Terai M, Sakotsubo Y, Kotsuji S, Hada H: Resistance controllability of Ta2O5/TiO2 stack ReRAM for low-voltage and multilevel operation. IEEE Electron Device Lett 2010, 31: 204.
Ninomiya T, Wei Z, Muraoka S, Yasuhara R, Katayama K, Takagi T: Conductive filament scaling of TaO x bipolar ReRAM for improving data retention under low operation current. IEEE Trans Electron Devices 2013, 60: 1384.
Wei Z, Kanzawa Y, Arita K, Katoh Y, Kawai K, Muraoka S, Mitani S, Fujii S, Katayama K, Iijima M, Mikawa T, Ninomiya T, Miyanaga R, Kawashima Y, Tsuji K, Himeno A, Okada T, Azuma R, Shimakawa K, Sugaya H, Takagi T, Yasuhara R, Horiba K, Kumigashira H, Oshima M: Highly reliable TaO x ReRAM and direct evidence of redox reaction mechanism. Tech Dig - Int Electron Devices Meet 2008, 293: 293.
The interactive Ellingham diagram .] [http://www.doitpoms.ac.uk/tlplib/ellingham_diagrams/interactive.php [.]
Michaelson HB: The work function of the elements and its periodicity. J Appl Phys 1977, 48: 4729. 10.1063/1.323539
Stille S, Lenser C, Dittmann R, Koehl A, Krug I, Muenstermann R, Perlich J, Schneider CM, Klemradt U, Waser R: Detection of filament formation in forming-free resistive switching SrTiO3 devices with Ti top electrodes. Appl Phys Lett 2012, 100: 223503. 10.1063/1.4724108
Aarik J, Aidla A, Kiisler AA, Uustare T, Sammelselg V: Effect of crystal-structure on optical-properties of TiO2 films grown by atomic layer deposition. Thin Solid Films 1997, 305: 270. 10.1016/S0040-6090(97)00135-1
Gu D, Li J, Dey SK, Waard HD, Marcus S: Nanochemistry, nanostructure, and electrical properties of Ta2O5 film deposited by atomic layer deposition and plasma-enhanced atomic layer deposition. J Vac Sci Technol B 2006, 24: 2230. 10.1116/1.2335432
Maikap S, Wang TY, Tzeng PJ, Lin CH, Tien TC, Lee LS, Yang JR, Tsai MJ: Band offsets and charge storage characteristics of atomic layer deposited high- k HfO2/TiO2 multilayers. Appl Phys Lett 2007, 90: 262901. 10.1063/1.2751579
Yang JJ, Zhang MX, Strachan JP, Miao F, Pickett MD, Kelley RD, Medeiros-Ribeiro G, Williams RS: High switching endurance in TaO x memristive devices. Appl Phys Lett 2010, 97: 232102. 10.1063/1.3524521
Prakash A, Maikap S, Rahaman SZ, Majumdar S, Manna S, Ray SK: Resistive switching memory characteristics of Ge/GeO x nanowires and evidence of oxygen ion migration. Nanoscale Res Lett 2013, 8: 220. 10.1186/1556-276X-8-220
Yasuhara R, Fujiwara K, Horiba K, Kumigashira H, Kotsugi M, Oshima M, Takagi H: Inhomogeneous chemical states in resistance-switching devices with a planar-type Pt/CuO/Pt structure. Appl Phys Lett 2009, 95: 012110. 10.1063/1.3175720
Acknowledgments
This work was supported by the National Science Council (NSC), Taiwan, under contract numbers NSC-98-2221-E-182-052-MY3, NSC-101-2221-E-182-061, and NSC-102-2221-E-182-057-MY2. The authors are grateful to the Electronic and Optoelectronic Research Laboratories, Industrial Technology Research Institute, Hsinchu, Taiwan for their support on W bottom electrode pattern.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
AP carried out this research work under the instruction of SM. Fabrication process was also instructed by HCC and CSL. AES spectra were taken by TCT under the instruction of SM. All authors read and approved the final manuscript.
A retraction note to this article can be found online at http://dx.doi.org/10.1186/1556-276X-8-419.
An erratum to this article is available at http://dx.doi.org/10.1186/1556-276X-8-419.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Prakash, A., Maikap, S., Chiu, HC. et al. Enhanced resistive switching memory characteristics and mechanism using a Ti nanolayer at the W/TaO x interface. Nanoscale Res Lett 9, 125 (2014). https://doi.org/10.1186/1556-276X-9-125
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-125