Abstract
Steel production causes a third of all industrial CO2 emissions due to the use of carbon-based substances as reductants for iron ores, making it a key driver of global warming. Therefore, research efforts aim to replace these reductants with sustainably produced hydrogen. Hydrogen-based direct reduction (HyDR) is an attractive processing technology, given that direct reduction (DR) furnaces are routinely operated in the steel industry but with CH4 or CO as reductants. Hydrogen diffuses considerably faster through shaft-furnace pellet agglomerates than carbon-based reductants. However, the net reduction kinetics in HyDR remains extremely sluggish for high-quantity steel production, and the hydrogen consumption exceeds the stoichiometrically required amount substantially. Thus, the present study focused on the improved understanding of the influence of spatial gradients, morphology, and internal microstructures of ore pellets on reduction efficiency and metallization during HyDR. For this purpose, commercial DR pellets were investigated using synchrotron high-energy X-ray diffraction and electron microscopy in conjunction with electron backscatter diffraction and chemical probing. Revealing the interplay of different phases with internal interfaces, free surfaces, and associated nucleation and growth mechanisms provides a basis for developing tailored ore pellets that are highly suited for a fast and efficient HyDR.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
D. Raabe, C.C. Tasan and E.A. Olivetti, Strategies for improving the sustainability of structural metals, Nature, 575(2019), No. 7781, p. 64.
World Steel Association, World Steel in Figures 2021 [2022-01-24]. https://worldsteel.org/wp-content/uploads/2021-World-Steel-in-Figures.pdf
M. Flores-Granobles and M. Saeys, Minimizing CO2 emissions with renewable energy: A comparative study of emerging technologies in the steel industry, Energy Environ. Sci., 13(2020), No. 7, p. 1923.
F. Patisson and O. Mirgaux, Hydrogen ironmaking: How it works, Metals, 10(2020), No. 7, p. 922.
W. Jaimes and S. Maroufi, Sustainability in steelmaking, Curr. Opin. Green Sustainable Chem., 24(2020), p. 42.
M. Pei, M. Petäjäniemi, A. Regnell, and O. Wijk, Toward a fossil free future with HYBRIT: Development of iron and steel-making technology in Sweden and Finland, Metals, 10(2020), No. 7, p. 972.
S. Lechtenböhmer, C. Schneider, M. Yetano Roche, and S. Höller, Re-industrialisation and low-carbon economy—Can they go together? Results from stakeholder-based scenarios for energy-intensive industries in the German state of north Rhine Westphalia Energies, 8(2015), No. 10, p. 11404.
M. Fischedick, J. Marzinkowski, P. Winzer, and M. Weigel, Techno-economic evaluation of innovative steel production technologies, J. Clean. Prod., 84(2014), p. 563.
S.H. Kim, X. Zhang, Y. Ma, et al., Influence of microstructure and atomic-scale chemistry on the direct reduction of iron ore with hydrogen at 700°C, Acta Mater., 212(2021), p. 116933.
I.R. Souza Filho, Y. Ma, M. Kulse, et al., Sustainable steel through hydrogen plasma reduction of iron ore: Process, kinetics, microstructure, chemistry, Acta Mater., 213(2021), p. 116971.
D. Spreitzer and J. Schenk, Reduction of iron oxides with hydrogen—A review, Steel Res. Int., 90(2019), No. 10, p. 1900108.
Y. Ma, I.R. Souza Filho, Y. Bai, et al., Hierarchical nature of hydrogen-based direct reduction of iron oxides, Scripta Mater., 213(2022), p. 114571.
E.T. Turkdogan and J.V. Vinters, Gaseous reduction of iron oxides: Part I. Reduction of hematite in hydrogen, Metall. Mater. Trans. B, 2(1971), No. 11, p. 3175.
M.V.C. Sastri, R.P. Viswanath, and B. Viswanathan, Studies on the reduction of iron oxide with hydrogen, Int. J. Hydrogen Energy, 7(1982), No. 12, p. 951.
H.Y. Lin, Y.W. Chen, and C. Li, The mechanism of reduction of iron oxide by hydrogen, Thermochim. Acta, 400(2003), No. 1–2, p. 61.
M. Moukassi, P. Steinmetz, B. Dupre, and C. Gleitzer, A study of the mechanism of reduction with hydrogen of pure wustite single crystals, Metall. Trans. B, 14(1983), No. 1, p. 125.
M.J. Tiernan, P.A. Barnes, and G.M.B. Parkes, Reduction of iron oxide catalysts: The investigation of kinetic parameters using rate perturbation and linear heating thermoanalytical techniques, J. Phys. Chem. B, 105(2001), No. 1, p. 220.
J. Zieliński, I. Zglinicka, L. Znak, and Z. Kaszkur, Reduction of Fe2O3 with hydrogen, Appl. Catal. A Gen., 381(2010), No. 1–2, p. 191.
A. Pineau, N. Kanari, and I. Gaballah, Kinetics of reduction of iron oxides by H2: Part I: Low temperature reduction of hematite, Thermochim. Acta, 447(2006), No. 1, p. 89.
A. Pineau, N. Kanari, and I. Gaballah, Kinetics of reduction of iron oxides by H2: Part II: Low temperature reduction of hematite, Thermochim. Acta, 456(2007), No. 2, p. 75.
H.B. Zuo, C. Wang, J.J. Dong, K.X. Jiao, and R.S. Xu, Reduction kinetics of iron oxide pellets with H2 and CO mixtures, Int. J. Miner. Metall. Mater., 22(2015), No. 7, p. 688.
Q.T. Tsay, W.H. Ray, and J. Szekely, The modeling of hematite reduction with hydrogen plus carbon monoxide mixtures: Part I. The behavior of single pellets, AIChE J., 22(1976), No. 6, p. 1064.
E. Kawasaki, J. Sanscrainte, and T.J. Walsh, Kinetics of reduction of iron oxide with carbon monoxide and hydrogen, AIChE J., 8(1962), No. 1, p. 48.
K. Piotrowski, K. Mondal, H. Lorethova, L. Stonawski, T. Szymański, and T. Wiltowski, Effect of gas composition on the kinetics of iron oxide reduction in a hydrogen production process, Int. J. Hydrogen Energy, 30(2005), No. 15, p. 1543.
K. Piotrowski, K. Mondal, T. Wiltowski, P. Dydo, and G. Rizeg, Topochemical approach of kinetics of the reduction of hematite to wüstite, Chem. Eng. J., 131(2007), No. 1–3, p. 73.
H. Hamadeh, O. Mirgaux, and F. Patisson, Detailed modeling of the direct reduction of iron ore in a shaft furnace, Materials (Basel), 11(2018), No. 10, art. No. 1865.
A. Bonalde, A. Henriquez, and M. Manrique, Kinetic analysis of the iron oxide reduction using hydrogen-carbon monoxide mixtures as reducing agent, ISIJ Int., 45(2005), No. 9, p. 1255.
M. Auinger, D. Vogel, A. Vogel, M. Spiegel, and M. Rohwerder, A novel laboratory set-up for investigating surface and interface reactions during short term annealing cycles at high temperatures, Rev. Sci. Instrum., 84(2013), No. 8, p. 085108.
A.P. Hammersley, FIT2D: A multi-purpose data reduction, analysis and visualization program, J. Appl. Crystallogr., 49(2016), No. 2, p. 646.
L. Lutterotti, Total pattern fitting for the combined size-strainstress-texture determination in thin film diffraction, Nucl. Instrum. Methods Phys. Res., Sect. B, 268(2010), No. 3–4, p. 334.
A. Ranzani da Costa, D. Wagner, and F. Patisson, Modelling a new, low CO2 emissions, hydrogen steelmaking process, J. Clean. Prod., 46(2013), p. 27.
D. Wagner, O. Devisme, F. Patisson, and D. Ablitzer, A laboratory study of the reduction of iron oxides by hydrogen, [in] F. Kongoli and R.G. Reddy, eds., Proceedings of Sohn International Symposium, San Diego, 2006, p. 111.
W.C. Mao and W.G. Sloof, Reduction kinetics of wüstite scale on pure iron and steel sheets in Ar and H2 gas mixture, Metall. Mater. Trans. B, 48(2017), No. 5, p. 2707.
Y. Bai, J. R. Mianroodi, Y. Ma, A.K. da Silva, B. Svendsen, and D. Raabe, Chemo-mechanical phase-field modeling of iron oxide reduction with hydrogen, Acta Mater., 231(2022), p. 117899.
Acknowledgements
Y. Ma acknowledges the financial support from the Walter Benjamin Programme of the Deutsche Forschungsgemeinschaft (No. 468209039). I.R. Souza Filho acknowledges the financial support from Capes-Humboldt (No. 88881.512949/2020-01). H. Springer acknowledges the financial support from the Heisenberg Programme of the Deutsche Forschungsgemeinschaft (SP 1666 2/1). The authors would like to acknowledge the support provided by N. Schell and A. Stark (Helmholtz-Zentrum Hereon) for the high-energy X-ray diffraction experiments at the P07 High Energy Materials Science beamline. The Deutsches Elektronen-Synchrotron (DESY) is acknowledged for the provision of synchrotron radiation facilities in the framework of proposal I-20191042.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Conflict of Interest
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ma, Y., Souza Filho, I.R., Zhang, X. et al. Hydrogen-based direct reduction of iron oxide at 700°C: Heterogeneity at pellet and microstructure scales. Int J Miner Metall Mater 29, 1901–1907 (2022). https://doi.org/10.1007/s12613-022-2440-5
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-022-2440-5