Abstract
Perpendicular magnetic anisotropy (PMA) ferromagnetic CoFeB with dual MgO interfaces is an attractive material system for realizing magnetic memory applications that require highly efficient, high speed current-induced magnetic switching. Using this structure, a sub-nanometer CoFeB layer has the potential to simultaneously exhibit efficient, high speed switching in accordance with the conservation of spin angular momentum, and high thermal stability owing to the enhanced interfacial PMA that arises from the two CoFeB-MgO interfaces. However, the difficulty in attaining PMA in ultrathin CoFeB layers has imposed the use of thicker CoFeB layers which are incompatible with high speed requirements. In this work, we succeeded in depositing a functional CoFeB layer as thin as five monolayers between two MgO interfaces using magnetron sputtering. Remarkably, the insertion of Mg within the CoFeB gave rise to an ultrathin CoFeB layer with large anisotropy, high saturation magnetization, and good annealing stability to temperatures upwards of 400 °C. When combined with a low resistance-area product MgO tunnel barrier, ultrathin CoFeB magnetic tunnel junctions (MTJs) demonstrate switching voltages below 500 mV at speeds as fast as 1 ns in 30 nm devices, thus opening a new realm of high speed and highly efficient nonvolatile memory applications.
Similar content being viewed by others
Introduction
PMA-MTJs composed of a CoFeB free layer and MgO tunnel barrier have yielded numerous breakthroughs including scalability, endurance, and high thermal stability1,2,3,4,5,6,7,8,9. From a technological perspective, CoFeB-MgO-based spin-transfer-torque magnetic random access memory (STT-MRAM) has emerged as the most promising alternative to existing silicon-based memory technologies. However, one prominent shortcoming of conventional CoFeB-MgO structures is the requirement for lower switching voltage at faster switching speeds. To attain a low switching voltage, the conservation of spin angular momentum stipulates the need for low magnetic moment which is embodied by an ultrathin ferromagnetic free layer. PMA in ultrathin Fe has been demonstrated10, but the inability to achieve PMA in ultrathin CoFeB with dual MgO interfaces stems from the delicate balance between achieving layer continuity, preserving free layer metallicity, and retaining a low resistance-area product (RA) for the MgO layers. Here, we report the use of an Mg insertion layer within an ultrathin CoFeB layer that gives rise to PMA. The device performance of this ultrathin free layer was recently reported as it achieved breakthroughs in low magnetic moment and low damping that gave rise to ultra-low voltage and ultra-low power devices11,12. In this work, we show that the achievement of ultrathin CoFeB layers are of technological importance as they fulfill the requirements for reversal of the free layer magnetization at short pulse lengths below 10 ns, and at deep error rates of less than 1 ppm which are essential to applications such as last level cache that use static random access memory technology.
Conventional free layers use thicker CoFeB (CFB) layers that consist of refractory metal interfaces or insertions13,14,15. These free layers can exhibit good thermal stability withstanding 400 °C back end of line process temperatures and a wide range of operating temperatures, but require a high switching voltage. By contrast, the conservation of spin angular momentum argues that a lower moment free layer is important for the design of low switching voltage magnetic random access memory (MRAM) devices12,14,,16,14,. This study shows that ultrathin, thermally stable, high saturation magnetization CFB free layers can be achieved with the incorporation of Mg, enabling a low switching voltage at short pulse lengths. The effect of Mg is remarkable as PMA is observed in CFB free layers with thicknesses tFL as low as 6.6 Å, whereas in the absence of Mg, PMA is first observed for an 11 Å CFB free layer. For a 30 nm device, estimates of the upper limit of the energy barrier Eb between parallel and anti-parallel states are large, thus good thermal stability is expected up to the maximum operating temperature of 85 °C. Experimentally, nominal 30 nm devices with a 9 Å free layer exhibit sharp switching of the free layer magnetization with respect to applied field or current, and a very low RA of 3.5 Ω·μm2 with a tunnel magnetoresistance ratio (TMR) up to 150%. High speed testing revealed these devices are capable of switching at 1 ns with a writing voltage below 500 mV, and below 300 mV for pulse lengths ranging from 3 to 50 ns. These properties highlight the promise of PMA-MTJs, consisting of ultrathin CFB free layers with dual MgO interfaces, for expanding MRAM into new memory applications.
Results
We report on full MTJ film stacks that include a seed layer, synthetic antiferromagnet reference layer, MgO barrier, CFB free layer, MgO Hk-enhancing layer, and nitride-based cap. As depicted in Fig. 1, two variations of the CoFeB free layer are investigated. Each free layer is an ultrathin, 9 Å CoFeB free layer that consists of Fe-rich (CoFe)1-yBy, where the Co:Fe ratio is 1:2.7 and y is 24 percent. The first free layer variation, shown in Fig. 1a, depicts the insertion of an Mg layer with a nominal thickness of 5 Å within the CFB free layer. The second variation, illustrated in Fig. 1b, omits the Mg layer in favor a continuous CFB layer. All samples are annealed at 400 °C for 3.5 hours after the deposition of the MTJ stack was complete.
We use vibration sample magnetometry (VSM) to measure the magnetic properties of the free layer along the out-of-plane easy direction at temperatures between 25 °C and 375 °C. Figure 2a displays hysteresis loops of magnetic moment versus applied magnetic field measured at room temperature on blanket films. In the absence of Mg, a 9 Å CoFeB free layer does not exhibit PMA; whereas, the addition of 5 Å of Mg clearly exhibits free layer PMA. Furthermore, the addition of Mg results in a slightly higher Ms × tFL than a free layer without Mg consistent with better magnetic properties. Figure 2b shows that the addition of Mg to CFB results in a room temperature saturation magnetization Ms of 1350 emu/cm3 with Ms disappearing at 860 K (\({T}_{{M}_{s}}=0\)). The temperature dependence of the free layer Ms is fitted by the T1/3 power law indicated by the solid line, where \({M}_{s}(T)={M}_{0}\times {(1-\frac{T}{{T}_{{M}_{s}}=0})}^{\frac{1}{3}},\) and is consistent with previous studies of CFB free layers and other ferromagnets15,17,18.
The anisotropy field Hk measured by ferromagnetic resonance spectroscopy (FMR) as a function of the free layer CFB and Mg thickness are depicted with solid symbols in Fig. 3a,b, respectively. In Fig. 3a, free layer PMA and Hk demonstrate a strong dependence on the thickness of CFB and the presence of Mg. Figure 3a reveals a decrease in Hk with CFB thickness due to increasing free layer magnetic moment, Ms × tFL. Interestingly, the addition of Mg to the free layer demonstrates PMA for free layer thicknesses as thin as 6.6 Å and up to 12.2 Å, the lower and upper limits of this study, respectively. In contrast, Fig. 2a displayed the absence of PMA for a no-Mg 9 Å CFB free layer. Without Mg, the triangular symbols in Fig. 3a assert that PMA occurs at an increased CFB thickness of 11 Å with Hk less than 500 Oe at 35 °C. Below this critical thickness, the CFB free layer exhibits in-plane anisotropy. These observations are important as they show that the addition of Mg extends the range of PMA in CFB free layers to ultrathin thickness levels required for low switching voltages in PMA-MTJs.
Next, Fig. 3b demonstrates the sensitivity of the free layer Hk on Mg content. Over the nominal Mg thickness range of this study, 2 Å to 9 Å, a 9 Å CFB free layer demonstrates PMA for all Mg thicknesses. Hk sharply increases from a nominal Mg thickness of 2 Å reaching a maximum near 7 Å. From 7 Å to 9 Å, the Hk dependence on Mg weakened suggesting an upper limit for Mg. This upper limit, and more generally, the range of PMA enabled by the insertion of Mg can be tuned by the oxidation conditions of the adjacent MgO barrier and Hk-enhancing layer, nitridation conditions of the nitride-based cap, and Mg content of the often under-oxidized Hk-enhancing layer.
To better understand the role of the Mg insertion, Fig. 4 shows a cross-sectional transmission electron microscopy (TEM) micrograph and a corresponding energy dispersive spectroscopy (EDS) line scan of a 9 Å CFB free layer with a 5 Å Mg insertion layer. The microstructure of the free layer depicted in the TEM micrograph reveals a continuous, crystalline layer with clear rows of atoms. The ultrathin free layer is believed to benefit from templating effects of the neighboring (001) MgO barrier and Hk-enhancing layers, such that the (001) texture appears to extend from the MgO barrier into the nitride-based cap. Surprisingly, both the TEM micrograph and EDS line scan could not confirm the presence of a distinct Mg insertion layer. Therefore, TEM and EDS were extended to an as-deposited sample to understand the effects of annealing on Mg diffusion. Again, unexpectedly, the TEM micrograph and EDS line scan revealed the absence of an Mg layer. Since annealing is not the reason for the absence of the Mg layer, we attribute the absence of the Mg layer to the low binding energy of the Mg-Mg bond (Table 1) that results in the loss of Mg through re-sputtering or the intermixing of Mg during the subsequent deposition of the 4 Å CoFeB layer. We also hypothesize that the 4 Å of CFB may punch through the Mg layer effectively implanting into the lower 5 Å CoFeB layer resulting in a “floating” Mg layer that is partially incorporated into the MgO Hk-enhancing layer. Although Mg cannot be accurately quantified in TEM and EDS, a small portion of Mg is believed to remain within the structure. This is supported by the free layer properties which exhibit a strong dependence on Mg content.
Our experimental results enable us to derive the effective anisotropy constant Keff and the interfacial anisotropy constant Ki which are defined as: \({K}_{eff}=\frac{{M}_{s}{H}_{k}}{2}=\frac{{K}_{i}}{{t}_{FL}}-2\pi {M}_{s}^{2}\). At 25 °C, a 9 Å CFB free layer with Mg insertion exhibits Ms of 1350 emu/cm3 and Hk of 7.3 kOe. These properties correspond to a free layer with Keff × tFL of 0.44 erg/cm2 and Ki of 1.48 erg/cm2. The anisotropy constants of the 9 Å CFB free layer with Mg are close to values previously reported for thicker free layers designed for high thermal stability and data retention over very wide operating temperature ranges15. Given the similarities of the anisotropy constants, MTJs consisting of a 9 Å CFB free layer should exhibit good thermal stability represented by the thermal stability factor Δ. Additionally, with a high \({T}_{{M}_{s}}=0\) and high Hk at 85 °C as shown in Fig. 3, MTJs consisting of a 9 Å CFB free layer should also exhibit good data retention up to 85 °C.
Next, the results of these studies are discussed from the perspective of the requirements for PMA-MTJs for MRAM applications. We can approximate Δ, defined as \(\frac{{E}_{b}}{{k}_{B}T},\) using both magnetization reversal models for a circular 30 nm MTJ device fabricated with an ideal, damage-free fabrication process. Under the first model, switching can be described by the macrospin approximation (MS) in which the free layer magnetic moment rotates uniformly. In this case, the energy barrier is given by Eb,MS = \({K}_{eff}S{t}_{FL},\) where S is the device surface area19. For larger diameters, magnetization reversal is mediated by the nucleation and propagation of a domain wall (DW) across the device leading to the following expression for the energy barrier20: Eb,DW = 4 \(d{t}_{FL}\sqrt{A\times {K}_{eff}}\), where d is the device diameter and A is the exchange stiffness constant. The exchange stiffness constant A varies as \({M}_{s}^{2\,}\) such that \(A={A}_{0,CoFe}{(\frac{{M}_{s,FL}}{{M}_{0,CoFe}})}^{2},\) where \({A}_{0,CoFe}\) = 35.8 × 10−7 erg/cm and \({M}_{0,CoFe}\)= 1946 emu/cm3 15,21. In order to calculate Eb, we must account for the reduction of the demagnetization factor as it relates to Hk using the expressions discussed in ref. 15. This relationship finds that Hk for a 30 nm diameter device is 8.9 kOe at 25 °C, and 7.8 kOe at 85 °C. Under a macrospin model of magnetic reversal, a 30 nm device exhibits a high Δ of 93 at 25 °C that decreases to 65 at 85 °C. Under a domain wall model of magnetic reversal, a 30 nm device also exhibits a high Δ of 85 at 25 °C that decreases to 61 at 85 °C. The estimated values of Δ indicate for a 30 nm device, magnetization reversal for a 9 Å CFB free layer occurs by domain wall nucleation and propagation. The crossover for switching mechanisms occurs at a device diameter of 27 nm as shown in Fig. 5. In any case, both reversal models show that ultrathin CFB free layer MTJs are capable of high thermal stability for 30 nm devices between 25 °C and 85 °C. However, as Δ assumes a perfect patterning process in which the cylindrical MTJ pillars incur no damage, the estimated values represent the upper limit for Δ. A previously reported study finds ΔMS = 59 at 25 °C and the difference between the estimated Δ and experimental Δ is attributed to MTJ pillar damage incurred during fabrication12.
Next, we examine the switching characteristics of nominal 30 nm diameter ultrathin CFB free layer MTJ devices. Figure 6a depicts a resistance versus magnetic field (R-H) loop measured with an applied DC bias of 20 mV. The R-H loop exhibits sharp switching of the free layer between high and low resistance states corresponding to anti-parallel and parallel states, respectively. Figure 6b displays the corresponding resistance versus DC voltage (R-V) loops. R-V measurements consist of sweeping DC voltage between −400 to 400 mV. Again, clear switching of the free layer between anti-parallel and parallel states is observed. The change in resistance is consistent between R-H and R-V loops, and corresponds to a TMR of 150% with a low RA of 3.5 Ω·μm2. Note this is not the highest reported TMR for the ultrathin CFB free layer as we have recently reported TMR greater than 180% for a similar structure with a slightly higher RA12.
Finally, we discuss the high speed switching characteristics of nominal 30 nm devices summarized in Table 2. Bit error rate tests were first performed with a 10 ns pulse length at an error rate below 10−6 or 1 ppm. In Fig. 6c, nominal 30 nm, ultrathin CFB free layer devices demonstrate writing at short pulse lengths with a low switching error rate below 1 ppm. At 1 ppm, the devices exhibit a low writing voltage below 300 mV. The low switching voltage is correlated with the thickness of the CFB free layer as shown in Fig. 6d. While the median 50% switching voltage V0 shows little dependence on the CFB thickness, V1 clearly shows an increase in writing voltage with free layer thickness which is consistent with the conservation of spin angular momentum12,16. As an extension of these findings, we look more closely at the ability of these devices to switch at pulse lengths below 10 ns. Figure 6e displays the median 50% switching voltage of nominal 30 nm diameter devices with Rp of 4.7 kΩ as a function of pulse length ranging from 1 ns to 50 ns. We observe switching voltages less than 300 mV for pulse lengths of 3 ns or longer. We also observe switching of the free layer at the fastest switching speed of 1 ns with a writing voltage below 500 mV. These low switching voltages correspond to a low switching energy of 0.056 pJ at 10 ns and 0.044 pJ at 1 ns. These findings highlight the importance of a thin, low moment free layer for the design of efficient, low switching voltage MRAM devices, with the inclusion of Mg serving a critical role for enabling thermally stable, ultrathin PMA CFB free layers.
In conclusion, our studies demonstrate the remarkable role of Mg that enables PMA at ultrathin thicknesses of CoFeB free layers. Without an Mg insertion layer, PMA is first observed for an 11 Å CFB free layer, but with an Mg insertion layer, PMA is observed in CFB free layers as thin as 6.6 Å, the lower limit of this study. A free layer composed of 9 Å CFB with a nominal 5 Å Mg insertion layer, followed by a 3.5 hour annealing at 400 °C, exhibits a high Ms of 1350 emu/cm3 and Hk of 7.3 kOe with anisotropy constants identical to conventional, thicker free layers. For 30 nm devices, we observe good thermal stability as the calculated upper limit of Δ is large, approximated at 93 at 25 °C using a macrospin model, and 85 at 25 °C using a domain wall model. At device level, a nominal 30 nm device with a 9 Å free layer exhibits sharp switching of the free layer with a low RA of 3.5 Ω·μm2 and TMR of 150%. High speed testing reveal these devices are capable of switching at 1 ns with a writing voltage below 500 mV; and below 300 mV for pulse lengths ranging from 3 to 50 ns. Consistent with the conservation of spin angular momentum, an ultrathin free layer is important for the design of efficient, low switching voltage MRAM devices, and thermally stable, ultrathin free layers can be achieved with the incorporation of Mg.
Methods
All MTJ film stacks presented in this work were prepared using magnetron sputtering in an Anelva C-7100 deposition system. After deposition, the blanket film wafers were annealed at 400 °C for 3.5 hours. PMA-MTJ films were also patterned into circular devices with diameters of 30 nm using UV photolithography and etched by a combination of reactive ion etching and argon ion beam etching. Patterned device wafers were annealed at 400 °C for 3.5 hours only after the completion of the fabrication process. Device diameters are electrical diameters calculated from resistance measurements. VSM was used to measure the out-of-plane magnetic moment for temperatures between 25 °C and 375 °C. Ms is defined as the magnetic moment normalized by the nominally-deposited ferromagnetic free layer thickness. FMR was used to measure Hk, with error less than 5%, for temperatures between 30 °C and 85 °C. Structural characterization was performed using cross-sectional TEM with elemental compositional analysis performed using EDS. TMR is defined as \(\frac{{R}_{AP}-{R}_{P}}{{R}_{P}}.\) The bit error rate is calculated from data collected from up to 1,200,000 test cycles, and defined as the number of write errors divided by the number of write errors and successes for a single device.
Data availability
The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.
References
Ikeda, S. et al. A perpendicular-anisotropy CoFeB–MgO magnetic tunnel junction. Nat. Mater. 9, 721–724 (2010).
Gajek, M. et al. Spin torque switching of 20 nm magnetic tunnel junctions with perpendicular anisotropy. Appl. Phys. Lett. 100, 132408 (2012).
Jan, G. et al. High Spin torque efficiency of magnetic tunnel junctions with MgO/CoFeB/MgO free layer. Appl. Phys. Express 5, 093008 (2012).
Kang, S. H. Embedded STT-MRAM for energy-efficient and cost-effective mobile systems. Tech. Dig. Pap. Symp. VLSI Technol. 2014, 5.2 (2014).
Slaughter, J. M. et al. High density ST-MRAM technology. Tech. Dig. – Int. Electron Devices Meet. 2012(29), 3 (2012).
Jan, G. et al. Achieving Sub-ns switching of STT-MRAM for future embedded LLC applications through improvement of nucleation and propagation switching mechanisms. Tech. Dig. Pap. Symp. VLSI Technol. 2016(2), 4 (2016).
Jan, G. et al. Demonstration of fully functional 8Mb perpendicular STT-MRAM chips with sub-5ns writing for non-volatile embedded memories. Tech. Dig. Pap. Symp. VLSI Technol. 2014, 42 (2014).
Lu, Y. et al. Fully Functional perpendicular STT-MRAM macro embedded in 40 nm logic for energy-efficient IOT applications. Tech. Dig. – Int. Electron Devices Meet. 2015, 26.1 (2015).
Shih, M.-C. et al. Reliability study of perpendicular STT-MRAM as emerging embedded memory qualified for reflow soldering at 260 °C. Tech. Dig. Pap. Symp. VLSI Technol. 2016, 14.1 (2016).
Koo, J. W. et al. Large perpendicular magnetic anisotropy at Fe/MgO interface. Appl. Phys. Lett. 103, 192401 (2013).
Jan, G. et al. Demonstration of Ultra-Low Voltage and Ultra Low Power STT-MRAM designed for compatibility with 0x node embedded LLC applications. Tech. Dig. Pap. Symp. VLSI Technol. 2018, 65 (2018).
Thomas, L. et al. STT-MRAM devices with low damping and moment optimized for LLC applications at 0x nodes. Tech. Dig. Int. Electron Devices Meet. 2018, 27.3 (2018).
Liu, T., Zhang, Y. & Pan, H. Y. Thermally robust Mo/CoFeB/MgO/trilayers with strong perpendicular magnetic anisotropy. Sci. Rep. 4, 5895 (2014).
Kim, J.-H. et al. Ultrathin W space layer-enabled thermal stability enhancement in a perpendicular MgO/CoFeB/W/CoFeB/MgO recording frame. Sci. Rep. 5, 16903 (2015).
Iwata-Harms, J. M. et al. High-temperature thermal stability driven by magnetization dilution in CoFeB free layers for spin-transfer-torque magnetic random access memory. Sci. Rep. 8, 14409 (2018).
Slonczewski, J. C. Current-driven excitation of magnetic multilayers. J. Magn. Magn. Mater. 159, L1 (1996).
Callen, E. & Callen, H. Ferromagnetic transitions and the one-third-power law. J. Appl. Phys. 36, 1140 (1965).
Kuz’min, M. D. Shape of temperature dependence of spontaneous magnetization of ferromagnets: quantitative analysis. Phys. Rev. Lett. 94, 107204 (2005).
Stoner, E. C. & Wohlfarth, E. P. A mechanism of magnetic hysteresis in heterogeneous alloys. Phil. Trans. R. Soc. Lond. A 240, 599–642 (1948).
Thomas, L. et al. Solving the paradox of the inconsistent size dependence of thermal stability at device and chip-level in perpendicular STT-MRAM. Tech. Dig. Int. Electron Devices Meet. 2015, 26.4 (2015).
Herring, C. & Kittel, C. On the theory of spin waves in ferromagnetic media. Phys. Rev. 81, 869 (1951).
Luo, Y.-R. Bond disassociation energies in Comprehensive Handbook of Chemical Bond Energies (ed. Lide, D. R.) 574, 803, 855 (CRC Press, 2007).
Author information
Authors and Affiliations
Contributions
P.-K.W. supervised the study. J.M.I.-H. and G.J. designed the study. J.M.I.-H. and G.J. wrote the manuscript. J.M.I.-H., S.S.G., L.T., H.L., J.Z. and Y.-J.L. performed measurements, data analysis, and data interpretation. R.T., S.P. and V.S. performed the thin film deposition for all samples used in this study. D.S. and Y.Y. developed the etching processes for all device samples used in this study. R.H., J.H., Z.T., V.L. and P.L. developed and oversaw the integration of MTJ thin films into devices. Y.-J.W., T.Z. and H.F. supervised the processing of all blanket film and patterned device wafers used in this study. S.L. provided support for the testing and characterization equipment. D.S. provided assistance with TEM studies. All authors discussed the results and reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Iwata-Harms, J.M., Jan, G., Serrano-Guisan, S. et al. Ultrathin perpendicular magnetic anisotropy CoFeB free layers for highly efficient, high speed writing in spin-transfer-torque magnetic random access memory. Sci Rep 9, 19407 (2019). https://doi.org/10.1038/s41598-019-54466-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-54466-7
- Springer Nature Limited
This article is cited by
-
Single-nanometer CoFeB/MgO magnetic tunnel junctions with high-retention and high-speed capabilities
npj Spintronics (2024)
-
Influence of CoFeB layer thickness on elastic parameters in CoFeB/MgO heterostructures
Scientific Reports (2023)
-
Influence of Cu Insertion Layer on Magnetic Properties of Co-Tb/Cu/Co-Tb Thin Films
Journal of Superconductivity and Novel Magnetism (2020)