Abstract
Carbon nanotubes (CNTs) and carbon microfibers (CMFs) have received significant attention due to their exceptional mechanical and electrical properties, which make them promising materials for various applications. This study introduces a novel approach to integrate CNTs and CMFs into a unified architecture by simultaneously conducting pyrolysis and chemical vapor deposition (CVD). The localized CVD of CNTs on suspended CMFs was achieved by utilizing Fe–Co nanoparticles (NPs) embedded in polyacrylonitrile (PAN) fibers as catalysts. Scanning electron microscopy and elemental analysis confirmed the formation of needle-like carbon structures on the pyrolyzed fiber surface, where carbon gases released from the pyrolyzing PAN fiber acted as the carbon source for the localized CVD. The incorporation of an additional carbon source, such as camphor vapor, significantly enhanced the growth and density of CNTs on the CMF. Various characterization techniques, including transmission electron microscopy, X-ray diffraction, Raman spectroscopy, and Atomic Force Microscopy, were employed to analyse the properties of the synthesized materials. The substantial increase in electrical conductivity upon incorporating CNTs highlights their positive influence on electrical properties and defect reduction. These characterization results highlight the potential applications of the fabricated structures in various fields, including sensors, lithium-ion electrodes, and microfabrication. In addition, the economic advantages of optimizing the process by integrating CVD with pyrolysis were assessed, revealing decreased operation time, lower energy consumption, and reduced chemical costs in comparison to conventional methods involving multiple intermediate processing steps.
Graphical Abstract
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Since their discovery in 1991 [1], carbon nanotubes (CNTs) have undergone significant advancements in research over the past three decades [2]. The exceptional mechanical, electrical, and thermal properties exhibited by CNTs present huge opportunities for the development of electric devices [3, 4], sensors [5], energy harvesting systems [6], and more. Concurrently, carbon microfibers (CMFs) represent a highly interesting one-dimensional material and serve as a crucial component in carbon microelectromechanical systems (C-MEMS) [7, 8], exhibiting unique transport properties. By adopting a hanging geometry, CMFs can fully utilize their functional potential without compromising performance, unlike fibers attached to substrates [9]. Consequently, the integration of CNTs and suspended CMFs within a unified architecture represents a significant advancement in the integration of micro and nano structures, holding the promise of significantly enhancing the performance and properties of C-MEMS-based devices [10, 11]. On the other hand, carbon fiber mats, known for their exceptional conductivity and surface area, are intentionally investigated for various electronic applications [12, 13]. To generate hierarchical structures of CNTs on carbon fibers (CFs), multistep synthesis strategies have been implemented, involving separate pyrolysis and subsequent chemical vapor deposition (CVD) steps to grow CNTs on CFs using a gaseous carbon precursor [14]. In this study, we streamlined the process by incorporating localized CVD during pyrolysis to facilitate the growth of a CNT forest on the surface of suspended CMFs. Importantly, we are in line with the current trend of utilizing thermosetting resins, such as SU-8, as precursors to fabricate high-quality C-MEMS devices, which exhibit exceptional mechanical and electrical properties [15, 16]. Furthermore, we are actively exploring the utilization of polyacrylonitrile (PAN), a widely recognized non-photoresist resin, as a polymer precursor in our research. By employing PAN instead of SU-8, we can achieve high-quality fibers with low electrical resistance and a high graphitic content. The final carbon structure comprises a supportive pattern made from SU-8 and suspended CMFs made from PAN. Remarkably, we observe a particularly high yield of CNTs grown on a catalyst incorporating cobalt ferrite spinel in conjunction with a carbonaceous precursor (camphor). Our integrated process involves using a highly viscoelastic near-field electrospinning ink that incorporates metal nanoparticles (NPs). To assess the advantages of the integrated process, we conduct approximate economic calculations. Based on an analysis of the corresponding properties, we outline potential applications of hierarchical CNTs on CMFs for future investigations.
Experimental
Fabrication of a single polymeric fiber using near-field electrospinning (NFES) and a nanofiber mat using far-field electrospinning (FFES)
Using the negative photoresist SU-8 as a carbon precursor, a supporting structure comprising two rectangular walls and connecting pads was fabricated through photolithography. Subsequently, a single polymeric fiber was suspended over the two SU-8 walls using NFES (Supplementary Sect. 1, Fig. S1). A detailed description of this process can be found in Salazar et al. [17]. Prior to depositing the fiber, the carbon walls were pyrolyzed. The polymeric fiber deposited in this study was PAN fiber, and the preparation details for the PAN solution can be found in the work of George et al. [18]. Before employing NFES, the PAN-based solutions were prepared by mixing with Fe–Co NPs. The PAN solutions and NPs were mixed at 70 °C for 24 h. The molecular weight of PAN obtained from Sigma Aldrich was determined to be 150000 g mol−1. The loading of NPs in the PAN solution ranged from 0 to 10 wt%.
Far-field electrospinning is employed to produce a carbon nanofiber mat. The PAN solution is prepared with 11 wt% PAN polymer in dimethylformamide, supplemented with 5 wt% NPs. The mixture is stirred extensively at 70 °C for 24 h. The electrospinning process is conducted with an operational voltage set at 25 kV, a pump flow rate of 0.01 mL min−1, and a distance of 30 cm between the syringe tip and collector.
Synthesis of metal NPs
The synthesis of the NPs followed a standardized procedure [19]. Initially, 3.5 g of iron (III) nitrate nonahydrate (Fe(NO3)3·9H2O, ACS reagent, ≥ 98%, Sigma Aldrich) and 1.1 g of cobalt (II) nitrate hexahydrate (Co(NO3)2·6H2O, ACS reagent, ≥ 98%, Sigma Aldrich) were combined with 100 mL of ethanol (ACS grade, ≥ 99%). To achieve complete dissolution of the metal salts, the mixture underwent ultrasonication for 1 h. Subsequently, the resulting solution was subjected to continuous stirring at 90 °C until the complete evaporation of ethanol occurred, leaving behind a solid residue. The residual solid was then subjected to baking at 180 °C until it was entirely dry. Finally, thorough grinding of the resulting solid was performed to obtain a fine powder consisting of Fe–Co NPs.
Pyrolysis and local CVD
The functionalization of suspended CMFs with a dense forest of CNTs was conducted using a tube furnace (MTI, mini-CVD tube furnace, OTF-1200X) during the pyrolysis process for carbonizing PAN fiber. Following the established protocol for regular pyrolysis described in [17], the furnace temperature was gradually increased to 900 °C at a rate of 10 °C min−1. Throughout the entire process, a continuous flow of nitrogen gas (N2) at a rate of 40 cm3 min−1 was maintained. At the temperature of 900 °C, camphor was introduced into the reactor via N2 flow for a duration of 1 h. Subsequently, once the combined pyrolysis and CNT growth process were completed, the reactor was passively cooled to ambient temperature. In summary, to attain PAN fiber functionalized with a dense forest of CNTs, the comprehensive process involves the synthesis of NPs, the creation of a polymeric fiber through NFES, and the functionalization of suspended CMF structures with a CNT forest through pyrolysis and local CVD. Each step plays a crucial role in crafting the intricate architecture of the final product. The carbon nanofiber mat, integrated with CNTs, is fabricated using the proposed process. The summary of the work is visually presented in Fig. 1.
Characterization
The properties of the NPs and CMFs were investigated using various characterization techniques. The field emission scanning electron microscopy (FESEM) with an EDX detector and X-ray diffraction (XRD) analysis were performed using the ZEISS Supra 40VP (Germany) and Bruker Advance D8 instruments, respectively. To examine the microstructure and morphology of the functional CNTs, transmission electron microscopy (TEM) was employed using the Fei Taitan 80–300 kV instrument. For TEM sample preparation, carbon fibers were grown on a TEM grid (Silicon nitride, 5 nm) at a temperature of 900 °C for 1 h. Raman characterization was carried out using a Renishaw 1000 spectrometer equipped with an 8.5 mW He–Ne laser operating at 633 nm. The spectra were recorded from 1130 to 2760 cm−1 to assess the defects in the CNT structure, while a low wave number scanning range (115–411 cm−1) was used to evaluate the metallic and semiconducting properties.
To emphasize enhanced electrical conductivity, we assessed the resistance of carbon fiber mats integrated with a dense forest of CNTs. The mats, measuring approximately 0.10 cm × 0.02 cm, were affixed to two gold electrodes. Subsequently, the samples were connected to an electrical circuit measurement system via a feedthrough connection and placed within a 3L stainless steel vacuum chamber. To prevent oxidation, it was crucial to purge the chamber with N2 before the experiment. The chamber pressure was maintained at ambient levels. The control and recording of the carbon mat’s resistance were conducted using an electric source meter (Keithley 2636B), applying a voltage of 0.2 V for a duration of 10 s. The Vista One AFM by Molecular Vista was utilized to analyse the topography of the fiber surface in noncontact mode, covering a scan area of 4 mm × 4 mm. During the measurements, a gold-coated silicon tip was employed. The adhesion characteristics of the fiber surface were investigated by varying the vertical movement of the AFM tip from − 40 to 40 nm. The adhesion properties were assessed based on the force–distance relationship between the tip and the sample surface.
Results
Local CVD of CNTs on suspended CMF
In Fig. 2a, a representative SEM image is presented, depicting the surface of a PAN fiber loaded with Fe–Co NPs prior to pyrolysis. Subsequent pyrolysis of the fiber at 900 °C, even in the absence of an intentional gaseous carbon source, results in surface roughening when compared to the polymer fiber pre-pyrolysis (refer to Fig. 2b). Notably, needle-like growths can be observed on the surface of the pyrolyzed fiber. Elemental analysis using SEM–EDX reveals that these needles consist of more than 81 at% carbon (EDX spectra are provided in Supplementary Sect. 2, Fig. S2). The remaining elements detected are Co, Fe, and O.
The growth of these new carbon structures necessitates a carbon source, and during the pyrolysis of the PAN fiber depicted in Fig. 2b, no additional carbon source was introduced into the reactor. Consequently, the feasible carbon precursors in this scenario are derived from the pyrolyzing PAN fiber itself. The PAN polymer, composed of interconnected polyethylene chains via nitrile groups (—CN), undergoes fragmentation when exposed to high temperatures. This fragmentation releases carbon gases like methane, carbon dioxide (CO2), and carbon monoxide (CO), which are vital for the localized CVD process [20,21,22]. The CVD process, facilitated by these carbon gases, leads to the formation of carbon nanostructures.
Furthermore, SEM images of the PAN fibers post-pyrolysis reveal a significant reduction in fiber volume, ranging from 21 to 55 vol% (Supplementary Sect. 3, Fig. S3). This observed shrinkage in fiber volume can be attributed to the release of gaseous components, such as water, hydrogen, carbon monoxide (CO), carbon dioxide (CO2), etc., at elevated temperatures. The emission of these volatile substances from the PAN fibers during pyrolysis serves as a crucial source of precursors for the localized CVD, leading to the formation of small needle-like structures on the fiber surface. The term “Local CVD” refers to the localized deposition of this forest of CNTs solely on the CMF, without contaminating the entire carbon chip. To facilitate the expansion of carbon nanostructures, experiments were undertaken to introduce camphor vapor as an additional carbon source. The outcomes revealed a substantial growth of CNTs on the CMF, as illustrated in Fig. 2c. The microstructure and morphology of the CNT functional material were analyzed using TEM characterization. Figure 2d displays a representative TEM micrograph of the CNTs, revealing an entangled mesh of CNTs with a significant size distribution. Examination of numerous TEM images indicates that the CNT diameters range from 16 to 245 nm, while the lengths can extend up to 40 µm, resulting in aspect ratios reaching up to 800. To prevent contamination on the carbon electrodes, we reduced the amount of dimethylformamide solvent from 89 to 85 wt%, while also increasing the applied voltage during electrospinning from 110 to 300 V. A small-size syringe needle with a 30G needle was used. Figure 2e illustrates that the CNTs were exclusively grown on the CMF without contaminating the silicon substrate.
The XRD profiles of the PAN fiber pyrolyzed without camphor and the PAN fiber laden with Fe–Co NPs pyrolyzed in the presence of an external carbon source are presented in Fig. 3a. The introduction of camphor, as observed, induces abundant CVD of CNTs. The XRD pattern of the carbonized PAN fiber, as depicted in Fig. 3a, exhibits diffraction peaks at 20.96° and 25.04°, corresponding to the (010) and (002) crystallographic planes of the graphite structure [23]. Notably, with the substantial growth of CNTs, two prominent additional diffraction peaks emerge at 2θ = 9.13° and 28.96°, corresponding to the (110) and (002) planes of CNTs, respectively [24, 25]. The sharpness of these peaks indicates the high crystallinity of the deposited CNTs.
The powder XRD pattern of Fe–Co NPs is presented in Fig. 3b, revealing the presence of three primary phases in the catalyst powder: spinel ferrite (CoFe2O4), β-Fe2O3 and Co hydroxide (Co(OH)2). The XRD peaks obtained at 2θ values of 18.6°, 30.5°, 35.6°, and 37.5° correspond to the (111), (022), (113), and (222) crystallographic planes of pure CoFe2O4 spinel (JCPDS card no. 22-1086). The reflections observed at 2θ values of 13.2°, 20.0°, and 28.5° are attributed to the (002), (010), and (013) planes, respectively, of the pristine β-Fe2O3 phase (No.1214964). Furthermore, the peaks observed at 19.1°, 32.6°, and 38.0° correspond to the (001), (010), and (011) planes, respectively, of the standard Co(OH)2 phase (No.1713580). It is highly believable that the nature of the original catalyst powder significantly influences the properties of CNTs during the pyrolysis/CVD process.
Raman analysis of CMFs
In order to assess the potential applications of the hierarchical material consisting of CNTs on CMF platforms, Raman spectra were collected to analyse the nanostructures, relative mechanical strengths, and electronic properties. Figure 4a illustrates the distinct D-band and G-band Raman characteristics of carbon structures at approximately ⁓1331 and ⁓1576 cm−1, respectively, observed in both pristine CMFs and CMFs with CNTs. However, the G-peak of pristine CMFs appears broader and less intense, while the G-peak of hierarchical CMFs is sharper and higher. The shape of the G-peaks has changed due to the presence of graphene sheets in the carbon material mixture [26]. The original CMFs exhibit an ID/IG ratio of 1.09 (Fig. 4a), indicating a high degree of disorder in the hexagonal carbon lattice and the presence of numerous defects such as heptagons, pentagons, and vacancies [27]. Conversely, the Raman data of CNTs grown using Fe–Co NPs embedded in PAN fiber show an ID/IG ratio closer to 1 (around 1.01), indicating the formation of higher quality CNTs with a high degree of symmetry. The presence of CNTs contributes to an 8% reduction in the original ID/IG ratio. To further investigate the nature of the CNTs, the RBM spectra of CNTs grown using Fe–Co NPs embedded in CMFs were examined and are presented in Fig. 4b. The RBM spectrum reveals two distinct peaks at 217 cm−1 and 282 cm−1.
The mechanical strength of CMFs is closely associated with their nanostructures. We examined the structural improvement of CMFs by varying the content of embedded Fe–Co NPs within the host fiber. Figure 4c displays two shifts in the adsorption wavelength as the concentration of Fe–Co NPs in CMFs changes from 0 to 3 wt%. The D-peak undergoes a red shift from 1349 to 1331 cm−1, while the G-peak experiences a blue shift from 1560 to 1588 cm−1.
Examination of electrical conductivity and surface properties
To underscore the potential applications of hierarchical carbon fiber structures in various scenarios, we conducted an investigation into the resistance of a carbon fiber mat subjected to a 0.2 V application for 10 s. As shown in Fig. 5a, the standard carbon fiber mat is attached to gold electrodes and connected to the circuit system. Figure 5b illustrates the enhanced electrical properties of hierarchical carbon fiber mat structures compared to pristine carbon fiber mat, with resistance significantly reduced from 536 kΩ to 58 Ω.
The improvement of surface properties was investigated by examining adhesion properties during AFM tip scanning on fiber surfaces. Figure 6a and b illustrates the surface topography of pristine CMFs and PAN fibers functionalized with a dense forest of CNTs. Figure 6c presents the adhesion force between the AFM tip and the surface of pristine CMFs. The X-axis represents the force converted to an electrical signal in millivolts (mV), while the Y-axis indicates the vertical movement of the AFM tip during surface scanning. Figure 6d displays the adhesion force between the AFM tip and the PAN fiber functionalized with a dense forest of CNTs.
Discussions
In a previous study [28], we observed the local deposition of carbon nanomaterials on pyrolyzing SU-8 pillars, even in the absence of intentionally introduced gaseous carbon sources. We observed significant carbon nano growth beyond the small amount of initially embedded CNTs. In this research, we validate our hypothesis that the local emission of gaseous carbon vapors during the pyrolysis of SU-8 and CFs is responsible for the additional growth of carbon nanostructures.
Raman characterization of our samples indicates that their quality, as measured by the ID/IG ratio, is comparatively superior to CNTs synthesized using alternative ferrite spinel catalysts such as cobalt ferrite and iron nanoparticles, which exhibit ID/IG ratios of approximately 1.9 [29] and 1.89 [30], respectively. For nickel ferrite catalysts, this ratio is reported to be around 0.94 [31]. Importantly, the red shift of the D-peak can be attributed to the development of covalent crosslinking between the graphite planes, which prevents the slipping of carbon planes under shearing forces during tensile experiments. The increased amount of crosslinking implies enhanced tensile strength of the host CMFs [32]. Additionally, the blue shift of the G-peak and the narrower peaks indicate a higher ordered structure, suggesting a higher tensile modulus [32]. Although we have not measured the mechanical properties in this study, the reinforcing effect of Fe–Co NPs on CMFs provides strong evidence of the quality of our samples in terms of mechanical properties. The existence of features in the RBM region of Raman spectra suggests that the CNTs exhibit metallic and conductive characteristics [33]. Moreover, the reported Young’s modulus and electrical conductivity of the host CFs fall within the ranges of 100–400 GPa and 103–107 S m−1, respectively [15, 34]. Therefore, we anticipate that the addition of CNT material will enhance the performance of existing CMFs. By comparing the Raman characteristics of the current hierarchical CMFs with other previously studied CFs, we can gain initial insights into their potential applications. The suspended hierarchical CMFs hold promise for sensor applications [35, 36] due to their ultra-sensitivity and fast response times [37]. With an ID/IG ratio around 1 and CNT diameters ranging from 16 to 245 nm, this material is suitable for fabricating lithium-ion electrodes [38]. Furthermore, the high aspect ratio CNTs, reaching up to 800, provides a large surface area that meets the demands of microfabrication in the C-MEMS system [39, 40].
The electrical improvement is attributed to the presence of CNTs, which enhance conductivity and reduce defects [41]. This outcome is further supported by the Raman results. Additionally, the electrical enhancement can be ascribed to the expanded surface area, facilitating more contact points between conductive carbon fibers [42]. In comparison to the force–distance curve in Fig. 6c, the force–distance relationship in Fig. 6d exhibits more peaks in both the approach and retract curves. These peaks seem to correlate with the surface roughness of the hierarchical structure observed in Fig. 6b. The variation in the shape of the force–distance curve reflects interactions between the tip and different regions of the sample surface [43]. Additionally, the additional peaks could be attributed to the unique conductivity properties of CNTs, leading to distinct electrostatic interactions between the AFM tip and the CNTs [44]. The diverse improvements observed in hierarchical carbon fiber structures, such as enhanced conductivity, reduced resistance, and unique surface properties, position them as versatile materials with applications in various electronic devices. The enhanced conductivity and reduced defects in the hierarchical structures address challenges related to conductivity and charge transport for electric applications [45]. Additionally, the expanded surface area and improved electrical characteristics can serve as components in microdevices and electronic circuits, contributing to the development of efficient and high-performance electronic systems [46]. The CMF structure significantly influences the growth and properties of the CNTs. Detailed investigations are described in Supplementary Sect. 4. This study primarily focuses on the preparation and characterization technique of an integrated micro/nano carbon structure using a novel method that combines subtractive (pyrolysis) and additive (deposition) processes. Based on these findings, a detailed investigation of the applications of the CNT forest on CMF platforms warrants a separate investigation in the future.
To assess the economic benefits of our integrated process combining CVD with pyrolysis, we conducted a preliminary comparison with the current technique used for decorating CNTs using embedded catalyst NPs within the CF matrix. The conventional CNT growing procedure, commonly found in literature [47, 48], involves multiple high-temperature thermal treatment stages in an inert or reductive atmosphere to reduce metallic sites and create particles. In the final step, CVD is performed to promote CNT growth on the CFs. The stringent treatment conditions can significantly diminish the mechanical and electrical performance of the resulting hierarchical fibers. Moreover, the catalyst precursors used in most cases are noble metals or high-cost materials such as Palladium (II) acetate (Pd(CH3CO2)2·xH2O) [49] or Nickel (II) acetate (Ni(CH3CO2)2·xH2O) [50]. Through screening calculations, our integrated process has been shown to reduce the operation time by 81% to 90%. The energy consumption and carrier gas usage are less than 3% and 1%, respectively. Further details of this calculation can be found in Supplementary Sect. 5. Thanks to the high activity of Fe–Co NPs, we eliminate the need for a reduction gas such as hydrogen, which requires stringent safety conditions. Additionally, our chemical compound cost is 1.7 USD/1 g, while other processes range from 1.2 to 7 USD/1 g (Supplementary Sect. 6). The preparation of Fe–Co NPs can be scaled up for industrial manufacturing using conventional equipment such as precipitation, stirring, and grinding devices. The raw materials, Fe and Co, are readily available as nitrate salts, and ethanol serves as the solvent. These chemicals are abundant and commonly used in the industry [51, 52]. The operating temperature range is not severe, typically between 70 and 200 °C at atmospheric pressure. Furthermore, we avoid the use of base or acid solutions, which can cause corrosion, thereby eliminating the need for resistance materials in the equipment. Importantly, our process does not generate harmful waste residues, and ethanol vapor can be easily recycled through a simple condensation process.
The characterization results suggest potential applications for hierarchical CMF structures with CNTs in sensors and lithium-ion electrodes, offering advantages such as ultra-sensitivity and fast response times. The hierarchical CMF structures also demonstrate suitability for microfabrication in C-MEMS systems. The enhanced electrical conductivity, reduced resistance, and distinctive surface properties position hierarchical carbon fiber structures favorably for a range of electronic applications. Adhesion force measurements, reflecting surface roughness and electrostatic interactions, further underscore these advantages. The integrated process, combining CVD with pyrolysis, demonstrates economic benefits over traditional multi-step processes, highlighting its potential for large-scale, cost-effective industrial manufacturing.
Conclusion
In conclusion, this study successfully demonstrates the fabrication of hierarchical CMF structures decorated with CNTs by simultaneously conducting pyrolysis and CVD. The local CVD of CNTs on suspended CMFs was achieved by utilizing Fe–Co NPs embedded in PAN fibers as catalysts. The SEM and elemental analysis revealed the formation of needle-like carbon structures on the pyrolyzed fiber surface, with carbon gases released from the pyrolyzing PAN fiber serving as the carbon source for localized CVD. The presence of an additional carbon source, such as camphor vapor, significantly enhanced the growth and density of CNTs on the CMF. XRD analysis confirmed the crystalline nature of the deposited CNTs and identified the phases of the catalyst powder. TEM characterization revealed entangled CNT mesh structures with varying diameters and lengths, indicating the successful growth of CNTs on CMFs. Raman analysis provided insights into the nanostructures and mechanical strengths of the hierarchical CMFs. The presence of CNTs resulted in sharper and higher G-band peaks, indicating an enhancement in structural order. The ID/IG ratio of the CNTs suggested higher-quality CNTs compared to other catalysts. The mechanical strength of CMFs improved with the addition of Fe–Co NPs, as evidenced by shifts in the D-peak and G-peak wavelengths and narrower peak widths. The RBM spectra of CNTs indicated metallic and conductive characteristics. The characterization results indicate potential applications in sensors and lithium-ion electrodes. The suspended configuration of the hierarchical CMFs provided advantages for ultra-sensitivity, fast response times, and microfabrication in C-MEMS systems. Additional enhancements, including improvements in conductivity, resistance reduction, and distinctive surface properties, have been thoroughly investigated to elucidate the advantages of hierarchical carbon fiber structures. Adhesion force measurements, revealing additional peaks in the force–distance relationship, indicate correlations with surface roughness and distinct electrostatic interactions. The significant reduction from 536 kΩ to 58 Ω upon incorporating CNTs underscores their positive impact on electrical conductivity and defect reduction. Collectively, the enhanced electrical conductivity and surface properties position hierarchical carbon fiber structures as promising candidates for a wide array of electronic applications. Furthermore, optimizing the process by integrating CVD with pyrolysis demonstrated economic benefits compared to traditional processes involving multiple intermediate steps. The reduction in operation time, energy consumption, and carrier gas usage, along with the elimination of costly catalyst precursors and the need for reduction gases, presented significant advantages. Overall, this study provides a promising approach for the efficient fabrication of hierarchical CMFs decorated with CNTs. The presented integrated process shows great potential for industrial manufacturing with its simplified and cost-effective methodology, making it a viable option for large-scale production.
Abbreviations
- CVD:
-
Chemical vapor deposition
- CNTs:
-
Carbon nanotubes
- PAN:
-
Polyacrylonitrile
- CNFs:
-
Carbon nanofibers
- CMF:
-
Carbon microfiber
- C-MEMS:
-
Carbon microelectromechanical system
- NPs:
-
Nanoparticles
- Fe–Co:
-
Cobalt ferrite
- NFES:
-
Near-field electrospinning
References
Iijima S (1991) Helical microtubules of graphitic carbon. Nature 354(6348):56–58. https://doi.org/10.1038/354056a0
Jyoti J, Singh BP (2021) A review on 3D graphene–carbon nanotube hybrid polymer nanocomposites. J Mater Sci 56(31):17411–17456. https://doi.org/10.1007/s10853-021-06370-7
Li Y, Wu J, Chopra N (2015) Nano-carbon-based hybrids and heterostructures: progress in growth and application for lithium-ion batteries. J Mater Sci 50(24):7843–7865. https://doi.org/10.1007/s10853-015-9429-7
Thapa A, Jungjohann KL, Wang X, Li W (2020) Improving field emission properties of vertically aligned carbon nanotube arrays through a structure modification. J Mater Sci 55(5):2101–2117. https://doi.org/10.1007/s10853-019-04156-6
Ma H, Gao Y, Liu W, Farha FI, Zhang K, Guo L, Xu F (2021) Light-weight strain sensor based on carbon nanotube/epoxy composite yarn. J Mater Sci 56(23):13156–13164. https://doi.org/10.1007/s10853-021-06146-z
Das S, Sa K, Alam I, Mahanandia P (2019) Enhancement of photocurrent in Cu2ZnSnS4 quantum dot-anchored multi-walled carbon nanotube for solar cell application. J Mater Sci 54(11):8542–8555. https://doi.org/10.1007/s10853-019-03467-y
Forouzanfar S, Pala N, Madou M, Wang C (2021) Perspectives on C-MEMS and C-NEMS biotech applications. Biosens Bioelectron 180:113119. https://doi.org/10.1016/j.bios.2021.113119
Zhang L, Aboagye A, Kelkar A, Lai C, Fong H (2014) A review: carbon nanofibers from electrospun polyacrylonitrile and their applications. J Mater Sci 49(2):463–480. https://doi.org/10.1007/s10853-013-7705-y
Machín A, Fontánez K, Arango JC, Ortiz D, De León J, Pinilla S, Márquez F (2021) One-dimensional (1d) nanostructured materials for energy applications. Materials 14(10):2609. https://doi.org/10.3390/ma14102609
Pramanick B, Meyn MM, Shrivastava K, Martinez-Chapa SO, Madou MJ (2018) Recent trends in the processing and applications of carbon nanotubes and C-MEMS-based carbon nanowires nanomaterials and their applications (pp. 97–141): Springer. https://doi.org/10.1007/978-981-10-6214-8¬-4
Muhammed F, Lavaggi T, Advani S, Mirotznik M, Gillespie JW (2021) Influence of material and process parameters on microstructure evolution during the fabrication of carbon–carbon composites: a review. J Mater Sci 56(32):17877–17914. https://doi.org/10.1007/s10853-021-06401-3
Yang S, Cheng Y, Xiao X, Pang H (2020) Development and application of carbon fiber in batteries. Chem Eng J 384:123294. https://doi.org/10.1016/j.cej.2019.123294
Zhang X, Lu W, Zhou G, Li Q (2020) Understanding the mechanical and conductive properties of carbon nanotube fibers for smart electronics. Adv Mater 32(5):1902028. https://doi.org/10.1002/adma.201902028
Qiu Y, Li G, Hou Y, Pan Z, Li H, Li W, Zhang Y (2015) vertically aligned carbon nanotubes on carbon nanofibers: a hierarchical three-dimensional carbon nanostructure for high-energy flexible supercapacitors. Chem Mater 27(4):1194–1200. https://doi.org/10.1021/cm503784x
Canton G, Do T, Kulinsky L, Madou M (2014) Improved conductivity of suspended carbon fibers through integration of C-MEMS and electro-mechanical spinning technologies. Carbon 71:338–342. https://doi.org/10.1016/j.carbon.2014.01.009
Lim Y, Kim S, Kwon YM, Baik JM, Shin H (2018) A highly sensitive gas-sensing platform based on a metal-oxide nanowire forest grown on a suspended carbon nanowire fabricated at a wafer level. Sens Actuators B Chem 260:55–62. https://doi.org/10.1016/j.snb.2017.12.167
Salazar A, Perez-Gonzalez VH (2020) Reduction of electrical resistance on suspended glassy carbon nanofibers by localized thermal annealing. Mater Today Proc. https://doi.org/10.1016/j.matpr.2020.08.300
George D, Garcia A, Pham Q, Perez MR, Deng J, Nguyen MT, Liu C (2020) Fabrication of patterned graphitized carbon wires using low voltage near-field electrospinning, pyrolysis, electrodeposition, and chemical vapor deposition. Microsyst Nanoeng 6(1):1–12. https://doi.org/10.1038/s41378-019-0117-7
Lassoued A, Dkhil B, Gadri A, Ammar S (2017) Control of the shape and size of iron oxide (α-Fe2O3) nanoparticles synthesized through the chemical precipitation method. Results physics 7:3007–3015. https://doi.org/10.1016/j.rinp.2017.07.066
Lee TS, Witting P (2016) Computational fluid dynamics (CFD) analysis for off-gas mixing and ventilation inside carbonization furnace during PAN-based carbon fiber manufacturing. Paper presented at the SAMPE 2016 conference proceeding
Li Z, Chen J, Zhang X, Li Y, Fung KK (2002) Catalytic synthesized carbon nanostructures from methane using nanocrystalline Ni. Carbon 40(3):409–415. https://doi.org/10.1016/S0008-6223(01)00117-8
Kim GM, Lim W-G, Kang D, Park JH, Lee H, Lee J, Lee JW (2020) Transformation of carbon dioxide into carbon nanotubes for enhanced ion transport and energy storage. Nanoscale 12(14):7822–7833. https://doi.org/10.1039/C9NR10552B
Bucknum MJ, CEA, (2006) The carbon allotrope hexagonite and its potential synthesis from cold compression of carbon nanotubes. J Chem Theory Comput 2(3):775–781. https://doi.org/10.1021/ct060003n
Allaf RM, Rivero IV, Spearman SS, Hope-Weeks LJ (2011) On the preparation of as-produced and purified single-walled carbon nanotube samples for standardized X-ray diffraction characterization. Mater Charact 62(9):857–864. https://doi.org/10.1016/j.matchar.2011.06.005
Doroodmand M, Sobhani S, Ashoori A (2012) Sulfonated multiwalled carbon nanotubes (MWCNTs) as a new, efficient, and recyclable heterogeneous nanocatalyst for the synthesis of amines. Can J Chem 90(8):701–707. https://doi.org/10.1139/v2012-049
Schuepfer DB, Badaczewski F, Guerra-Castro JM, Hofmann DM, Heiliger C, Smarsly B, Klar PJ (2020) Assessing the structural properties of graphitic and non-graphitic carbons by Raman spectroscopy. Carbon 161:359–372. https://doi.org/10.1016/j.carbon.2019.12.094
Hoa LTM (2018) Characterization of multi-walled carbon nanotubes functionalized by a mixture of HNO3/H2SO4. Diam Relat Mater 89:43–51. https://doi.org/10.1016/j.diamond.2018.08.008
Wang C, Zaouk R, Madou M (2006) Local chemical vapor deposition of carbon nanofibers from photoresist. Carbon 44(14):3073–3077. https://doi.org/10.1016/j.carbon.2006.05.007
Ateia EE, Morsy M, Ahmed EM, Soliman FS (2020) Growth and characterization of carbon nanotubes over CoFe2O4–MgO catalysts at different temperatures. Fuller Nanotub Carbon Nanostruct 28(10):815–822. https://doi.org/10.1080/1536383X.2020.1767078
Bajorek A, Szostak B, Dulski M, Greneche JM, Lewińska S, Liszka B, Pawlyta M, Ślawska-Waniewska A (2022) A comprehensive study of Pristine and calcined f-MWCNTs functionalized by Nitrogen-containing functional groups. Materials 15(3):977. https://doi.org/10.3390/ma15030977
Javed H, Islam M, Mahmood N, Achour A, Hameed A, Khatri N (2016) Catalytic growth of multi-walled carbon nanotubes using NiFe2O4 nanoparticles and incorporation into epoxy matrix for enhanced mechanical properties. J Polym Eng 36(1):53–64. https://doi.org/10.1515/polyeng-2015-0137
Qian X, Wang X, Zhong J, Zhi J, Heng F, Zhang Y, Song S (2019) Effect of fiber microstructure studied by Raman spectroscopy upon the mechanical properties of carbon fibers. J Raman Spectrosc 50(5):665–673. https://doi.org/10.1002/jrs.5569
Trushkevych O, Collings N, Hasan T, Scardaci V, Ferrari A, Wilkinson T, Johnson B (2008) Characterization of carbon nanotube–thermotropic nematic liquid crystal composites. J Phys D Appl Phys 41(12):125106. https://doi.org/10.1088/0022-3727/41/12/125106
Canton G (2014) Development of electro-mechanical spinning for controlled deposition of carbon nanofibers. PhD dissertation, University of California, Irvine
Monea BF, Ionete EI, Spiridon SI, Ion-Ebrasu D, Petre E (2019) Carbon nanotubes and carbon nanotube structures used for temperature measurement. Sensors 19(11):2464. https://doi.org/10.3390/s19112464
Seo J, Lim Y, Shin H (2017) High-performance hydrogen sensor based on an array of single suspended carbon nanowires selectively functionalized with palladium nanoparticles. Paper presented at the 2017 IEEE 30th international conference on micro electro mechanical systems (MEMS). https://doi.org/10.1109/MEMSYS.2017.7863597
Umar A, Rahman MM, Hahn Y-B (2009) Ultra-sensitive hydrazine chemical sensor based on high-aspect-ratio ZnO nanowires. Talanta 77(4):1376–1380. https://doi.org/10.1016/j.talanta.2008.09.020
Kobashi K, Ata S, Yamada T, Futaba DN, Okazaki T, Hata K (2019) Classification of commercialized carbon nanotubes into three general categories as a guide for applications. ACS Appl Nano Materials 2(7):4043–4047. https://doi.org/10.1021/acsanm.9b00941
Hanein Y (2010) Carbon nanotube integration into MEMS devices. Physica status solidi (b) 247((11–12)):2635–2640. https://doi.org/10.1002/pssb.201000109
Zang X, Zhou Q, Chang J, Liu Y, Lin L (2015) Graphene and carbon nanotube (CNT) in MEMS/NEMS applications. Microelectron Eng 132:192–206. https://doi.org/10.1016/j.mee.2014.10.023
Zhang S, Hao A, Nguyen N, Oluwalowo A, Liu Z, Dessureault Y, Liang R (2019) Carbon nanotube/carbon composite fiber with improved strength and electrical conductivity via interface engineering. Carbon 144:628–638. https://doi.org/10.1016/j.carbon.2018.12.091
Zhang Y, Wang L, Xu H, Cao J, Chen D, Han W (2020) 3D chemical cross-linking structure of black phosphorus@ CNTs hybrid as a promising anode material for lithium ion batteries. Adv Func Mater 30(12):1909372. https://doi.org/10.1002/adfm.201909372
Jones R, Hodges C (2004) Applications of atomic force microscopy to granular materials: interparticle forces in air. In: Joseph Antony S, Hoyle W, Ding Y (eds) Granular Materials, RSC, London, pp 229–254
Chaw K, Manimaran M, Tay FE (2005) Role of silver ions in destabilization of intermolecular adhesion forces measured by atomic force microscopy in Staphylococcus epidermidis biofilms. Antimicrob Agents Chemother 49(12):4853–4859. https://doi.org/10.1128/aac.49.12.4853-4859.2005
Zhao Q, Zhang K, Zhu S, Xu H, Cao D, Zhao L, Yin W (2019) Review on the electrical resistance/conductivity of carbon fiber reinforced polymer. Appl Sci 9(11):2390. https://doi.org/10.3390/app9112390
Vomero M, Gueli C, Zucchini E, Fadiga L, Erhardt JB, Sharma S, Stieglitz T (2020) Flexible bioelectronic devices based on micropatterned monolithic carbon fiber mats. Adv Mater Technol 5(2):1900713. https://doi.org/10.1002/admt.201900713
Chen Y, Li X, Park K, Song J, Hong J, Zhou L, Goodenough JB (2013) Hollow carbon-nanotube/carbon-nanofiber hybrid anodes for Li-ion batteries. J Am Chem Soc 135(44):16280–16283. https://doi.org/10.1021/ja408421n
Hou H, Reneker DH (2004) Carbon nanotubes on carbon nanofibers: a novel structure based on electrospun polymer nanofibers. Adv Mater 16(1):69–73. https://doi.org/10.1002/adma.200306205
Lai C, Guo Q, Wu X-F, Reneker DH, Hou H (2008) Growth of carbon nanostructures on carbonized electrospun nanofibers with palladium nanoparticles. Nanotechnology 19(19):195303. https://doi.org/10.1088/0957-4484/19/19/195303
Alali KT, Liu J, Aljebawi K, Liu Q, Chen R, Yu J, Wang J (2019) 3D hybrid Ni-Multiwall carbon nanotubes/carbon nanofibers for detecting sarin nerve agent at room temperature. J Alloy Compd 780:680–689. https://doi.org/10.1016/j.jallcom.2018.11.317
Nicholls D (2013) The chemistry of iron, cobalt and nickel: comprehensive inorganic chemistry, vol 24. Elsevier
Khodakov AY, Chu W, Fongarland P (2007) Advances in the development of novel cobalt Fischer–Tropsch catalysts for synthesis of long-chain hydrocarbons and clean fuels. Chem Rev 107(5):1692–1744. https://doi.org/10.1021/cr050972v
Acknowledgements
The authors thankfully acknowledge the supports provided by CONACYT grant for PhD. studies. The authors are thankful to the Manufacturing Laboratory of the Center for Innovation in Design and Technology (CIDyT), the Laboratory of Nano and Microstructures at Tecnologico de Monterrey, Monterrey, Mexico; the FIME-CIIDIT Laboratory at Universidad Autónoma de Nuevo León, Monterrey, Mexico. The authors are also grateful to Dr. Derosh George, Princeton University for the preparation of the electrospun solution. We express our gratitude to Kevin Armando Rodríguez Mireles and Professor Irvin Fernando Guzmán González for their assistance in the AFM characterization process.
Funding
This work was financially supported by CONACYT grant for PhD. studies.
Author information
Authors and Affiliations
Contributions
SN contributed to methodology, conceptualization, investigation, analysis, writing, and initial draft; CB F contributed to supervision, methodology, conceptualization, technical assistance and support for nanoparticles preparation, CVD, sample preparation, writing, review and editing; MJ M contributed to supervision, conceptualization, writing, review and editing; MR helped in supervision, conceptualization, writing, review and editing; AS done supervision, technical assistance and support for near field electrospinning, photolithography, review and editing; RV helped in technical assistance and support for sem characterization; IA helped in raman measurements and visualization. NO done visualization and review. AT-C helped in technical assistance and support for tem characterization; SO M contributed to supervision, project administration and review. All authors have given approval to the final version of the manuscript.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no competing financial interest.
Additional information
Handling Editor: Annela M. Seddon.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Nguyen, S., Flores, C.B., Madou, M.J. et al. Synthesis and characterization of hierarchical suspended carbon fiber structures decorated with carbon nanotubes. J Mater Sci 59, 2893–2906 (2024). https://doi.org/10.1007/s10853-024-09359-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-024-09359-0