Abstract
Wood in service is sequestering carbon, but it is principally prone to deterioration where different fungi metabolize wood, and carbon dioxide is released back to the atmosphere. A key prerequisite for fungal degradation of wood is the presence of moisture. Conversely, keeping wood dry is the most effective way to protect wood from wood degradation and for long-term binding of carbon. Wood is porous and hygroscopic; it can take up water in liquid and gaseous form, and water is released from wood through evaporation following a given water vapour pressure gradient. During the last decades, the perception of wood-water relationships changed significantly and so did the view on moisture-affected properties of wood. Among the latter is its susceptibility to fungal decay. This paper reviews findings related to wood-water relationships and their role for fungal wood decomposition. These are complex interrelationships not yet fully understood, and current knowledge gaps are therefore identified. Studies with chemically and thermally modified wood are included as examples of fungal wood substrates with altered moisture properties. Quantification and localization of capillary and cell wall water – especially in the over-hygroscopic range – is considered crucial for determining minimum moisture thresholds (MMThr) of wood-decay fungi. The limitations of the various methods and experimental set-ups to investigate wood-water relationships and their role for fungal decay are manifold. Hence, combining techniques from wood science, mycology, biotechnology and advanced analytics is expected to provide new insights and eventually a breakthrough in understanding the intricate balance between fungal decay and wood-water relations.
Key points
• Susceptibility to wood-decay fungi is closely linked to their physiological needs.
• Content, state and distribution of moisture in wood are keys for fungal activity.
• Quantification and localization of capillary and cell wall water in wood is needed.
• New methodological approaches are expected to provide new insights
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Wood is the largest pool of above-ground terrestrial carbon, and fungi dominate the recycling of this sequestered carbon (Zhang et al. 2019a, b). Wood-decaying fungi have traditionally been assigned to three major groups referring to the macroscopic and microscopic degradation pattern they form in wood, i.e. brown-rot, white-rot and soft-rot decay. However, based on genome comparison, Riley et al. (2014) found ‘a continuum rather than a dichotomy between the white-rot and brown-rot modes of wood decay’, where brown-rot fungi are a polyphyletic group evolved from at least seven white-rot lineages (Floudas et al. 2012; Hibbett and Donoghue 2001; Zhang et al. 2019c). But the terms brown-, white- and soft-rot are still widely used because they are providing information about general decay mechanisms.
Since brown-rot fungi have a lower repertoire of known enzymes than white-rot fungi (Riley et al. 2014), brown-rot fungi have historically been less studied than white-rot fungi. The details about brown-rot mechanisms are still under discussion, but it is generally agreed that brown-rot fungi use a two-step oxidative-enzymatic mechanism (Wei et al. 2010; Korripally et al. 2013; Arantes and Goodell 2014; Zhang et al. 2016), and efforts are now done to reveal more about the mechanisms (e.g. Goodell et al. 2017; Presley and Schilling 2017; Zhang and Schilling 2017; Castaño et al. 2018; Presley et al. 2018; Wu et al. 2018; 2019; Zhang et al. 2019a, b, c). Brown-rot fungi prefer conifers and degrade hemicellulose and cellulose while leaving a modified (brown) lignin-rich residue behind (Cowling 1961; Filley et al. 2002; Pandey and Pitman 2003; Arantes and Goodell 2014). Even if brown-rot fungi lack > 60% of the genes known to be involved in white rot, they degrade wood at a higher rate than white-rot fungi in monocultures in laboratory (Castaño et al. 2018). In general, brown-rot fungi have greater effects on the elastomechanical properties of wood than white-rot fungi (Winandy and Morell 1993).
Complete lignin degradation is mainly known for white-rot fungi, but there are also instances of brown-rot fungi degrading significant portions of lignin such as Gloeophyllum trabeum (Kaffenberger and Schilling 2013). Since lignin is a recalcitrant material, white-rot decay and the enzymes involved have been explored in more detail, lately with focus on biorefinery utilization. White-rot fungi prefer deciduous trees and use powerful oxidative and hydrolytic enzymes that gradually degrade cellulose while lignin is completely mineralized, leaving lighter coloured (white) cellulose behind (Riley et al. 2014). The major lignin-degrading enzyme systems of white-rot fungi include lignin peroxidase, manganese peroxidase, versatile peroxidase and laccase (Manavalan et al. 2015).
While brown and white rot is caused by basidiomycetes, soft-rot is caused by ascomycetes and fungi imperfecti. Soft-rot fungi primarily degrade hemicelluloses and cellulose; lignin degradation is less extensive than by white-rot fungi. The decomposition process can lead to formation of cavities inside the cell wall and sometimes a discoloration and cracking pattern like that of brown-rot fungi (Manavalan et al. 2015). At advanced stages of decay, the lignin-rich middle lamella is left behind as a skeleton of the wood structure with low strength properties (Daniel and Nilsson 1997; Kim and Singh 2000). Soft rot tends to occur in environments where basidiomycetes are restricted by factors such as low aeration, high moisture levels or high temperatures (Goodell et al. 2008; Manavalan et al. 2015).
Wood will also get attacked by blue stain and mould, but they are regarded mainly as an aesthetical issue since they primarily use the easily available nutrients (sugars) in the wood and do not degrade the structural biopolymers. Moulds only cause superficial discoloration while the dark-coloured hyphae of blue-stain fungi give dark discolouration of the sapwood. Blue-stain fungi degrade the pit membranes, and this causes increased water permeability. Beyond that, moulds can become an indoor problem with respect to allergic reactions of inhabitants against their spores (Crook and Burton 2010).
The degradation of the different wood constituents such as hemicelluloses, cellulose, and lignin are partly enzymatic, partly oxidative and still not entirely understood, but differ between decay types and partly also between fungal species. However, moisture has been recognized as a key parameter and governing factor for fungal growth and decomposition of wood. It has long been agreed that liquid water (i.e. capillary water) is a prerequisite to allow extracellular transport of fungal metabolites and subsequent breakdown of cell wall components.
Wood is porous and hygroscopic; it can take up water in liquid and gaseous form, and water is released from wood through evaporation following a given water vapour pressure gradient. Wood moisture content (MC) is not the mass fraction of water, but rather the ratio of water mass (total mass of water in the wood) to wood mass (the dry mass of the wood alone). Therefore, MC of over 100% is possible if the mass of the water is greater than the mass of the wood itself. MC and wood-water interactions affect several wood properties important for applied purposes like strength and stiffness properties (Tiemann 1906), dimensional stability (Stamm 1959), biological degradation (Schmidt 2006) and fastener corrosion (Zelinka and Rammer 2009; Jakes et al. 2013).
Different models exist to describe absorption and desorption processes as well as different moisture states when wood is in equilibrium with the ambient air. In contrast, wood in outdoor applications undergoes frequent changes of wetting and drying, and sorption of water in the vapour phase can be easily overruled by liquid water uptake due to precipitation or condensation. During the last three decades, the perception of wood-moisture-relationships changed significantly and so did the view on moisture-induced properties. Among the latter is the susceptibility of wood to fungal decay. Many new insights on the mode of fungal action and the effect of moisture during wood decay were derived from studies with chemically and thermally modified wood. This paper reviews the state of the art of wood-water relationships and their role for decomposition by wood-destroying fungi. These are complex interrelationships not yet fully understood, and current knowledge gaps are therefore identified.
Physiological needs of wood-decay fungi
Historic insight
The process of wood infestation by decay fungi can be divided into different phases. The authors suggest the following: (1) spore arrival, (2) spore germination, (3) mycelial growth, (4) wood metabolism, (5) autolysis of fungal hyphae and (6) formation of fruiting bodies and sporulation. It is assumed that the requirements regarding moisture and other physico-chemical parameters (e.g. pH, temperature, nutrients) differ between the six phases. But the six phases of fungal infestation will overlap in the wood substrate because of spatial colonization, and the required physico-chemical factors can also overlap between phases of wood decomposition. Most relevant for wood in service – especially in above-ground situations – and therefore in the focus of wood pathologists are the phases of spore germination, mycelial growth and metabolization of wooden cell walls. Wood exposed in soil contact is often in direct contact with fully developed fungal mycelium, and the phases of spore arrival and spore germination is only relevant for the transition zone between soil and air.
In the following, a chronological synopsis is given on methods, thresholds and experimental limitations regarding the moisture requirements for fungal growth and decay in wood based on a literature review by Brischke et al. (2018a). Several authors starting in the 1850s performed experiments where wood specimens were subjected to different climatic conditions, and spore germination or mycelial growth were monitored (Zeller 1920). Moisture requirements were often in the focus (e.g. Münch 1909; Wehmer 1914). Since then, thresholds for fungal growth and decay of wood were sought in numerous research works, where the experimental set-ups differed in external moisture supply and the way of infecting the wood specimens, and consequently, various minimum moisture thresholds (MMThr) were determined for different combinations of wood and fungal species.
Among the first, Zeller (1920) reported on the relationship between relative humidity (RH) and spore germination of wood-destroying fungi and found that the percentage of germinating spores of the brown-rot Lenzites saepiaria (syn. Gloeophyllum sepiarium) escalated above 90% RH, i.e. below the fibre saturation point (FSP), which he considered to be at 95% RH. It is important to keep in mind in the following that the terminology regarding the FSP is not consistent in literature and refers to different moisture states. For more discussion see the ‘Cell wall saturation’ section below. Butin (1962) reported about germination experiments with spores of the ascomycete Cryptodiaporthe populea at varying vapour pressure, and the results aligned with the basidiomycete findings by Zeller (1920). Ascospores on malt agar germinated at 20 °C between 100 and 89% RH and conidia between 100 and 95.5% RH. However, the application of spores on wooden substrates at a given moisture content (MC) is challenging. Usually, for this purpose, spores are dispersed in water, and an aqueous spore suspension is sprayed or otherwise applied on the wood surface, which inevitably leads to a superficial increment in moisture. The latter can be reversed by rapid re-drying. However, it is also challenging to produce viable spores in sterile laboratory conditions. Alternatively, spores can be allowed to drop from fruiting bodies directly on wood samples as reported by Zeller (1920), but the method bears a high risk of contamination by non-target organisms such as mould fungi and bacteria.
It has been frequently shown that fungal spores were able to germinate at RH below 95% (Gottlieb 1950) corresponding to wood MC below fibre saturation. One might hypothesize that this also allows for the colonization of the wood substrate with fungal mycelium, but to the authors knowledge, evidence from experimental studies is still lacking. Other factors such as pH, oxygen content, volatile organic compounds and temperature are likely affecting both the germination of spores (Zeller 1920; Gottlieb 1950; Merrill 1970; Viitanen 1994) and the formation of mycelium, but their effects are not necessarily the same. Wood protection systems will obviously also alter the wood substrate by adding chemicals that are toxic for the fungi and/or by changing the wood-water properties.
Minimum moisture thresholds (MMThr)
An extensive chronology of experimental studies to determine the moisture requirements for mycelial growth and wood decomposition by different wood-destroying basidiomycetes has been provided by Brischke et al. (2018a). A brief and updated summary is provided below. An overview of corresponding MMThr values is given in Table 1.
Several experiments to determine MMThr for fungal growth and decay were performed using saturated salt solutions to establish well-defined climates and monocultures of wood-destroying fungi. Bavendamm and Reichelt (1938) conducted fungal growth tests on malt agar with wood saw dust and small wood blocks at different RH between 81.5 and 99% in small jars. Sodium chloride solutions of different concentration were used to obtain defined climates. Wood specimens were infested using pre-inoculated saw dust. After 4 months of exposure, more than 2% mass loss (ML) was detected on blocks stored at only 85.6% RH, but the MC after incubation was not determined. Theden (1941) determined the MMThr for new infection through mycelium, progress of decay in already incubated samples and reactivation of decay in infected, dried, and remoistened samples. The MMThr for onset of fungal decay was achieved at 98.2% RH for different test fungi. The higher the ML by fungal decay, the higher was the MC after incubation, which Theden (1941) explained by the production of water during the biochemical degradation of wood. In summary, Theden (1941) did not determine a MMThr below fibre saturation, even though decay started at RH below 100%. Similar discrepancies between target MC and actual MC after incubation were reported by Ammer (1963), who used pre-inoculated specimens and stored them in screw-top jars above different saturated salt solutions. Ammer (1963) examined Norway spruce (Picea abies) sapwood and determined at 85% RH an MMThr of 19% for fungal decay, which was approximately 7% points below its FSP. In a similar set-up, Saito et al. (2012) exposed specimens made from Japanese red pine (Pinus densiflora) in small vessels with even smaller containers filled with different saturated salt solutions. In contrast to the above-cited studies, no decay was observed at MC below fibre saturation.
In a different approach, a wide range of wood MC was generated by piling wood specimens in Erlenmeyer flasks where the bottom of the piles was exposed to malt agar inoculated with fungal mycelium serving as nutrition and water source at the same time (Schmidt et al. 1996; Huckfeldt et al. 2005; Huckfeldt and Schmidt 2006; Stienen et al. 2014; Meyer and Brischke 2015; Meyer et al. 2015b). The test fungus stopped growing upwards where moisture was insufficient, and ML decreased with the pile height. Within all the above-mentioned studies using the piling method, the MMThr were below FSP (Table 1), partly remarkably far below FSP. For instance, Meyer et al. (2015b) found a lower moisture limit for decay (ML = 2.2%) of beech wood by the white-rot Trametes versicolor of only 15.4% MC. However, the malt agar at the bottom of the pile served as an external moisture and nutrition source. The fungus is able to transport water and likely nutrition from the agar pile upwards through mycelium and strains, which can barely reflect the real-life situation for decay fungi on wood exposed above ground. In contrast, a permanent source of water and nutrients is available when wood is exposed in soil. Hence, Höpken (2015) modified the pile test method to examine the ability of decay fungi to transport water. Capillary water transport in the pile was interrupted by stainless steel washers between the wood specimens, and tests were conducted with and without malt agar. Höpken (2015) clearly showed that different fungi could actively transport water within the piles.
Brischke et al. (2017) determined MMThr in different experiments without an external moisture source. These tests referred to the experimental set-up suggested by Ammer (1963) using different saturated salt solutions and to the pile tests conducted by Meyer and Brischke (2015), but omitting malt agar as nutrition and moisture source. The MMThr for T. versicolor that caused significant ML on beech was achieved at 96% RH, i.e. at 25.3% MC, when specimens were conditioned above saturated salt solutions and deionized water, respectively, before inoculation with basidiomycete mycelium. Piled Norway spruce specimens showed significant ML already at 16.3% MC caused by T. versicolor without external supply of liquid water.
Vanpachtenbeke (2019) abstained from the use of any pre-infection with decay fungi and exposed wood specimens at given climates for several months. In so-called fungal control units (FCU), wood samples were exposed to high humidity (25 °C, 97% RH). In a second set-up, two modules (25 °C, 97% RH and 5 °C/80% RH) were separated by mineral wool and a wind barrier. The vapour pressure gradient between the modules allowed for interstitial condensation and thus moistening of the wood specimens. However, in both FCU, no fungal decay occurred during 3, 9, and 12 months of exposure, respectively.
Vanpachtenbeke (2019) also studied fungal decay in wood specimens with different initial MC at different RH compared to specimens incubated at 100% RH. The effect of RH on ML became evident, but it was also shown that within a few days even at low RH (e.g. 43%) the MC increased rapidly above FSP which can be attributed to active moisture transport from the malt agar by the brown-rot fungus C. puteana.
To determine the moisture requirements of wood and decay fungi is challenging. Besides the various limitations with fungal experiments and the difficulties to determine wood MC accurately, it appeared that the most challenging task is the interpretation of the test results. Rather often, the origin and the exact location of water in wood stay unclear. The latter is closely related to the relationship between air humidity and the equilibrium moisture content (EMC) of wood. However, different physico-chemical processes are involved in wetting and drying of wood. Hence, the moisture requirements of decay fungi cannot be reduced to static wood MC values but need to be seen in the context of dynamic processes including adsorption, diffusion, capillary condensation, desorption, and active moisture transport by the fungus itself. Usually, only an average wood MC (global MC) is measured, and MC gradients between different locations in wood (local MC) are barely accounted for (Meyer et al. 2015a). Finally, fungal degradation of wood itself supplies moisture.
Research often focussed on the question whether fungal decay can be initiated below fibre saturation or in other words whether capillary water in the cell lumens or other larger voids in the cell wall is needed for fungal decay. However, the definition of fibre saturation is somewhat diffuse and changed a lot during recent years and so did the understanding of wood-water relationships.
Wood-water relationships
The interrelationship between wood and water has been subject to research for more than a century, and scientific literature on the topic was reviewed at irregular intervals (e. g. Venkateswaran 1970; Skaar 1988; Hartley et al. 1992; Engelund et al. 2013; Thybring et al. 2019). Established models and theories were critically and controversially discussed (Fredriksson and Thybring 2018, 2019; Zelinka et al. 2018) coming along with new methods and techniques for analysing sorption processes and localizing water inside wood tissues and within the cell wall.
Plaza (2019) reviewed recent experimental assessment of the molecular-scale interactions between wood and water, including infrared spectroscopy methods, neutron scattering and nuclear magnetic relaxometry experiments. Much of the experiments have used extracted or derived polymers. Since at molecular level, polymers might not be comparable to the in situ wood polymers in native wood, Plaza (2019) states that ‘More experimental studies that probe the unmodified wood as a whole are still needed’.
Cell wall saturation (CWS)
Green wood contains water-saturated cell walls and lumens which can be filled to different extents with liquid water, water vapour or both. During drying, cell lumens release liquid water, and cell walls arrive in the transition between a saturated and an unsaturated state, i.e. the so-called ‘fibre saturation point (FSP)’ or ‘fibre saturation state’. The term as such is somewhat misleading since fibres are not saturated with water, but the cell wall is. ‘Cell wall saturation (CWS)’ would therefore better describe the phenomena attributed with this particular state. Such a state can be reached only theoretically. More likely, adsorption and desorption are temporarily and spatially ongoing processes which never attain to an equilibrium. However, among the first, Tiemann (1906) defined the FSP as the moisture content (MC) when lumens are empty of liquid water, cell walls begin to dry and strength begins to decrease. As previously stated by Engelund et al. (2013), this definition is problematic, since the three criteria are not fulfilled at the same MC (e.g. Stamm 1971), and fibre saturation is not a steady state (e.g. Hernández and Bizoň 2007).
The FSP can also be defined through the climatic conditions needed to achieve complete saturation of the cell walls, which should happen in equilibrium with air at 100% RH. Experimentally, this is hardly ever reached since minimal deviations in temperature can lead either to condensation or a drop in RH (Fredriksson 2019). Therefore, Popper and Niemz (2009) used the Hailwood-Horrobin model (Hailwood and Horrobin 1946) for computing FSP values of more than 30 different wood species to avoid conditioning of wood samples at 100% RH. Hoffmeyer et al. (2011) suggested an EMC at a matric water potential of − 0.1 MPa corresponding to 99.93% RH.
Wood is occasionally stored above deionized water at 20 °C to achieve full saturation of the cell walls corresponding to what is often named FSP (e.g. Meyer and Brischke 2015; Meyer et al. 2015b; Brischke et al. 2017, 2018a). As reported by Hunter (1995) and Fredriksson (2019), this might be incorrect since very small changes in temperature would either lower the RH or induce condensation, where the latter likely occurs not inside conditioned wood samples, but at the outer boundary of the conditioning room. Nevertheless, the EMC of seven different European-grown wood species was between 23 and 39% when stored above deionized water until constant weight in a study reported by Meyer and Brischke (2015). This coincides with early findings by Zeller (1920) who reported about 21 and 36% EMC above deionized water at 25 °C. Such findings support the theory of Fredriksson and Thybring (2019) that cell wall saturation (syn. fibre saturation) occurs at RH levels as high as those where capillary water is present in adjacent cell lumens. In other words, it is suggested that conditioning wood above deionized water does not lead to full cell wall saturation, while at the same time, capillary water is already present, and therefore the wood MC can be in a range between approximately 20 and 40%.
Based on Engelund et al. (2013) will a FSP definition based on changes in strength properties (FSP around 30%) or a definition based on ‘the amount of water contained within the saturated cell wall’ (FSP around 40%) result in a difference of about 10%. The question is why the last 10% MC do not affect the physical properties of the cell wall as much as the first 30% MC. The explanation provided was that below 30% MC new water molecules break different H-bonds in the wood cell polymer, while from about 30% to 40%, new water molecules are incorporated without breaking any cell wall polymer H-bonds. Regardless of how FSP is defined, the FSP can also vary based on the method used. More details about experimental techniques for characterizing water in wood covering the range from dry to fully water-saturated is found in the review by Thybring et al. (2017).
Fredriksson (2019) claimed that other techniques than those commonly used in the hygroscopic range are needed to achieve RH higher than 95–97% and suggested, for instance, the pressure plate technique, the pressure membrane technique, centrifuge techniques or hanging water columns. The MC of wood in the over-hygroscopic range (i.e. above 95% RH) was well correlated with the water potential and was up to 200% as reported by Cloutier and Fortin (1991), Tremblay et al. (1996) and Almeida and Hernández (2007). Also, Hunter (1995) reported about wood MC well above 100% between fibre saturation at 99.9% and 100% RH.
Fredriksson and Thybring (2019) used a novel combination of experimental techniques (i.e. pressure plate and differential scanning calorimetry) to separate total sorption hysteresis into hysteresis in cell wall water and capillary water, respectively, in the whole moisture range. They found that ‘sorption hysteresis in wood cell walls exists in the whole moisture range. The cell walls were not saturated with water until the whole wood specimen was saturated which contradicts the long-held dogma that cell walls are saturated before significant amounts of capillary water are present in wood’. Consequently, CWS might be considered as a quasi-stationary state, since drying and moistening of wood are processes going on in parallel. Wood conditioned at such high RH provides plenty of condensation nucleoli, which explains that condensation can happen significantly below CWS. Seemingly, the water vapour pressure gradients are barely high enough to stimulate condensation to an extent that corresponds with a wood MC of 100% and higher as suggested by Fredriksson (2019) who referred to estimates based on the pore structure of Norway spruce (Fredriksson and Johannsson 2016).
The definitions in literature of maximum amount of water in the wood cell wall are manifold and partly contradictory. The authors consider CWS as a state of wood when cell walls are completely saturated with water, i.e. cell wall water, and the cell walls are swollen at their maximum. When this happens, pores already start to get filled with capillary water. Consequently, the maximum amount of cell wall water in wood is not reached in the absence of capillary water. The latter is important for interpreting data from experiments regarding the physiological needs of decay fungi.
Sorption isotherms
Sorption experiments have been frequently conducted in conditioning chambers with a constant climate defined by temperature (T) and RH of the air. In conventional conditioning chambers both, T and RH are subject to oscillation which is a limitation of the method (Thybring et al. 2019). More stable conditions can be achieved when exposing wood samples above different saturated salt solutions (e.g. Ammer 1963; Peralta 2007; Saito et al. 2012; Brischke et al. 2017), salt solutions of different concentration (Bavendamm and Reichelt 1938; Theden 1941) or sulphuric acid at different concentrations (Zeller 1920) at a constant temperature. Alternatively, vacuum balances of various kinds were used for determining sorption isotherms, and today, automated continuous-flow sorption balances are frequently used for measuring sorption isotherms and for studying sorption kinetics (Thybring et al. 2019). The latter technique is also known as ‘dynamic vapour sorption (DVS)’, but limited to very small samples with a mass in the milligramme range.
Fredriksson and co-workers highlighted the importance of the so-called super-hygroscopic or over-hygroscopic range (Fredriksson and Johansson 2016; Fredriksson and Thybring 2018; Fredriksson 2019) where wood takes up a substantial amount of water in a narrow RH range due to uptake by capillary condensation in the macro-voids, i.e. cell lumens and pit chambers. In contrast, in the hygroscopic range (i.e. between 0 and about 30% MC), wood absorbs water molecules in cell walls, which interact with hydroxyl groups and is bound by hydrogen bonds (Fredriksson 2019). The over-hygroscopic moisture range is the moisture range exceeding 95–98% RH and is sometimes also called ‘capillary moisture range’ (e.g. Nilsson et al. 2018).
Murr and Lackner (2018) found that grain size and grain layer thickness influenced the initial sorption kinetics, with the latter showing a larger impact. This confirmed the notion of a transport-limited initial mass increase, possibly due to water vapour diffusion to the sorption sites. Long-term behaviour was less affected and was attributed to the ‘concept of a relaxation and reorganisation dominated long-time behaviour’; Murr (2019) confirmed that water vapour transport influenced the sorption kinetics of small sample sizes and concluded that this result need to be considered in modelling and interpretation of water vapour sorption experiments.
Similar to other porous materials, wood exhibits sorption hysteresis. At a given climate, the EMC of wood is not necessarily the same, since it depends on the moisture history (Fredriksson and Thybring 2018, 2019). Usually, the MC is higher during desorption compared to absorption, where the amplitude of the hysteresis strongly depends on the respective ambient climate. For interpretation of experimental data on the physiological needs of decay fungi, it is therefore essential to know the moisture history of the samples and to assure that theoretical EMC values are either based on absorption or desorption but never on different moistening or drying regimes. Hysteresis is more pronounced at high RH (Fredriksson and Thybring 2019) and therefore particularly important for the interpretation of MMThr values. However, in most studies, specimens were used to determine MMThr values, which underwent absorption.
Accessibility of sorption sites and localization of water
Hydroxyl groups (OH groups) are the predominant sorption sites for water molecules in wood. The amount of OH groups in hemicelluloses is twice as high as in lignin and four times higher compared to cellulose fibrils (Thybring et al. 2017). One approach to determine accessible OH groups in wood (in the hygroscopic range) is gravimetrically by hydrogen-deuterium exchange (Morrison 1960; Sepall and Mason 1961). The concept is initial drying, deuterium oxide (D2O) conditioning and final drying; deuterium oxide causes hydrogen on accessible OH groups to be exchanged with deuterium (heavy water), and the number of exchanged OH groups can be determined from change in mass. Beck et al. (2018a) reported that the OH accessibility (measured by deuterium exchange) in Pinus radiata earlywood stayed almost constant (6.5–8 mmol/g) during decay up to 50% ML caused by Rhodonia placenta. This might seem illogical since hemicellulose is degraded first by brown-rot fungi. It was hypothesized that new OH groups were exposed by (1) the opening of the cellulose micro-fibrils and (2) the modification of lignin by hydroxyl radicals from Fenton chemistry.
Numerous insights on wood-water relationships and fungal decay potential were derived from studies on thermally and chemically modified wood. In this regard, it has been shown that water was excluded from acetylated wood cell walls due to both direct substitution of OH groups leading to less primary sorption sites for water molecules and steric hindrance of unmodified OH groups by the bulky acetyl groups (Papadopoulos and Hill 2003; Popescu et al. 2014; Beck et al. 2017). In acetylated wood with an average weight percent gain (WPG) of 21.4%, Beck et al. (2018a) found that onset of substantial ML was preceded by a deacetylation phase. OH accessibility before decay was lower than for unmodified wood. Initiation of decay tended to increase the OH accessibility, and the reason is most likely due to oxidative degradation and deacetylation. At later stages of decay, the OH accessibility decreased again, probably due to residual acetyl groups on lignin. During the decay process, the acetylated samples never reached the OH levels found in unmodified wood.
Before and after brown-rot decay (R. placenta), wood-water relations were determined with low-field nuclear magnetic resonance (LFNMR) relaxometry. LFNMR can provide insights into wood-water chemical interactions as well as information about the distribution of water within the macro-void structure of the wood anatomy in the over-hygroscopic range. In acetylated wood decayed by brown rot, the behaviour of the cell wall wood-water relations (i.e. LFNMR T2 relaxation of water populations) corresponded well with the deacetylation observed by chemical characterization. Acetylation causes the water to become more mobile due to its reduced affinity for the acetylated cell wall, but the total amount of water within the cell wall is reduced (Beck et al. 2018b). Like acetylation, furfurylation was shown to reduce the amount of water within the cell wall determined with LFNMR (Thygesen and Elder 2009) However, in contrast to acetylation, furfurylation did not change the interaction of water with the cell wall surface. In the over-hygroscopic region furfurylated wood took up more water than untreated wood (voids and cracks during treatment). The same Pinus radiata material and test design as in Beck et al. (2017, 2018a, b) was used for furfurylated wood (Beck et al. 2019). OH accessibility in sound, furfurylated samples did not change with increasing WPG, suggesting little cross-linking occurs between the furfuryl polymer and the wood cell wall. OH accessibility in furfurylated wood samples at 32.1% WPG increased significantly after initiation of decay. This increase was attributed to opening of crystalline cellulose regions and formation of new OH groups in lignin and the furfural polymer due to oxidative alterations. The OH accessibility in sound furfurylated wood was lower than in unmodified wood, but after initiation of decay, it was slightly higher than in unmodified decayed wood (around 9 mmol/g).
Attempts to visualize capillary water in wood were made by Li et al. (2013) who used X-ray computed tomography and monitored water uptake processes in solid wood and different wood-based products. Similarly, De Ligne et al. (2019) observed density changes of small Scots pine sapwood blocks during decay by C. puteana with the help of X-ray CT. They hypothesized that different processes such as moisture uptake, moisture production by the fungus and ML due to fungal degradation caused density changes but struggled to ‘untangle these factors’. In many other studies (Watanabe et al. 2012; Lindgren et al. 2016; Hall 2019) micro-CT scanners were used to visualize and quantify wood moisture as well as its spatial distribution, for instance, during drying. However, to the best knowledge of the authors, micro-CT techniques have not yet been successfully applied to distinguish between bound and capillary water in wood during sorption or decay processes on cell and cell wall level.
Transport processes in wood in the absence of capillary water
Fungal decay alters the sorption and electrical conductivity of wood, and an increase of accessible OH groups at initiation of decay is suggested to be linked to a change of electrical conductivity. More OH groups could contribute to a percolating network. The analysis by Zelinka et al. (2008) ‘indicates that electrical conduction in wood can be explained by percolation theory and that there exists a continuous path of Type II water in wood at wc, which is below the traditional fiber saturation point’. Thybring et al. (2017) suggested that an ion transport in wood is linked with the formation of a continuous network of cell wall water, and limiting cell wall moisture, e.g. chemical modification, ‘might prevent the formation of such a network, hereby disrupting the physical pathways for transport of solutes’. Jakes et al. (2013) observed that the onset of metal corrosion and fungal decay in wood occurred before capillary water is formed in cavities and aqueous chemical transport would be possible. The percolation threshold when hemicelluloses undergo glass transition is likely far below the traditional FSP, i.e. around 16% MC according to Zelinka et al. (2008) and Jakes et al. (2019).
Brischke et al. (2018b) found that brown rot and white rot reduced the sorption of wood and lowered its electrical resistance in the hygroscopic range. Decayed specimens showed a MC well above fibre saturation and an increased electrical resistance compared to undecayed wood at a given MC as long as the fungal mycelium penetrating the wood blocks was alive. The hyphae network itself served apparently as an additional pathway for ions and water. When brown-rot decayed specimens were dried and re-wetted, they showed an elevated electrical resistance beyond cell wall saturation. In white-rot decayed specimens, the resistance was reduced at a given MC.
Oven-drying of the specimens led to a breakdown of the gelatinous extracellular matrix (ECM) formed by the fungus (Kirker et al. 2017). Afterwards, changes in electrical conductivity became apparent but were the consequence of the respective degradation patterns of brown- and white-rot fungi. During active fungal infestation, the fungi-induced changes of the cell wall chemistry are overruled by the presence of liquid water, not only in cell wall voids but also in the cell lumens.
Jakes et al. (2019) reviewed and applied approaches established in polymer science as a tool to understanding the effects of moisture on diffusion in unmodified wood cell walls. The premise was that ‘the movement of chemicals through wood cell walls is a diffusion process through a solid polymer’ and in contrast to previous assumptions of aqueous pathways. They conclude that both lignin and the amorphous polysaccharides in wood are likely to have glass transitions. Glass transition temperatures are affected by moisture and will increase when moisture decrease. This is of importance because diffusion strongly depends on the state of the polymer (i.e. rigid glassy state or soft rubbery state). The effects of water sorption and plasticization are not directly proportional, and water in ‘holes’ does not contribute to plasticization. The implications regarding fungal decay are not explicitly mentioned by Jakes et al. (2019), but several of their findings can be important to fungal metabolism, for example: (1) the parallel existence (in time and space) of different proposed states of water could help explain why fungal decay sometimes seems to start at wood MC below the traditional FSP, and (2) absorption of water molecules in ‘holes’ and the formation of water clusters might serve as ‘initiation spots’ of fungal enzymatic activity (provided the enzymes have access) and ‘may provide avenues for aqueous diffusion of chemicals through cell walls’. Crucial questions that arise are: (1) Is wood a miscible blend, a compatible blend, or an immiscible blend? (i.e. what is the glass transition point of wood cell walls?), and (2) does fungal decay depend on the glass transition point of a single component? (i.e. do fungi start to degrade hemicelluloses as soon as their enzymes can diffuse into them?). They further highlight a difference in diffusion through wood polymers vs. typical polymers, the high swelling pressures that can develop in unmodified wood cell walls and that this pressure should be given attention in future diffusion models.
Quantification of fungal responses
As an alternative to traditional mass and strength loss measurements, the metabolic activity of wood-decay fungi can be determined by microcalorimetry where the heat production rate is measured (Xie et al. 1997; Bjurman and Wadsö 2000; Wadsö et al. 2013; 2017). Bjurman and Wadsö (2000) applied the technique for studying the effect of temperature on fungal decay. Wadsö et al. (2013) studied the effect of different MC on fungal metabolism, and Wadsö et al. (2017) aimed on utilizing isothermal microcalorimetry for determining the durability of different wooden materials against fungal decay. Calorimetry measurements are very sensitive to small changes in fungal metabolic activity, and measurements can be conducted continuously. Hence, they are outperforming ML measurements for monitoring fungal decay development. One limitation of this method, and most other methods with a very well-controlled environment, is the limited number of samples allowed for each experimental run, often only one.
DNA-based methods are powerful tools for identification of wood-decaying organisms and for quantification of fungal biomass. Profiling of fungal communities related to wood protection include different materials exposed in experimental test fields (Råberg et al. 2007, 2009, 2013; Prewitt et al. 2014) and fence poles (Råberg and Daniel 2009). Profiling of species succession during decay of different wood materials using molecular tools is very limited. Råberg et al. (2007) compared species composition in six German test fields for two preceding years using terminal restriction fragment length polymorphism (T-RFLP), cloning and subsequent sequencing (semi-destructive sampling by drilling). Jacobs et al. (2019) studied fungal community succession in pine and beech stakes every half year, over a period of 3 years, using both morphological methods and DNA analysis (destructive sampling). None of the studies have taken moisture into account. The challenge of identification of fungal communities in field samples is that the analysis requires only a small amount of sample. To represent even a relatively small field test stake, a high number of replicates must be taken to get an estimate of the fungal community. And the fungal community will change over time. Reproducibility is challenging even within the same test site, a larger variation will occur between sites because of differences in inoculum potential, temperature and moisture. Hence, from an applied aspect, it does not so much focus on which fungal species decay the wood but on the resistance of the material against fungal degradation in general.
Methods to quantify fungal biomass in wood samples include ergosterol or chitin assays (traditional biomass assays, e.g. Matcham et al. 1985; Schnürer 1993) or DNA quantification with quantitative real-time PCR (qRT-PCR) (Eikenes et al. 2005). qRT-PCR has the advantage that it can be used for identification and quantification on species level (species specific primer) or at group level (e.g. basidiomycete-specific primer). When compared to chitin and ergosterol, qRT-PCR was shown to be the most sensitive method both in laboratory (Eikenes et al. 2005) and for field test stakes (Pilgård et al. 2011).
Unlike the genome, which is roughly fixed, the transcriptome can vary with external environmental conditions. The transcriptome reflects the genes that are being actively expressed at any given time. Gene expression studies of untreated wood have provided new insight regarding basidiomycete decay mechanisms (e.g. Sato et al. 2009; Martinez et al. 2009; MacDonald et al. 2011, 2012; Van den Wymelenberg 2009, 2010, 2011; Suzuki et al. 2012; Doria et al. 2014; Gaskell et al. 2014; Zhang et al. 2016; Zhang and Schilling 2017). Gene expression studies on preservative-treated (e.g. Kang et al. 2009a, b; Tang et al. 2013) and preservative-modified wood are still relatively limited (Alfredsen and Pilgård 2014; Ringman et al. 2014, 2015; Alfredsen et al. 2016a, b; Beck et al. 2018b; Skrede et al. 2019; Kölle et al. 2019). To the best knowledge of the authors, no experiments have been done on gene expression where the focus was to study the effect of different moisture levels. One reason is that it would be technically challenging to keep the wood moisture stable throughout the decay test. But the effect of moisture on fungal gene expression should, indirectly, have been captured in the modified wood experiments. Wood modifications have been claimed to have a non-toxic mode of action against decay fungi, and the lower EMC is believed to be the main effect against decay fungi as recently reviewed by Ringman et al. (2019). According to recent gene expression studies (Beck et al. 2018a; b; Skrede et al. 2019), the fungus starts a common decay process in the modified wood but proceeds at a slower pace. The slower process in modified wood could be due to reduced access to cell wall polysaccharides and/or lower EMC. The lower EMC will result in reduced transport of enzymes or water in an inadequate location or form. Ringman et al. (2019) review in more detail the role of water in brown-rot decay of chemically and thermally modified wood.
Important aspects that should be given more attention in future gene expression studies of wood-decomposing fungi are: (1) specimen design and harvest intervals (Zhang et al. 2016; Kölle et al. 2019), (2) substrate/culture conditions (Wu et al. 2018; 2019), (3) relevant comparison between treatments, (4) how to handle reference genes for accurate normalization (Zhang et al. 2019b) and (5) in situ mRNA hybridization rather than bulk sampling (Zhang et al. 2019a). It is worth to keep in mind that according to Vogel and Marcotte (2012) ∼ 60% of variation in protein concentration cannot be explained by measuring mRNAs alone. Hence, there is a need to expand the knowledge of what is secreted, especially for brown-rot fungi, and using a realistic substrate, i.e. solid wood (Presley and Schilling 2017; Presley et al. 2018; Wu et al. 2018).
Conclusions
Research on both wood-water relationships and the physiological needs of wood-decaying fungi has been consecutively performed during the last 150 years. Regardless, the interrelationships between moisture dynamics in wood and its effect on the activity of decay fungi are still not fully understood. Fortunately, respective research activities have been intensified during recent years. From the review of these rather complex interactions, one might conclude the following:
-
Understanding the moisture requirements of decay fungi is key for interpreting wood durability test data, for analysing the protective mode of action of new wood protection systems and for accurate modelling of degradation processes and the resulting service lifetimes of wood products.
-
Because of the assumed non-toxic effect and the change in MC, studies on fungal decay of modified wood provide insight regarding the wood-water effect on fungal behaviour. In the future, more targeted modifications (e.g. Digatis et al. 2019) of the cell wall, to increase or decrease moisture, could provide important new insight.
-
Quantification and localization of capillary and cell wall water – especially in the over-hygroscopic range – is considered crucial for determining minimum moisture thresholds (MMThr) of wood-decay fungi. In particular, the role of capillary or loosely bound water in modified wood necessitates clarification, i.e. it is still not understood whether decay fungi can utilize capillary water in cell lumens or larger cell wall voids for metabolizing cell wall substance. Increased knowledge about the potential transport processes in wood in the absence of capillary water might add additional pieces to this puzzle.
-
Further unknowns are the minimum wood volume that needs to exceed a certain MMThr and the time needed to allow for onset of decay under such marginal conditions. In this respect and for practical purposes, it is also interesting to increase the understanding about the effect of dry periods on fungal mycelium and its ability to get revitalized after re-wetting.
-
The limitations of the various methods and experimental set-ups to investigate wood-water relationships and their role for fungal decay are manifold. Hence, combining techniques from wood science, mycology, biotechnology, and advanced analytics, such as calorimetry, DVS, DSC, LFNMR, fungal transcriptome and secretome, microspectroscopy and chemometrics with sub-cell wall spatial resolution using incubation experiments on solid wood substrate in strictly controlled environments might provide new insights and eventually a breakthrough in understanding.
-
It is commonly agreed that knowledge about how fungi sense the dynamic composition of the wood cell wall (incl. water amount and distribution) and adapt their secretome in response are still fragmentary. Still, huge efforts are needed to close the existing gaps in our understanding of fungal biodegradation. The detailed laboratory studies suggested might seem irrelevant from an applied perspective. But a breakthrough on a detailed level will potentially have big direct implications for different applications. Examples include, e.g. targeted blocking of fungal metabolic pathways for improved wood protection, precision of modelling tools and new enzymes or enzyme combinations for biorefinery applications. Regarding the bigger picture, climate change is the grand challenge of our time. Since more than half of all biomass on Earth is wood, part of the solution is improved utilization and longer service life (i.e. carbon storage) and valorization (i.e. biorefinery applications) of the renewable wood source as a substitute for more energy-consuming raw material sources. By unravelling the intricate details about decomposition of wood by lignocellulolytic fungi, we will also have tools to better quantify carbon storage and release both in nature and for wood in service.
Change history
02 August 2021
A Correction to this paper has been published: https://doi.org/10.1007/s00253-021-11408-6
References
Alfredsen G, Pilgård A (2014) Postia placenta decay of acetic anhydride modified wood – effect of leaching. Wood Mat Sci Eng 9:162–169. https://doi.org/10.1080/17480272.2014.887776
Alfredsen G, Fossdal CG, Nagy NE, Jellison J, Goodell B (2016a) Furfurylated wood - impact on Postia placenta gene expression and oxalate crystal formation. Holzforschung. 70:947–962. https://doi.org/10.1515/hf-2015-0203
Alfredsen G, Pilgård A, Fossdal CG (2016b) Characterisation of Postia placenta colonisation during 36 weeks in acetylated southern yellow pine sapwood at three acetylation levels including genomic DNA and gene expression quantification of the fungus. Holzforschung 70(11):1055–1065. https://doi.org/10.1515/hf-2016-0009
Almeida G, Hernández RE (2007) Influence of the pore structure of wood on moisture desorption at high relative humidities. Wood Mat Sci Eng 2:33–44. https://doi.org/10.1080/17480270701538383
Ammer U (1963) Untersuchungen über das Wachstum von Rotstreifepilzen in Abhängigkeit von der Holzfeuchtigkeit. Forstw Centralbl 82:360–391. https://doi.org/10.1007/BF02202726
Arantes V, Goodell B (2014) Current understanding of brown-rot fungal biodegradation mechanisms: a review. In: Deterioration and protection of sustainable biomaterials. American Chemical Society, Washington, DC, pp 3–21. https://doi.org/10.1021/bk-2014-1158.ch001
Bavendamm W, Reichelt H (1938) Die Abhängigkeit des Wachstums holzzersetzender Pilze vom Wassergehalt des Nährsubstrates. Arch Mikrobiol 9:486–544. https://doi.org/10.1007/BF00407374
Beck G, Strohbusch S, Larnøy E, Militz H, Hill CAS (2017) Accessibility of hydroxyl groups in anhydride modified wood as measured by deuterium exchange and saponification. Holzforschung 72(1):17–23. https://doi.org/10.1515/hf-2017-0059
Beck G, Thybring EE, Thygesen LG (2018a) Brown-rot fungal degradation and de-acetylation of acetylated wood. Int Biodeterior Biodegradation 135:62–70. https://doi.org/10.1016/j.ibiod.2018.09.009
Beck G, Hegnar OA, Fossdal CG, Alfredsen G (2018b) Acetylation of Pinus radiata delays hydrolytic depolymerisation by the brown-rot fungus Rhodonia placenta. Int Biodeterior Biodegradation 135:39–52. https://doi.org/10.1016/j.ibiod.2018.09.003
Beck G, Hill C, Cocher PM, Alfredsen G (2019) Accessibility of hydroxyl groups in furfurylated wood at different weight percent gains and during Rhodonia placenta decay. Eur J Wood Wood Prod 77:953–955. https://doi.org/10.1007/s00107-019-01445-4
Bjurman J, Wadsö L (2000) Microcalorimetric measurements of metabolic activity of six decay fungi on spruce wood as a function of temperature. Mycologia 92:23–28. https://doi.org/10.1080/00275514.2000.12061126
Brischke C, Soetbeer A, Meyer-Veltrup L (2017) The minimum moisture threshold for wood decay by basidiomycetes revisited. A review and modified experiments with Norway spruce and European beech decayed by Coniophora puteana and Trametes versicolor. Holzforschung 71:893–903. https://doi.org/10.1515/hf-2017-0051
Brischke C, Meyer-Veltrup L, Soetbeer A (2018a) Moisture requirements of wood decay fungi – review on methods, thresholds and experimental limitations. Holztechnologie 59:36–42
Brischke C, Stricker S, Meyer-Veltrup L, Emmerich L (2018b) Changes in sorption and electrical properties of wood caused by fungal decay. Holzforschung 73:445–455. https://doi.org/10.1515/hf-2018-0171
Butin H (1962) Keimung und Lebensdauer der Sporen von Dothichiza populea Sacc. et Br. bei verschiedener Luftfeuchtigkeit. Ber Deut Bot Ges 75:221–232
Castaño JD, Zhang J, Anderson CE, Schilling JS (2018) Oxidative damage control during decay of wood by brown-rot fungus using oxygen radicals. Appl Environ Microbiol 84:e01937–e01918. https://doi.org/10.1128/AEM.01937-18
Cloutier A, Fortin Y (1991) Moisture content—water potential relationship of wood from saturated to dry conditions. Wood Sci Technol 25:263–280. https://doi.org/10.1007/BF00225466
Cowling EB (1961) Comparative biochemistry of the decay of sweetgum sapwood by white-rot and brown-rot fungi. US Dept. of Agriculture. Technical Bulletin No. 1258. Washington DC, USA. https://doi.org/10.22004/ag.econ.170882
Crook B, Burton NC (2010) Indoor moulds, sick building syndrome and building related illness. Fung Biol Rev 24:106–113. https://doi.org/10.1016/j.fbr.2010.05.001
Daniel G, Nilsson T (1997) Developments in the study of soft-rot and bacterial decay. Ch. 3:37-62. In: Bruce A, Palfreyman JW (eds) Forest products biotechnology. Taylor & Francis, United Kingdom
De Ligne L, Van den Bulcke J, De Muynck A, Baetens J, De Baets B, Van Hoorebeke L, Van Acker J (2019) Exploring the use of X-ray micro CT as a tool for the monitoring of moisture production and mass loss during lab-based fungal degradation testing. International Research Group on Wood Protection, 50th Annual Conference, Quebec City, Canada, IRG/WP 19-20654
Digatis R, Thygesen LG, Thybring EE, Fredriksson M (2019) Targeted acetylation of Norway spruce tissue and its effect on moisture states in wood. In: Fredriksson M (ed) Proceedings of the 15th Annual Meeting of the Northern European Network for Wood Science and Engineering – WSE 9-10 October 2019. Lund University
Doria E, Altobelli E, Girometta C, Nielsen E, Zhang T, Savino E (2014) Evaluation of lignocellulolytic activities of ten fungal species able to degrade poplar wood. Int Biodeterior Biodegradation 94:160–166. https://doi.org/10.1186/s13068-016-0461-x
Eikenes M, Hietala A, Alfredsen G, Fossdal CG, Solheim H (2005) Comparison of chitin, ergosterol and real-time PCR based assays for monitoring colonization of Trametes versicolor in birch wood. Holzforschung 59:568–573. https://doi.org/10.1515/HF.2005.093
Engelund ET, Thygesen LG, Svensson S, Hill CA (2013) A critical discussion of the physics of wood–water interactions. Wood Sci Technol 47:141–161. https://doi.org/10.1007/s00226-012-0514-7
Filley TR, Cody GD, Goodell B, Jellison J, Noser C, Ostrofsky A (2002) Lignin demethylation and polysaccharide decomposition in spruce sapwood degraded by brown-rot fungi. Org Geochem 33:111–124. https://doi.org/10.1016/S0146-6380(01)00144-9
Floudas D, Binder M, Riley R, Barry K, Blanchette RA, Henrissat B, Martínez AT, Otillar R, Spatafora JW, Yadav JS, Aerts A, Benoit I, Boyd A, Carlson A, Copeland A, Coutinho PM, de Vries RP, Ferreira P, Findley K, Foster B, Gaskell J, Glotzer D, Górecki P, Heitman J, Hesse C, Hori C, Igarashi K, Jurgens JA, Kallen N, Kersten P, Kohler A, Kües U, Kumar TKA, Kuo A, LaButti K, Larrondo LF, Lindquist E, Ling A, Lombard V, Lucas S, Lundell T, Martin R, McLaughlin DJ, Morgenstern I, Morin E, Murat C, Nagy LG, Nolan M, Ohm RA, Patyshakuliyeva A, Rokas A, Ruiz-Duenas FJ, Sabat G, Salamov A, Samejima M, Schmutz J, Slot JC, John FS, Stenlid J, Sun H, Syed K, Tsang A, Wiebenga A, Young D, Pisabarro A, Eastwood DC, Martin F, Cullen D, Grigoriev IV, Hibbett DS (2012) The Paleozoic origin of enzymatic lignin decomposition reconstructed from 31 fungal genomes. Science 336:1715–1719. https://doi.org/10.1126/science.1221748
Fredriksson M (2019) On wood-water interactions in the over-hygroscopic moisture range – mechanisms, methods, and influence of wood modification. Forests 10:779. https://doi.org/10.3390/f10090779
Fredriksson M, Johansson P (2016) A method for determination of absorption isotherms at high relative humidity levels: measurements on lime-silica brick and Norway spruce (Picea abies (L.) Karst.). Dry Technol 34:132–141
Fredriksson M, Thybring EE (2018) Scanning or desorption isotherms? Characterising sorption hysteresis of wood. Cellulose 25:4477–4485. https://doi.org/10.1007/s10570-018-1898-9
Fredriksson M, Thybring EE (2019) On sorption hysteresis in wood: separating hysteresis in cell wall water and capillary water in the full moisture range. PLoS One 14(11):e0225111. https://doi.org/10.1371/journal.pone.0225111
Gaskell J, Amber Marty A, Mozuch M, Kersten PJ, BonDurant SS, Sabat G, Azarpira A, Ralph J, Skyba O, Mansfield SD, Blanchette RA, Cullena D (2014) Influence of populus genotype on gene expression by the wood decay fungus Phanerochaete chrysosporium. Appl Environ Microbiol 80(18):5828–5835. https://doi.org/10.1128/AEM.01604-14
Goodell B, Qian Y, Jellison J (2008) Fungal decay of wood: soft-rot-brown-rot-white-rot. Chapter 2. In: Development of Commercial Wood Preservatives. ACS Symposium Series 982:9–31. https://doi.org/10.1021/bk-2008-0982.ch002
Goodell B, Zhu Y, Kim S, Kafle K, Eastwood D, Daniel G, Jellison J, Yoshida M, Groom L, Pingali SV, O’Neill H (2017) Modification of the nanostructure of lignocellulose cell walls via a non-enzymatic lignocellulose deconstruction system in brown-rot wood-decay fungi. Biotechnol Biofuels 10:179. https://doi.org/10.1186/s13068-017-0865-2
Gottlieb D (1950) The physiology of spore germination in fungi. Bot Rev 16:229–257. https://doi.org/10.1146/annurev.py.08.090170.001433
Hailwood AJ, Horrobin S (1946) Absorption of water by polymers: analysis in terms of a simple model. Trans Faraday So 42B:84–102
Hall S (2019) 3D and 4D x-ray imaging of wood structures and processing. In: Fredriksson M (ed) Proceedings of the 15th Annual Meeting of the Northern European Network for Wood Science and Engineering – WSE 9-10 October 2019. Lund University, pp 1–2
Hartley ID, Kamke FA, Peemoeller H (1992) Cluster theory for water sorption in wood. Wood Sci Technol 26:83–99. https://doi.org/10.1007/BF00194465
Hernández RE, Bizoň M (2007) Changes in shrinkage and tangential compression strength of sugar maple below and above the fiber saturation point. Wood Fiber Sci 26:360–369
Hibbett DS, Donoghue MJ (2001) Analysis of character correlations among wood decay mechanisms, mating systems, and substrate ranges in homobasidiomycetes. Syst Biol 50:215–242. https://doi.org/10.1080/10635150151125879
Hoffmeyer P, Engelund ET, Thygesen LG (2011) Equilibrium moisture content (EMC) in Norway spruce during the first and second desorptions. Holzforschung 65:875–882. https://doi.org/10.1515/HF.2011.112
Höpken M (2015) Untersuchungen zu Wachstum und Feuchtetransport von Hausfäulepilzen anhand gestapelter Holzklötzchen. Master thesis. University of Hamburg
Huckfeldt T, Schmidt O (2006) Hausfäule- und Bauholzpilze. Diagnose und Sanierung, Müller, Cologne
Huckfeldt T, Schmidt O, Quader H (2005) Ökologische Untersuchungen am Echten Hausschwamm und weiteren Hausfäulepilzen. Holz Roh Werkst 63:209–219. https://doi.org/10.1007/s00107-004-0559-x
Hunter AJ (1995) Equilibrium moisture content and the movement of water through wood above fibre saturation. Wood Sci Technol 29:129–135. https://doi.org/10.1007/BF00229342
Jacobs K, Plaschkies K, Scheiding W, Weiß B, Melcher E, Conti E, Fojutowski A, Le Bayon I (2019) Natural durability of important European wood species against wood decay fungi. Part 2: field tests and fungal community. Int Biodeterior Biodegradation 137:118–126. https://doi.org/10.1016/j.ibiod.2018.12.002
Jakes JE, Hunt CG, Zelinka SL, Ciesielski PN, Plaza NZ (2019) Effects of moisture on diffusion in unmodified Wood cell walls: a phenomenological polymer science approach. Forests 10:1084. https://doi.org/10.3390/f10121084
Jakes JE, Plaza N, Stone DS, Hunt CG, Glass SV, Zelinka SL (2013) Mechanism of transport through wood cell wall polymers. J For Prod Ind 2:10–13
Kaffenberger JT, Schilling JS (2013) Using a grass substrate to compare decay among two clades of brown rot fungi. Appl Microbiol Biotechnol 97:8831–8840. https://doi.org/10.1007/s00253-013-5142-0
Kang YM, Prewitt ML, Diehl S (2009a) Gene expression of selected decay enzymes produced during biodeterioration of three wood types. International Research Group on Wood Protection, 40th Annual Conference, Beijing, China, IRG/WP 09-10702
Kang YM, Prewitt ML, Diehl SV (2009b) Proteomics for biodeterioration of wood (Pinus taeda L.): challenging analysis by 2-D PAGE and MALDI-TOF/TOF/MS. Int Biodeterior Biodegradation 63:1036–1044. https://doi.org/10.1016/j.ibiod.2009.07.008
Kim YS, Singh AP (2000) Micromorphological characteristics of wood biodegradation in wet environments: a review. IAWA J 21:135–155
Kirker GT, Zelinka SL, Gleber S-C, Vine D, Finney L, Chen S, Hong YP, Uyarte O, Vogt S, Jellison J, Goodell B, Jakes JE (2017) Synchrotron-based X-ray fluorescence microscopy enables multiscale spatial visualization of ions involved in fungal lignocellulose deconstruction. Sci Rep 7:41798. https://doi.org/10.1038/srep41798
Kölle M, Ringman R, Pilgård A (2019) Initial Rhodonia placenta gene expression in acetylated wood: group-wise upregulation of non-enzymatic oxidative wood degradation genes depending on the treatment level. Forests 10:1117. https://doi.org/10.3390/f10121117
Korripally P, Timokhin VI, Houtman CJ, Mozuch MD, Hammel KE (2013) Evidence from Serpula lacrymans that 2,5-dimethoxyhydroquinone is a lignocellulolytic agent of divergent brown-rot basidiomycetes. Appl Environ Microbiol 79:2377–2383. https://doi.org/10.1128/AEM.03880-12
Li W, Van den Bulcke J, De Windt I, Van Loo D, Dierick M, Brabant L, Van Acker J (2013) Combining electrical resistance and 3-D X-ray computed tomography for moisture distribution measurements in wood products exposed in dynamic moisture conditions. Build Environ 67:250–259. https://doi.org/10.1016/j.buildenv.2013.05.026
Lindgren O, Seifert T, Du Plessis A (2016) Moisture content measurements in wood using dual-energy CT scanning – a feasibility study. Wood Mat Sci Eng 11:312–317. https://doi.org/10.1080/17480272.2016.1201863
MacDonald J, Doering M, Canam T, Gong Y, Guttman DS, Campbell MM, Master ER (2011) Transcriptomic responses of the softwood-degrading white-rot fungus Phanerochaete carnosa during growth on coniferous and deciduous wood. Appl Environ Microbiol 77:3211–3218. https://doi.org/10.1128/AEM.02490-10
MacDonald J, Master ER (2012) Time-dependent profiles of transcripts encoding lignocellulose-modifying enzymes of the white-rot fungus Phanerochaete carnosa grown on multiple wood substrates. Appl Environ Microbiol 78:1596–1600. https://doi.org/10.1128/AEM.06511-11
Manavalan T, Manavalan A, Heese K (2015) Characterization of lignocellulolytic enzymes from white-rot fungi. Curr Microbiol 70:485–498. https://doi.org/10.1007/s00284-014-0743-0
Martinez D, Challacombea J, Morgensternc I, Hibbettc D, Schmolld M, Kubicekd CP, Ferreirae P, Ruiz-Duenase FJ, Martineze AT, Kerstenf P, Hammelf KE, Vanden Wymelenberg A, Gaskellf J, Lindquisth E, Sabati G, BonDuranti SS, Larrondoj LF, Canessaj P, Vicunaj R, Yadavk J, Doddapanenik H, Subramaniank V, Pisabarrol AG, Lavínl JL, Oguizal JA, Masterm E, Henrissatn B, Coutinhon PM, Harriso P, Magnusonp JK, Bakerp SE, Brunop K, Kenealyq W, Hoegger PJ, Kuesr U, Ramaiyao P, Lucash S, Salamovh A, Shapiroh H, Tuh H, Cheeb CL, Misraa M, Xiea G, Tetero S, Yavero D, Jamess T, Mokrejst M, Pospisekt M, Grigorievh IV, Brettina T, Rokhsarh D, Berkao R, Cullenf D (2009) Genome, transcriptome, and secretome analysis of wood decay fungus Postia placenta supports unique mechanisms of lignocellulose conversion. Proc Natl Acad Sci 106:1954–1959. https://doi.org/10.1073/pnas.0809575106
Matcham SE, Jordan BR, Wood DA (1985) Estimation of fungal biomass in a solid substrate by three independent methods. Appl Microbiol Biotechnol 21:108–112. https://doi.org/10.1007/BF00252371
Merrill W (1970) Spore germination and host penetration by heartrotting hymenomycetes. Annu Rev Phytopathol 8:281–300. https://doi.org/10.1146/annurev.py.08.090170.001433
Meyer L, Brischke C (2015) Fungal decay at different moisture levels of selected European-grown wood species. Int Biodeterior Biodegradation 103:23–29. https://doi.org/10.1016/j.ibiod.2015.04.009
Meyer L, Brischke C, Kasselmann M (2015a) Holzfeuchte-Monitoring im Rahmen von Dauerhaftigkeitsprüfungen - Praktische Erfahrungen aus Freilandversuchen. Holztechnologie 56:11–19
Meyer L, Brischke C, Treu A, Larsson-Brelid P (2015b) Critical moisture conditions for fungal decay of modified wood by basidiomycetes as detected by pile tests. Holzforschung 70:331–339. https://doi.org/10.1515/hf-2015-0046
Morrison J (1960) Deuterium-hydrogen exchange between water and macromolecules: accessibility of cellulose. Nature 185:160–161
Münch E (1909) Untersuchungen über Immunität und Krankheitsempfänglichkeit der Holzpflanzen. Naturwiss Zeitschr Forst Landw 7:54–75
Murr A (2019) The relevance of water vapour transport for water vapour sorption experiments on small wooden samples. Transp Porous Media 128:385–404. https://doi.org/10.1007/s11242-019-01253-7
Murr A, Lackner R (2018) Analysis on the influence of grain size and grain layer thickness on the sorption kinetics of grained wood at low relative humidity with the use of water vapour sorption experiments. Wood Sci Technol 52:753–776. https://doi.org/10.1007/s00226-018-1003-4
Nilsson L-O, Franzoni E, Paroll H (2018) Introduction. In: Nilsson J-O (ed) Methods of measuring moisture in building materials and structures. Springer, Heidelberg Berlin
Pandey KK, Pitman AJ (2003) FTIR studies of the changes in wood chemistry following decay by brown-rot and white-rot fungi. Int Biodeterior Biodegradation 52:151–160. https://doi.org/10.1016/S0964-8305(03)00052-0
Papadopoulos AN, Hill CAS (2003) The sorption of water vapour by anhydride modified softwood. Wood Sci Technol 37:221–231. https://doi.org/10.1007/s00226-003-0192-6
Peralta PN (2007) Sorption of moisture by wood within a limited range of relative humidities. Wood Fiber Sci 27:13–21
Pilgård A, Alfredsen G, Björdal CG, Børja I, Fossdal CG (2011) qPCR as a tool to study basidiomycete colonization in wooden field stakes. Holzforschung 65:889–895
Plaza NZ (2019) On the experimental assessment of the molecular-scale interactions between wood and water. Forests 10:616. https://doi.org/10.3390/f10080616
Popescu C-M, Hill CAS, Curling S, Ormondroyd G, Xie Y (2014) The water vapour sorption behaviour of acetylated birch wood – how acetylation affects the sorption isotherm and accessible hydroxyl content. J Mater Sci 49:2362–2371. https://doi.org/10.1007/s10853-013-7937-x
Popper R, Niemz P (2009) Wasserdampfsorptionsverhalten ausgewählter heimischer und überseeischer Holzarten. Bauphysik 31:117–121. https://doi.org/10.1002/bapi.200910017
Presley GN, Schilling JS (2017) Distinct growth and secretome strategies for two taxonomically divergent brown-rot fungi. Appl Environ Microbiol 83:e02987–e02916. https://doi.org/10.1128/AEM.02987-16
Presley GN, Panisko E, Purvine SO, Schilling JS (2018) Coupling secretomics with enzyme activities to compare the temporal process of wood metabolism among white and brown-rot fungi. Appl Environ Microbiol 84:e00159–e00118. https://doi.org/10.1128/AEM.00159-18
Prewitt L, Kang Y, Kakumanu M, Williams M (2014) Fungal and bacterial community succession differs for three wood types during decay in a forest soil. Microb Ecol 68:212–221. https://doi.org/10.1007/s00248-014-0396-3
Råberg U, Daniel G (2009) Brown-rot decay of copper-chromated-phosphorus impregnated fence poles: characterization by molecular analyses and microscopy. Int Biodeterior Biodegradation 63(7):906–912. https://doi.org/10.1016/j.ibiod.2009.04.009
Råberg U, Brischke C, Rapp A, Högberg NOS, Land CJ (2007) External and internal fungal flora of pine sapwood (Pinus sylvestris L.) specimens in above-ground field tests at six different sites in South-West Germany. Holzforschung 61:104–111. https://doi.org/10.1515/HF.2007.017
Råberg U, Terziev N, Land CJ (2009) Early soft-rot colonization of scots sapwood pine in above-ground exposure. Int Biodeterior Biodegradation 63(2):236–240. https://doi.org/10.1016/j.ibiod.2007.10.005
Råberg U, Terziev N, Daniel G (2013) Degradation of scots pine and beech wood exposed in four test fields used for testing of wood preservatives. Int Biodeterior Biodegradation 79:20–27. https://doi.org/10.1016/j.ibiod.2012.12.010
Riley R, Salamov AA, Brown DW, Nagy LG, Floudas D, Held BW, Levasseur A, Lombard V, Morin E, Otillar R, Lindquist EA, Sun H, LaButti KM, Schmutz J, Jabbour D, Luo H, Baker SE, Pisabarro AG, Walton JD, Blanchette RA, Henrissat B, Martin F, Cullen D, Hibbett DS, Grigoriev IV (2014) Extensive sampling of basidiomycete genomes demonstrates inadequacy of the white-rot/brown-rot paradigm for wood decay fungi. Proc Natl Acad Sci 111:9923–9928. https://doi.org/10.1073/pnas.1400592111
Ringman R, Beck G, Pilgård A (2019) The importance of moisture for brown-rot degradation of modified wood: a critical discussion. Forests 10:522. https://doi.org/10.3390/f10060522
Ringman R, Pilgård P, Kölle M, Brischke C, Richter K (2015) Effects of thermal modification on Postia placenta wood degradation dynamics: measurements of mass loss, structural integrity and gene expression. Wood Sci Technol 50:385–397. https://doi.org/10.1016/j.ibiod.2013.09.002
Ringman R, Pilgård A, Richter K (2014) Effect of wood modification on gene expression during incipient Postia placenta decay. Int Biodeterior Biodegradation 86:86–91. https://doi.org/10.1016/j.ibiod.2013.09.002
Saito H, Fukuda K, Sawachi T (2012) Integration model of hygrothermal analysis with decay process for durability assessment of building envelopes. Build Simul 5:315–324. https://doi.org/10.1007/s12273-012-0081-8
Sato S, Feltus FA, Iyer P, Tien M (2009) The first genome-level transcriptome of the wood-degrading fungus Phanerochaete chrysosporium grown on red oak. Curr Genet 55(3):273–286. https://doi.org/10.1007/s00294-009-0243-0
Schmidt O (2006) Wood and tree fungi. Biology, damage, protection, and use. Springer, Berlin
Schmidt O, Liese W, Moreth U (1996) Decay of timber in a water cooling tower by the basidiomycete Physisporinus vitreus. Mater Org 30:161–178
Schnürer J (1993) Comparison of methods for estimating the biomass of three food-borne fungi with different growth patterns. Appl Environ Microbiol 59:552–555
Sepall O, Mason SG (1961) Hydrogen exchange between cellulose and water: I. measurement of accessibility. Can J Chem 39:1934–1943
Skaar C (1988) Wood water relations. Springer, Berlin
Skrede I, Solbakken MH, Hess J, Fossdal CG, Hegnar O, Alfredsen G (2019) Wood modification by furfuryl alcohol resulted in a delayed decomposition response in Rhodonia (Postia) placenta. Appl Environ Microbiol 85:e00338–e00319. https://doi.org/10.1128/AEM.00338-19
Stamm AJ (1959) The dimensional stability of wood. For Prod J 9:375–381
Stamm AJ (1971) A review on nine methods for determining the fiber saturation point of wood and wood products. Wood Sci 4:114–128
Stienen T, Schmidt O, Huckfeldt T (2014) Wood decay by indoor basidiomycetes at different moisture and temperature. Holzforschung 68:9–15. https://doi.org/10.1515/hf-2013-0065
Suzuki H, MacDonald J, Syed K, Salamov A, Hori C, Aerts A, Henrissat B, Wiebenga A, van Kuyk PA, Barry K, Lindquist E, Labutti K, Lapidus A, Lucas S, Coutinho P, Gong Y, Samejima M, Mahadevan R, Abou-Zaid M, de Vries RP, Igarashi K, Yadav JS, Grigoriev IV, Master ER (2012) Comparative genomics of the white-rot fungi, Phanerochaete carnosa and P. chrysosporium, to elucidate the genetic basis of the distinct wood types they colonize. BMC Genomics 13:–444. https://doi.org/10.1186/1471-2164-13-444
Tang J, Parker LA, Perkins AD, Sonstegard TS, Schroeder SG, Nicholas DD, Diehl SV (2013) Gene expression analysis of copper tolerance and wood decay in the brown-rot fungus Fibroporia radiculosa. Appl Environ Microbiol 79:1523–1533. https://doi.org/10.1128/AEM.02916-12
Theden G (1941) Untersuchungen über die Feuchtigkeitsansprüche der wichtigsten in Gebäuden auftretenden holzzerstörenden Pilze. Dissertation. Friedrich Wilhelms-University, Berlin. Angew Bot 23:189–253
Thybring EE, Kymäläinen M, Rautkari L (2017) Experimental techniques for characterising water in wood covering the range from dry to fully water-saturated. Wood Sci Technol 52:1–33
Thybring EE, Glass SV, Zelinka SL (2019) Kinetics of water vapor sorption in wood cell walls: state of the art and research needs. Forests 10:704. https://doi.org/10.3390/f10080704
Thygesen LG, Elder T (2009) Moisture in untreated, acetylated, and furfurylated Norway spruce monitored during drying below fiber saturation using time domain NMR. Wood Fiber Sci 41:194–200
Tiemann HD (1906) Effect of moisture on the strength and stiffness of wood. USDA Forest Serv Bull 70
Tremblay C, Cloutier A, Fortin Y (1996) Moisture content-water potential relationship of red pine sapwood above the fiber saturation point and determination of the effective pore size distribution. Wood Sci Technol 30:361–371. https://doi.org/10.1007/BF00223556
Van den Wymelenberg A, Gaskell J, Mozuch M, Kersten P, Sabat G, Martinez D, Cullen D (2009) Transcriptome and secretome analysis of Phanerochaete chrysosporium reveal complex patterns of gene expression. Appl Environ Microbiol 75:4058–4068. https://doi.org/10.1128/AEM.00314-09
Van den Wymelenberg A, Gaskell J, Mozuch M, Sabat G, Ralph J, Skyba O, Mansfield SD, Blanchette RA, Martinez D, Grigoriev I, Kersten PJ, Cullen D (2010) Comparative transcriptome and secretome analysis of wood decay fungi Postia placenta and Phanerochaete chrysosporium. Appl Environ Microbiol 76:3599–3610. https://doi.org/10.1128/AEM.00058-10
Van den Wymelenberg A, Gaskell J, Mozuch M, BonDurant SS, Sabat G, Ralph J, Skyba O, Mansfield SD, Blanchette RA, Grigoriev IV, Kersten J, Cullen D (2011) Significant alteration of gene expression in wood decay fungi Postia placenta and Phanerochaete chrysosporium. Appl Environ Microbiol 77:4499–4507. https://doi.org/10.1128/AEM.00508-11
Vanpachtenbeke M (2019) Timber frame walls with brick veneer cladding – reliability to fungal decay. University Leuven, Dissertation
Venkateswaran A (1970) Sorption of aqueous and non-aqueous media by wood and cellulose. Chem Rev 70:619–637. https://doi.org/10.1021/cr60268a001
Viitanen H (1994) Factors affecting the development of biodeterioration in wooden constructions. Mater Struct 27:483–493. https://doi.org/10.1007/BF02473453
Vogel C, Marcotte EM (2012) Insights into the regulation of protein abundance from proteomic and transcriptomic analyses. Nat Rev Genet 13:227–232. https://doi.org/10.1038/nrg3185
Wadsö L, Johansson S, Pilgård A, Alfredsen G (2013) The activity of rot fungi (Postia placenta) during drying and rewetting cycles measured by isothermal calorimetry. Eng Life Sci 13:536–540. https://doi.org/10.1002/elsc.201200096
Wadsö L, Johansson S, Bardage S (2017) Monitoring of fungal colonization of wood materials using isothermal calorimetry. Int Biodeterior Biodegrad 120:43–51. https://doi.org/10.1016/j.ibiod.2017.02.003
Watanabe K, Lazarescu C, Shida S, Avramidis S (2012) A novel method of measuring moisture content distribution in timber during drying using CT scanning and image processing techniques. Dry Technol 30:256–262. https://doi.org/10.1080/07373937.2011.634977
Wehmer C (1914) Hausschwammstudien I-V. Versuche über die Bedingungen der Holzansteckung und -Zersetzung durch Merulius. Myc Centralbl 3:321–332
Wei D, Houtman CJ, Kapich AN, Hunt CG, Cullen D, Hammel KE (2010) Laccase and its role in production of extracellular reactive oxygen species during wood decay by the brown-rot basidiomycete Postia placenta. Appl Environ Microbiol 76:2091–2097. https://doi.org/10.1128/AEM.02929-09
Winandy JE, Morell JJ (1993) Relationship between incipient decay, strength, and chemical composition of Douglas-fir heartwood. Wood Fiber Sci 25:278–288
Wu B, Gaskell J, Held BW, Toapanta C, Vuong T, Ahrendt S, Lipzen A, Zhang J, Schilling JS, Master E, Grigoriev IV, Blanchette RA, Cullen D, Hibbett DS (2018) Substrate-specific differential gene expression and RNA editing in the brown-rot fungus Fomitopsis pinicola. Appl Environ Microbiol 84(16):e00991–e00918. https://doi.org/10.1128/AEM.00991-18
Wu B, Gaskell J, Zhang J, Toapanta C, Ahrendt S, Grigoriev IV, Blanchette RA, Schilling JS, Master E, Cullen D, Hibbett DS (2019) Evolution of substrate-specific gene expression and RNA editing in brown-rot wood-decaying fungi. ISME J 13:1391–1403. https://doi.org/10.1038/s41396-019-0359-2
Xie Y, Bjurman J, Wadsö L (1997) Microcalorimetric characterization of the recovery of a brown-rot fungus after exposures to high and low temperature, oxygen depletion, and drying. Holzforschung 51:201–206. https://doi.org/10.1515/hfsg.1997.51.3.201
Zelinka SL, Rammer DR (2009) Corrosion rates of fasteners in treated wood exposed to 100% relative humidity. J Mater Civ Eng 21:758–763. https://doi.org/10.1061/(ASCE)0899-1561
Zelinka SL, Glass SV, Stone DS (2008) A percolation model for electrical conduction in wood with implications for wood-water relations. Wood Fiber Sci 40:544–552
Zelinka SL, Glass SV, Thybring EE (2018) Myth versus reality: do parabolic sorption isotherm models reflect actual wood–water thermodynamics? Wood Sci Technol 52:1701–1706. https://doi.org/10.1007/s00226-018-1035-9
Zeller SM (1920) Humidity in relation to moisture imbibition by wood and to spore germination on wood. Ann Mo Bot Gard 7:51–75. https://doi.org/10.2307/2990045
Zhang J, Hub D, Orr G, Schilling J (2019a) Fluorescence in situ mRNA hybridization for gene expression detection in a wood decay fungus. Int Biodeterior Biodegrad 143:104731. https://doi.org/10.1016/j.ibiod.2019.104731
Zhang J, Mitchell HD, Markillie LM, Gaffrey MJ, Orr G, Schilling J (2019b) Reference genes for accurate normalization of gene expression in wood-decomposing fungi. Fungal Genet Biol 123:33–40. https://doi.org/10.1016/j.fgb.2018.11.005
Zhang J, Schilling JS (2017) Role of carbon source in the shift from oxidative to hydrolytic wood decomposition by Postia placenta. Fungal Genet Biol 106:1–8. https://doi.org/10.1016/j.fgb.2017.06.003
Zhang J, Presley GN, Hammel KE, Ryu J-S, Menke JR, Figueroa M, Hu D, Orr G, Schilling JS (2016) Localizing gene regulation reveals a staggered wood decay mechanism for the brown-rot fungus Postia placenta. Proc Natl Acad Sci U S A 113:10968–10973. https://doi.org/10.1073/pnas.1608454113
Zhang J, Silverstein KAT, Castano JD, Figueroa M, Schilling JS (2019c) Gene regulation shifts shed light on fungal adaptation in plant biomass decomposers. mBio 10:e02176–e02119. https://doi.org/10.1128/mBio.02176-19
Acknowledgements
The authors gratefully acknowledge Greeley Beck, Susanne Bollmus, Lukas Emmerich, Maria Fredriksson, and Emil Engelund Thybring for constructive comments that improved the manuscript.
Funding
Open access funding enabled and organized by Projekt DEAL. The authors received funding in the frame of the research project CLICKdesign, which is supported under the umbrella of ERA-NET Cofund ForestValue by the Ministry of Education, Science and Sport (MIZS) - Slovenia; The Ministry of the Environment (YM) - Finland; The Forestry Commissioners (FC) - UK; Research Council of Norway (RCN) - Norway; The French Environment & Energy Management Agency (ADEME) and The French National Research Agency (ANR) - France; The Swedish Research Council for Environment, Agricultural Sciences and Spatial Planning (FORMAS), Swedish Energy Agency (SWEA), Swedish Governmental Agency for Innovation Systems (Vinnova) - Sweden; Federal Ministry of Food and Agriculture (BMEL) and Agency for Renewable Resources (FNR) - Germany. ForestValue has received funding from the European Union’s Horizon 2020 research and innovation programme under grant agreement N° 773324.
Author information
Authors and Affiliations
Contributions
CB and GA conceived and designed the research, reviewed literature, analysed data and wrote the manuscript. Both authors read and approved the manuscript.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Ethical approval
This article does not contain any studies with human participants or animals performed by any of the authors.
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
The original online version of this article was revised due to a retrospective Open Access order.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Brischke, C., Alfredsen, G. Wood-water relationships and their role for wood susceptibility to fungal decay. Appl Microbiol Biotechnol 104, 3781–3795 (2020). https://doi.org/10.1007/s00253-020-10479-1
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00253-020-10479-1