Abstract
Two principally novel chromophores A, B based on fluorene electron donor were synthesized and explored by 1H NMR, 13C NMR, and MS spectra. The delocalized energy levels have been estimated by UV–Vis absorption spectra. The principal innovation consists in modification by addition of amino group. The titled materials have demonstrated a high solubility in common organic solvents, good compatibility with polymers. The maximally achieved electro-optic efficiency of the poled film possessing 25 wt% of A doped in PMMA (25 wt% A/PMMA) achieved a value of 18 pm/V at wavelength 1310 nm, and 25 wt% B/PMMA possessed an electrooptical coefficient equal to 43 pm/V. This one open a perspective of their direct application in optoelectronic telecommunication devices for laser light modulation.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
The design and search of novel promising chromophores materials for the optoelectronic applications is very important for modern organic materials science engineering due to their promising parameters with respect to high-speed and broadband telecommunication technology [1,2,3,4,5,6]. For today different materials are just used for the nonlinear optical and electrooptical laser modulators [7,8,9,10,11,12,13].
However, for wide applications, one of the restraining factor consists in reliable production of excellent organic electro-optic (EO) modulator materials to develop NLO chromophores with relatively high first-order hyperpolarizability (β) [14,15,16], good thermal, photochemical stabilities as well as good solubility and compatibility with the polymer matrix.
To obtain sufficiently high EO activity and suppress the undesirable dipole–dipole interactions among the chromophores, an appropriate molecular design has been made using the conjugated push–pull molecules. Many efforts have been made here to design and synthesize novel NLO chromophores, searching the NLO molecules with higher electrooptical coefficients (r33) [15,16,17]. The previous efforts for the NLO chromophores were mainly focused on the construction of the extended charge transfer pi-electron bridges and electron acceptors [16,17,18,19]. However, the electron donors, playing crucial role for NLO chromophores, are still less explored and vry promising may be traditional alkyl and aryl anilines which are suitable electron donors and for these goals they are just widely studied [20, 21]. Following the mentioned above one can conclude that design and fabrication of novel conjugated groups with stronger electron-donating ability is still extremely desirable.
In this report, fluorene with embedded amino groups have been utilized as electron donor. Two chromophores with these donors were fabricated. Additionally extended and larger peripheral modified groups were added to chromophores to enhance their EO efficiencies. These material demonstrate high solubility in traditional organic solvents, sufficiently good compatibility with polymers, and high EO tensor coefficients for the poled films. 1H-NMR and 13C-NMR analyses were carried out to demonstrate the potential of these chromophores. Thermal stability, photophysical features, DFT calculations and EO activities of these chromophores have been complexely explored.
2 Experimental
2.1 Materials and instruments
All the chemicals are commercially available and have been used without additiaonol purification. N,N-dimethylformamide (DMF) was distilled over calcium hydride and stored over molecular sieves (pore size 3 Å).
2-Dicyanomethylene-3-cyano-4-methyl-2,5-dihydrofuran (TCF) and 2-(3-cyano-4-methyl-5-phenyl-5-(trifluoromethyl)furan-2(5H)-ylidene)malononitrile (CF3-Ph-TCF) were synthesized similarly to the described in the to the references [22, 23]. TLC analyses were performed for 0.25 mm thick pre-coated silica plates and they have been visualized using UV light. Chromatography of silica gel was done on Kieselgel (200–300 mesh). and 1H NMR spectra were measured by Advance Bruker 400 M (400 MHz) NMR spectrometer (tetramethylsilane as internal reference). UV–Vis spectra were done using Cary 5000 photo spectrometer. TGA and DSC were monitored by TA-instrument Q50 and Q10 with a heating rate of 10 K min−1 under N2, respectively.
2.2 Synthesis procedure
2.2.1 Compound 2
A mixture of 1 (4.22 g, 20.0 mmol), iron powder (3.35 g, 60.0 mmol, 3.0 equiv.) and ammonia chloride (2.14 g, 40.0 mmol, 2.0 equiv.) in aqueous ethanol (140 mL of alcohol and 40 mL of water) was refluxed in argon atmosphere. After complete transformation of the initial compound (about 5 h) upon inspection by TLC, the reaction mixture was treated with 70 mL of aqueous saturated sodium bicarbonate and filtered. After removing the ethanol from the filtrate obtained under reduced pressure, the resultant mixture was filtered. The solid obtained was then washed with water (3 × 30 mL) and dried in vacuum atmosphere at 50 °C. The crude product was used without further purification for the next step. A solution of the crude product, bromobutane (13.7 g, 100 mmol) and sodium tert-butoxide (9.6 g 100 mmol) in DMF (50 ml) for 8 h, and then poured into distilled water (250 mL). ethyl acetate (3 × 50 mL) was used to extract the product. The extracts were combined, washed with saturated NaCl solution, dried over anhydrous magnesium sulfate. After removal of the solvents, the product was purified by column chromatography and obtained as a syrup (6.01 g, yield: 74%). 1H NMR (400 MHz, CDCl3) δ 7.83 (dd, J = 7.9, 3.0 Hz, 2H), 7.55 (dd, J = 17.7, 7.4 Hz, 2H), 7.43 (t, J = 7.4 Hz, 1H), 6.96 (d, J = 11.9 Hz, 2H), 3.69–3.59 (m, 4H), 2.34–2.19 (m, 4H), 1.99–1.87 (m, 4H), 1.68 (dd, J = 14.9, 7.4 Hz, 4H), 1.43 (dd, J = 14.7, 7.3 Hz, 4H), 1.27 (t, J = 7.4 Hz, 6H), 1.03 (dd, J = 16.6, 9.1 Hz, 10H). 13C NMR (101 MHz, CDCl3) δ 152.41, 149.93, 148.42, 142.33, 129.80, 126.85, 124.96, 122.66, 120.66, 118.29, 111.29, 106.92, 54.92, 51.55, 40.89, 29.91, 26.28, 23.47, 20.74, 14.34, 14.12. ESI–MS (C29H43N): calcd: 405.34; found: [M + 1]+, 406.34.
2.2.2 Compound 3
To a solution of compound 2 (5.0 g, 12.3 mmol) in anhydrous chloroform (50 mL) at ambient temperature was successively added anhydrous DMF (1.0 mL, 12.3 mmol) and POCl3 (1.7 mL, 18.5 mmol), and the mixture was refluxed during one night. After hydrolysis for 2 h under vigorous stirring at ambient temperature using an aqueous solution of sodium acetate 2 M (400 mL), the product has been extracted using CH2Cl2. When the solvent was removed, the crude product has been purified by chromatography to receive a yellow oil (3.3, 62.1% yield).
1H NMR (400 MHz, CDCl3) δ 9.87 (s, 1H), 7.70 (s, 1H), 7.65 (d, J = 7.8 Hz, 1H), 7.51–7.45 (m, 2H), 6.54 (d, J = 8.6 Hz, 1H), 6.49 (s, 1H), 3.30–3.22 (m, 4H), 1.93–1.78 (m, 4H), 1.57–1.49 (m, 4H), 1.29 (dd, J = 14.9, 7.4 Hz, 4H), 0.99 (dd, J = 14.6, 7.3 Hz, 4H), 0.87 (t, J = 7.4 Hz, 6H), 0.62–0.54 (m, 10H). 13C NMR (101 MHz, CDCl3) δ 192.10, 154.28, 150.39, 149.42, 148.96, 133.28, 131.25, 127.32, 122.43, 122.03, 117.78, 111.05, 105.81, 54.73, 51.11, 40.30, 29.54, 25.94, 23.05, 20.40, 14.05, 13.81. ESI–MS (C30H43NO): calcd: 433.33; found: [M + 1]+, 434.34, [M + 23]+, 456.32.
2.2.3 Compound A
A solution of compound 3 (1.0 g, 2.3 mmol) and TCF acceptor (0.75 g, 3.7 mmol) in ethanol (20 mL) allows to stir at 70 °C during 3 h and after removal of the solvent under reduced pressure, the crude product has been additionally purified by silica chromatography to obtain A as a purple solid in 56.9% yield (0.86 g, 1.4 mmol) 1H NMR (400 MHz, CDCl3) δ 7.70 (d, J = 16.2 Hz, 1H), 7.56 (d, J = 6.5 Hz, 3H), 7.49 (s, 1H), 7.02 (d, J = 16.2 Hz, 1H), 6.65 (d, J = 8.6 Hz, 1H), 6.57 (d, J = 9.4 Hz, 1H), 3.41–3.34 (m, 4H), 2.02–1.90 (m, 4H), 1.83 (s, 6H), 1.63 (dt, J = 15.0, 7.6 Hz, 4H), 1.40 (dd, J = 15.0, 7.5 Hz, 4H), 1.12 (dd, J = 13.9, 6.6 Hz, 4H), 0.99 (t, J = 7.3 Hz, 6H), 0.71 (t, J = 7.3 Hz, 6H), 0.67–0.59 (m, 4H). 13C NMR (101 MHz, CDCl3) δ 175.98, 174.25, 154.62, 151.30, 149.90, 149.12, 148.77, 131.01, 130.48, 130.26, 128.95, 127.41, 122.81, 122.37, 118.73, 112.34, 111.94, 111.35, 105.71, 97.39, 97.00, 54.96, 51.23, 40.39, 29.63, 26.88, 26.02, 23.10, 20.47, 14.13, 13.93. ESI–MS (C41H50N4O): calcd: 614.40; found: [M + 1]+, 615.40, [M + 23]+, 637.38.
2.2.4 Compound B
A solution of compound 3 (0.5 g, 1.1 mmol) and CF3-Ph-TCF acceptor (0.38 g, 1.1 mmol) in ethanol (20 mL) was stired at 70 °C for 3 h, then after removal of the solvent under reduced pressure, the crude product was purified by silica chromatography to recive B as a green solid in 78% yield (0.65 g, 0.9 mmol)
1H NMR (400 MHz, CDCl3) δ 7.71 (d, J = 15.8 Hz, 1H), 7.48 (s, 6H), 7.41 (d, J = 7.9 Hz,1H), 7.31 (s, 2H), 6.94 (d, J = 15.8 Hz, 1H), 6.57 (d, J = 8.5 Hz, 1H), 6.46 (s, 1H), 3.30 (t, J = 7.1 Hz, 4H), 1.85 (d, J = 8.5 Hz, 4H), 1.60–1.50 (m, 4H), 1.32 (dd, J = 14.6, 7.2 Hz, 4H), 1.03 (d, J = 6.5 Hz, 4H), 0.91 (t, J = 7.2 Hz, 6H), 0.62 (t, J = 7.1 Hz, 6H), 0.54 (d, J = 6.3 Hz, 4H).
13C NMR (101 MHz, CDCl3) δ 175.47, 163.52, 155.28, 152.17, 151.39, 150.29, 149.93, 131.73, 131.29, 130.50, 129.95, 129.78, 127.33, 127.05, 123.60, 122.82, 118.79, 111.87, 111.53, 111.02, 110.87, 110.60, 105.63, 98.10, 96.96, 96.64, 54.93, 51.26, 40.24, 29.66, 26.01, 23.06, 20.47, 14.12, 13.90. ESI–MS (C46H49F3N4O): calcd: 730.39; found: [M + 1]+, 731.39, [M + 23]+, 785.40.
3 Results and discussion
3.1 Characterization of chromophore
The synthetic route of the chromophore preparation was sketched in scheme 1. 2-Nitrofluorene reduced with iron powder and then reacted with 1-bromobutane to produce compound 2. Then the door was subjected to Vilsmeier reactions in the presence of POCl3 and DMF, affording the aldehyde compound 3. The target chromophore A and B were obtained by condensing aldehyde 3 with TCF and CF3-Ph-TCF in refluxed ethanol, respectively.
3.2 Thermal properties
The thermal stability of chromophore A and B were explored using TGA. The decomposition temperature (Td, temperature at which 5% weight loss is occurred during heating), is presented in Fig. 1 and Table 1. Chromophores A and B displayed sufficiently good thermal stability with Td equal to about 140 °C, which is quite sufficient for the process of EO device preparation with higher temperatures (> 100 °C) during electric field poling.
3.3 Optical properties
UV–Vis absorption spectra for two chromophores performed on a Cary 5000 photo spectrometer were measured for six organic solvents (see Fig. 2) with spectral resolution 1 nm. The spectral data are summarized in Table 1. The λmax of the chromophores A and B are equal to 639 nm and 720 nm in chloroform, respectively. Moreover, it should be emphasized that A and B possess a bathochromic spectral shift equal to 64 nm and 75 nm from dioxane to chloroform, respectively. Those results clearly showed that fluorene electron donor modified by amino group play a positive effect on improving the strength of donor and shifting the ICT absorption band of chromophores to lower energy.
3.4 Theoretical simulations
To evaluate the microscopic NLO properties of the designed chromophores, DFT calculations were carried out to explore the frontier molecular orbitals and β value of A and B. The geometries of chromophores were optimized within a framework of B3LYP/6-31G∗ level. First hyperpolarizabilities (β) were estimated within the CAM-B3LYP/6-31G∗ approach. All the calculations were carried out using Gaussian 09 quantum chemical package. The used DFT approach is used for evaluation of the space charge density acentricity which is directly related to the second order nonlinear optical susceptibility.
The calculations performed by the DFT calculations, are summarized in Table 1. The obtained energy gap (ΔE) values of chromophores A and B are equal to 2.25 eV and 2.14 eV, respectively. At the same time the second order hyperpolarizaiblities for β of A and B are equal to 616 × 10−30 esu and 701 × 10−30 esu, respectively. The general space distribution of the HOMO and LUMO orbitals are presented in the Fig. 3 for A and B, respectively. These one confirm a fact that fluorene electron dominating donor origin of chromophores A and B which is beneficial for largely improvement of the donor ability due to enhancement of the space acentriicty.
3.5 Electro-optic parameters
To evaluate EO property of guest–host chromophore films A and B were prepared by doping of 25 wt% chromophores in PMMA. Corona poling was applied to induce the acentric long-range ordering of chromophores and EO coefficients were measured at wavelength 1310 nm. Film A and B afforded r33 values equal to 18 pm/V and 43 pm/V, respectively. The principal parameters are comparable with other material [24,25,26,27,28,29,30]. Following the Table 1 it is necessary to emphasize that the agreement between the calculations and the experiment is very good which confirm that the role of the phonon subsystem is not so important here.
4 Conclusions
Fluorene modified by amino groups have been syntehsized as a principally novel electron donor group. These groups possess simpler synthetic route and stronger electron donating ability with respect to the known. The results demonstrate a good performance of chromophores A and B. The EO coefficients of poled 25 wt% A/PMMA and 25 wt% B/PMMA films afford second order optical susceptibilities equal to 18 pm/V and 43 pm/V at wavelength 1310 nm, respectively. In addition, chromophores A and B demonstrate a good solubility and compatibility with traditional polymer matrices. It is demonstrated a good agreement of the experimental magnitudes with the performed quantum chemical simulations which confirm principal role of the electron subsystem and low contribution of the quasi-phonon subsystem. These results indicated that modification in fluorene may be a promising way to design and preparation of electron donor NLO chromophore.
References
J.W. Kang, T.D. Kim, J. Luo, M. Haller, A.K.Y. Jen, Very large electro-optic coefficients from in situ generated side-chain nonlinear optical polymers. Appl. Phys. Lett. 87(7), 071109 (2005)
I. Fuks-Janczarek, I.V. Kityk, R. Miedzinski, E. Gondek, J. Ebothe, I. Nzoghe-Mendome, A. Danel, Push-pull benzoxazole based stilbenes as new promising electrooptics materials. J. Mater. Sci.: Mater. Electron. 18, 519–526 (2007)
R. Tang, Z. Li, Second-order nonlinear optical dendrimers and dendronized hyperbranched polymers. Chem. Rec. 17(1), 71–89 (2017)
J. Liu, G. Xu, F. Liu, I. Kityk, X. Liu, Z. Zhen, Recent advances in polymer electro-optic modulators. RSC Adv. 5(21), 15784–15794 (2015)
G.Y. Xu, Z.F. Liu, J. Ma, B.Y. Liu, S.T. Ho, L. Wang, P.W. Zhu, T.J. Marks, J.D. Luo, A.K.Y. Jen, Organic electro-optic modulator using transparent conducting oxides as electrodes. Opt. Express 13(19), 7380–7385 (2005)
F. Qiu, H. Sato, A.M. Spring, D. Maeda, M.A. Ozawa, K. Odoi, I. Aoki, A. Otomo, S. Yokoyama, Ultra-thin silicon/electro-optic polymer hybrid waveguide modulators. Appl. Phys. Lett. 107(12), 123302 (2015)
S. Shettigar, G. Umesh, P. Poornesh, K.B. Manjunatha, A.M. Asiri, The third-order nonlinear optical properties of novel styryl dyes. Dyes Pigment. 83, 207–210 (2009)
J.L. Liu, W. Gao, I.V. Kityk, X.H. Liu, Z. Zhen, Optimization of polycyclic electron-donors based on julolidinyl structure in push-pull chromophores for second order NLO effects. Dyes Pigment. 122, 74–84 (2015)
S. Pramodini, P. Poornesh, Third-order nonlinear optical response of indigo carmine under 633 nm excitation for nonlinear optical applications. Opt. Laser Technol. 63, 114–119 (2014)
M.D. Zidan, M. Al-Ktaifani, A. Allahham, Investigation of optical nonlinearity of 3,3′-dimethylbiphenyl 4,4′-diamine and 4,4′-diisocyano-3,3′-dimethylbiphenyl using a Z-scan technique. Opt. Laser Technol. 70, 45–49 (2015)
S. Pramodini, Y.N. Sudhakar, M. SelvaKumar, P. Poornesh, Studies on third-order optical nonlinearity and power limiting of conducting polymers using the z-scan technique for nonlinear optical applications. Laser Phys. 24, 045408 (2014)
Kristyna Jilkova, Martin Mika, Petr Kostka, Frantisek Lahodny, Pavla Nekvindova, Ondrej Jankovsky, Richard Bures, Maria Kavanova, Electro-optic glass for light modulaotrs. J. Non-Cryst. Solids 518, 51–56 (2019)
P. Seetharam Shettigar, P. Poornesh, G. Umesh, B.K. Sarojini, B. Narayana, K. Prakash Kamath, Investigation of third-order nonlinear optical properties of conjugated benzodioxal derivatives. Opt. Laser Technol. 24, 1162–1166 (2010)
J. Liu, P. Si, X. Liu, Z. Zhen, Copper-catalyzed Huisgen cycloaddition reactions used to incorporate NLO chromophores into high Tg side-chain polymers for electro-optics. Opt. Mater. 47, 256–262 (2015)
Y. Yang, H. Xu, F. Liu, H. Wang, G. Deng, P. Si, H. Huang, S. Bo, J. Liu, L. Qiu, Z. Zhen, X. Liu, Synthesis and optical nonlinear property of Y-type chromophores based on double-donor structures with excellent electro-optic activity. J. Mater. Chem. C 2(26), 5124–5132 (2014)
Y. Yang, F. Liu, H. Wang, M. Zhang, H. Xu, S. Bo, J. Liu, L. Qiu, Z. Zhen, X. Liu, Synthesis and characterization of a novel second-order nonlinear optical chromophore based on a new julolidine donor. Phys. Chem. Chem. Phys. 16(37), 20209–20215 (2014)
J. Wu, S. Bo, J. Liu, T. Zhou, H. Xiao, L. Qiu, Z. Zhen, X. Liu, Synthesis of novel nonlinear optical chromophore to achieve ultrahigh electro-optic activity. Chem. Commun. 48(77), 9637–9639 (2012)
C. Hu, F. Liu, H. Zhang, F. Huo, Y. Yang, H. Wang, H. Xiao, Z. Chen, J. Liu, L. Qiu, Z. Zhen, X. Liu, S. Bo, Synthesis of novel nonlinear optical chromophores: achieving excellent electro-optic activity by introducing benzene derivative isolation groups into the bridge. J. Mater. Chem. C 3(44), 11595–11604 (2015)
H. Wang, Y. Yang, J. Liu, F. Liu, L. Qiu, X. Liu, Z. Zhen, Great improvement of performance for NLO chromophore with cyclopentadithiophenone unit as π-electron bridge. Mater. Lett. 161, 674–677 (2015)
M. Li, H. Zhang, Y. Zhang, B. Hou, C. Li, X. Wang, J. Zhang, L. Xiao, Z. Cui, Y. Ao, Facile synthesis of benzothiadiazole-based chromophores for enhanced performance of second-order nonlinear optical materials. J. Mater. Chem. C 4(38), 9094–9102 (2016)
H. Wang, M. Zhang, Y. Yang, F. Liu, C. Hu, H. Xiao, L. Qiu, X. Liu, J. Liu, Z. Zhen, Synthesis and characterization of one novel second-order nonlinear optical chromophore based on new benzoxazin donor. Mater. Lett. 164, 644–646 (2016)
L. Chen, Y. He, F. Liu, J. Liu, H. Zhang, F. Huo, S. Bo, H. Xiao, Z. Zhen, Enhanced electro-optic activity from the triarylaminophenyl-based chromophores by introducing different steric hindrance groups. Mater. Lett. 196, 230–233 (2017)
P. Si, J. Liu, Z. Zhen, X. Liu, G. Lakshminarayana, I.V. Kityk, Synthesis and characterization of NLO chromophore with benzo [1,2-b:4,5-b′]dithiophene unit as π-electron bridge. Tetrahedron Lett. 53(26), 3393–3396 (2012)
F. Liu, H. Zhang, H. Xiao, H. Xu, S. Bo, L. Qiu, Z. Zhen, L. Lai, S. Chen, J. Wang, Structure–function relationship exploration for enhanced electro-optic activity in isophorone-based organic NLO chromophores. Dyes Pigment. 157, 55–63 (2018)
H. Zhang, Y. Yang, H. Xiao, F. Liu, F. Huo, L. Chen, Z. Chen, S. Bo, L. Qiu, Z. Zhen, Enhancement of electro-optic properties of bis(N, N-diethyl)aniline based second order nonlinear chromophores by introducing a stronger electron acceptor and modifying the π-bridge. J. Mater. Chem. C 5(27), 6704–6712 (2017)
J.D. Luo, M. Haller, H. Ma, S. Liu, T.D. Kim, Y.Q. Tian, B.Q. Chen, S.H. Jang, L.R. Dalton, A.K.Y. Jen, Nanoscale architectural control and macromolecular engineering of nonlinear optical dendrimers and polymers for electro-optics. J. Phys. Chem. B 108(25), 8523–8530 (2004)
J.A. Davies, A. Elangovan, P.A. Sullivan, B.C. Olbricht, D.H. Bale, T.R. Ewy, C.M. Isborn, B.E. Eichinger, B.H. Robinson, P.J. Reid, X. Li, L.R. Dalton, Rational enhancement of second-order nonlinearity: bis-(4-methoxyphenyl)hetero-aryl-amino donor-based chromophores: design, synthesis, and electrooptic activity. J. Am. Chem. Soc. 130(32), 10565–10575 (2008)
X.H. Zhou, J. Luo, J.A. Davies, S. Huang, A.K.Y. Jen, Push–pull tetraene chromophores derived from dialkylaminophenyl, tetrahydroquinolinyl and julolidinyl moieties: optimization of second-order optical nonlinearity by fine-tuning the strength of electron-donating groups. J. Mater. Chem. 22(32), 16390 (2012)
M. He, T.M. Leslie, J.A. Sinicropi, α-Hydroxy Ketone Precursors Leading to a Novel Class of Electro-optic Acceptors. Chem. Mater. 14(5), 2393–2400 (2002)
M.Q. He, T.M. Leslie, J.A. Sinicropi, Synthesis of chromophores with extremely high electro-optic activity 1. Thiophene-bridge-based chromophores. Chem. Mater. 14(11), 4662–4668 (2002)
Author information
Authors and Affiliations
Corresponding authors
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Huo, F., Zhang, H., Chen, Z. et al. Novel nonlinear optical push–pull fluorene dyes chromophore as promising materials for telecommunications. J Mater Sci: Mater Electron 30, 12180–12185 (2019). https://doi.org/10.1007/s10854-019-01576-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-019-01576-7